FLUOROSILICONE SURFACTANT, PREPARATION METHOD THEREFOR AND APPLICATION THEREOF

Abstract

A fluorosilicone surfactant, and a preparation method and a use thereof are provided. The preparation method of the fluorosilicone surfactant includes: mixing alkynol or a derivative thereof, an allylpolyether, and an alkenyl fluorine-containing monomer with hydrogen-containing silicone oil to allow a hydrosilylation reaction, where a structural formula of the hydrogen-containing silicone oil includes at least three Si—H bonds. The fluorosilicone surfactant prepared by the present disclosure has both excellent wettability and low-foaming performance.

Claims

1. A preparation method of a fluorosilicone surfactant, comprising: mixing alkynol or a derivative the alkynol, an allylpolyether, and an alkenyl fluorine-containing monomer with a hydrogen-containing silicone oil to allow a hydrosilylation reaction, wherein the alkynol or the derivative the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer are grafted to the hydrogen-containing silicone oil to obtain the fluorosilicone surfactant, wherein a structural formula of the hydrogen-containing silicone oil comprises at least three Si—H bonds; and alkenyl in the alkenyl fluorine-containing monomer is selected from the group consisting of vinyl and propenyl.

2. The preparation method of the fluorosilicone surfactant according to claim 1, comprising: mixing a mixture of the alkynol or the derivative the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer with the hydrogen-containing silicone oil to allow the hydrosilylation reaction to obtain the fluorosilicone surfactant; or mixing a mixture of the alkynol or the derivative of the alkynol and the allylpolyether with the hydrogen-containing silicone oil to allow the hydrosilylation reaction to obtain an intermediate, and mixing the intermediate with the alkenyl fluorine-containing monomer to allow the hydrosilylation reaction to obtain the fluorosilicone surfactant, wherein a molar ratio of multiple bonds in the alkynol or the derivative the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer to the at least three Si—H bonds in the hydrogen-containing silicone oil is (0.9-1.1):1.

3. The preparation method of the fluorosilicone surfactant according to claim 1, wherein the hydrogen-containing silicone oil has a hydrogen content of 0.2% to 1.5% and an average molecular weight of 500 to 3,000.

4. The preparation method of the fluorosilicone surfactant according to claim 1, wherein the alkynol has a structural formula of ##STR00013## wherein z and g are each an integer, and 0≤z≤4 and 0≤g≤4; R″ is C.sub.0-C.sub.12 alkyl; and .sub.1R″ is C.sub.0-C.sub.12 alkyl; the alkenyl fluorine-containing monomer has a structural formula of ##STR00014## wherein R is C.sub.2-C.sub.12 alkyl; R′″ is selected from the group consisting of vinyl and propenyl; e is 0 or 1; and Rf is fluorine-substituted alkyl; the allylpolyether has a structural formula of ##STR00015## wherein x and y are each an integer, and 0≤x≤12 and 0≤y≤14; when one of x and y is 0, the other one of x and y is greater than 0; and R′ is one selected from the group consisting of hydrogen, methyl, ethyl, and butyl; and the hydrogen-containing silicone oil has a structural formula of ##STR00016## wherein a≥0; b+c+d≥3; a, b, c, and d are each an integer; and b, c, and d are each a positive integer.

5. The preparation method of the fluorosilicone surfactant according to claim 1, comprising: in the presence of a catalyst and a solvent, slowly adding a mixture of the alkynol or the derivative the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer to the hydrogen-containing silicone oil at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h.

6. The preparation method of the fluorosilicone surfactant according to claim 1, comprising: in the presence of a solvent and a catalyst, slowly adding a mixture of the alkynol or the derivative the alkynol and the allylpolyether to the hydrogen-containing silicone oil at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h to obtain an intermediate, and slowly adding the intermediate to the alkenyl fluorine-containing monomer at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h.

7. The preparation method of the fluorosilicone surfactant according to claim 5, wherein the catalyst is selected from the group consisting of a Karstedt's catalyst and chloroplatinic acid; and the solvent is xylene.

