POSITIVE ELECTRODE MATERIALS OF LOW-COST ALKALINE SECONDARY BATTERIES AND PREPARATION METHODS AND APPLICATIONS THEREOF
20250197240 ยท 2025-06-19
Assignee
Inventors
- Enbo SHANGGUAN (Xinxiang, CN)
- Qingxia LIU (Xinxiang, CN)
- Huijie LI (Xinxiang, CN)
- Jing LI (Xinxiang, CN)
- Mingyu WANG (Xinxiang, CN)
- Liangsheng LI (Xinxiang, CN)
- Song XU (Xinxiang, CN)
- Lirong LUO (Xinxiang, CN)
- Liangdong ZHAO (Xinxiang, CN)
Cpc classification
C01P2002/72
CHEMISTRY; METALLURGY
International classification
Abstract
Embodiments of the present disclosure disclose a low-cost alkaline secondary battery positive electrode material and a preparation method and application thereof, which belongs to the technical field of alkaline secondary battery. The positive electrode material includes a composite positive electrode material including manganese dioxide and partially oxidized layered hydroxide, etc. The composite positive electrode material prepared by the embodiments of the present disclosure has the advantage of a high discharge platform, or the like, with respect to a conventional manganese electrode, which significantly improves the cycling stability and reversibility of the zinc-manganese alkaline secondary battery.
Claims
1. A positive electrode material of a low-cost alkaline secondary battery, comprising: a composite positive electrode material including manganese dioxide and layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], a composite positive electrode material including the manganese dioxide and partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], a composite positive electrode material including the manganese dioxide and layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH], or a composite positive electrode material including the manganese dioxide, a conductive material, and one of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math. [(B.sup.a).sub.b.Math.mH.sub.2O], and the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH], the composite positive electrode material having a three-dimensional structure, wherein M is Bi or Ti, A is one or two of Ce, Al, Zn, Ca, Mg, Co, Y, Ga, Sb, Yb, and Cu, B.sup.a is one or more of OH.sup., Cl.sup., F.sup., PO.sub.4.sup.3, SO.sub.4.sup.2, CO.sub.3.sup.2, NO.sub.3.sup., BO.sub.2, MoO.sub.4.sup.2, and WO.sub.4.sup.2, 0.9x0.5, 0.3y0.1, 0.2z0.01, x+y+z=1, b>0, and m>0.
2. The positive electrode material of the low-cost alkaline secondary battery of claim 1, wherein a mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 5%-75%.
3. The positive electrode material of the low-cost alkaline secondary battery of claim 1, wherein the conductive material is one or two of graphene, carbon nanotube, acetylene black, flake graphite, hydroxyl cobalt oxide, nitrogen carbide, titanium carbide, niobium carbide, and titanium nitride, a mass percentage of the conductive material in the composite positive electrode material is within a range of 0.5%-20%; and the manganese dioxide is one or more of -MnO.sub.2, -MnO.sub.2, -MnO.sub.2, -MnO.sub.2, and -MnO.sub.2.
4. A method for preparing the positive electrode material of the low-cost alkaline secondary battery of claim 1, comprising a preparation process of the composite positive electrode material comprising the manganese dioxide and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] including: S1, performing a ball-milling operation and a sieving operation on a manganese dioxide precursor to obtain a processed manganese dioxide precursor S2, formulating a compound salt solution by dissolving a soluble nickel salt, a soluble bismuth salt or a soluble titanium salt, and an A-metal salt in deionized water, formulating an alkaline solution by dissolving an alkaline hydroxide in deionized water, adding the alkaline solution to the compound salt solution at a temperature within a range of 15-50 C., and continuous stirring until pH of a suspension liquid being within a range of 7-11, wherein the suspension liquid is kept at a temperature within a range of 50-95 C. for 5 to 48 hours, after being cooled to room temperature, the suspension liquid is filtered, washed, and dried to obtain a powder, the powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, and borate, processing the solution including the powder under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours, and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] is obtained by filtering, washing and drying the solution including the powder; S3, mixing the processed manganese dioxide precursor obtained from S1 with the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] obtained from S2, and obtaining the composite positive electrode material by performing a high-energy ball-milling operation.
5. A method for preparing the positive electrode material of the low-cost alkaline secondary battery of claim 1, wherein a preparation process of the composite positive electrode material comprising the manganese dioxide and the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] and the composite positive electrode material of the manganese dioxide and the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] includes: S1, performing a ball-milling operation and a sieving operation on a manganese dioxide precursor to obtain a processed manganese dioxide precursor; S2, formulating a compound salt solution by dissolving a soluble nickel salt, a soluble bismuth salt or a soluble titanium salt, and an A-metal salt in deionized water, formulating an alkaline solution by dissolving an alkaline hydroxide in deionized water, adding the alkaline solution to the compound salt solution at a temperature within a range of 15-50 C., and continuous stirring until pH of a suspension liquid being within a range of 7-11, wherein the suspension liquid is kept at a temperature within a range of 50-95 C. for 5 to 48 hours, after being cooled to room temperature, the suspension liquid is filtered, washed, and dried to obtain a powder, the powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, and borate, processing the solution including the powder under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours, and the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] or a fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] is obtained by oxidizing the layered hydroxide by chemical oxidation or electrolytic oxidation; S3, mixing the processed manganese dioxide precursor obtained from S1 with the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] or the fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] obtained from S2, and obtaining the composite positive electrode material by performing a high-energy ball-milling operation.
6. A method for preparing the positive electrode material of the low-cost alkaline secondary battery of claim 1, comprising: a preparation process of the composite positive electrode material comprising the manganese dioxide, the conductive material, and one of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], and the layered hydroxyl oxide [NixMyAZOOH] including: S1, performing a ball-milling operation and a sieving operation on a manganese dioxide precursor to obtain a processed manganese dioxide precursor; S2, formulating a compound salt solution by dissolving a soluble nickel salt, a soluble bismuth salt or a soluble titanium salt, and an A-metal salt in deionized water, formulating an alkaline solution by dissolving an alkaline hydroxide in deionized water, adding the alkaline solution to the compound salt solution at a temperature within a range of 15-50 C., and continuous stirring until pH of a suspension liquid being within a range of 7-11, wherein the suspension liquid is kept at a temperature within a range of 50-95 C. for 5 to 48 hours, after being cooled to room temperature, the suspension liquid is filtered, washed, and dried to obtain a powder, the powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, and borate, processing the solution including the powder under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours, and the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] or a fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] is obtained by oxidizing the layered hydroxide by chemical oxidation or electrolytic oxidation; S3, homogeneously dispersing the processed manganese dioxide precursor obtained from S1, the conductive material, and one of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], and the fully oxidized layered hydroxy oxide [Ni.sub.xM.sub.yA.sub.ZOOH] obtained step S2 into water or an organic solvent for reacting at a temperature within a range of 15-90 C. in an atmospheric pressure vessel to obtain a product, and obtaining the composite positive electrode material by drying the product.
