Engine lubricant composition

Abstract

Lubricant compositions include: (a) one or more polyalkylene glycol base oils obtained by polymerization or copolymerization of alkylene oxides comprising from 3 to 8 carbon atoms, include at least one butylene oxide and (b) at least one detergent chosen from salicylates or phenates. The present disclosure also relates to: 1) use of a lubricant composition as engine oil, preferably as oil for the engines of petrol or diesel motor vehicles; 2) use of a group of additives for an engine lubricant comprising polyalkylene glycol bases obtained by polymerization or copolymerization of alkylene oxides comprising from 3 to 8 carbon atoms; and 3) use of at least one additive chosen from salicylates, phenates, dithiocarbamates, amine-based or phenol-based antioxidants, preferably from salicylates or phenates, for reducing the Noack volatility of the base oils of polyalkylene glycol type, obtained from alkylene oxides comprising from 3 to 8 carbon atoms.

Claims

1. A lubricant composition comprising: (a) a single base oil of the lubricant composition consisting of: (i) at least one polyalkylene glycol base oil obtained by reacting at least one alcohol comprising from 8 to 20 carbon atoms and a mixture of butylene oxide and propylene oxide, the mixture having a mass ratio of butylene oxide over propylene oxide comprised between 3:1 and 1:3, said polyalkylene glycol base oil having a molar mass measured according to the ASTM D2502 standard comprised between 300 and 1,000 grams per mole, and a kinematic viscosity at 100 C. measured according to the ASTM D445 standard comprised between 1 and 12 cSt, wherein lubricant composition is devoid of a polyalkylene glycol obtained or partly obtained from ethylene oxide, (ii) at least one oil of API group classification III, and (iii) optionally at least one oil of API group classification I, II, or IV; and (b) from 0.2 to 2% of at least one detergent selected from salicylates or phenates.

2. The composition according to claim 1, wherein the polyalkylene glycol base oil (i) is such that the alcohol with which it may be obtained includes from 8 to 12 carbon atoms.

3. The composition according to claim 1, wherein the polyalkylene glycol base oil (i) is such that the alcohol with which it may be obtained is selected from monoalcohols.

4. The composition according to claim 1, wherein the polyalkylene base oil (i) has a mass ratio of carbon over oxygen of at least 3:1.

5. The lubricant composition according to claim 1, wherein a Noack volatility, measured according to a CEC L 40-93 standard, is less than 15%.

6. The lubricant composition according to claim 1, wherein the polyalkylene glycol base oil (i) is a majority component.

7. The lubricant composition according to claim 1, comprising from 20 to 90% of polyalkylene glycol base oil (i).

8. The lubricant composition according to claim 1 comprising at least one salicylate as a detergent (b).

9. The lubricant composition according to claim 1 free of any detergent of the sulfonate type.

10. The lubricant composition according to claim 1 further comprising: (c) at least one dithiocarbamate as an anti-wear additive.

11. The lubricant composition according to claim 1 free of anti-wear additive of the dithiophosphate type.

12. The lubricant composition according to claim 1, further comprising an amine antioxidant and/or a phenol antioxidant.

13. The lubricant composition according to claim 1 which is motor oil.

14. A method of using at least one additive for engine oil, the method comprising: providing the engine oil comprising an additive selected from salicylates, phenates, dithiocarbamates, amine or phenol antioxidants, for reducing the Noack volatility as measured according to a CEC L 40-93 standard, and a single base oil consisting of (a) base oils of a polyalkylene glycol type obtained by reacting at least one alcohol comprising from 8 to 20 carbon atoms and a mixture of butylene oxide and propylene oxide, the mixture having a mass ratio of butylene oxide over propylene oxide comprised between 3:1 and 1:3, said polyalkylene glycol base oil having a molar mass measured according to the ASTM D2502 standard comprised between 300 and 1,000 grams per mole, and a kinematic viscosity at 100 C. measured according to the ASTM D445 standard comprised between 1 and 12 cSt; (b) at least one oil of API group classification III; and (c) optionally at least one oil of API group classification I, II, or IV, wherein the engine oil is devoid of a polyalkylene glycol obtained or partly obtained from ethylene oxide, and lubricating an engine with the engine oil including the additive.

