PROCESSES FOR EXTRACTING LIGNIN FROM BLACK LIQUOR

Abstract

The present invention relates to processes for extracting lignin from black liquor. In particular, processes for both extracting acidic lignin and extracting alkaline lignin from black liquor are disclosed, comprising: precipitating lignin by acidification of black liquor; adjusting the temperature to above 60° C.; cooling; separation; and displacement washing and/or washing by ion exchange.

Claims

1-43. (canceled)

44. A process for extracting lignin from black liquor, characterized in that it comprises the steps of: a) precipitating lignin by acidifying black liquor; b) adjusting the temperature to above 60° C.; c) cooling; d) separation; and e) displacement washing, ion exchange washing, or both displacement washing and ion exchange washing.

45. The process according to claim 44, wherein: (i) displacement washing is performed with a salt solution, and/or (ii) ion exchange washing is performed with water with addition of acid.

46. The process according to claim 45, wherein displacement washing is performed with a salt solution, and the salt solution comprises sodium salt.

47. The process according to claim 45, wherein displacement washing is performed with a salt solution, and the salt solution has a conductivity greater than 30 mS/cm.

48. The process according to claim 47, wherein the salt solution has a conductivity greater than 80 mS/cm.

49. The process according to claim 45, wherein ion exchange washing is performed with water with addition of acid, and the acid is sulfuric acid.

50. The process according to claim 44, characterized in that i) the black liquor is acidified in step (a) to a pH of less than 11.5, ii) step (a) of precipitation by acidifying black liquor is performed with an acidifier selected from inorganic acids, organic acids or acid oxides, or with a solution comprising said acidifier, and/or iii) it further comprises the oxidation of black liquor concurrently with step (a).

51. The process according to claim 50, wherein i) the black liquor is acidified in step (a) to a pH in the range of 2.5 to 11.5, and ii) the acidifier in step (a) is acid oxide or CO.sub.2.

52. The process according to claim 44, characterized in that the temperature adjustment of step (b) ranges from 60° C. to 200° C.; and/or the temperature adjusted in step (b) is maintained for a time interval from 2 minutes to 24 hours.

53. The process according to claim 44, characterized in that steps (a) and (b) are performed concurrently.

54. The process according to claim 44, characterized in that in step (c) the black liquor is cooled to a temperature below 50° C., and/or step (d) is performed at a temperature below 50° C.

55. The process of claim 54, wherein step (d) is performed at a temperature below 40° C.

56. The process according to claim 44, characterized in that separation step (d) is a solid-liquid type separation.

57. The process according to claim 56, wherein the solid-liquid separation is performed by filtration.

58. The process according to claim 44, characterized in that after step (d) the solid phase goes to washing step (e) and the liquid phase is conducted to evaporation; or after step (d) a pH fractionation takes place.

59. The process according to claim 44, characterized in that the washing performed in step (e) is in suspension or countercurrent to the solid phase obtained in step (d).

60. The process of claim 59, wherein the washing performed in step (e) is countercurrent to the solid phase obtained in step (d).

61. The process according to claim 44, characterized in that it further comprises step (f) of resuspending the solid phase and/or it further comprises the dehydration step after washing step (e) and/or after resuspension step (f).

62. The process of claim 61, wherein the dehydration is performed by pressing, dewatering with compressed air and/or drying with a dryer, and/or the resuspension step (f) is performed in water with subsequent addition of acid or in acidic solution, and/or the resuspension step (f) further comprises filtration and, optionally, washing with industrial water.

63. The process according to claim 44, characterized in that the gases emitted from the tanks containing black liquor from the process and/or from the first acid washing are captured, treated and reused in the process, as energy and/or as chemical and/or the water used in countercurrent washings is reused in the process.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0067] FIG. 01 shows a simplified version of the kraft process.

[0068] FIG. 02 shows the supposed generic chemical structure for lignin.

[0069] FIGS. 03 and 04 show microscopy images of lignin granules.

[0070] FIG. 05 shows a comparison between the final qualities, indicated by the ash contents, of a resuspended cake that underwent alkaline washing and a second resuspended cake that did not undergo alkaline washing.

