ELECTROMAGNETIC DEVICE HAVING LAYERED MAGNETIC MATERIAL COMPONENTS AND METHODS FOR MAKING SAME

Abstract

A micro fabricated electromagnetic device and method for fabricating its component structures, the device having a layered magnetic core of a potentially unlimited number of alternating insulating and magnetic layers depending upon application, physical property and performance characteristic requirements for the device. Methods for fabricating the high performing device permit cost effective, high production rates of the device and its component structures without any degradation in device performance resulting from component layering.

Claims

1. A multilayered magnetic structure comprising: a substrate; a magnetic laminate core including a first layer of a magnetic laminate core material (core material) deposited on and operatively connected to the substrate; one or more layers of the core material sequentially deposited on the first layer and operatively connected thereto and to one another, each layer of core material further including a first layer of magnetic material and a second layer of insulating material.

2. The multilayered magnetic structure of claim 1 wherein the substrate comprises silicon.

3. The multilayered magnetic structure of claim 1 wherein the magnetic material forming the first layer of the core material comprises an alloy of cobalt, nickel and iron.

4. The multilayered magnetic structure of claim 1 wherein the insulating material forming the second layer of the core material comprises electroless iron oxide.

5. The multilayered magnetic structure of claim 4 wherein the electroless iron oxide comprises hematite (Fe.sub.2O.sub.3) or magnetite (Fe.sub.3O.sub.4).

6. The multilayered magnetic structure of claim 1 wherein each layer of insulating material is of a preselected thickness in the range of approximately 0.05 m to approximately 0.5 m.

7. The multilayered magnetic structure of claim 1 wherein each layer of insulating material is of a thickness of approximately 0.1 m.

8. The multilayered magnetic structure of claim 1 further including a cobalt layer having a preselected thickness disposed intermediate one or more of the magnetic laminate core material layers.

9. The multilayered magnetic material of claim 8 wherein the thickness of the cobalt layer is approximately 0.5 m or less.

10. The multilayered magnetic structure of claim 8 wherein the cobalt layer is disposed intermediate the one or more layers of the magnetic laminate core material at every fifth layer interval.

11. The multilayered magnetic structure of claim 8 wherein the cobalt layer is disposed intermediate the one or more layers of the magnetic laminate core material at every tenth layer interval.

12. The multilayered structure of claim 3 wherein the alloy comprises cobalt in a range of approximately 25% to approximately 45%, nickel in a range of approximately 45% to approximately 65%, and iron in a range of approximately 1% to approximately 18%.

13. The multilayered magnetic structure of claim 12 wherein the magnetic laminate core includes from approximately 150 to approximately 200 layers of core material.

14. The multilayered magnetic structure of claim 13 wherein the magnetic laminate core has a thickness of approximately 250 m.

15. In a transformer for powering an integrated circuit system, the transformer having large magnetizing inductance, low parasitic inductance and high current and voltage operating characteristics, the improvement comprising: a coil having first and second arm portions; a continuous closed loop laminated magnetic core, the magnetic core being wrapped around and tightly coupled to each of the first and second arms of the coil, the laminated magnetic core having a substrate; a first layer of a magnetic laminate core material (core material) deposited on and operatively connected to the substrate; one or more layers of the core material sequentially deposited on the first layer and operatively connected thereto and to one another, each layer of core material further including a first layer of magnetic material and a second layer of insulating material.

16. The transformer of claim 15 wherein the coil includes a plurality of planar primary and secondary windings coated with an organic polymer material.

17. The transformer of claim 15 wherein the magnetic material forming the first layer of the core material comprises and alloy of cobalt, nickel and iron.

18. The transformer of claim 17 wherein the insulating material forming the second layer of the core material comprises electroless iron oxide.

19. The transformer of claim 17 wherein the alloy comprises cobalt in a range of approximately 25% to approximately 45%, nickel in a range of approximately 45% to approximately 65%, and iron in a range of approximately 1% to approximately 18%.

20. The transformer of claim 18 wherein the electroless iron oxide comprises hematite (Fe.sub.2O.sub.3) or magnetite (Fe.sub.3O.sub.4).

