High molecular weight polymers having high olefin content

Abstract

The present invention discloses polymers prepared from polar vinyl monomers and non-polar olefin monomers with the polymers having high olefin content and high weight average molecular weights as well as methods of preparing them. The inventive polymers possess interesting properties that make them particularly attractive in several industrial applications.

Claims

1. A method of preparing a functionalized polymer with a weight average molecular weight in the range 50,000-3.0 million, wherein said polymer comprises, in its repeat unit, (i) one or more activated olefins independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, alkylidene malonate and cinnamate and (ii) one or more non-activated olefins independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulphide and allylamide, wherein said one or more non-activated olefins constitutes at least 30% of the polymer, said method comprising the steps of: (a) preparing a solution containing said one or more of activated olefins and said one or more non-activated olefins, optionally in the presence of a solvent; (b) precomplexing equimolar amounts of said one or more of activated olefins and a Lewis acid to form a mix and adding the mix to the solution in (a) to form a mixture; (c) optionally adding a radical initiator; and (d) reacting said mixture at temperatures of from 78 C. to room temperature for a time sufficient to obtain the desired polymer.

2. The method of claim 1, wherein said radical initiator is present.

3. The method of claim 1, wherein said polymer is a copolymer or a terpolymer comprising said activated olefins and said non-activated olefins.

4. The method of claim 1, wherein said terpolymer further comprises one or more crosslinkable functionality.

5. The method of claim 1, wherein the Lewis acid is selected from the group consisting of EtAlCl.sub.2, ethyl aluminum sesquichloride, ZnCl.sub.2, AlCl.sub.3, AlBr.sub.3, BF.sub.3, TiCl.sub.4 and combinations thereof.

6. The method of claim 1, wherein said activated olefin is a (meth)acrylate wherein said (meth)acrylate is represented by the formula H.sub.2CC(G)CO.sub.2R.sub.1, where G may be hydrogen, halogen or alkyl of 1 to 6 carbon atoms, and R.sub.1 may be selected from alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, aralkyl or aryl groups of 1 to 16 carbon atoms, any of which may be optionally substituted or interrupted as the case may be with the moiety selected from the group consisting of silane, silicon, oxygen, halogen, carbonyl, hydroxyl, ester, carboxylic acid, urea, urethane, carbamate, amine, amide, sulfur, sulfonate and sulfone and combinations thereof.

7. The method of claim 1, wherein said non-activated olefin is selected from the group consisting of an unsubstituted alkene, a monosubstituted alkene, a disubstituted alkene and a trisubstituted alkene.

8. The method of claim 6, wherein said (meth)acrylate is selected from the group consisting of methyl(meth)acrylate, ethyl(meth)acrylate, butyl(meth)acrylate, isobutyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, isooctyl(meth)acrylate, glycidyl(meth)acrylate, cyclohexyl(meth)acrylate, isobornyl(meth)acrylate, benzyl(meth)acrylate, 2-hydroxy(meth)acrylate, trimethoxybutyl(meth)acrylate, ethylcarbitol(meth)acrylate, phenoxyethyl(meth)acrylate, 2-hydroxyethyl(meth)acrylate, trimethylolpropanetri(meth)acrylate, tetramethylolmethane tetra(meth)acrylate, pentaerythritol hexa(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol monohydroxy penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, 1,4-butyleneglycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, polyethyleneglycol di(meth)acrylate and oligoester(meth)acrylate.

9. The method of claim 7, wherein said non-activated olefin is selected from the group consisting of ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 3-methyl-1-butene, isobutylene, diisobutylene, 2-methyl-1-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1,1-dimethylpentene, vinylcyclohexane, cyclopropene, cyclobutene, cyclopentene, cyclohexene, norbornene, limonene, -pinene, -pinene, camphene, cis-cyclooctene and trans-cyclooctene.

10. The method of claim 1, wherein said optional solvent, if present, is a hydrocarbon or a halogenated hydrocarbon.

11. The method of claim 10, wherein said hydrocarbon is selected from the group consisting of toluene, xylene, benzene, n-hexane, n-heptane, chlorobenzene, methylene chloride, 1,2-dichloroethane, cyclohexane, methyl cyclohexane and mixtures thereof.

