Can for an Electric Machine

Abstract

Various embodiments of the teachings herein include a can for an electrical rotating machine and/or a liquid pump. The can may comprise a barrier layer including a barrier film and/or a barrier coating.

Claims

1. A can for an electrical rotating machine and/or a liquid pump, the can comprising: a barrier layer including a barrier film and/or a barrier coating.

2. The can as claimed in claim 1, further comprising a hybrid construction with at least two at least partly overlapping layers.

3. The can as claimed in claim 2, further comprising a barrier film between the at least two layers.

4. The can as claimed in claim 1, wherein the barrier layer includes a barrier film with a surface coating.

5. The can as claimed in claim 1, the barrier layer includes a multilayer barrier coating.

6. The can as claimed in claim 1, wherein the barrier layer is disposed within the can.

7. The can as claimed in claim 1, wherein the barrier layer is disposed on an inside surface and/or an outside surface of the can.

8. The can as claimed in claim 1, wherein the barrier film comprises an electrically nonconductive metal oxide and/or element organyl material as filler in a matrix material.

9. The can as claimed in claim 1, wherein the barrier film comprises a polymer film.

10. The can as claimed in claim 1, wherein the barrier film coats at least in part one or both sides of the can.

11. The can as claimed in claim 1, wherein the barrier film comprises multiple layers.

12. The can as claimed in claim 1, wherein the barrier coating comprises a resin filled with nanofiller.

13. The can as claimed in claim 1, wherein the barrier coating is to the can as a liquid lacquer or as a powder coating on one or both sides of the can.

14. The can as claimed in claim 1, wherein the barrier coating is produced on the can by gas phase deposition.

15. The can as claimed in claim 1, wherein the barrier layer has a thickness in the range between 0.1 μm and a few millimeters.

Description

DETAILED DESCRIPTION

[0026] A coating and/or a thin film made of media-tight material has good incorporability into a can made of fiber composite material, especially in the case of a hybrid construction composed of layers and/or laminate plies, and distinctly increases the media-tightness of a can produced from the fiber composite material, such that lower wall thicknesses of a can produced from fiber composite material should be achievable than to date. This has already been confirmed in first tests and studies. According to the construction of the can, the barrier layer may be incorporated onto and/or into the can over the full area or only in regions. Essentially, the barrier layer is sensibly formed over the full extent, at least over the full area, on the side(s) of the can under pressure stress.

[0027] In some embodiments, the barrier layer is incorporated into a hybrid structure composed of layers and/or laminate plies of a can. In some embodiments, a barrier layer is provided, for example, as interlayer within the layers of the hybrid construction. For example, the layers of the hybrid construction comprise layers with fiber reinforcement, especially with carbon-based fiber reinforcement, for example including high-modulus carbon fibers—i.e. with modulus of elasticity up to 500 GPa—and ultrahigh-modulus carbon fibers—i.e. with modulus of elasticity over and above 500 GPa. The position of these electrically conductive reinforcing fibers within the layers of the hybrid construction is preferably transverse to axial direction, especially at a setting angle in the range between 80° and 90° to the rotor axis. In this alignment, the disruptive eddy current effect on the electrical machine that results from the electrical conductivity of the material of the can is particularly low.

[0028] For example, the layers of the hybrid construction, additionally or alternatively to the abovementioned carbon-based fiber-reinforced layers, comprise those with oriented fiber reinforcement that lie at a setting angle between 20° and 70° to the rotor axis. These reinforcing fibers generally comprise fibers of zero or very low electrical conductivity, for example glass fibers, polymer fibers, ceramic fibers, especially those based on metal oxides, silicon carbide fibers, boron fibers, aramid fibers and/or other known reinforcing fibers, alone in any combination and/or mixtures.

[0029] In some embodiments, the barrier layer comprises a barrier film. This is present, for example, over the full area, such that it is provided, for example, as an interlayer in the interface region between two layers of the hybrid construction of the can. This barrier layer is correspondingly provided within the can.

[0030] In some embodiments, one or more barrier layer(s) may be provided on the outside and/or inside on the surface of the can. It is immaterial here whether the can has or does not have a hybrid construction composed of at least two layers. The barrier layer provided on the surface may take the form of at least one barrier film and/or at least one barrier coating. A suitable barrier film is, for example, a nonconductive metal oxide and/or ceramic film, for example a metal oxide film, a film of silicon carbide, a film of boron nitride and/or a carbon-based film made of graphenes, carbon flakes or the like.

[0031] A barrier film may, for example, also be a matrix material in the form of a polymer film that has been filled with filler particles, such as a film of thermoset or thermoplastic material, such as a PET (polyethylene terephthalate) film, a PP (polypropylene) film, a PI (polyimide) film, a PEEK (polyetheretherketone) film, a PPS (polyphenylene sulfide) film, a PPSU (polyphenylene sulfide) film, and a material combination, i.e. a film made from any copolymer, a film made from a polymer mixture or combination of different compounds and/or derivatives of the aforementioned polymers, and a blend of different copolymers and/or polymers.

[0032] The polymer film may also be composed of a filled material, especially filled with fine filler particles. The filler particles embedded in the matrix material of the barrier film may be made of any material, for example a metal oxide and/or element organyl material.

[0033] In some embodiments, the barrier film itself is still coated over the whole of its surface, i.e. on both sides, or over part, i.e. either in regions on one or two sides and/or only on one side. In some embodiments, there is a film structure in which a polymeric film with a single-sided or double-sided thin metal oxide and/or element organyl coating forms a barrier film or a layer of a barrier film.