[0071] FIG. 06 shows a comparison between lignin extraction efficiencies in a process that comprises alkaline washing and a second process that does not comprise washing.

[0072] FIG. 07 shows the influence of temperature on the ash content.

[0073] FIG. 08 shows a comparison between the specific consumption of sulfuric acid in a process that comprises washing with salt solution and a second process that does not include washing.

[0074] FIG. 09 is a graph illustrating the lignin precipitation efficiency as a function of pH.

[0075] FIG. 10 shows a simplified scheme of a preferred embodiment of the lignin extraction process according to the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0076] The present invention relates to processes for extracting lignin from black liquor. Specifically, the present invention relates to processes for extracting acidic lignin from black liquor and processes for extracting alkaline lignin from black liquor, with modifications only in the washing step.

[0077] The present invention has the advantage of flexibility to obtain different products: alkaline lignin and acidic lignin. The alkaline lignin obtained by the processes of the present invention has great advantages for applications in resole resins.

[0078] The lignin extraction processes of the present invention can take place continuously or in batches. Preferably, the processes take place in batches.

[0079] The black liquor used in the processes described in the present invention is pumpable as it has a solids content of 15% to 50%.

[0080] The processes disclosed herein differ from those described in the state of the art mainly by the formation of lignin granules resulting from specific temperature variations performed at the beginning of the processes and by the strategy adopted in the washing step, which provides flexibility in obtaining different types of lignin.

[0081] At the beginning of the processes, there is a temperature control in the sense that, during or after precipitation, the temperature is adjusted to 60° C. or above and then there is a temperature decrease. This temperature variation induces the formation of lignin granules, which result in a significant improvement in the subsequent separation step, as well as an easier washing.

[0082] Microscopy images of the granules formed due to temperature variation at the beginning of the processes of the present invention can be seen in FIGS. 03 and 04. In FIG. 03, the granules are those contained in the first cake, i.e., in the first filtration. FIG. 04, by its turn, shows the granules when the resuspension step occurs in the process, these granules being formed due to temperature variation at the beginning of the processes.

[0083] FIGS. 03 (a) and 04 (a) show granules formed at 40° C.; FIGS. 03 (b) and 04 (b) show granules formed at 60° C.; FIGS. 03 (c) and 04 (c) show granules formed at 70° C.; and FIGS. 03 (d) and 04 (d) show granules formed at 80° C.

[0084] The washing steps of the processes described herein comprise specific washing stages that result in advantages such as improving the quality of the lignin cake, which has a reduced ash content, and an improvement in the lignin extraction efficiency. These advantages are exemplified in FIGS. 05 and 06, respectively. These figures indicate the influence of alkaline washing in the first stage, i.e., right after the separation step. The alkaline washing, as mentioned in FIGS. 05 and 06, refers to a wash with a salt solution.

[0085] In particular, FIG. 05 shows a comparison between the final qualities, indicated by the ash contents, of a cake that underwent alkaline washing in the first stage (right after the separation step) and a second cake that did not undergo any washing. Both cakes did not undergo washing of the second cake (after resuspension). This figure illustrates one of the technical advantages of the present invention, namely, a better final quality of the lignin cake due to the washing step.

[0086] FIG. 06, by its turn, shows a comparison between the lignin extraction efficiencies in a process that comprises alkaline washing in the first stage (right after the separation step) and a second process that does not comprise washing. Extraction efficiency is measured in the lignin fraction extracted from the first cake. As there is no washing of the lignin in the second process (right column in the figure—“no wash”) and washing takes place in the first process (left column in the figure—“alkaline wash”), it was expected that there would be loss of material in the first process, with alkaline washing. However, when washing was performed in the processes of the present invention, it was observed that the extraction efficiency is not impaired, which represents a surprising effect of the present invention. The difference between the two columns in FIG. 06 is not significant, yet the indicated behavior was not expected, since less efficiency was expected when washing the lignin, and this was not demonstrated.

[0087] FIG. 06 thus illustrates one of the technical advantages of the present invention, namely, improvement in the lignin extraction efficiency due to the washing step.