Description

DETAILED DESCRIPTION

Polyalkylene Glycol Bases (a)

(1) Polyalkylene glycol bases (a) of the compositions according to the invention have properties adapted to use in motor oil. These are (random or block) polymers or copolymers of alkylene oxides, for example prepared according to the known methods described in application WO 2009/134716, page 2 line 26 to page 4 line 12, for example by the attack of an alcohol initiator on the epoxy bond of an alkylene oxide and propagation of the reaction.

(2) The polyalkylene glycol (PAG) bases of the composition according to the invention fit the general formula:

(3) ##STR00001##
wherein Y.sub.1 and Y.sub.2 independently of each other are hydrogen or a hydrocarbon group, for example an alkyl or alkylphenyl group having between 1 and 30 carbon atoms,
n represents an integer greater than or equal to 2, preferentially less than 60, preferentially comprised between 5 and 30, preferentially comprised between 7 and 15,
x represents one or more integers between 1 and n.

(4) The groups R.sub.2x-1 and R.sub.2x independently of each other are hydrogen or hydrocarbon radicals comprising between 1 and 6 carbon atoms, preferentially alkyls and R.sub.ex is preferentially hydrogen. The sum of the numbers of carbon atoms of R.sub.2x-1 and R.sub.ex is comprised between 1 and 6. For at least one value of x, the sum of the number of carbon atoms of R.sub.2x-1 and R.sub.ex is equal to 4.

(5) The alkylene oxides used for the PAG bases of the compositions according to the invention include between 3 and 8 carbon atoms, with at least one butylene oxide, said butylene oxide being 1,2-butylene oxide or 2,3-butylene oxide, preferably 1,2-butylene oxide. Indeed, the PAGs (partly) obtained from ethylene oxide do not have sufficient liphophilicity for being used in motor oil formulations. In particular, they cannot be used in combination with other mineral, synthetic or natural base oils. The neutral or overbased detergents, indispensable for formulating lubricants guaranteeing engine cleanliness, cannot either be solubilized or kept in suspension in these PAG bases (partly) obtained from ethylene oxide.

(6) The use of alkylene oxides comprising more than 8 carbon atoms is not desired either since for producing bases having the molar mass and therefore the viscosimetric grade targeted for engine applications, one would then have a reduced number of monomers (small n in the formulae (A) above), with long side chains R.sub.2x-1 and R.sub.2x. This is detrimental to the overall linearity of the PAG molecule and leads to too low viscosity indexes (VI) for a motor oil application. Preferentially, their viscosity indexes VI (measured according to the NFT 60136 standard) is greater than 100, preferentially greater than 120.

(7) In order to give them sufficient lipophilicity, and therefore good solubility in the other synthetic base oils, the mineral or natural base oils, and good compatibility with certain additives indispensable for motor oils, such as detergents, the PAG bases (a) of the compositions according to the invention are obtained from alkylene oxides comprising at least one butylene oxide (BO). Among these PAG bases, the copolymers of butylene oxide (BO) and propylene oxide (PO) will be more preferred, since they have both good tribological and rheological properties of the PAGs containing ethylene oxide units, and good solubility in conventional mineral, synthetic and natural bases and other oily compounds.

(8) Application WO2011/011656, paragraphs [011] to [014] describes the preparation method, the features and properties (notably, solubility and miscibility in base oils) of such butylene oxide/propylene oxide copolymer PAG bases. These bases are prepared in a conventional way, by reacting one or more alcohols with a mixture of butylene oxide and propylene oxide. In order to give the PAGs good solubility and good miscibility in mineral, synthetic and natural base oils, the use in the compositions according to the invention of PAGs prepared with a mixture of butylene oxide and propylene oxide will be preferred, wherein the mass ratio between butylene oxide and propylene oxide is comprised between 3:1 and 1:3. The PAG bases prepared with a mixture where this ratio is comprised between 3:1 and 1:1 are particularly well miscible and soluble in the other base oils, including the synthetic oils of group IV (polyalphaolefins).

