COMPOSITIONS AND METHODS FOR PFAS DEFLUORINATION

Abstract

Certain embodiments provide ligand-metal composite materials and compositions that could serve as catalyst-reductive agents to accelerate PFAS compounds defluorination. Certain embodiments provide optionally substituted 2,2-bipyridine and 1,10-Phenanthroline ligand coordinated zero-valent metal as described herein and their use for defluorinating PFAS compounds.

Claims

1. A composition comprising: 1) a zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg; and 2) a ligand compound having structure of ##STR00039## wherein R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN; wherein R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro or CN, or R.sub.7 and R.sub.8 along with the intervening carbon atoms form a six membered carbocycle ring A; wherein ring A is absent, or is the six membered carbocycle ring optionally substituted with R.sub.9 and R.sub.10, or is the six membered carbocycle ring fused with a six-membered heteroaryl ring B that is optionally substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN; and wherein R.sub.9, and R.sub.10 are each independently absent, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, oxo (O), or CN.

2. The composition of claim 1, wherein the ligand compound has structure of ##STR00040##

3. The composition of claim 1, wherein the ligand compound has structure of ##STR00041##

4. The composition of claim 1, wherein the ligand compound has structure of ##STR00042##

5. The composition of claim 1, wherein the ligand compound is 2,2-bipyridine optionally substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN.

6. The composition of claim 5, wherein the ligand compound has structure of ##STR00043## wherein each R is independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

7. The composition of claim 1, wherein the ligand compound is selected from the group consisting of ##STR00044##

8. The composition of claim 6, wherein the ligand compound is selected from the group consisting of ##STR00045##

9. The composition of claim 8, wherein the ligand compound is selected from the group consisting of ##STR00046##

10. The composition of claim 9, wherein the ligand compound is ##STR00047##

11. The composition of claim 1, wherein the ligand compound is selected from the group consisting of ##STR00048##

12. The composition of claim 3, wherein the ligand compound is selected from the group consisting of ##STR00049##

13. The composition claim 1, wherein the zero-valent metal comprises metal nanoparticles.

14. The composition of claim 13, wherein the zero-valent metal is Zn.sup.0.

15. The composition of claim 1, comprising the ligand at a concentration of about 0.025 to 0.25 mM.

16. The composition of claim 15, comprising the metal at a concentration of about 5 to 12.5 mg mL.sup.1.

17. The composition of claim 1, wherein the composition has a pH of about 8-9.

18. A filtering device comprising the composition of claim 1.

19. A method for making the composition of claim 1, comprising mixing the zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg, with the ligand compound of claim 1.

20. A method for degrading a PFAS compound, comprising contacting the PFAS compound with the composition of claim 1.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0015] FIGS. 1A-1H. Background information: (FIGS. 1A-1C) Co complex catalysts for reductive defluorination of branched PFAS; (FIG. 1D) a model Co complex synthesized from CoCl.sub.2 and two N,N-bidentate ligands (ref 58); (FIGS. 1E-1F) examples of PFAS structures that could or could not be defluorinated by known Co catalysts (ref. 28); (FIG. 1G) an enzymatic Mo cofactor complex and (FIG. 1H) an artificial Mo complex synthesized from the (NH.sub.2).sub.2bpy ligand for perchlorate reduction (ref. 50).

[0016] FIGS. 2A-2F. (FIG. 2A) Defluorination of PF-3,7-Me.sub.2OA (0.1 mM) at pH 9.0. Reaction conditions for the Zn.sup.0 system: Me.sub.2bpy (0.25 mM), nZn.sup.0 (12.5 mg mL.sup.1), NH.sub.4Cl buffer (10 mM), 70 C. The optimized condition used 0.025 mM of Me.sub.2bpy and 10 mg mL.sup.1 of nZn.sup.0 at 90 C. Reaction conditions for the Co-catalyzed systems (data reproduced from ref. 28): B.sub.12 or protoporphyrin-Co (CoPP) (0.25 mM), Ti.sup.III-citrate (36 mM), carbonate buffer (40 mM), 70 C.; (FIG. 2B) defluorination of linear PFCAs with Me.sub.2bpy (0.025 mM), nZn.sup.0 (10 mg mL.sup.1), NH.sub.4Cl (10 mM), 90 C.; (FIG. 2C) CF bond dissociation energies of PFAS containing eight fluorinated carbons (data reproduced from ref. 67); (FIG. 2D-2F) defluorination of Cl.sub.xPFCAs at the optimized condition unless specified (L=Me.sub.2bpy); all three panels share the same legend.

[0017] FIG. 3. Comparison of deF % from various PFAS by Me.sub.2bpy-Zn.sup.0 and UV/sulfite reported earlier (refs. 66 and 68). Corresponding PFAS structures are shown in Table 2. Each left column is Me.sub.2bpy-Zn.sup.0 at conditions as shown, and each right column is UV/sulfite at conditions as shown.

[0018] FIGS. 4A-4D. Optimization of reaction regarding: (FIG. 4A) the amount of nZn.sup.0 in batch reactions; (FIG. 4B) ligand ((Me).sub.2bpy) concentrations at optimized nZn.sup.0 (10 mg/mL); (FIG. 4C) temperature at optimized nZn.sup.0 (10 mg/mL) and (Me).sub.2bpy (0.025 mM); (FIG. 4D) initial pH (10 mg/mL) at (Me).sub.2bpy (0.025 mM), and temperature (90 C.) in stirring reactions, 4 h. Default reaction conditions: PFMe.sub.2OA (0.1 mM), NH.sub.4Cl (10 mM), stirring.

[0019] FIGS. 5A-5B. nZn.sup.0 powder scanning transmission electron microscope (STEM) images: (FIG. 5A) nZn.sup.0 powder image with scale bar 500 nm and (FIG. 5B) nZn.sup.0 powder image with scale bar 20 nm.

DETAILED DESCRIPTION

[0020] New composite, composition, device, system, and/or methods are described herein for PFAS defluorination. It was surprisingly shown herein that organic ligands surprisingly led to reductive defluorination from per- and polyfluoroalkyl substances (PFAS) compounds, including linear Perfluoroalkyl carboxylic acids (PFCAs) and Perfluoroalkyl ether carboxylic acids (PFECAs), by zero valent metal as described herein.

[0021] Certain embodiments of the composite, composition, device, system, and methods can be used for in-situ remediation of soil and groundwater from PFAS contamination. For illustrative purposes, the materials and compositions described herein may be used in a permeable reactive barrier installed underground for groundwater remediation. Exemplary application also includes expansion to filter systems for treating water and wastewater streams that contain PFAS. For example, the composite described herein (e.g., Ligand-Zinc composite) can be loaded in the filter system for proactive treatment.

[0022] Accordingly, certain embodiments of the invention provide a composition comprising: [0023] 1) a zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg (zinc, iron, aluminum, titanium, and magnesium); and [0024] 2) a ligand compound having structure of

##STR00002## [0025] wherein R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN; [0026] wherein R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro or CN, or R.sub.7 and R.sub.8 along with the intervening carbon atoms form a six membered carbocycle ring A; [0027] wherein ring A is absent, or is the six membered carbocycle ring optionally substituted with R.sub.9 and R.sub.10, or is the six membered carbocycle ring fused with a six-membered heteroaryl ring B that is optionally substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN; and [0028] wherein R.sub.9, and R.sub.10 are each independently absent, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, oxo (O), or CN.

[0029] In certain embodiments, R.sub.9, and R.sub.10 are oxo (O).

[0030] In certain embodiments, the ring A is absent.

[0031] For example, in certain embodiments, the composition comprises: [0032] 1) a zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg (zinc, iron, aluminum, titanium, and magnesium); and [0033] 2) a ligand compound that is 2,2-bipyridine optionally substituted with one or more (e.g., 1, 2, 3, 4 substituents) substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN.

[0034] In certain embodiments, the ligand compound has structure of

##STR00003##

[0035] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0036] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.4)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0037] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.3)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0038] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.4)alkyl, halo, amino, or CN.

[0039] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, (C.sub.1-C.sub.3)alkyl, halo, amino, or CN.

[0040] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.7, and R.sub.8 are each independently H, methyl, halo (e.g., Cl), or CN.

[0041] In certain embodiments, the ring A is a six membered carbocycle ring that is optionally substituted with R.sub.9 and R.sub.10.

[0042] For example, in certain embodiments, the ligand compound has structure of

##STR00004##

[0043] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0044] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, (C.sub.1-C.sub.4)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0045] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, (C.sub.1-C.sub.3)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0046] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, (C.sub.1-C.sub.4)alkyl, halo, amino, or CN.

[0047] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, (C.sub.1-C.sub.3)alkyl, halo, amino, or CN.

[0048] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, R.sub.6, R.sub.9, and R.sub.10 are each independently H, methyl, or halo (e.g., Cl).

[0049] In certain embodiments, R.sub.9, and R.sub.10 are absent, the ring A is a six membered carbocycle ring fused (at R.sub.7 and R.sub.8 position) with a six-membered heteroaryl ring B, and ring B is optionally substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN.

[0050] In certain embodiments, the ligand compound has structure of

##STR00005##

[0051] In certain embodiments, the six-membered heteroaryl ring B is a pyrazine ring, that is fused to carbocycle ring A (at R.sub.7 and R.sub.8 position).

[0052] In certain embodiments, the six-membered heteroaryl ring B is a pyrazine ring substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN.

[0053] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0054] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, (C.sub.1-C.sub.4)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0055] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, (C.sub.1-C.sub.3)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0056] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, (C.sub.1-C.sub.4)alkyl, halo, amino, or CN.

[0057] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, (C.sub.1-C.sub.3)alkyl, halo, amino, or CN.

[0058] In certain embodiments, R.sub.1, R.sub.2, R.sub.3, R.sub.4, R.sub.5, and R.sub.6, are each independently H, methyl, halo (e.g., Cl), or CN.

[0059] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00006##

[0060] In certain embodiments, the ligand compound has structure of

##STR00007## [0061] wherein each R is independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0062] A specific value of R is H, or methyl.

[0063] A specific value of R is CN.

[0064] A specific value of R is halo (e.g., Cl).

[0065] A specific value of R is t-butyl.

[0066] A specific value of R is methoxy.

[0067] A specific value of R is amino or nitro group.

[0068] In certain embodiments, each R is independently H, (C.sub.1-C.sub.4)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0069] In certain embodiments, each R is independently H, (C.sub.1-C.sub.3)alkyl, (C.sub.1-C.sub.3)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0070] In certain embodiments, each R is independently H, (C.sub.1-C.sub.4)alkyl, halo, amino, or CN.

[0071] In certain embodiments, each R is independently H, (C.sub.1-C.sub.3)alkyl, halo, amino, or CN.

[0072] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00008##

[0073] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00009##

[0074] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00010##

[0075] In certain embodiments, the ligand compound is

##STR00011##

[0076] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00012##

[0077] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00013##

[0078] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00014##

[0079] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00015##

[0080] In certain embodiments, the ligand compound is selected from the group consisting of

##STR00016##

[0081] In certain embodiments, the ligand compound is

##STR00017##

[0082] In certain embodiments, the ligand compound is

##STR00018##

[0083] In certain embodiments, the composition comprises two or more ligands as described herein.

[0084] In certain embodiments, the zero-valent metal is Zn.sup.0. In certain embodiments, the zero-valent metal is Fe.sup.0. In certain embodiments, the zero-valent metal is Al.sup.0. In certain embodiments, the zero-valent metal is Ti.sup.0. In certain embodiments, the zero-valent metal is Mg.sup.0.

