Adhesive Composition

Abstract

An adhesive composition of general use is described, and particularly suitable for welding plastic parts, in the form of a two-component composition. The first of the two components being a cyanoacrylate based glue, and the second of the two components includes a blend, in powder form, of a polymeric origin component and an organic origin component.

Claims

1. A two-component type adhesive composition, the first of the two components being a cyanoacrylate based glue, and wherein the second of the two components comprises a powder blend of polymeric origin components and organic origin components.

2. The adhesive composition, according to claim 1, wherein the polymeric origin component comprises an elastomer.

3. The adhesive composition, according to claim 2, wherein the polymeric origin component comprises natural or synthetic rubbers, preferably recycled.

4. The adhesive composition, according to claim 2, wherein the polymeric origin component further comprises a plastic polymer.

5. The adhesive composition, according to claim 4, wherein the plastic polymer component comprises ABS, PE, PS, PET or PP, preferably recycled.

6. The adhesive composition according to claim 1, wherein the organic origin component comprises an organic alloy material.

7. The adhesive composition according to claim 1, wherein the organic origin component of comprises an organic fiber material.

8. The adhesive composition according to claim 6, wherein the organic alloy material comprises gluten.

9. The adhesive composition, according to claim 6, wherein the alloy organic origin component comprises cellulose.

10. The adhesive composition, according to claim 6, wherein the alloy organic origin component comprises glucose.

11. The adhesive composition, according to claim 6, wherein the organic alloy material comprises wheat flour, corn flour, cornmeal or cassava flour.

12. The adhesive composition, according to claim 7, wherein the organic fiber material comprises starch.

13. The adhesive composition according to claim 1, wherein a proportion between the organic origin component in relation to the polymeric origin component is comprised between 10% and 90%.

14. The adhesive composition, according to claim 1, wherein said composition has a distribution of the powder blend particles from 1 mm to 1 micron, and preferably from 0.1 mm to 6 microns.

Description

DESCRIPTION OF THE INVENTION

[0012] As said, the present composition is defined by two individual two-components, which are applied and mixed directly on the damaged area.

[0013] The first of the two-components, with an aggregator and integrator objective, is a cyanoacrylate based glue. For the purposes of the invention, such first two-component can be selected among the glues commercially available on the market, provided that they have an acrylic base and that they are activated in the presence of oxygen (air). In addition, said cyanoacrylate two-component must have low viscosity, in order to assimilate the other components more easily, causing a natural, full and immediate mixture, without effort, pressure or compression at room temperature.

[0014] The second of the two-components comprises a mixture or blend of materials, called filling, since they are intended not only to unite the damaged parts of the damaged parts, but also to recompose missing parts and parts removed when the part is repaired.

[0015] Said second two-component, or blend, is presented in the form of a mixture of dry or substantially dry powders, comprising organic origin components and inorganic origin components.

[0016] Among the inorganic components, elastomer powders or elastomeric polymers, including natural or synthetic rubbers, are particularly suitable. Despite the powders used may come from virgin rubbers, the present composition is equally suitable for the use of materials such as recycled rubbers or elastomers, thus contributing to the reuse of discarded elastomeric materials within the general spirit of the invention.

[0017] Among the inorganic components, materials such as plastic polymers can also be used additively, in the form of powders, and selected from a wide range of plastic materials, such as ABS, PE, PS, PET, PP and others. As in the case of elastomeric materials, plastic polymer powders can be virgin, but the best direction of the invention advocates the use of recycled plastic materials. When present, plastic polymer materials are blended, or blended, with elastomeric materials in varying amounts.

[0018] Complementing the blend of powders, an organic component is also foreseen, which is formed from one or more organic materials, also in powder, with low relative humidity and comprising organic alloy materials, in addition to organic fiber materials.

[0019] Among the organic polymeric alloy materials, gluten is particularly suitable for use in the invention, because its polymeric composition includes gliadin and glutemin. Gluten sources suitable for use in the present invention, such as organic binding material, polymeric fibers, which are present in flours in general, in particular in wheat or corn flour, in addition to cornmeal, cassava flour, etc.

[0020] Among the organic fiber materials, cellulose, also a polymer, is particularly advantageous for the purposes of the invention because it is a long chain of glucose, responding very well to cyanogenic interactions (after mixing with the first two-component, the cyanoacrylate based glue), resulting in cyanogenic glycosides. In this sense, starch is also an important source to be considered, since it comes from the organic synthesis of glucose and therefore able to provide the organic component of the alloy, according to the invention.

[0021] In this way, and despite the possibility of using individual elements such as the sources of alloy organics and organic fibers, wheat flour is preferably used as a common source of such component organic elements, since it gathers most of them and is of low cost, having high integrative power.

