Method for producing cold-worked centrifugal cast composite tubular products

Abstract

A method of producing a seamless, composite tubular product includes centrifugally casting a metal or alloy into a tubular workpiece having an inner diameter. The method then centrifugally casts a corrosion resistant alloy in the inner diameter of the tubular workpiece to form a composite tubular workpiece having an inner diameter and an outer diameter. The inner diameter of the composite tubular workpiece is formed of the corrosion resistant alloy, and the outer diameter is formed of the metal or alloy. The method then subjects the composite tubular workpiece to at least about a 25% wall reduction at a temperature below a recrystallization temperature of the workpiece using a metal forming process. The metal forming process includes radial forging, rolling, pilgering, and/or flowforming.

Claims

1. A method of producing a seamless, composite tubular product, the method comprising: centrifugally casting a metal or alloy into a tubular workpiece having an inner diameter; centrifugally casting a corrosion resistant alloy in the inner diameter of the tubular workpiece to form a composite tubular workpiece having an inner diameter and an outer diameter, the inner diameter of the composite tubular workpiece formed of the corrosion resistant alloy and the outer diameter formed of the metal or alloy; and subjecting the composite tubular workpiece to at least about a 25% wall reduction using a metal forming process, the metal forming process comprising providing at least two rollers having a displacement from one another in an axial direction with respect to the composite tubular workpiece, and compressing the outer diameter of the composite tubular workpiece with the rollers at a temperature below a recrystallization temperature of the composite tubular workpiece using a combination of axial and radial forces so that the inner diameter of the composite tubular workpiece has a compressive hoop stress of at least 500 MPa.

2. The method of claim 1, further comprising centrifugally casting one or more metals or alloys in the inner diameter of the tubular workpiece before centrifugally casting the corrosion resistant alloy.

3. The method of claim 1, wherein the wall reduction is at least about 35% and includes at least two reductions, wherein the first reduction is at least about a 25% wall reduction.

4. The method of claim 1, wherein the wall reduction is at least about 50%.

5. The method of claim 4, wherein the at least about 50% wall reduction includes at least two reductions, wherein the first reduction is at least about a 25% wall reduction.

6. The method of claim 1, wherein the corrosion resistant alloy includes a stainless steel alloy, a titanium-based alloy, a nickel-based alloy, a cobalt-based alloy or a zirconium-based alloy.

7. The method of claim 1, further comprising removing material from the outer diameter of the composite tubular workpiece before subjecting the composite tubular workpiece to the wall reduction.

8. The method of claim 1, further comprising annealing the composite tubular workpiece after subjecting the composite tubular workpiece to the wall reduction.

9. The method of claim 8, further comprising subjecting the composite tubular workpiece to at least about a 10% wall reduction after annealing the composite tubular workpiece.

10. The method of claim 1, further comprising annealing, age hardening, and then annealing the workpiece before subjecting the composite tubular workpiece to the wall reduction.

11. The method of claim 1, further comprising forming a rifling on an inner diameter of the composite tubular workpiece.

12. The method of claim 1, further comprising removing material from the inner diameter of the tubular workpiece before centrifugally casting the corrosion resistant alloy.

13. The method of claim 1, further comprising removing material from the inner diameter of the composite tubular workpiece before subjecting the composite tubular workpiece to the wall reduction.

14. The method of claim 1, wherein the wall reduction is from about 25% to about 75%.

15. A tubular component produced according to the method of claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The foregoing features of the invention will be more readily understood by reference to the following detailed description, taken with reference to the accompanying drawings, in which:

(2) FIG. 1 shows a process of producing a seamless, composite tubular product according to embodiments of the present invention;

(3) FIG. 2 is a macrograph showing a transverse cross-sectional view of a centrifugally cast tube before cold-working according to embodiments of the present invention;

(4) FIG. 3 is a photomicrograph showing a longitudinal cross-sectional view of a centrifugally cast stainless steel tube before cold-working according to embodiments of the present invention;

(5) FIG. 4 is a photomicrograph showing a transverse cross-sectional view of a centrifugally cast stainless steel tube before cold-working according to embodiments of the present invention;