7. The method for preparing the positive electrode material of the low-cost alkaline secondary battery of claim 4, wherein the soluble nickel salt is one or more of nickel nitrate, nickel sulfate, nickel acetate, and nickel chloride; the soluble bismuth salt is bismuth nitrate; the soluble titanium salt is titanium sulfate; the A-metal salt is one or more of cerium nitrate, cerium chloride, aluminum nitrate, aluminum chloride, aluminum sulfate, zinc nitrate, zinc sulfate, zinc chloride, calcium acetate, calcium chloride, magnesium acetate, magnesium chloride, cobalt nitrate, cobalt chloride, cobalt sulfate, yttrium nitrate, yttrium sulfate, yttrium chloride, gallium nitrate, antimony sulfate, antimony chloride, ytterbium nitrate, ytterbium chloride, copper chloride, copper sulfate, copper nitrate; the phosphate is one or more of potassium phosphate, sodium hydrogen phosphate, and sodium phosphate; the tungstate is one or more of potassium tungstate, sodium tungstate, and lithium tungstate; the molybdate is one or more of potassium molybdate and sodium molybdate; the chlorinated salt is one or more of potassium chloride and sodium chloride; the fluorinated salt is one or more of potassium fluoride and sodium fluoride; the carbonate is one or more of potassium carbonate and sodium carbonate; the metaborate is one or more of potassium metaborate, sodium metaborate, and lithium metaborate; the borate is one or more of potassium metaborate, sodium metaborate, and lithium metaborate; and the alkaline hydroxide is one or more of sodium hydroxide, potassium hydroxide, and lithium hydroxide.
8. A positive electrode plate for an alkaline secondary battery, wherein the positive electrode plate for the alkaline secondary battery is made from the positive electrode material of the low-cost alkaline secondary battery of claim 1.
9. The positive electrode plate for the alkaline secondary battery of claim 8, wherein the low-cost alkaline secondary battery positive electrode material is supplemented with an additive having a mass fraction within a range of 0.5%-10%, and the additive is one or two of chromium oxide, chromium hydroxide, strontium oxide, strontium hydroxide, ytterbium oxide, and antimony doped tin oxide.
10. An alkaline secondary battery, comprising a battery housing, an electrode plate set sealed in the battery housing, and an electrolyte, wherein the electrode plate set includes a positive electrode plate of claim 8, a negative electrode plate, and a diaphragm, the electrolyte is an alkaline solution of potassium hydroxide, and the electrolyte is added with sodium hexafluoroantimonate with a mass fraction within a range of 0.1%-2%.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0009] The present disclosure is further illustrated in terms of exemplary embodiments. These exemplary embodiments are described in detail with reference to the drawings. These embodiments are non-limiting exemplary embodiments, in which like reference numerals represent similar structures, and wherein:
[0010]
[0011]
[0012]
[0013]
[0014]
[0015]
[0016]
DETAILED DESCRIPTION
[0017] To more clearly illustrate the technical solutions related to the embodiments of the present disclosure, a brief introduction of the drawings referred to the description of the embodiments is provided below. The accompanying drawings do not represent the entirety of the embodiments.
[0018] It should be understood that system, device, unit and/or module as used herein is a manner used to distinguish different components, elements, parts, sections, or assemblies at different levels. However, if other words serve the same purpose, the words may be replaced by other expressions.
[0019] When describing the operations performed in the embodiments of the present disclosure in step-by-step instructions, the order of the steps are all interchangeable if not otherwise indicated, the steps may be omitted, and other steps may be included in the process of operation.
[0020] In some embodiments, a positive electrode material of a low cost alkaline secondary battery includes a composite positive electrode material including manganese dioxide and layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], a composite positive electrode material including the manganese dioxide and partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b-mH.sub.2O], a composite positive electrode material including the manganese dioxide and layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH], or a composite positive electrode material including the manganese dioxide, a conductive material, and one of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], and the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH]. The composite positive electrode material has a three-dimensional structure. M in the composite positive electrode material includes Bi or Ti, etc. A includes one or two of Ce, Al, Zn, Ca, Mg, Co, Y, Ga, Sb, Yb, Cu, etc., B.sup.a is OH.sup., Cl.sup., F.sup., PO.sub.4.sup.3, SO.sub.4.sup.2, CO.sub.3.sup.2, NO.sub.3.sup., BO.sub.2.sub.
[0021] The low-cost alkaline secondary battery refers to an alkaline secondary battery that has a cost value lower than a cost threshold. The cost threshold is pre-set based on historical experience.
[0022] The cost value is used to measure the cost of the alkaline secondary battery. In some embodiments, the cost value correlates to the preparation material and the preparation process. The more diverse the source of the preparation material and the more simplified the preparation process, the lower the cost value.
[0023] In some embodiments, the three-dimensional structure includes a multi-stage pore structure, a cladding structure, or the like, a hybrid structure thereof, or a customized three-dimensional structure.
[0024] In some embodiments, the values of x, y, z, b, and m in the above embodiments may be adjusted or set accordingly based on actual preparation needs.
[0025] In some embodiments of the present disclosure, Bi or Ti fills tunnels and interlayers during the charging and discharging process of the MnO.sub.2, so that the protons and electrons flow freely between lattices, inhibiting the lattices to be expanded and stabilizing the lattices and the active sites.
[0026] In some embodiments, a mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 5%-75%.
[0027] In some embodiments, the mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 15%-65%. As another example, the mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 25%-55%. As yet another example, the mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 35%-45%.
[0028] In some embodiments, the mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a) 6-mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material in the above embodiments may be adjusted or set accordingly based on the actual preparation needs. For example, the mass percentage of the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] in the composite positive electrode material is within a range of 3%-80%, etc.
[0029] In some embodiments, the conductive material includes one or two of graphene, carbon nanotube, acetylene black, flake graphite, hydroxyl cobalt oxide, nitrogen carbide, titanium carbide, niobium carbide, titanium nitride, etc. A mass percentage of the conductive material in the composite positive electrode material is within a range of 0.5%-20%. The manganese dioxide includes -MnO.sub.2, -MnO.sub.2, -MnO.sub.2, -MnO.sub.2, -MnO.sub.2, etc., or a combination thereof.
[0030] In some embodiments, the mass percentage of the conductive material in the composite positive electrode material is within a range of 4.5%-16%. As another example, the mass percentage of the conductive material in the composite positive electrode material is within a range of 6.5%-14%. As yet another example, the mass percentage of the conductive material in the composite positive electrode material is within a range of 8.5%-12%.
[0031] In some embodiments, the mass percentage of the conductive material in the composite positive electrode material may be adjusted or set accordingly based on actual preparation needs. For example, the mass percentage of the conductive material in the composite positive electrode material is within a range of 0.5%-25%, or the like.
[0032] In some embodiments, the composite positive electrode material including manganese dioxide and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] is prepared as follows.
[0033] In S1, a ball-milling operation and a sieving operation is performed on a manganese dioxide precursor to obtain a processed manganese dioxide precursor.
[0034] In some embodiments, the processing of the manganese dioxide precursor may also include a plurality of manners, such as ultrasonic grinding.
[0035] In S2, a compound salt solution is prepared by dissolving a soluble nickel salt, one of a soluble bismuth salt and a soluble titanium salt, and an A-metal salt in deionized water, an alkaline solution is prepared by dissolving an alkaline hydroxide in deionized water, the alkaline solution is added to the compound salt solution at a temperature within a range of 15-50 C. to form a mixed liquid, and the mixed liquid is continuously stirred to react and form a suspension liquid with PH within a range of 7-11 after the reaction is completed.
[0036] In some embodiments, in addition to the range of 15-50 C. as described above, the temperature required for the reaction of the alkaline solution with the compound salt solution may be adjusted or set accordingly based on the actual preparation needs.
[0037] In some embodiments, in addition to 7-11 as described above, the pH of the suspension liquid required to be achieved after completion of the reaction may be adjusted or set accordingly based on the actual preparation needs.
[0038] The suspension liquid is reacted at a temperature within a range 50-95 C. for 5 to 48 hours, cooled to room temperature, and then filtered, washed and dried to obtain a powder. The powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, or borate. The solution with the powder is processed under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours. The layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] is obtained by filtering, washing and drying the processed solution with the powder.
[0039] The inert atmosphere includes nitrogen or helium, etc. The room temperature is preset (e.g., 25 C., etc.).