[0085] In certain embodiments, the zero-valent metal comprises, or can be provided as, metallic powders or grains.

[0086] In certain embodiments, the zero-valent metal comprises, or can be provided as, metallic particles (e.g., nanometer, micrometer, and/or millimeter-sized metallic particles of Zn (Zinc), Fe (iron), Al (aluminum), Ti (titanium), or Mg (magnesium)).

[0087] In certain embodiments, the zero-valent metal (e.g., Zn, Fe, Al, Ti, or Mg) comprises nanoparticles having size (e.g., averaged diameter) of less than 1000 nm, for example about 1-999 nm, 20-500 nm, or 40-60 nm. In certain embodiments, the zero-valent metal comprises nanoparticles having size (e.g., averaged diameter) of about 1, 5, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 150, 200, 250, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750, 800, 850, 900, or 950 nm. In certain embodiments, the zero-valent metal comprises nanoparticles having size (e.g., averaged diameter) of about 5-600, 1-500, 10-90, 20-80, 40-70, 60-80, 10-100, 20-150, 10-200, 20-250, 10-300, 20-350, 10-400, 20-450, 10-500, 20-600, 10-700, 20-800, or 10-900 nm.

[0088] In certain embodiments, the zero-valent metal (e.g., Zn, Fe, Al, Ti, or Mg) comprises microparticles having size of less than 1 mm, for example about 1-999 m). In certain embodiments, the zero-valent metal comprises microparticles having size (e.g., averaged diameter) of about 1, 5, 10, 20, 30, 40, 50, 60, 70, 80, 90, 100, 150, 200, 250, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750, 800, 850, 900, or 950 m. In certain embodiments, the zero-valent metal comprises microparticles having size (e.g., averaged diameter) of about 5-600, 1-500, 10-90, 20-80, 40-70, 60-80, 10-100, 20-150, 10-200, 20-250, 10-300, 20-350, 10-400, 20-450, 10-500, 20-600, 10-700, 20-800, or 10-900 m.

[0089] In certain embodiments, the zero-valent metal (e.g., Zn, Fe, Al, Ti, or Mg) comprises particles having size of less than 1 cm, for example about 1-9.9 mm). In certain embodiments, the zero-valent metal comprises particles having size (e.g., averaged diameter) of about 1, 2, 3, 4, 5, 6, 7, 8, or 9 mm. In certain embodiments, the zero-valent metal comprises particles having size (e.g., averaged diameter) of about 1-9, 2-8, 3-7, 4-9, or 5-8 mm.

[0090] In certain embodiments, the ligand binds to the metal (Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) particle surface. In certain embodiments, the composition comprises ligand coordinated Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0, such as a ligand coordinated or adsorbed on a metal particle surface.

[0091] In certain embodiments, the composition is a liquid composition (e.g., aqueous composition).

[0092] In certain embodiments, the composition comprises a ligand as described herein at a concentration of about 0.005-0.3, 0.005-0.25, 0.005-0.125, 0.01-0.12, 0.015-0.11, 0.02-0.1, 0.025-0.09, 0.03-0.08, or 0.025-0.25 mM. In certain embodiments, the composition comprises a ligand at a concentration of about 0.005, 0.01, 0.015, 0.02, 0.025, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.125, 0.2, 0.25, or 0.3 mM. In certain embodiments, the composition comprises a ligand at a concentration of about 0.25 mM. In certain embodiments, the composition comprises a ligand at a concentration of about 0.025 mM.

[0093] In certain embodiments, the composition comprises metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle as described herein at a concentration of about 1-20, 2-18, 5-15, 5-10, 6-12, 10-16, 5-12.5, or 6-16 mg mL.sup.1. In certain embodiments, the composition comprises metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle as described herein at a concentration of about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or 20 mg mL.sup.1. In certain embodiments, the composition comprises metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle as described herein at a concentration of about 5, 10, or 12.5 mg mL.sup.1.

[0094] In certain embodiments, the composition has a pH7 (e.g., pH8, 9, 10, or 11). In certain embodiments, the composition has a pH of about 7. 7.5, 8, 8.5, 9, 9.5, 10, 10.5, 11, 11.5 or 12. In certain embodiments, the composition has a pH of about 7-12, 8-11, 8-10, 8-9, 7-9, 9-10, or 9-11.

[0095] In certain embodiments, the composition further comprises ammonium or borate based buffer component or salt. In certain embodiments, the composition further comprises ammonia/ammonium salt buffer component, such as NH.sub.4Cl. In certain embodiments, the composition comprises ammonium salt (e.g., NH.sub.4Cl, (NH.sub.4).sub.2SO.sub.4, or ammonium acetate) at a concentration of about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, or 16 mM. In certain embodiments, the composition comprises ammonium salt (e.g., NH.sub.4Cl) at a concentration of about 1-16, 2-12, 3-11, 4-10, or 5-10 mM.

[0096] In certain embodiments, the composition is a solid composition (e.g., powder).

[0097] In certain embodiments, the composition further comprises a carrier (e.g., porous carrier, such as activated carbon, or porous silica). For example, the carrier media may be blended with the ligand-metal (e.g., ligand-zine, ligand-Fe, ligand-Al, ligand-Ti, or ligand-Mg) composite or serve as support for the ligand-metal composite.

[0098] Certain embodiments of the invention provide a method of making a composition as described herein, comprising mixing 1) a zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg (zinc, iron, aluminum, titanium, and magnesium); and 2) a ligand compound as described herein.

[0099] In certain embodiments, the mixing comprising mixing the zero-valent metal and the ligand compound in a liquid (e.g., an aqueous solution). In certain embodiments, the mixing comprising mixing the zero-valent metal at a concentration (e.g., 5-12.5 mg mL.sup.1) described herein with the ligand compound at a concentration (e.g., 0.025-0.25 mM) described herein.

[0100] In certain embodiments, the method further comprises adding ammonium salt (e.g., NH.sub.4Cl), for example, to a concentration (e.g., 10 mM) as described herein. In certain embodiments, the method further comprises adjusting the pH of the composition to a pH as described herein (e.g., to pH 9).

[0101] In certain embodiments, the method further comprises adding a carrier (e.g., porous carrier, such as activated carbon, or porous silica) to the composition.

[0102] In certain embodiments, the method further comprises drying the liquid (e.g., the aqueous solution) to provide a concentrated liquid composition or a solid composition (e.g., powders).

[0103] Certain embodiments of the invention provide a device or system as described herein.

[0104] In certain embodiments, the device or system is a filtering device or system comprising a composite or composition described herein. For example, a compartment or chamber of the filtering device could be loaded with a composite material or composition as described herein. In certain embodiments, the composition further comprising a carrier such as activated carbon is loaded within a filtering device. In certain embodiments, the composite material or composition may be contained or sandwiched between permeable membranes or meshes. In certain embodiments, a filtering device or system further comprises one or more carrier material(s), such as sand, clay, carbon, resin, plastic beads, glass beads, or a mixture thereof. In certain embodiments, the carrier material(s) may facilitate the immobilization of the metal-ligand composite described herein and provide adequate water conductivity (i.e., allowing the water to penetrate at a desirable rate).

[0105] In certain embodiments, the device or system is a reactive barrier comprising a composite or composition described herein (e.g., permeable reactive barrier loaded with metallic particles and organic ligands described herein, which can be used for in situ PFAS groundwater remediation). In certain embodiments, the filtering device is a permeable reactive barrier.

[0106] Certain embodiments of the invention provide a method comprising contacting a PFAS compound with a composite, composition or a device or system as described herein.

[0107] In certain embodiments, the PFAS compound is a per- or polyfluoroalkyl compound of branched or unbranched, hydrocarbon chain having from 2 to 30 (e.g., 2-16, 7-15, or 8-14) carbon atoms, wherein one or more of the carbon atoms is optionally replaced by (O), wherein the hydrocarbon chain is substituted on carbon with one or more (e.g., two or more) substituents selected from the group consisting of halo (e.g., F, Cl, Br, and I), carboxyl, and SO.sub.3. In certain embodiments, all CH bonds of the compound are substituted with halo (e.g., all CF bonds in the compound and no CH bond). In certain embodiments, at least 90%, 80%, 70%, 60%, 50%, 40%, 30%, 20%, or 10% of all CH bonds of the compound are substituted with halo (e.g., compound having a plurality of CF bonds, CCl, CBr, and/or CI bonds).

[0108] In certain embodiments, the PFAS compound is a linear PFAS compound.

[0109] In certain embodiments, the PFAS compound is a branched PFAS compound.

[0110] In certain embodiments, the PFAS compound is a perfluorocarboxylate compound that has one terminal carboxyl group that is directly linked with the perfluoroalkyl chain.

[0111] In certain embodiments, the PFAS compound is a long-chain perfluorocarboxylate compound of C.sub.nF.sub.2n+1COO.sup., wherein n is 7 (e.g., n8).

[0112] In certain embodiments, the PFAS compound is a perfluoroether carboxylate compound (having one or more ether oxygen, such as 1, 2, or 3 O).

[0113] In certain embodiments, the PFAS compound is a chlorinated polyfluorocarboxylate compound.

[0114] In certain embodiments, the PFAS compound is a, branched or unbranched, per- or polyfluoroalkyl compound that comprises sulfonic acid group S(O).sub.2OH, and wherein one or more of the carbon atoms is optionally replaced by (O) and the compound optionally further comprises carboxyl group. In certain embodiments, the PFAS compound is a perfluoroalkylsulfonate compound that has one terminal sulfonic acid group S(O).sub.2OH that is directly linked with the perfluoroalkyl chain. For example, in certain embodiments, the PFAS compound is perfluorobutanesulfonic acid (PFBS). In certain embodiments, the PFAS compound is perfluorohexanesulfonic acid (PFHxS). In certain embodiments, the PFAS compound is perfluorooctanesulfonic acid (PFOS). In certain embodiments, the PFAS compound is a Nafion byproduct (e.g., Nafion byproduct-2, Nafion byproduct-5, or Nafion byproduct-6).

[0115] In certain embodiments, the PFAS compound is contacted at a pH7 (e.g., pH8, 9, 10, or 11). In certain embodiments, the PFAS compound is contacted at a pH of about 7. 7.5, 8, 8.5, 9, 9.5, 10, 10.5, 11, 11.5 or 12. In certain embodiments, the PFAS compound is contacted at a pH of about 7-12, 8-11, 8-10, 8-9, 7-9, 9-10, or 9-11.

[0116] In certain embodiments, the PFAS compound is contacted at a temperature of 10, 20, 30, 40, 50, 60, 70, 80, or 90 C. In certain embodiments, the PFAS compound is contacted at room temperature of about 20-25 C. In certain embodiments, the PFAS compound is contacted without heating. In certain embodiments, the PFAS compound is contacted under heating. In certain embodiments, the PFAS compound is contacted at a temperature of about 40-95, 50-95, 60-90, 70-90, 80-95, or 90-95 C.

[0117] In certain embodiments, the PFAS compound is contacted at a metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle concentration of about 1-20, 2-18, 5-15, 5-10, 6-12, 10-16, 5-12.5, or 6-16 mg mL.sup.1. In certain embodiments, the PFAS compound is contacted at a metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle concentration of about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or 20 mg mL.sup.1. In certain embodiments, the PFAS compound is contacted at a metal (e.g., Zn.sup.0, Fe.sup.0, Al.sup.0, Ti.sup.0, or Mg.sup.0) grain or particle concentration of about 5, 10, or 12.5 mg mL.sup.1.

