MACHINE COMPONENT COMPOSED OF METAL AND RUBBER AND MANUFACTURING METHOD OF THE SAME

Abstract

The present invention is intended to provide a machine component composed of metal and rubber that results in no increase of material costs for an adhesive or increase of manufacturing costs for metal molding, causes no contamination of the metal mold or generates no foreign matter on the metal mold due to adhesion of the adhesive at the time of molding, causes no failure by separation of the adhesive from a fitting portion at the time of fitting the metal component, and is clean and favorable in appearance. A machine component 1 composed of metal and rubber is formed by applying a thermoset resin adhesive A to a surface of a metal component 2 of a predetermined shape, and vulcanizing and adhering a rubber 3 of a predetermined shape to part of the surface of the metal component 2 by metal molding.

Claims

1. A machine component composed of metal and rubber that is formed by applying a thermoset resin adhesive to a surface of a metal component of a predetermined shape, and vulcanizing and adhering a rubber of a predetermined shape to part of the surface of the metal component by metal molding, wherein the range of the adhesive applied to the surface of the metal component before the metal molding covers only a joint surface relative to the rubber.

2. The machine component composed of metal and rubber according to claim 1, wherein the machine component composed of metal and rubber is a protective cover for a bearing device, and a seal as the rubber is vulcanized and adhered to the outer peripheral surface of a cup-shaped stainless-steel main body as the metal component.

3. A manufacturing method of a machine component composed of metal and rubber, comprising: an adhesive application step of applying a thermoset resin adhesive to a surface of a metal component of a predetermined shape; and a metal molding step of vulcanizing and adhering a rubber of a predetermined shape to part of the surface of the metal component, wherein at the adhesive application step, the adhesive is applied to only a joint surface of the metal component relative to the rubber.

4. The manufacturing method of a machine component composed of metal and rubber according to claim 3, wherein the application of the adhesive to the metal component at the adhesive application step is performed by a pad printing process in which the adhesive is transferred to the metal component by pressing a pad as a transfer body with the adhesive in a predetermined region against the metal component, a screen printing process in which the adhesive on a screen plate with pores in a predetermined region is transferred to the metal component by extruding the adhesive through the pores, a brushing process, or a masking and spraying process.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0033] FIG. 1 is a vertical cross-sectional view of a bearing device with a protective cover as a machine component composed of metal and rubber according to a first embodiment of the present invention;

[0034] FIG. 2 is an enlarged vertical cross-sectional view of main parts of the same;

[0035] FIG. 3 is a vertical cross-sectional view of the protective cover as a machine component composed of metal and rubber according to the first embodiment of the present invention;

[0036] FIG. 4(a) and FIG. 4(b) are enlarged vertical cross-sectional views of main parts: FIG. 4(a) illustrates a stainless-steel main body to which an adhesive is applied; and FIG. 4(b) illustrates a protective cover manufacturing by vulcanizing and adhering a rubber seal to the stainless-steel main body by metal molding;

[0037] FIG. 5 is a vertical cross-sectional view illustrating an example of metal molding in the case of direct-pressure molding (compression (vulcanizing) molding);

[0038] FIG. 6 is a vertical cross-sectional view illustrating an example of metal molding in the case of injection (vulcanizing) molding;

[0039] FIG. 7 is a vertical cross-sectional view of a damper component as a machine component composed of metal and rubber according to a second embodiment of the present invention; and

[0040] FIG. 8(a) and FIG. 8(b) illustrate a rubber packing-equipped plate as a machine component composed of metal and rubber according to a third embodiment of the present invention: FIG. 8(a) is a plane view and FIG. 8(b) is a vertical cross-sectional view.

DESCRIPTION OF EMBODIMENTS

First Embodiment

[0041] As illustrated in the vertical cross-sectional view of FIG. 1 and the enlarged vertical cross-sectional view of main parts of FIG. 2, a bearing device 11 with a protective cover 1A as a machine component 1 composed of metal and rubber according to a first embodiment of the present invention, includes: a bearing having an inner ring 12 with an inner ring track surface 12A on an outer peripheral surface, an outer ring 13 with an outer ring track surface 13A on an inner peripheral surface, and rolling elements 14, 14, . . . rolling between the inner ring track surface 12A and the outer ring track surface 13A; a magnetic encoder 8 that is positioned at one axial end portion of the bearing and fixed to the inner ring 12 by a fixing member 9; a sensor 10 that is fixed to the outer ring 13 and opposed to a magnetic pole of the magnetic encoder 8 to detect rotation of the magnetic encoder 8; and a seal member 15 that is arranged at the other axial end portion of the bearing, and the like.