8. A fluorosilicone surfactant prepared by the preparation method according to claim 1.

9. The fluorosilicone surfactant according to claim 8, wherein the fluorosilicone surfactant has a structural formula of ##STR00017## wherein 1) a≥0; b+c +d≥3; a, b, c, and d are each an integer; and b, c, and d are each a positive integer; 2) x and y are each an integer, and 0≤x≤12 and 0≤y≤14; when one of x and y is 0, the other one of x and y is greater than 0; and R′ is aw.sub.y—one selected from the group consisting of hydrogen, methyl, ethyl, and butyl; and ##STR00018##

3. A is wherein Rf is fluorine-substituted alkyl; R is C.sub.2-C.sub.12 alkyl; e is 0 or 1; and .sub.1R′″ is ethyl or propyl; and B is ##STR00019## wherein z and g are each an integer, and 0≤≤4 and 0≤g≤4; and .sub.1R″ and R″ are each C.sub.0-C.sub.12 alkyl.

10. A method of use of the fluorosilicone surfactant according to claim 8 as an anti-foaming wetting agent in a coating film.

11. The preparation method of the fluorosilicone surfactant according to claim 6, wherein the catalyst is selected from the group consisting of a Karstedt's catalyst and chloroplatinic acid; and the solvent is xylene.

12. The fluorosilicone surfactant according to claim 8, wherein the preparation method of the fluorosilicone surfactant comprises: mixing a mixture of the alkynol or the derivative of the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer with the hydrogen-containing silicone oil to allow the hydrosilylation reaction to obtain the fluorosilicone surfactant; or mixing a mixture of the alkynol or the derivative of the alkynol and the allylpolyether with the hydrogen-containing silicone oil to allow the hydrosilylation reaction to obtain an intermediate, and mixing the intermediate with the alkenyl fluorine-containing monomer to allow the hydrosilylation reaction to obtain the fluorosilicone surfactant, wherein a molar ratio of multiple bonds in the alkynol or the derivative of the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer to the at least three Si—H bonds in the hydrogen-containing silicone oil is (0.9-1.1):1.

13. The fluorosilicone surfactant according to claim 8, wherein the hydrogen-containing silicone oil used in a preparation of the fluorosilicone surfactant has a hydrogen content of 0.2% to 1.5% and an average molecular weight of 500 to 3,000.

14. The fluorosilicone surfactant according to claim 8, wherein in a preparation of the fluorosilicone surfactant, the alkynol has a structural formula of ##STR00020## wherein z and g are each an integer, and 0≤z≤4 and 0≤g≤4; R″ is C.sub.0-C.sub.12 alkyl; and .sub.1R″ is C.sub.0-C.sub.12 alkyl; the alkenyl fluorine-containing monomer has a structural formula of ##STR00021## wherein R is C.sub.2-C.sub.12 alkyl; R′″ is selected from the group consisting of vinyl and propenyl; e is 0 or 1; and Rf is fluorine-substituted alkyl; the allylpolyether has a structural formula of ##STR00022## wherein x and y are each an integer, and 0<x<12 and 0<y<14; when one of x and y is 0, the other one of x and y is greater than 0; and R′ is one selected from the group consisting of hydrogen, methyl, ethyl, and butyl; and the hydrogen-containing silicone oil has a structural formula of ##STR00023## wherein a≥0; b+c+d≥3; a, b, c, and d are each an integer; and b, c, and d are each a positive integer.

15. The fluorosilicone surfactant according to claim 8, wherein the preparation method of the fluorosilicone surfactant comprises: in the presence of a catalyst and a solvent, slowly adding a mixture of the alkynol or the derivative of the alkynol, the allylpolyether, and the alkenyl fluorine-containing monomer to the hydrogen-containing silicone oil at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h.

16. The fluorosilicone surfactant according to claim 8, wherein the preparation method of the fluorosilicone surfactant comprises: in the presence of a solvent and a catalyst, slowly adding a mixture of the alkynol or the derivative of the alkynol and the allylpolyether to the hydrogen-containing silicone oil at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h to obtain an intermediate, and slowly adding the intermediate to the alkenyl fluorine-containing monomer at 75° C. to 160° C. to allow the hydrosilylation reaction for 2 h to 19 h.

17. The fluorosilicone surfactant according to claim 15, wherein the catalyst is selected from the group consisting of a Karstedt's catalyst and chloroplatinic acid; and the solvent is xylene.

Description

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0036] The present disclosure will be further described below in conjunction with specific examples.

[0037] It should be noted that, unless otherwise specified, the raw materials used in the technical solutions provided by the present disclosure are all prepared by conventional means or purchased from commercial sources.