(9) According to a preferred embodiment, the PAG bases of the compositions according to the invention are prepared from an alcohol including from 8 to 12 carbon atoms. 2-ethylhexanol and dodecanol, either alone or as a mixture, and in particular dodecanol, are more preferred, since the PAG bases prepared from these alcohols have very low traction coefficients. According to a preferred embodiment, the PAG bases of the compositions according to the invention are such that their carbon-over-oxygen molar ratio is greater than 3:1, preferentially comprised between 3:1 and 6:1. This gives said PAGs bases, polarity and viscosity index properties particularly suitable for use in motor oils.

(10) The molar mass, measured according to the ASTM D2502 standard, of PAG bases of the compositions according to the invention is preferentially comprised between 300 and 1,000 grams per mole (g/mol), preferentially between 350 and 600 g/mol (this is why they contain a limited number n of alkylene oxide units as described above in formula (A)). This gives them kinematic viscosities at 100 C. (KV100) generally comprised between 1 to 2 cSt and 12 cSt at 100 C., preferentially between 3 and 7 cSt, preferentially between 3.5 and 6.5 or between 4 and 6 cSt or between 3.5 and 4.5 cSt. The KV100 of the composition is measured according to the ASTM D445 standard.

(11) The PAG bases are preferentially used as light bases in lubricant compositions for automobile engines according to the invention where they are preferentially associated with viscosity index enhancer polymers (VI improver) and/or other heavier bases. The use of light PAG bases (a) (KV100 approximately between 2 and 6.5 cSt) is preferentially selected in the compositions according to the invention in order to be able to formulate more easily 5 W or 0 W cold grade multi-grade oils according to the SAEJ300 classification, since the heavier PAG bases (a) have cold properties (high CCS) with which it is not possible to easily attain these grades. The PAG bases (a), notably those with KV100 values comprised between 3.5 and 4.5 cSt, of the order of 4 cSt, have Noack volatilities according to the CEC L 40-93 standard of the order of 35 to 40%, which is very high and cannot be caught up in a formulation with viscosity index enhancer polymers (VI improvers) or other less volatile bases.

(12) On the other hand, when they are combined with certain additives in the lubricant compositions according to the invention, their volatility is strongly lowered and is typically located between 15 and 20%, which is the order of magnitude of mineral, synthetic or natural bases typically used in motor oil formulations. With this volatility level of the bases, it is possible to formulate finished engine lubricants having volatility comprised between 10 and 15%, by mixture with viscosity index enhancer polymers (VI improvers) and optionally with other heavier bases, which is compatible with the requirements specification of this type of product.

(13) The lubricant composition according to the invention preferentially have a Noack volatility measured according to the CEC L 40-93 standard, of less than 15%, preferentially less than 13%. It is typically comprised between 8 and 15%, or further between 10 and 13%. Preferentially, in the compositions according to the invention, the PAG base(s) (a) is(are) the majority base(s). This means that the mass percentage of the PAG base (a) or the mass percentage of the accumulation of the PAG bases (a) is greater than the mass percentage of each of the other bases present in the compositions according to the invention; the mass percentages being expressed on the basis of the total weight of lubricant composition.

(14) Preferentially, in the compositions according to the invention, the PAG base(s) (a) is(are) the majority component(s). This means that the mass percentage of the PAG base (a), or the mass percentage of the accumulation of PAG bases (a) is greater than the mass percentage of each of the other components present in the compositions according to the invention; the mass percentages are expressed on the basis of the total weight of lubricant composition. According to an embodiment, in the compositions according to the embodiment, the PAG base(s) (a) represent(s) between 20 and 90% by weight, preferentially between 25% and 85% by weight, preferentially between 30 and 80% by weight or further between 50 and 75% by weight of the lubricant compositions according to the invention.