(6) FIGS. 5A and 5B are photomicrographs showing the as-cast microstructure in the interior zone and exterior zones, respectively, of the centrifugally cast tube shown in FIG. 2;

(7) FIG. 6 schematically shows an illustrative flowforming device according to embodiments of the present invention;

(8) FIG. 7 schematically shows a side-view of a workpiece undergoing a forward flowforming process according to embodiments of the present invention;

(9) FIG. 8 schematically shows a side-view of a workpiece undergoing a reverse flowforming process according to embodiments of the present invention;

(10) FIG. 9 schematically shows a perspective view of rollers according to embodiments of the present invention;

(11) FIG. 10 schematically shows a side-view of a roller configuration with a workpiece undergoing a forward flowforming process according to embodiments of the present invention;

(12) FIG. 11 shows a graph of residual hoop stress distribution for tubular components made of a superalloy material that has undergone an autofrettage process according to embodiments of the present invention;

(13) FIG. 12 is a photomicrograph showing a longitudinal cross-sectional view of a centrifugally cast stainless steel tube after flowforming according to embodiments of the present invention; and

(14) FIGS. 13A and 13B are photomicrographs showing the outer diameter and inner diameter areas, respectively, of the flowformed, centrifugally cast stainless steel tube shown in FIG. 10 at a 500 magnification.

DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

(15) Various embodiments of the present invention provide a method of producing a seamless, composite tubular product from a centrifugally cast, corrosion resistant alloy. The method entails centrifugally casting a metal or alloy, e.g., steel or corrosion resistant alloy, to form the outer layer or shell in a centrifugal casting and then using that shell as the mold for subsequently centrifugally casting a corrosion resistant alloy in order to form a composite tubular workpiece made of at least the two materials. The process then cold-works the composite tubular workpiece with at least about a 25% wall reduction using a metal forming process, such as flowforming, in order to bond or clad the two or more layers together when forming the workpiece into the desired length, thickness, and/or shape. Other metal forming processes may also be used such as radial forging, rolling and/or pilgering. Preferably, the metal forming process includes a series of smaller and smaller reductions. Typically, in wrought material like billets or extrusions, if smaller incremental flowforming passes are used, the material near the outer diameter of the component is subjected to enough deformation that the material plastically deforms, but the inner diameter does not sufficiently plastically deform. This unacceptably leads to the material ripping apart. Surprisingly, it was found that in centrifugally cast corrosion resistant alloys a series of smaller incremental passes may be used and allows the large radially-oriented grain structure to be realigned along the longitudinal direction. This may be due, in part, to the different grain structures present in the inner and outer diameter of a centrifugally cast component. When at least a 25% wall reduction is used, both the outer and inner diameters of the workpiece plastically deforms sufficiently enough. After this initial first reduction, smaller incremental reductions may also be used. Thus, embodiments allow the centrifugally cast composite workpiece to be formed into a high strength, composite corrosion resistant component without having to undergo a series of hot work and cold work tube reductions. Details of illustrative embodiments are discussed below.

(16) FIG. 1 shows a process of producing a seamless, composite tubular product according to embodiments of the present invention. The process begins at step 100, in which a metal or alloy is centrifugally cast into a tubular workpiece in order to form the mold for another centrifugal casting. For example, any metal or alloy that is able to be centrifugally cast may be used for the outer layer or mold, such as steel or another corrosion resistant alloy. In step 110, a corrosion resistant alloy is centrifugally cast in an inner diameter of the tubular workpiece in order to form a composite tubular workpiece. Preferably, the second centrifugal casting is formed within the inner diameter of the first centrifugal casting in such a way so as to reduce or eliminate the formation of any intermetallic layer between the two castings. Appropriate methods to reduce or eliminate the formation of any intermetallic layers are known in the art, e.g., U.S. Pat. No. 5,558,150, which is incorporated by reference herein in its entirety. One or more other metals or alloys may also be centrifugally cast in the inner diameter of the tubular workpiece before centrifugally casting the corrosion resistant alloy in order to form a multilayer composite tubular workpiece. The corrosion resistant alloy may include a stainless steel alloy, a titanium-based alloy, a nickel-based alloy, and/or a zirconium-based alloy (e.g., alloys such as alloy 28, 316, 625, 718, 825, 925, G-3, 050, C-276, 22Cr, 25Cr, Duplex stainless steel, Nitronic stainless steel, Nickel 200, Monel 400 and Inconel 600). Corrosion resistant alloys may be used in a variety of different applications. Thus, this listing of specific alloys is merely intended to be illustrative of suitable materials for use in embodiments of the invention.