[0038] A preparation method of a fluorosilicone surfactant is provided, including: mixing alkynol or a derivative thereof, an allylpolyether, and an alkenyl fluorine-containing monomer with hydrogen-containing silicone oil to allow a hydrosilylation reaction, such that the alkynol or the derivative thereof, the allylpolyether, and the alkenyl fluorine-containing monomer are grafted to the hydrogen-containing silicone oil to obtain the fluorosilicone surfactant. The structural formula of the hydrogen-containing silicone oil includes at least three Si—H bonds. Alkenyl in the alkenyl fluorine-containing monomer is selected from the group consisting of vinyl and propenyl.

[0039] Preferably, the preparation method of a fluorosilicone surfactant may include: mixing a mixture of the alkynol or the derivative thereof, the allylpolyether, and the alkenyl fluorine-containing monomer with the hydrogen-containing silicone oil to allow a hydrosilylation reaction to obtain the fluorosilicone surfactant; or mixing a mixture of the alkynol or the derivative thereof and the allylpolyether with the hydrogen-containing silicone oil to allow a hydrosilylation reaction to obtain an intermediate, and mixing the intermediate with the alkenyl fluorine-containing monomer to allow a hydrosilylation reaction to obtain the fluorosilicone surfactant. The molar ratio of multiple bonds in the alkynol or the derivative thereof, the allylpolyether, and the alkenyl fluorine-containing monomer to the Si—H bonds in the hydrogen-containing silicone oil is (0.9-1.1):1. The hydrogen-containing silicone oil has a hydrogen content of 0.2% to 1.5% and an average molecular weight of preferably 500 to 3,000. The molar ratio of the multiple bonds to the Si—H bonds in the hydrogen-containing silicone oil is (0.9-1.1):1, such that the reaction is complete and thorough.

[0040] Preferably, the preparation method of a fluorosilicone surfactant may include: in the presence of a catalyst and a solvent, slowly adding the mixture of the alkynol or the derivative thereof, the allylpolyether, and the alkenyl fluorine-containing monomer to the hydrogen-containing silicone oil at 75° C. to 160° C. to allow a reaction for 2 h to 19 h, preferably 3 h to 19 h, and most preferably 10 h to 19 h. The reaction time of 3 h to 19 h is favorable because the reaction is mostly likely complete.

[0041] Of course, after the reaction is completed, the solvent and unreacted monomer can be removed under vacuum.

[0042] In Examples 1 to 6, unless otherwise specified, a structural formula of the alkynol is the first general formula; a structural formula of the alkenyl fluorine-containing monomer is the second general formula; a structural formula of the allylpolyether is the third general formula; a structural formula of the hydrogen-containing silicone oil is the fourth general formula; and a structural formula of the fluorosilicone surfactant is the fifth general formula.

[0043] In Examples 1 to 6, the hydrogen content of the hydrogen-containing silicone oil refers to a mass percentage content of hydrogen from the silicon-hydrogen bonds of the hydrogen-containing silicone oil in the hydrogen-containing silicone oil.

[0044] In Examples 1 to 6, a molecular weight of the allylpolyether refers to an average molecular weight because there is a small amount of impurity in addition to the main part in the third general formula (values of x and y may be biased (values of x and y will float up and down in rare cases)). The molecular weight can be a molecular weight provided by a supplier of a product when the product is purchased. A molecular weight of the hydrogen-containing silicone oil also refers to an average molecular weight. A chloroplatinic acid solution is an aqueous chloroplatinic acid solution with a chloroplatinic acid content of 8%. .sub.1R″ is straight-chained or branched alkyl, and R″ is straight-chained or branched alkyl.

[0045] In the third general formula of the present disclosure, x and y refer to x and y of the main part.

Example 1

[0046] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0047] 2) A temperature in the four-necked flask was lowered to 75° C. 220 g (0.11 mol) of hydrogen-containing silicone oil (with a hydrogen content of 0.2% and an average molecular weight of 2,000) was added to the four-necked flask. A mixture of 130 g (0.20 mol) of an allylpolyether (the third general formula, where x was 0, y was about 14, and R′ was methyl, which had an average molecular weight of 650 and was also called allyl polyethylene glycol monomethyl ether), 40.2 g (0.12 mol) of alkynol (the first general formula, where z was 2, g was 2, .sub.1R″ was C.sub.4 alkyl, and R″ was C.sub.4 alkyl, which was also known as tetraethoxydecynediol and had a molecular weight of 346), 23.6 g (0.10 mol) of hexafluorobutyl acrylate (HFBA) (with a molecular weight of 236), and 0.0414 g of a chloroplatinic acid solution was evenly added dropwise for 12 h to the four-necked flask. The resulting reaction system was gradually heated to 100° C. and kept at 90° C. to 110° C. for 3 h. .sub.1R″ and R″ could both be —CH.sub.2—CH.sub.2—CH.sub.2—CH.sub.2—.