[0088] Regarding the ease of washing resulting from the temperature adjustment, a statistical study was performed on the influence of temperature on the ash content. The result of that study is shown in FIG. 07. The decrease in the ash percentage, observed at higher temperatures, demonstrates improved cake washability. The less ash, the easier or more effective the washing. Thus, the increase in temperature that takes place at the beginning of the processes of the present invention facilitates the washing step.

[0089] Described herein are processes for extracting lignin from black liquor comprising the steps of:

[0090] a) precipitating lignin by acidifying black liquor;

[0091] b) adjusting the temperature to above 60° C.;

[0092] c) cooling;

[0093] d) separation; and

[0094] e) displacement washing and ion exchange washing.

[0095] Such processes refer to processes for extracting acidic lignin from black liquor. The lignin that precipitates from the black liquor is alkaline and in displacement washing it remains alkaline. When there is ion exchange washing (acid washing), the lignin becomes acidic.

[0096] Also described herein are processes for extracting lignin from black liquor comprising the steps of:

[0097] a) precipitating lignin by acidifying black liquor;

[0098] b) adjusting the temperature to above 60° C.;

[0099] c) cooling;

[0100] d) separation; and

[0101] e) ion exchange washing.

[0102] Such processes refer to processes for extracting acidic lignin from black liquor. The lignin that precipitates from the black liquor is alkaline, and when ion exchange washing (acid washing) takes place, the lignin becomes acidic.

[0103] Additionally described herein are processes for extracting lignin from black liquor comprising the steps of:

[0104] a) precipitating lignin by acidifying black liquor;

[0105] b) adjusting the temperature to above 60° C.;

[0106] c) cooling;

[0107] d) separation; and

[0108] e) displacement washing.

[0109] Such processes refer to processes for extracting alkaline lignin from black liquor. The lignin that precipitates from the black liquor is alkaline and in displacement washing it remains alkaline.

[0110] In one embodiment of the invention, (i) the displacement washings are performed with salt solution; and (ii) the ion exchange washings are performed with water with addition of acid.

[0111] The salt solution may comprise any salts, preferably sodium salts, such as, for example, sodium sulfate, sodium sesquisulfate, sodium carbonate and sodium bicarbonate. Sodium sesquisulfate, when used, comes from a chlorine dioxide plant, and/or salts from the boiler's electrostatic precipitator. The latter refer to a mixture consisting mainly of sulfate, carbonate and sodium chloride.

[0112] The salt solution used in the displacement washings has a conductivity greater than 30 mS/cm, preferably greater than 80 mS/cm.

[0113] The use of salts in the processes of the present invention represents an economic advantage of lignin extraction processes, since the salts already used in the kraft process are used, whereby costs with this product can be saved.

[0114] Displacement washing allows the filtrate present in between the cake to be displaced before placing acid, preferably sulfuric acid, in contact with the lignin. The filtrate has a much higher alkalinity than lignin and therefore consumes more acid. The salt solution is able to displace the filtrate solubilizing only a small amount of lignin. Furthermore, the salt solution has no alkalinity and therefore the addition of acid after the salt solution only displaces the solution without consuming acid.

[0115] Thus, displacement washing with salt solution reduces the amount of acid needed in the next ion exchange washing, solving the problem existing in current processes related to the large amount of acidifying agents needed. FIG. 08 illustrates the influence on the specific consumption of sulfuric acid caused by washing with a salt solution in the first stage (right after the separation step).

[0116] Due to displacement washing, the amount of acid that is included in the processes is spent only with the lignin present in the solution and not with other compounds, so that it is possible to save the amount of acidic products of the process.

[0117] Lignin itself requires a small amount of acid to make its ion exchange (by measurements of carboxylic groups, around 20 to 30 kg of H.sub.2SO.sub.4). Most of the acid in the prior art processes is spent with the filtrate where the lignin is immersed. The acid in contact with the filtrate releases CO.sub.2 and H.sub.2S and is also spent with buffer compounds present in the filtrate.

