Method For Manufacturing Coloring Ceramics Via Colloidal Dispersion Followed By Conventional Pressing Techniques

Abstract

A colored ceramic powder is produced from a mixture of coloring solutions consisting of metallic salts that are introduced to a ceramic slurry and subsequently dried. The coloring solution may comprise for example of chosen metallic salts, a solvent, an organic solvent such as derivatives of propylene oxides, an acid and a possible binder. Once all the constituents are thoroughly mixed to a homogeneous state, the slip is dried to a powder form, which spray drying equipment can be used. The dried powder can then be subjected to an isostatic or biaxial press manufacturing process to create a green state ceramic body. Once pressed, the ceramic body can be subjected to a sintering process. After final sinter, the resulting ceramic body possesses an innate color that is homogenous throughout its composition. The method is especially useful for coloring zirconia dental restorations.

Claims

1. A colored zirconia ceramic slurry fabricated by a colloidal mixing process comprising the steps of: a) obtaining a coloring solution consisting essentially of at least one metallic salt as a coloring agent, a solvent, and optionally, an organic solvent and optionally, an acid, wherein the at least one metallic salt is soluble in the solvent; b) choosing the relative constituents of the coloring solution to provide a selected color for use in a zirconia ceramic dental restoration; c) choosing a relative amount of the coloring solution for an amount of a zirconia ceramic slurry comprising a ceramic material that is predominantly a zirconia ceramic material, to provide a selected color intensity for use in the zirconia ceramic dental restoration; d) mixing the amount of the coloring solution and the amount of zirconia ceramic slurry to distribute the coloring solution throughout the zirconia ceramic slurry; and e) adding a binder in an amount of from 0.5% to 10% by weight of the coloring solution, to the mixture of the coloring solution and the zirconia ceramic slurry to form the colored zirconia ceramic slurry, wherein, the colored zirconia ceramic slurry comprises the zirconia ceramic slurry, the coloring solution, and the binder.

2. The colored zirconia ceramic slurry of claim 1 wherein the colored zirconia ceramic slurry consists essentially of the ceramic material, the coloring solution, and the binder.

3. The colored zirconia ceramic slurry of claim 1 wherein the at least one metallic salt comprises metallic salts of chromium and terbium as the coloring agent.

4. The colored zirconia ceramic slurry of claim 1 wherein the at least one metallic salt consists essentially of metallic salts of chromium and terbium as the coloring agent.

5. The colored zirconia ceramic slurry of claim 1 wherein the coloring solution of step (a) comprises 0.01% to 5% by weight of the at least one metallic salt.

6. The colored zirconia ceramic material of claim 1 wherein the coloring agent comprises CrCl.sub.3 and TbCl.sub.3 in a weight ratio of approximately 2 to 3 (CrCl.sub.3 to TbCl.sub.3).

7. The colored zirconia ceramic slurry of claim 1, wherein the zirconia ceramic slurry of step c) comprises a colloidal dispersion of white zirconia powder.

8. The colored zirconia ceramic slurry of claim 1 wherein the coloring solution comprises water as the solvent.

9. The colored zirconia ceramic slurry of claim 1 wherein the organic solvent is an alcohol or ketone.

10. The colored zirconia ceramic slurry of claim 1 wherein the organic solvent is a derivative of a propylene oxide or propylene glycol.

11. A colored zirconia ceramic slurry for use in a dental restoration comprising a mixture of a) a ceramic material that is predominantly a zirconia ceramic material; b) a coloring solution consisting essentially of a solvent and a coloring agent consisting essentially of metallic salts of terbium and chromium dissolved in the solvent; and optionally, an organic solvent; and optionally, an acid; and c) a binder.

12. A colored zirconia ceramic powder for use in a zirconia ceramic dental restoration comprising ceramic material that is predominantly a zirconia ceramic material, a coloring agent consisting essentially of metallic components of terbium and chromium to provide a selected color for the dental restoration, and a binder.

13. The colored zirconia ceramic powder of claim 12 wherein the metallic components of chromium and terbium are present in a weight ratio of approximately 2 to 3 (chromium component to terbium component).

14. A colored zirconia ceramic body for use in making a zirconia dental restoration comprising a green state, zirconia ceramic body consisting essentially of the colored zirconia ceramic powder of claim 12, wherein the coloring agent is distributed throughout the colored zirconia body.

15. The colored zirconia ceramic body of claim 14, wherein the metallic components are present in a weight ratio of approximately 2 to 3 (chromium component to terbium component).

Description

DETAILED DESCRIPTION

[0027] The present invention relates to color a ceramic body during the initial process and fabrication of the ceramic. A coloring solution is added to the ceramic system during the processing stage. The result is a ceramic with intrinsic color properties and complete color saturation.

[0028] A color solution of known compositions and concentrations can be used to create any color of desired hue, chroma and value. Using metallic salts as the coloring agent, as well as a solvent to disperse the salts into solution, this invention relates to a process that is designed for coloring a ceramic during the manufacturing process of the material.