(17) The centrifugal casting process may use a variety of parameters (e.g., rotation speed, cooling rate, etc.) depending upon the materials used and the dimensions of the part produced. For example, a 316 stainless steel material may be formed having a one-inch thick sidewall. As mentioned above, a centrifugally cast tubular workpiece before cold working typically includes three basic solidification zones, such as shown in FIG. 2. As shown, the exterior zone consists of a fine, equiaxed grain structure near the outer diameter of the workpiece, the columnar zone consists of columnar grains oriented parallel to the radial direction, and the interior zone consists of a coarse, equiaxed grain structure. FIGS. 3 and 4 are photomicrographs showing a longitudinal and transverse cross-sectional view, respectively, of a centrifugally cast 316 stainless steel tube before cold working showing the radially-oriented, large columnar grain structure. In the composite tubular workpiece, both the outer layer formed of the metal or alloy and the inner layer formed of the corrosion resistant alloy may each include the three solidification zones.

(18) For heat treatable or age hardenable materials, such as 410 stainless steel or 718 Inconel, an optional heat treatment may be used on the workpiece after the two centrifugal casting processes. For example, the workpiece may be age hardened and annealed one or more times. The phase transformations from the heat treatment cycle may help reduce the large, columnar grains in the centrifugal casting before any subsequent metal forming process is used. The heat treatments may include an annealing, age hardening and annealing treatment in order to break up and somewhat refine the cast grain structure.

(19) In a centrifugally cast composite tubular workpiece, the interior zone usually has limited ductility compared to the rest of the workpiece due, in part, to higher porosity present in this zone. For example, FIGS. 5A and 5B are photomicrographs showing the as-cast microstructure in the interior zone and exterior zones, respectively. As shown, a higher pore volume fraction is present in the interior zone than the exterior zone. One of the basic causes for porosity in metals and alloys is gas evolution during solidification. In centrifugal casting, when the molten material is poured into the rotating mold, bubbles of gas may form in the material. As these bubbles have a low density, they are subjected to a lower centrifugal force than the melt, and will tend to collect in the interior zone on the inner diameter of the centrifugally cast component. The heterogeneity of ductility between the three zones introduces a risk factor during the subsequent processing stages. Therefore, the amount of deformation each zone is subjected to needs to be considered when designing the processing stages to maintain uniform quality in the final product along the width of the tube.

(20) Returning to the process of FIG. 1, the composite tubular workpiece is subjected to at least a 25% wall reduction at a temperature below the recrystallization temperature of the composite tubular workpiece using a metal forming process in step 120. Optionally, material may be removed from the inner diameter of the composite tubular workpiece by any known removal process, such as machining or honing. Although the remaining discussion will be in the context of using flowforming as the metal forming process, discussion of flowforming is illustrative and not intended to limit the scope of various embodiments. Accordingly, metal forming processes may include other metal forming processes that apply compressive forces to reduce an inner and outer diameter of a tubular workpiece in order to obtain a reduction in the wall thickness of the component, such as rolling, radial forging and pilgering.