[0034] An organometallic compound is what is called a metal organyl or element organyl. These are generally what are called “complexes” in which an organic—i.e. carbon-based—radical is bonded to one or more central atoms, which are generally metals. “Metal” in this context also refers to silicon and/or boron. A metal oxide compound is a compound of a metal with one or more oxygen atoms, generally having a strongly polar construction, especially also of the salt type.

[0035] For production of a barrier layer in the form of a coated barrier film, the latter is subjected to vapor deposition, for example, of a metal oxide and/or element organyl, or coated in turn, for example, by means of a PVD (physical vapor deposition) and/or CVD (chemical vapor deposition) process. By means of these processes, it is possible to produce ultrafine and ultrathin coatings of the barrier film, especially those with layer thicknesses in the single-digit nanometer range up to several hundreds of nanometers, especially also up to 10 micrometers.

[0036] A barrier film may also comprise multiple plies and, for example, comprise polymeric and ceramic, coated, single- or double-sidedly coated, plies. The incorporation of a barrier film into a can producible via wet winding, for example, is accomplished by simple inlaying of the film by wet winding, laminating, prepreg winding and/or pultrusion.

[0037] In some embodiments, the barrier layer comprises a single- or double-sided barrier coating applied to the surface of the can. The barrier layer as barrier coating is present in turn, for example, over the full area of the surface of the can, or in regions of the surface, which may relate either to the inside or outside of the can and to regions on one side of the can. The barrier layer as barrier coating of the can may additionally also have a multilayer structure like the barrier layer as barrier film.

[0038] It is likewise possible here for there to be a surface coating of a barrier layer in the form of a barrier coating with the same material structure as the coating of a barrier layer in the form of a barrier film. It is merely the thickness of this barrier coating—because it is applied to the surface—that is greater, for example, than the thickness of the coating of a barrier film. The layer thickness of a coating of a barrier coating is also again produced, for example, via gas phase deposition. By means of this process, it is possible to produce ultrafine and ultrathin coatings of the barrier film, especially those with layer thicknesses in the single-digit nanometer range up to several hundreds of nanometers, especially also from a few micrometers up to 10 micrometers.

[0039] In some embodiments, a barrier coating is, for example, what is called a high barrier coating on the surface of the inside and/or outside of a can. This is producible, for example, but not necessarily, via a gas phase deposition process. Formation of a high barrier coating can be accomplished, for example, using a matrix material, such as a resin, which, for example, forms the thermoplastic basis of the matrix material of a fiber-reinforced composite material. This matrix material is then correspondingly filled via particle modification for improvement of its barrier properties. The particle modification improves the barrier character of the resin and/or polymer which is open to diffusion. The finer the filler particles, i.e. the smaller and finer-grain, the better the barrier action thereof within the filled matrix material, resin and/or polymer. In some embodiments, nanoparticles are thus used here—possibly also in a blend with coarser-grain filler, for filling of the matrix material.

[0040] The filler material may again comprise ceramic, metal oxides, element organyl and/or polymeric particles, each of which may take the form of core-shell particles, of coated, partly coated and/or uncoated particles, of hollow bodies and/or of solid particles. These properties may be newly combined and/or adjusted by blends depending on the application, adjusted both in relation to the matrix and in relation to the can.

[0041] For example, the filler particles may comprise the following compounds, alone or in any blend and/or combination: aluminum oxide, zirconium oxide, titanium oxide, boron nitride, silicon oxide, silicon carbide, carbon-based fillers, graphenes, carbon flakes, carbon nanotubes, etc.

[0042] A matrix material in a barrier layer in the form of a barrier coating can be chosen just like the fiber composite materials; virtually all plastics are usable for this purpose, but useful materials in particular are inorganic materials that can also be used as lacquers. In particular, it is possible to use polymeric, hybrid polymeric and/or largely inorganic commercial lacquers, for example including silicatic lacquers, but avoiding brittle lacquers, especially ethyl silicate lacquers, and/or organosilicon lacquers, silazanes, siloxanes, silanes, ceramic green bodies as lacquers. The emphasis here is on the flexibility of the lacquers.

[0043] For such a barrier coating, a lacquer may be applied in liquid form to the inside and/or outside of the can by suitable wet-chemical coating and/or printing methods, such as spraying, knife coating, brushing, rolling, dipping, spin coating etc. This establishes layer thicknesses in the range from 0.1 μm to 10 mm, from 5 μm to 1 mm, or from 250 μm to 700 μm. On the other hand, it is also possible to apply a coating in the form of a powder coating, especially in the case of ceramic-based and/or highly filled coatings.

[0044] In some embodiments, the metal oxide- and/or element organyl-filled barrier coating may also be applied via gas phase deposition.

[0045] The thickness of a barrier layer, of a possibly coated barrier coating and/or of a likewise possibly coated barrier film is, for example, in the range from 20 μm up to a few millimeters, in the range of 20 μm to 1 mm, in the range between 20 μm and 800 μm, or in the range between 20 μm and 100 μm.

[0046] It is possible for the first time, without changing process conditions and production methods, in a simple manner, to generate media-tightness in a can produced from fiber composite material, based on such simple additional operating steps as painting with one or more lacquer layers and/or laminating. As a result, media-tight filler is introduced into ceramic and/or polymeric matrix materials and this embedded filler is then used to produce a coating and/or film which is mounted within and/or on the surface of the can, where it increases media-tightness by several times.