Polypropylene Tube

Abstract

A tube (3) for a product, in particular a cosmetic product, of liquid or pasty consistency or in the form of a gel, having tube head (5), and a skirt (7) having a proximal end (9) connected to the tube head (5) and an opposite distal end, and forming an internal volume (V) suitable for receiving the product. The skirt (7) and the tube head (5) are polypropylene.

Claims

1. Tube for a product, in particular a cosmetic product, of liquid or pasty consistency or in the form of a gel, comprising: a tube head, a skirt having a proximal end connected to the tube head and an opposite distal end, and forming an internal volume (V) suitable for receiving the product, said skirt and said tube head comprising polypropylene.

2. Tube according to claim 1, wherein said skirt further comprises one or more polyethylene components.

3. Tube according to the claim 1, wherein one of the polyethylene components is made of polyethylene obtained by metallocene catalysis, optionally accompanied by another polyethylene component in the form of polyethylene not obtained by metallocene catalysis.

4. Tube according to claim 1, wherein the skirt is multilayer.

5. Tube according to claim 4, wherein polypropylene and polyethylene obtained by metallocene catalysis are separately present in at least two individual layers of the skirt.

6. Tube according to claim 4, wherein polypropylene is present in an inner layer of the skirt and the head is attached to said skirt so as to be in contact with said inner layer.

7. Tube according to claim 6, wherein polyethylene obtained by metallocene catalysis is present in a layer adjacent to the inner layer.

8. Tube according to claim 5, wherein the layer comprising polyethylene obtained by metallocene catalysis is a central layer.

9. Tube according to claim 4, wherein at least one of the layers comprises polyethylene not obtained by metallocene catalysis, and the thickness of one of the layers comprising polyethylene not obtained by metallocene catalysis represents at least of the total thickness of the skirt.

10. Tube according to claim 4, wherein polyethylene not obtained by metallocene catalysis is present in an outer layer.

11. Tube according to claim 1, wherein the skirt comprises a layer formed of a mixture of polypropylene and of polyethylene obtained by metallocene catalysis.

12. Tube according to claim 11, wherein the mixture comprises at least 20 wt. % of polyethylene obtained by metallocene catalysis.

13. Tube according to claim 11, wherein the mixture comprises at most 80 wt. % of polypropylene.

14. Assembly of a cap and a tube according to claim 1.

15. Assembly according to claim 14, wherein the cap in continuity of material of the tube head.

Description

[0041] Other features, objects and advantages of the invention will become apparent from the following description, which is purely illustrative and not limitative, and which should be read with reference to the accompanying drawings, in which:

[0042] FIG. 1 shows schematically a partial sectional view of an assembly of a cap and a tube according to one aspect of the invention,

[0043] FIG. 2 shows schematically a partial sectional view of a multilayer skirt according to one aspect of the invention.

[0044] In all the figures, common elements are marked by identical reference numerals.

[0045] FIG. 1 partially shows an assembly of a cap 1 and a tube 3 for a product, in particular a cosmetic product, of liquid or pasty consistency or in the form of a gel, according to one aspect of the invention. The tube 3 comprises: [0046] a tube head 5, [0047] a skirt 7 having a proximal end 9 connected to the tube head 5 and an opposite distal end (not shown), and forming an internal volume V suitable for receiving the product.

[0048] In this embodiment, said tube head 5 comprises a flat transverse wall 11 that extends in a plane orthogonal to the axis of the skirt 7 and is provided with an opening 13 for dispensing the product contained in the internal volume V of the tube 3. Said tube head 5 is connected to the cap 1 by means of a hinge 15.

[0049] Said tube head 5 may further comprise an insert (not shown here) arranged in contact with the transverse wall 11, typically in contact with a face of the transverse wall 11 which is oriented towards the internal volume V of the tube 3, which volume is defined by the skirt 7.

[0050] Typically, said insert is made of a multilayered material comprising a barrier layer limiting the infiltration and the leakage of the undesirable components through the tube head. The inserts commonly used are composed of two layers of plastics material surrounding the intermediate barrier layer. The two layers of plastics material serve to isolate the metal layer from the product contained in the tube, which is liable to damage it. The barrier layer typically comprises a metal layer and/or a layer of ethylene vinyl alcohol (EVOH).

[0051] The head comprises an attachment surface 17 to which the proximal end 9 of the skirt 7 is connected, and an upper annular portion 19 located on the periphery of the head 5 covering the edge of the proximal end 9 of the skirt 7.

[0052] The skirt 7 may be connected to the tube head 5 either by overmoulding the tube head 5 on the skirt 7 or by welding or bonding by fitting the skirt 7 to the tube head 5 formed previously, in particular by injection or by injection compression, or by any other techniques.

