Cosmetic ceramic massage head formula and preparation technology

Abstract

The invention discloses a cosmetic ceramic massage head formula and a preparation technology. The formula comprises the following raw materials: aluminum oxide fine powder, fused quartz powder, kaolin, calcium carbonate and graphene. The preparation technology comprises the steps of making ceramic slurry; injecting the ceramic slurry into a mold to make a blank, modifying and blowing the blank dry, placing the blank in a low-temperature furnace, a degreasing furnace and a high-temperature furnace separately to complete the preparation; vibrating and polishing, and soaking and cleaning to obtain a finished product. The impact strength is high, the tear resistance is good, and through adoption of the preparation technology, serious deformation with changes in temperature during preparation and explosion during high-temperature sintering are not easy to occur, so that the stability and fullness, and surface strength and abrasive resistance are improved, and accordingly the service life is prolonged.

Claims

1. A cosmetic ceramic massage head formula, characterized by comprising the following raw materials in parts by weight: 92.6% of aluminum oxide fine powder, 1.4% of fused quartz powder, 1.9% of kaolin, 2.6% of calcium carbonate, and 1.5% of graphene.

2. A cosmetic ceramic massage head formula according to claim 1, characterized in that the specific origin of the kaolin is Suzhou.

3. A preparation technology of a cosmetic ceramic massage head formula, characterized by comprising the following steps: step one: performing feeding according to an established formula (see the ingredient list), placing the materials into a ball mill, injecting pure water into the ball mill, and stirring to make ceramic slurry; step two: performing die-cast formation on the ceramic slurry with a metal mold, to make a blank; step three: correcting the blank according to the drawing until it is smooth, and then blowing the blank dry; step four: arranging bowls in layers with heat transfer crystal sand materials; step five: feeding the bowls into a low-temperature furnace for cooling, transferring the bowls into a degreasing furnace after cooling is completed, and performing natural cooling after medium-temperature degreasing is completed; step six: transferring the bowls into a high-temperature furnace, turning off the furnace fire after sintering, and taking the bowls out after the interior of the furnace is naturally cooled; step seven: performing taking out after vibration and polishing are performed through stone rices; step eight: performing soaking for 24 hours with pure water, cleaning surface residues with an ultrasonic machine, and then completing the selection to make the formula.

4. A preparation technology of a cosmetic ceramic massage head formula according to claim 3, characterized in that the ball milling treatment time in the step one is 48 hours.

5. A preparation technology of a cosmetic ceramic massage head formula according to claim 3, characterized in that the internal temperature of the low-temperature furnace in the step five is 300 degrees Celsius, and the low-temperature treatment time is 48 hours; the internal temperature of the degreasing furnace is 1100 degrees Celsius, and the medium-temperature degreasing treatment time is 120 hours.

6. A preparation technology of a cosmetic ceramic massage head formula according to claim 3, characterized in that the internal temperature of the high-temperature furnace in the step six is 1600 degrees Celsius, and the sintering time is 48 hours.

7. A preparation technology of a cosmetic ceramic massage head formula according to claim 3, characterized in that the stone rices in the step seven are selected according to the shapes of workpieces and the relevant sizes of all components; the sizes are selected between 1 and 10 mm; the polishing treatment time is 72 hours.

Description

DETAILED DESCRIPTION OF EMBODIMENTS

[0024] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention, and it is clear that the embodiments described are a part of the embodiments of the present invention, and not all of them. Based on the embodiments of the present invention, all other embodiments obtained by a person skilled in the art without inventive work shall fall within the scope of protection of the present invention.

[0025] In this embodiment: a cosmetic ceramic massage head formula comprises the following raw materials in parts by weight: 92.6% of aluminum oxide fine powder, 1.4% of fused quartz powder, 1.9% of kaolin, 2.6% of calcium carbonate, and 1.5% of graphene, wherein the specific origin of the kaolin is Suzhou.

[0026] Based on the cosmetic ceramic massage head formula, a preparation technology of the cosmetic ceramic massage head formula is proposed: [0027] which comprises the following steps: [0028] step one: performing feeding according to an established formula (see the ingredient list), placing the materials into a ball mill, injecting pure water into the ball mill, and stirring to make ceramic slurry; [0029] step two: performing die-cast formation on the ceramic slurry with a metal mold, to make a blank; [0030] step three: correcting the blank according to the drawing until it is smooth, and then blowing the blank dry; [0031] step four: arranging bowls in layers with heat transfer crystal sand materials; [0032] step five: feeding the bowls into a low-temperature furnace for cooling, transferring the bowls into a degreasing furnace after cooling is completed, and performing natural cooling after medium-temperature degreasing is completed; [0033] step six: transferring the bowls into a high-temperature furnace, turning off the furnace fire after sintering, and taking the bowls out after the interior of the furnace is naturally cooled; [0034] step seven: performing taking out after vibration and polishing are performed through stone rices; [0035] step eight: performing soaking for 24 hours with pure water, cleaning surface residues with an ultrasonic machine, and then completing the selection to make the formula.

[0036] It should be noted that the ball milling treatment time is 48 hours; the internal temperature of the low-temperature furnace is 300 degrees Celsius, and the low-temperature treatment time is 48 hours; the internal temperature of the degreasing furnace is 1100 degrees Celsius, and the medium-temperature degreasing treatment time is 120 hours; the internal temperature of the high-temperature furnace is 1600 degrees Celsius, and the sintering time is 48 hours; the stone rices are selected according to the shapes of workpieces and the relevant sizes of all components; the sizes are selected between 1 and 10 mm; the polishing treatment time is 72 hours.

[0037] Finally, it should be noted that the foregoing is only a preferable embodiment of the present invention, and is not intended to limit the present invention. Although the present invention is described in details with reference to the foregoing embodiments, it is still possible for a person skilled in the art to modify the technical solutions described in the foregoing embodiments or to make equivalent substitutions for some of the technical features therein. Any modification, equivalent replacement and improvement made within the spirit and principle of the present invention shall be included within the protection scope of the present invention.