(15) Detergents (b), Salicylates and Phenates

(16) The detergents used in the lubricant compositions according to the present invention are well known to one skilled in the art. The detergents commonly used in the formulation of lubricant compositions are typically anionic compounds including a long lipophilic hydrocarbon chain (typically comprising at least 9, preferentially at least 12 carbon atoms) and a hydrophilic head. The associated cation is typically a metal cation of an alkaline metal, preferentially lithium, sodium or potassium.

(17) The detergents (b) of the compositions according to the invention are selected from the salts of alkaline or earth alkaline metals of the salicylate and phenate type. These metal salts may contain the metal in an approximately stoichiometric amount. In this case, these are referred to as non-overbased or neutral detergents, although they also provide some basicity. These neutral detergents typically have a base number (BN), measured according to ASTM D2896, of less than 150 mg KOH/g or less than 100, or even less than 80 mg KOH/g.

(18) When the metal is in excess (in an amount above the stoichiometric amount), we are dealing with so-called overbased detergents. Their BN is high, greater than 150 mg KOH/g, typically comprised between 200 and 700 mg KOH/g, generally comprised between 250 and 450 mg KOH/g. The excess metal providing the overbasicity to the detergent appears in the form of metal salts insoluble in the oil, for example a carbonate, hydroxide, oxalate, acetate, glutamate, preferentially carbonate. Overbased detergents in the form of micelles consisting of insoluble metal salts maintained in suspension in the lubricant composition by the detergents in the form of metal salts soluble in the oil.

(19) The lubricant compositions according to the invention contain at least one detergent of the alkaline or earth alkaline metal salicylate type or at least one detergent of the alkaline or earth alkaline metal phenate type, either neutral or overbased by the aforementioned metal salts insoluble in the oil. According to an embodiment, they contain at least one salicylate detergent and at least one phenate detergent. Preferentially, the amounts of detergents included in the lubricant compositions according to the invention are adjusted so that the BN of said compositions, as measured according to the ASTM D2896 standard, is comprised between 3 and 12 mg of KOH per gram of lubricant, preferentially comprised between 5 and 10, preferentially between 6 and 9 mg of KOH per gram of lubricant. Typically, the amount of phenate and/or salicylate detergents included in the lubricant compositions according to the invention will be comprised between 0.2 and 1.5%, preferentially between 0.5 and 2% by mass.

(20) Typically, the salicylates and phenates used as detergents (b) in the lubricant compositions according to the invention are prepared from salicylic acid and phenol derivatives fitting the formulae (I) and (II) below:

(21) ##STR00002##
wherein X.sub.1, X.sub.2, X.sub.3, X.sub.4, X.sub.5 are either hydrogen or hydrocarbon radicals, preferentially alkyls, or alkyl aryls, or aryl alkyls, and at least one of the groups X.sub.1, X.sub.2, X.sub.3, X.sub.4, X.sub.5 is a hydrocarbon radical having a sufficient amount of carbon atoms (typically at least about 9 carbon atoms, preferentially at least 12 carbon atoms), in order to give the salicylate, solubility in oil, and M is an alkaline metal.

(22) One of the groups X.sub.1 to X.sub.5 may for example be a linear or branched alkyl group comprising at least 9 carbon atoms, preferentially between 10 and 160, preferentially between 12 and 40, preferentially between 14 and 28 carbon atoms. According to an embodiment, at least one of the groups X.sub.1 to X.sub.5 is a linear alkyl comprising at least 9 carbon atoms, preferentially between 10 and 160, preferentially between 12 and 40, preferentially between 14 and 28 atoms or between 18 and 24 carbon atoms. These detergents may be neutral, or overbased by salts of alkaline metals insoluble in oil, such as carbonates, hydroxides, oxalates, acetates, glutamates.

(23) The detergents (b) of the compositions according to the invention may be neutral or overbased salicylates, fitting the formulae (III), (IV), (V), below, wherein X.sub.1, X.sub.2, X.sub.3, X.sub.4, X.sub.5 are as defined above, and X.sub.6 and X.sub.7 also have the same meaning, M.sub.1 is an alkaline metal, preferentially selected from sodium, potassium, lithium, and M.sub.2 is an earth alkaline metal, preferentially selected from calcium or magnesium.