[0118] In certain embodiments, the PFAS compound is contacted with a composite or composition described herein at a concentration of Zn.sup.0 particles of about 5-12.5 mg/mL.

[0119] In certain embodiments, the PFAS compound is contacted with a composite or composition described herein at a concentration of ligand of about 0.005-0.125 mM.

[0120] In certain embodiments, the PFAS compound is contacted at a ligand concentration of about 0.005-0.3, 0.005-0.25, 0.005-0.125, 0.01-0.12, 0.015-0.11, 0.02-0.1, 0.025-0.09, 0.03-0.08, or 0.025-0.25 mM. In certain embodiments, the PFAS compound is contacted at a ligand concentration of about 0.005, 0.01, 0.015, 0.02, 0.025, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.125, 0.2, 0.25, or 0.3 mM. In certain embodiments, the PFAS compound is contacted at a ligand concentration of about 0.25 mM. In certain embodiments, the PFAS compound is contacted at a ligand concentration of about 0.025 mM.

[0121] In certain embodiments, the PFAS compound is contacted for about at least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 12, 16, 20, 24, 36, 48 hours or longer. In certain embodiments, the PFAS compound is contacted for about at least 1-72, 2-48, 3-36, 4-24, 5-20, 6-18, 7-16, 8-12, or 9-10 hours.

[0122] In certain embodiments, the method does not comprise contacting the PFAS compound with CoCl.sub.2. In certain embodiments, the method further comprises contacting the PFAS compound with CoCl.sub.2.

[0123] In certain embodiments, the defluorination percentage (deF %) of a contacted PFAS compound is increased by at least 30%, 40%, 50%, 60%, 70%, 80%, 90%, 100%, 150%, 200% or more by a ligand coordinated metal described herein, as compared to a control, such as a control metal in the absence of the ligand.

[0124] In certain embodiments, the defluorination reaction is accelerated or the same defluorination percentage (deF %) of a contacted PFAS compound can be achieved in a time period that is at least 30%, 40%, 50%, 60%, 70%, 80%, or 90% shorter by a ligand coordinated metal described herein, as compared to a control, such as a control metal in the absence of the ligand.

[0125] Certain non-limiting, exemplary embodiments include:

[0126] Embodiment 1. A composite or composition as described herein.

[0127] Embodiment 2. A composite or composition comprising: [0128] 1) a zero-valent metal selected from the group consisting of Zn, Fe, Al, Ti, and Mg; [0129] 2) a ligand compound that is 2,2-bipyridine optionally substituted with one or more substituent selected from the group consisting of (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, and CN.

[0130] Embodiment 3. The composite or composition of Embodiment 2, wherein the ligand compound has structure of

##STR00019## [0131] wherein each R is independently H, (C.sub.1-C.sub.6)alkyl, (C.sub.1-C.sub.6)alkoxy, halo, amino, hydroxy, nitro, or CN.

[0132] Embodiment 4. The composite or composition of Embodiment 2 or 3, wherein the zero-valent metal is Zn.sup.0.

[0133] Embodiment 5. The composite or composition of any one of Embodiments 2-4, wherein the zero-valent metal comprises nanoparticles (e.g., nZn.sup.0).

[0134] Embodiment 6. A device or system comprising the composite or composition of any one of Embodiments 1-5.

[0135] Embodiment 7. A method as described herein.

[0136] Embodiment 8. A method comprising contacting a PFAS compound with a composite or a composition or a device or a system as described herein.

[0137] Embodiment 9. The method of Embodiment 8, wherein the PFAS compound is a linear PFAS compound.

[0138] Embodiment 10. The method of Embodiment 8, wherein the PFAS compound is a branched PFAS compound.

[0139] Embodiment 11. The method of Embodiment 8, wherein the PFAS compound is a long-chain perfluorocarboxylate compound of C.sub.nF.sub.2n+1COO.sup., wherein n is 7 (e.g., n8).

[0140] Embodiment 12. The method of Embodiment 8, wherein the PFAS compound is a chlorinated polyfluorocarboxylate compound.

[0141] Embodiment 13. The method of Embodiment 8, wherein the PFAS compound is a perfluoroether carboxylate compound.

[0142] Certain non-limiting, advantageous features include, but not limited to, no need for external energy input (e.g., UV light or electricity), enhanced cost-effectiveness and less expensive than other methods using external energy input (in situ reaction), high efficacy in selectively treating long-chain PFAS, which cannot be removed by current pump-and-treat for groundwater remediation, unique application value for groundwater remediation, such as permeable reactive barrier, unique application value for wastewater treatment without using external energy, and easy system construction by blending the ligand-metal (e.g., ligand-zinc) composite with porous media/carrier, etc.

[0143] The term alkyl, by itself or as part of another substituent, means, unless otherwise stated, a straight or branched chain hydrocarbon radical, having the number of carbon atoms designated (i.e., C.sub.1-8 means one to eight carbons). Examples include (C.sub.1-C.sub.8)alkyl, (C.sub.2-C.sub.8)alkyl, (C.sub.1-C.sub.6)alkyl, (C.sub.2-C.sub.6)alkyl, (C.sub.1-C.sub.3)alkyl, and (C.sub.3-C.sub.6)alkyl. Examples of alkyl groups include methyl, ethyl, n-propyl, iso-propyl, n-butyl, t-butyl, iso-butyl, sec-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl, and higher homologs and isomers.

[0144] The term alkoxy refers to the formula OR or radical thereof, where R is an alkyl as defined.

[0145] The term halo or halogen refers to bromo, chloro, fluoro or iodo. In some embodiments, halogen refers to chloro or fluoro.

[0146] The term cycloalkyl or carbocycle refers to a saturated or partially unsaturated (non-aromatic) all carbon ring having 3 to 8 carbon atoms (i.e., (C.sub.3-C.sub.8)carbocycle). The term also includes multiple condensed, saturated all carbon ring systems (e.g., ring systems comprising 2, 3 or 4 carbocyclic rings). Accordingly, carbocycle includes multicyclic carbocyles such as a bicyclic carbocycles (e.g., bicyclic carbocycles having about 3 to 15 carbon atoms, about 6 to 15 carbon atoms, or 6 to 12 carbon atoms such as bicyclo[3.1.0]hexane and bicyclo[2.1.1]hexane), and polycyclic carbocycles (e.g tricyclic and tetracyclic carbocycles with up to about 20 carbon atoms). The rings of the multiple condensed ring system can be connected to each other via fused, spiro and bridged bonds when allowed by valency requirements. For example, multicyclic carbocyles can be connected to each other via a single carbon atom to form a spiro connection (e.g., spiropentane, spiro[4,5]decane, etc), via two adjacent carbon atoms to form a fused connection (e.g., carbocycles such as decahydronaphthalene, norsabinane, norcarane) or via two non-adjacent carbon atoms to form a bridged connection (e.g., norbornane, bicyclo[2.2.2]octane, etc). Non-limiting examples of cycloalkyls include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, bicyclo[2.2.1]heptane, pinane, and adamantane. In certain embodiments, the carbocycle is a C.sub.6 carbocycle.

[0147] The term aryl as used herein refers to a single all carbon aromatic ring or a multiple condensed all carbon ring system wherein at least one of the rings is aromatic. For example, in certain embodiments, an aryl group has 6 to 20 carbon atoms, 6 to 14 carbon atoms, 6 to 12 carbon atoms, or 6 to 10 carbon atoms. Aryl includes a phenyl radical. Aryl also includes multiple condensed carbon ring systems (e.g., ring systems comprising 2, 3 or 4 rings) having about 9 to 20 carbon atoms in which at least one ring is aromatic and wherein the other rings may be aromatic or not aromatic (i.e., cycloalkyl). The rings of the multiple condensed ring system can be connected to each other via fused, spiro and bridged bonds when allowed by valency requirements. It is to be understood that the point of attachment of a multiple condensed ring system, as defined above, can be at any position of the ring system including an aromatic or a carbocycle portion of the ring. Non-limiting examples of aryl groups include, but are not limited to, phenyl, indenyl, indanyl, naphthyl, 1, 2, 3, 4-tetrahydronaphthyl, anthracenyl, and the like.

[0148] The term heterocycle or heterocycloalkyl refers to a single saturated or partially unsaturated ring that has at least one atom other than carbon in the ring, wherein the atom is selected from the group consisting of oxygen, nitrogen and sulfur; the term also includes multiple condensed ring systems that have at least one such saturated or partially unsaturated ring, which multiple condensed ring systems are further described below. Thus, the term includes single saturated or partially unsaturated rings (e.g., 3, 4, 5, 6 or 7-membered rings) from about 1 to 6 carbon atoms and from about 1 to 3 heteroatoms selected from the group consisting of oxygen, nitrogen and sulfur in the ring. The sulfur and nitrogen atoms may also be present in their oxidized forms. Exemplary heterocycles include but are not limited to azetidinyl, tetrahydrofuranyl and piperidinyl. The term heterocycle or heterocycloalkyl also includes multiple condensed ring systems (e.g., ring systems comprising 2, 3 or 4 rings) wherein a single heterocycle ring (as defined above) can be condensed with one or more groups selected from cycloalkyl, aryl, and heterocycle to form the multiple condensed ring system. The rings of the multiple condensed ring system can be connected to each other via fused, spiro and bridged bonds when allowed by valency requirements. It is to be understood that the individual rings of the multiple condensed ring system may be connected in any order relative to one another. It is also to be understood that the point of attachment of a multiple condensed ring system (as defined above for a heterocycle) can be at any position of the multiple condensed ring system including a heterocycle, aryl and carbocycle portion of the ring. In one embodiment the term heterocycle includes a 3-15 membered heterocycle. In one embodiment the term heterocycle includes a 3-10 membered heterocycle. In one embodiment the term heterocycle includes a 3-8 membered heterocycle. In one embodiment the term heterocycle includes a 3-7 membered heterocycle. In one embodiment the term heterocycle includes a 3-6 membered heterocycle. In one embodiment the term heterocycle includes a 4-6 membered heterocycle. In one embodiment the term heterocycle includes a 3-10 membered monocyclic or bicyclic heterocycle comprising 1 to 4 heteroatoms. In one embodiment the term heterocycle includes a 3-8 membered monocyclic or bicyclic heterocycle heterocycle comprising 1 to 3 heteroatoms. In one embodiment the term heterocycle includes a 3-6 membered monocyclic heterocycle comprising 1 to 2 heteroatoms. In one embodiment the term heterocycle includes a 4-6 membered monocyclic heterocycle comprising 1 to 2 heteroatoms. Exemplary heterocycles include, but are not limited to aziridinyl, azetidinyl, pyrrolidinyl, piperidinyl, homopiperidinyl, morpholinyl, thiomorpholinyl, piperazinyl, tetrahydrofuranyl, dihydrooxazolyl, tetrahydropyranyl, tetrahydrothiopyranyl, 1,2,3,4-tetrahydroquinolyl, benzoxazinyl, dihydrooxazolyl, chromanyl, 1,2-dihydropyridinyl, 2,3-dihydrobenzofuranyl, 1,3-benzodioxolyl, 1,4-benzodioxanyl, spiro[cyclopropane-1,1-isoindolinyl]-3-one, isoindolinyl-1-one, 2-oxa-6-azaspiro[3.3]heptanyl, imidazolidin-2-one imidazolidine, pyrazolidine, butyrolactam, valerolactam, imidazolidinone, hydantoin, dioxolane, phthalimide, and 1,4-dioxane.