21. A method for manufacturing a multilayered magnetic structure having one or more layers of a magnetic core material, the core material having a presented thickness and physical properties, the method comprising the steps of: 1). fabricating an insulating layer comprising an electroless iron oxide on a substrate employing the steps of: a. filling a vessel suitable for performing a plating deposition process with approximately 400 mL of deionized (DI) water forming a water bath; b. heating the water to approximately 50 C. with gentle stirring with a mechanical stirrer while monitoring the water temperature; c. immersing a surface area of the substrate to be layered with the electroless iron oxide in the water bath; d. initiating a deposition reaction in response to the temperature being monitored in step b reaching a temperature of approximately 43 C., by adding approximately 0.20 g FeC12.4H2O (ferrous chloride tetrahydrate, formula weight (FW)=198.81 g/mol) to make approximately a 0.0025 M (2.5 mM) solution. e. increasing the stirring rate so that the solution is stirring vigorously; f. allowing the substrate to sit for approximately 10 minutes in the ferrous chloride solution for a maximum time period of 20 minutes, whereby ferrous ions (Fe.sup.2+) are adsorbed onto the surface are of the substrate (absorption period); g. adding approximately 26 mL of 0.1 N KOH solution to the bath at the end of the adsorption period. h. verifying that the final pH of the bath is between approximately 6 and 7 and adjusting it as required; i. retrieving the substrate from the bath and washing it gently and thoroughly with DI water; 2) fabricating a CoNiFe magnetic layer of the multilayered magnetic structure employing the steps of: a. preparing a CoNiFe bath solution in vessel suitable for carrying out a galvanostatic plating process (constant current) at room temperature and pressure comprising the following: 1) CoSO.sub.4-7H.sub.2O at a concentration range of approximately 0.015 M to approximately 0.05 M; 2) NiSO.sub.4-6H.sub.2O at a concentration range of approximately 0.2 M to approximately 0.459 M; 3) NiCl.sub.2-6H.sub.2O at a concentration range of approximately 0.081 M; 4) FeSO.sub.4-7H.sub.2O at a concentration range of 0.01 M to approximately 0.05M; 5) H.sub.3BO.sub.3 at a concentration range of approximately 0.136 M to approximately 0.4 M; 6) H.sub.2SO.sub.4 in trace amounts; b. inserting a substrate having an insulating layer formed thereon into the bath solution; c. initiating the plating process at a current density of approximately 7 mA/cm.sup.2 to approximately 10 mA/cm.sup.2 until a plating layer having a thickness in a range of approximately 1 m to approximately 5 m is deposited on the substrate; and 3) sequentially repeating steps 1 and 2 until a multilayered magnetic structure having the preselected thickness and properties is formed.

22. The method of claim 21 further including the steps of forming a thin cobalt layer intermediate at least one insulating layer and at least one CoNiFe magnetic layer at preselected intervals between the layers of magnetic core material using a plating bath having the following components: a. CoCl.sub.2-6H.sub.2O at a concentration of approximately 0.19 M; b. CoSO.sub.4-7H.sub.2O at a concentration of approximately 1.17 M; c. H.sub.3BO.sub.3 at a concentration of approximately 0.49 M; and d. NaCl at a concentration of approximately 0.29 M.

23. The method of claim 22 wherein the preselected intervals between the layers of magnetic core material comprise every fifth layer of magnetic core material.

24. The method of claim 22 wherein the preselected intervals between the layers of magnetic core material comprise every tenth layer of magnetic core material.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0017] FIG. 1 is a perspective view of a micro fabricated electromagnetic transformer device having a layered magnetic laminate core;

[0018] FIG. 2 is a cross-sectional view of the micro fabricated electromagnetic transformer device of FIG. 1 showing the elements thereof in greater detail;

[0019] FIG. 3 is a cross-sectional view of a segment of the micro fabricated electromagnetic device of FIGS. 1 and 2 having a portion enlarged to better illustrate the elements thereof;

[0020] FIG. 3.A is an enlarged cross-sectional view of the segment of the micro fabricated electromagnetic transformer device of FIG. 3;

[0021] FIG. 4 is a cross-sectional electron micrograph of a 100 layer, 200 m thick plated test wafer of a layered magnetic material in accordance with an embodiment;