[0040] In some embodiments, in addition to 50-95 C. and 5 to 48 hours as described above, the temperature range and reaction time required for the suspension liquid to undergo the reaction may be adjusted or set accordingly based on the actual preparation needs.
[0041] In some embodiments, in addition to 25-200 C. and 1 to 24 hours as described above, the temperature and reaction time required for the reaction of the powder with the solution formulated from the alkaline hydroxide, or the like, may be adjusted or set accordingly based on the actual preparation needs.
[0042] In S3, the processed manganese dioxide precursor obtained in S1 and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] obtained in S2 are mixed to obtain a mixture and then the mixture is subjected to a high-energy ball-milling operation to obtain the composite positive electrode material.
[0043] In some embodiments, the processing of the above mixture may also include a plurality of manners, such as ultrasonic grinding, or the like.
[0044] In some embodiments, the preparation materials used in each step of the above preparation process, the manner of reaction or processing, as well as the temperature and time of the reaction or processing, etc., may be adjusted or set accordingly based on the actual preparation needs.
[0045] In some embodiments, the composite positive electrode material including the manganese dioxide and the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] and the composite positive electrode material including the manganese dioxide and the layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] are prepared as follows.
[0046] In S1, a ball-milling operation and a sieving operation is performed on a manganese dioxide precursor to obtain a processed manganese dioxide precursor.
[0047] In some embodiments, the processing of the manganese dioxide precursor may also include a plurality of manners, such as ultrasonic grinding.
[0048] In S2, a compound salt solution is prepared by dissolving a soluble nickel salt, one of a soluble bismuth salt and a soluble titanium salt, and an A-metal salt in deionized water, an alkaline solution is prepared by dissolving an alkaline hydroxide in deionized water, the alkaline solution is added to the compound salt solution at a temperature within a range of 15-50 C. to form a mixed liquid, and the mixed liquid is continuously stirred to react and form a suspension liquid with PH within a range of 7-11 after the reaction is completed.
[0049] The suspension liquid is reacted at a temperature within a range 50-95 C. for 5 to 48 hours, cooled to room temperature, and then filtered, washed and dried to obtain a powder. The powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, or borate. The solution with the powder is processed under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours. The layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] is obtained by filtering, washing, and drying the processed solution with the powder. The partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] or a fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] is obtained by oxidizing the layered hydroxide by chemical oxidation or electrolytic oxidation.
[0050] In S3, the processed manganese dioxide precursor obtained in S1 is mixed with the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] or the fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] obtained in S2 to obtain a mixture, and the composite positive electrode material is obtained by performing a high-energy ball-milling operation on the mixture.
[0051] In some embodiments, the processing of the above mixture may also include a plurality of manners, such as ultrasonic grinding, or the like.
[0052] In some embodiments, the preparation materials used in each step of the above preparation process, the manner of reaction or processing, as well as the temperature and time of the reaction or processing, etc., may be adjusted or set accordingly based on the actual preparation needs.
[0053] In some embodiments, the composite positive electrode material including the manganese dioxide, the conductive material, and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the layered hydroxyl oxide [NixMyAZOOH] is prepared as follows.
[0054] In S1, a ball-milling process is performed on a manganese dioxide precursor, and a processed manganese dioxide precursor is obtained by sieving.
[0055] In some embodiments, the treatment of the manganese dioxide precursor may also include a plurality of manners, such as ultrasonic grinding.
[0056] In S2, a compound salt solution is prepared by dissolving a soluble nickel salt, one of a soluble bismuth salt and a soluble titanium salt, and an A-metal salt in deionized water, an alkaline solution is prepared by dissolving an alkaline hydroxide in deionized water, the alkaline solution is added to the compound salt solution at a temperature within a range of 15-50 C., and the solution is continuously stirred until pH of a suspension liquid is within a range of 7-11 after the reaction is completed.
[0057] The suspension liquid is reacted at a temperature within a range 50-95 C. for 5 to 48 hours, cooled to room temperature, and then filtered, washed and dried to obtain a powder. The powder is transferred to a solution prepared from one or more of alkaline hydroxide, phosphate, tungstate, molybdate, chlorinated salt, fluorinated salt, carbonate, metaborate, or borate. The solution with the powder is processed under an inert atmosphere or in air at a temperature within a range of 25-200 C. for 1 to 24 hours. The layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O] is obtained by filtering, washing, and drying the processed solution with the powder. The partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b-mH.sub.2O] or a fully oxidized layered hydroxyl oxide [Ni.sub.xM.sub.yA.sub.ZOOH] is obtained by oxidizing the layered hydroxide by chemical oxidation or electrolytic oxidation.
[0058] In S3, the processed manganese dioxide precursor obtained in S1, the conductive material and the layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2]. [(B.sup.a).sub.b.Math.mH.sub.2O], the partially oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.Z(OH).sub.2].Math.[(B.sup.a).sub.b.Math.mH.sub.2O], or the fully oxidized layered hydroxide [Ni.sub.xM.sub.yA.sub.ZOOH] obtained in S2 are homogeneously dispersed into water or an organic solvent. The reaction is carried out at a temperature within a range of 15-90 C. in an atmospheric pressure vessel to obtain a product, and then the composite positive electrode material is obtained by drying the product.
[0059] The atmospheric pressure vessel refers to a container with a pressure within a preset pressure range. The preset pressure range is pre-set based on historical experience.
[0060] In some embodiments, in addition to 15-90 C. as described above, the temperature required for the water or organic solvent for the reaction in the atmospheric pressure vessel described above may be adjusted or set accordingly based on the actual preparation needs.
[0061] In some embodiments, the preparation materials used in each step of the above preparation process, the manner of reaction or processing, as well as the temperature and time of the reaction or processing, etc., may be adjusted or set accordingly based on the actual preparation needs.
[0062] In some embodiments, the soluble nickel salt is one or more of nickel nitrate, nickel sulfate, nickel acetate, or nickel chloride. The soluble bismuth salt is bismuth nitrate. The soluble titanium salt is titanium sulfate. The A-metal salt is one or more of cerium nitrate, cerium chloride, aluminum nitrate, aluminum chloride, aluminum sulfate, zinc nitrate, zinc sulfate, zinc chloride, calcium acetate, calcium chloride, magnesium acetate, magnesium chloride, cobalt nitrate, cobalt chloride, cobalt sulfate, yttrium nitrate, yttrium sulfate, yttrium chloride, gallium nitrate, antimony sulfate, antimony chloride, ytterbium nitrate, ytterbium chloride, copper chloride, copper sulfate, copper nitrate; the phosphate is one or more of potassium phosphate, sodium hydrogen phosphate, or sodium phosphate. The phosphate is one or more of potassium phosphate, sodium hydrogen phosphate, or sodium phosphate. The tungstate is one or more of potassium tungstate, sodium tungstate, or lithium tungstate. The chloride salt is one or more of potassium chloride or sodium chloride. The molybdate is one or more of potassium molybdate or sodium molybdate. The chlorinated salt is one or more of potassium chloride or sodium chloride; the fluorinated salt is one or more of potassium fluoride or sodium fluoride. The carbonate is one or more of potassium carbonate or sodium carbonate. The metaborate is one or more of potassium metaborate, sodium metaborate, or lithium metaborate. The borate is one or more of potassium metaborate, sodium metaborate, or lithium metaborate. The alkaline hydroxide is one or more of sodium hydroxide, potassium hydroxide, or lithium hydroxide.
[0063] In some embodiments, the above-described soluble nickel salt, soluble bismuth salt, soluble titanium salt, or the like, in addition to metal salts or inorganic salts, etc., as described above, may be adjusted or set accordingly based on the actual preparation needs.