(21) Flowforming is a metal forming process used to produce precise, thin wall, cylindrical components. Flowforming is typically performed by compressing the outer diameter of a cylindrical workpiece over an inner, rotating mandrel using a combination of axial, radial and tangential forces from two or more rollers. The material is compressed above its yield strength, causing plastic deformation of the material. As a result, the outer diameter and the wall thickness of the workpiece are decreased, while its length is increased, until the desired geometry of the component is achieved. Flowforming is a cold-forming process. Although adiabatic heat is generated from the plastic deformation, the workpiece, mandrel and rollers are typically flooded with a refrigerated coolant to dissipate the heat. This ensures that the material is worked well below its recrystalization temperature. Being a cold-forming process, flowforming increases the material's strength and hardness, textures the material, and often achieves mechanical properties and dimensional accuracies that are far closer to requirements than any warm or hot forming manufacturing process known to the inventor.

(22) Two examples of flowforming methods are forward flowforming and reverse flowforming. Generally, forward flowforming is useful for forming tubes or components having at least one closed or semi-closed end (e.g., a closed cylinder). Reverse flowforming is generally useful for forming tubes or components that have two open ends (e.g., a cylinder having two open ends). In some cases, a combination of forward and reverse flowforming may be utilized to successfully achieve the desired geometry. Typically, forward flowforming and reverse flowforming may be performed on the same flowforming machine by changing the necessary tooling.

(23) FIG. 6 schematically shows an illustrative flowforming device 10 according to some embodiments of the present invention. In this case, the flowforming device 10 is configured for forward flowforming. The flowforming device 10 includes a mandrel 12 for holding a cylindrical workpiece 18, a tailstock 14 that secures the workpiece 18 to the mandrel 12, two or more rollers 16 for applying force to the outer surface of the workpiece 18, and a movable carriage 19 coupled to the rollers 16. As shown in FIG. 6, the rollers 16 may be angularly equidistant from each other relative to the center axis of the workpiece 18. The rollers 16 may be hydraulically-driven and CNC-controlled.

(24) FIG. 7 shows a side-view of a workpiece 18 undergoing a forward flowforming process. During this process, the workpiece 18 may be placed over the mandrel 12 with its closed or semi-closed end toward the end of the mandrel 12 (to the right side of the mandrel, as shown in FIG. 6). The workpiece 18 may be secured against the end of the mandrel 18 by the tailstock 14, e.g., by means of a hydraulic force from the tailstock 14. The mandrel 12 and workpiece 18 may then rotate about an axis 20 while rollers 16 are moved into a position of contact with the outer surface of the workpiece 18 at a desired location along its length. The headstock 34 rotates or drives the mandrel 12 and the tailstock 14 provides additional help to rotate the mandrel 12, so that the long mandrel 12 spins properly.

(25) The carriage 19 may then move the rollers 16 along the workpiece 18 (traveling from right to left, as shown in FIG. 6), generally in direction 24. The rollers 16 may apply one or more forces to the outside surface of the workpiece 18 to reduce its wall thickness 26 and its outer diameter, e.g., using a combination of controlled radial, axial and tangential forces. One or two jets 36 may be used to spray coolant on the rollers 16, workpiece 18 and mandrel 12, although more jets may be used to dissipate the adiabatic heat generated when the workpiece 18 undergoes large amounts of plastic deformation. The mandrel 12 may even be submersed in coolant (not shown), e.g., in a trough type device, so that the coolant collects and pools on the mandrel 12 to keep the workpiece 18 cool.

(26) Rollers 16 may compress the outer surface of the workpiece 18 with enough force that the material is plastically deformed and moves or flows in direction 22, generally parallel to axis 20. Rollers 16 may be positioned at any desired distance from the outer diameter of mandrel 12 or the inner wall of workpiece 18, to produce a wall thickness 26 that may be constant along the length of the workpiece 18 or varied, as shown in FIG. 7. Length 28 represents the portion of the workpiece 18 that has undergone the flowforming process, whereas length 30 is the portion that has yet to be deformed. This process is termed forward flowforming because the deformed material flows in the same direction 22 as the direction 24 that the rollers are moving.