[0022] FIG. 5.A. shows graphically magnetic density vs. applied magnetic field in a single-layered structure of magnetic materials of in accordance with the composition of an embodiment to demonstrate the ability to control magnetic properties of the material via material composition;

[0023] FIG. 5.B. shows graphically magnetic density vs. applied magnetic field in an eleven-layered structure of a magnetic material in accordance with an embodiment to demonstrate the ability to control magnetic properties of the material via layering;

[0024] FIG. 6 is a graph of the mass gain as a function of the number of layers on the plated test wafer of FIG. 3;

[0025] FIG. 7 is a graph of the differential mass gain as a function of the number of layers on the plated test wafer of FIG. 3;

[0026] FIG. 8 is a graph of the material composition by layer as a function of the number of layers on the plated test wafer of FIG. 3 showing the consistency of layering composition deposited in accordance with the methods of the present invention;

[0027] FIG. 9 is a graph of inductance as a function of frequency in a primary coil of a transformer having a 50-layer core showing the effectiveness of layering on the physical properties of the material;

[0028] FIG. 10 is a graph of the data shown in FIG. 9 normalized to more clearly illustrate the effects of layering on the physical properties of the material;

[0029] FIG. 11 is a photomicrograph of a cross section of a prior art layered magnetic material showing the adverse effect of Ni content on the growth of successive layers in the structure;

[0030] FIG. 11.A is an enlarged photomicrograph of a portion of the cross section of a prior art layered magnetic material of FIG. 11;

[0031] FIG. 12 is a photomicrograph of a cross section of a layered magnetic material illustrating the positive effect of the electrodeposition of a thin layer of Co on the growth of successive layers in the structure; and

[0032] FIG. 13 is a flow chart of a process for manufacturing an insulating layer of a layered magnetic material in accordance with an embodiment.

DESCRIPTION OF THE INVENTION

[0033] It should be noted that the present description is by way of illustration only, and that the concepts and examples presented herein are not limited to use or application with any single layered magnetic material and manufacturing process. Hence, while the details of the layered magnetic material and process for the making thereof described herein are for the convenience of illustration and explanation with respect to the exemplary embodiments, the principles disclosed may be applied to other types of layered magnetic materials and associated manufacturing processes without departing from the scope of the present invention.

[0034] Referring now to FIG. 1, a unique micro fabricated electromagnetic transformer device in accordance with the present invention is illustrated generally at 10. The device is designed to address demanding application requirements and includes a copper coil 12 having arms 13, each arm being wrapped around with and tightly coupled to a compact and continuous, closed-loop laminated magnetic core 20, thus creating a monolithic integration of the coil and core. Tight coupling, as that term is used in the art, refers generally to the amount of flux created in an alternating magnetic field in a transformer coil that is received by the receiving coil. The greater the amount of flux that is received by the receiving coil, the tighter the coils are coupled; thereby reducing heating and enhancing efficiency.

[0035] As shown in greater detail in FIG. 2, the copper coil 10 includes a plurality of planar copper primary and secondary windings 14 (further designated for ease of identification by P for Primary and S for Secondary windings of the transformer respectively) in a thickness range of approximately 50 m to approximately 450 m and coated with an organic isolation coating material layer 16, for example, Parylene. The windings are separated by layers of silicon 18 positioned intermediate the windings and further include a plurality of out-of-plane copper crossovers, each of which, by way of example and not of limitation, are approximately 50 m thick that are not visible in the drawings.

[0036] Referring to FIGS. 3, and 3.A., a portion of the continuous, closed-loop laminated magnetic core 20 is depicted in greater detail. The laminated core includes a silicon microbeam 24 which is covered with a seed layer or substrate 26 of suitable dielectric material such as Parylene as noted above or other vapor deposited polymers suitable for the application. The magnetic core further includes a micro fabricated laminated multilayered magnetic structure 30 formed of a first core layer of cobalt-nickel-iron (CoNiFe) alloy magnetic material and an iron oxide insulating material or layer deposited on and operatively connected to the seed layer. Thereafter, alternating layers of CoNiFe alloy material and iron-oxide insulating material sequentially are deposited on and operatively connected to one another until a magnetic core of a desired thickness and having properties suitable for an intended application is formed. The overall thickness of the laminate having approximately 150 to 200 layers of material is on the order of approximately 250 m; although, laminates of fewer or more numbers of layers of laminate core materials in varying thicknesses may be used, depending upon the needs of a specific application, without departing from the scope of the present invention.

