GLASS DISK FOR MAGNETIC RECORDING MEDIUM AND MAGNETIC RECORDING DEVICE USING THE SAME

Abstract

A glass disk for a magnetic recording medium of the present invention has a disk shape, and has a strain point of 695° C. to 780° C., a temperature at 10.sup.4.5 dPa.Math.s of 1300° C. or lower, and a Young's modulus of 78 GPa or higher.

Claims

1. A glass disk for a magnetic recording medium, wherein the glass disk has a disk shape, and has a strain point of 695° C. to 780° C., a temperature at 10.sup.4.5 dPa.Math.s of 1300° C. or lower, and a Young's modulus of 78 GPa or higher.

2. The glass disk for a magnetic recording medium according to claim 1, wherein a circular opening is formed in a central portion of the glass disk.

3. The glass disk for a magnetic recording medium according to claim 1, wherein the glass disk contains, as a glass composition, in terms of mol %, 60% to 71% of SiO.sub.2, 10% to 16% of Al.sub.2O.sub.3, 0% to 5% of B.sub.2O.sub.3, 0% to 0.1% of Na.sub.2O, 0% to 1% of K.sub.2O, 0% to 12% of MgO, 0% to 12% of CaO, 0% to 10% of SrO, 0% to 10% of BaO, 0% to 1% of ZrO.sub.2, and 0% to 1% of SnO.sub.2.

4. The glass disk for a magnetic recording medium according to claim 1, wherein an average surface roughness Ra of a surface of the glass disk is 1.0 nm or less.

5. The glass disk for a magnetic recording medium according to claim 1, wherein an average linear transmittance in an optical path length of 1 mm and a wavelength range of 350 nm to 1500 nm is 70% or more.

6. A glass disk for a magnetic recording medium, wherein the glass disk has a disk shape, and contains, as a glass composition, in terms of mol %, 60% to 71% of SiO.sub.2, 10% to 16% of Al.sub.2O.sub.3, 0% to 5% of B.sub.2O.sub.3, 0% to 0.1% of Na.sub.2O, 0% to 1% of K.sub.2O, 0% to 12% of MgO, 0% to 12% of CaO, 0% to 10% of SrO, 0% to 10% of BaO, 0% to 1% of ZrO.sub.2, and 0% to 1% of SnO.sub.2.

7. The glass disk for a magnetic recording medium according to claim 1, wherein a magnetic layer is provided on a surface of the glass disk.

8. A magnetic recording device, comprising: the glass disk for a magnetic recording medium according to claim 1.

9. A glass substrate for a magnetic recording medium, wherein the glass substrate has a strain point of 695° C. to 740° C., a temperature at 10.sup.4.5 dPa.Math.s of 1300° C. or lower, and a Young's modulus of 78 GPa or higher.

10. The glass substrate for a magnetic recording medium according to claim 9, wherein the glass substrate contains, as a glass composition, in terms of mol %, 60% to 71% of SiO.sub.2, 10% to 16% of Al.sub.2O.sub.3, 0% to 5% of B.sub.2O.sub.3, 0% to 0.1% of Na.sub.2O, 0% to 1% of K.sub.2O, 0% to 12% of MgO, 0% to 12% of CaO, 0% to 10% of SrO, 0% to 10% of BaO, 0% to 1% of ZrO.sub.2, and 0% to 1% of SnO.sub.2.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0021] The FIGURE is an upper perspective view showing a disk shape.

DESCRIPTION OF EMBODIMENTS

[0022] In a glass disk for a magnetic recording medium of the present invention, a strain point is 695° C. or higher, preferably 697° C. or higher, 700° C. or higher, 702° C. or higher, 705° C. or higher, 710° C. or higher, 711° C. or higher, 712° C. or higher, 713° C. or higher, 714° C. or higher, and particularly 715° C. or higher. When the strain point is too low, it is difficult to perform heat treatment at a high temperature and laser irradiation, and it is difficult to manufacture a magnetic recording medium having a high recording density. On the other hand, when the strain point is too high, a melting temperature and a forming temperature are high, and thus production efficiency of a glass substrate is likely to be decreased. Therefore, the strain point is 780° C. or lower, preferably 775° C. or lower, 770° C. or lower, 768° C. or lower, 765° C. or lower, 763° C. or lower, 760° C. or lower, 758° C. or lower, 755° C. or lower, 753° C. or lower, 750° C. or lower, 748° C. or lower, 745° C. or lower, 743° C. or lower, 740° C. or lower, 738° C. or lower, 735° C. or lower, 733° C. or lower, 730° C. or lower, 725° C. or lower, 720° C. or lower, and particularly 715° C. or lower. A most preferred range of the strain point is 715° C. to 770° C.

[0023] In the glass disk for a magnetic recording medium of the present invention, as a temperature at a viscosity in high temperature of 10.sup.45 dPa.Math.s is lower, a load applied to forming equipment can be more reduced. The temperature at 10.sup.45 dPa.Math.s is 1300° C. or lower, preferably 1290° C. or lower, 1280° C. or lower, 1275° C. or lower, 1270° C. or lower, 1265° C. or lower, 1260° C. or lower, 1255° C. or lower, and particularly 1250° C. or lower. On the other hand, when the temperature at 10.sup.45 dPa.Math.s is too low, the strain point cannot be designed to be high. Therefore, the temperature at 10.sup.45 dPa.Math.s is preferably 1150° C. or higher, 1170° C. or higher, 1180° C. or higher, 1185° C. or higher, 1190° C. or higher, 1195° C. or higher, and particularly 1200° C. or higher.

[0024] In the glass disk for a magnetic recording medium of the present invention, a Young's modulus is 78 GPa or higher, preferably 80 GPa or higher, 81 GPa or higher, 82 GPa or higher, and particularly preferably 83 GPa to 100 GPa. When the Young's modulus is too low, bending and flapping (fluttering) of the glass disk are likely to occur at the time of high-speed rotation, and thus an information recording medium and a magnetic head are likely to collide with each other.

[0025] The glass disk for a magnetic recording medium of the present invention preferably contains, as a glass composition, in terms of mol %, 60% to 71% of SiO.sub.2, 10% to 16% of Al.sub.2O.sub.3, 0% to 5% of B.sub.2O.sub.3, 0% to 0.1% of Na.sub.2O, 0% to 1% of K.sub.2O, 0% to 12% of MgO, 0% to 12% of CaO, 0% to 10% of SrO, 0% to 10% of BaO, 0% to 1% of ZrO.sub.2, and 0% to 1% of SnO.sub.2. Reasons for limiting a content range of each component as described above are shown below. In the description of the content range of each component, “%” means “mol %”.

[0026] When a content of SiO.sub.2 is too small, chemical resistance, particularly acid resistance, is likely to be decreased, and the strain point is likely to be decreased. On the other hand, when a content of SiO.sub.2 is too large, an etching rate with hydrofluoric acid or a mixed solution of hydrofluoric acid is likely to be decreased, the viscosity in high temperature is increased, meltability is likely to be decreased, and further, SiO.sub.2-based crystals, particularly cristobalite, are precipitated, and a liquidus viscosity is likely to be decreased. Therefore, an upper limit content of SiO.sub.2 is suitably 71%, 70.5%, 70%, 69.5%, 69%, 68.5%, 68%, and particularly 67.5%, and a lower limit content is suitably 60%, 61%, 62%, 62.5%, 63%, 63.5%, 64%, 64.5%, and particularly 65%. A most preferred content range is 66% to 70.5%.