12. The method of claim 2, wherein said radical initiator is a peroxide selected from the group consisting of benzoyl peroxide, methyl ethyl ketone peroxides, di-t-butyl peroxide, di-t-amyl peroxide, dicumyl peroxide, diacyl peroxide, decanoyl peroxide, lauroyl peroxide, peroxydicarbonates, peroxyesters, dialkyl peroxides, hydroperoxide, peroxyketals, 4,4-azobis(4-cyanovaleric acid), 1,1-azobis(cyclohexanecarbonitrile), 2,2-azobisisobutyronitrile (AIBN), and mixtures thereof.

13. The method of claim 12, wherein said peroxide is benzoyl peroxide.

14. The method of claim 1, wherein said one or more activated (meth)acrylates is selected from methyl acrylate or n-butyl acrylate, and said one or more non-activated olefins is selected from isobutylene, 1-octene or 2-methylpentene.

15. A method of preparing a polymer with a weight average molecular weight in the range 50,000-3.0 million, wherein said polymer comprises, in its repeat unit, (i) one or more activated olefins independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, alkylidene malonate and cinnamate and (ii) one or more non-activated olefins independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulphide and allylamide, wherein said one or more non-activated olefins constitutes at least 30% of the polymer, said method comprising the steps of: (a) preparing a solution containing said one or more of activated olefins and said one or more non-activated olefins, optionally in the presence of a solvent; (b) precomplexing equimolar amounts of said one or more of activated olefins and a Lewis acid to form a mix and adding the mix to the solution in (a) to form a mixture; (c) optionally adding a radical initiator; and (d) reacting said mixture at temperatures of about 78 C. to about 80 C. for a time sufficient to obtain the desired polymer, wherein said polymer is further reacted such that one or more functionalities are incorporated into the polymer to prepare a functionalized polymer.

16. The method of claim 15, wherein said one or more functionalities are selected from the group consisting of epoxy, carboxylic acid, hydroxy, thiol, amide, oxazoline, acetoacetate, isocyanate, carbamate, amine, amine salt, quaternized amine, thioether, sulfide, sulfonium salt, acetophenone, acyl phosphine oxide, thioxanthone, benzoin ether, benzyl ketal and combinations thereof.

17. The method of claim 1, wherein said polymer comprises at least 50% of said one or more non-activated olefin.

18. A polymer prepared by the method of claim 1.

19. A reaction product prepared by a Lewis acid-catalyzed copolymerization reaction, wherein said product comprises, in its repeat unit, one or more activated olefins and at least 30% content of one or more non-activated olefins, and has a weight average molecular weight in the range 50,000-3.0 million, wherein said one or more activated olefins are independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, cinnamate and alkylidene malonate, and said one or more non-activated olefins are independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulfide and allyl amide.

20. A reaction product prepared by a Lewis acid-catalyzed copolymerization reaction, wherein said product comprises, in its repeat unit, one or more activated olefins and at least 30% content of one or more non-activated olefins, and has a weight average molecular weight in the range 50,000-3.0 million, wherein said one or more activated olefins are independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, cinnamate and alkylidene malonate, and said one or more non-activated olefins are independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulfide and allyl amide, wherein said reaction product is a terpolymer further comprising one or more crosslinkable functionalities.

21. The reaction product of claim 20, wherein said one or more crosslinkable functionalities are selected from the group consisting of benzophenone, acetophenone, phosphine oxide, thioxanthone, benzoin ether, benzyl ketal, carboxylic acid, hydroxyl, thiol and combinations thereof.

22. A material comprising the reaction product of claim 19.

23. The material of claim 22 being an adhesive, an elastomer, a toughener for a cyanoacrylate and/or epoxy, a polymeric photoinitiator or a personal care product.

24. The reaction product of claim 19, wherein the weight average molecular weight is in the range 500,000-1.5 million.

25. The reaction product of claim 19, wherein the Lewis acid is selected from the group consisting of EtAlCl.sub.2, ethyl aluminum sesquichloride, ZnCl.sub.2, AlCl.sub.3, AlBr.sub.3, BF.sub.3, TiCl.sub.4 and combinations thereof.

26. The reaction product of claim 19, wherein said activated olefin is a (meth)acrylate, wherein said (meth)acrylate is represented by the formula H.sub.2CC(G)CO.sub.2R.sub.1, where G may be hydrogen, halogen or alkyl of 1 to 6 carbon atoms, and R.sub.1 may be selected from alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, aralkyl or aryl groups of 1 to 16 carbon atoms, any of which may be optionally substituted or interrupted as the case may be with the moiety selected from the group consisting of silane, silicon, oxygen, halogen, carbonyl, hydroxyl, ester, carboxylic acid, urea, urethane, carbamate, amine, amide, sulfur, sulfonate and sulfone and combinations thereof.