[0037] An enlarged cross-sectional electron micrograph of the microstructure of one segment of the laminated multilayered magnetic structure 30 is shown magnified in FIG. 4 to better illustrate the structure's individual layers. As discussed above, these layers comprise alternating layers of a magnetic material such as a cobalt-nickel-iron alloy and an insulating material such as ferrite (a solid solution of carbon in -Fe having a body-centered cubic (BCC) crystal structure), hematite (Fe.sub.2O.sub.3) or magnetite (Fe.sub.3O.sub.4). The specifics of these materials will be discussed in greater detail below.

[0038] A particular advantage of the layered magnetic material of the present invention and the associated manufacturing method is the ability to control the magnetic properties of the material. FIGS. 5.A and 5.B. are both magnetization curves along multiple N-S and E-W magnetic poles, which show the effects of and layering of a CoNiFe alloy formed in accordance with the composition changes herein disclosed on saturation and coercivity. Saturation is a term used to describe the magnetization state of a material when an increase in an applied external magnetic field cannot further increase the magnetization of the material. This property is illustrated in the upper right and lower left portions of the curves in both FIGS. 5.A. (one layer) and 5.B. (11 ferrite layers), where the magnetization density levels off to a relatively constant value, even though strength of the applied field in either direction shown along the horizontal axis increases steadily from the zero point. The material is magnetically saturated at these points.

[0039] Coercivity is a measure of the strength of an applied magnetic field needed to reduce the magnetization of a particular material to zero after it is saturated. An interrelated parameter, magnetic permeability, is the ability of a material to support a magnetic field within itself, pure iron (Fe), by way of example, having a higher permeability than air. Materials with high coercivity are known as magnetically hard materials, and materials with low coercivity are said to be magnetically soft materials.

[0040] Soft materials are used in electrical power transformers and inductor cores and, accordingly, are important materials for efforts to miniaturize power supplies and transformers for microchip applications, as noted above. However, heretofore, problems associated with layering of thin film magnetic materials have limited efforts to downsize these electronic components for semiconductor applications to approximately 10 to 20 layers as a result of progressive deterioration of magnetic properties and device performance as the number of layers increases.

[0041] Referring again to FIG. 4, the photomicrograph of the microstructure of a laminated multilayered magnetic structure 30 of the present invention which overcomes the aforementioned problems is illustrated at 700 magnification to show the sequential interrelationship and positioning of the layers thereof. The structure shown is a 100 layer, 200 m plating wafer consisting of ring test structures or layers at approximately 0.08 gm/layer. This structure comprises a number of layers well above the number of layers found in prior art devices and demonstrates the robust layering capabilities of the novel layering material and manufacturing process of the present invention.

[0042] The laminated multilayered magnetic structure 30 comprises a substrate 40, which in the embodiment shown is silicon; however, as discussed above, it is to be understood that other substrate materials may be used without departing from the scope of the present invention. One or more layers 42 of the multilayered magnetic structure 30 forming magnetic laminate core 20 (FIGS. 1 and 2) are sequentially deposited on the substrate, the first of these layers being operatively connected to it via chemically bonding as a result of the plating manufacturing process, as will be described in greater detail below. Each core layer 42 further includes a first layer of magnetic material 44 and a second layer of insulating material 46. By way of example and not of limitation, each first layer of magnetic material may be formed of a cobalt-nickel-iron (CoNiFe) alloy having an exemplary composition of cobalt in a range of approximately 25% to approximately 45%, nickel in a range of approximately 45% to approximately 65%, and iron in a range of approximately 1% to approximately 18%. The second layer 46 of insulating material comprising the core may be an electroless iron oxide or ferrite, for example, hematite (Fe.sub.2O.sub.3) or magnetite (Fe.sub.3O.sub.4), both naturally occurring magnetic materials of the spinel group. While other insulating materials suitable for the application may also be used, such a goethite (SeOOH), cobalt ferrites, or cobalt nickel ferrites, without departing from the scope hereof, magnetite is a preferred material, inasmuch as it possesses the highest exchange coupling properties, i.e., the exchange of magnetic flux (not electrons) between adjacent material layers. As will be discussed in greater detail below, magnetite may also be applied or deposited in extremely thin layers, thus further enhancing the exchange coupling between layers.