[0149] The term heteroaryl as used herein refers to a single aromatic ring that has at least one atom other than carbon in the ring, wherein the atom is selected from the group consisting of oxygen, nitrogen and sulfur; heteroaryl also includes multiple condensed ring systems that have at least one such aromatic ring, which multiple condensed ring systems are further described below. Thus, heteroaryl includes single aromatic rings of from about 1 to 6 carbon atoms and about 1-4 heteroatoms selected from the group consisting of oxygen, nitrogen and sulfur. The sulfur and nitrogen atoms may also be present in an oxidized form provided the ring is aromatic. Exemplary heteroaryl ring systems include but are not limited to pyridyl, pyrimidinyl, oxazolyl or furyl. Heteroaryl also includes multiple condensed ring systems (e.g., ring systems comprising 2, 3 or 4 rings) wherein a heteroaryl group, as defined above, is condensed with one or more rings selected from cycloalkyl, aryl, heterocycle, and heteroaryl. It is to be understood that the point of attachment for a heteroaryl or heteroaryl multiple condensed ring system can be at any suitable atom of the heteroaryl or heteroaryl multiple condensed ring system including a carbon atom and a heteroatom (e.g., a nitrogen). Exemplary heteroaryls include but are not limited to pyridyl, pyrrolyl, pyrazinyl, pyrimidinyl, pyridazinyl, pyrazolyl, thienyl, indolyl, imidazolyl, triazolyl, tetrazolyl, oxazolyl, isoxazolyl, thiazolyl, furyl, oxadiazolyl, thiadiazolyl, quinolyl, isoquinolyl, benzothiazolyl, benzoxazolyl, indazolyl, quinoxalyl, and quinazolyl.

[0150] Certain non-limiting embodiments are further illustrated by the Example below:

Example 1. Organic Ligand Enabled PFAS Defluorination by Metallic Zinc

[0151] This study explores the ligand-enabled reductive defluorination of per- and polyfluoroalkyl substances (PFAS) by metallic zinc. Adding a N,N-bidentate ligand, 4,4-dimethyl-2,2-bipyridine (Me.sub.2bpy), to nano-sized zinc powder (nZn.sup.0) enabled rapid and significant defluorination from linear long-chain perfluorocarboxylates (C.sub.nF.sub.2n+1COO.sup.) and perfluoroether carboxylates (C.sub.xF.sub.2x+1OC.sub.yF.sub.2yCOO.sup.) that did not degrade in the cobalt (e.g., vitamin B12)-catalyzed systems. The heterogeneous nature of reductive PFAS defluorination by nZn.sup.0 was confirmed by comparison among diverse PFAS substrates and with the homogeneous UV-sulfite system. The examined PFAS substrates include C.sub.nF.sub.2n+1COO.sup., .sup.OOCC.sub.nF.sub.2nCOO.sup., C.sub.nF.sub.2n+1CH.sub.2CH.sub.2COO.sup., C.sub.nF.sub.2n+1SO.sub.3.sup., C.sub.xF.sub.2x+1OC.sub.yF.sub.2yCOO.sup., and Cl(CF.sub.2CFCl).sub.nCF.sub.2COO.sup. of various chain lengths and linear/branch patterns. The results provide mechanistic insights into designing and understanding heterogeneous reaction systems for PFAS degradation. This study also demonstrates the critical role of organic ligands in enhancing the reactivity of metallic nanoparticles for potential in situ PFAS remediation, highlighting the environmental significance of coordination chemistry.

INTRODUCTION

[0152] The urgent demand for the degradation of per- and polyfluoroalkyl substances (PFAS) in the global water environment has led to flourishing technology innovations in the past two decades. The majority of engineering approaches use energetic inputs such as hydrothermal,.sup.1-3 ultraviolet light,.sup.4-11 plasma,.sup.12-15 electricity,.sup.16-19 ultrasonication,.sup.20,21 and even gamma ray.sup.22-24 to cleave the strong CF bonds. In many systems, hydrated electrons, hydroxyl radicals, and semiconductor holes are the primary reactive species. However, PFAS destruction does not necessarily require advanced redox reactive species or reaction conditions. For example, using NaOH in water/DMSO mixed solvent achieved defluorination of perfluorocarboxylates (PFCAs, n=1-8 C.sub.nF.sub.2n+1COO.sup.) and GenX (C.sub.3F.sub.7OCF(CF.sub.3)COO.sup.) at 40-120 C..sup.25, 26 Traditional chemical systems were generally considered ineffective for PFAS destruction, although might worth further re-investigation.

[0153] In 2008, Ochoa-Herrea et al..sup.27 reported B.sub.12 (a corrin-Co.sup.III complex, FIG. 1A)-catalyzed reductive defluorination of branched PFOS isomers by citrate-stabilized Ti.sup.III. The investigation of Co complexes was further extended to various porphyrin-Co.sup.II/III structures (FIGS. 1B and 1C)..sup.28, 29 The reducing agent was later switched to nanometer-sized zinc and iron particles (nZn.sup.0 and nFe.sup.0).sup.30 and sulfide..sup.31 In studies using technical PFOS as the substrate, the branched isomers were the primary source of defluorination..sup.27, 30-32 In our study, the Co-catalyzed systems defluorinated branched PFCAs (FIG. 1E) but not linear PFOA or branched hexafluoropropylene oligomer trimer acid (HFPO-TrA, FIG. 1F)..sup.28 In 2018, Blotevogel et al..sup.33 developed a theoretical model and predicted the half-lives for the first reductive PFOA defluorination step by micrometer-sized Zn.sup.0 and Fe.sup.0 as 7.6 years and 520,000 years, respectively.

[0154] While the above results have persuaded engineering practices to adopt advanced reaction systems to degrade common PFAS pollutants, the biomimetic design might be an alternative route to overcoming kinetic barriers and obtaining novel functions..sup.34, 35 Enzymatic metal complexes such as B.sub.12, chlorophyll (chlorin-Mg), heme (porphyrin-Fe), and Mo cofactor (pyranopterin-dithiolate-Mo, FIG. 1G) exhibit distinct functions that aqueous Co.sup.2+, Mg.sup.2+, Fe.sup.2+, and Mo oxyanions do not have. However, using organic ligands to enhance metal-mediated pollutant degradation via either oxidative.sup.36-42 or reductive.sup.43-48 mechanisms has been largely underdeveloped. Recently, we added bipyridine (R.sub.2bpy, R=variable substitution groups such as NH.sub.2 or CH.sub.3) to an inorganic MoO.sub.xPd/C catalyst.sup.49 to enable perchlorate (ClO.sub.4) reduction..sup.50 Under the reducing environment by H.sub.2+Pd/C, the (NH.sub.2).sub.2bpy and Na.sub.2MoO.sub.4 assembled in situ into a highly active catalytic site (FIG. 1H). The (NH.sub.2).sub.2bpy-MoO.sub.xPd/C catalyst treated multiple spikes of concentrated ClO.sub.4 (10 g L.sup.1, which microbes could not tolerate) without deactivation,.sup.51 showing the important roles of coordination chemistry for water pollutant degradation.

[0155] Because the property tuning of anionic N,N,N,N-tetradentate ligands in Co complexes is challenging (e.g., limited locations for structural modification, tedious synthesis, and low solubility),.sup.52-54 we sought to yield similar functions of the porphyrin-Co complexes by mixing N,N-bidentate (R).sub.2bpy ligands with CoCl.sub.2 (FIG. 1D)..sup.55-59 We used nZn.sup.0 as the reducing agent, a promising electron source for groundwater remediation.sup.60-62 and a much cleaner reagent than citrate-Ti.sup.III for lab research..sup.30, 63 To our surprise, the control experiment without CoCl.sub.2 showed the highest defluorination performance. The new system even worked for linear PFCAs, suggesting the novel function of using R.sub.2bpy and nZn.sup.0 together. Hence, we optimized the reactivity and probed mechanisms of the ligand-enhanced traditional reduction system using metallic particles.

Materials and Methods

[0156] Chemicals. The nano-sized Zn.sup.0 powder was purchased from SkySpring Nanomaterials (9920XH, 99.7%, 40-60 nm).sup.30 and used as received. Additional details of the R.sub.2bpy ligands, PFAS substrates, inorganic chemicals, and the preparation of stock solutions are also provided in the Supporting Information (SI) section below.

[0157] Reactions. All reactions were conducted in an anaerobic glove bag (Coy Laboratories, 95% N.sub.2 and 5% H.sub.2). For a typical reaction, a 15 mL round-bottom flask was loaded with 10 mL of an aqueous suspension containing individual PFAS (0.1 mM), nZn.sup.0 (10 mg mL.sup.1), Me.sub.2bpy (0.025 mM), and NH.sub.4Cl buffer (10 mM, pH adjusted to 9.0). The flask was sealed with a rubber stopper (penetrated with a 22-gauge needle as the H.sub.2 outlet) and heated with 240 rpm magnetic stirring at 90 C. in a silicone oil bath. At designated reaction times, 1 mL of the suspension was collected and centrifuged at 12000 rpm to obtain the clear aqueous phase for further analysis.

[0158] Sample Analyses. The fluoride ion (F.sup.) was measured by an ion-selective electrode (ISE, Fisherbrand Accumet) with a Thermo Scientific Orion Versa Star Pro meter. Unlike Ti.sup.III-citrate,.sup.28 nZn.sup.0 did not interfere with the ISE measurement. Transformation products of selected PFAS were analyzed by liquid chromatography equipped with a high-resolution quadrupole orbitrap mass spectrometer (LC-HRMS/MS) (Q Exactive, Thermo Fisher Scientific) following established protocols..sup.64 Scanning transmission electron microscopy (STEM) characterization was conducted for both pristine and used nZn.sup.0. Further technical details are described in the SI.

Results and Discussion

[0159] Ligand-Enhanced Zn.sup.0 Reduction System. In the beginning, we added H.sub.2bpy to the mixture of CoCl.sub.2 and nZn.sup.0 for the defluorination of perfluoro-3,7-dimethyloctanoic acid (PF-3,7-Me.sub.2OA). The H.sub.2bpy+CoCl.sub.2+nZn.sup.0 combination yielded 2.4% of defluorination percentage (deF %), much lower than using corrin-Co and porphyrin-Co in the first 24 h (Table 1, entry 1 versus 11 and 12). However, the deF % by the control setting (H.sub.2bpy+nZn.sup.0, no CoCl.sub.2) surprisingly reached 36.6%. Further screening of various R.sub.2bpy ligands confirmed superior performance by nZn.sup.0 without CoCl.sub.2. The deF % by Me.sub.2bpy+nZn.sup.0 (Table 1, entry 2) exceeded those by corrin-Co and porphyrin-Co. Interestingly, the effect of R.sub.2bpy ligands did not follow the trend of Hammett constants of R (Table 1, entries 1, 2, and 5). Moreover, Cl.sub.2bpy resulted in very similar deF % as H.sub.2bpy (Table 1, entry 9 versus 1), probably due to the rapid reductive dechlorination by nZn.sup.0..sup.65 The nZn.sup.0 reduction of nitro group.sup.66 could also explain the similar deF % by using (NO.sub.2).sub.2bpy and (NH.sub.2).sub.2bpy (Table 1, entry 8 versus 6). In addition, mixing 1-3 equivalents of Me.sub.2bpy with ZnCl.sub.2 and citrate-Ti.sup.III (as a potential bulk reductant) resulted in no defluorination.