27. The reaction product of claim 19, wherein said non-activated olefin is selected from the group consisting of an unsubstituted alkene, a monosubstituted alkene, a disubstituted alkene and a trisubstituted alkene.

28. The method of claim 15, wherein said radical initiator is present.

29. The method of claim 28, wherein said radical initiator is a peroxide selected from the group consisting of benzoyl peroxide, methyl ethyl ketone peroxides, di-t-butyl peroxide, di-t-amyl peroxide, dicumyl peroxide, diacyl peroxide, decanoyl peroxide, lauroyl peroxide, peroxydicarbonates, peroxyesters, dialkyl peroxides, hydroperoxide, peroxyketals, 4,4-azobis(4-cyanovaleric acid), 1,1-azobis(cyclohexanecarbonitrile), 2,2-azobisisobutyronitrile, and combinations thereof.

30. The method of claim 29, wherein said peroxide is benzoyl peroxide.

Description

DETAILED DESCRIPTION OF THE INVENTION

(1) For purpose of this present invention, the following definitions will apply:

(2) The terms (meth)acrylate or (meth)acryloxy will include methacrylate and acrylate and methacryloxy and acryloxy, respectively, as applicable.

(3) The terms halogen, halo, or hal when used alone or part of another group mean chlorine, fluorine, bromine or iodine.

(4) In an embodiment, the present invention discloses a process to prepare a polymer with weight average molecular weight in the range 50,000-3.0 million, wherein said polymer comprises, in its repeat unit, (i) one or more activated olefins independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, alkylidene malonate and cinnamate and (ii) one or more non-activated olefins independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulphide and allylamide, wherein said one or more non-activated olefins constitutes at least 30% of the polymer, said method comprising the steps of:

(5) (a) preparing a solution containing said one or more of activated olefins and said one or more non-activated olefins, optionally in the presence of a solvent;

(6) (b) precomplexing equimolar amounts of said one or more of activated olefins and a Lewis acid to form a mix and adding the mix to the solution in (a) to form a mixture;

(7) (c) optionally adding a radical initiator; and

(8) (d) polymerizing said mixture at temperatures of about 78 C. to about 80 C. for a time sufficient to obtain the desired polymer.

(9) In another embodiment, the activated olefin is a (meth)acrylate wherein said (meth)acrylate is represented by the formula H.sub.2CC(G)CO.sub.2R.sub.1, where G may be hydrogen, halogen or alkyl of 1 to 6 carbon atoms, and R.sub.1 may be selected from alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkaryl, aralkyl or aryl groups of 1 to 16 carbon atoms, any of which may be optionally substituted or interrupted as the case may be with the moiety selected from the group consisting of silane, silicon, oxygen, halogen, carbonyl, hydroxyl, ester, carboxylic acid, urea, urethane, carbamate, amine, amide, sulfur, sulfonate and sulfone and combinations thereof.

(10) Non-limiting examples of suitable (meth)acrylates are methyl(meth)acrylate, ethyl(meth)acrylate, butyl(meth)acrylate, isobutyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, isooctyl(meth)acrylate, glycidyl(meth)acrylate, cyclohexyl(meth)acrylate, isobornyl(meth)acrylate, benzyl(meth)acrylate, 2-hydroxy(meth)acrylate, trimethoxybutyl(meth)acrylate, ethylcarbitol(meth)acrylate, phenoxyethyl(meth)acrylate, 2-hydroxyethyl(meth)acrylate, trimethylolpropanetri(meth)acrylate, tetramethylolmethane tetra(meth)acrylate, pentaerythritol hexa(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol monohydroxy penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, 1,4-butyleneglycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, polyethyleneglycol di(meth)acrylate and oligoester(meth)acrylate.

(11) In one particularly useful aspect of the invention, the (meth)acrylate is methyl(meth)acrylate, ethyl(meth)acrylate, butyl(meth)acrylate, isobutyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, isooctyl(meth)acrylate, glycidyl(meth)acrylate or cyclohexyl(meth)acrylate.

(12) The non-activated olefin is selected from the group consisting of an unsubstituted alkene, a monosubstituted alkene, a disubstituted alkene and a trisubstituted alkene.