[0043] Referring now to FIGS. 6 and 7, mass gain and the differential mass gain test data respectively are shown graphically as a function of layering. FIG. 6 displays the relatively uniform mass gain test data for platings around a cantilever test structure manufactured in accordance with the present invention as a function of the number of CoNiFe layers deposited. FIG. 7 illustrates uniform differential mass gain data as a function of the number of CoNiFe layers deposited on a test ring wafer. Using the novel materials and manufacturing methodology herein disclosed, no limits on the number of possible layers have been encountered, and laminates of CoNiFe/iron oxide (electroless ferrite) with high relative permeability (greater than 300 H/m) in 100 m thick laminations have been produced. Moreover, unlike the insulating layers in prior art structure which are relatively thick, on the order of magnitude of 10 to 100 m, to keep the insulation between alternating conductive layers robust, the insulating layers in the layered material of the present invention are in a range of approximately 0.05 to approximately 0.5 m and preferably approximately 0.1 m thick. The novel layering structure of the present invention minimizes the potential of electrical shorting between the layers and contributes to the overall permeability of the laminate, enhances exchange coupling between the materials, and reduces loss of inductance at higher switching frequencies via eddy current loss and other effects which have a significant negative impact upon the performance of prior art devices.

[0044] FIGS. 8, 9 and 10 show the effectiveness of the layering process of the present invention. It may be seen from FIG. 8 that the relative composition by layer of the key elements remains constant over at least fifty layers and no limits on the number of layers appear to exist. This effectiveness is further demonstrated in a comparison of the performance of a multilayered material as a function of frequency of a 5:1 transformer having fifty layers as shown graphically in FIG. 9 and normalized as shown graphically in FIG. 10.

[0045] It has been found that pure nickel forms a passivating oxide layer on its surface, which inhibits the formation of magnetite thereon. This phenomenon is illustrated in FIGS. 11 and 11.A, which is a rendering of a photomicrograph of a cross section of a prior art layered magnetic material core 50 showing the adverse effect of Ni content on the growth of the magnetite insulation layers 52 on the inert nickel surfaces of the magnetic layers 54. To overcome this problem, a very thin layer of cobalt is deposited intermediate the one or more core layers 50 at preselected layer intervals. As noted above with respect to the insulating material layers, in the same manner, the cobalt material should be layered as thinly as possible, approximately 0.5 m or less. For example, in the embodiment of FIG. 12, a very thin cobalt layer 56 is shown positioned intermediate the magnetic laminate core layers 20 to produce a non-inert layer that facilitates the iron oxide deposition and successive layering. It has been shown that depositing a cobalt layer at every fifth magnetic core layer interval is effective in overcoming this problem. Moreover, it has been observed that depending upon the number of core layers and resulting thickness of the final overall structure of the microelectronic device, positioning a cobalt layer at every tenth magnetic core layer interval provides satisfactory magnetite bonding.

Ferrite/Magnetite Insulating Layer Forming Process

[0046] Referring now to FIG. 13, a process flow chart is shown which describes the steps of manufacturing the insulating or ferritic layer of the multilayered magnetic structure of the present invention. As noted above, which various insulating materials are available for the instant application, electroless iron oxide or ferritic materials, preferable magnetite are preferred due to their height exchange coupling properties. This process protocol is the base procedure for plating in a medium-sized water bath in which all volumes and masses disclosed should be adhered to as accurately as possible. The process variables and parameters may be scaled up or down according to the requirements of a specific application.

[0047] 1. Equip a glass water bath with a mechanical stirrer.

[0048] 2. Fill water bath with approximately 400 mL of deionized (DI) water, and heat it to approximately 50 C. with gentle stirring with the mechanical stirrer.

[0049] 3. Suspend the area of a substrate material to be coated in the water bath. Immerse the material in the water if water level is not high enough to cover desired area.

