Process for producing fluorine-containing combined salt

Abstract

Disclosed is a process for producing a fluorine-containing complex salt, characterized by that, on a reaction mother liquor containing a plurality of cation species and a fluoroanion in a state that they have been dissolved in a solvent, a trigger for accelerating decomposition of the fluoroanion is allowed to act, thereby precipitating a complex salt containing a plurality of cation species and fluorine, as a solid, from the reaction mother liquor. According to this process, it is possible to produce a monodispersed fluorine-containing complex salt with uniform particle size and shape.

Claims

1. A process for producing a fluorine-containing complex salt comprising the step of triggering a reaction on a reaction mother liquor containing a plurality of cation species and a fluoroanion in a state that they have been dissolved in a solvent, wherein triggering the reaction applies energy to the reaction mother liquor, changes acidity of the reaction mother liquor, or both, thereby accelerating decomposition of the fluoroanion and precipitating a complex salt containing a plurality of cation species and fluorine, as a solid, from the reaction mother liquor, wherein the fluoroanion has an A-F bond, wherein A is at least one element selected from the group consisting of Al, Ti, B, Si, P, S, As, Se, Sb and Te.

2. The process for producing a fluorine-containing complex salt as claimed in claim 1, wherein at least one species of the plurality of cation species is a monovalent cation of an element of group 1, an at least divalent cation of an element of group 2, or an at least trivalent cation of an element of group 3 to group 13.

3. The process for producing a fluorine-containing complex salt as claimed in claim 1, wherein the fluoroanion is at least one selected from the group consisting of TiF.sub.6.sup.2, AlF.sub.6.sup.3, BF.sub.4.sup., SiF.sub.6.sup.2, PF.sub.6.sup., PO.sub.3F.sub.2.sup., PO.sub.2F.sub.2.sup., and SO.sub.3F.sup..

4. The process for producing a fluorine-containing complex salt as claimed in claim 1, wherein the substance for changing acidity of the reaction mother liquor is at least one selected from the group consisting of an acid, a base, and a chemical species that generates an acid or base by applying energy.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is an electron microscope photograph showing one example of a fluorine-containing complex salt produced by the production process of the present invention, and

(2) FIG. 2 is an electron microscope photograph showing one example of a fluorine-containing complex salt produced by a production process for comparison.

DETAILED DESCRIPTION

(3) The present invention is a process for producing a fluorine-containing complex salt, characterized by that, on a reaction mother liquor containing a plurality of cation species and fluoroanions in a state that they have been dissolved in a solvent, a trigger for accelerating decomposition of the fluoroanions is allowed to act, thereby precipitating a complex salt containing a plurality of cation species and fluorine, as a solid, from the reaction mother liquor.

(4) It is preferable that major constituent cations of the fluorine-containing complex salt as the target for synthesis are hard acids defined in Pearson's HSAB concept. That is, it is preferable that they are cations that have a localized positive charge and a low polarizability. In the case of an element capable of taking a plurality of valences, a cation having a larger positive charge is preferable. In the case of cations of the same group and the same valence, one having a smaller ionic radius is preferable. Specifically, it is preferable to contain at least one selected from onium ions, monovalent cations of elements of group 1, at least divalent cations of elements of group 2, and at least trivalent cations of elements of groups 3 to 13.

(5) As the onium ions, for example, NH.sub.4.sup.+ can be mentioned. As the monovalent cations of elements of group 1, it is possible to mention, for example, H.sup.+, Li.sup.+, Na.sup.+, K.sup.+ and Rb.sup.+. As the at least divalent cations of elements of group 2, it is possible to mention, for example, Be.sup.2+, Mg.sup.2+, Ca.sup.2+, Sr.sup.2+, Ba.sup.2+, and Ra.sup.2+.

(6) As the at least trivalent cations of elements of groups 3 to 13, it is possible to mention Sc.sup.3+, Y.sup.3+, La.sup.3+, Ce.sup.3+, Ce.sup.4+, Pr.sup.3+, Pr.sup.4+, Nd.sup.3+, Pm.sup.3+, Sm.sup.3+, Eu.sup.3+, Gd.sup.3+, Tb.sup.3+, Tb.sup.4+, Dy.sup.3+, Ho.sup.3+, Er.sup.3+, Tm.sup.3+, Yb.sup.3+, Lu.sup.3+, Ac.sup.3+, Th.sup.4+, Pa.sup.4+, Pa.sup.5+, U.sup.3+, U.sup.4+, U.sup.5+, U.sup.6+, Np.sup.3+, Np.sup.4+, Np.sup.5+, Np.sup.6+, Np.sup.7+, Pu.sup.3+, Pu.sup.4+, Pu.sup.5+, Pu.sup.6+, Pu.sup.7+, Ti.sup.3+, Ti.sup.4+, Zr.sup.3+, Zr.sup.4+, Hf.sup.3+, Hf.sup.4+, V.sup.3+, V.sup.4+, V.sup.5+, Nb.sup.3+, Nb.sup.4+, Nb.sup.5+, Ta.sup.3+, Ta.sup.4+, Ta.sup.5+, Cr.sup.3+, Cr.sup.4+, Cr.sup.5+, Cr.sup.6+, Mo.sup.3+, Mo.sup.4+, Mo.sup.5+, Mo.sup.6+, W.sup.3+, W.sup.4+, W.sup.5+, W.sup.6+, Mn.sup.3+, Mn.sup.4+, Mn.sup.5+, Mn.sup.6+, Mn.sup.7+, Tc.sup.4+, Tc.sup.5+, Tc.sup.6+, Tc.sup.7+, Re.sup.4+, Re.sup.6+, Fe.sup.3+, Fe.sup.4+, Fe.sup.6+, Ru.sup.3+, Ru.sup.4+, Ru.sup.6+, Ru.sup.8+, Os.sup.3+, Os.sup.4+, Os.sup.5+, Os.sup.6+, Os.sup.7+, Os.sup.8+, Co.sup.3+, Co.sup.4+, Rh.sup.3+, Rh.sup.4+, Rh.sup.5+, Rh.sup.6+, Ir.sup.3+, Ir.sup.4+, Ir.sup.6+, Ni.sup.3+, Ni.sup.4+, Ni.sup.5+, Pt.sup.4+, Pt.sup.5+, Pt.sup.6+, Cu.sup.3+, Al.sup.3+, Ga.sup.3+, In.sup.3+, and Tl.sup.3+.