(24) ##STR00003##

(25) The detergents of formula (III) and methods for producing them are for example described in the application EP 1 548 089. The detergents of formulae (IV) and (V) and methods for producing them are for example described in the applications U.S. Pat. No. 6,348,438, and WO 2004/041767, and EP 0786 448. The application WO 2004/009747 also describes detergents of the earth alkaline metal salicylate type which may be used as a detergent (b) in the compositions according to the invention.

(26) The detergents (b) of the compositions according to the invention may be phenates, either neutral or overbased, fitting the formulae (VI), (VII), (VIII), below, wherein X.sub.1, X.sub.2, X.sub.3, X.sub.4, X.sub.5, X.sub.6, X.sub.7 are as defined above and X.sub.8 and X.sub.9 have the same meaning, M.sub.1 is an alkaline metal, preferentially selected from sodium, potassium, lithium and M.sub.2 is an earth alkaline metal, preferentially selected from calcium or magnesium.

(27) ##STR00004##
The detergents of formula (VI) and (VII) and (VIII) and methods for producing them are for example described in applications EP 2 055 761, and EP 0 786 448.

(28) Sulfurized derivatives of salicylates and phenates, described above, may also be used as detergents (b). These sulfurized derivatives and methods for producing them are for example described in applications EP 2 055 761 and EP 0786 448. The latter application also describes mixed sulfurized phenate salicylate detergents, fitting formula (IX) which may also be used as detergent (b) in the compositions according to the invention.

(29) ##STR00005##
wherein X.sub.1 to X.sub.7 are as defined above, M.sub.2 and M.sub.3 are earth alkaline metals preferentially selected from calcium or magnesium.

(30) In the compositions according to the invention, salicylate and phenate detergents (b) may be used alone or as a mixture. They may be present in combination with other detergents known to one skilled in the art, such as for example other carboxylates. However it is preferable to avoid the presence of detergents of the sulfonate type which are difficult to solubilize in the PAG bases, in particular when the PAG base(s) form(s) the sole base oil(s) of the composition, or when the PAG base(s) form(s) the majority base oil(s) of the composition, or when the PAG base(s) form(s) at least 20% by weight of the lubricant composition. According to an embodiment, and in particular in the last three cases, the compositions according to the invention are free of sulfonate detergents.

(31) Dithiocarbamates (c):

(32) The lubricant compositions according to the invention may contain one or more dithiocarbamate additives (c). Dithiocarbamates are well known to one skilled in the art as multifunctional additives for lubricants, in particular providing anti-wear properties, but also antioxidant, extreme pressure and friction modifier properties. Dithiocarbamates used in the compositions according to the invention are for example described in the applications EP 1 730 107, WO 2005/007786, U.S. Pat. No. 4,997,969.

(33) The compositions according to the invention may also contain molybdenum dithiocarbamates, friction modifier additives for motor oils, well-known to one skilled in the art. These molybdenum dithiocarbamate organometallic friction modifiers may for example fit formula (XI):

(34) ##STR00006##
wherein X11, X12, X13, X14 are alkyl chains, preferentially including from 8 to 13 carbon atoms.

(35) In the compositions according to the invention, dithiocarbamates (c) may be used alone or as a mixture. They may be present in combination with other anti-wear, extreme pressure or friction modifier additives known to one skilled in the art. However it is preferable to avoid the presence of an anti-wear agent of the dithiophosphate type, in particular zinc dithiophosphates which are difficult to solubilize in the PAG bases, in particular when the PAG base(s) form(s) the only base oil(s) of the composition or the majority base oil(s), or when the PAG base(s) form(s) at least 20% by weight of the lubricant composition. According to an embodiment, and in particular in these last three cases, the compositions according to the invention are without any anti-wear agent of the dithiophosphate type, in particular zinc dithiophosphates.