(27) In reverse flowforming, a flowforming device may be configured in a similar manner to that shown in FIG. 6, but a drive ring 32, rather than the tailstock 14, secures the workpiece 18 to the mandrel 12. As shown in FIG. 6, the drive ring 32 is located near the headstock 34 at the other end of the mandrel 12. FIG. 8 shows a side-view of a workpiece undergoing a reverse flowforming process. During this process, the workpiece 18 may be placed on the mandrel 12 and pushed all the way against the drive ring 32 at one end of the mandrel 12 (to the left side, as shown in FIG. 6). Rollers 16 may be moved into a position of contact with the outer surface of the workpiece 18 at a desired location along its length. The carriage 19 may then move towards the drive ring 32 (in a right to left direction, as shown in FIG. 6) applying a force to the workpiece 18. The force may push the workpiece 18 into the drive ring 32 where it may be entrapped or secured by a series of serrations or other securing means on the face of the drive ring 32. This allows the mandrel 12 and the workpiece 18 to rotate about an axis 20 while rollers 16 may apply one or more forces to the outer surface of the workpiece 18. The material is plastically deformed and moves or flows in direction 23, generally parallel to axis 20. Similar to forward flowforming, rollers 16 may be positioned at any desired distance from the outer diameter of mandrel 12 or the inner wall of workpiece 18, to produce a wall thickness 26 that may be constant or varied along the length of the workpiece 18. Length 28 represents the portion of the workpiece 18 that has undergone the flowforming process whereas length 30 is the portion that has yet to be deformed. As the workpiece 18 is processed, it extends down the length of the mandrel 12 away from drive ring 32. This process is termed reverse flowforming because the deformed material flows in the direction 22 opposite to the direction 24 that the rollers are moving.

(28) In addition to flowforming parts over a smooth mandrel to create a smooth inner diameter of the flowformed tube, splines or rifling may be formed into the bore of a flowformed tube. This may be accomplished by having the outer surface of the mandrel 12 constructed in such a way as to impart rifling, grooves, notches, or other configurations to the inner surface of the workpiece as it is flowformed. For example, the mandrel may be constructed with spiral, straight, periodic, or other desired ridges on its surface. These ridges leave the rifling, grooves, notches and/or other configurations in the inner surface of the workpiece after the final flowforming pass is completed. Alternatively, rifling and/or other configurations may be imparted to the inner surface of the workpiece by, for example, appropriate machining of the inner surface of the workpiece after the flowforming process is completed.

(29) When the material is plastically deformed and trapped/compressed onto the hard mandrel under the set of rotating rollers, large wall reductions may be realized at one time. In centrifugally cast corrosion resistant alloys, if less than a 20% wall reduction is used per flowform pass, the outermost part of the workpiece may be plastically deformed, but the material closest to the inner mandrel may not have enough plastic deformation and the material may catastrophically tear apart during processing. However, if too large of wall reductions are used in one pass (e.g., greater than 75%, or maybe even as low as 65%), the workpiece may not be able to be acceptably processed. The flowforming process is unable to substantially move the material and the inner diameter develops a roughened texture. Therefore, it was discovered that a certain amount of wall reduction was needed on the first pass with smaller reductions used after the first pass, if necessary. When at least a 25% wall reduction is used, both the outer and inner diameters of the workpiece plastically deforms sufficiently enough. The flowforming process homogenously refines the grains' size, and realigns the microstructure, relatively uniformly, in the longitudinal direction, parallel to the center line of the flowformed tube. The flowforming process may be conducted in one or more flowforming passes. When two or more passes are used, the first pass, preferably, is larger than the subsequent passes, and is at least a 25% wall reduction. For example, for a 35% wall reduction using more than one pass, the first pass may be at least a 25% wall reduction and the second pass may be a 10% wall reduction. In another example, for a 50% wall reduction using more than one pass, the first pass may be at least a 25% wall reduction, the second pass may be a 15% wall reduction, and the third pass may be a 10% wall reduction. Preferably, the wall reduction ranges from about 25% to about 75% in one pass.

(30) With the degree of cold work, the hardness and tensile strength of a material are increased while the ductility and impact values are lowered. In addition, the porosity of the castings should be substantially eliminated through the cold work deformations. Cold working also usually reduces the grain size of the material. When a material is cold worked, microscopic defects are nucleated throughout the deformed area. As defects accumulate through deformation, it becomes increasingly more difficult for slip, or the movement of defects, to occur. This results in a hardening of the material. If a material is subjected to too much cold work, the hardened material may fracture. Thus, with each flowforming pass, the material becomes harder and less ductile, so a series of smaller and smaller reductions may be used after the first pass.