[0064] By introducing other elements into the layered hydroxide, it is also possible to enhance the bonding force between the metal and the oxygen layer, effectively improving the structural stability and cycling reversibility of the composite positive electrode material in the charging and discharging process.
[0065] According to some embodiments of the present disclosure, a positive electrode plate for an alkaline secondary battery is provided. The positive electrode plate for an alkaline secondary battery is made from the positive electrode material of a low-cost alkaline secondary battery as described in the above embodiments.
[0066] In some embodiments, the positive electrode material of a low-cost alkaline secondary battery is supplemented with an additive having a mass fraction within a range of 0.5%-10%. The additive is one or two of chromium oxide, chromium hydroxide, strontium oxide, strontium hydroxide, ytterbium oxide, or antimony doped tin oxide.
[0067] In some embodiments, the additive in the above embodiments, in addition to chromium oxide or chromium hydroxide, etc., as described above, may be adjusted or set accordingly based on the actual preparation needs.
[0068] In some embodiments, the mass fraction of the additive is within a range of 2.5%-8%. As another example, the mass fraction of the additive is within a range of 3.5%-6%. As yet another example, the mass fraction of the additive is within a range of 4.5%-5%.
[0069] In some embodiments, the mass fraction of the additive in the above embodiments may be adjusted or set accordingly based on actual preparation needs. For example, the mass fraction of the additive is within a range of 0.3%-12%, or the like.
[0070] In some embodiments of the present disclosure, the alkaline secondary battery includes a battery housing, an electrode plate set sealed in the battery housing, and an electrolyte. The electrode plate set includes a positive electrode plate, a negative electrode plate, and a diaphragm. The positive electrode plate includes the alkaline secondary battery positive electrode plate as described in the above embodiment. The electrolyte is any feasible electrolyte, such as an alkaline solution of potassium hydroxide, and the electrolyte is added with sodium hexafluoroantimonate with a mass fraction within a range of 0.1%-2%.
[0071] In some embodiments, the mass fraction of the sodium hexafluoroantimonate in the above embodiments may be adjusted or set accordingly based on the actual preparation needs. For example, the mass fraction of the sodium hexafluoroantimonate is within a range of 0.05%-2.5%, or the like.
[0072] In some embodiments, one or more physical properties such as the shape of the battery housing are pre-set based on the actual preparation needs.
[0073] The following is a further detailed description of the foregoing contents of the present disclosure by means of embodiments, but it should not be construed as meaning that the scope of the foregoing subject matter of the present disclosure is limited to the following embodiments. Any technology realized on the basis of the above contents of the present disclosure is within the scope of the present disclosure.
Embodiment 1
[0074] A composite positive electrode material MnO.sub.2/[Ni.sub.0.8Bi.sub.0.1Al.sub.0.1 (OH).sub.2.Math.[(A.sup.a).sub.b.Math.mH.sub.2O] (A=Cl.sup., b=0.1, m=2) is prepared as follows.
[0075] In some embodiments, nickel nitrate, bismuth nitrate, and aluminum chloride were first mixed at a molar ratio of Ni:Bi:Al=0.8:0.1:0.1 in a fume hood, and then prepared at 25 C. to form a compound salt solution with a molar concentration of 0.5 mol/L. Potassium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 3 mol/L. The alkaline solution was added dropwise to the compound salt solution at 25 C. using an infusion pump (e.g., a peristaltic pump, etc.) with constant stirring until the pH of the reaction suspension liquid reached 7.5. The reaction suspension liquid refers to the suspension liquid during the reaction of the alkaline solution with the compound salt solution.
[0076] In some embodiments, the suspension liquid obtained after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 20 hours, cooled to room temperature (e.g., 25 C.), and then filtered, washed, and dried to obtain a powder. The powder was transferred to a sodium chloride solution at a molar concentration of 0.5 mol/L. The sodium chloride solution with the powder was treated at 150 C. for 12 hours under the protection of inert gas (e.g., nitrogen, etc.), filtered, washed, and dried to obtain the layered hydroxide.
[0077] In some embodiments, the manganese dioxide is ball-milled, processed, and sieved to obtain a processed manganese dioxide precursor. The processed manganese dioxide precursor and the layered hydroxide prepared as described above were mixed in a mass ratio of 3:1 to obtain a mixture and then the mixture was subjected to a high-energy ball-milling processing to obtain a composite positive electrode material including the manganese dioxide and nickel-bismuth multilayered hydroxide. A scanning electron microscopy, an elemental distribution, an XRD pattern, and a charge/discharge curve of the composite positive electrode material are shown in
[0078]
Embodiment 2
[0079] The composite positive electrode material including MnO.sub.2 and the partially oxidized layered hydroxide [Ni.sub.0.7Bi.sub.0.2Cu.sub.0.1(OH).sub.2.Math.[(A.sup.a).sub.b.Math.mH.sub.2O] (A=WO.sub.4.sup.2, OH.sup., n=0.2, m=2) is prepared as follows.
[0080] In some embodiments, nickel chloride, bismuth nitrate, and copper chloride were first mixed in a molar ratio of Ni:Bi:Cu=0.7:0.2:0.1 in a fume hood and then formulated at room temperature into a compound salt solution with a molar concentration of 0.4 mol/L. Sodium hydroxide was dissolved in deionized water to form an alkaline solution with a molar concentration of 2 mol/L. The alkaline solution was added dropwise to the compound salt solution at room temperature with constant stirring until the pH of the reaction suspension liquid reached 9.
[0081] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution is reacted at 90 C. for 10 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to an alkaline solution of sodium tungstate at a molar concentration of 0.5 mol/L. The alkaline solution with the powder was treated at 120 C. for 15 hours under the protection of inert gas nitrogen, filtered, and washed to obtain a layered hydroxide sample. Under the protection of nitrogen, 5 g of the layered hydroxide sample was added to 100 ml of solution dissolved with 5 g of potassium persulfate and 2M potassium hydroxide and stirred for 20 minutes, filtered, washed, and dried under vacuum at 80 C. for 5 hours to obtain partially oxidized layered hydroxide.
[0082] In some embodiments, the manganese dioxide was ball-milled, processed, and sieved to obtain a processed manganese dioxide precursor. The composite positive electrode material including MnO.sub.2 and the partially oxidized layered hydroxide was obtained by mixing the spare manganese dioxide precursor and the partially oxidized layered hydroxide prepared as described above in a mass ratio of 2:1 to obtain a mixture and then the mixture was then subjected to high-energy ball-milling processing.
Embodiment 3
[0083] The composite positive electrode material including MnO.sub.2 and the layered hydroxide [Ni.sub.0.6Bi.sub.0.2Sb.sub.0.2OOH.Math.[(A.sup.a).sub.b.Math.mH.sub.2O] (A=MoO.sub.4.sup.2, OH.sup., b=0.2, m=2) is prepared as follows.
[0084] In some embodiments, nickel sulfate, bismuth nitrate, and antimony chloride were first mixed at a molar ratio of Ni:Bi:Sb=0.6:0.2:0.2 in a fume hood and then formulated at room temperature to form a compound salt solution with a molar concentration of 1.0 mol/L. Sodium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 1 mol/L. At room temperature, the alkaline solution was added dropwise to the compound salt solution with constant stirring until the pH of the reaction suspension liquid reached 8.5.
[0085] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 60 C. for 24 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to an alkaline solution of sodium molybdate at a molar concentration of 3 mol/L. The alkaline solution with the powder was treated at 180 C. for 4 hours under the protection of the inert gas, nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. Under the protection of nitrogen, 5 g of layered hydroxide was added to 100 mL of solution dissolved with 15 g of potassium persulfate and 4M potassium hydroxide and stirred for 60 minutes, filtered, washed, and dried in vacuum at 80 C. for 5 hours, and the layered hydroxide was obtained.