[0118] With the displacement of the filtrate in the processes of the present invention, the lignin immersed in sulfate solution is obtained. The subsequent addition of acid only makes the ion exchange with lignin, since there are no carbonate, sulfide or buffer molecules in the washing water.

[0119] Thus, the alkaline wash (by displacement) allows the filtrate to be separated from the lignin cake. A solution with high ionic strength is used, but does not consume acid, for example, Na.sub.2SO.sub.4. Washing is performed prior to the protonation of the phenolic and carboxylic groups, which allows the acid not to be spent with ions present in the filtrate.

[0120] Also, in displacement washing there is no exhalation of H.sub.2S and CO.sub.2 gases nor protonation of buffer molecules present in the filtrate. The displacement still allows for greater purity, as these and other compounds present in the filtrate will not be present in the final alkaline cake.

[0121] Due to the technical advance in carrying out the initial washing by displacement, parallel reactions with other compounds are avoided, which leads to a decrease in the amount of acid used and the amount of gases generated is very low, there being therefore no advantages in reusing them in the processes of the present invention. Otherwise, when there is excess acid, as in prior art processes, more gases are generated, and more reactions are triggered.

[0122] In addition, the low amount of acid used in the processes disclosed herein minimizes the need for disposing of sulfate-containing salts in landfills, which represents a technical and environmental advantage. This advantage solves the problem that currently exists regarding the need to dispose of sulfate salts in landfills, generated by the high sulfuric acid consumption. Existing prior art lignin extraction processes that use too much acid necessarily generate too many sulfate salts that need to be disposed of in landfills.

[0123] Ion exchange washings are performed with recovered water with an acid-adjusted pH below 1.5. Said acid may be selected from the group consisting of strong acids having a pH below 1.5. Preferably, the acid added to the water in the ion exchange washing is sulfuric acid.

[0124] In the acidic lignin extraction process comprising ion exchange washing and final washing it can occur, for example, (i) a first washing with water recovered mainly from a second washing and with pH adjusted with H.sub.2SO.sub.4, acid filtrate from a chlorine dioxide plant or other acid source, to less than 1.0, preferably less than 0.5; and (ii) a second washing with water recovered mainly from a third washing with pH adjusted with H.sub.2SO.sub.4, acid filtrate from a chlorine dioxide plant or other acid source, to less than 1.0, preferably less than 0.8, wherein said third washing would be performed with industrial water.

[0125] In the acidic lignin extraction process comprising displacement washing followed by ion exchange washing, the ion exchange cations are used in the displacement washing of the next batch. In this configuration, only one ion-exchange washing takes place after the displacement washing.

[0126] In a preferred embodiment of the invention, after displacement washing and/or ion exchange washing, final washing is still performed, preferably with industrial water.

[0127] In one embodiment of the invention, the black liquor is acidified in step (a) to a pH of less than 11.5, preferably to a pH in the range of 2.5 to 11.5.

[0128] Step (a) of precipitating lignin by acidifying black liquor can be performed with any acidic source. In one embodiment of the invention, acidification is performed with an acidifier, selected from inorganic acids, organic acids or acid oxides, or with a solution comprising said acidifier.

[0129] Non-limiting examples of inorganic acids may be selected from the group consisting of sulfuric acid and hydrochloric acid.

[0130] Non-limiting examples of organic acids may be selected from the group consisting of acetic acid and formic acid.

[0131] Non-limiting examples of acidic oxides may be selected from the group consisting of CO.sub.2, SO.sub.2 and SO.sub.3.

[0132] In a preferred embodiment of the invention, step (a) of precipitating lignin by acidifying black liquor is performed with an acid oxide. In a more preferred embodiment, the acid oxide is CO.sub.2. Such a compound is relatively cheap, thus rendering the process more economical.

[0133] Acidification is performed in order to protonate the phenolic groups present in lignin. When protonated, the solubility of these molecules decreases considerably, and precipitates are formed that are filterable/separable.