(36) Amine or Phenol Antioxidants (d):

(37) The lubricant compositions according to the invention may optionally comprise amine or phenol antioxidants, either alone or as a mixture. These are phenols or secondary amines, the amine and phenol function is sterically hindered, as well-known to one skilled in the art for their antioxidant action in lubricants. The phenol antioxidants of the compositions according to the invention are phenols substituted on at least one, preferably both, of their ortho positions, with alkyl groups comprising from 1 to 10 carbon atoms, for example methyl, isopropyl or tertiobutyl groups, preferentially with 1 to 3 carbon atoms. They may also be used as dimers.

(38) The amine antioxidants of the compositions according to the invention are secondary amines, the nitrogen atom of which is connected to at least one aryl group. Preferentially, these are secondary amines of formulae R8NHR9, wherein R8 and R9 independently of each other are: a phenyl group optionally substituted, preferably in the para position of the amine function, with alkyl or alkenyl groups including from 1 to 10 carbon atoms, preferentially from 1 to 3 carbon atoms, a naphthyl group optionally substituted with alkyl or alkenyl groups including from 1 to 10 carbon atoms, preferentially from 1 to 3 carbon atoms,
or else R8 is a phenyl group, and R9 forms with the nitrogen atom of the amine function and the R8 cycle, a C.sub.6 heterocycle, optionally substituted with alkyl groups.

(39) Other Base Oils:

(40) The lubricant compositions according to the present invention may comprise, in combination with the PAG bases (a) described above, one or several other base oils, which may be oils of mineral or synthetic origin of groups I to V according to the classes defined in the API classification (or their equivalents according to the ATIEL classification) as summarized below, alone or as a mixture.

(41) TABLE-US-00001 Saturated Viscosity index content Sulfur content (VI) Group 1 mineral oils <90% >0.03% 80 VI < 120 Group II hydrocracked oils 90% 0.03% 80 VI < 120 Group III hydrocracked or 90% 0.03% 120 hydro-isomerized oils Group IV Polyalphaolefins (PAO) Group V Esters and other bases not included in the bases of groups I to IV

(42) These oils may be oils of vegetable, animal origin or mineral oils. The mineral base oils of the compositions according to the invention include all types of bases obtained by atmospheric and vacuum distillation of crude oil, followed by refining operations such as extraction with a solvent, deasphalting, deparaffining with a solvent, hydrotreatment, hydrocracking and hydroisomerization, hydrofinishing. The other base oils of the compositions according to the present invention may also be synthetic oils, such as certain esters of carboxylic acids and alcohols, GTL bases which may be obtained by hydroisomerization of a Fischer-Tropsch wax, or polyalphaolefins. The polyalphaolefins used as base oils, are for example obtained from monomers having from 4 to 32 carbon atoms (for example octane, decene), and have a viscosity at 100 C. comprised between 1.5 and 15 cSt. Their average weight molecular mass is typically comprised between 250 and 3,000.

(43) Preferably, the lubricant compositions according to the present invention have a kinematic viscosity at 100 C. comprised between 5.6 and 16.3 cSt measured by the ASTM D445 standard, (SAE grade 20, 30 and 40), preferentially comprised between 9.3 and 12.5 cSt (grade 30). According to a more preferred embodiment, the compositions according to the present invention are multi-grade oils of grade 5 W or 0 W according to the SAEJ300 classification. The compositions according to the present invention preferably also have a viscosity index VI greater than 130, preferentially greater than 150, preferentially greater than 160.

(44) Other Additives:

(45) The lubricant compositions according to the invention may also contain all types of additives suitable for their use, in particular as a motor oil, preferentially for an automobile vehicle engine. These additives may be added individually or else as additives package, guaranteeing a certain performance level to the lubricant compositions, as required for example by the EAMA (European Automobile Manufacturers' Association). These are for example and in a non-limiting way: dispersants, such as for example succinimides, PIB (polyisobutene) succinimides, Mannich bases. They ensure the maintaining in suspension and removal of the insoluble solid contaminants formed by the secondary oxidation products which form when the motor oil is in operation. antioxidants which delay the degradation of the operating oils, a degradation which may be expressed by the formation of deposits, the presence of sludges, or an increase in the viscosity of the oil. They act as radical inhibitors or destructive agents of hydroperoxides. Among the currently used antioxidants, are found antioxidants of the phenol type, of the sterically hindered amine type. Another class of antioxidants is that of soluble copper compounds in the oil, for example copper thio- or dithio-phosphates, copper carboxylic acid salts, copper dithiocarbamates, sulfonates, phenates, acetylacetonates. Copper (I) and (II) succinic acid or anhydride salts are used. anti-wear additives protect the frictional surfaces by forming a protective film adsorbed on these surfaces, various phosphorus, sulfur, nitrogen, chlorine or boron compounds are found in this category. and also anti-foam agents, viscosity index enhancer polymers (VI improver), flow point lowering agents, corrosion inhibitors, . . . .

(46) In the lubricant compositions according to the invention, all the additives, for example those described above, including the detergents (b), the dithiocarbamates (c), the antioxidants (d) are preferentially used in the usual mass contents of formulations for motor oils.

EXAMPLES

(47) The Noack volatility of polyalkylene glycol bases (PAG) alone or in the presence of additives was measured according to the CEC L 40-93 standard. The mass compositions and Noack volatility of the different samples are given in Table 1 and Table 2 hereafter.

(48) Table 1 relates to PAG and mineral base oils, either alone or as a mixture. A is a polyalkylene glycol (PAG), obtained from alkylene oxides, in particular butylene oxide (BO) and propylene oxide (PO) with a mass ratio of BO/PO of 50/50, with a molar mass of 388 g/mol according to ASTM D2502, with a kinematic viscosity at 100 C. (KV100) of 3.982 m.sup.2/s according to ASTM D445, with a viscosity index (VI) of 118. Its Noack volatility is very high (39.4%) as compared with a mixture of mineral bases of group III (cf. Table 1, A1, Noack of 11.2%). By mixing PAG base A with mineral bases of group III it is possible to obtain an intermediate Noack volatility (cf. Table 1, A2, Noack of 22%).

(49) Table 2 relates to compositions comprising PAG bases alone or in the presence of additives. The compositions B1 and B3 are compositions according to the invention containing an additives package which comprises a salicylate detergent, a dithiocarbamate anti-wear agent, an amine antioxidant and a phenol antioxidant. The Noack volatility is of the order of magnitude of that of known motor oils.

(50) The composition B1 comprises a mixture of PAG bases and of mineral bases of Group III comparable with the mixture of bases A2. If the Noack volatility of B1 (14%) is compared with that of A2 (22%), it is seen that the presence of additives allows strong lowering of the Noack volatility. The composition B2 also comprises a mixture of PAG bases and of mineral bases of Group III, comparable with the mixture of bases A2. B2 does not comprise any salicylate or phenate additives and is not according to the invention. B2 comprises a viscosity index enhancer polymer (VI improver) on the other hand.

(51) If the Noack volatility of B2 (21.3%) is compared with that of A2 (22%), it is seen that the effect of the viscosity index enhancer polymer (VI improver) on the Noack volatility is zero or close to it. The lowering of volatility observed in B3 (11%) is actually due to the effect of the additives of the package and not to the viscosity index enhancer polymer (VI improver). This effect is reinforced by adding a viscous PAO base.

(52) The compositions C to K contain the PAG base A combined with various additives. The compositions F and G are compositions according to the invention. Their Noack volatility is of the order of magnitude of those of light base oils conventionally used in the formulation of motor oils.

(53) The samples H, J, K also have strongly lowered Noack volatility with respect to that of the base A, by the respective presence of dithiocarbamate, of an amine antioxidant, a phenol antioxidant, and confirm the possibility of using these additives according to the invention for lowering the Noack volatility of a PAG base comprising at least one butylene oxide unit. L is a polyalkylene glycol (PAG) base, obtained from ethylene and propylene oxides, with a molar mass of 388 g/mol, with a KV100 of 3.981 mm.sup.2/s, with a viscosity index of 119. Its Noack volatility is very high (37.4%).