TABLE-US-00001 TABLE 1 Defluorination of PF-3, 7-Me2OA by Various Reaction Systems..sup.a ligand/catalyst deF % after 24 h (%) entry [00020] nZn.sup.0 only nZn.sup.0 + CoCl.sub.2 1 R = H 36.6 2.5 2.4 0.1 2 R = Me 68.2 3.1 5.6 2.1 (0.6% without nZn.sup.0) 3 R = tBu 28.0 0.2 11.7 0.5 4 R = OH 1.6 0.4 1.0 0.1 5 R = OMe 17.8 2.0 2.6 0.5 6 R = NH.sub.2 14.0 0.3 1.5 0.2 7 R = CN 43.1 0.7 4.0 0.1 8 R = NO.sub.2 14.1 1.2 1.3 0.3 9 R = Cl 33.6 1.6 24.5 0.8 10 no ligand 1.2 0.7 previous results (Ti.sup.III citrate as the reductant, reaction conditions optimized) 11 B.sub.12 (corrin-Co.sup.III) 31% 12 porphyrin-Co.sup.III 50% .sup.aReaction conditions: PF-3,7-Me.sub.2OA (0.1 mM), nZn.sup.0 (5 mg/mL.sup.1), individual ligand (0.25 mM), NH.sub.4Cl (10 mM), CoCl.sub.2 (0.125 mM, if added), initial pH 9.0, and 70 C. Errors indicate the standard deviation of triplicate reactions.

[0160] We used Me.sub.2bpy to sequentially optimize the dose of nZn.sup.0 (10 mg mL.sup.1), the concentration of Me.sub.2bpy (0.025 mM, one-tenth of the original level), temperature (90 C.), and pH (9.0) for the treatment of 0.1 mM PF-3,7-Me.sub.2OA (FIG. 4). Under the optimized conditions, the parent compound was fully degraded, and the deF % reached 84% within 4 h (FIG. 2A), corresponding to the cleavage of 16 of the 19 CF bonds in each PF-3,7-Me.sub.2OA molecule. Hence, the Me.sub.2bpy+nZn.sup.0 system outperformed the previous systems using Co complexes as catalysts..sup.28

[0161] The use of borate (pK.sub.a=9.23) as pH buffer yielded only 59% of defluorination, while those using ammonium buffers (pK.sub.a=9.25) with Cl.sup., SO.sub.4.sup.2, and CH.sub.3COO.sup. counter anions reached 80-83%. Borate is known for passivating Zn solid surface..sup.67 The optimized loading of nZn.sup.0 (10 g L.sup.1, equivalent to 154 mM if dissolved) far exceeded PF-3,7-Me.sub.2OA (0.1 mM). Hence, it appears that the reaction involved Zn.sup.0 below the outmost surface layer. Because nZn.sup.0 reacts with water and produces H.sub.2, the reaction stoichiometry could not be established between dissolved Zn.sup.2+ and released F.sup.. The ligand concentration (0.025 mM) is lower than the parent PF-3,7-Me.sub.2OA (0.1 mM) and released F.sup. (up to 1.6 mM). Hence, the Me.sub.2bpy ligand acted as a catalyst, whereas nZn.sup.0 served as the bulk reductant. The most probable reaction scheme is that Me.sub.2bpy binds to a Zn.sup.0 atom on the particle surface (see below for the heterogeneous nature of the reaction) and facilitates the reductive CF cleavage. The addition of CoCl.sub.2 competed for the ligand, thus resulting in a much lower deF % (Table 1). However, the ligand/metal stoichiometry and the coordination structure of the Me.sub.2bpy-Zn.sup.0 complex remain elusive. In addition, the -Me substitution was superior to both H and OMe, whereas OH and NH.sub.2 allowed unexpectedly low defluorination. Therefore, the binding pattern for all R.sub.2bpy ligands coordinating with the surface Zn.sup.0 is probably variable. The structure-activity relationship for the R.sub.2bpy ligands is different from another Mo-catalyzed heterogeneous system for aqueous perchlorate reduction, where (NH.sub.2).sub.2bpy outperformed all other ligands, including Me.sub.2bpy..sup.50

[0162] Defluorination of Various PFAS by Me.sub.2bpy-Zn.sup.0. In view of the high activity of Me.sub.2bpy-Zn.sup.0 in PF-3,7-Me.sub.2OA defluorination, we examined the reactivity with linear perfluorocarboxylates (PFCAs), which did not degrade in either CoZn.sup.0 or CoTi.sup.III systems..sup.28, 30 Surprisingly, PFOA (C.sub.7F.sub.15COO.sup.) showed 6.9% of defluorination within 4 h (FIG. 2B). Further extension of the substrate scope to longer (n=8-11) and shorter (n=2,6) C.sub.nF.sub.2n+1COO.sup. found a dependence on the fluoroalkyl chain length (Table 2, entries 1-8). Up to 60% of defluorination was achieved from long-chain linear PFCAs containing 17 to 23 CF bonds, corresponding to the cleavage of 6 to 11 CF bonds from the parent structures. In contrast, short-chain PFCAs showed negligible defluorination.

TABLE-US-00002 TABLE 2 Defluorination of various PFAS by the Me.sub.2bpy-Zn.sup.0 Systems..sup.a abbreviated # of F.sup. released entry PFAS structure name deF % at 8 h per molecule perfluorocarboxylate [PFCA] 1 C.sub.2F.sub.5COO.sup. PFPrA 1.6% 0.1/5 2 C.sub.6F.sub.13COO.sup. PFHpA 1.3% 0.2/13 3 C.sub.7F.sub.15COO.sup. PFOA 6.9% 1.0/15 4 C.sub.8F.sub.17COO.sup. PFNA 33% 5.7/17 5 C.sub.9F.sub.19COO.sup. PFDA 60% 11.3/19 6 [00021] PF-3,7-Me.sub.2OA 85% 16.2/19 7 C.sub.10F.sub.21COO.sup. PFUdA 53% 11.2/21 8 C.sub.11F.sub.23COO.sup. PFDdA 41% 9.4/23 fluorotelomer carboxylate [FTCA] 9 C.sub.4F.sub.9CH.sub.2CH.sub.2COO.sup. 4:3 FTCA 0.2% 0.0/9 10 C.sub.6F.sub.13CH.sub.2CH.sub.2COO.sup. 6:3 FTCA 0.6% 0.1/13 11 C.sub.8F.sub.17CH.sub.2CH.sub.2COO.sup. 8:3 FTCA 0.5% 0.1/17 Perfluoroalkane sulfonate [PFSA] 12 C.sub.4F.sub.9SO.sub.3.sup. PFBS 1.5% 0.1/9 13 C.sub.6F.sub.13SO.sub.3.sup. PFHxS 4.7% 0.6/13 14 C.sub.8F.sub.17SO.sub.3.sup. PFOS 9.1% 1.5/17 perfluorodicarboxylate [PFdiCA] 15 .sup.OOCC.sub.6F.sub.12COO.sup. 4.6% 0.6/12 16 .sup.OOCC.sub.8F.sub.16COO.sup. 7.7% 1.2/16 perfluoroether carboxylate [PFECA] hexafluoropropylene oxide oligomer acid [HFPO-XA], branched 17 [00022] HFPO-DA (GenX) 0.3% 0.0/9 18 [00023] HFPO-TeA 12% 2.7/23 linear 19 [00024] 1 + 2 + 2 6.7% 0.6/9 20 [00025] 1 + 2 + 2 + 2 26% 3.4/13 chlorinated polyfluorocarboxylate [Cl.sub.xPFCA] 21 [00026] Cl.sub.2PFBA 55%, 80%, 92% at 8 h, 24 h, 48 h.sup.b 4.6/5 (48 h) 22 [00027] Cl.sub.3PFHxA 86%, 100% at 15 min, 4 h.sup.b 8/8 23 [00028] Cl.sub.4PFOA 96%, 101% at 15 min, 30 min.sup.b 11/11 .sup.aReaction conditions: individual PFAS (0.1 mM), nZn.sup.0 powder (10 mg/mL.sup.1), Me.sub.2bpy (0.025 mM), NH.sub.4Cl (10 mM), initial pH 9.0, 90 C., 8 h. .sup.bTime profiles at both 90 C. and 20 C. are shown in FIG. 2.

[0163] We hypothesized that the long fluoroalkyl chain (containing weak CF bonds, FIG. 2C) was a contributing factor for defluorination. Hence, we further tested three fluorotelomer carboxylates (FTCAs, C.sub.nF.sub.2n+1CH.sub.2CH.sub.2COO.sup., Table 2, entries 9-11). However, even the longest n=8 FTCA (FIG. 2C) did not allow defluorination. Notably, C.sub.8F.sub.17CH.sub.2CH.sub.2COO.sup. have the same number of total carbon as C.sub.10F.sub.21COO.sup. (Table 2, entry 11 versus 7) and the same number of fluorinated carbon as C.sub.8F.sub.17COO.sup. (Table 2, entry 11 versus 4). Therefore, the molecular reactivity might be influenced by the direct link between the fluoroalkyl chain and the carboxylate group. The three perfluoroalkane sulfonates (PFSAs, C.sub.nF.sub.2n+1SO.sub.3.sup.) showed slightly higher deF % than FTCAs. While we could not rule out the possibility of defluorination from branched isomers in PFSA reagents,.sup.30 the largely different deF % from C.sub.8F.sub.17SO.sub.3 and C.sub.8F.sub.17COO.sup. (Table 2, entry 14 versus 4) suggest the important role of the carboxylate group. The general trend of much higher reactivity of PFCAs than PFSAs and FTCAs is similar to that observed in a homogeneous reaction system, which used hydrated electrons generated from sulfite under 254 nm UV irradiation..sup.68

[0164] However, the hydrophobicity of PFAS might be another contributing factor. When the terminal CF.sub.3 in C.sub.9F.sub.19COO.sup. was replaced by another carboxylate (COOC.sub.8F.sub.16COO PFdiCA, FIG. 2C), the deF % was significantly lowered (Table 2, entry 16 versus 5). In contrast, in the homogeneous UV/sulfite system, PFdiCAs allowed faster and higher deF % than PFCAs..sup.64,68 Hence, the reduced hydrophobicity of PFdiCAs is the most probable cause for the diminished deF % by Me.sub.2bpy-Zn.sup.0. We further examined four perfluoroethercarboxylates (PFECAs) with varying linear/branch patterns and chain lengths (Table 2, entries 17-20). The results corroborate the role of the carboxylate group and the dependence on the chain length. In particular, the branched, longer, and more hydrophobic hexafluoropropylene oxide tetramer acid (HFPO-TeA) showed a lower deF % than the linear, shorter, and less hydrophobic structure (Table 2, entry 18 versus 20). Therefore, the degradability of the former is inferior to the latter, similar to the trend observed for PFECA defluorination in the homogeneous UV/sulfite system..sup.69

[0165] An earlier study found that the chlorinated polyfluorocarboxylate, Cl.sub.4-PFOA (structure shown in Table 2, entry 23), could react with acid-treated 30-mesh (<600 m) Zn.sup.0 grains at room temperature and release up to four F from each Cl.sub.4-PFOA molecule in 5 days..sup.33 We used nZn.sup.0 powder (20-500 nm, FIG. 5) at 20 C. and achieved 100% defluorination within 24 h (FIG. 2D). As expected, the shorter-chain Cl.sub.3-PFHxA and Cl.sub.2-PFBA yielded lower deF %. Adding Me.sub.2bpy not only accelerated the defluorination from Cl.sub.4-PFOA, but also allowed deeper defluorination from Cl.sub.3-PFHxA and Cl.sub.2-PFBA (FIG. 2E). Elevating the temperature to 90 C. still could not achieve 100% defluorination from Cl.sub.2-PFBA (FIG. 2F). Because the bond dissociation energies of CF and CCl are similar among the three Cl.sub.xPFCAs,.sup.70 the difference in reactivity is most likely attributed to mass transfer, further consolidating the heterogeneous nature of the Me.sub.2bpy-Zn.sup.0 system.