[0050] 4. Once temperature has reached approximately 43 C., initiate the reaction by adding approximately 0.20 g FeCl.sub.2.4H.sub.2O (ferrous chloride tetrahydrate, formula weight (FW)=198.81 g/mol) to make approximately a 0.0025 M (2.5 mM) solution.

[0051] 5. Increase the stirring rate so that the solution is stirring vigorously, and let the sample sit for approximately 10 minutes in the ferrous chloride solution. This is the critical phase in which ferrous ions (Fe.sup.2+) are adsorbed onto the surface of the substrate. This adsorption period can be extended to a maximum of 20 minutes as needed to complete the formation of the layer.

[0052] 6. At the end of the adsorption period, add approximately 26 mL of 0.1 N KOH solution. This is 2.5 equivalents of KOH relative to the moles of ferrous chloride added. It is critical to add an amount of KOH commensurate with the amount of ferrous chloride added according to the following formula:

[00001]$\begin{array}{cc}\mathrm{Volume}.Math..Math.\mathrm{KOH}.Math..Math.\left(\mathrm{mL}\right)=\mathrm{mass}.Math..Math.{\mathrm{FeCl}}_2.Math.4.Math.H_2.Math.O\left(g\right)\frac{1.Math..Math.\mathrm{mol}}{198.81.Math..Math.g}2.5\frac{1.Math..Math.L}{0.1.Math..Math.\mathrm{mol}}\frac{1000.Math..Math.\mathrm{mL}}{L}& \left(\mathrm{eq}..Math.1\right)\end{array}$

[0053] Always round the calculated volume to be added up to the next 0.5 mL.

[0054] Add the amount of KOH slowly over about 10 seconds.

[0055] 7. At a time interval no longer that 20 minutes as measured from the time KOH was added, retrieve the substrate from the bath and wash it gently and thoroughly with DI water.

[0056] As implied in step 4, deviating from the 2.5 mM concentration for ferrous chloride is acceptable, but it is vital that the volume of KOH solution be calculated using the actual mass of ferrous chloride added and the actual concentration of KOH, if it is not 0.1 M. The general formula is:

[00002]$\begin{array}{cc}\mathrm{Volume}.Math..Math.\mathrm{KOH}.Math..Math.\left(\mathrm{mL}\right)=\frac{\mathrm{mass}.Math..Math.{\mathrm{FeCl}}_2.Math.4.Math.H_2.Math.O\left(g\right)2.51000.Math..Math.\mathrm{mL}.Math.\text{/}.Math.L}{198.81.Math..Math.g.Math.\text{/}.Math.\mathrm{mol}\left[\mathrm{KOH}\right]},& \left(\mathrm{eq}..Math.2\right)\end{array}$

[0057] where [KOH] is the concentration of KOH in molarity units (moles solute/liters of solvent).

[0058] 8. Endpoint Verification: The final pH of the solution should be between 6 and 7, inclusive. This can be verified with a pH strip. The solution should also contain brown magnetite particulates that settle slowly and that respond to a magnet. If the final pH is less than 6, then add approximately 1 extra mL of KOH in order to correct for errors in mass or concentration.

Magnetic Laminate Core Layer Fabrication Process

[0059] The CoNiFe alloy layer is then deposited on the surface of the magnetite layer using conventional metal deposition techniques such as electroplating, thereby forming a magnetic laminate core layer. The process is repeated sequentially in alternating layering steps, inserting a thin cobalt layer at a preselected interval intermediate successive core layers as described above, until a multilayered magnetic structure having the desired number of layers and thickness is attained. The process protocol for the fabrication of the CoNiFe layers of the multilayered magnetic structure of the present invention is as follows:

[0060] 1. Prepare a CoNiFe bath solution in vessel suitable for carrying out a galvanostatic plating process (constant current) at room temperature and pressure of the following: [0061] a. CoSO.sub.4-7H.sub.2O at a concentration range of approximately 0.015 M to approximately 0.05 M; [0062] b. NiSO.sub.4-6H.sub.2O at a concentration range of approximately 0.2 M to approximately 0.459 M; [0063] c. NiCl.sub.2-6H.sub.2O at a concentration range of approximately 0.081 M; [0064] d. FeSO.sub.4-7H.sub.2O at a concentration range of 0.01 M to approximately 0.05M; [0065] e. H.sub.3BO.sub.3 at a concentration range of approximately 0.136 M to approximately 0.4 M; [0066] f. H.sub.2SO.sub.4 in trace amounts; and [0067] g. Thiourea (SC(NH.sub.2).sub.2 at a concentration of approximately 50 mg/l. [0068] h. Optionally, Saccharin at a concentration range of approximately 0.91 g/l to approximately 1.83 g/l.