(13) Non-limiting examples of suitable non-activated olefins are ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 2-methyl-pentene, 3-methyl-1-butene, isobutylene, diisobutylene, 2-methyl-1-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1,1-dimethylpentene, vinylcyclohexane, cyclopropene, cyclobutene, cyclopentene, cyclohexene, norbornene, limonene, -pinene, -pinene, camphene, cis-cyclooctene and trans-cyclooctene.

(14) In one particularly useful aspect of the invention, the non-activated olefin is selected from ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 2-methylpentene, 3-methyl-1-butene, isobutylene or diisobutylene.

(15) In one particularly useful aspect of the invention, the activated olefin is selected from methyl acrylate or n-butyl acrylate, and the non-activated olefin is selected from 2-methylpentene, isobutylene or 1-octene.

(16) A solvent is generally not necessary for the reaction to proceed if the reactants are liquid and soluble enough in each other as well as to dissolve the catalyst sufficiently for the reaction to proceed. However, if a solvent is desired, suitable solvent may be selected from a hydrocarbon, halogenated hydrocarbon, alkyl ester (e.g. ethyl acetate, butyl acetate and the like) or mixtures thereof. Non-limiting examples of suitable solvents are toluene, xylene, benzene, n-hexane, n-heptane, chlorobenzene, methylene chloride, 1,2-dichloroethane, cyclohexane, methyl cyclohexane and mixtures thereof. A particularly preferred solvent is toluene.

(17) The reaction is performed in the presence of a Lewis acid catalyst. Non-limiting examples of suitable Lewis acids include EtAlCl.sub.2, ethyl aluminum sesquichloride, ZnCl.sub.2, AlCl.sub.3, AlBr.sub.3, BF.sub.3, TiCl.sub.4 and combinations thereof. The choice of the Lewis acid depends on any solvent selected for the reaction since solubility of the Lewis acid in that particular solvent should be taken into consideration. A particularly preferred Lewis acid is EtAlCl.sub.2.

(18) The activated olefin and the Lewis acid catalyst are ideally precomplexed to form a mix prior to the addition of the copolymerization reactant mixture.

(19) A free radical initiator is not always necessary for the polymerization reaction to proceed. Thus, it was found that the polymerization reaction could be performed with an initiator as well as without initiator to satisfactory and desired yields, conversion and molecular weights. If an initiator is used, suitable radical initiators may be selected from the group consisting of benzoyl peroxide, methyl ethyl ketone peroxides, di-t-butyl peroxide, di-t-amyl peroxide, dicumyl peroxide, diacyl peroxide, decanoyl peroxide, lauroyl peroxide, 2,4-dichlorobenzoyl peroxide, t-butyl perbenzoate, cumene hydroperoxide (CHP), 2,5-bis(t-butylperoxy) 2,5-dimethylhexane, peroxydicarbonates, peroxyesters, dialkyl peroxides, hydroperoxide, peroxyketals, 4,4-azobis(4-cyanovaleric acid), 1,1-azobis(cyclohexanecarbonitrile), 2,2-azobisisobutyronitrile (AIBN), and mixtures thereof. A particularly preferred initiator in such cases is benzoyl peroxide. Free radical initiators may be incorporated in any amounts useful to achieve the desired reaction or cure. Desirably, they are present in amounts of about 0.01% to about 10% by weight of the total composition. Combinations of the free-radical initiators are also useful.

(20) The reaction temperature and duration may be selected as is suitable or sufficient to obtain the desired polymer in desired yields. Reaction temperatures, for example, may range generally from about 78 C. to about 80 C., specifically from about 78 C. to about 40 C. and more specifically from about 78 C. to about the room temperature (RT).

(21) In an illustrative process of the invention, methyl acrylate (MA, 1 eq) and isobutylene (IB, 10 eq) were reacted in the presence of benzoyl peroxide (BPO, 0.01 eq) as radical initiator and EtAlCl.sub.2 (0.2 eq) as Lewis acid in toluene solvent. The Lewis acid was complexed with equimolar amount of the acrylate prior to the addition of the copolymerization mixture. Several runs were performed and the copolymers in the molecular weight range 500,000-1.5 million were obtained (Table 1, entries 1 and 2). Higher molecular weights copolymers were also obtained even with higher alkene such as 1-octene (entry 3). 1,1-Disubstituted alkene such as 2-methyl pentene also gave higher molecular weight copolymer under similar conditions (entry 4). These results established that high molecular weight copolymers with high olefin content can be obtained under low temperature conditions in the presence of Lewis acids. The excess olefin can be distilled and recycled to make the process more economical.