[0086] In some embodiments, the manganese dioxide is ball-milled and processed and sieved to obtain a spare manganese dioxide precursor. The spare manganese dioxide precursor, the layered hydroxide prepared above are mixed at a mass ratio of 4:1 to obtain a mixture and then the mixture was then subjected to a high-energy ball-milling processing to obtain the composite positive electrode material including MnO.sub.2 and the layered hydroxide.
Embodiment 4
[0087] The composite positive electrode material including MnO.sub.2 and the layered hydroxide [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.05Zn.sub.0.05 (OH).sub.2.Math.[(A.sup.a).sub.b.Math.mH.sub.2O] (A=F.sup., PO.sub.4.sup.3, BO.sub.2.sup., n=0.2, m=2) is prepared as follows.
[0088] In some embodiments, nickel acetate, bismuth nitrate, cerium nitrate, and zinc chloride were first mixed in a molar ratio of Ni:Bi:Ce:Zn=0.8:0.1:0.05:0.05 in a fume hood, and then prepared at room temperature to form a compound salt solution with a molar concentration of 2.0 mol/L. Potassium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2 mol/L. The alkaline solution was added dropwise to the compound salt solution at room temperature with constant stirring until the pH of the reaction suspension liquid reached 9.
[0089] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution is reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to a mixed solution of sodium fluoride, sodium phosphate, and sodium metaborate at a molar concentration of 3.0 mol/L (the molar ratio of sodium fluoride, sodium phosphate, and sodium metaborate was 0.2:0.2:1). The solution was treated at 150 C. for 12 hours under the protection of the inert gas, nitrogen, and filtered, washed, and dried to obtain the layered hydroxide.
[0090] In some embodiments, the manganese dioxide is ball-milled and processed and sieved to obtain a spare manganese dioxide precursor. The manganese dioxide composite nickel-bismuth multilayered hydroxide composite positive electrode material may be obtained by mixing the spare manganese dioxide precursor, the layered hydroxide prepared as described above in a mass ratio of 5:2 to obtain a mixture and the mixture was then subjected to a high-energy ball-milling processing.
Embodiment 5
[0091] The composite positive electrode material including MnO.sub.2, layered hydroxide [Ni.sub.0.8 Bi.sub.0.1Al.sub.0.05Y.sub.0.05 (OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=Cl.sup., n=0.2, m=2), and graphene composite is prepared as follows.
[0092] In some embodiments, the manganese dioxide was first treated by ball-milling and sieved to obtain a spare manganese dioxide precursor. Nickel nitrate, bismuth nitrate, aluminum chloride, and yttrium nitrate were mixed at a molar ratio of Ni:Bi:Al:Y=0.8:0.1:0.05:0.05 in a fume hood and then formulated at 25 C. into a compound salt solution with a molar concentration of 0.5 mol/L. Potassium hydroxide solid was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 3 mol/L. The alkaline solution was added dropwise to the compound salt solution at 25 C. using a peristaltic pump with constant stirring until the pH of the reaction suspension liquid reached 8.
[0093] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution is reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to a sodium chloride solution with a molar concentration of 0.5 mol/L. The sodium chloride solution with the powder was treated at 150 C. for 12 hours under the protection of inert gas, nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. The spare manganese dioxide precursor, the graphene, and the layered hydroxide prepared were dispersed (e.g., ultrasonically dispersed, etc.) into an aqueous solution according to a mass ratio of 4:1:1 to obtain a mixture and the mixture was then subjected to a freeze-drying process to obtain the composite positive electrode material including MnO.sub.2, the layered hydroxide, and the graphene.
Embodiment 6
[0094] The composite positive electrode material including MnO.sub.2, layered hydroxide [Ni.sub.0.6Bi.sub.0.2Sb.sub.0.2OOH.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=MoO.sub.4.sup.2, OH.sup., n=0.2, m=2), and acetylene black is prepared as follows.
[0095] In some embodiments, the manganese dioxide solid powder was ground and sieved to obtain a spare manganese dioxide precursor. The spare manganese dioxide precursor, acetylene black, and layered hydroxide prepared in Embodiment 3 were subjected to high-energy ball-milling processing in a mass ratio of 5:2:3 to obtain the composite positive electrode material including MnO.sub.2, layered hydroxide, and acetylene black.
Embodiment 7
[0096] The composite positive electrode material including MnO.sub.2, layered hydroxide [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.05Zn.sub.0.05(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=F.sup., PO.sub.4.sup.3, BO.sub.2.sup., n=0.2, m=2), and carbon nanotube is prepared as follows.
[0097] In some embodiments, the manganese dioxide solid powder was first ground and sieved to obtain a spare manganese dioxide precursor. The spare manganese dioxide precursor, carbon nanotube, and layered hydroxide prepared in embodiment 4 were then subjected to high-energy ball-milling processing in a mass ratio of 6:1:2 to obtain the composite positive electrode material including MnO.sub.2, layered hydroxide, and carbon nanotube.
Embodiment 8
[0098] The composite positive electrode material including MnO.sub.2, layered hydroxide [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.06Y.sub.0.04(OH).sub.2.Math.(A.sup.a).sub.n.Math.mH.sub.2O] (A=Cl.sup., n=0.2, m=2), and flake graphite is prepared as follows.
[0099] In some embodiments, nickel acetate, bismuth nitrate, cerium nitrate, and yttrium sulfate were first mixed in a molar ratio of Ni:Bi:Ce:Y=0.8:0.1:0.06:0.04 in a fume hood and then dispensed at room temperature to form a compound salt solution with a molar concentration of 2.0 mol/L. The flake graphite was weighed and ultrasonically dispersed into the compound salt solution, where the mass ratio of the flake graphite and the target-prepared layered hydroxide [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.06Y.sub.0.04(OH).sub.2.Math.(A.sup.a).sub.n.Math.mH.sub.2O] was controlled to be 1:3. Potassium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2 mol/L.
[0100] In some embodiments, the alkaline solution was added dropwise to the compound salt solution at room temperature with constant stirring until the pH of the reaction suspension liquid reached 9. The suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed and dried to obtain powder. The powder was transferred to a mixed solution of sodium chloride at a molar concentration of 1.0 mol/L. The mixed solution of sodium chloride with the powder was treated at 100 C. for 4 hours under the protection of the inert gas, nitrogen, and filtered, washed, and dried to obtain a composite material including the layered hydroxide and flake graphite.
[0101] In some embodiments, the manganese dioxide solid powder was ground and sieved to obtain a spare manganese dioxide precursor. The spare manganese dioxide precursor, the above-prepared composite material including the layered hydroxide and flake graphite was subjected to high-energy ball-milling processing at a mass ratio of 3:4 to obtain the composite positive electrode material including the MnO.sub.2, layered hydroxide, and flake graphite.
[0102] In some embodiments, a positive electrode plate is prepared based on the composite positive electrode material obtained in Embodiments 1-8 as follows. 0.4 g of the composite positive electrode material prepared in each of the embodiments and 0.1 g of superconducting carbon black were ground in a mortar (e.g., an onyx mortar, etc.) for 20 minutes, and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry is coated onto a nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make a positive electrode plate.
Embodiment 9
[0103] A positive electrode plate doped with 5 wt % Cr(OH).sub.3 is prepared as follows.
[0104] In some embodiments, 0.375 g of the composite positive electrode material prepared in Embodiment 1 above, 0.025 g of chromium hydroxide, and 0.1 g of superconducting carbon black were ground for 20 minutes in the onyx mortar, and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry is coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make a positive electrode plate.