[0027] When a content of Al.sub.2O.sub.3 is too small, the strain point is decreased, an amount of thermal shrinkage is increased, and the Young's modulus is decreased, so that the glass disk is likely to be bent. On the other hand, when a content of Al.sub.2O.sub.3 is too large, buffered hydrofluoric acid (BHF) resistance is decreased, a glass surface is likely to be clouded, and crack resistance is likely to be decreased. Further, SiO.sub.2—Al.sub.2O.sub.3-based crystals, particularly mullite, are precipitated in a glass, and the liquidus viscosity is likely to be decreased. An upper limit content of Al.sub.2O.sub.3 is suitably 16%, 15.5%, 15%, 14.5%, and particularly 14%, and a lower limit content is suitably 10%, 10.5%, 11%, 11.5%, and particularly 12%. A most preferred content range is 12% to 14%.

[0028] B.sub.2O.sub.3 is a component that acts as a flux, reduces a viscosity, and increases the meltability. When a content of B.sub.2O.sub.3 is too small, B.sub.2O.sub.3 does not sufficiently act as a flux, and the BHF resistance and the crack resistance are likely to be decreased. Further, a liquidus temperature is likely to rise. On the other hand, when a content of B.sub.2O.sub.3 is too large, the strain point, heat resistance, and the acid resistance are likely to be decreased, and particularly, the strain point is likely to be decreased. The glass is likely to be phase-separated. An upper limit content of B.sub.2O.sub.3 is suitably 5% and particularly 4.5%, and a lower limit content is suitably 0%, 1%, 1.5%, 2%, and particularly 2.5%. A most preferred content range is 2.5% to 4.5%.

[0029] Since alkali metal oxides (Li.sub.2O, Na.sub.2O, and K.sub.2O) deteriorate properties of a magnetic film formed on the glass disk, a content of each of the alkali metal oxides is preferably reduced to 0.1% (desirably 0.06%, 0.05%, 0.02%, and particularly 0.01%).

[0030] MgO is a component that decreases the viscosity in high temperature without decreasing the strain point and improves the meltability. In addition, MgO has an effect of decreasing a density most in RO, but when MgO is excessively introduced, the SiO.sub.2-based crystals, particularly the cristobalite, are precipitated, and the liquidus viscosity is likely to be decreased. Further, MgO is a component that easily reacts with BHF to form a product. The reaction product may be fixed or attached to the glass surface, which may make the glass cloudy. Further, impurities such as Fe.sub.2O.sub.3 may be mixed into the glass from a raw material for introducing MgO such as dolomite, and a transmittance of the glass disk may be reduced. Therefore, an upper limit content of MgO is suitably 12%, 11.5%, 11%, 10.5%, 10%, 9.5%, 9.3%, 9%, 8.5%, 8%, 7.5%, 7%, 6.5%, and particularly 6%, and a lower limit content is suitably 0%, 1%, 1.5%, 2%, 2.5%, 3%, 3.5%, 4%, and particularly 4.5%. A most preferred content range is 4.5% to 6%.

[0031] Similar to MgO, CaO is a component that decreases the viscosity in high temperature without decreasing the strain point and remarkably improves the meltability. However, when a content of CaO is too large, SiO.sub.2—Al.sub.2O.sub.3—RO-based crystals, particularly anorthite, are precipitated, the liquidus viscosity is likely to be decreased, the BHF resistance is decreased, and a reaction product is fixed or attached to the glass surface, which may make the glass cloudy. Therefore, an upper limit content of CaO is suitably 12%, 11.5%, 11%, 10.5%, 10%, 9.5%, 9%, and particularly 8.5%, and a lower limit content is suitably 0%, 1%, 2%, 3%, 3.5%, 4%, 4.5%, 5%, 5.5%, 5.6%, 6%, and particularly 6.5%. A most preferred content range is 6.5% to 8.5%.

[0032] SrO is a component that increases the chemical resistance and devitrification resistance, but when a ratio thereof is excessively increased in the entire RO, the meltability is likely to be decreased, and the density and a thermal expansion coefficient are likely to be increased. Therefore, a content of SrO is preferably 0% to 10%, 0% to 9%, 0% to 8%, 0% to 7%, 0% to 6%, and particularly 0% to 5%.

[0033] BaO is a component that increases the chemical resistance and the devitrification resistance, but when a content thereof is too large, the density is likely to be increased. A SiO.sub.2—Al.sub.2O.sub.3—B.sub.2O.sub.3—RO-based glass is generally difficult to melt, and thus it is very important to increase meltability and reduce a defective rate due to bubbles, foreign substances, and the like from a viewpoint of supplying a high-quality glass disk at a low cost and in a large amount. However, BaO has a poor effect of increasing the meltability in RO. Therefore, an upper limit content of BaO is suitably 10%, 9%, 8%, 7%, 6%, and particularly 5%, and a lower limit content thereof is suitably 0%, 0.1%, 0.3%, and particularly 0.2%.

[0034] SnO.sub.2 has a function as a fining agent for reducing bubbles in the glass. On the other hand, when a content of SnO.sub.2 is too large, devitrified crystals of SnO.sub.2 are likely to be generated in the glass. An upper limit content of SnO.sub.2 is suitably 1%, 0.5%, 0.4%, and particularly 0.3%, and a lower limit content is suitably 0%, 0.01%, 0.03%, and particularly 0.05%. A most preferred content range is 0.05% to 0.3%.

[0035] ZrO.sub.2 is a component that increases chemical durability, but when an introduction amount thereof is large, crystals of ZrSiO.sub.4 are likely to be generated. An upper limit content of ZrO.sub.2 is suitably 1%, 0.5%, 0.3%, 0.2%, and particularly 0.1%, and it is preferable to introduce ZrO.sub.2 in an amount of 0.001%% or more from a viewpoint of chemical durability. A most preferred content range is 0.001% to 0.1%. ZrO.sub.2 may be introduced from a raw material or may be introduced by extraction from a refractory.

[0036] In addition to the above components, other components may be introduced. An introduction amount thereof is preferably 5% or less, 3% or less, and particularly 1% or less.

[0037] ZnO is a component that improves the meltability and the BHF resistance, but when a content thereof is too large, the glass is likely to devitrify or the strain point is decreased, so that it is difficult to secure the heat resistance. Therefore, a content of ZnO is preferably 0% to 10%, 0% to 5%, 0% to 3%, 0% to 2%, and particularly 0% to 1%.

[0038] P.sub.2O.sub.5 is a component that decreases a liquidus temperature of SiO.sub.2—Al.sub.2O.sub.3—CaO-based crystals (particularly, anorthite) and SiO.sub.2—Al.sub.2O.sub.3-based crystals (particularly, mullite). However, when a large amount of P.sub.2O.sub.5 is introduced, the glass is likely to be phase-separated. Therefore, a content of P.sub.2O.sub.5 is preferably 0% to 10%, 0% to 5%, 0% to 3%, 0% to 2%, 0% to 1%, and particularly 0% to 0.1%.