[0134] In this context, step (a) of lignin precipitation by acidification takes place at a pH of less than 11.5 due to the fact that the pKa of the aforementioned phenolic compounds is in the range of 10.0 to 11.0 and it is necessary to reach a pH compatible with these pKa to precipitate lignin. The higher the final extraction pH, the larger the chain size and the smaller the presence of carboxylic groups. There are then two aspects that are impacted by the final pH to be reached: the fraction of lignin to be recovered and the specific consumption of CO.sub.2. Therefore, according to the desired pH, the lignin fraction and the amount of CO.sub.2 change.

[0135] There is H.sub.2S emission from tanks containing black liquor from the processes, especially at the pH of the final acidification condition. H.sub.2S, as well as other gases that may be emitted from tanks containing black liquor in the processes of the present invention, are captured and treated appropriately, thus solving the current problem related to the emission of sulfur compounds in lignin extraction processes.

[0136] In an optional embodiment of the invention, the lignin extraction processes further comprise black liquor oxidation concurrently with step (a) of precipitation by acidification, to reduce the odor in the process. In the optional oxidation step, H.sub.2S is oxidized to a thiosulfate or a sulfate, thus avoiding problems with H.sub.2S emission, minimizing bad odor in the factory environment.

[0137] The current need for environmentally friendly lignin separation processes is solved in the present invention, since in the processes disclosed herein there is a reduction in the generated gases, as well as the treatment of waste gases. Furthermore, the low amount of acid used minimizes the need for disposing of sulfate-containing salts in landfills.

[0138] In one embodiment of the invention, before or after step (a) of the lignin extraction processes, cellulose fibers remaining from the black liquor resulting from the kraft process cooking are optionally separated by a separation process selected from: filtration, centrifugation or decantation.

[0139] In a preferred embodiment of the invention, the temperature adjustment of step (b) ranges from 60° C. to 200° C.

[0140] In one embodiment of the invention, the temperature adjusted in step (b) is maintained for any time interval. In a preferred embodiment of the invention, such time interval is greater than 2 minutes. In a more preferred embodiment, the time interval is between 10 minutes and 24 hours.

[0141] In one embodiment of the invention, steps (a) and (b) of the processes described herein may be performed concurrently.

[0142] The black liquor used in the processes of the present invention can be at any temperature, however it needs to have a temperature of 60° C. or above when or after it precipitates, and then undergo cooling, as this temperature variation ensures the size of the granules, improving lignin separation.

[0143] In one embodiment of the invention, in step (c) of the lignin extraction processes the black liquor is cooled to a temperature below 50° C.

[0144] The purpose of the temperature increase/adjustment followed by cooling is to agglomerate the lignin crystals. It was observed that the lignin crystals need a certain time to agglomerate and form granules, and that this granule formation allows a better separation later.

[0145] The temperature variation at the beginning of the processes of the present invention, thus, solves the currently existing problem related to the filtration capacity that requires large separation equipment (and large investments), since the separation is facilitated by granule formation and no further investments are required at this step of the process.

[0146] Microscopy images of the granules formed due to temperature variation at the beginning of the processes of the present invention can be seen in FIGS. 03 and 04. In FIG. 03, the granules are those contained in the first cake, i.e., in the first filtration. FIG. 04, by its turn, shows the granules in the resuspension step, granules that are formed due to temperature variation at the beginning of the processes.

[0147] FIGS. 03 (a) and 04 (a) show granules formed at 40° C.; FIGS. 03 (b) and 04 (b) show granules formed at 60° C.; FIGS. 03 (c) and 04 (c) show granules formed at 70° C.; and FIGS. 03 (d) and 04 (d) show granules formed at 80° C.

[0148] In one embodiment of the invention, separation step (d) is a solid-liquid type separation. The purpose of this step is to separate the crystals from the liquid remaining in the processes.

[0149] In a preferred embodiment, the solid-liquid type separation is performed by means of filters, settlers, decanters, centrifuges, among others. In a more preferred embodiment, separation step (d) is performed by filtration.

[0150] In one embodiment of the invention, separation step (d) is performed at a temperature below 50° C., preferably below 40° C.

[0151] In one embodiment of the invention, after separation step (d), the solid phase goes to washing step (e) and the liquid phase is directed to evaporation.