[0166] In addition to the bipyridine ligands, certain triple-ring ligands, such as 1,10-Phenanthroline ligands, were also investigated (see Table 3) in this Example 1, and showed similar or superior performance as compared to Me.sub.2bpy.

TABLE-US-00003 TABLE 3 Defluorination of linear PFDA (C.sub.9F.sub.19COO.sup.) by various triple-ring ligands in comparison to 4,4-dimethyl-2,2-bipyridine..sup.a entry ligand/catralyst deF % after 4 h (%) 1 [00029] 9.5 2 [00030] 24.5 3 [00031] 56.0 4 [00032] 24.1 5 [00033] 32.3 6 [00034] 10.7 7 [00035] 1.2 8 [00036] 5.8 9 [00037] 7.9 10 [00038] 26.0.sup.b .sup.aReaction conditions: PFDA (0.1 mM), nZn.sup.0 powder (10 mg mL.sup.1), individual ligand (0.025 mM), NH.sub.4Cl (10 mM), initial pH 9.0, 90 C., 4 h. .sup.bThe deF % value is less than earlier results due to the aging and slow oxidation of the same batch of nZn.sup.0 powder. However, all data in this table 3 were produced in the same batch, so direct comparison among these ligands is valid. Significantly higher deF % values are expected with freshly made nZn.sup.0 powder in the same or different sizes.

[0167] Mechanistic Insights. Beyond confirming the heterogeneous nature of the reaction system, our current experimental approaches cannot probe more detailed information at the molecular level.

[0168] Nevertheless, the outstanding performance by Me.sub.2bpy among various R.sub.2bpy ligands (without following the trend of Hammett constants) may indicate the complexity of the R.sub.2bpy-Zn coordination pattern. Moreover, the primary role of Me.sub.2bpy is likely not to enhance the mass transfer of PFAS to the nZn.sup.0 surface. First, the initial probe, PF-3,7-Me.sub.2PFOA, is a highly hydrophobic structure and thus strongly favors aggregation at the heterogeneous interface. But the control experiment without ligand yielded negligible defluorination (Table 1, entry 10). In comparison, Cl.sub.4-PFOA was completely defluorinated at the nZn.sup.0 surface without Me.sub.2bpy. Second, adding octadecyltrimethylammonium chloride (C.sub.18TMAC), a cationic surfactant used for enhancing the mass transfer of high-solubility anionic PFAS to the reactive water-gas interface,.sup.71 did not increase the deF % of PFOA by Me.sub.2bpy-Zn.sup.0 (5.3%, versus 6.9% without C.sub.18TMAC).

[0169] In earlier studies on B.sub.12-catalyzed dechlorination of sp.sup.3 CCl bonds in CCl.sub.4 and ClCH.sub.2CN, mechanisms with various differences in subtle details were proposed. In general, (L)Co.sup.1 could attack the CCl bond and yield (L)Co.sup.IIIC and Cl.sup...sup.72 When (L)Co.sup.II was the catalytic center, the single electron transfer converted the CCl into a C.Math. radical and Cl.sup...sup.73, 74 Because Zn.sup.II is not reductive and Zn.sup.1 is rare,.sup.75 the most probable reaction species is Me.sub.2bpy-coordinated Zn.sup.0. However, C.sub.8F.sub.17COO.sup., C.sub.8F.sub.17CH.sub.2CH.sub.2COO.sup., and C.sub.8F.sub.17SO.sub.3 all contain weak CF bonds (FIG. 2C) but exhibit very different reactivities (Table 2, entries 4, 11, and 14). Thus, the selective attack of weak CF by Zn.sup.0 (i.e., forming Zn.sup.IIC bonds at specific positions) is less likely. Instead, we propose that two electrons were directly transferred from Me.sub.2bpy-Zn.sup.0 to the adsorbed PFAS molecule. Our preliminary analysis of transformation products from C.sub.9F.sub.19COO.sup. found two H/F exchange intermediates (C.sub.9F.sub.18HCOO.sup. and C.sub.9F.sub.16H.sub.3COO.sup.) and one chain-shortened intermediate (C.sub.8F.sub.17COO.sup.). These products suggest similar reaction pathways found in the homogeneous UV/sulfite system that generates hydrated electrons (e.sub.aq.sup.):

CF+2e.sub.aq.sup.+H.sup.+.fwdarw.CH+F.sup.(1)

CF+[ligand-Zn.sup.0]+H.sup.+.fwdarw.CH+F.sup.+[ligand-Zn.sup.2+](2)

Further comparison of deF % values for various PFAS by Me.sub.2bpy-Zn.sup.0 and UV/sulfite.sup.68, 69 also found high similarities for the long-chain PFAS (FIG. 3). At this moment, the mechanistic discussion could not go further because the reductive defluorination processes have not been well understood, such as how the chain-shortening occurred via a reductive process..sup.76 In addition, how the Me.sub.2bpy ligand facilitates electron transfer from Zn.sup.0 to PFAS remains elusive and warrants further investigation.

[0170] Implications for Environmental Remediation. The Me.sub.2bpy ligand surprisingly led to reductive defluorination from linear PFCAs and PFECAs by nZn.sup.0. Together with the smaller metallic particles and elevated temperature, the addition of Me.sub.2bpy shortened the half-life of the first reductive defluorination step for PFOA from the model-predicted 7 years.sup.33 to the experimentally observed 4 hours. The current Me.sub.2bpy-Zn.sup.0 system may not fully satisfy all the requirements of PFAS degradation in certain polluted water samples, particularly for (i) limited reactivity toward short-chain PFAS and (ii) limited reactivity toward PFSAs and FTCAs. Extension of the PFAS substrate scope is urgent for many recently reported technologies that only demonstrated the efficacy toward PFOA. For the ligand-nZn.sup.0 system, we emphasize the high promise of coordination chemistry to further enhance intrinsic reactivity (and other approaches to enhance mass transfer of short-chain PFAS).

[0171] The use of Zn.sup.0 for environmental remediation has been explored for chlorinated organic pollutants..sup.33,60-62 This study shows that specific organic ligands could add or enhance the reactivity of Zn.sup.0 with fluorinated chemicals. The current selectivity toward long-chain PFAS has a significant value for in situ groundwater or soil remediation. Long-chain PFAS are highly hydrophobic, strongly bind to soil organics, and thus cannot be effectively cleaned via the ex situ pump-and-treat strategy..sup.77, 78 In multiple surface soil samples of the U.S. East Coast region, the n=8-11 C.sub.nF.sub.2n+1COO took more than 50% of the total PFCAs..sup.79 Chlorine-containing PFAS, which have much higher reactivity with Zn.sup.0 than perfluorinated counterparts, have also been confirmed as widespread soil pollutants..sup.80-82 Hence, a reactive barrier loaded with metallic particles and organic ligands may be a viable technical solution for in situ PFAS remediation.

Supporting Information

PFAS Chemicals.

[0172] PFAS chemicals were purchased from Oakwood Chemicals (OC), Apollo Scientific (AS), Manchester Organics (MO), and SynQuest Laboratories (SQ). Table A1 summarizes the name, purity, and CAS number.

TABLE-US-00004 TABLE A1 PFAS chemicals tested in this study. Stock Solution Preparation Number of Fluorinated Entry Chemical Name Carbons Purity CAS# Cl(CF.sub.2).sub.nCOOH (or sodium salt) 1 sodium chlorodifluoroacetate 1 97% 1895-39-2 2 3-chlorotetrafluoropropionic acid 2 97% 661-82-5 3 5-chlorooctafluoropentanoic acid 4 N/A 66443-79-6 4 9-chlorohexadecafluorononanoic acid 8 97% 865-79-2 ClCF.sub.2(CFClCF.sub.2).sub.nCOOH 5 3,4-dichloropentafluorobutyric acid 4 97% 375-07-5 6 3,5,6-trichlorooctafluorohexanoic acid 6 95% 2106-54-9 7 3,5,7,8-tetrachloroperfluorooctanoic acid 8 95% 2923-68-4 special structures 8 potassium 9-chlorohexadecafluoro-3-oxanonane-1-sulfonate 6:2 ether 97% 73606-19-6 9 perfluoro(2-ethoxyethane)sulfonic acid 2:2 ether 97% 113507-82-7 10 2-(fluorosulfonyl)difluoroacetic acid 1 98% 1717-59-5

[0173] Stock solutions were prepared with degassed solvents in an anaerobic glove bag (95% N.sub.2 and 5% H.sub.2 atmosphere; Coy Laboratories). PFASs were dissolved in methanol as 15 mM stock solutions. Substituted 2,2-bipyridine ligands were dissolved in ethanol as 5 mM stock solutions. CoCl.sub.2 was dissolved in DI water as 5 mM stock solution. Ammonia-ammonium buffer was prepared by dissolving 107.0 mg NH.sub.4Cl in a 200 mL DI water, followed by adding 0.1 M NaOH solution until the pH reached 9.0.

LC-HRMS Analysis.

[0174] All samples were diluted by 10 times and centrifuged at 12000 rpm before dilution for MS analysis.

STEM Analysis.

[0175] Zn particles after reaction were filtered by DI water, and dried at 90 C. in the glove bag before the characterization by a scanning transmission electron microscope (STEM, FEI Titan Themis 300) equipped with an energy dispersive X-ray spectrometer (EDS) system at 300 kV accelerating voltage. STEM images were acquired with a high-angle annular dark-field (HAADF) detector.

[0176] Our attempts found that energy-dispersive X-ray (EDX) elemental analysis might be unsuitable for characterizing either Me.sub.2bpy or PFAS adsorbed on the nZn.sup.0 surface. The thin organic layer could emit negligible signal compared to the bulk non-porous Zn particles.