[0039] TiO.sub.2 is a component that decreases the viscosity in high temperature and increases the meltability, and is a component that increases the chemical durability, but when TiO.sub.2 is excessively introduced, an ultraviolet transmittance is likely to be decreased. A content of TiO.sub.2 is preferably 3% or less, 1% or less, 0.5% or less, 0.1% or less, 0.05% or less, 0.03%, and particularly 0.01% or less. When a very small amount of TiO.sub.2 is introduced (for example, 0.0001% or more), an effect of preventing coloring due to ultraviolet rays is obtained. A most preferred content range is 0.0001% to 0.01%.

[0040] As.sub.2O.sub.3 and Sb.sub.2O.sub.3 are components that act as fining agents, but are environmentally hazardous chemical substances, and thus it is desirable not to use As.sub.2O.sub.3 and Sb.sub.2O.sub.3 as much as possible. A content of each of As.sub.2O.sub.3 and Sb.sub.2O.sub.3 is preferably less than 0.3%, less than 0.1%, less than 0.09%, less than 0.05%, less than 0.03%, less than 0.01%, less than 0.005%, and particularly less than 0.003%.

[0041] Fe is a component mixed from a raw material as an impurity, but when a content of Fe is too large, the ultraviolet transmittance may be decreased. Therefore, a lower limit content of Fe is suitably 0.0001%, 0.0005%, 0.001%, and particularly 0.0015% in terms of Fe.sub.2O.sub.3, and an upper limit content is suitably 0.01%, 0.009%, 0.008%, 0.007%, and particularly 0.006% in terms of Fe.sub.2O.sub.3. A most preferred content range is 0.0015% to 0.006%.

[0042] Cr.sub.2O.sub.3 is a component mixed from a raw material as an impurity, but when a content of Cr.sub.2O.sub.3 is too large, in a case of performing foreign substance inspection of an inside of the glass disk with scattered light, transmission of light is difficult to occur, and a failure may occur in the foreign substance inspection. Particularly, when a substrate size is 730 mm×920 mm or more, this failure is likely to occur. When a thickness of the glass disk is small (for example, 0.5 mm or less, 0.4 mm or less, and particularly 0.3 mm or less), an amount of scattered light is decreased, and thus it is more meaningful to regulate a content of Cr.sub.2O.sub.3. An upper limit content of Cr.sub.2O.sub.3 is suitably 0.001%, 0.0008%, 0.0006%, 0.0005%, and particularly 0.0003%, and a lower limit content is suitably 0.00001%. A most preferred content range is 0.00001% to 0.0003%.

[0043] SO.sub.3 is a component mixed from a raw material as an impurity, but when a content of SO.sub.3 is too large, bubbles called reboil may be generated during melting or forming, which may cause defects in the glass. An upper limit content of SO.sub.3 is suitably 0.005%, 0.003%, 0.002%, and particularly 0.001%, and a lower limit content is suitably 0.0001%. A most preferred content range is 0.0001% to 0.001%.

[0044] The glass disk for a magnetic recording medium of the present invention preferably has the following properties.

[0045] The glass disk for a magnetic recording medium is required to have an appropriate thermal expansion coefficient in order to enhance reliability of recording and reproduction of a magnetic recording medium. More specifically, a hard disk drive (HDD) incorporating the magnetic recording medium has a structure in which a central portion is pressed by a spindle of a spindle motor to rotate the magnetic recording medium itself. Therefore, when a difference in thermal expansion coefficient between the glass disk and a spindle material is too large, thermal expansion and thermal shrinkage of the glass disk and the spindle material are different from each other with respect to an ambient temperature change, and thus a phenomenon occurs in which the magnetic recording medium is deformed. When such a phenomenon occurs, written information cannot be read by a magnetic head, and the reliability of recording and reproduction may be impaired. Therefore, the glass disk for a magnetic recording medium desirably has a thermal expansion coefficient matching a thermal expansion coefficient of a spindle material (for example, stainless steel). From such a viewpoint, an average linear thermal expansion coefficient in a temperature range of 30° C. to 380° C. is preferably 25×10.sup.−7/° C. to 60×10.sup.−7/° C., 28×10.sup.−7/° C. to 55×10.sup.−7/° C., and particularly 30×10.sup.−7/° C. to 50×10.sup.−7/° C.

[0046] The liquidus temperature is preferably 1350° C. or lower, 1330° C. or lower, 1300° C. or lower, 1280° C. or lower, 1260° C. or lower, 1250° C. or lower, 1240° C. or lower, and particularly 1230° C. or lower. The liquidus viscosity is preferably 10.sup.3.8 dPa.Math.s or more, 10.sup.4.4 dPa.Math.s or more, 10.sup.4.6 dPa.Math.s or more, 10.sup.4.8 dPa.Math.s or more, and particularly 10.sup.5.0 dPa.Math.s or more. Accordingly, devitrified crystals are less likely to be precipitated at the time of forming, and the glass is easily formed into a sheet shape by an overflow down-draw method or the like, and thus the average surface roughness Ra of the surface can be made 1.0 nm or less and particularly 0.2 nm or less without polishing the surface or by polishing a small amount. As a result, magnetic properties can be increased with miniaturization of a bit size. The cost of the glass disk can be reduced by reducing the devitrified crystals or an amount of polishing. Here, the term “liquidus temperature” can be calculated by putting a glass powder that passes through a standard sieve of 30 mesh (500 μm) and remains on a sieve of 50 mesh (300 μm) into a platinum boat, holding the platinum boat in a temperature gradient furnace for 24 hours, and measuring a temperature at which crystals are precipitated. The term “liquidus viscosity” refers to a viscosity of a glass at a liquidus temperature, and can be measured by a platinum sphere pull up method.

[0047] An average linear transmittance in an optical path length of 1 mm and a wavelength range of 350 nm to 1500 nm is preferably 70% or more, 80% or more, and particularly 90% or more. When the average linear transmittance in the optical path length of 1 mm and the wavelength range of 350 nm to 1500 nm is too low, the magnetic layer is not sufficiently irradiated with laser light at the time of laser irradiation, and it is difficult to achieve a high Ku of the magnetic layer.

[0048] The β-OH is preferably 0.30/mm or less, 0.25/mm or less, 0.20/mm or less, 0.15/mm or less, and particularly 0.10/mm or less. When β-OH is too large, an annealing point is likely to be decreased. When β-OH is too small, it is highly necessary to introduce a dry component such as chlorine, and in that case, chlorine and the like in the glass remain in a high state, which may increase an environmental load. Therefore, β-OH is preferably 0.01/mm or more, and particularly 0.02/mm or more.

[0049] Examples of a method for reducing β-OH include the following methods. (1) A raw material having a low water content is selected. (2) A component (Cl, SO.sub.3, or the like) that reduces β-OH is added to the glass. (3) An amount of water in an atmosphere in a furnace is reduced. (4) N.sub.2 bubbling is performed in a molten glass. (5) A small melting furnace is adopted. (6) A flow rate of the molten glass is increased. (7) An electric melting method is adopted.

[0050] Here, the term “δ-OH” refers to a value obtained, using the following equation, by measuring a transmittance of the glass disk using FT-IR.