[0152] In another embodiment of the invention, the lignin extraction processes comprise, after separation step (d), a pH fractionation. Said fractionation can be performed whenever the liquid phase of step (d)—filtered, in the case where the separation is made by filtration—is directed to step (a) and precipitated again at a lower pH.

[0153] The pH fractionation aims to separate different lignin fractions through a fractional decrease in pH. FIG. 09 is a graph illustrating lignin precipitation as a function of pH. The four curves contained in the graph represent different tests performed, which prove the reproducibility of the results. Through this graph, it is possible to notice that the lower the acidification pH of the lignin fraction, the higher the precipitation efficiency.

[0154] In addition, pH fractionation provides lignin fractions with different specifications for different desired applications. For example, the greater the amount of phenolic hydroxyls and the lower the molecular weight, the better the antioxidant power of lignin (i.e., the lower the EC50 value); the lower the molecular weight, the better the lignin as additive for melt flow of thermoplastics, which is measured by the melt flow index. Therefore, fractionation has as advantage—in addition to obtaining a greater amount of lignin recovered from the black liquor—the flexible fractionation according to the needs of the final application.

[0155] Table 01 below illustrates specifications of lignin fractions obtained with pH fractionation. Molecular weight, OH indices and ash content are commonly measured data for lignin specifications.

TABLE-US-00001 TABLE 01 pH cake Mw phenolic OH acid OH aliphatic OH EC50 Tg Soluble Insoluble Ashes Sugars precipitation pH (Da) PD (mmol/g) (mmol/g) (mmol/g) S/G (mg/L) (° C.) (%) (%) (%) (%) 8.02 3.91 2515 1.91 4.39 0.41 1.41 2.42 222.0 129 8.4 87.4 2.7 0.93 8.53 4.75 1.90 4.16 0.39 1.36 2.59 134 4.4 84.8 4.4 0.90 9.08 5.12 2685 1.98 4.27 0.38 1.41 2.38 230.0 136 7.4 85.2 2.1 1.13 9.46 6.42 1.94 3.95 0.38 1.37 2.48 142 5.1 87.6 1.7 0.74 10.00 7.59 3677 2.29 3.18 0.32 1.41 2.11 270.0 161 6.8 87.4 4.2 0.93 Mw = molecular weight; PD = polydispersity; S/G = syringyl/guaiacyl ratio; EC50 = antioxidant power; Tg = glass transition temperature

[0156] When the processes of the present invention are performed in batches, each batch can be adjusted according to the lignin fraction of interest. Thus, batch processes allow for greater flexibility and homogeneity when pH fractionation is desired.

[0157] In one embodiment of the invention, the washing performed in step (e) can be countercurrent or in suspension with industrial water of the solid phase obtained in step (d). In a preferred embodiment, the washing performed in step (e) is countercurrent to the solid phase obtained in step (d). Therefore, when the separation is performed by means of filtration, the cake is washed in countercurrent (product retained in the filtration) obtained in step (d).

[0158] In one embodiment of the invention, the lignin extraction processes further comprise step (f) of resuspending the solid phase. In a preferred embodiment of the invention, step (f) is performed in water with subsequent addition of acid or in an acidic solution, with pH adjustment to a value lower than 3.5. The water used in the resuspension is directed to the final washing of the first cake obtained from the first filtration.

[0159] In the resuspension step, the washed solid phase—or cake, if separation by filtration takes place—is placed in a disperser, where a small amount of water is added.

[0160] For processes that have undergone ion exchange washing, especially for those where washing has occurred partially (or not completely), later, in another tank, acid is added until the pH reaches a value between 2 and 3. The acid added can be any acid, preferably sulfuric acid.

[0161] In this acidification stage of the resuspension step, a small amount of gases evolve. These gases are captured, treated and directed to a boiler for burning.

[0162] It is imperative that there is at least one wash before the resuspension step.

[0163] In one embodiment of the invention, resuspension step (f) further comprises filtering and, optionally, washing with industrial water.