(22) TABLE-US-00001 TABLE 1 Copolymerization study of olefins (10 eq) and acrylates (1 eq) in the presence of 0.01 eq of BPO and 0.2 eq of EtAlCl.sub.2 in toluene Acrylate:Olefin Entry Acrylate Olefin Mol. wt. Range ratio 1 MA Isobutylene 500,000-1.5 million ~1:1 2 n-BA isobutylene 500,000-1.5 million ~1:1 3 n-BA 1-Octene 200,000-400,000 ~1:1 4 n-BA 2-methyl ~250,000 ~1:1 pentene

(23) Table 2 lists the properties (e.g. mol. weights) of several other polymers prepared by the process of the invention, demonstrating the flexibility of the process as well as the feasibility to produce polymers with tailor-made properties by adjusting the reaction conditions suitably.

(24) TABLE-US-00002 TABLE 2 Lewis Non-activated acid(eq)/initiator Entry Acrylate Olefin Temp. Solvent Initiator (eq) Mol. Wt. 1 n-BA 2- RT Toluene BPO 0.2/0.01 90,000 methylpentene 2 n-BA 2- 40 C. Toluene BPO 0.2/0.01 242,000 methylpentene 3 n-BA 1-Octene RT Toluene BPO 0.2/0.01 183,000 4 n-BA 1-Octene 40 C. none BPO 0.2/0.01 340,000 5 MA 1-Octene RT Toluene BPO 0.2/0.01 127,634 6 MA 1-Octene 40 C. toluene BPO 0.2/0.01 304,512 7 n-BA 1-Octene 40 C. None BPO 0.4/0.02 260,000 8 n-BA 1-Octene 40 C. Toluene BPO 0.4/0.02 150,000 9 n-BA 1-Octene 40 C. None BPO 0.2/0.01 580,000 10 n-BA 1-Octene 40 C. Toluene BPO 0.2/0.01 236,000

(25) Characterization

(26) .sup.1H and .sup.13C NMR spectral techniques were used to establish % of alkene and acrylate present in the copolymer. The data indicated that all of these copolymers contained olefins and acrylates in approximately 1:1 ratio. A copolymerization experiment was performed by lowering the 1-octene reactant ratio from 10:1 to 4:1 with respect to acrylate. However, this did not appear to affect the 1-octene content in the copolymer significantly. GC/pyrolysis data of several copolymers indicated mostly alternating type sequence of alkene and acrylate in the copolymer. Alkene-acrylate dimeric and trimeric fragments appeared in the GC pyrolysis spectrum, which indicated mostly alternating type of sequence. The polymers obtained by the inventive process had high weight average molecular weights. Weight average molecular weights of about 50,000 to about 3.0 million could be routinely obtained in the polymers.

(27) The reaction lends itself to the preparation of copolymers, terpolymers and the like with equal ease. Several such reactions are described in more detail in the Examples section. Functionalized polymers could be prepared as well. Polymers with suitable functionalities could be prepared. Non-limiting examples of such functionalities include functional groups such as epoxy, carboxylic acid, hydroxy, thiol, amide, oxazoline, acetoacetate, isocyanate, carbamate, aceto, amine, amine salt, quaternized amine, thioether, sulfide, sulfonium salt, acetophenone, acyl phosphine oxide, thioxanthone, benzoin ether, benzyl ketal, siloxy, cyano, cyanoacrylate, cyanoacetate, alkyl ether, reactive silanes such as alkoxy silanes, e.g., tetramethyoxysilane, epoxyether and vinyl ether and combinations thereof. The functional groups could be introduced by processes such as, for example, starting with a functional group-containing monomer as a reactant or preparing a non-functionalized polymer which is further reacted with suitable reagents to introduce the functional groups. Creating functional ends on the polymer may also be done by performing an end-capping reaction. For example, these groups may be added to one or more of the terminal ends of the inventive resin via reaction with compounds containing these functionalities.