β-OH=(1/X)log(T.sub.1/T.sub.2)  [Equation 1]

[0051] X: thickness (mm)

[0052] T.sub.1: transmittance (%) at a reference wavelength of 3846 cm.sup.−1

[0053] T.sub.2: minimum transmittance (%) at a hydroxy group absorption wavelength of around 3600 cm.sup.−1

[0054] The average surface roughness Ra of the surface is preferably 1.0 nm or less, 0.7 nm or less, 0.4 nm or less, and particularly 0.2 nm or less. When the average surface roughness Ra of the surface is too large, improvement of the magnetic properties cannot be expected even if the bit size is miniaturized for a high recording density.

[0055] The thickness is preferably 1.5 mm or less, 1.2 mm or less, 0.2 mm to 1.0 mm, and particularly 0.3 mm to 0.9 mm. When the thickness is too large, polishing needs to be performed to a desired thickness, which may increase the processing cost.

[0056] A total thickness variation (TTV) is preferably less than 2.0 μm, 1.5 μm or less, 1.0 μm or less, and particularly 0.1 μm to less than 1.0 μm. When the total thickness variation (TTV) is too large, the improvement of the magnetic properties cannot be expected even if the bit size is miniaturized for the high recording density. Here, the term “total thickness variation (TTV)” is a difference between a maximum thickness and a minimum thickness of the entire glass disk, and can be measured by, for example, SBW-331ML/d manufactured by Kobelco Research Institute, Inc.

[0057] The entire surface of the glass disk for a magnetic recording medium of the present invention is preferably a polished surface. Accordingly, the total thickness variation (TTV) is likely to be regulated to less than 2.0 μm, 1.5 μm or less, 1.0 μm or less, and particularly less than 1.0 μm. As a method for a polishing treatment, various methods can be adopted, but a method of sandwiching both surfaces of the glass disk between a pair of polishing pads and performing the polishing treatment on the glass disk while rotating both the glass disk and the pair of polishing pads is preferred. Further, the pair of polishing pads preferably have different outer diameters, and the polishing treatment is preferably performed such that a part of the glass disk intermittently protrudes from the polishing pads at the time of polishing. Accordingly, the total thickness variation (TTV) is likely to be reduced, and an amount of warpage is also likely to be reduced. In the polishing treatment, a polishing depth is not particularly limited, and the polishing depth is preferably 50 μm or less, 30 μm or less, 20 μm or less, and particularly 10 μm or less. As the polishing depth is smaller, productivity of the glass disk is more improved.

[0058] The glass disk for a magnetic recording medium of the present invention can be produced, for example, by the following method. First, it is preferable that glass raw materials mixed so as to have a desired glass composition are put into a continuous melting furnace, heated and melted at 1500° C. to 1700° C., and fined, and then a molten glass is supplied to a forming device, formed into a sheet shape, and cooled. A known method can be adopted as a method of performing cutting into a disk shape after the forming into the sheet shape. As a method for forming a glass substrate, various methods can be adopted, and it is preferable to adopt an overflow down-draw method, a slot-down method, or the like in order to improve surface smoothness. It is possible to adopt, as appropriate, polishing of a disk surface for adjusting a thickness or TTV, drilling of a circular opening in a central portion of a disk, polishing of inner and outer peripheral end faces, forming of a magnetic layer on the disk surface, and the like.

Example 1

[0059] Hereinafter, the present invention will be described based on Examples. The following Examples are merely illustrative. The present invention is not limited to the following Examples.

[0060] Tables 1 to 5 show Examples (Samples Nos. 1 to 131) of the present invention.

TABLE-US-00001 TABLE 1 No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8 No. 9 No. 10 Glass SiO.sub.2 mol % 67.32 67.97 67.34 64.92 64.87 64.75 65.86 65.80 65.87 66.80 composi- Al.sub.2O.sub.3 mol % 12.57 12.70 12.27 13.93 13.97 14.14 13.98 14.02 14.05 13.00 tion B.sub.2O.sub.3 mol % 3.00 3.00 2.80 3.98 3.99 4.04 3.01 3.02 3.05 3.05 Na.sub.2O mol % 0.011 0.013 0.015 0.011 0.010 0.013 0.012 0.013 0.015 0.013 K.sub.2O mol % 0.002 0.001 0.002 0.003 0.001 0.002 0.001 0.002 0.002 0.003 MgO mol % 6.02 5.69 7.01 6.04 5.05 4.94 6.04 5.04 4.93 7.07 CaO mol % 6.49 6.49 6.24 7.00 7.98 6.98 6.99 7.97 6.97 6.97 SrO mol % 2.02 1.43 1.23 2.02 2.03 2.52 2.02 2.03 2.51 1.47 BaO mol % 2.46 2.60 2.98 1.99 1.99 2.51 1.98 1.99 2.50 1.51 TiO.sub.2 mol % 0.003 0.003 0.003 0.002 0.003 0.003 0.003 0.004 0.002 0.001 ZrO.sub.2 mol % 0.003 0.005 0.011 0.005 0.003 0.004 0.005 0.008 0.010 0.011 SnO.sub.2 mol % 0.090 0.089 0.089 0.090 0.090 0.091 0.090 0.090 0.091 0.088 Fe.sub.2O.sub.3 mol % 0.004 0.004 0.003 0.004 0.005 0.005 0.004 0.004 0.004 0.004 β-OH /mm 0.15 0.15 0.14 0.18 0.18 0.18 0.15 0.15 0.15 0.15 Density g/cm.sup.3 2.569 2.575 2.593 2.585 2.587 2.608 2.589 2.592 2.613 2.559 Thermal expansion ×10.sup.−7/ 38.2 37.8 38.9 38.9 39.7 39.8 38.7 39.6 40.0 38.0 coefficient ° C. Young's modulus GPa 82.3 82.2 82.9 82.8 82.4 81.8 83.4 83.1 82.6 83.6 Strain point ° C. 722 725 719 717 716 715 726 727 726 723 Temperature at ° C. 1255 1260 1250 1226 1227 1231 1240 1240 1245 1243 10.sup.4.5 dPa .Math. s Liquidus ° C. 1188 1191 1183 1177 1216 1205 1227 1247 1216 1199 temperature Liquidus viscosity dPa .Math. s 5.2 5.2 5.2 5.0 4.6 4.8 4.6 4.5 4.8 4.9 (log η at TL)