[0164] The resuspension step is performed in order to carry out the ion exchange and more effectively separate the lignin from the solution, however it is not essential in the processes disclosed herein. Adjusting the temperature at the beginning of the processes promotes better separation and greater ease of washing, allowing a well-washed product to be obtained, without the need for resuspension to result in a cleaner product. Therefore, the resuspension step is optional.

[0165] In one embodiment of the invention, the lignin extraction processes further comprise a dehydration step after washing step (e) and/or after resuspension step (f). Dehydration can be performed by pressing, dewatering with compressed air and/or drying with a dryer.

[0166] In a preferred embodiment of the invention, after washing step (e) the cake is dehydrated by pressing. The maximum pressure in that step is about 1.5×10.sup.6 Pa (15 bar).

[0167] Dewatering with compressed air is performed with compressed air between 0.6×10.sup.6 Pa (6 bar) and 3.0×10.sup.5 Pa (3 bar).

[0168] The gases emitted from tanks containing black liquor and the waste gases emitted from the first acid washing of the processes are captured, treated and reused in the processes.

[0169] The gases are washed in an absorption tower with a soda solution, with a pH greater than 10, and/or burned in a boiler and reused in the processes as energy and/or as chemicals for the processes.

[0170] The water used in the countercurrent washes of the lignin extraction processes of the present invention are reused in the processes themselves. Countercurrent washing waters can be reused, for example, in the previous washing or in the optional resuspension step. After reuse, the washing waters proceed to evaporation or effluent treatment.

[0171] Lastly, dry lignin obtained from the processes of the present invention can be packaged.

[0172] In a preferred embodiment of the invention, the processes for extracting lignin from black liquor comprise the steps of:

[0173] A) precipitating lignin by acidifying black liquor with CO.sub.2 up to a pH range between 2.5 and 11.5 and, optionally, concurrent oxidation of the black liquor;

[0174] B) adjusting the temperature to above 60° C., preferably at a temperature ranging from 60° C. to 200° C.;

[0175] C) cooling to a temperature below 50° C.;

[0176] D) separation, preferably filtration;

[0177] E) displacement washing and/or ion exchange washing and, optionally, final washing;

[0178] F) optionally, resuspending the solid phase in water with subsequent addition of acid or in an acidic solution, followed by filtration and, optionally, washing with industrial water; and

[0179] G) dehydration by pressing, dewatering with compressed air and/or drying with a dryer.

[0180] A simplified schematic of a lignin extraction process according to this preferred embodiment of the present invention can be seen in FIG. 10.

[0181] As can be seen, the present invention overcomes the disadvantages and inconveniences of the state of the art. It is noteworthy that the examples below, as well as the figures presented should not be considered as limiting the present invention, since a person skilled in the art is fully capable of recognizing that modifications can be made within the scope of the invention.

EXAMPLES

[0182] The examples presented herein are non-exhaustive, intended only to illustrate the invention and should not be used as a basis for limiting it.

Example 1

[0183] In this example a process for extracting acidic lignin from black liquor according to the present invention is described, in which displacement washing and ion exchange washing occurred, and the optional resuspension step was not performed. Said process comprises the following steps:

[0184] a) acidification of black liquor with CO.sub.2 up to pH 8.53;

[0185] b) adjusting the temperature to 77° C. and maintaining this temperature for 30 minutes;

[0186] c) cooling to a temperature of about 38° C.;

[0187] d) filtering the product obtained in step (c) in a filter press and obtaining the first lignin cake;

[0188] e) countercurrent washing in the filter of cake obtained in step (d) (product retained from filtration), by means of the following washing sequence: [0189] washing with the water recovered from the second wash with sodium sulfate solution adjusted to a conductivity of 99 mS/cm; [0190] washing with water recovered mainly from the third wash and with pH adjusted to 0.83 with H.sub.2SO.sub.4; and [0191] last washing with industrial water;

[0192] f) pressing the washed cake obtained in step (e) in the filter press itself up to 6×10.sup.5 Pa (6 bar);

[0193] g) dewatering of the cake by displacement with compressed air;

[0194] h) drying of the cake in a dryer; and

[0195] i) packaging of the lignin dried in the dryer.