[0048] 3) Then the reaction system was heated to 120° C. and kept at the temperature for 4 h, and then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 100° C. to 120° C. to remove the solvent and unreacted monomer to obtain a sample 1.

[0049] The HFBA had a structural formula of

##STR00009##

Example 2

[0050] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0051] 2) A temperature in the four-necked flask was lowered to 95° C. A mixture of 110 g (0.10 mol) of allyl polyethylene glycol polypropylene glycol monobutyl ether (the third general formula, where x was about 12, y was about 9, and R′ was butyl, which had an average molecular weight of 1,100), 28.4 g (0.25 mol) of hexynediol (the first general formula, where z and g were both 0, .sub.1R″ was —CH.sub.2—CH.sub.2—, and R″ was —CH.sub.2—CH.sub.2—, which had a molecular weight of 114), 30 g (0.10 mol) of octafluoropentyl acrylate (OFPA) (with a molecular weight of 286), and 0.0139 g of a Karstedt's catalyst was added to the four-necked flask. 110 g (0.07 mol) of hydrogen-containing silicone oil (with a hydrogen content of 0.4% and an average molecular weight of 1,500) was evenly added dropwise for 8 h to the four-necked flask. The resulting reaction system was gradually heated to 100° C. and kept at 90° C. to 110° C. for 3 h.

[0052] 3) Then the reaction system was heated to 130° C. and kept at the temperature for 4 h, and then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 100° C. to 130° C. to remove the solvent and unreacted monomer to obtain a sample 2.

[0053] The OFPA had a structural formula of

##STR00010##

Example 3

[0054] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0055] 2) A temperature in the four-necked flask was lowered to 85° C., then 100 g (0.03 mol) of hydrogen-containing silicone oil (with a hydrogen content of 0.6% and an average molecular weight of 3,000) was added to the four-necked flask. A mixture of 170 g (0.20 mol) of an allylpolyether (the second general formula, where x was about 8, y was about 8, and R′ was hydrogen, which had a molecular weight of 850), 78.6 g (0.30 mol) of tetraethoxybutynediol (the first general formula, where .sub.1R″ was —CH.sub.2—, R″ was —CH.sub.2—, and z and g were both 2, which had a molecular weight of 262), 43.2 g (0.10 mol) of perfluorooctyl methacrylate (PFOMA) (with a molecular weight of 432), and 0.0784 g of a chloroplatinic acid solution was evenly added dropwise for 12 h to the four-necked flask. The resulting reaction system was gradually heated to 145° C. and kept at 140° C. to 150° C. for 3 h.

[0056] The PFOMA had a structural formula of

##STR00011##

[0057] 3) Then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 140° C. to 150° C. to remove the solvent and unreacted monomer to obtain a sample 3.

Example 4

[0058] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0059] 2) A temperature in the four-necked flask was lowered to 105° C., then a mixture of 105 g (0.30 mol) of allyl polyethylene glycol butyl ether (the third general formula, where x was 0, y was about 5 or 6, and R′ was butyl, which had an average molecular weight of 350), 425.4 g (0.77 mol) of octaethoxydodecynediol (the first general formula, where .sub.1R″ was C.sub.5 alkyl, R″ was C.sub.5 alkyl, and z and g were both 4, which had a molecular weight of 550), 64.8 g (0.15 mol) of PFOMA (with a molecular weight of 432), and 0.0705 g of a chloroplatinic acid solution was added to the four-necked flask. 137.5 g (0.14 mol) of hydrogen-containing silicone oil (with an average molecular weight of 1,000 and a hydrogen content of 0.8%) was evenly added dropwise for 8 h. The resulting reaction system was gradually heated to 150° C. and kept at 150° C. to 160° C. for 3 h. .sub.1R″ and R″ could be both —CH.sub.2CH.sub.2CH.sub.2CH.sub.2CH.sub.2—.

[0060] 3) Then vacuum-pumping was conducted for 30 min at a vacuum degree of −0.09 or higher and a temperature of 150° C. to 160° C. to remove the solvent and unreacted monomer to obtain a sample 4.