TABLE-US-00001 TABLE 1 Composition of the p/p powder blend (second Two-component) Origin Type percentage Powder Inorganic Elastomer 100% Blend Component Elastomer + plastic 90-10% to 10-90% (when present) Organic Polymeric 90-10% to 10-90% component alloy + organic fiber Organic + Relationship between 90-10% to 10-90% Inorganic organic/inorganic components

[0022] Finally, the blend or mixture of powders (second two-component, also called two-component 2), formulated according to the above proportions, is duly deposited on a first layer of cyanoacrylate (first two-component, also called two-component 1), followed by successive and alternating layers of two-components 1 and 2. In particular , two-component 1 is always applied after removing the excess of the powder blend (two-component 2) (and this excess is reusable, increasing its yield and reducing its cost), assimilated by component 1, which is, in the amount it needs, without interference from the applicator, thus avoiding complicating dosimetries. The inventor suspects that two-component 1 assimilates more or less from two-component 2, depending on the subject they are touching, given numerous face-to-face tests.

[0023] The tests showed that the reaction times between the two two-components are short, with such time being around, at most, a few seconds.

[0024] Finally, and in order to prove the results proclaimed, specimens were submitted to structural and behavioral analyzes for plastic specimens, together with the IPT, according to the analyzes according to ASTM D695-15 standards (behavior of rigid plastics in compression ratio); ASTM D 2240-15e1 (Shore B hardness analysis); ASTM D638-14 (Stress Properties Analysis); and ASTM D1238-13 (flow index analysis). The results indicated below are reported from Test Report 1 113 432-203 of December 2019.

[0025] The tests were carried out comparing two identical specimens, taken from a vehicle bumper (formed from PP and EPDM), the first being for comparative purposes (undamaged), while the second (test effective) had a tear which was subsequently repaired from the adhesive composition according to the invention.

[0026] In the formulation of the adhesive composition used to repair this specimen,

TABLE-US-00002 TABLE 2 Rupture tension (MPa) .sup.[1] Rupture strength (N) .sup.[1] Specimen Base material Weld Base material Weld 1 125.99 84.39 22034.73 14759.70 2 110.69 110.69  19358.22 - 12385.38 3 133.92 133.92 23421.13  19977.89 - 4 119.34 119.34 20871.89 16999.28 5 121.12 121.12 21182.44 18494.37 Average 122 ± 11 114 ± 23 21374 ± 1860 16523 ± 3739
the powder blend was formed by a polymeric origin component in the form of vulcanized rubber powder (recycled tire, with powder formation mechanically), mixed with an organic origin component in the form wheat flour (commercial product) as a single source for alloy organics and organic fibers.

[0027] For the repair of the bumper, the procedure of overlapping layers was used, directly on the damage, without patches or overlapping of accessory plates, as described above.

[0028] According to the results obtained from the above and below specified analyses, it was determined that, among other tests, the compressive resistance, indicated in rupture tension (MPa), practically the same results between the base material and the weld.

[0029] It should also be noted, in the same test, that the rupture tension required to break the welpture strength necessary to break the base material in specimen 2.

[0030] In relation to Shore hardness, the weld region of the specimen showed a hardness about 13% lower than the hardness of the comparison body. Specifically, the average Shore D hardness values for said base material were measured to be D/72±1, while the Shore D hardness in the weld resulted in D/62±1. Such a result is particularly important considering that, in the repair of a bumper, or any similar part, the weld zone must be sanded for later painting. If the Shore D resistance of the weld were higher than that of the plastic part (which does not occur) it would result in greater difficulty in sanding the weld than the plastic part, which would cause depressions in the part due to the excavation of the sandpaper on the sides of the weld, for this reason be harder than the part being repaired, forcing the subsequent application of corrective leveling masses, which reduces the useful life of these repairs, since such masses are fragile and crack very easily, in the daily use of vehicles, and, with the use of the composite in mesh, objective of this patent, such use of putties is unnecessary, since its sanding is as soft as that of the welded piece, in addition, its micronized grains allow a result after sanding compact and without craters, or holes, in addition to completely leveling with the part being repaired, thus, resulting in defined, not causing lateral excavations to the weld and completely dispensing with the use of such leveling masses, immediately passing to the works painting hours and, thus, increasing the useful life of repairs, significantly reducing the time required for such repairs, thus increasing the profitability of the workshops.

[0031] Another relevant feature of the invention resides in the final elasticity of the weld region, which makes the present adhesive composition particularly suitable for joining plastic materials, as reported in Table 3 below, where a result of a higher modulus of elasticity of the weld is observed in relation to that of the welded part, in the specimen 3.

[0032] In addition, the weld showed a fluidity index (g/10 min) slightly higher than twice the index (measured) obtained for the comparison body (base material).

[0033] As can be interpreted from the results reported here, one of the most important characteristics of the region repaired from the two-component adhesive composition, according to the present invention, is its malleability, allowing the piece to be bent, after repair, as it was bent before, when still intact and without damage, and its smooth, fast and level sanding, possible immediately after its application, significantly reducing repair times, which is radically opposed to the non-malleability, rigidity and high hardness for sanding resulting from welded regions from cyanoacrylate and other epoxy based glues known in the art.