Embodiment 10
[0105] A positive electrode plate dope with 1 wt % Sr(OH).sub.2 and 2 wt % Cr.sub.2O.sub.3 is prepared as follows.
[0106] In some embodiments, 0.385 g of the composite positive electrode material prepared in Embodiment 2 above, 0.005 g of strontium hydroxide, 0.01 g of chromium oxide, and 0.1 g of superconducting carbon black were ground for 20 minutes in the onyx mortar, and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry is coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make the positive electrode plate.
Embodiment 11
[0107] A positive electrode plate dope with 2 wt % Cr.sub.2O.sub.3 and 2 wt % antimony doped tin oxide is prepared as follows.
[0108] In some embodiments, 0.38 g of the composite positive electrode material prepared in Embodiment 3 above, 0.01 g of chromium oxide, 0.01 g of antimony doped tin oxide, and 0.1 g of superconducting carbon black were ground for 20 minutes in the onyx mortar, and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry was coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make the positive electrode plate.
Embodiment 12
[0109] A positive electrode plate dope with 5 wt % YbO is prepared as follows.
[0110] In some embodiments, 0.375 g of the composite positive electrode material prepared in Embodiment 4 above, 0.025 g of ytterbium oxide, and 0.1 g of superconducting carbon black were ground for 20 minutes in the onyx mortar, and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry was coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make the positive electrode plate.
[0111] In some embodiments, the battery of Embodiments 1-12 was assembled as follows. A special diaphragm (e.g., a microporous polypropylene membrane, etc.) for zinc-nickel batteries was arranged between the prepared positive electrode plate and a negative electrode plate (e.g., a zinc negative electrode plate, etc.) to obtain an intermediate structure and the intermediate structure were mounted in a special simulated battery housing, and an electrolyte (e.g., a saturated zinc oxide with a 6 mol/L KOH solution containing 0.2% sodium hexafluoroantimonate) was injected to the special simulated battery housing to form a semi-sealed zinc-manganese secondary battery.
Comparative Example 1
[0112] In some embodiments, manganese dioxide was used as an active substance. The positive electrode plate was prepared as follows. 0.4 g of manganese dioxide and 0.1 g of superconducting carbon black were milled for 20 minutes in the onyx mortar and mixed well. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to make a positive electrode slurry, the positive electrode slurry was coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make the positive electrode plate. A special diaphragm (e.g., a microporous polypropylene membrane, etc.) for zinc-nickel batteries was arranged between the prepared positive electrode plate and a negative electrode plate to obtain an intermediate structure and the intermediate structure were mounted in a special simulated battery housing, and an electrolyte (e.g., 6 mol/L KOH solution of saturated zinc oxide) was injected to the special simulated battery housing to form a semi-sealed zinc-manganese secondary battery.
[0113] In some embodiments, battery performance was tested as follows. The zinc-manganese secondary batteries fabricated in Embodiments 1-12 and Comparative example 1 were tested for discharge capacity performance and cycling stability performance after being activated by an activation current of 0.2C. For each of the zinc-manganese secondary batteries fabricated in Embodiments 1-12 and Comparative example 1, after being charged by a 0.2C charging current, the zinc-manganese secondary battery was set aside for 10 minutes, discharged to a termination voltage of 1.0 V at a discharge rate of 0.2C, and the discharge capacity performance of the positive electrode material was determined by cycling 150 times. The test results of the charging and discharging performance of the zinc-manganese secondary batteries are listed in Table 1.
TABLE-US-00001 TABLE 1 Test of battery charging/discharging performance 0.1 C 0.5 C gravi- gravi- metric metric capacity capacity Capacity (mAh .Math. (mAh .Math. insurance Battery type Positive electrode material g.sup.1) g.sup.1) rate % Embodi- Doping of MnO.sub.2/[Ni.sub.0.8Bi.sub.0.1Al.sub.0.1(OH).sub.2[(A.sup.a).sub.nmH.sub.2O] 214.8 202.2 85.9 ment 1 different (ACl.sup.) Embodi- elements MnO.sub.2/partially oxidized 226.2 212.6 87.6 ment 2 [Ni.sub.0.7Bi.sub.0.2Cu.sub.0.1(OH).sub.2[(A.sup.a).sub.nmH.sub.2O](AWO.sub.4.sup.2, OH.sup.) Embodi- MnO.sub.2/[Ni.sub.0.6Bi.sub.0.2Sb.sub.0.2OOH[(A.sup.a).sub.nmH.sub.2O] 201.0 189.2 90.3 ment 3 (AMoO.sub.4.sup.2, OH.sup.) Embodi- MnO.sub.2/[Ni.sub.0.8Bi.sub.0.1Ce.sub.0.05Zn.sub.0.05[(A.sup.a).sub.nmH.sub.2O] 219.5 208.2 88.8 ment 4 (AF.sup., PO.sub.4.sup.3, BO.sub.2.sup.) Embodi- Doping of MnO.sub.2/ 237.1 219.2 91.2 ment 5 different [Ni.sub.0.8Bi.sub.0.1Al.sub.0.05Y.sub.0.05(OH).sub.2[(A.sup.a).sub.nmH.sub.2O](ACl.sup.)/ conductive graphene Embodi- materials MnO.sub.2/[Ni.sub.0.6Bi.sub.0.2Sb.sub.0.2OOH[(A.sup.a).sub.nmH.sub.2O] 249.9 225.6 93.6 ment 6 (AMoO.sub.4.sup.2, OH.sup.)/acetylene black Embodi- MnO.sub.2/ 232.1 221.2 92.8 ment 7 [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.05Zn.sub.0.05(OH).sub.2[(A.sup.a).sub.nmH.sub.2O](AF.sup., PO.sub.4.sup.3, BO.sub.2.sup.)/carbon nanotube Embodi- MnO.sub.2/ 243.8 219.0 94.2 ment 8 [Ni.sub.0.8Bi.sub.0.1Ce.sub.0.06Y.sub.0.04(OH).sub.2(A.sup.a).sub.nmH.sub.2O](ACl.sup.)/ scale graphite Embodi- Adding Material in Embodiment 1 + 5 wt % Cr(OH).sub.3 222.2 207.5 87.5 ment 9 different Embodi- additives Material in Embodiment 2 + 1 wt % 228.0 216.3 88.8 ment 10 Sr(OH).sub.2 + 2 wt % Cr.sub.2O.sub.3 Embodi- Material in Embodiment 3 + 2 wt % Cr.sub.2O.sub.3 + 2 wt % 212.5 198.7 92.6 ment 11 Sb-doped SnO Embodi- Material in Embodiment 4 + 5 wt % YbO 225.3 212.4 90.5 ment 12 Compar- MnO.sub.2 188.4 152.2 12.3% ative example 1
[0114] The 0.1C gravimetric capacity refers to the amount of electricity that may be discharged by the zinc-manganese secondary battery when discharged at a discharge rate of 0.1C. The 0.5C gravimetric capacity is the amount of electricity that may be discharged when the zinc-manganese secondary battery is discharged at a discharge rate of 0.5C. The capacity insurance rate is used to measure the capacity retention of the zinc-manganese secondary battery after a period of use.
[0115] As can be seen from Table 1 and
Embodiment 13
[0116] The composite positive electrode material including MnO.sub.2 and layered hydroxide [Ni.sub.0.8Ti.sub.0.2(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=NO.sub.3.sup., n=0.1, m=2) is prepared as follows.
[0117] In some embodiments, nickel nitrate and titanium sulfate were first mixed at a molar ratio of Ni:Ti=0.8:0.2, and then formulated into a compound salt solution with a molar concentration of 0.5 mol/L at 25 C. Potassium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 3 mol/L. The alkaline solution was added dropwise to the compound salt solution at 25 C. with a peristaltic pump, with constant stirring until the pH of the reaction suspension liquid reached 9.