Example 5

[0061] 1) 200 g of xylene was added to a four-necked flask, and heated to reflux at 140° C. for 2 h to remove water.

[0062] 2) A temperature in the four-necked flask was lowered to 115° C., then 100.0 g (0.20 mol) of hydrogen-containing silicone oil (with a hydrogen content of 1.0% and a molecular weight of 500) was added to the four-necked flask. A mixture of 75.0 g (0.10 mol) of allyl polypropylene glycol monomethyl ether (the third general formula, where x was about 12, y was 0, and R′ was methyl, which had a molecular weight of about 750), 161.6 g (0.80 mol) of diethoxyhexynediol (the first general formula, .sub.1R″ was —CH.sub.2—CH.sub.2—, R″ was —CH.sub.2—CH.sub.2—, and z and g were both 1, which had a molecular weight of 202), 30.8 g (0.20 mol) of trifluoroethyl acrylate (TFEA) (with a molecular weight of 154), and 0.0367 g of a chloroplatinic acid solution was evenly added dropwise for 6 h to the four-necked flask. The resulting reaction system was gradually heated to 130° C. and kept at 120° C. to 140° C. for 3 h. The TFEA had a structural formula of

##STR00012##

[0063] 3) Then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 120° C. to 140° C. to remove the solvent and unreacted monomer to obtain a sample 5.

Example 6

[0064] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0065] 2) A temperature in the four-necked flask was lowered to 75° C. 80 g (0.11 mol) of hydrogen-containing silicone oil (with a hydrogen content of 1.5% and an average molecular weight of 750) was added to the four-necked flask. A mixture of 120 g (0.30 mol) of ally! polyethylene glycol monobutyl ether (the third general formula, where y was 6 or 7 and R′ was butyl, which had an average molecular weight of 400), 120 g (0.75 mol) of diethoxypropynediol (the first general formula, where .sub.1R″ was —CH.sub.2—, R″ was absent or was —CH.sub.2—, .sub.1R″ was absent, and z and g were both 1, which had a molecular weight of 160), 60.6 g (0.18 mol) of tridecafluoro-1-octene (with a molecular weight of 346), and 0.0381 g of a Karstedt's catalyst was evenly added dropwise for 6 h to the four-necked flask. The resulting reaction system was gradually heated to 100° C. and kept at 90° C. to 110° C. for 6 h. The tridecafluoro- 1-octene had a CAS number of 25291-17-2 and a structural formula of CF.sub.3(CF.sub.2).sub.5CH=CH.sub.2.

[0066] 3) Then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 120° C. to 140° C. to remove the solvent and unreacted monomer to obtain a sample 6.

[0067] The preparation methods of a fluorosilicone surfactant in Examples 1 to 6 can also be as follows: in the presence of a solvent and a catalyst, a mixture of alkynol or a derivative thereof and an allylpolyether is slowly added to hydrogen-containing silicone oil at 75° C. to 160° C. to allow a reaction for 2 h to 19 h (preferably 3 h to 19 h) to obtain an intermediate. The intermediate is slowly added to an alkenyl fluorine-containing monomer at 75° C. to 160° C. to allow a reaction for 2 h to 19 h (preferably 3 h to 19 h).

[0068] For example, in Example 4, the preparation method could be as follows:

[0069] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0070] 2) A temperature in the four-necked flask was lowered to 105° C. A mixture of 105 g (0.30 mol) of ally! polyethylene glycol butyl ether (the third general formula, where x was 0, y was about 5 or 6, and R′ was butyl, which had an average molecular weight of 350), 425.4 g (0.77 mol) of octaethoxydodecynediol (the first general formula, where .sub.1R″ was C.sub.5 alkyl, R″ was C.sub.5 alkyl, and z and g were both 4, which had a molecular weight of 550), and 0.0705 g of a chloroplatinic acid solution was added to the four-necked flask, 137.5 g (0.14 mol) of hydrogen-containing silicone oil (with an average molecular weight of 1,000 and a hydrogen content of 0.8%) was evenly added dropwise for 8 h. The resulting reaction system was gradually heated to 150° C. and kept at 150° C. to 160° C. for 2 h to 11 h to obtain an intermediate. The system was cooled to 105° C., and 64.8 g (0.15 mol) of PFOMA (with a molecular weight of 432) was evenly added dropwise for 8 h to the four-necked flask. The resulting reaction system was gradually heated to 150° C. and kept at 150° C. to 160° C. for 2 h to 11 h.