[0042] As illustrated in the enlarged vertical cross-sectional view of main parts of FIG. 2 and the vertical cross-sectional view of FIG. 3, in the protective cover 1A, a first cylindrical part 4 and a second cylindrical part 5 smaller in diameter than the first cylindrical part 4 and connected to an end edge of the first cylindrical part 4 are provided at a maximum outer diameter part of a main body 2A as a machine component 2, and a seal 3A as a rubber 3 is vulcanized and adhered to the outer peripheral surface of the second cylindrical part 5.

[0043] In the protective cover 1A, a fitting portion C as the outer peripheral surface of the first cylindrical part 4 is pushed into the outer ring 13 to cover the magnetic encoder 8 and intervene between the magnetic encoder 8 and the sensor 10.

[0044] Accordingly, the inside of the bearing is sealed by the protective cover 1 having the seal 3A and the seal member 15 at the axial both end portions of the bearing. The magnetic encoder 8 is accommodated in the inner space of the bearing to protect the magnetic encoder 8 and the interior of the bearing from foreign matter and the like.

[0045] The main body 2A of the protective cover 1A is formed by pressing a stainless steel plate material such as SUS304 into a cup shape to include the first cylindrical part 4, the second cylindrical part 5, and the like.

[0046] The seal 3A as the rubber 3 may be one of oil-resistant rubber materials such as nitrile rubber (NBR), hydrogenated nitrile rubber (HNBR), acrylic rubber (ACM), ethylene-acrylic rubber (AEM), fluorine rubber (FKM, FPM), and silicon rubber (VQM), or a blend of two or more of the same.

[0047] Next, an adhesive application step of applying a thermoset resin adhesive to the surface of the stainless steel main body 2A as the metal component 2 will be described.

[0048] First, the thermoset resin adhesive may be any of general rubber vulcanizing adhesives such as a phenolic resin adhesive and a silane adhesive.

[0049] For example, in the case of using a phenolic resin adhesive, although there is no particular limitation on its composition, the resin adhesive may be formed by dissolving a novolac-type phenolic resin, a resol-type phenolic resin, and a hardening agent such as hexamethylenetetramine in methanol or methylethylketone. For increasing adhesiveness, a novolac-type epoxy resin may be mixed into the foregoing adhesive.

[0050] As illustrated in the enlarged vertical cross-sectional view of main parts of FIG. 4(a), the range of application of a thermoset resin adhesive A to the surface of the stainless steel main body 2A covers only a joint surface B as a predetermined range in which the seal 3A as the rubber 3 is adhered. The adhesive A is not applied to portions other than the joint surface B.

[0051] The application of the adhesive A to the predetermined range (joint surface B) of part of the surface of the main body 2A can be performed by a pad printing process in which a pad as a transfer body with the adhesive A in a predetermined region is pressed against the main body 2A, a screen printing process in which the adhesive A on a screen plate with pores in a predetermined region is extruded through the pores to transfer the adhesive A to the main body 2A, a brushing process, or a masking and spraying process.

[0052] According to the foregoing application method, it is possible to perform an application work in a stable and reliable manner such that the adhesive A is applied to only the joint surface B of the main body 2A as the metal component 2 relative to the seal 3A as the rubber 3, and the adhesive A is not applied to portions other than the joint surface B.

[0053] Next, descriptions will be given as to a metal molding step of vulcanizing and adhering the seal 3A as the rubber 3 of a predetermined shape to the main body 2A as the metal component 2 to which the adhesive A is applied as illustrated in FIG. 4(a), thereby to manufacture the protective cover 1A as the machine component 1 composed of metal and rubber illustrated in the enlarged vertical cross-sectional view of FIG. 4(b).

[0054] Such metal molding can be performed by direct-pressure molding (compression (vulcanizing) molding) by which, in the state where the main body 2A is set in a heated lower metal mold part 6A, an upper metal mold part 6B is closed and a raw rubber material D is pressed and hardened as illustrated in the vertical cross-sectional view of FIG. 5.

[0055] Alternatively, as illustrated in the vertical cross-sectional view of FIG. 6, the metal molding may be performed by injection (vulcanizing) molding by which, in the state where the main bodies 2A, 2A, . . . are set in a lower metal mold part 7A and an upper metal mold part 7B is closed, a liquefied raw rubber material E is charged into cavities.

[0056] In the example 1 described above, the bearing device 11 to which the protective cover 1A is to be attached includes the magnetic encoder 8. However, the protective cover 1A is also usable for a bearing device without the magnetic encoder 8.