[0118] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to a sodium nitrate solution with a molar concentration of 0.5 mol/L. The sodium nitrate solution with the powder was treated at 130 C. for 1 hour under the protection of inert gas, nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. Then the manganese dioxide precursor obtained by electrolysis and the layered hydroxide were mixed at a mass ratio of 3:1 to obtain a mixture and the mixture was then subjected to a high-energy ball-milling processing to obtain the composite positive electrode material including MnO.sub.2 and layered hydroxide [Ni.sub.0.8Ti.sub.0.2(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O].
[0119]
Embodiment 14
[0120] The composite positive electrode material including MnO.sub.2m and layered hydroxide [Ni.sub.0.75Ti.sub.0.15Zn.sub.0.1(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=SO.sub.4.sup.2, OH, n=0.1, m=2) is prepared as follows.
[0121] In some embodiments, nickel sulfate, titanium sulfate, and zinc sulfate were mixed in a molar ratio of Ni:Ti:Cu=0.7:0.2:0.1 and then formulated into a compound salt solution with a molar concentration of 0.4 mol/L at room temperature. Sodium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2 mol/L. The alkaline solution was added dropwise to the compound salt solution at room temperature with constant stirring until the pH of the reaction suspension liquid reached 9.
[0122] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution is reacted at 90 C. for 10 hours, cooled to room temperature, filtered, washed, and dried to obtain the layered hydroxide. The manganese dioxide was treated by ball-milling and sieved to obtain manganese dioxide precursor. The manganese dioxide precursor, the produced layered hydroxide was mixed at a mass ratio of 2:1 to obtain a mixture and then the mixture was subjected to a high-energy ball-milling processing to obtain manganese dioxide composite nickel-titanium multilayered hydroxide composite positive electrode material.
Embodiment 15
[0123] The composite positive electrode material including MnO.sub.2 and layered hydroxide [Ni.sub.0.7Ti.sub.0.1Co.sub.0.1Y.sub.0.1(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=WO.sub.4.sup.2, OH.sup., n=0.1, m=2) is prepared as follows.
[0124] In some embodiments, nickel sulfate, titanium sulfate, cobalt sulfate, and yttrium nitrate were first mixed in a molar ratio of Ni:Ti:Co:Y=0.7:0.15:0.1:0.05, and then formulated at room temperature into a compound salt solution with a molar concentration of 1.6 mol/L. Sodium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2.5 mol/L. At room temperature, the alkaline solution was added dropwise to the compound salt solution with constant stirring until the pH of the reaction suspension liquid reached 8.
[0125] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 60 C. for 18 hours, cooled to room temperature, filtered, washed, and dried to obtain a powder. The powder was transferred to an alkaline solution of sodium tungstate at a molar concentration of 2 mol/L. The alkaline solution with the powder was treated at 120 C. for 4 hours under the protection of the inert gas nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. The manganese dioxide was ball-milled and sieved to obtain a manganese dioxide precursor. The manganese dioxide precursor and the layered hydroxide were mixed at a mass ratio of 1:1 to obtain a mixture and the mixture was then subjected to a high-energy ball-milling processing to obtain the composite positive electrode material including MnO.sub.2 and layered hydroxide.
Embodiment 16
[0126] The composite positive electrode material including MnO.sub.2 and partially oxidized layered hydroxide [Ni.sub.0.8Ti.sub.0.1Ca.sub.0.1(OH).sub.2.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=F.sup., MoO.sub.4.sup.3, n=0.2, m=2) is prepared as follows.
[0127] In some embodiments, nickel acetate, titanium sulfate, and calcium chloride were first mixed at a molar ratio of Ni:Ti:Ca=0.8:0.1:0.1, and then formulated into a compound salt solution with a molar concentration of 2.0 mol/L at room temperature. Potassium hydroxide was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2 mol/L. The alkaline solution was added dropwise to the compound salt solution at room temperature with constant stirring until the pH of the reaction suspension liquid reached 9.
[0128] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to a mixture of sodium fluoride and sodium molybdate at a molar concentration of 3.0 mol/L (the molar ratio of sodium fluoride to sodium molybdate was 2:1). The mixture of sodium fluoride and sodium molybdate with the powder was treated at 150 C. for 12 hours under the protection of the inert gas nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. Then, under the protection of nitrogen, 5 g of layered hydroxide was added to 100 mL of a solution dissolved with 5 g of potassium persulfate and 1.0 M potassium hydroxide solution and stirred for 30 minutes, filtered, washed, and dried in a vacuum at 80 C. for 5 hours to obtain partially oxidized layered hydroxide.
[0129] In some embodiments, the manganese dioxide was ball-milled and sieved to obtain the manganese dioxide precursor. The composite positive electrode material including MnO.sub.2 and partially oxidized layered hydroxide was obtained by mixing the manganese dioxide precursor and the partially oxidized layered hydroxide in a mass ratio of 5:3 to obtain a mixture and the mixture was then subjected to high-energy ball-milling processing.
Embodiment 17
[0130] The composite positive electrode material including MnO.sub.2, layered hydroxide [Ni.sub.0.8Ti.sub.0.1Al.sub.0.1OOH.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=PO.sub.4.sup.3, n=0.2, m=2), and carbon nanotubes is prepared as follows.
[0131] In some embodiments, nickel nitrate, titanium sulfate, and aluminum chloride were first mixed at a molar ratio of Ni:Ti:Al=0.8:0.1:0.1, and then formulated into a compound salt solution with a molar concentration of 0.5 mol/L at 25 C. The carbon nanotube was then ultrasonically dispersed into the compound salt solution, with a mass percent of carbon nanotube of about 2.5%. Potassium hydroxide solid was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 3 mol/L. The alkaline solution was added dropwise to the compound salt solution at 25 C. using a peristaltic pump with constant stirring until the pH of the suspension liquid solution reached 8.
[0132] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder was transferred to a sodium phosphate solution at a molar concentration of 0.5 mol/L. The sodium phosphate solution with the powder was treated at 150 C. for 12 hours under the protection of inert gas nitrogen, and filtered, washed, and dried to obtain a composite including the layered hydroxide and the carbon nanotube. Then, under the protection of nitrogen, 5 g of the composite material including the layered hydroxide and the carbon nanotube was added to 100 mL of a solution dissolved with 15 g of potassium persulfate and 3M of potassium hydroxide and stirred for 70 minutes, filtered, washed, and dried, and dried in a vacuum at 60 C. for 8 hours, then the composite including the layered hydroxide and the carbon nanotube was obtained. Finally, the manganese dioxide obtained by electrolysis and the composite including the layered hydroxide and the carbon nanotube were mixed according to the mass ratio of 3:2 to obtain a mixture and the mixture was then subjected to a ball-milling processing to obtain the composite including MnO.sub.2, layered hydroxide, and carbon nanotube composite positive electrode material.
Embodiment 18
[0133] The composite including MnO.sub.2, layered hydroxide [Ni.sub.0.6Ti.sub.0.15Sb.sub.0.1Ce.sub.0.1Bi.sub.0.05OOH.Math.[(A.sup.a).sub.n.Math.mH.sub.2O] (A=Cl.sup., n=0.2, m=2), and titanium nitride is prepared as follows.
[0134] In some embodiments, nickel chloride, titanium sulfate, antimony chloride, cerium nitrate, and bismuth nitrate were firstly mixed in a molar ratio of Ni:Ti:Sb:Ce:Bi=0.6:0.15:0.1:0.1:0.05, and formulated at room temperature into a compound salt solution with a molar concentration of 1.8 mol/L. Potassium hydroxide solid was dissolved in deionized water to formulate an alkaline solution with a molar concentration of 2.5 mol/L. The alkaline solution was added dropwise to the compound salt solution at 25 C. with a peristaltic pump, with constant stirring until the pH of the reaction suspension liquid reached 8.5.