(7) Furthermore, it is more preferable to contain at least one of at least divalent cations of elements of group 2 and at least trivalent cations of elements of group 3 and Al, Ti, V, Cr, Mn, Fe, Co, and Ni.

(8) The solvent contained in the reaction mother liquor is not particularly limited, as long as it is capable of dissolving the raw material cations. Aqueous and nonaqueous ones are both usable. In particular, ones having polarity are preferable from the side of solubility of the raw material cations. As examples of the polar solvent, it is possible to mention water, alcohol, glycols such as ethylene glycol and PEG, and glycerol. It is also possible to use an acid liquid such as acetic acid. There is selected the optimum one as the solvent, from the viewpoints of the effects on the crystal particle size and the plane orientation of the crystal growth of the fluorine-containing complex salt and the degree of contamination of the fluorine-containing complex salt by the solvent and/or by-products, in addition to the degree of solubility of cations as mentioned above. From the viewpoint of cost, aqueous ones are the most preferable.

(9) As counter anions of the raw material cations, it is possible to select acetate, chloride, hydroxide, nitrate, sulfate, etc. It is preferable to select a counter anion having a high solubility corresponding to the cation species to be used. For example, in the case of Mg, solubility of the hydroxide is low. In the case of Ba, solubility of the sulfate is low. Therefore, in the case of producing BaMgF.sub.4, acetates, chlorides and nitrates are preferable as the raw materials.

(10) As the fluoroanions, one having A-F bond (A is a typical element) is preferable. In particular, it is more preferable that A is at least one element selected from the group consisting of Al, Ti, B, Si, P, S, As, Se, Sb, and Te. It is more preferable that the above A is at least one element selected from the group consisting of B, Si, P, S, As, Se, Sb, and Te. It is particularly preferable that the above A is at least one element selected from the group consisting of B, Si, P, and S.

(11) As typical examples of specific anion species, it is possible to mention TiF.sub.6.sup.2, AlF.sub.6.sup.3, BF.sub.4.sup., SiF.sub.6.sup.2, PF.sub.6.sup., PO.sub.3F.sub.2.sup., PO.sub.2F.sub.2.sup., SO.sub.3F.sup., etc. It is more preferable that the fluoroanions are at least one selected from the group consisting of BF.sub.4.sup., SiF.sub.6.sup.2, PF.sub.6.sup., PO.sub.3F.sub.2.sup., PO.sub.2F.sub.2.sup., and SO.sub.3F.sup.. It is the most preferably BF.sub.4.sup. or PF.sub.6.sup.. In the case of producing the complex fluoride, it is preferable that the number of fluorine atoms becomes greater than the equivalence. This is because the yield may lower, or impurity phases or amorphous phases may be produced as by-products, if the number of fluorine atoms becomes less than the equivalence.

(12) As the trigger for accelerating decomposition of the fluoroanions, it is possible to use the application of an energy, such as heat, pressure, electromagnetic waves such as light and microwaves, etc., and the change of acidity of the reaction mother liquor by an action of a substance for changing acidity, such as acid and base. It is also possible to use a combination of these. Furthermore, in the reaction mother liquor, it is also possible to contain a chemical species that is decomposed by the application of energy, such as heat or electromagnetic waves, to generate acid or base, and apply the energy. As examples of the chemical species that are decomposed by applying energy to generate acid, it is possible to mention esters such as ethyl acetate, and photoacid generators such as benzophenones, acetophenones, diazonium salts, iodonium salts and sulfonium salts. As examples of a chemical species that is decomposed by applying energy to generate a base, it is possible to mention urea, hexamethylene tetramine, etc.