[0029] The process hereof ensures total and homogeneous color penetration into a ceramic body. Such a ceramic body can then be cut or milled into any shape or form. The final sintered ceramic body will be colored completely without the need for an extra coloring process that normally takes hours using conventional ceramic color methods.

[0030] The coloring solution and process hereof do not adversely affect the mechanical and optical properties of the natural ceramic. Because the coloring agent is mixed in a colloidal process, the coloring ions are homogenously distributed through the ceramic's crystal structure. Therefore, the coloring ions are incorporated throughout the ceramic.

Application

[0031] The present invention relates to the fabrication of a colored ceramic using a unique colloidal mixing process of a coloring agent into a ceramic slurry. Such a process can be applied to the dental industry, particularly in the fabrication of dental zirconia. At present, zirconia blocks are fabricated for the milling of dental crowns, bridges and copings. Due to the natural strength and aesthetics of teeth, such mechanical and optical properties are needed in dental ceramics.

[0032] At present, dental frameworks are milled from zirconia blocks. Because the natural color of zirconia is white, there is a need to color the ceramic. The ceramic is therefore colored using conventional dipping methods using coloring liquids. Current methods involve dipping a pre-sintered zirconia framework of final shape into the color liquid for a specified soaking time period. Frameworks are subsequently dried and sintered. The dental industry at large uses the VITA classic shade guide as a standard for teeth aesthetics. These colors are unique in hue, chroma and value. Conventional color liquids are made to match these properties.

[0033] The present invention can eliminate the need for the coloring process of the pre-sintered dental frameworks. A zirconia dental ceramic can be fabricated with the innate color properties of the final desired product.

[0034] It is within the scope of the present invention to fabricate a dental zirconia ceramic with a color that matches the hue, chroma and value of the VITA Classic dental shades.

[0035] It is also within the scope of the present invention to fabricate a dental zirconia ceramic block that can be milled to a specified dental framework of final shape and subsequently sintered. The resulting sintered zirconia framework will be of final shape and color that matches the VITA Classic shades.

Testing Results

[0036] Successful results have been achieved with the present invention. A coloring solution of known concentration and composition and mixed it into a colloidal zirconia slurry was used.

[0037] A coloring solution containing TbCl.sub.3, CrCl.sub.3, propylene glycol, 37% hydrochloric acid and de-ionized water was added to a zirconia slurry.

[0038] The exact composition of the coloring solution is as follows: 0.0914 wt % TbCl.sub.3, 0.0609 wt % CrCl.sub.3, 2.070 wt % propylene glycol, and 0.104 wt % hydrochloric acid. The balance was de-ionized water. The final pH of the solution was measured to be 1.93.

[0039] A ratio of 0.0218 grams of coloring liquid per gram of zirconia slurry was blended into a homogeneous mixture.

[0040] The slurry was subsequently combined with a binder, dried and pressed. This was followed by a sintering process during which the discs were fired into a pre-sintered bisque stage. After final sinter, the colored ceramic was cut to assure complete color saturation.

[0041] Total and homogenous coloring of the ceramic block was achieved. Using a VITA Easyshade instrument, the color was checked to verify if a dental shade had indeed been matched. The final color matched closely to the VITA Classic shade B2.

[0042] A second test was performed to verify the results of the first. A coloring liquid of different composition and concentration was used for processing.

[0043] The exact composition of the coloring solution is as follows: 0.122 wt % TbCl.sub.3, 0.081 wt % CrCl.sub.3, 2.030 wt % propylene glycol, and 0.104 wt % hydrochloric acid. The balance was de-ionized water. The final pH of the solution was measured to be 1.96.

[0044] A ratio of 0.0218 grams of coloring liquid per gram of zirconia slurry was blended into a homogeneous mixture with a binder.

[0045] The slurry was subsequently dried and pressed into a disc shape. This was followed by a sintering process during which the discs were fired into a pre-sintered bisque stage. After final sinter, the colored ceramic was cut to assure complete color saturation.

[0046] Total and homogenous coloring of the ceramic block was achieved. Using a VITA Easyshade instrument, the color was checked to verify if dental shade had indeed been matched. The final color matched closely to the VITA Classic shade A1

[0047] Therefore, it will be understood that the present invention, as it relates to a coloring liquid that is introduced to a colloidal process by which a colored ceramic is fabricated, has proven to be particularly useful in the dental industry to create a dental ceramic with intrinsic colors that match the desired aesthetics of dental frameworks.

[0048] It will now be appreciated that the present invention relates to a unique process for providing selected coloring of ceramic materials in pressing fabrication by introducing a coloring solution of metallic salts into the slurry. This invention is particularly applicable to the coloring of fabricated zirconia blocks for use as dental restorations such as full contour crowns, bridges and the like. While exemplary embodiments have been disclosed herein, the scope hereof will be limited only by the appended claims and their legal equivalents.