[0071] 3) Then vacuum-pumping was conducted for 30 min at a vacuum degree of -0.09 or higher and a temperature of 150° C. to 160° C. to remove the solvent and unreacted monomer to obtain a sample 4.

[0072] For example, in Example 6, the preparation method could be as follows:

[0073] 1) 200 g of xylene was added to a four-necked flask and heated to reflux at 140° C. for 2 h to remove water.

[0074] 2) A temperature in the four-necked flask was lowered to 75° C. 80 g (0.11 mol) of hydrogen-containing silicone oil (with a hydrogen content of 1.5% and an average molecular weight of 750) was added to the four-necked flask. A mixture of 120 g (0.30 mol) of allyl polyethylene glycol monobutyl ether (the third general formula, where y was about 6 or 7 and R′ was butyl, which had an average molecular weight of 400), 120 g (0.75 mol) of diethoxypropynediol (the first general formula, where .sub.1R″ was —CH.sub.2—, R″ was absent or was —CH.sub.2—, .sub.1R″ was absent, and z and g were both 1, which had a molecular weight of 160), and 0.0381 g of a Karstedt's catalyst was evenly added dropwise for 6 h to the four-necked flask. The resulting reaction system was gradually heated to 100° C. and kept at 90° C. to 110° C. for 6 h to obtain an intermediate. The system was cooled to 75° C., and 60.6 g (0.18 mol) of tridecafluoro-1-octene (with a molecular weight of 346) was evenly added dropwise for 6 h to the four-necked flask. The resulting reaction system was gradually heated to 100° C. and kept at 90° C. to 110° C. for 6 h.

[0075] 3) Then vacuum-pumping was conducted for 1 h at a vacuum degree of -0.09 or higher and a temperature of 120° C. to 140° C. to remove the solvent and unreacted monomer to obtain a sample 6.

Result Test

Comparative Test

[0076] Step 1) 10 containers were taken, and 85 g of water-based acrylic resin (trade brand: DSM; and model: Neocryl XK14) and 15 g of deionized water were added to each container.

[0077] Step 2) 10 samples that were each of 0.3 g were taken and respectively added to the containers.

[0078] Step 3) Materials in each container were thoroughly mixed and allowed to stand for 2 h, and then the anti-foaming ability, wettability, appearance, and leveling property were tested.

[0079] The 10 samples were respectively: six products prepared in Examples 1 to 6 (product 1, product 2, product 3, product 4, product 5, and product 6) and four typical wetting agent products on the market (commodity 1, commodity 2, commodity 3, and commodity 4). The four typical products on the market were all commercially-available polyether-modified silicones.

[0080] The liquid samples in the containers were respectively liquid sample 1 (the product 1 was added), liquid sample 2 (the product 2 was added), liquid sample 3 (the product 3 was added), liquid sample 4 (the product 4 was added), liquid sample 5 (the product 5 was added), liquid sample 6 (the product 6 was added), liquid sample 7 (the commodity 1 was added), liquid sample 8 (the commodity 2 was added), liquid sample 9 (the commodity 3 was added), and liquid sample 10 (the commodity 4 was added).

Anti-Foaming Ability Test

[0081] The liquid samples 1 to 10 in the containers were each shaken for 10 min on a shaker and then respectively poured into 10 graduated bottles (which were cylindrical and had a volume of 100 mL and a height of 6 cm). An initial foam height was recorded, and then a foam height was recorded at 2 h and 24 h. Experimental results were shown in Table 1.

TABLE-US-00001 TABLE 1 Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid sample sample sample sample sample sample sample sample sample sample 1 Sample 1 2 3 4 5 6 7 8 9 0 Initial foam h 75 65 60 70 68 80 100 90 85 95 eight (mm) 2 h 55 58 55 50 50 58 80 85 70 65 (mm) 24 h 52 53 50 50 50 51 58 55 53 52 (mm)

[0082] The data in Table 1 shows that the fluorosilicone surfactant prepared by the present disclosure is low-foam forming and is much superior to products on the market in this aspect. The initial foam height and the foam height at 2 h of the fluorosilicone surfactant are significantly lower than that of the commercial wetting agents on the market, indicating that the product prepared by the present disclosure is low-foam forming.