(13) In the case of using the above-mentioned chemical species, it is necessary to control the reaction conditions in order to prevent precipitation of by-products. For example, in the case of producing BaMgF.sub.4 by decomposing BF.sub.4.sup., a precipitate of magnesium hydroxide is precipitated as solid by making the reaction mother liquor strongly alkaline. Thus, it is necessary to use an acidic reaction mother liquor, and it is preferable to gradually weaken acidity (i.e., increase pH) of the liquid in order to accelerate decomposition of BF.sub.4.sup.. In this synthesis, however, the addition of urea may cause precipitation of a carbonate such as barium carbonate. In this synthesis, hexamethylene tetramine is preferable and can maintain the liquid after the decomposition at around neutrality even if it is added to large excess.

(14) In the case of applying energy to the reaction mother liquor as the trigger for accelerating decomposition of the fluoroanions, specifically, for example, the following methods can be mentioned.

(15) (1) In the case of accelerating decomposition of the fluoroanions only by applying energy to the reaction mother liquor

(16) (2) In the case of accelerating decomposition of the fluoroanions by containing acid or base as a substance for changing acidity in the reaction mother liquor and applying energy

(17) (3) In the case of accelerating decomposition of the fluoroanions by containing a chemical species, which generates acid or base by the application of energy, as a substance for changing acidity in the reaction mother liquor and applying energy.

(18) Furthermore, in the case of utilizing the change of acidity of the reaction mother liquor by the action of a substance for changing acidity as a trigger for accelerating decomposition of the fluoroanions, specifically, for example, the following methods can be mentioned.

(19) (4) In the case of accelerating decomposition of the fluoroanions by containing acid or base as a substance for changing acidity in the reaction mother liquor

(20) In the following, details of each of the above-mentioned specific examples are mentioned.

(21) (1) In the case of accelerating decomposition of the fluoroanions only by applying energy to the reaction mother liquor

(22) It is optional to apply energy to the reaction mother liquor containing a plurality of cation species and fluoroanions in a state that they have been dissolved in a solvent. Furthermore, it is optional that, while energy is applied to the reaction mother liquor containing a plurality of cation species in a state that they have been dissolved, the fluoroanions are mixed with the reaction mother liquor.

(23) By conducting the above treatment, a fluorine-containing complex salt is precipitated as a solid from the reaction mother liquor. When preparing the reaction mother liquor, it is preferable from the viewpoint of productivity to use both of heating and mechanical stirring, while trying to prevent the amount of the solvent from decreasing by a large amount by evaporation. In the case of applying energy by applying heat, it is preferable to conduct mechanical stirring too in order to avoid depletion of the solvent by evaporation or boiling and to maintain uniformity of the liquid. In the case of applying heat, it is preferable to maintain the temperature of the reaction mother liquor at a temperature of from 40 C. to the boiling point of the mother liquor. Furthermore, it is preferable to avoid depletion of the solvent by using a vapor reflux condensing mechanism or a pressure sealed container. In the case of applying energy by applying pressure, it is preferably a uniform pressurization on the entirety of the liquid phase, such as solvothermal method. In the case of applying energy by applying electromagnetic waves such as light and microwaves, it is preferable to uniformly apply electromagnetic waves to the inside of a container or circularly supply the reaction mother liquor to a section where electromagnetic waves are applied.

(24) Furthermore, the above assumes precipitation of a fluorine-containing complex salt by the reaction in the container, but it is also possible to precipitate a fluorine-containing complex salt in a condition that the reaction mother liquor has been uniformly applied onto a substrate. In this case, it is preferable that heat application is conducted to the substrate itself or uniformly conducted by a heater carrying the substrate, and it is preferable that pressure application is conducted to the container whole after putting the substrate into the container.

(25) Furthermore, it is also possible to uniformly apply electromagnetic waves onto the substrate, but it is also possible to selectively conduct that on only a place where the precipitation is conducted for the purpose of a patterning onto the substrate. It is optional to apply energy by combining energies such as heat, pressure, and electromagnetic waves such as light and microwaves.

(26) (2) In the case of accelerating decomposition of the fluoroanions by containing acid or base as a substance for changing acidity in the reaction mother liquor and applying energy

(27) As a method of containing acid or base in the reaction mother liquor, there is used a reagent kit comprising a reaction mother liquor containing a plurality of cation species and fluoroanions in a condition that they have been dissolved in a solvent, and the acid or base, and it is conducted by mixing them.

(28) Alternatively, there is used a reagent kit comprising a reaction mother liquor containing a plurality of cation species and the acid or base in a condition that they have been dissolved in a solvent, and fluoroanions, and it is conducted by mixing them.

(29) The application of energy may be conducted to either one or both of the above-mentioned reagent kit prior to the mixing. It may be conducted to the mixed liquid while mixing the reagent kit. It may be conducted to the reaction mother liquor after the mixing.

(30) By conducting the above treatment, a fluorine-containing complex salt is precipitated as a solid from the reaction mother liquor. In the case of applying energy by applying heat, it is preferable to conduct mechanical stirring too in order to avoid depletion of the solvent by evaporation or boiling and to maintain uniformity of the liquid. In the case of applying heat, it is preferable to maintain the temperature of the reagent prior to the mixing, its mixed liquid, or the reaction mother liquor at a temperature of from 40 C. to the boiling point of the liquor. Furthermore, it is preferable to avoid depletion of the solvent by using a vapor reflux condensing mechanism or a pressure sealed container. In the case of applying energy by applying pressure, it is preferably a uniform pressurization on the entirety of the liquid phase, such as solvothermal method. In the case of applying energy by applying electromagnetic waves such as light and microwaves, it is preferable to uniformly apply electromagnetic waves to the inside of a container or circularly supply the reagent prior to the mixing, its mixed liquid or the reaction mother liquor to a section where electromagnetic waves are applied.