REFERENCES IN EXAMPLE 1

[0177] 1. Hori, H.; Nagaoka, Y.; Murayama, M.; Kutsuna, S., Efficient decomposition of perfluorocarboxylic acids and alternative fluorochemical surfactants in hot water. Environmental Science & Technology 2008, 42, 7438-7443. [0178] 2. Wu, B.; Hao, S.; Choi, Y.; Higgins, C. P.; Deeb, R.; Strathmann, T. J., Rapid destruction and defluorination of perfluorooctanesulfonate by alkaline hydrothermal reaction. Environmental science & technology letters 2019, 6, 630-636. [0179] 3. Hao, S.; Choi, Y.-J.; Wu, B.; Higgins, C. P.; Deeb, R.; Strathmann, T. J., Hydrothermal alkaline treatment for destruction of per- and polyfluoroalkyl substances in aqueous film-forming foam. Environmental Science & Technology 2021, 55, 3283-3295. [0180] 4. Hori, H.; Hayakawa, E.; Einaga, H.; Kutsuna, S.; Koike, K.; Ibusuki, T.; Kiatagawa, H.; Arakawa, R., Decomposition of environmentally persistent perfluorooctanoic acid in water by photochemical approaches. Environmental science & technology 2004, 38, 6118-6124. [0181] 5. Huang, L.; Dong, W.; Hou, H., Investigation of the reactivity of hydrated electron toward perfluorinated carboxylates by laser flash photolysis. Chemical Physics Letters 2007, 436, 124-128. [0182] 6. Park, H.; Vecitis, C. D.; Cheng, J.; Choi, W.; Mader, B. T.; Hoffmann, M. R., Reductive defluorination of aqueous perfluorinated alkyl surfactants: Effects of ionic headgroup and chain length. The Journal of Physical Chemistry A 2009, 113, 690-696. [0183] 7. Li, X.; Ma, J.; Liu, G.; Fang, J.; Yue, S.; Guan, Y.; Chen, L.; Liu, X., Efficient reductive dechlorination of monochloroacetic acid by sulfite/UV process. Environmental science & technology 2012, 46, 7342-7349. [0184] 8. Liu, Z.; Chen, Z.; Gao, J.; Yu, Y.; Men, Y.; Gu, C.; Liu, J., Accelerated Degradation of Perfluorosulfonates and Perfluorocarboxylates by UV/Sulfite+Iodide: Reaction Mechanisms and System Efficiencies. Environmental Science & Technology 2022, 56, 3699-3709. [0185] 9. Liu, Z.; Bentel, M. J.; Yu, Y.; Ren, C.; Gao, J.; Pulikkal, V. F.; Sun, M.; Men, Y.; Liu, J., Near-Quantitative Defluorination of Perfluorinated and Fluorotelomer Carboxylates and Sulfonates with Integrated Oxidation and Reduction. Environmental Science & Technology 2021. [0186] 10. Hori, H.; Yamamoto, A.; Hayakawa, E.; Taniyasu, S.; Yamashita, N.; Kutsuna, S.; Kiatagawa, H.; Arakawa, R., Efficient decomposition of environmentally persistent perfluorocarboxylic acids by use of persulfate as a photochemical oxidant. Environmental Science & Technology 2005, 39, 2383-2388. [0187] 11. Qanbarzadeh, M.; Wang, D.; Ateia, M.; Sahu, S. P.; Cates, E. L., Impacts of Reactor Configuration, Degradation Mechanisms, and Water Matrices on Perfluorocarboxylic Acid Treatment Efficiency by the UV/Bi3O(OH)(PO4)2 Photocatalytic Process. ACS ES & T Engineering 2020. [0188] 12. Stratton, G. R.; Dai, F.; Bellona, C. L.; Holsen, T. M.; Dickenson, E. R.; Mededovic Thagard, S., Plasma-based water treatment: efficient transformation of perfluoroalkyl substances in prepared solutions and contaminated groundwater. Environmental science & technology 2017, 51, 1643-1648. [0189] 13. Saleem, M.; Biondo, O.; Sretenovid, G.; Tomei, G.; Magarotto, M.; Pavarin, D.; Marotta, E.; Paradisi, C., Comparative performance assessment of plasma reactors for the treatment of PFOA; reactor design, kinetics, mineralization and energy yield. Chemical Engineering Journal 2020, 382, 123031. [0190] 14. Singh, R. K.; Multari, N.; Nau-Hix, C.; Woodard, S.; Nickelsen, M.; Mededovic Thagard, S.; Holsen, T. M., Removal of Poly- and Per-Fluorinated Compounds from Ion Exchange Regenerant Still Bottom Samples in a Plasma Reactor. Environmental Science & Technology 2020, 54, 13973-13980. [0191] 15. Singh, R. K.; Brown, E.; Thagard, S. M.; Holsen, T. M., Treatment of PFAS-containing landfill leachate using an enhanced contact plasma reactor. Journal of Hazardous Materials 2021, 408, 124452. [0192] 16. Niu, J.; Lin, H.; Gong, C.; Sun, X., Theoretical and experimental insights into the electrochemical mineralization mechanism of perfluorooctanoic acid. Environmental science & technology 2013, 47, 14341-14349. [0193] 17. Yang, S.; Fernando, S.; Holsen, T. M.; Yang, Y., Inhibition of perchlorate formation during the electrochemical oxidation of perfluoroalkyl acid in groundwater. Environmental Science & Technology Letters 2019, 6, 775-780. [0194] 18. Huang, D.; Wang, K.; Niu, J.; Chu, C.; Weon, S.; Zhu, Q.; Lu, J.; Stavitski, E.; Kim, J.-H., Amorphous Pd-Loaded Ti4O7 Electrode for Direct Anodic Destruction of Perfluorooctanoic Acid. Environmental Science & Technology 2020, 54, 10954-10963. [0195] 19. Radjenovic, J.; Duinslaeger, N.; Avval, S. S.; Chaplin, B. P., Facing the challenge of poly- and perfluoroalkyl substances in water: is electrochemical oxidation the answer?Environmental Science & Technology 2020, 54, 14815-14829. [0196] 20. Sidnell, T.; Wood, R. J.; Hurst, J.; Lee, J.; Bussemaker, M. J., Sonolysis of Per- And Poly Fluoroalkyl Substances (PFAS): A meta-analysis. Ultrasonics sonochemistry 2022, 105944. [0197] 21. Vecitis, C. D.; Park, H.; Cheng, J.; Mader, B. T.; Hoffmann, M. R., Kinetics and mechanism of the sonolytic conversion of the aqueous perfluorinated surfactants, perfluorooctanoate (PFOA), and perfluorooctane sulfonate (PFOS) into inorganic products. The Journal of Physical Chemistry A 2008, 112, 4261-4270. [0198] 22. Zhang, Z.; Chen, J.-J.; Lyu, X.-J.; Yin, H.; Sheng, G.-P., Complete mineralization of perfluorooctanoic acid (PFOA) by 7-irradiation in aqueous solution. Scientific reports 2014, 4, 1-6. [0199] 23. Trojanowicz, M.; Bartosiewicz, I.; Bojanowska-Czajka, A.; Kulisa, K.; Szreder, T.; Bobrowski, K.; Nichipor, H.; Garcia-Reyes, J. F.; Nalcz-Jawecki, G.; Mczyska-Wielgosz, S., Application of ionizing radiation in decomposition of perfluorooctanoate (PFOA) in waters. Chemical Engineering Journal 2019, 357, 698-714. [0200] 24. Trojanowicz, M.; Bartosiewicz, I.; Bojanowska-Czajka, A.; Szreder, T.; Bobrowski, K.; Nalcz-Jawecki, G.; Mczyska-Wielgosz, S.; Nichipor, H., Application of ionizing radiation in decomposition of perfluorooctane sulfonate (PFOS) in aqueous solutions. Chemical Engineering Journal 2020, 379, 122303. [0201] 25. Trang, B.; Li, Y.; Xue, X.-S.; Ateia, M.; Houk, K.; Dichtel, W. R., Low-temperature mineralization of perfluorocarboxylic acids. Science 2022, 377, 839-845. [0202] 26. Zhang, C.; McElroy, A. C.; Liberatore, H. K.; Alexander, N. L. M.; Knappe, D. R., Stability of Per- and Polyfluoroalkyl Substances in Solvents Relevant to Environmental and Toxicological Analysis. Environmental Science & Technology 2021. [0203] 27. Ochoa-Herrera, V.; Sierra-Alvarez, R.; Somogyi, A.; Jacobsen, N. E.; Wysocki, V. H.; Field, J. A., Reductive defluorination of perfluorooctane sulfonate. Environmental Science & Technology 2008, 42, 3260-3264. [0204] 28. Liu, J.; Van Hoomissen, D. J.; Liu, T.; Maizel, A.; Huo, X.; Fernndez, S. R.; Ren, C.; Xiao, X.; Fang, Y.; Schaefer, C. E., Reductive defluorination of branched per- and polyfluoroalkyl substances with cobalt complex catalysts. Environmental Science & Technology Letters 2018, 5, 289-294. [0205] 29. Sun, J.; Jennepalli, S.; Lee, M.; Jones, A.; O'Carroll, D. M.; Manefield, M. J.; Bhadbhade, M.; Akermark, B. r.; Das, B.; Kumar, N., Efficient Reductive Defluorination of Branched PFOS by Metal-Porphyrin Complexes. Environmental Science & Technology 2022. [0206] 30. Park, S.; de Perre, C.; Lee, L. S., Alternate reductants with VB12 to transform C8 and C6 perfluoroalkyl sulfonates: Limitations and insights into isomer-specific transformation rates, products and pathways. Environmental Science & Technology 2017, 51, 13869-13877. [0207] 31. Sun, Z.; Geng, D.; Zhang, C.; Chen, J.; Zhou, X.; Zhang, Y.; Zhou, Q.; Hoffmann, M. R., Vitamin B12 (CoII) initiates the reductive defluorination of branched perfluorooctane sulfonate (br-PFOS) in the presence of sulfide. Chemical Engineering Journal 2021, 423, 130149. [0208] 32. Li, F.; Yang, N.; Yang, Z.; Cao, W.; Zhou, Z.; Liao, X.; Sun, W.; Yuan, B., Biomimetic degradability of linear perfluorooctanesulfonate (L-PFOS): Degradation products and pathways. Chemosphere 2020, 259, 127502. [0209] 33. Blotevogel, J.; Giraud, R. J.; Borch, T., Reductive defluorination of perfluorooctanoic acid by zero-valent iron and zinc: A DFT-based kinetic model. Chemical Engineering Journal 2018, 335, 248-254. [0210] 34. Bullock, R. M.; Chen, J. G.; Gagliardi, L.; Chirik, P. J.; Farha, O. K.; Hendon, C. H.; Jones, C. W.; Keith, J. A.; Klosin, J.; Minteer, S. D., Using nature's blueprint to expand catalysis with Earth-abundant metals. Science 2020, 369, eabc3183. [0211] 35. Holm, R. H.; Solomon, E. I., Preface: biomimetic inorganic chemistry. Chemical Reviews 2004, 104, 347-348. [0212] 36. Jans, U.; Prasse, C.; von Gunten, U., Enhanced treatment of municipal wastewater effluents by Fe-Taml/H2O2: Efficiency of micropollutant abatement. Environmental Science & Technology 2021, 55, 3313-3321. [0213] 37. Collins, T. J., TAML oxidant activators: a new approach to the activation of hydrogen peroxide for environmentally significant problems. Accounts of chemical research 2002, 35, 782-790. [0214] 38. Collins, T. J.; Ryabov, A. D., Targeting of high-valent iron-TAML activators at hydrocarbons and beyond. Chemical reviews 2017, 117, 9140-9162. [0215] 39. Canals, M.; Gonzalez-Olmos, R.; Costas, M.; Company, A., Robust iron coordination complexes with N-based neutral ligands as efficient Fenton-like catalysts at neutral pH. Environmental science & technology 2013, 47, 9918-9927. [0216] 40. Ellis, W. C.; Tran, C. T.; Denardo, M. A.; Fischer, A.; Ryabov, A. D.; Collins, T. J., Design of more powerful iron-TAML peroxidase enzyme mimics. Journal of the American Chemical Society 2009, 131, 18052-18053. [0217] 41. Kundu, S.; Chanda, A.; Khetan, S. K.; Ryabov, A. D.; Collins, T. J., TAML activator/peroxide-catalyzed facile oxidative degradation of the persistent explosives trinitrotoluene and trinitrobenzene