(28) In another embodiment, the present invention includes reaction products (polymers) formed by the inventive process described above. Thus, in an embodiment, the invention provides a reaction product prepared by a Lewis acid-catalyzed copolymerization reaction, wherein said product comprises, in its repeat unit, one or more activated olefins and at least 30% content of one or more non-activated olefins, and has a weight average molecular weight in the range 50,000-3.0 million, wherein said one or more activated olefins are independently selected from the group consisting of a (meth)acrylate, acrylonitrile, (meth)acrylamide, maleimide, itaconimide, citroconimide, maleic anhydride, cyanoacrylate, maleate, fumarate, crotonate, cinnamate and alkylidene malonate, and said one or more non-activated olefins are independently selected from the group consisting of an unsubstituted alkene, monosubstituted alkene, disubstituted alkene, trisubstituted alkene, allyl ether, allyl ester, allyl sulfide and allyl amide.

(29) The reaction product can be a copolymer, terpolymer and the like. The copolymer, terpolymer and the like may also comprise one or more crosslinkable functionalities such as, for example, those described above.

(30) In yet another embodiment, the present invention includes materials or articles formed using the reaction products of the invention. Non-limiting examples of such materials and articles include an adhesive, an elastomer, a toughener for a cyanoacrylate and/or epoxy, a polymeric photoinitiator or a personal care product.

(31) The present invention is further described by the Examples shown below. The Examples are provided for illustrative purposes only and are not to be considered as limiting the scope of the invention or the claims in any way.

EXAMPLES

Example 1

Synthesis of Methyl Acrylate (MA) and Isobutylene Copolymer

(32) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath was taken 65.6 g of toluene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture. 90 g of isobutylene was transferred to the flask.

(33) In another separate flask 0.43 g of BPO in 13.3 g of methyl acrylate (MA) was dissolved and transferred to the reaction flask.

(34) In a separate flask 2.1 g of MA and 2.4 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 19.5 mL of 25 wt % ethyl aluminum dichloride was added to this flask dropwise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (26 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 2

Synthesis of n-butyl acrylate/1-Octene Copolymer

(35) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 40 g of toluene and 40 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(36) In a separate flask 86 mg of BPO in 3.66 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(37) In another separate flask 0.91 g of BA and 2 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 3.9 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (8 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 3

Synthesis of Butyl Acrylate and Isobutylene Copolymer

(38) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath was taken 110.8 g of toluene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture. 150 g of isobutylene was transferred to the flask.

(39) In a separate flask 0.72 g of BPO in 30.46 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(40) In another separate flask 7.61 g of BA and 8 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 32.54 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask dropwise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (58.5 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 4

Synthesis of Butyl Acrylate (BA), Ethyleneglycol Phenylether Acrylate and 1-Octene Terpolymer

(41) ##STR00001##
(m and n indicate the amount of each monomer moiety incorporated into the repeat unit of the polymer.)

(42) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 130 g of toluene and 175 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(43) In a separate flask 0.76 g of BPO in 34 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(44) In another separate flask 6 g of BA, 3 g of ethyleneglycol phenyl ether acrylate and 8 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 34.2 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the terpolymer (crude 67.8 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 5

Synthesis of Copolymer of Methyl Methacrylate (MMA) and 1-Octene

(45) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 40 mL of toluene and 56.1 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(46) In a separate flask 0.24 g of BPO in 8 g of methyl methacrylate (MMA) was dissolved and transferred to the reaction flask.

(47) In another separate flask 2 g of MMA and 2 mL toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 11 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (2 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 6

Synthesis of Butyl Acrylate (BA), Benzylacrylate and 1-Octene Terpolymer

(48) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 115 g of toluene and 87.6 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(49) In a separate flask 0.38 g of BPO in 16 g of butyl acrylate (BA) and 1.27 g of benzyl acrylate was dissolved and transferred to the reaction flask.

(50) In another separate flask 4 g of BA and 5 mL toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 17.1 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the terpolymer (36.9 g, crude). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 7

Synthesis of Butyl Acrylate (BA) and Diisobutylene Copolymer

(51) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath was taken 80 g of toluene and 87.6 g of diisobutylene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(52) In another separate flask 0.38 g of BPO in 20 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(53) In a separate flask 4 g of BA and 4 mL of toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 17.1 mL of 25 wt % ethyl aluminum dichloride was added to this flask dropwise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (26.6 g, crude). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 8

Synthesis of butyl acrylate (BA), 4[2-acryloxyethoxy]benzophenone and 1-Octene Terpolymer

(54) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 40 g of toluene and 40 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(55) In a separate flask 0.17 g of BPO in 7.34 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(56) In another separate flask 1.34 g of BA, 1.05 g of 4[2-acryloxyethoxy]benzophenone and 2 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 7.81 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the terpolymer (8 g). The composition was determined by proton NMR (benzophenone protons at 6-8.8 ppm) and the molecular weight was determined by Gel Permeation Chromatography (GPC). The GPC analysis was performed using both RI and UV techniques. UV GPC indicated the presence of UV active polymer peaks similar to those indicated by the RI detector. This established the incorporation of 4-[2-acryloxyethoxy]benzophenone unit in the terpolymer.