(31) Furthermore, the above assumes precipitation of a fluorine-containing complex salt by the reaction in the container, but it is also possible to precipitate a fluorine-containing complex salt in a condition that the reaction mother liquor has been uniformly applied onto a substrate. In this case, it is preferable that heat application is conducted to the substrate itself or uniformly conducted by a heater carrying the substrate, and it is preferable that pressure application is conducted to the container whole after putting the substrate into the container. Furthermore, it is also possible to uniformly supply the acid, base or fluoroanions in a condition of vapor or mist to the entirety of the substrate.

(32) Furthermore, it is also possible to uniformly apply electromagnetic waves onto the substrate, but it is also possible to selectively conduct that on only a place where the precipitation is conducted for the purpose of a patterning onto the substrate. It is optional to apply energy by combining energies such as heat, pressure, and electromagnetic waves such as light and microwaves.

(33) In case that, even if acid or base is contained as a substance for changing acidity, the substance alone does not cause decomposition of the fluoroanions, it is preferable to previously contain the substance in the reaction mother liquor and then apply energy. For example, decomposition of PF.sub.6.sup. does not occur only by adding acetic acid. Therefore, after preparing a uniform mother liquor in which the acid has been contained, it is possible to apply energy to this. According to this method, it is possible to precipitate a more uniform, fluorine-containing complex salt as a solid. Therefore, it is preferable.

(34) (3) In the case of accelerating decomposition of the fluoroanions by containing a chemical species, which generates acid or base by the application of energy, as a substance for changing acidity in the reaction mother liquor and applying energy

(35) As a method of obtaining a mother liquor in which the chemical species has been contained, there is used a reagent kit comprising a reaction mother liquor containing a plurality of cation species and fluoroanions in a condition that they have been dissolved in a solvent, and the chemical species, and it is conducted by mixing them.

(36) Alternatively, there is used a reagent kit comprising a reaction mother liquor containing a plurality of cation species and the chemical species in a condition that they have been dissolved in a solvent, and fluoroanions, and it is conducted by mixing them.

(37) The application of energy may be conducted to either one or both of the above-mentioned reagent kit prior to the mixing. It may be conducted to the mixed liquid while mixing the reagent kit. It may be conducted to the reaction mother liquor after the mixing.

(38) By conducting the above treatment, a fluorine-containing complex salt is precipitated as a solid from the reaction mother liquor. In the case of applying energy by applying heat, it is preferable to conduct mechanical stirring too in order to avoid depletion of the solvent by evaporation or boiling and to maintain uniformity of the liquid. In the case of applying heat, it is preferable to maintain the temperature of the reagent prior to the mixing, its mixed liquid, or the reaction mother liquor at a temperature of from 40 C. to the boiling point of the liquor. Furthermore, it is preferable to avoid depletion of the solvent by using a vapor reflux condensing mechanism or a pressure sealed container. In the case of applying energy by applying pressure, it is preferably a uniform pressurization on the entirety of the liquid phase, such as solvothermal method. In the case of applying energy by applying electromagnetic waves such as light and microwaves, it is preferable to uniformly apply electromagnetic waves to the inside of a container or circularly supply the reagent prior to the mixing, its mixed liquid or the reaction mother liquor to a section where electromagnetic waves are applied.

(39) Furthermore, the above assumes precipitation of a fluorine-containing complex salt by the reaction in the container, but it is also possible to precipitate a fluorine-containing complex salt in a condition that the reaction mother liquor has been uniformly applied onto a substrate. In this case, it is preferable that heat application is conducted to the substrate itself or uniformly conducted by a heater carrying the substrate, and it is preferable that pressure application is conducted to the container whole after putting the substrate into the container.

(40) Furthermore, it is also possible to uniformly apply electromagnetic waves onto the substrate, but it is also possible to selectively conduct that on only a place where the precipitation is conducted for the purpose of a patterning onto the substrate. It is optional to apply energy by combining energies such as heat, pressure, and electromagnetic waves such as light and microwaves.

(41) Even if the chemical species is contained as a substance for changing acidity, the chemical species alone does not cause decomposition of the fluoroanions. Therefore, it is preferable to previously contain the substance in the reaction mother liquor and then apply energy. For example, decomposition of BF.sub.4.sup. does not occur only by adding urea or hexamethylene tetramine. Therefore, after preparing a uniform mother liquor in which the urea or hexamethylene tetramine has been contained, it is possible to apply energy to this. According to this method, it is possible to precipitate a more uniform, fluorine-containing complex salt as a solid. Therefore, it is preferable. Urea or hexamethylene tetramine is gradually decomposed even at room temperature particularly in solvent. Therefore, it is preferable to use the mother liquor as soon as after its preparation.