Static Surface Tension Test

[0083] A ring-type static surface tensiometer (model: SFZL-A1, product number: 20170501003) was used to test a surface tension. The smaller the reading, the lower the surface tension. Experimental results were shown in Table 2.

TABLE-US-00002 TABLE 2 Liquid Liquid s Liquid s Liquid s Liquid s Liquid s Liquid s Liquid s Liquid s Liquid s sample Sample ample 1 ample 2 ample 3 ample 4 ample 5 ample 6 ample 7 ample 8 ample 9 10 Static 32.5 31.3 31.0 32.2 32.8 32.4 32.9 33.8 32.4 33.7 surface tension (mN/m)

[0084] The data in Table 1 shows that the fluorosilicone surfactant prepared by the present disclosure has a very low surface tension and high wettability, which can meet market needs. Most of the samples have a lower surface tension than the products on the market, which can well meet the needs.

Compatibility, Gloss, and State (Edge Shrinking) of Coating Films

[0085] 1. Fabrication of a scraper: Each sample was coated on a flat plate and pressed with a film maker (which was a hollow object with left and right sides and a top surface). The film maker was pulled up to obtain a coating film with a thickness of 100 pm. After the coating film was dried, various properties of the coating film (which was a dry film) were measured. A process of fabricating a dry film is also called a scraper fabrication process.

[0086] The state of the dry film was observed, the compatibility was determined, and then the gloss was measured. Experimental results are shown in Table 3. Compatibility determination criteria: The permeability of a coating film was classified into levels 1 to 5, where level 5 represented the highest permeability and level 1 represented the lowest permeability. The gloss was measured by a specular gloss meter with an incident angle of 60°. The higher the gloss, the better the compatibility of the coating film. The smaller the shrinkage width, the better the wettability of the coating film.

TABLE-US-00003 TABLE 3 Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid sample sample sample 3 sample sample sample sample sample sample sample 1 2 4 5 6 7 8 9 10 Permeability 4 4 4 5 5 5 5 4 5 4 (level) Shrinkage 2 2 2 1 0 1 4 3 2 3 width (mm) Gloss 85 86 84 88 85 87 82 80 84 83 (degree)

[0087] It can be seen from Table 3 that the samples of the present disclosure all have excellent compatibility and wettability.

[0088] 2. Two parts were taken from each of the liquid samples 1 to 10, and an antifoaming agent BYK022 was added to each part, such that a mass fraction of the antifoaming agent BYK022 in one part was 0.2% (which was recorded as liquid sample 1#) and a mass fraction of BYK022 in the other part was 0.4% (which was recorded as liquid sample 2#). Liquid samples 1# and 2#190 were each used to fabricate a scraper, and the anti-shrinkage ability of the wetting agent was observed. The more the number of shrinkage cavities on the coating film, the worse the wettability of the wetting agent. Experimental results are shown in Table 4.

TABLE-US-00004 TABLE 4 Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Liquid Sample sample 1 sample 2 sample 3 sample 4 sample 5 sample 6 sample 7 sample 8 sample 9 sample 10 Liquid 0 0 0 0 0 0 2 1 2 3 sample 1 # Liquid 2 0 2 0 0 1 7 6 3 5 sample 2 #

[0089] It can be seen from Table 4 that, after the antifoaming agent is added, the products in Examples 1 to 6 of the present disclosure exhibit a significantly better anti-shrinkage ability than the wetting agents on the market, indicating that the products in Examples 1 to 6 have excellent wettability and are obviously superior to the products on the market. In the presence of the antifoaming agent, the products of the present disclosure still exhibit prominent anti-shrinkage ability, that is, prominent wettability, and thus exhibit strong destruction resistance, which can well resist the interference of other components.

[0090] It should be noted that C.sub.0 in the present disclosure refers to no carbon.

[0091] The allylpolyether in the present disclosure can be purchased from Nantong Chenrun Chemical Co., Ltd. or Hangzhou Danwei Technology Co., Ltd., and can also be purchased from other companies.

[0092] The technical solutions provided by the examples of the present disclosure are described in detail above, and the principles and implementations of the examples of the present disclosure are described herein by using specific examples. The description of the above examples is provided merely to help explain the principles of the examples of the present disclosure. In addition, those of ordinary skill in the art can make changes to the specific implementations and applications according to the examples of the present disclosure. In conclusion, the content of this specification should not be construed as limiting the present disclosure.