[0135] In some embodiments, the suspension liquid after the reaction of the alkaline solution with the compound salt solution was reacted at 80 C. for 12 hours, cooled to room temperature, filtered, washed, and dried to obtain powder. The powder is transferred to a sodium chloride solution with a molar concentration of 1.0 mol/L. The sodium chloride solution with the powder was treated at 120 C. for 3 hours under the protection of the inert gas nitrogen, and filtered, washed, and dried to obtain the layered hydroxide. Then, under the protection of nitrogen, 5 g of layered hydroxide was added to 100 mL of a solution dissolved with 15 g of potassium persulfate and 3M of potassium hydroxide and stirred for 70 minutes, filtered, washed, and dried in a vacuum at 60 C. for 8 hours to obtain the layered hydroxide. The manganese dioxide solid powder obtained by electrolysis was ground and sieved to obtain a manganese dioxide precursor. The manganese dioxide precursor, titanium nitride, and prepared layered hydroxides were ultrasonically dispersed into an aqueous solution at a mass ratio of 5:1:4, stirred at 50 C. for 2 hours, and freeze-dried to obtain the composite positive electrode material including MnO.sub.2, layered hydroxide, and graphene.
Embodiment 19
[0136] A positive electrode plate doped with 1 wt % Sr(OH).sub.2 and 2 wt % Sb doped SnO are prepared as follows.
[0137] In some embodiments, 0.385 g of the composite positive electrode material prepared in Embodiment 15 above, 0.005 g of strontium hydroxide, 0.01 g of antimony doped tin oxide, and 0.1 g of superconducting carbon black were ground for 20 minutes in an onyx mortar and mixed homogeneously to form a mixture. Then 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added to the mixture make a positive electrode slurry, the positive electrode slurry was coated onto the nickel foam by a slurry coating mold, and then the nickel foam coated with the positive electrode slurry dried in a vacuum at 60 C. for 12 hours and pressed under a pressure of 12 MPa for 10 seconds to make the positive electrode plate.
[0138] In some embodiments, the battery of Embodiments 13-19 was assembled as follows. A special diaphragm for zinc-nickel batteries was arranged between the prepared positive electrode plate and a negative electrode plate to obtain an intermediate structure and the intermediate structure were mounted in a special simulated battery housing, and an electrolyte (e.g., saturated zinc oxide and containing 0.2 wt % of sodium hexaflurorantimonate in a 6 mol/L KOH solution) (e.g., saturated zinc oxide and containing 0.2 wt % of sodium hexaflurorantimonate in a 6 mol/L KOH solution) was injected to the special simulated battery housing to form a semi-sealed zinc-manganese secondary battery.
Comparative Example 2
[0139] Manganese dioxide was used as an active substance.
[0140] In some embodiments, manganese dioxide was used as the active substance. The positive electrode plate was prepared as follows. 0.39 g of manganese dioxide, 0.01 g of bismuth oxide, 0.1 g of superconducting carbon black, were ground for 20 minutes in an onyx mortar, and mixed well. Then, 0.05 g of CMC solution with a mass concentration of 2.5% and 0.05 g of PTFE aqueous solution with a mass concentration of 60% were added and mixed well to make the positive electrode slurry, and the positive electrode slurry was coated onto the nickel foam through a slurry coating mold. After the nickel foam coated with the positive electrode slurry was dried in a vacuum at 60 C. for 12 hours, the positive electrode plate was pressed under the pressure of 12 MPa for 10 seconds to produce the positive electrode plate. A special diaphragm for zinc-nickel batteries was arranged between the prepared positive electrode plate and a negative electrode plate to obtain an intermediate structure and the intermediate structure were mounted in a special simulated battery housing, and an electrolyte (e.g., a 6 mol/L KOH solution saturated with zinc oxide) was injected to the special simulated battery housing to form a semi-sealed zinc-manganese secondary battery.
[0141] In some embodiments, battery performance was tested as follows. The zinc-manganese secondary batteries fabricated in Embodiments 13-21 and Comparative example 2 were tested for discharge capacity performance and cycling stability performance after being activated by an activation current of 0.2C. For each of the zinc-manganese secondary batteries fabricated in Embodiments 13-21 and Comparative example 2, after being charged by a 0.2C charging current, the zinc-manganese secondary battery was set aside for 10 minutes, discharged to a termination voltage of 1.0 V at a discharge rate of 0.2C, and the discharge capacity performance of the positive electrode material was determined by cycling 150 times. The test results of the charging and discharging performance of the zinc-manganese secondary batteries are listed in Table 2.
TABLE-US-00002 TABLE 2 Test of battery charging/discharging performance 0.1 C 0.5 C gravimetric gravimetric Capacity capacity capacity insurance Battery type Positive electrode material (mAh .Math. g.sup.1) (mAh .Math. g.sup.1) rate % Embodiment 13 MnO.sub.2/[Ni.sub.0.8Ti.sub.0.2(OH).sub.2[(A.sup.a).sub.nmH.sub.2O] 220.3 212.5 84.9 (ANO.sub.3.sup.) Embodiment 14 MnO.sub.2/[Ni.sub.0.75Ti.sub.0.15Zn.sub.0.1(OH).sub.2[(A.sup.a).sub.nmH.sub.2O] 239.8 223.6 90.2 (ASO.sub.4.sup.2, OH.sup.) Embodiment 15 MnO.sub.2/[Ni.sub.0.7Ti.sub.0.1Co.sub.0.1Y.sub.0.1(OH).sub.2[(A.sup.a).sub.nmH.sub.2O] 246.9 235.2 94.6 (AWO.sub.4.sup.2, OH.sup.) Embodiment 16 MnO.sub.2/partially oxidized 233.4 222.8 91.9 [Ni.sub.0.8Ti.sub.0.1Ca.sub.0.1(OH).sub.2[(A.sup.a).sub.nmH.sub.2O] (AF.sup., MoO.sub.4.sup.3) Embodiment 17 MnO.sub.2//[Ni.sub.0.8Ti.sub.0.1Al.sub.0.1OOH[(A.sup.a).sub.nmH.sub.2O] 241.6 227.0 93.7 (APO.sub.4.sup.3)/carbon nanotube Embodiment 18 MnO.sub.2/ 248.5 229.6 95.1 [Ni.sub.0.6Ti.sub.0.15Sb.sub.0.1Ce.sub.0.1Bi.sub.0.05OOH[(A.sup.a).sub.nmH.sub.2O] (ACl.sup.)/titanium nitride Embodiment 19 Embodiment 15 + 1% Sr(OH).sub.2 + 2% 259.7 242.2 96.0 Sb-doped SnO Comparative MnO.sub.2 195.6 175.6 25.2 example 2
[0142] As can be seen from Table 2 and
[0143] The above embodiment describes the basic principles, main features and advantages of the present disclosure. The person skilled in the art should understand that the present disclosure is not limited by the above embodiments, and that the above embodiments and the description in the present disclosure are only illustrative of the principles of the present disclosure. The present disclosure will have various variations and improvements without departing from the scope of the principles of the present disclosure, and these variations and improvements are within the scope of protection of the present disclosure.
[0144] In addition, certain features, structures, or characteristics of one or more embodiments of the present disclosure may be suitably combined.
[0145] In the event of any inconsistency or conflict between the descriptions, definitions, and/or use of terminology in the materials cited in the present disclosure and those described in the present disclosure, the descriptions, definitions, and/or use of terminology in the present disclosure shall prevail.