(42) (4) In the case of accelerating decomposition of the fluoroanions by containing acid or base as a substance for changing acidity in the reaction mother liquor

(43) It is optional to add acid or base to the reaction mother liquor containing a plurality of cation species and fluoroanions in a state that they have been dissolved in a solvent. Furthermore, it is optional to simultaneously mix fluoroanions and acid or base with the reaction mother liquor containing a plurality of cation species in a state that they have been dissolved. Furthermore, it is optional that, to the reaction mother liquor containing a plurality of cation species in a state that they have been dissolved, acid or base and then fluoroanions are added.

(44) By conducting the above treatment, a fluorine-containing complex salt is precipitated as a solid from the reaction mother liquor. When preparing the reaction mother liquor, it is preferable from the viewpoint of productivity to use both of heating and mechanical stirring, while trying to prevent the amount of the solvent from decreasing by a large amount by evaporation. It is preferable to add acid or base, while sufficiently conducting a mechanical stirring and mixing. For example, ammonia as a weak base is high in reactivity to rapidly change acidity of the reaction mother liquor. Therefore, it is preferable to add ammonia dropwise to conduct the reaction while stirring the reaction mother liquor. Alternatively, it is preferable to introduce ammonia vapor or mist into a sealed reaction container while stirring the reaction mother liquor.

(45) Except for the case of conducting pressure application as energy application, in the above methods (1) to (4), it is possible to arbitrarily select the pressure when accelerating decomposition of the fluoroanions. In particular, an open system under atmospheric pressure or a sealed system (solvothermal method) is preferable. In the case of conducting it in an open system, the solvent may be discharged to the outside of the system by volatilization or boiling. Therefore, it is desirable to use an apparatus having a reflux mechanism. Furthermore, the atmosphere control is also admissible. In particular, for the purpose of controlling oxidation state of the fluorine-containing complex salt, it is also possible to conduct the production in an inert gas atmosphere. Furthermore, to the reaction mother liquor, it is optional to add an additive, such as ethylene glycol, polyethylene glycol, polyvinylpyrrolidone, hexylamine, high-order carboxylic acids, peroxides, or ascorbic acid, formic acid, sulfur-containing acids such as thiosulfuric acid, phosphorus-containing acids such as phosphonic acid, and salts of these. Depending on the type of the additive, it may be possible to achieve the crystal growth control or the oxidation state control.

(46) In the present production process, a fluorine-containing complex salt is produced in the reaction mother liquor. As a post-treatment method for recovering the complex salt, it is optional to use separation such as filtration and centrifugation, purification, and washing. Furthermore, it is optional to subsequently conduct baking or the like. Without separating the solid, it may be used as a slurry or suspension.

EXAMPLES

(47) In the following, the present invention is explained in more detail by examples. Embodiments of the present invention are not limited to this.

Example 1

(48) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(49) Magnesium acetate tetrahydrate: 0.10 mmol/g (2.1 mass %)

(50) Barium acetate: 0.10 mmol/g (2.5 mass %)

(51) Ammonium hexafluorophosphate: 0.23 mmol/g (3.8 mass %)

(52) Acetic acid: 5.14 mmol/g (30.8 mass %)

(53) Ethylene glycol: 40.0 mass %

(54) Water: 20.8 mass %

(55) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. It was heated at 130 C. for three hours with stirring. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 1. The dry substance salt 1 and a baked substance of the dry substance salt 1 prepared by baking the dry substance salt 1 at 150 C., 400 C. or 600 C. for two hours each were confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 1 with a scanning electron microscope, as shown in FIG. 1, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 2

(56) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(57) Magnesium acetate tetrahydrate: 0.11 mmol/g (2.4 mass %)

(58) Barium acetate: 0.11 mmol/g (2.8 mass %)

(59) Acetic acid: 5.69 mmol/g (34.7 mass %)

(60) Ethylene glycol: 43.8 mass %

(61) Water: 16.3 mass %

(62) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. It was heated at 130 C. with stirring. An ammonium hexafluorophosphate aqueous solution (concentration: 2.4 mmol/g) equivalent to 10.5 mass % of the total of the mother liquor was added dropwise, followed by maintaining for three hours. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 2. The obtained dry substance salt 2 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 2 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 3

(63) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(64) Magnesium acetate tetrahydrate: 0.14 mmol/g (3.0 mass %)

(65) Barium acetate: 0.14 mmol/g (3.6 mass %)

(66) Ammonium hexafluorophosphate: 0.32 mmol/g (5.2 mass %)

(67) Ethylene glycol: 58.0 mass %

(68) Water: 30.2 mass %

(69) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. It was heated at 130 C. with stirring. Acetic acid equivalent to 45 mass % of the total of the mother liquor was added dropwise, followed by maintaining for three hours. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 3. The obtained dry substance salt 3 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 3 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 4

(70) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(71) Magnesium acetate tetrahydrate: 0.08 mmol/g (1.7 mass %)

(72) Barium acetate: 0.08 mmol/g (2.0 mass %)

(73) Ammonium hexafluorophosphate: 0.16 mmol/g (2.6 mass %)

(74) Acetic acid: 3.41 mmol/g (20.8 mass %)