(54) The composition M, which contains the base L and a phenol antioxidant, has its volatility strongly lowered to a level of the order of magnitude of those of light base oils conventionally used in the formulation of motor oils. The sample N demonstrates that the base L does not solubilize the salicylate detergents. O is a polyalkylene glycol (PAG) base, obtained from propylene oxide (PO 100%), with a molar mass of 750 g/mol, with a KV100 of 6 cSt, with a viscosity index VI of 179.

(55) The composition P contains the base named O and 1% detergent phenate. The sample P shows that the base named O, which does not contain butylene oxide units, does not dissolve detergents, especially phenolates, contrary to the base A in the composition F.

(56) The composition B5 comprises the base named O in a motor oil formulation. Again, this composition B5 demonstrates that the base named O does not solubilize additives packages traditionally used and/or the base named O is not compatible with the base oils used traditionally. The same is observed with the composition B4 comprising the base L in a motor oil formulation. Only, the base A used in a formulation motor (see composition B3) allows compatibility, solubility with base oils and additives.

(57) TABLE-US-00002 TABLE 1 mass percentages and Noack A A1 A2 PAG with BO 100% 38.3% (BO/PO: 50/50) (KV100 = 4 cSt) Base group III 77.4% 50.8% UCBO4R KV100 = 4.135 cSt Base group III 22.6% 10.9% UCBO7R KV100 = 6.918 mm.sup.2/s Noack, CEC L 40-93 39.4% 11.2% 22.02% Standard

(58) TABLE-US-00003 TABLE 2 A B1 B2 B3 C D E F G PAG with butylene 100% 31.9% 35.6% 30% 99% 99% 49.5% 99% 99% oxide BO/PO KV100 = 4 cSt PAG with ethylene oxide EO/PO KV100 = 4 cSt VI enhancer 7.1% 6% polymer Base group I KV100 42.3% 47.2% 48.3% 4 cSt Base group III 9.1% 10.1% KV100 7 cSt PAO 4 49.5% KV100 4 cSt Additives package 16.7% 15.7% Succinimide 1% dispersant Amine antioxidant Phenol antioxidant Sulfonate detergent 1% 1% Phenate detergent 1% Salicylate detergent 1% Dithiocarbamate anti- wear agent Zinc dithiophosphate anti- wear agent Noack volatility 39.4% 14% 21.3% 11% 39% Detergent PAO/PAG 20% 16% CEC L 40-93 insoluble demixing in PAG H I J K L M N PAG with butylene 99% 99% 99% 99% oxide BO/PO KV100 = 4 cSt PAG with ethylene 100% 99% 99% oxide EO/PO KV100 = 4 cSt VI enhancer polymer Base group I KV100 4 cSt Base group III KV100 7 cSt PAO 4 KV100 4 cSt Additives package Succinimide dispersant Amine antioxidant 1% Phenol antioxidant 1% 1% Sulfonate detergent Phenate detergent Salicylate detergent 1% Dithiocarbamate anti- 1% wear agent Zinc 1% dithiophosphate anti- wear agent Noack volatility 21% Poor 22% 22% 37.4% 20.9% Detergent CEC L 40-93 solubilisation Insoluble and hot deposits in PAG B4 B5 O P PAG with butylene oxide BO/PO KV100 = 4 cSt PAG with ethylene oxide 30% EO/PO KV100 = 4 cSt PAG PO 100% 30% 100% 99% KV100 = 6 cSt VI enhancer polymer 6% 6% Base group I 48.3% 48.3% KV100 4 cSt Base group III KV100 7 cSt PAO 4 KV100 4 cSt Additives package 15.7% 15.7% Succinimide dispersant Amine antioxidant Phenol antioxidant Sulfonate detergent Phenate detergent 1% Salicylate detergent Dithiocarbamate anti-wear agent Zinc dithiophosphate anti-wear agent Noack volatility CEC L 40-93 Cloudy Cloudy Cloudy