Example 9

Synthesis of Butyl Acrylate (BA) and 1-Octene Copolymer in the Absence of Radical Initiator

(57) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 40 g of toluene and 40 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture. 3.66 g of butyl acrylate (BA) was transferred to the reaction flask.

(58) In another separate flask 0.91 g of BA and 2 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 3.9 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (4 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

(59) By following a similar method, a copolymer of MA and 1-octene was also synthesized in the absence of a free radical initiator.

(60) The polymers were found to have the following data

(61) TABLE-US-00003 Non-activated Acrylate:Octene Entry Acrylate Olefin Mol. Wt. ratio by .sup.1HNMR 1 n-BA 1-octene 242,000 50:50 2 MA 1-Octene 300,000 53:47

Example 10

Synthesis of Methyl Acrylate/1-Octene Copolymer at Room Temperature

(62) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 94 g of toluene and 150 g of 1-octene. The reaction flask was purged with nitrogen.

(63) In a separate flask 81 mg of BPO in 23 g of methyl acrylate (MA) was dissolved and transferred to the reaction flask.

(64) In another separate flask 5.75 g of MA and 6 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 36.6 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (44 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

(65) BA and 1-Octene compositions were also synthesized at room temperature.

Example 11

Synthesis of Methyl Acrylate (MA) and 1-Octene Copolymer in the Absence of Radical Initiator

(66) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were, taken 94 g of toluene and 150 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture. 23 g of methyl acrylate (MA) was transferred to the reaction flask.

(67) In another separate flask 5.75 g of MA and 6 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 36.6 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the copolymer (16.5 g). The composition was determined by proton NMR and the molecular weight was determined by GPC.

Example 12

Synthesis of Butyl Acrylate (BA), 4-Allyloxy Benzophenone and 1-Octene Terpolymer

(68) Example 8 described the synthesis of a terpolymer where the benzophenone moiety was part of the acrylate unit. Conversely, the terpolymer where the benzophenone moiety is part of the olefin (and not the acrylate) could also be prepared by a similar process where n-BA, 1-octene and 4-allyloxy benzophenone were polymerized at RT as shown below.

(69) ##STR00002##

(70) In a 500 mL 4 necked round bottom flask equipped with a stainless steel stirrer with banana shaped blade, thermometer, cold finger condenser, nitrogen inlet and a cold finger condenser containing dry ice-acetone bath were taken 171 g of toluene, 20 g 4-allyloxy benzophenone and 37.5 g of 1-octene. The reaction flask was purged with nitrogen while it was cooled using dry ice-o-xylene cooling mixture.

(71) In a separate flask 0.41 g of BPO in 17 g of butyl acrylate (BA) was dissolved and transferred to the reaction flask.

(72) In another separate flask 4 g of BA and 4 g toluene were taken in a 100 mL 1 necked round bottom flask. Nitrogen was purged through the flask while it was cooled using an ice bath. 18.3 mL of 25 wt % toluene solution of ethyl aluminum dichloride was added to this flask drop wise with occasional swirling. After about 5 minutes, the solution containing the precomplex was transferred to the main reaction flask using a syringe. The mixture was stirred at 40 C. for 8 h and at RT overnight. Next day, the reaction was quenched using 20 g of isopropanol. The mixture was transferred to a separatory funnel, washed several times with water, and dried over anhydrous sodium sulfate. After filtering the solvent was evaporated using rotovap to give the crude terpolymer. The crude terpolymer was purified by precipitating it from methanol. Purified terpolymer (27 g) was obtained. The molecular weight was determined by GPC. .sup.1H NMR analysis of the terpolymer after purification clearly showed the incorporation of 5 mol % of benzophenone. Absence of allylic protons in the NMR confirmed that the benzophenone moiety was polymer bound.