(75) Glycerol: 72.9 mass %

(76) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. It was heated at 130 C. for three hours with stirring. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was centrifuged, followed by washing with methanol and then air-drying, thereby obtaining a dry substance salt 4. The obtained dry substance salt 4 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 4 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 5

(77) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(78) Magnesium acetate tetrahydrate: 0.24 mmol/g (5.1 mass %)

(79) Barium acetate: 0.24 mmol/g (6.1 mass %)

(80) Ammonium hexafluorophosphate: 0.50 mmol/g (8.2 mass %)

(81) Acetic acid: 4.06 mmol/g (24.7 mass %)

(82) Water: 55.9 mass %

(83) This mother liquor was put into a sealed reactor. With stirring, it was heated for three hours in an oil bath of 150 C. With this, the inside pressure of the container gradually increased and reached 0.25 MPa-G. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was centrifuged, followed by washing with methanol and then air-drying, thereby obtaining a dry substance salt 5. The obtained dry substance salt 5 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 5 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 6

(84) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(85) Magnesium acetate tetrahydrate: 0.24 mmol/g (5.1 mass %)

(86) Barium acetate: 0.24 mmol/g (6.1 mass %)

(87) Tetrafluoroboric acid: 0.50 mmol/g (4.4 mass %)

(88) Hexamethylene tetramine: 1.68 mmol/g (23.6 mass %)

(89) Water: 60.8 mass %

(90) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. With stirring, it was heated for three hours at 130 C. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 6. A liquid prepared by combining the filtrate with the primary washing water was neutral (pH: about 6-8). The obtained dry substance salt 6 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 6 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 7

(91) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(92) Magnesium acetate tetrahydrate: 0.22 mmol/g (4.7 mass %)

(93) Barium acetate: 0.22 mmol/g (5.6 mass %)

(94) Tetrafluoroboric acid: 0.88 mmol/g (7.7 mass %)

(95) Hexamethylene tetramine: 1.53 mmol/g (21.4 mass %)

(96) Water: 60.6 mass %

(97) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. With stirring, it was heated for three hours at 80 C. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 7. A liquid prepared by combining the filtrate with the primary washing water was neutral (pH: about 6). The obtained dry substance salt 7 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 7 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 8

(98) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(99) Strontium chloride hexahydrate: 0.18 mmol/g (4.8 mass %)

(100) Aluminum chloride hexahydrate: 0.18 mmol/g (4.3 mass %)

(101) Tetrafluoroboric acid: 0.89 mmol/g (7.8 mass %)

(102) Hexamethylene tetramine: 1.57 mmol/g (22.0 mass %)

(103) Water: 61.1 mass %

(104) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. With stirring, it was heated for two hours at 80 C. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 8. The obtained dry substance salt 8 and a baked body of the dry substance salt 8 prepared by baking the dry substance salt at 600 C. for two hours were each confirmed by a powder X-ray diffraction method to be SrAlF.sub.5. As a result of observing the dry substance salt 8 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 9

(105) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(106) Lithium chloride: 0.15 mmol/g (0.6 mass %)

(107) Strontium chloride hexahydrate: 0.15 mmol/g (4.0 mass %)

(108) Aluminum chloride hexahydrate: 0.15 mmol/g (3.6 mass %)

(109) Tetrafluoroboric acid: 0.89 mmol/g (7.8 mass %)

(110) Hexamethylene tetramine: 1.61 mmol/g (22.6 mass %)

(111) Water: 61.4 mass %

(112) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. With stirring, it was heated for six hours at 80 C. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 9. The obtained dry substance salt 9 was confirmed by a powder X-ray diffraction method to be LiSrAlF.sub.6. As a result of observing the dry substance salt 9 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 10

(113) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(114) Lithium chloride: 0.15 mmol/g (0.6 mass %)

(115) Calcium chloride dihydrate: 0.15 mmol/g (2.2 mass %)

(116) Aluminum chloride hexahydrate: 0.15 mmol/g (3.6 mass %)

(117) Tetrafluoroboric acid: 0.92 mmol/g (8.1 mass %)

(118) Hexamethylene tetramine: 1.67 mmol/g (23.4 mass %)

(119) Water: 62.1 mass %

(120) This mother liquor was put into an open-to-the-atmosphere type reactor equipped with a reflux condenser. With stirring, it was heated for six hours at 80 C. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 10. The obtained dry substance salt 10 was confirmed by a powder X-ray diffraction method to be LiCaAlF.sub.6. As a result of observing the dry substance salt 10 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 11

(121) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(122) Lithium acetate: 0.20 mmol/g (1.3 mass %)

(123) Strontium acetate 0.5-hydrate: 0.20 mmol/g (4.3 mass %)

(124) Aluminum chloride hexahydrate: 0.20 mmol/g (4.8 mass %)

(125) Ammonium hexafluorophosphate: 0.62 mmol/g (10.1 mass %)

(126) Acetic acid: 6.00 mmol/g (36.0 mass %)