Second Embodiment

[0057] As illustrated in the vertical cross-sectional view of FIG. 7, a damper component 1B as the machine component 1 composed of metal and rubber according to a second embodiment of the present invention is formed by vulcanizing and adhering a damper 3B as the rubber 3 of a predetermined shape to a metal fitting 2B as the metal component 2.

[0058] In the damper component 1B, at the same adhesive application step as that in the first embodiment, the adhesive is applied to only a joint surface B of the metal fitting 2B relative to the damper 3B, and at the same metal molding step as that in the first embodiment, the damper 3B is vulcanized and adhered to the metal fitting 2B.

Third Embodiment

[0059] As illustrated in the vertical cross-sectional views of FIG. 8(a) and FIG. 8(b), a rubber packing-equipped plate 1C as the machine component 1 composed of metal and rubber according to a third embodiment of the present invention is formed by vulcanizing and adhering a packing 3C as the rubber 3 of a predetermined shape to a metal plate 2C as the metal component 2.

[0060] In the rubber packing-equipped plate 1C, at the same adhesive application step as that in the first embodiment, the adhesive is applied to only a joint surface B of the metal plate 2C relative to the packing 3C, and at the same metal molding step as that in the first embodiment, the packing 3C is vulcanized and adhered to the metal plate 2C.

[0061] Applicable objects in the present invention are not limited to the protective cover 1A, the damper component 1B, and the rubber packing-equipped plate 1C in the foregoing embodiments but the present invention is also applicable to all kinds of metal components 1 composed of metal and rubber formed by applying the thermoset resin adhesive A to the surface of the metal component 2 of a predetermined shape, and vulcanizing and adhering the rubber 3 of a predetermined shape to part of the surface of the metal component 2 by metal molding.

[0062] According to the machine component 1 composed of metal and rubber and the manufacturing method of the same as described above, since the range of the adhesive A applied to the surface of the metal component 2 covers only the joint surface B relative to the rubber 3, the adhesive A is not applied to portions other than the predetermined range of the rubber 3 to be adhered. This results in a very small amount of waste adhesive A without increase of material costs for the adhesive A.

[0063] In addition, since the range of the adhesive A applied to the surface of the metal component 2 covers only the joint surface B relative to the rubber 3, there occurs no failure that the rubber material is vulcanized and adhered beyond the predetermined range of the rubber 3 to be adhered. This eliminates the need for a complicated and high-accuracy metal mold structure, which suppresses increase of manufacturing costs at metal molding. In addition, this configuration can be used for all of vulcanizing production systems with a high degree of flexibility in manufacture.

[0064] Further, since the range of the adhesive A applied to the surface of the metal component 2 covers only the joint surface B relative to the rubber 3, the adhesive A does not stick to the metal mold to contaminate the metal mold or generate foreign matter on the metal mold at the time of molding.

[0065] Furthermore, since the range of the adhesive A applied to the surface of the metal component 2 covers only the joint surface B relative to the rubber 3, when the metal component 2 is fitted, there occurs no failure resulting from the separation of the adhesive A from the fitting portion C. For example, in the case where the machine component 1 composed of metal and rubber is the protective cover 1A, when the main body 2A is pushed into the outer ring 13 of the bearing, there occurs no situation in which the adhesive A separates from the fitting portion C and bites into the rubber seal 3A to cause airtightness failure or the separated adhesive A remains as foreign matter in the bearing.

[0066] Moreover, since the range of the adhesive A applied to the surface of the metal component 2 covers only the joint surface relative to the rubber 3, the adhesive A does not exist on the surface of the metal component 2 to be visually checked. Accordingly, the finished product is clear and favorable in appearance and is improved in commodity value.

REFERENCE SIGNS LIST

[0067] A Thermoset resin adhesive [0068] B Joint surface [0069] C Fitting portion [0070] D Raw rubber material [0071] E Liquefied raw rubber material [0072] 1 Machine component composed of metal and rubber [0073] 1A Protective cover [0074] 1B Damper component [0075] 1C Rubber packing-equipped plate [0076] 2 Metal component [0077] 2A Stainless steel main body [0078] 2B Metal fitting [0079] 2C Metal plate [0080] 3 Rubber [0081] 3A Seal [0082] 3B Damper [0083] 3C Packing [0084] 4 First cylindrical part [0085] 5 Second cylindrical part [0086] 6A, 7A Lower metal mold part [0087] 6B, 7B Upper metal mold part [0088] 8 Magnetic encoder [0089] 9 Fixing member [0090] 10 Sensor [0091] 11 Bearing device [0092] 12 Inner ring [0093] 12A Inner ring track surface [0094] 13 Outer ring [0095] 13A Outer ring track surface [0096] 14 Rolling element [0097] 15 Seal member