TABLE-US-00002 TABLE 2 No. 11 No. 12 No. 13 No. 14 No. 15 No. 16 No. 17 No. 18 No. 19 No. 20 Glass SiO.sub.2 mol % 66.88 66.80 66.92 66.77 66.76 67.87 67.72 67.76 67.94 64.89 composi- Al.sub.2O.sub.3 mol % 13.04 13.00 13.00 13.02 13.01 12.02 12.02 11.98 11.98 13.97 tion B.sub.2O.sub.3 mol % 2.96 3.00 2.97 3.00 3.03 3.00 3.03 3.04 2.97 3.98 Na.sub.2O mol % 0.011 0.011 0.011 0.012 0.012 0.013 0.015 0.011 0.014 0.013 K.sub.2O mol % 0.002 0.001 0.002 0.001 0.002 0.003 0.001 0.002 0.002 0.001 MgO mol % 5.94 6.01 4.96 5.01 5.06 6.95 7.03 6.06 5.96 7.03 CaO mol % 8.06 6.96 9.03 8.05 7.04 8.02 7.05 8.01 7.02 6.02 SrO mol % 1.48 2.01 1.48 2.02 2.50 1.01 1.53 1.53 2.00 2.02 BaO mol % 1.52 2.11 1.52 2.02 2.48 1.02 1.50 1.51 2.00 1.98 TiO.sub.2 mol % 0.004 0.003 0.003 0.002 0.003 0.002 0.002 0.001 0.002 0.001 ZrO.sub.2 mol % 0.016 0.011 0.014 0.010 0.006 0.006 0.007 0.006 0.007 0.008 SnO.sub.2 mol % 0.088 0.089 0.088 0.089 0.090 0.087 0.087 0.088 0.089 0.090 Fe.sub.2O.sub.3 mol % 0.004 0.004 0.005 0.005 0.005 0.005 0.006 0.005 0.004 0.004 β-OH /mm 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.18 Density g/cm.sup.3 2.555 2.581 2.563 2.581 2.604 2.527 2.548 2.551 2.572 2.582 Thermal expansion ×10.sup.−7/ 38.4 39.0 39.3 39.6 39.4 37.5 37.9 38.6 39.1 38.3 coefficient ° C. Young's modulus GPa 83.7 83.0 83.2 82.4 82.2 83.7 83.3 82.8 82.7 83.2 Strain point ° C. 722 721 721 720 720 717 716 717 715 718 Temperature at ° C. 1243 1246 1244 1247 1250 1245 1247 1247 1253 1227 10.sup.4.5 dPa .Math. s Liquidus ° C. 1208 1210 1239 1216 1211 1258 1222 1221 1234 1193 temperature Liquidus viscosity dPa .Math. s 4.8 4.9 4.6 4.8 4.9 4.5 4.7 4.7 4.7 4.8 (log η at TL)

TABLE-US-00003 TABLE 3 No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 No. 27 No. 28 No. 29 No. 30 Glass SiO.sub.2 mol % 64.90 64.88 65.75 65.80 65.85 65.76 65.86 66.83 66.86 66.80 composi- Al.sub.2O.sub.3 mol % 14.10 14.01 14.03 14.01 13.99 13.02 14.01 12.98 13.01 13.99 tion B.sub.2O.sub.3 mol % 3.93 4.05 3.00 3.04 2.98 3.01 3.99 4.03 3.97 3.01 Na.sub.2O mol % 0.012 0.016 0.013 0.010 0.011 0.013 0.011 0.011 0.011 0.013 K.sub.2O mol % 0.001 0.001 0.001 0.002 0.002 0.001 0.002 0.002 0.001 0.002 MgO mol % 5.95 5.96 7.03 5.93 4.98 7.05 6.05 5.97 6.01 6.04 CaO mol % 5.98 6.98 6.02 6.09 6.05 6.04 6.04 7.03 6.00 6.03 SrO mol % 2.51 0.00 2.02 2.51 3.01 2.48 1.96 1.03 2.01 2.02 BaO mol % 2.50 3.99 2.02 2.50 3.02 2.52 1.99 2.01 2.02 1.98 TiO.sub.2 mol % 0.003 0.002 0.003 0.004 0.003 0.003 0.003 0.003 0.003 0.003 ZrO.sub.2 mol % 0.010 0.013 0.013 0.011 0.006 0.005 0.011 0.005 0.003 0.004 SnO.sub.2 mol % 0.091 0.091 0.090 0.091 0.092 0.090 0.090 0.089 0.089 0.090 Fe.sub.2O.sub.3 mol % 0.004 0.005 0.005 0.005 0.004 0.004 0.003 0.004 0.005 0.005 β-OH /mm 0.18 0.18 0.15 0.15 0.14 0.15 0.18 0.18 0.18 0.15 Density g/cm.sup.3 2.603 2.609 2.586 2.610 2.633 2.612 2.571 2.549 2.564 2.576 Thermal expansion ×10.sup.−7/ 39.3 39.0 38.2 39.3 40.4 40.1 37.6 37.4 37.8 37.4 coefficient ° C. Young's modulus GPa 82.3 81.7 84.1 83.1 82.4 83.2 82.4 81.9 81.7 83.5 Strain point ° C. 716 715 727 726 725 717 721 715 715 729 Temperature at ° C. 1232 1228 1241 1247 1250 1235 1242 1241 1246 1261 10.sup.4.5 dPa .Math. s Liquidus ° C. 1200 1186 1200 1205 1191 1222 1195 1223 1213 1219 temperature Liquidus viscosity dPa .Math. s 4.8 4.9 4.9 4.9 5.1 4.6 5.0 4.7 4.8 4.9 (log η at TL)

TABLE-US-00004 TABLE 4 No. 31 No. 32 No. 33 No. 34 No. 35 No. 36 No. 37 No. 38 No. 39 No. 40 Glass SiO.sub.2 mol % 64.87 66.15 65.77 66.80 66.79 66.22 66.88 66.64 67.87 66.77 composi- Al.sub.2O.sub.3 mol % 13.99 13.84 14.00 14.03 14.00 14.51 14.03 14.04 12.99 14.03 tion B.sub.2O.sub.3 mol % 4.04 3.96 4.00 2.99 3.01 3.02 2.99 3.03 2.99 2.96 Na.sub.2O mol % 0.012 0.013 0.011 0.013 0.011 0.011 0.011 0.012 0.011 0.013 K.sub.2O mol % 0.001 0.002 0.002 0.003 0.002 0.001 0.002 0.001 0.002 0.003 MgO mol % 6.97 6.00 6.07 6.00 6.04 6.06 6.00 6.09 6.00 5.12 CaO mol % 5.99 6.95 6.06 7.07 6.03 6.05 5.99 6.08 5.99 6.01 SrO mol % 0.00 0.97 1.51 0.97 2.02 2.03 2.98 0.99 2.01 1.99 BaO mol % 4.02 2.02 2.48 2.02 1.98 1.99 1.01 3.02 2.02 3.00 TiO.sub.2 mol % 0.003 0.004 0.002 0.003 0.004 0.003 0.003 0.002 0.003 0.003 ZrO.sub.2 mol % 0.006 0.008 0.010 0.011 0.016 0.011 0.014 0.010 0.005 0.007 SnO.sub.2 mol % 0.091 0.089 0.090 0.089 0.090 0.090 0.089 0.090 0.089 0.091 Fe.sub.2O.sub.3 mol % 0.004 0.004 0.004 0.004 0.004 0.004 0.005 0.005 0.005 0.006 β-OH /mm 0.18 0.18 0.18 0.15 0.15 0.15 0.15 0.15 0.15 0.14 Density g/cm.sup.3 2.608 2.557 2.577 2.563 2.576 2.581 2.563 2.589 2.567 2.606 Thermal expansion ×10.sup.−7/ 38.6 37.2 37.7 37.2 37.2 37.0 37.1 37.2 37.3 38.5 coefficient ° C. Young's modulus GPa 82.9 83.1 82.8 84.0 83.6 84.1 83.9 83.3 82.8 82.6 Strain point ° C. 716 719 719 730 731 733 733 733 727 730 Temperature at ° C. 1230 1235 1238 1252 1254 1251 1253 1258 1260 1259 10.sup.4.5 dPa .Math. s Liquidus ° C. 1207 1192 1189 1221 1202 1239 1214 1208 1188 1204 temperature Liquidus viscosity dPa .Math. s 4.7 4.9 5.0 4.8 5.0 4.6 4.9 5.0 5.2 5.0 (log η at TL)