in micellar solutions. Environmental science & technology 2013, 47, 5319-5326. [0218] 42. Tang, L. L.; DeNardo, M. A.; Gayathri, C.; Gil, R. R.; Kanda, R.; Collins, T. J., TAML/H.sub.2O.sub.2 oxidative degradation of metaldehyde: pursuing better water treatment for the most persistent pollutants. Environmental Science & Technology 2016, 50, 5261-5268. [0219] 43. Huang, J.; Jones, A.; Waite, T. D.; Chen, Y.; Huang, X.; Rosso, K. M.; Kappler, A.; Mansor, M.; Tratnyek, P. G.; Zhang, H., Fe (II) redox chemistry in the environment. Chemical reviews 2021, 121, 8161-8233. [0220] 44. Hurley, K. D.; Zhang, Y.; Shapley, J. R., Ligand-Enhanced Reduction of Perchlorate in Water with Heterogeneous RePd/C Catalysts. Journal of the American Chemical Society 2009, 131, 14172-14173. [0221] 45. Liu, J.; Choe, J. K.; Wang, Y.; Shapley, J. R.; Werth, C. J.; Strathmann, T. J., Bioinspired complex-nanoparticle hybrid catalyst system for aqueous perchlorate reduction: Rhenium speciation and its influence on catalyst activity. ACS Catalysis 2015, 5, 511-522. [0222] 46. Liu, J.; Chen, X.; Wang, Y.; Strathmann, T. J.; Werth, C. J., Mechanism and mitigation of the decomposition of an oxorhenium complex-based heterogeneous catalyst for perchlorate reduction in water. Environmental science & technology 2015, 49, 12932-12940. [0223] 47. Liu, J.; Su, X.; Han, M.; Wu, D.; Gray, D. L.; Shapley, J. R.; Werth, C. J.; Strathmann, T. J., Ligand design for isomer-selective oxorhenium (V) complex synthesis. Inorganic chemistry 2017, 56, 1757-1769. [0224] 48. Ren, C.; Liu, J., Bioinspired Catalytic Reduction of Aqueous Perchlorate by One Single-Metal Site with High Stability against Oxidative Deactivation. ACS Catalysis 2021, 11, 6715-6725. [0225] 49. Ren, C.; Yang, P.; Gao, J.; Huo, X.; Min, X.; Bi, E. Y.; Liu, Y.; Wang, Y.; Zhu, M.; Liu, J., Catalytic Reduction of Aqueous Chlorate With MoOx Immobilized on Pd/C. ACS Catalysis 2020, 10, 8201-8211. [0226] 50. Ren, C.; Yang, P.; Sun, J.; Bi, E. Y.; Gao, J.; Palmer, J.; Zhu, M.; Wu, Y.; Liu, J., A Bioinspired Molybdenum Catalyst for Aqueous Perchlorate Reduction. Journal of the American Chemical Society 2021, 143, 7891-7896. [0227] 51. Ren, C.; Bi, E. Y.; Gao, J.; Liu, J., Molybdenum-Catalyzed Perchlorate Reduction: Robustness, Challenges, and Solutions. ACS ES & T Engineering 2022, 2, 181-188. [0228] 52. Hiroto, S.; Miyake, Y.; Shinokubo, H., Synthesis and functionalization of porphyrins through organometallic methodologies. Chemical reviews 2017, 117, 2910-3043. [0229] 53. Marlier, E. E.; Ulrich, B. A.; McNeill, K., Synthesis and reactivity of an isolable cobalt (I) complex containing a -diketiminate-based acyclic tetradentate ligand. Inorganic chemistry 2012, 51, 2079-2085. [0230] 54. Fritsch, J. M.; McNeill, K., Aqueous reductive dechlorination of chlorinated ethylenes with tetrakis (4-carboxyphenyl) porphyrin cobalt. Inorganic chemistry 2005, 44, 4852-4861. [0231] 55. Droghetti, F.; Lucarini, F.; Molinari, A.; Ruggi, A.; Natali, M., Recent findings and future directions in photosynthetic hydrogen evolution using polypyridine cobalt complexes. Dalton Transactions 2022. [0232] 56. He, W.; Fontmorin, J.-M.; Hapiot, P.; Soutrel, I.; Floner, D.; Fourcade, F.; Amrane, A.; Geneste, F., A new bipyridyl cobalt complex for reductive dechlorination of pesticides. Electrochimica Acta 2016, 207, 313-320. [0233] 57. Kliegman, S.; McNeill, K., Dechlorination of chloroethylenes by cob (I) alamin and cobalamin model complexes. Dalton Transactions 2008, 4191-4201. [0234] 58. McCauley, K. M.; Wilson, S. R.; Van der Donk, W. A., Synthesis and characterization of chlorinated alkenylcobaloximes to probe the mechanism of vitamin B12-catalyzed dechlorination of priority pollutants. Inorganic Chemistry 2002, 41, 393-404. [0235] 59. Margel, S.; Anson, F. C., Catalysis of the Electroreduction of Allyl Chloride by Cobalt 2, 2-Bipyridine Complexes. Journal of The Electrochemical Society 1978, 125, 1232. [0236] 60. Roberts, A. L.; Totten, L. A.; Arnold, W. A.; Burris, D. R.; Campbell, T. J., Reductive elimination of chlorinated ethylenes by zero-valent metals. Environmental Science & Technology 1996, 30, 2654-2659. [0237] 61. Sarathy, V.; Salter, A. J.; Nurmi, J. T.; O'Brien Johnson, G.; Johnson, R. L.; Tratnyek, P. G., Degradation of 1, 2, 3-trichloropropane (TCP): hydrolysis, elimination, and reduction by iron and zinc. Environmental Science & Technology 2010, 44, 787-793. [0238] 62. Salter-Blanc, A. J.; Tratnyek, P. G., Effects of solution chemistry on the dechlorination of 1, 2, 3-trichloropropane by zero-valent zinc. Environmental science & technology 2011, 45, 4073-4079. [0239] 63. Zehnder, A. J.; Wuhrmann, K., Titanium (III) citrate as a nontoxic oxidation-reduction buffering system for the culture of obligate anaerobes. Science 1976, 194, 1165-1166. [0240] 64. Gao, J.; Liu, Z.; Bentel, M. J.; Yu, Y.; Men, Y.; Liu, J., Defluorination of Omega-Hydroperfluorocarboxylates (HPFCAs): Distinct Reactivities from Perfluoro and Fluorotelomeric Carboxylates. Environmental Science & Technology 2021. [0241] 65. Arnold, W. A.; Roberts, A. L., Pathways of chlorinated ethylene and chlorinated acetylene reaction with Zn (0). Environmental Science & Technology 1998, 32, 3017-3025. [0242] 66. ROBERTSON, G. R.; EVANS, R. A., The formation of chloroaniline during reduction of nitrobenzene. The Journal of Organic Chemistry 1940, 5, 142-145. [0243] 67. Diomidis, N.; Celis, J.-P., Anodic film formation on zinc in alkaline electrolytes containing silicate and tetraborate ions. Journal of The Electrochemical Society 2007, 154, C711. [0244] 68. Bentel, M. J.; Yu, Y.; Xu, L.; Li, Z.; Wong, B. M.; Men, Y.; Liu, J., Defluorination of per- and polyfluoroalkyl substances (PFASs) with hydrated electrons: Structural dependence and implications to PFAS remediation and management. Environmental science & technology 2019, 53, 3718-3728. [0245] 69. Bentel, M. J.; Yu, Y.; Xu, L.; Kwon, H.; Li, Z.; Wong, B. M.; Men, Y.; Liu, J., Degradation of perfluoroalkyl ether carboxylic acids with hydrated electrons: Structure-reactivity relationships and environmental implications. Environmental science & technology 2020, 54, 2489-2499. [0246] 70. Gao, J.; Liu, Z.; Huang, J.; Liu, J., Degradation Pathways and Complete Defluorination of Chlorinated Polyfluoroalkyl Substances (Cl.sub.x-PFAS). ChemRxiv 2022, 10.26434/chemrxiv-2022-ql20q. [0247] 71. Nau-Hix, C.; Multari, N.; Singh, R. K.; Richardson, S.; Kulkarni, P.; Anderson, R. H.; Holsen, T. M.; Mededovic Thagard, S., Field demonstration of a pilot-scale plasma reactor for the rapid removal of poly- and perfluoroalkyl substances in groundwater. ACS ES & T Water 2021, 1, 680-687. [0248] 72. Argello, J. E.; Costentin, C.; Griveau, S.; Savant, J.-M., Role of protonation and of axial ligands in the reductive dechlorination of alkyl chlorides by vitamin B12 complexes. Reductive cleavage of chloroacetonitrile by Co (I) cobalamins and cobinamides. Journal of the American Chemical Society 2005, 127, 5049-5055. [0249] 73. Assaf-Anid, N.; Hayes, K. F.; Vogel, T. M., Reduction dechlorination of carbon tetrachloride by cobalamin (II) in the presence of dithiothreitol: mechanistic study, effect of redox potential and pH. Environmental science & technology 1994, 28, 246-252. [0250] 74. Chiu, P.-C.; Reinhard, M., Transformation of carbon tetrachloride by reduced vitamin B12 in aqueous cysteine solution. Environmental science & technology 1996, 30, 1882-1889. [0251] 75. Resa, I.; Carmona, E.; Gutierrez-Puebla, E.; Monge, A., Decamethyldizincocene, a stable compound of Zn (I) with a ZnZn bond. Science 2004, 305, 1136-1138. [0252] 76. Bentel, M. J.; Liu, Z.; Yu, Y.; Gao, J.; Men, Y.; Liu, J., Enhanced degradation of perfluorocarboxylic acids (PFCAs) by UV/sulfite treatment: Reaction mechanisms and system efficiencies at pH 12. Environmental Science & Technology Letters 2020, 7, 351-357. [0253] 77. Nguyen, T. M. H.; Brunig, J.; Thompson, K.; Thompson, J.; Kabiri, S.; Navarro, D. A.; Kookana, R. S.; Grimison, C.; Barnes, C. M.; Higgins, C. P., Influences of chemical properties, soil properties, and solution pH on soil-water partitioning coefficients of per- and polyfluoroalkyl substances (PFASs). Environmental science & technology 2020, 54, 15883-15892. [0254] 78. Maizel, A. C.; Shea, S.; Nickerson, A.; Schaefer, C.; Higgins, C. P., Release of per- and polyfluoroalkyl substances from aqueous film-forming foam impacted soils. Environmental Science & Technology 2021, 55, 14617-14627. [0255] 79. Rankin, K.; Mabury, S. A.; Jenkins, T. M.; Washington, J. W., A North American and global survey of perfluoroalkyl substances in surface soils: Distribution patterns and mode of occurrence. Chemosphere 2016, 161, 333-341. [0256] 80. Washington, J. W.; Rosal, C. G.; McCord, J. P.; Strynar, M. J.; Lindstrom, A. B.; Bergman, E. L.; Goodrow, S. M.; Tadesse, H. K.; Pilant, A. N.; Washington, B. J., Nontargeted mass-spectral detection of chloroperfluoropolyether carboxylates in New Jersey soils. Science 2020, 368, 1103-1107. [0257] 81. McCord, J. P.; Strynar, M. J.; Washington, J. W.; Bergman, E. L.; Goodrow, S. M., Emerging chlorinated polyfluorinated polyether compounds impacting the waters of southwestern New Jersey identified by use of nontargeted analysis. Environmental science & technology letters 2020, 7, 903-908. [0258] 82. Evich, M. G.; Davis, M.; Weber, E. J.; Tebes-Stevens, C.; Acrey, B.; Henderson, W. M.; Goodrow, S.; Bergman, E.; Washington, J. W., Environmental Fate of Cl-PFPECAs: Predicting the Formation of PFAS Transformation Products in New Jersey Soils. Environmental Science & Technology 2022.

[0259] All publications, patents, and patent documents are incorporated by reference herein, as though individually incorporated by reference. The invention has been described with reference to various specific and preferred embodiments and techniques. However, it should be understood that many variations and modifications may be made while remaining within the spirit and scope of the invention.