[0053] According to the invention, said skirt 7 and said tube head 5 comprise polypropylene (PP).

[0054] Preferably, the polypropylene is either a polypropylene homopolymer (PPH) or a polypropylene copolymer, in particular a random copolymer (PPR), or a mixture thereof. The type of polypropylene of the tube head 5 may be identical to or different from that of the skirt 7.

[0055] The polypropylene is advantageously a polymer having mechanical properties, in particular rigidity, hardness and strength, which are greater than those of polyethylene. Thus, the polypropylene tube head 5 makes it possible to resist handling better than conventional polyethylene tube heads. The fact that the head 5 and the skirt 7 both comprise polypropylene makes it possible to obtain effective adhesion therebetween and limits the risks of detachment.

[0056] Advantageously, the polypropylene is present in a layer of the skirt 7 which is in contact with the tube head 5.

[0057] Advantageously, said skirt 7 further comprises one or more polyethylene components. The polyethylene has the advantage of providing flexibility to the skirt 7 of the tube 3.

[0058] One of these polyethylene components is preferably polyethylene obtained by metallocene catalysis (PEm).

[0059] A polyethylene obtained by metallocene catalysis is a polyethylene obtained by a polymerisation reaction based on an organometallic catalytic system such as a metallocene. Metallocenes and such polymerisation reactions are known to the person skilled in the art.

[0060] Advantageously, the polyethylene obtained by metallocene catalysis is a copolymer of ethylene and an alpha-olefin, such as a C3-C20 alpha-olefin. Preferably, said copolymer consists of ethylene and octene.

[0061] Preferably, the density of the polyethylene obtained by metallocene catalysis, measured in accordance with ASTM Standard D792, is of between 0.890 and 0.920 g/cm.sup.3, preferably of between 0.900 and 0.915 g/cm.sup.3. Preferably, the melt flow index, measured in accordance with ASTM Standard D1238 at 190 C. using a charge of 2.16 kg, is of between 0.1 and 10 g/10 min, preferably between 0.1 and 5 g/10 min. This may for example be a copolymer from a range of copolymers sold by Dow under the name Affinity.

[0062] This polyethylene obtained by metallocene catalysis may optionally be added of polyethylene not obtained by metallocene catalysis. Advantageously, the polyethylene not obtained by metallocene catalysis is a mixture of low-density polyethylene (LDPE) and of linear low-density polyethylene (LLDPE). Preferably, LDPE and between 80 and 20%, or even between 80 and 50% of LLDPE: the mixture preferably comprises 30% of LDPE and 70% of LLDPE.

[0063] In a first embodiment of the skirt 7, shown in FIG. 2, said skirt 7 is a multilayer skirt in which the polypropylene and the polyethylene component obtained by metallocene catalysis are separately present in at least two individual layers of the skirt 7.

[0064] This embodiment in particular relates to a multilayer skirt comprising three superposed main layers: an inner layer 21 oriented towards the inside of the internal volume V of the tube 3, an outer layer 23 oriented towards the outside of the tube 3 and a central layer 25 located between the inner layer 21 and the outer layer 23.

[0065] Said inner layer 21 corresponds to the layer of the skirt 7 which is in contact with the tube head 5 and the polypropylene is present in said inner layer 21 of the skirt 7. Said head 5 is thus attached to said skirt 7 so as to be in contact with said inner layer 21. Such a configuration allows for contact between two polypropylene-based materials and effective adhesion between said materials.

[0066] If the embodiment comprises polyethylene not obtained by metallocene catalysis, said polyethylene is preferably present in an outer layer 23. This layer allows to provide flexibility to the skirt 7 of the tube 3, and an appearance (gloss and transparency, for example) and feel which are pleasant for the user and are similar to those of a skirt made entirely of polyethylene. The outer layer 23 may also comprise polypropylene.

[0067] The polyethylene obtained by metallocene catalysis is, for its part, present in a layer adjacent to the inner layer 21. Here, this layer is said central layer 25. It allows to provide not only flexibility to the skirt 7 but also effective adhesion between the polypropylene layer and another polyethylene layer, in particular the outer layer 23.

[0068] In a second embodiment (not shown), the skirt 7 may be a bilayer formed of an the skirt 7 in contact with the tube head 5 and the polypropylene is present in said inner layer 21 of the skirt 7. As described previously, such a configuration makes it possible to have a skirt 7 and a head 5 which are in contact by means of two polypropylene-based materials, permitting effective adhesion therebetween. In the case of a skirt 7 comprising polyethylene obtained by metallocene catalysis, said polyethylene is preferably present in the outer layer 23 that is adjacent to the inner layer 21. This polyethylene-based layer gives the skirt 7 flexibility and a pleasant appearance and feel. It is also possible for the outer layer 23 to comprise polypropylene.