(127) Water: 43.5 mass %

(128) This mother liquor was put into a sealed reactor. With stirring, it was heated for 16 hours in an oil bath of 170 C. The inside pressure of the container gradually increased and reached 0.52 MPa-G. It was allowed to cool by stopping the heating. After that, the precipitated solid was separated by decantation, followed by adding water to disperse it. Then, it was centrifuged and recovered by conducting filtration. After washing with acetone, it was air-dried to obtain a dry substance salt 11. The obtained dry substance salt 11 was confirmed by a powder X-ray diffraction method to be LiSrAlF.sub.6. As a result of observing the dry substance salt 11 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 12

(129) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(130) Lithium acetate: 0.25 mmol/g (1.6 mass %)

(131) Barium acetate: 0.25 mmol/g (6.4 mass %)

(132) Ammonium hexafluorophosphate: 0.76 mmol/g (12.4 mass %)

(133) Acetic acid: 3.75 mmol/g (22.5 mass %)

(134) Water: 57.1 mass %

(135) This mother liquor was put into a sealed reactor. With stirring, it was heated for 17 hours in an oil bath of 170 C. The inside pressure of the container gradually increased and reached 0.34 MPa-G. It was allowed to cool by stopping the heating. After that, the precipitated solid was recovered by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 12. The obtained dry substance salt 12 was confirmed by a powder X-ray diffraction method to be BaLiF.sub.3. As a result of observing the dry substance salt 12 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 13

(136) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(137) Sodium chloride: 0.40 mmol/g (2.3 mass %)

(138) Iron (III) chloride hexahydrate: 0.40 mmol/g (10.8 mass %)

(139) Tetrafluoroboric acid: 0.80 mmol/g (7.0 mass %)

(140) Hexamethylene tetramine: 1.20 mmol/g (16.8 mass %)

(141) Water: 63.1 mass %

(142) This mother liquor was put into a sealed reactor. With stirring, it was heated for 19 hours in an oil bath of 140 C. The inside pressure of the container increased and reached 0.6-0.86 MPa-G. It was allowed to cool by stopping the heating. After that, the precipitated solid was recovered by filtration, followed by washing with water and then drying at 140 C. under nitrogen flow, thereby obtaining a dry substance salt 13. The obtained dry substance salt 13 was confirmed by a powder X-ray diffraction method to be (NH.sub.4).sub.2NaFeF.sub.6. As a result of observing the dry substance salt 13 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 14

(143) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(144) Magnesium acetate tetrahydrate: 0.28 mmol/g (6.0 mass %)

(145) Barium acetate: 0.28 mmol/g (7.2 mass %)

(146) Tetrafluoroboric acid: 1.12 mmol/g (9.8 mass %)

(147) Water: 77.0 mass %

(148) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser. While conducting a heating at 80 C. with stirring, 25 mass % aqueous ammonia, which was equivalent to 53 mass % of the total of the reaction mother liquor, was gradually added dropwise by spending five hours. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 14. The obtained dry substance salt 14 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 14 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 15

(149) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(150) Strontium chloride hexahydrate: 0.23 mmol/g (6.2 mass %)

(151) Aluminum chloride hexahydrate: 0.23 mmol/g (5.6 mass %)

(152) Tetrafluoroboric acid: 1.14 mmol/g (10.0 mass %)

(153) Water: 78.2 mass %

(154) This mother liquor was put into an open-to-the-atmosphere reactor. With stirring at room temperature, 25 mass % aqueous ammonia, which was equivalent to 55 mass % of the total of the reaction mother liquor, was gradually added dropwise by spending ten hours. With the passage of time, a white-color solid was gradually precipitated. The precipitated solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 15. The obtained dry substance salt 15 was confirmed by a powder X-ray diffraction method to be SrAlF.sub.5. As a result of observing the dry substance salt 15 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 16

(155) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(156) Lithium chloride: 0.19 mmol/g (0.8 mass %)

(157) Strontium chloride hexahydrate: 0.19 mmol/g (5.2 mass %)

(158) Aluminum chloride hexahydrate: 0.19 mmol/g (4.7 mass %)

(159) Tetrafluoroboric acid: 1.15 mmol/g (10.1 mass %)

(160) Water: 79.2 mass %

(161) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser. While conducting a heating at 80 C. with stirring, 25 mass % aqueous ammonia, which was equivalent to 57 mass % of the total of the reaction mother liquor, was gradually added dropwise by spending ten hours. With the passage of time, a white-color solid was gradually precipitated. It was allowed to cool by stopping the heating. After that, the precipitated solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 16. The obtained dry substance salt 16 was confirmed by a powder X-ray diffraction method to be LiSrAlF.sub.6. As a result of observing the dry substance salt 16 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Example 17

(162) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(163) Sodium chloride: 0.48 mmol/g (2.8 mass %)

(164) Iron (III) chloride hexahydrate: 0.48 mmol/g (13.0 mass %)

(165) Tetrafluoroboric acid: 0.96 mmol/g (8.4 mass %)

(166) Water: 75.8 mass %

(167) This mother liquor was put into an open-to-the-atmosphere reactor. With stirring at room temperature, 25 mass % aqueous ammonia, which was equivalent to 39 mass % of the total of the reaction mother liquor, was gradually added dropwise by spending ten hours. With the passage of time, a solid was gradually precipitated. The precipitated solid was recovered by filtration, followed by washing with water and then drying at 140 C. under nitrogen flow, thereby obtaining a dry substance salt 17. The obtained dry substance salt 17 was confirmed by a powder X-ray diffraction method to be (NH.sub.4).sub.2NaFeF.sub.6. As a result of observing the dry substance salt 17 with a scanning electron microscope, it was found to be composed of monodispersed primary particles with uniform particle size and shape.