TABLE-US-00005 TABLE 5 No. 41 No. 42 No. 43 No. 44 No. 45 No. 46 No. 47 No. 48 No. 49 No. 50 Glass SiO.sub.2 mol % 67.14 67.65 67.78 66.85 67.06 67.33 67.21 67.37 67.88 67.88 composi- Al.sub.2O.sub.3 mol % 12.18 13.03 13.01 13.03 13.47 13.02 12.19 12.59 12.70 13.00 tion B.sub.2O.sub.3 mol % 2.91 3.03 2.93 4.05 2.93 2.93 2.86 2.99 3.00 3.00 Na.sub.2O mol % 0.011 0.011 0.014 0.013 0.012 0.011 0.013 0.010 0.011 0.011 K.sub.2O mol % 0.001 0.002 0.002 0.001 0.001 0.001 0.001 0.002 0.002 0.002 MgO mol % 6.87 5.07 5.57 5.99 5.57 5.06 6.93 6.00 6.00 5.70 CaO mol % 6.26 6.56 6.55 6.46 6.55 6.55 7.23 6.59 6.30 6.30 SrO mol % 1.30 1.51 0.53 1.49 1.51 2.50 1.28 2.33 1.70 1.40 BaO mol % 3.21 3.02 3.51 2.01 2.79 2.49 2.17 2.02 2.30 2.60 TiO.sub.2 mol % 0.002 0.003 0.002 0.003 0.003 0.002 0.003 0.003 0.003 0.003 ZrO.sub.2 mol % 0.008 0.007 0.007 0.008 0.010 0.013 0.013 0.011 0.005 0.005 SnO.sub.2 mol % 0.090 0.090 0.090 0.089 0.090 0.090 0.088 0.089 0.089 0.090 Fe.sub.2O.sub.3 mol % 0.006 0.005 0.004 0.004 0.004 0.005 0.005 0.005 0.004 0.004 β-OH /mm 0.14 0.15 0.14 0.18 0.14 0.14 0.14 0.15 0.15 0.15 Density g/cm.sup.3 2.596 2.590 2.588 2.554 2.592 2.619 2.574 2.561 2.572 2.569 Thermal expansion ×10.sup.−7/ 38.8 38.5 38.1 37.5 38.4 40.4 39.1 37.7 38.1 37.3 coefficient ° C. Young's modulus GPa 82.4 82.0 82.1 82.1 82.9 82.0 83.4 82.4 82.5 81.7 Strain point ° C. 718 726 727 717 728 721 717 726 723 728 Temperature at ° C. 1250 1263 1262 1244 1256 1251 1241 1258 1256 1266 10.sup.4.5 dPa .Math. s Liquidus ° C. 1158 1202 1181 1173 1200 1227 1192 1201 1196 1207 temperature Liquidus viscosity dPa .Math. s 5.4 5.1 5.3 5.2 5.1 4.7 5.0 5.1 5.1 5.1 (log η at TL)

TABLE-US-00006 TABLE 6 No. 51 No. 52 No. 53 No. 54 No. 55 No. 56 No. 57 No. 58 No. 59 No. 60 Glass SiO.sub.2 mol % 67.52 65.92 65.78 65.96 65.74 66.00 65.80 66.04 65.68 65.88 composi- Al.sub.2O.sub.3 mol % 13.11 14.93 14.90 14.95 14.99 14.84 14.98 14.86 15.17 14.97 tion B.sub.2O.sub.3 mol % 3.30 2.03 2.15 1.96 2.09 2.01 2.09 2.02 2.03 1.96 Na.sub.2O mol % 0.007 0.020 0.020 0.013 0.016 0.023 0.014 0.016 0.015 0.020 K.sub.2O mol % 0.000 0.003 0.002 0.002 0.001 0.002 0.002 0.001 0.002 0.002 MgO mol % 6.16 6.94 6.95 6.97 6.97 6.94 7.96 7.92 7.94 7.98 CaO mol % 6.50 6.05 6.10 4.06 4.10 4.10 6.04 6.05 4.05 4.08 SrO mol % 1.59 3.01 1.01 4.99 3.01 1.01 3.00 1.02 4.98 3.02 BaO mol % 1.69 0.99 2.98 1.00 2.99 4.98 0.03 1.97 0.04 2.00 TiO.sub.2 mol % 0.003 0.007 0.007 0.006 0.007 0.009 0.007 0.007 0.006 0.007 ZrO.sub.2 mol % 0.010 0.001 0.001 0.001 0.001 0.002 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.096 0.080 0.086 0.082 0.087 0.084 0.079 0.085 0.080 0.086 Fe.sub.2O.sub.3 mol % 0.003 0.007 0.007 0.007 0.006 0.007 0.007 0.007 0.007 0.007 β-OH /mm 0.10 0.14 0.14 0.14 0.15 0.15 0.15 0.13 0.13 0.15 Density g/cm.sup.3 2.549 2.586 2.614 2.616 2.644 2.669 2.558 2.583 2.590 2.613 Thermal expansion ×10.sup.−7/ 37.1 37.6 37.9 38.1 38.4 38.7 36.4 36.7 36.9 37.2 coefficient ° C. Young's modulus GPa 83.0 85.7 85.1 85.2 84.4 83.7 86.9 86.2 86.6 85.6 Strain point ° C. 725 741 740 741 740 740 741 741 742 740 Temperature at ° C. 1255 1247 1250 1250 1255 1255 1241 1242 1249 1249 10.sup.4.5 dPa .Math. s Liquidus ° C. 1184 1265 1256 1269 1253 1227 1295 1282 1294 1285 temperature Liquidus viscosity dPa .Math. s 5.2 4.3 4.5 4.3 4.5 4.8 4.0 4.1 4.1 4.2 (log η at TL)