[0069] Thus, in this embodiment, the tube head 5 may be of 100% polypropylene (for example a random polypropylene copolymer) and the skirt 7 may be made of polyethylene obtained by metallocene catalysis and of polypropylene, for example a random polypropylene copolymer. The skirt 7 is a multilayer skirt, obtained for example by coextrusion, in which the inner layer is made of polypropylene and the outer layer is made of polyethylene obtained by metallocene catalysis. Such a skirt has a gloss and a flexibility similar to a skirt made entirely of polyethylene. The skirt 7 and the tube head 5 formed previously can be fitted by welding, for example by hot-air welding.

[0070] In a third embodiment, not shown, the skirt 7 may be a multilayer skirt comprising a barrier layer. It may for example be a layer of ethylene vinyl alcohol (EVOH) and/or a metal layer such as an aluminium layer. The barrier layer is preferably a central layer located between an inner layer and an outer layer. As described previously in the first embodiment, said inner layer 21 corresponds to the layer of the skirt 7 in contact with the tube head 5, and the polypropylene is preferably present in the inner layer in order to be in contact with the polypropylene tube head 5 and to provide effective adhesion between the skirt 7 and the head 5. The outer layer may comprise polypropylene and/or polyethylene in order to provide flexibility to the skirt 7.

[0071] The multilayer may comprise adhesion layers between the main layers, in particular in the case of a multilayer comprising a barrier layer. This may be for example modified polypropylene and/or polyethylene.

[0072] More generally, the thickness of the layer comprising the polyethylene not obtained by metallocene catalysis represents at least of the total thickness of the skirt 7, or even at least of the total thickness of the skirt 7.

[0073] The multilayer skirt 7 may be obtained by coextrusion or lamination.

[0074] In a fourth embodiment, not shown, the skirt 7 may be a monolayer. This layer corresponds to the layer of the skirt 7 in contact with the tube head 5. It may comprise only polypropylene or a mixture of polypropylene and one or more polyethylene components. The polyethylene may be a polyethylene obtained by metallocene catalysis. Said mixture comprises at least 20%, or even at least 30%, or even at least 50%, by weight of polyethylene obtained by metallocene catalysis, and/or at most 80%, or even at most 70%, or even at most 50%, by weight of polypropylene.

Examples of Tubes 3 According to the Invention:

[0075] In the examples given below, the thicknesses are given solely by way of example, and may vary.

EXAMPLE 1

[0076]

TABLE-US-00001 Material Thickness Skirt: Inner layer PPR 100-150 m Outer layer PEm 200-250 m Head: Monolayer PPR

EXAMPLE 2

[0077]

TABLE-US-00002 Material Thickness Skirt: Inner layer PPR 100-150 m Central layer PEm 50-100 m Outer layer LDPE/LLDPE 100-150 m Head: Monolayer PPR or PPH

EXAMPLE 3

[0078]

TABLE-US-00003 Material Thickness Skirt: Inner layer PPR 100-200 m Central layer PEm 100-200 m Outer layer PPR 100-200 m Head: Monolayer PPR

EXAMPLE 4

[0079]

TABLE-US-00004 Material Thickness Skirt: Inner layer PPR 150-200 m Adhesion layer Modified PP 10-20 m Central layer EVOH 10-50 m Adhesion layer Modified PP 10-20 m Outer layer PPR 150-200 m Head: Monolayer PPR

EXAMPLE 5

[0080]

TABLE-US-00005 Material Thickness Skirt: Monolayer PPR 200-400 m Head: Monolayer PPR or PPH

EXAMPLE 6

[0081]

TABLE-US-00006 Material Thickness Skirt: Monolayer PPR/PEm 200-400 m 80:20 Head: Monolayer PPR

EXAMPLE 7

[0082]

TABLE-US-00007 Material Thickness Skirt: Monolayer PPR/PEm 200-400 m 70:30 Head: Monolayer PPR

EXAMPLE 8

[0083]

TABLE-US-00008 Material Thickness Skirt: Monolayer PPR/PEm 200-400 m 50:50 Head: Monolayer PPR

[0084] It should be noted that variants are of course possible and that the present invention is not limited to an assembly of a cap and a tube as described previously, i.e. a cap made of the same material as a tube head comprising a flat transverse wall. In particular, it is possible to extend the present invention to other types of tube heads, in particular conventional tube heads comprising a shoulder and a neck connected to the shoulder. Furthermore, said cap may be removable from the tube head in the form of a service-cap. It may then be fixed to said tube head, in particular to said neck, by snap-fitting and/or screwing.