Comparative Example 1

(168) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(169) Magnesium acetate tetrahydrate: 0.50 mmol/g (10.7 mass %)

(170) Barium acetate: 0.50 mmol/g (12.8 mass %)

(171) Water: 76.5 mass %

(172) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser. While conducting a heating at 80 C. with stirring, ammonium acid fluoride (NH.sub.4HF.sub.2) aqueous solution (concentration: 7.2 mmol/g), which was equivalent to 16.8 mass % of the total of the reaction mother liquor, was added dropwise. At the same time as this dropping, a precipitation was generated. While the temperature was maintained at 80 C., it was aged for two hours. After that, it was allowed to cool by stopping the heating. After that, the precipitated white-color solid was separated by filtration, followed by washing with water and acetone and then air-drying, thereby obtaining a dry substance salt 18. The obtained dry substance salt 18 was confirmed by a powder X-ray diffraction method to be BaMgF.sub.4. As a result of observing the dry substance salt 18 with a scanning electron microscope, as shown in FIG. 2, it was found that crystals had nonuniformly grown, and it was found to be composed of multidispersed particles with nonuniform particle sizes and shapes.

(173) From FIG. 1 and FIG. 2, it is understood that fluorine-containing complex salt particles (Comparative Example 1) for comparison, produced by using ammonium acid fluoride as a fluorine source, are multidispersed with nonuniform particle sizes and shapes. In contrast with this, it is understood that fluorine-containing complex salt particles of the present invention (Example 1) prepared by using fluoroanions as a fluorine source and using application of heat and addition of acid as a trigger are monodispersed with uniform particle size and shape.

Comparative Example 2

(174) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(175) Magnesium acetate tetrahydrate: 0.10 mmol/g (2.1 mass %)

(176) Barium acetate: 0.10 mmol/g (2.5 mass %)

(177) Trifluoroacetic acid: 1.08 mmol/g (12.3 mass %)

(178) 2-propanol 75.1 mass %

(179) Water: 8.0 mass %

(180) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser, followed by heating at 80 C. for three hours with stirring. Then, the mother liquor was transferred to an evaporating dish, followed by drying at 80 C. in a dryer to obtain a dry substance salt 19. The dry substance salt 19 was baked at 400 C. or 600 C. for two hours each. With this, it was confirmed by a powder X-ray diffraction method that, in each case, main products of the baked body were BaF.sub.2 and MgF.sub.2 and that diffraction intensity of BaMgF.sub.4 was weaker than those of these simple salts.

Comparative Example 3

(181) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(182) Magnesium trifluoromethanesulfonate: 0.30 mmol/g (9.5 mass %)

(183) Barium trifluoromethanesulfonate: 0.30 mmol/g (12.9 mass %)

(184) Trifluoromethanesulfonic acid: 0.57 mmol/g (8.6 mass %)

(185) Water: 69.0 mass %

(186) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser, followed by heating at 80 C. for three hours with stirring. Then, the mother liquor was transferred to an evaporating dish, followed by drying at 95 C. in a dryer to obtain a dry substance salt 20. The dry substance salt 20 was baked at 600 C. for two hours. With this, it was confirmed by a powder X-ray diffraction method that main products of the baked body were BaF.sub.2 and MgF.sub.2 and that diffraction intensity of BaMgF.sub.4 was weaker than those of these simple salts.

Comparative Example 4

(187) At room temperature, respective components were dissolved and mixed, to prepare a reaction mother liquor of the following composition.

(188) Strontium acetate hemihydrate: 0.10 mmol/g (2.1 mass %)

(189) Aluminum ethoxide: 0.10 mmol/g (1.6 mass %)

(190) Trifluoroacetic acid: 1.08 mmol/g (12.3 mass %) 2-propanol 76.0 mass %

(191) Water: 8.0 mass %

(192) This mother liquor was put into an open-to-the-atmosphere reactor equipped with a reflux condenser, followed by heating at 80 C. for three hours with stirring. Then, the mother liquor was transferred to an evaporating dish, followed by drying at 80 C. in a dryer to obtain a dry substance salt 21. The dry substance salt 21 was baked at 400 C. or 600 C. for two hours each. With this, it was confirmed by a powder X-ray diffraction method that, in each case, main products of the baked body were SrF.sub.2 and AlF.sub.3 and that diffraction intensity of SrAlF.sub.5 was weaker than those of these simple salts.

Comparative Example 5

(193) Equimolar amounts of powdery magnesium fluoride reagent and barium fluoride reagent were taken, followed by kneading in a mortar and then baking at 600 C. for two hours. It was confirmed by a powder X-ray diffraction method that the baked body remained a mixture of BaF.sub.2 and MgF.sub.2 and that BaMgF.sub.4 phase was not formed.