TABLE-US-00007 TABLE 7 No. 61 No. 62 No. 63 No. 64 No. 65 No. 66 No. 67 No. 68 No. 69 No. 70 Glass SiO.sub.2 mol % 65.85 66.01 66.01 66.90 66.90 68.68 68.79 68.76 68.83 68.86 composi- Al.sub.2O.sub.3 mol % 14.87 13.97 13.99 13.97 14.02 13.60 13.53 13.53 13.57 13.53 tion B.sub.2O.sub.3 mol % 2.08 1.92 1.92 1.92 0.96 1.11 1.03 1.05 0.86 0.97 Na.sub.2O mol % 0.018 0.027 0.017 0.015 0.015 0.017 0.014 0.016 0.014 0.012 K.sub.2O mol % 0.001 0.002 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 MgO mol % 7.97 6.95 7.94 7.04 6.94 6.96 6.96 6.98 6.99 6.98 CaO mol % 4.11 7.01 6.03 6.04 7.04 9.00 7.02 7.06 5.05 5.05 SrO mol % 1.02 3.00 3.00 3.01 3.02 0.52 2.52 0.51 4.52 2.51 BaO mol % 3.98 1.00 1.00 1.00 1.00 0.00 0.03 1.99 0.06 2.00 TiO.sub.2 mol % 0.007 0.006 0.006 0.006 0.006 0.010 0.009 0.007 0.007 0.008 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 0.002 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.087 0.080 0.080 0.080 0.093 0.086 0.082 0.088 0.084 0.085 Fe.sub.2O.sub.3 mol % 0.007 0.007 0.007 0.007 0.007 0.008 0.008 0.007 0.007 0.007 β-OH /mm 0.13 0.13 0.14 0.14 0.14 0.15 0.15 0.15 0.14 0.14 Density g/cm.sup.3 2.640 2.590 2.588 2.579 2.597 2.507 2.538 2.564 2.569 2.592 Thermal expansion ×10.sup.−7/ 37.5 39.4 38.6 37.8 39.2 35.8 36.3 36.6 36.8 37.1 coefficient ° C. Young's modulus GPa 84.9 85.5 86.0 85.3 86.5 86.9 86.3 85.5 85.7 85.1 Strain point ° C. 740 733 733 737 744 753 750 750 750 749 Temperature at ° C. 1254 1239 1239 1250 1253 1268 1273 1277 1279 1283 10.sup.4.5 dPa .Math. s Liquidus ° C. 1282 1243 1245 1222 1266 1282 1263 1273 1259 1262 temperature Liquidus viscosity dPa .Math. s 4.2 4.5 4.5 4.8 4.4 4.4 4.6 4.5 4.7 4.7 (log η at TL)

TABLE-US-00008 TABLE 8 No. 71 No. 72 No. 73 No. 74 No. 75 No. 76 No. 77 No. 78 No. 79 No. 80 Glass SiO.sub.2 mol % 68.75 68.07 67.75 67.77 68.06 67.90 67.84 66.83 67.35 66.96 composi- Al.sub.2O.sub.3 mol % 13.55 13.41 13.57 13.55 13.50 13.49 13.51 13.37 13.36 13.44 tion B.sub.2O.sub.3 mol % 0.98 1.11 1.03 1.04 0.86 0.96 0.98 3.26 2.78 3.57 Na.sub.2O mol % 0.012 0.015 0.015 0.013 0.015 0.013 0.012 0.020 0.017 0.030 K.sub.2O mol % 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.002 0.002 0.002 MgO mol % 6.96 7.84 7.96 7.95 7.91 7.94 7.93 6.37 6.35 5.87 CaO mol % 5.11 8.93 7.02 7.05 5.03 5.06 5.11 6.54 6.54 6.54 SrO mol % 0.52 0.51 2.52 0.51 4.47 2.53 0.51 1.81 1.81 1.61 BaO mol % 4.02 0.01 0.03 2.00 0.06 2.00 4.01 1.70 1.70 1.90 TiO.sub.2 mol % 0.009 0.007 0.007 0.007 0.007 0.008 0.009 0.006 0.006 0.006 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.086 0.081 0.082 0.088 0.083 0.085 0.086 0.080 0.075 0.076 Fe.sub.2O.sub.3 mol % 0.007 0.008 0.008 0.007 0.007 0.008 0.007 0.008 0.007 0.007 β-OH /mm 0.14 0.15 0.15 0.15 0.13 0.13 0.15 0.15 0.15 0.14 Density g/cm.sup.3 2.620 2.518 2.548 2.574 2.580 2.604 2.631 2.562 2.565 2.559 Thermal expansion ×10.sup.−7/ 37.4 36.6 37.1 37.4 37.6 37.9 38.2 37.6 37.5 37.3 coefficient ° C. Young's modulus GPa 84.5 87.7 87.2 86.5 86.5 85.8 85.1 83.5 84.0 82.9 Strain point ° C. 750 747 747 745 747 745 746 724 730 723 Temperature at ° C. 1287 1254 1257 1261 1259 1273 1271 1247 1256 1252 10.sup.4.5 dPa .Math. s Liquidus ° C. 1262.0 1255 1243 1280 1273 1267 1278 1202 1207 1190 temperature Liquidus viscosity dPa .Math. s 4.7 4.5 4.6 4.3 4.4 4.5 4.4 4.9 5.0 5.1 (log η at TL)

TABLE-US-00009 TABLE 9 No. 81 No. 82 No. 83 No. 84 No. 85 No. 86 No. 87 No. 88 No. 89 No. 90 Glass SiO.sub.2 mol % 67.22 67.59 67.61 67.28 67.59 67.55 67.60 67.54 67.63 67.29 composi- Al.sub.2O.sub.3 mol % 13.42 12.62 12.85 13.78 13.73 13.53 13.71 13.52 13.50 13.54 tion B.sub.2O.sub.3 mol % 3.28 3.16 3.06 1.52 1.51 1.51 1.51 1.50 1.41 1.50 Na.sub.2O mol % 0.024 0.027 0.016 0.030 0.024 0.023 0.020 0.032 0.020 0.018 K.sub.2O mol % 0.004 0.004 0.002 0.005 0.004 0.005 0.004 0.003 0.003 0.003 MgO mol % 5.74 6.45 6.45 7.53 7.53 75.3 7.52 7.52 7.80 7.79 CaO mol % 6.64 6.54 6.63 6.52 6.52 6.52 6.52 7.00 7.01 7.01 SrO mol % 1.61 1.51 1.60 2.76 2.75 2.99 3.00 2.74 2.50 2.49 BaO mol % 1.89 2.00 1.70 0.50 0.25 0.25 0.03 0.03 0.03 0.25 TiO.sub.2 mol % 0.007 0.007 0.007 0.007 0.007 0.006 0.007 0.007 0.017 0.007 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.080 0.075 0.079 0.079 0.078 0.078 0.078 0.078 0.078 0.082 Fe.sub.2O.sub.3 mol % 0.071 0.007 0.007 0.007 0.007 0.008 0.008 0.008 0.008 0.008 β-OH /mm 0.14 0.14 0.14 0.14 0.15 0.15 0.15 0.14 0.14 0.14 Density g/cm.sup.3 2.560 2.559 2.555 2.563 2.554 2.558 2.551 2.548 2.544 2.554 Thermal expansion ×10.sup.−7/ 37.3 37.9 37.6 37.5 37.0 37.5 37.0 37.4 37.1 37.6 coefficient ° C. Young's modulus GPa 83.1 82.4 83.0 86.2 86.4 86.2 86.6 86.5 86.6 86.6 Strain point ° C. 726 719 724 739 741 738 741 738 739 738 Temperature at ° C. 1256 1250 1252 1254 1257 1256 1255 1255 1253 1251 10.sup.4.5 dPa .Math. s Liquidus ° C. 1200 1184 1196 1240 1255 1240 1246 1239 1247 1246 temperature Liquidus viscosity dPa .Math. s 5.0 5.2 5.1 4.6 4.5 4.7 4.6 4.7 4.6 4.6 (log η at TL)