(31) In addition to an increase in the biaxial strength and wear resistance, embodiments may also provide compressive residual stresses at the inner diameter of the component induced by an autofrettage process. Autofrettage is a metal fabrication technique used on tubular components to provide increased strength and fatigue life to the tube by creating a compressive residual stress at the bore. During a typical autofrettage process, a pressure is applied within a component resulting in the material at the inner surface undergoing plastic deformation while the material at the outer surface undergoes elastic deformation. The result is that after the pressure is removed, there is a distribution of residual stress, providing a residual compressive stress on the inner surface of the component. In embodiments of the present invention in the final flowforming pass, the rollers 16 may be configured in such a way that the rollers compress the outer diameter of the workpiece using a combination of axial and radial forces so as to cause the inner diameter of the workpiece 18 to be compressed onto the mandrel 12 with sufficient force so that the inner diameter plastically deforms sufficiently enough, imparting a compressive stress to the inner diameter. This may be accomplished by pulling the rollers sufficiently apart from one another. The flowform process then causes the workpiece 18 to compress against and grip the mandrel 12 compared to the workpiece 18 just releasing from or springing back off of the mandrel 12 which is what typically occurs during a standard flowforming process. Causing the inner diameter to compress against the mandrel 12 in this way imparts a compressive hoop stress on the inner diameter of the flowformed component.

(32) FIGS. 9 and 10 show a perspective view and side view, respectively, of a roller configuration according to embodiments of the present invention. FIG. 9 shows a carriage that houses three flowforming rollers (shown as X, Y and Z in FIG. 10) that may move along three axes (shown as X-, Y- and Z-axes) and which are radially located around the spindle axis, e.g., at 120 apart from one another. Although the figures show three rollers, the process may use two or more rollers. The independently programmable X, Y and Z rollers provide the necessary radial forces, while the right to left programmable feed motion of the W-axis applies the axial force. Each of the rollers may have a specific geometry to support its particular role in the forming process. In addition, the position of the rollers 16 may be staggered with respect to one another. The amount of stagger may be varied and may be based on the initial wall thickness of the workpiece and the amount of wall reduction desired in a given flowforming pass. For example, as shown in FIG. 10, S.sub.o shows the wall thickness of a workpiece before a given flowforming pass and S.sub.1 shows its wall thickness after the flowforming process with the rollers 16 moving in the v direction. The rollers 16 may be staggered axially along an axial direction of the workpiece 18 (shown as the W-axis in FIG. 9) and may be staggered radially with respect to the centerline or inner diameter of the workpiece (along the X-, Y- and Z-axes), preferably to apply a relatively uniform compression to the outside of the workpiece 18. For example, as shown in FIG. 10, roller X may be separated from roller Y by a displacement or distance A.sub.1 and may be separated from roller Z by a distance A.sub.2 along an axial direction of the workpiece 18. Similarly, roller X may be radially displaced from the inner diameter of the workpiece a distance, S.sub.1, which is the desired wall thickness of the workpiece 18 after a given flowforming pass, roller Y may be radially displaced a distance, R.sub.1, and roller Z may be radially displaced a distance, R.sub.2. As shown, an angle K may be used to help determine the amount of radial staggering once an axial staggering amount has been determined.

(33) The more the rollers X, Y and Z are separated from one another the greater the helical twist imparted to the grain structure of the workpiece. A lubricant should be used between the inner diameter of the workpiece 18 and the mandrel 12 in order to reduce the problems of the workpiece 18 becoming stuck or jammed onto the mandrel 12 during this process. The compressive hoop stress imparted to the component in this way should reduce the probability of crack initiation and slow down the growth rate of any crack that may initiate on the inner diameter of the component, effectively improving the fatigue life of the tubular component. One benefit of this process is that the amount of compressive stress imparted to the inner diameter may be varied along the length of the tube depending on the roller configuration. For example, the rollers may be configured in such a way that a compressive stress is only imparted to one portion of the tube, e.g., on one end or in the middle of the tube.