[0034] Furthermore, in the same tests, analyzes were performed regarding the dimensional of the component particles of the powder blend, that is, both the particles of the organic component and the particles of the inorganic component. Such results confirm

TABLE-US-00003 TABLE 3 Elastic test region Specimen modulus (MPa) base 1 685.91 material 2 599.78 3  519.10 - 4 624.33 5 569.44 Average 600 ± 77 weld 1 487.88 2 453.07 3  537.81 - 4 513.79 5 314.16 Average  461 ± 109
a broad distribution of particle sizes in accordance with the assumption of the present invention. In the aforementioned test, particles with sizes from an order of magnitude of a micron to an order of magnitude of millimeters were identified. Such a wide distribution is understood by the inventor as necessary and highly beneficial, since it allows the adhesive of the invention to adapt to any material being welded and to promote its rooting in the microscopic pores of the parts, allowing even greater anchoring power. In this way, and as a feature of the invention, the particles of the powder blend must be distributed within a range encompassing from particles with a diameter of 1 micron to 1 millimeter, and more in particular with a diameter from 6 microns to 0.1 millimeters.

[0035] This characteristic makes the present adhesive composition particularly suitable for welding plastic materials, without compromising the original plastic and elastic characteristics, not forgetting its auspicious performance, also, in thermoset or thermostable materials, which in turn, do not respond to processes of heat welding.

[0036] On the other hand, and in order to contemplate the efficiency of the present two-component adhesive composition, complementary tests were carried out, also with the IPT, in which the functional behavior was evaluated with other specimens, that is, including materials other than plastics.

[0037] Thus, and according to Test Report No. .sup.1 120 876-203, completed on Nov. 17, 2020, specimens were considered, according to table 4, below:

TABLE-US-00004 TABLE 4 Identification types of material in the laboratory aluminum on steel LEL 188-20 aluminum on aluminum LEL 189-20 rubber on aluminum LEL 190-20 plastic on plastic LEL 191-20 plastic on steel LEL 192-20 steel on steel LEL 193-20 rubber on Plastic LEL 194-20 plastic on aluminum LEL 195-20

[0038] In these tests, specimens were formed from the union of individual pieces and different materials, in order to determine the effectiveness of the composite of the present invention in the union of different materials. Such trials were performed in accordance with ASTM D1002-10 (2019)—Standard Test Method for Apparent Shear Strength of Single-Lap-Joint Adhesively Bonded Metal Specimens by Tension Loading.

[0039] The results are reported in the Table below:

TABLE-US-00005 TABLE 5 Determination of shear strength Rupture Rupture width Length Strength Tension Failure fault Identification (mm) (mm) (N) (MPa) type [1] location LEL 188-20 26.31 75.27 2856.91 1.443 cohesive Interface LEL 189-20 27.37 63.83 2090.75 1.197 cohesive Interface LEL 190-20 26.07 55.53 414.75 0.286 Traction external LEL 191-20 24.55 49.96 899.64 0.733 Traction external LEL 192-20 26.29 48.72 1132.55 0.884 Traction external LEL 193-20 25.63 49.51 1954.55 1.540 cohesive Interface LEL 194-20 27.89 43.39 403.85 0.334 Traction external LEL 195-20 27.51 58.16 1097.13 0.686 Traction external [1] Some specimens suffered tensile failure due to the interface strength being higher than that of the polymeric substrate

[0040] As can be easily seen, several specimens showed failures outside the bonding region, that is, the rupture occurred in one of the materials of formation of the specimen, and not in the union of these by the adhesive composition in mesh.

[0041] According to the inventor, such highly efficient results are the result of a reaction sequence, which begins with the combination between cyanoacrylate and rubber, resulting in a thiocyanate, or sulfur cyanide, which, as soon as it is formed, acts in reaction with the fibers and the other organic polymers in the form of powder particles, initially interacting with the smaller particles and progressively with the larger particles. The polymer chains thus modified play an important role in joining or welding the pieces being glued. In addition, the inventor understands that the fibers and polymers also help in the positive results of compressive strength and shear strength, in addition to also guaranteeing the malleability of the joining region, as well as its immediate curing that gives rise to an immediate and high docility.

[0042] On the other hand, in ancillary information, preliminary tests pointed to unsatisfactory results, but also useful in terms of development, from the combination of cyanoacrylate only with fibers and organic polymers, when before, still at the beginning of the research, they were not combined with elastomers and plastics, also in powder form.

[0043] It is worth mentioning that in terms of quality control, the screen composition is quite constant in its results, even though several commercial brands of wheat flour, component of the powder blend, have been tested. In addition, wheat flours with and without additives were also tested, and the final result was always constant and consistent in terms of cohesion of the welded materials.