[0196] The lignin obtained by this process has as main characteristics an ash content of 1% and a pH of 4.63. In addition, in said process there was a specific consumption of H.sub.2SO.sub.4 of 130 kg per ton of lignin.

Example 2

[0197] In this example a process for extracting acidic lignin from black liquor according to the present invention is described, in which displacement washing occurred and the optional resuspension step was performed. Said process comprises the following steps:

[0198] a) acidification of black liquor with CO.sub.2 up to pH 8.52;

[0199] b) adjusting the temperature to 72.9° C. and maintaining this temperature for 30 minutes;

[0200] c) cooling to a temperature of 32° C.;

[0201] d) filtering the product obtained in step (c) in a filter press and obtaining the first lignin cake;

[0202] e) countercurrent washing in the filter of cake obtained in step (d), in which the water used in the washing comes from step (g) with conductivity adjustment to 88.6 mS/cm with sodium sulfate;

[0203] f) resuspending the cake obtained in step (e) in countercurrent water from the washing of step (h) and acid with pH adjustment to 2.5;

[0204] g) filtering the cake and directing the filtrate to be used as washing water in step (e);

[0205] h) washing with industrial water at neutral pH, without pH adjustment, and directing the washing water filtrate to the cake dilution in step (f); and

[0206] i) drying the cake in a dryer.

[0207] The lignin obtained by this process has as main characteristics an ash content of 1.1% and a pH of 2.5. In addition, in said process there was a specific consumption of H.sub.2SO.sub.4 of 67 kg per ton of lignin.

Example 3

[0208] In this example, a process for extracting acidic lignin from the black liquor according to the present invention is described, in which ion exchange washing occurred and the optional resuspension step was not performed. Said process comprises the following steps:

[0209] a) acidification of black liquor with CO.sub.2 up to pH 8.48;

[0210] b) adjusting the temperature to between 74.6° C. and maintaining this temperature for 30 minutes;

[0211] c) cooling to a temperature of 40.3° C.;

[0212] d) filtering the product obtained in step (c) in a filter press and obtaining the first lignin cake;

[0213] e) countercurrent washing in the filter of cake obtained in step (d) (product retained from filtration), by means of the following washing sequence: [0214] washing with water recovered from the second wash with pH adjusted to 0.45 with H.sub.2SO.sub.4; [0215] washing with water recovered mainly from the third wash and with pH adjusted to 0.82 with H.sub.2SO.sub.4; and [0216] last washing with industrial water;

[0217] f) pressing the washed cake obtained in step (e) in the filter press itself up to 6×10.sup.5 Pa (6 bar);

[0218] g) dewatering of the cake by displacement with compressed air;

[0219] h) drying of the cake in a dryer; and

[0220] i) packaging of the lignin dried in the dryer.

[0221] The lignin obtained by this process has as main characteristics an ash content of 0.39% and a pH of 3.44.

Example 4

[0222] In this example a process for extracting alkaline lignin from the black liquor according to the present invention is described, in which displacement washing occurred and the optional resuspension step was not performed. Said process comprises the following steps:

[0223] a) acidification of black liquor with CO.sub.2 up to pH 9.52;

[0224] b) adjusting the temperature to 74° C. and maintaining this temperature for 30 minutes;

[0225] c) cooling to a temperature of 37.7° C.;

[0226] d) filtering the product obtained in step (c) in a filter press and obtaining the first lignin cake;

[0227] e) countercurrent washing in the filter of cake obtained in step (d) (product retained from filtration), by means of the following washing sequence: [0228] washing with the water recovered from the second wash with sodium sulfate solution adjusted to a conductivity of 49.0 mS/cm; [0229] washing with the water recovered from the third wash with sodium sulfate solution adjusted to a conductivity of 28.5 mS/cm; and [0230] last washing with industrial water;

[0231] f) pressing the washed cake obtained in step (e) in the filter press itself up to 6×10.sup.5 Pa (8 bar);

[0232] g) dewatering of the cake by displacement with compressed air; and

[0233] h) drying the cake in a dryer.

[0234] The lignin obtained by this process has as main characteristics an ash content of 2.63% and a pH of 9.15.