(34) FIG. 11 shows a graph of the residual hoop stress distribution for tubular components made of a superalloy material that have undergone an autofrettage process. As shown, three tubular workpieces of L-605 material were formed and each workpiece's wall thickness was reduced by approximately 61%, 30% and 20% total wall reduction, respectively, according to embodiments of the present invention. In this case, the three samples had final dimensions of about one inch for the inner diameter and about 0.100-0.150 for the wall thickness. As shown in FIG. 11, each workpiece exhibited a residual compressive stress at its inner surface with a smaller residual compressive stress still seen within the workpiece for the depth measured in the samples. The 20% wall reduction workpiece showed a higher residual hoop stress at the inner surface (e.g., 0 depth from the inner surface) than the 61% wall reduction workpiece, although the higher 61% wall reduction exhibited a larger compressive stress within the workpiece (e.g., about 5-4010.sup.3 in. depth) than the 30% or 20% workpiece.

(35) FIG. 12 is a photomicrograph showing a longitudinal cross-sectional view of a centrifugally cast 316 stainless steel tube subjected to a flowforming process. The sample was etched in order to show the grain structure. The outer diameter of the component is shown at the top of FIG. 12 and the inner diameter is shown at the bottom. FIGS. 13A and 13B are photomicrographs showing the outer diameter and inner diameter areas, respectively, of the flowformed, centrifugally cast 316 stainless steel tube at a 500 magnification. As shown, there is a significant difference in the amount of cold work the grain structures have undergone in these two areas. In the outer diameter, the grain structure is more deformed and flattened than the inner diameter with the grains substantially aligned in the longitudinal direction, parallel to the center line of the flowformed component. In the inner diameter, the grain structure is less deformed than the outer diameter with the grains having some angled grain flow toward the radial direction. The outer diameter of the centrifugally cast flowformed component also exhibited substantially different hardness properties than the inner diameter. The hardness near the outer diameter measured a hardness level of Rockwell C 39-42, whereas the hardness near the inner diameter was Rockwell C 26-29.

(36) After the one or more flowforming passes, the component may undergo additional post processing, such as a heat treatment. As known by those skilled in the art, a material that has been hardened by cold working may be softened by annealing. Annealing may relieve stresses, allow grain growth, or restore the original properties of the alloy depending on the temperature and duration of the heat treatment used. Ductility may also be restored by annealing. Thus, after heat treating, the component may undergo one or more additional flowforming passes without fracturing.

(37) As mentioned above, the metal forming may include other cold working processes other than flowforming, such as pilgering, radial forging, and/or rolling. As known by those skilled in the art, in the pilgering process, the tubular component is rotated and reduced by forging and elongating the tube stepwise over a stationary tapered mandrel reducing the tube. Two rolls or dies, each with a tapering semi circular groove running along the circumference engage the tube from above and below and rock back and forth over the tube (the pass length) while a stationary tapering mandrel is held in the center of the finished tube. At the beginning of a stroke or pass, the circular section formed between the grooves of the two opposing rolls corresponds to the diameter of the tube and to the thickest section of the mandrel. As the dies move forward over the tube, the circular section reduces in area until, at the end of the pass length, the circular section corresponds to the outer diameter of the finished tube and the inner mandrel diameter corresponds to the inner diameter of the finished tube, resulting in a longer length, smaller outer and inner diameter finished tube. As known by those skilled in the art, a radial forge process may include four hammers moving in and out and hammering the workpiece over a mandrel. The driver and counter holder move the workpiece over the mandrel and into the reciprocating hammers. As known by those skilled in the art, a rotary swage process may include dies that rotate as a group inside of a stationary housing as the workpiece is pushed over the mandrel and into the dies which upsets/swages the material.

(38) Although the above discussion discloses various exemplary embodiments of the invention, it should be apparent that those skilled in the art can make various modifications that will achieve some of the advantages of the invention without departing from the true scope of the invention.