[0069] 2. Insert a substrate material into the bath solution (a seed layer such a Parylene or Si or a ferritic (magnetite) insulating layer fabricated in accordance with the methods of the present invention).

[0070] 3. Initiate the plating process at a current density of approximately 7 mA/cm.sup.2 to approximately 10 mA/cm.sup.2 until a plating layer having a thickness in a range of approximately 1 m to approximately 5 m is deposited.

[0071] A thin cobalt layer may be deposited optionally on every fifth to tenth magnetic laminate core layer using a plating bath having the following components: [0072] a. CoCl.sub.2-6H.sub.2O at a concentration of approximately 0.19 M; [0073] b. CoSO.sub.4-7H.sub.2O at a concentration of approximately 1.17 M; [0074] c. H.sub.3BO.sub.3 at a concentration of approximately 0.49 M; and [0075] d. NaCl at a concentration of approximately 0.29 M.

[0076] Other optional additives to the CoNiFe bath solution in minimal trace amounts include sodium lauryl sulfate, ammonium chloride, glycerol, iron oxide, MSG.

Micro Fabricated Electromagnetic Device Fabrication Process

[0077] The process flow sequence for the fabrication of a micro functional electromagnetic device in accordance with the present invention is set forth below. By way of example and not of limitation, the process is described with respect to the fabrication of a micro fabricated electromagnetic transformer as shown in FIGS. 1-3; however, the features of the methods and structures herein disclosed may be applied to the fabrication of other types of microelectronic devices for application on semiconductor wafers without departing from the scope of the present invention.

[0078] 1. Form a copper coil 12 based upon planar copper windings.

[0079] 2. Form a crossover wire structure.

[0080] 3. Form apertures and gaps adapted to receive a magnetic core in the copper coil by Si deep reactive ion etching (DRIE).

[0081] 4. Remove the inter-wafer areas via wet and/or dry full-body etching.

[0082] 5. Deposit blanket conformal organic isolation layer, e.g., Parylene.

[0083] 6. Deposit seed layer, e.g., Si via masked full body physical vapor deposition.

[0084] 7. Deposit multilayered magnetic core structure in sequential layers as described in greater detail above.

[0085] In accordance with the foregoing fabrication process steps, a multilayered micro fabricated magnetic device, by way of example, a transformer, is provided for use in demanding applications. The device of the instant invention possesses superior physical, electrical and magnetic properties heretofore unavailable in micro multilayered electronic devices via minimizing if not eliminating the disruptive effects of eddy currents normally found in multilayered materials, such as unacceptable heat generation, disrupted magnetic fields and accompanying loss of inductance and degradation of device performance.

General Interpretation of Terms

[0086] In understanding the scope of the present invention, the term configured as used herein to describe a component, section or part of a device that is constructed to carry out the desired function. In understanding the scope of the present invention, the term comprising and its derivatives, as used herein, are intended to be open ended terms that specify the presence of the stated features, elements, components, groups, integers, and/or steps, but do not exclude the presence of other unstated features, elements, components, groups, integers and/or steps. Finally, terms of degree such as substantially, about and approximately as used herein mean a reasonable amount of deviation of the modified term such that the end result is not significantly changed. For example, these terms can be construed as including a deviation of at least 5% of the modified term if this deviation would not negate the meaning of the word it modifies.

[0087] While only selected embodiments have been chosen to illustrate the layered magnetic structure, material and manufacturing process of the present invention, it will be apparent to those skilled in the art from this disclosure that various changes and modifications can be made herein without departing from the scope of the invention as defined in the appended claims. Furthermore, the foregoing descriptions of the embodiments according to the present invention are provided for illustration only, and not for the purpose of limiting the invention as defined by the appended claims and their equivalents.