TABLE-US-00010 TABLE 10 No. 91 No. 92 No. 93 No. 94 No. 95 No. 96 No. 97 No. 98 No. 99 No. 100 Glass SiO.sub.2 mol % 67.63 67.49 67.50 67.48 67.33 67.64 67.81 67.62 67.72 67.33 composi- Al.sub.2O.sub.3 mol % 13.52 13.38 13.35 13.37 13.37 13.35 12.75 12.87 12.85 13.39 tion B.sub.2O.sub.3 mol % 1.41 3.17 3.17 3.21 3.19 3.21 3.21 3.23 3.18 3.17 Na.sub.2O mol % 0.016 0.015 0.015 0.014 0.014 0.014 0.014 0.013 0.014 0.014 K.sub.2O mol % 0.003 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 MgO mol % 7.54 5.67 5.75 5.85 5.86 5.63 6.34 6.33 6.34 6.14 CaO mol % 6.78 6.55 6.59 6.55 6.60 6.53 6.56 6.53 6.57 6.52 SrO mol % 2.76 1.62 1.52 1.62 1.63 1.62 1.42 1.52 1.42 1.63 BaO mol % 0.25 2.01 2.01 1.81 1.91 1.91 1.80 1.80 1.81 1.71 TiO.sub.2 mol % 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 ZrO.sub.2 mol % 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SnO.sub.2 mol % 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 Fe.sub.2O.sub.3 mol % 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 β-OH /mm 0.15 0.15 0.15 0.13 0.13 0.15 0.13 0.13 0.14 0.14 Density g/cm.sup.3 2.555 2.561 2.559 2.555 2.559 2.556 2.549 2.552 2.550 2.552 Thermal expansion ×10.sup.−7/ 37.5 37.3 37.2 37.1 37.3 37.1 37.2 37.4 37.2 37.1 coefficient ° C. Young's modulus GPa 86.4 82.5 82.7 82.9 82.7 82.5 82.6 82.8 82.8 83.2 Strain point ° C. 738 724 724 725 723 725 721 721 720 725 Temperature at ° C. 1255 1259 1257 1256 1255 1257 1255 1252 1253 1255 10.sup.4.5 dPa .Math. s Liquidus ° C. 1228 1199 1199 1198 1191 1201 1191 1196 1180 1212 temperature Liquidus viscosity dPa .Math. s 4.8 5.1 5.1 5.1 5.1 5.1 5.1 5.1 5.2 4.9 (log η at TL)

TABLE-US-00011 TABLE 11 No. 101 No. 102 No. 103 No. 104 No. 105 No. 106 No. 107 No. 108 No. 109 No. 110 Glass SiO.sub.2 mol % 67.40 67.67 67.83 67.99 67.87 68.52 68.45 67.88 67.87 67.95 composi- Al.sub.2O.sub.3 mol % 13.08 13.33 13.35 13.50 13.49 13.50 13.50 13.50 13.42 13.51 tion B.sub.2O.sub.3 mol % 3.15 3.25 3.25 1.10 1.10 1.10 1.60 1.08 1.16 1.56 Na.sub.2O mol % 0.014 0.018 0.015 0.017 0.012 0.017 0.013 0.031 0.018 0.017 K.sub.2O mol % 0.001 0.003 0.004 0.007 0.001 0.007 0.001 0.007 0.003 0.003 MgO mol % 6.35 5.65 5.44 7.94 8.05 7.42 7.46 7.96 7.97 7.50 CaO mol % 6.56 6.55 6.57 8.94 8.96 8.93 8.46 9.04 9.06 8.94 SrO mol % 1.63 1.62 1.63 0.41 0.41 0.41 0.41 0.41 0.41 0.41 BaO mol % 1.70 1.80 1.80 0.00 0.00 0.00 0.00 0.00 0.00 0.01 TiO.sub.2 mol % 0.007 0.007 0.006 0.008 0.007 0.008 0.008 0.007 0.007 0.007 ZrO.sub.2 mol % 0.001 0.001 0.001 0.002 0.001 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.089 0.089 0.089 0.081 0.081 0.077 0.081 0.081 0.077 0.081 Fe.sub.2O.sub.3 mol % 0.007 0.007 0.007 0.009 0.009 0.009 0.008 0.009 0.009 0.009 β-OH /mm 0.14 0.15 0.15 0.15 0.14 0.14 0.14 0.15 0.15 0.15 Density g/cm.sup.3 2.553 2.552 2.551 2.515 2.516 2.509 2.500 2.515 2.514 2.507 Thermal expansion ×10.sup.−7/ 37.3 36.9 36.8 36.4 36.5 36.0 35.4 36.6 36.6 36.2 coefficient ° C. Young's modulus GPa 83.0 82.8 82.6 87.8 87.9 87.5 87.0 87.6 87.6 87.1 Strain point ° C. 722 723 725 747 747 749 746 747 745 743 Temperature at ° C. 1249 1258 1263 1254 1254 1263 1262 1254 1253 1256 10.sup.4.5 dPa .Math. s Liquidus ° C. 1194 1198 1181 1261 1265 1263 1257 1253 1255 1247 temperature Liquidus viscosity dPa .Math. s 5.0 5.1 5.3 4.4 4.4 4.5 4.6 4.5 4.5 4.6 (log η at TL)

TABLE-US-00012 TABLE 12 No. 111 No. 112 No. 113 No. 114 No. 115 No. 116 No. 117 No. 118 No. 119 No. 120 Glass SiO.sub.2 mol % 68.15 70.34 68.79 68.72 67.27 67.29 67.33 65.79 65.81 68.78 composi- Al.sub.2O.sub.3 mol % 13.32 13.48 13.47 13.54 13.47 13.47 13.48 13.47 13.47 12.50 tion B.sub.2O.sub.3 mol % 1.57 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na.sub.2O mol % 0.021 0.010 0.010 0.010 0.010 0.010 0.010 0.010 0.010 0.010 K.sub.2O mol % 0.003 0.002 0.002 0.001 0.001 0.001 0.001 0.001 0.001 0.001 MgO mol % 7.47 7.52 9.07 7.57 10.60 9.06 7.52 10.58 9.07 9.53 CaO mol % 8.96 8.03 8.04 9.55 8.05 9.55 11.04 9.54 11.04 8.56 SrO mol % 0.41 0.51 0.51 0.51 0.50 0.51 0.51 0.50 0.51 0.51 BaO mol % 0.00 0.01 0.01 0.00 0.00 0.01 0.00 0.00 0.00 0.01 TiO.sub.2 mol % 0.008 0.006 0.007 0.006 0.006 0.007 0.007 0.006 0.006 0.007 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.077 0.085 0.081 0.085 0.084 0.085 0.085 0.080 0.081 0.080 Fe.sub.2O.sub.3 mol % 0.009 0.008 0.009 0.008 0.009 0.009 0.009 0.010 0.009 0.010 β-OH /mm 0.13 0.13 0.15 0.15 0.15 0.14 0.14 0.14 0.14 0.15 Density g/cm.sup.3 2.505 2.505 2.521 2.525 2.537 2.541 2.544 2.557 2.561 2.523 Thermal expansion ×10.sup.−7/ 36.2 34.4 35.6 36.8 36.8 38.0 39.2 39.2 40.4 37.6 coefficient ° C. Young's modulus GPa 86.8 88.0 89.1 88.4 90.3 89.4 88.7 90.5 90.0 88.7 Strain point ° C. 743 767 761 762 754 756 757 750 750 753 Temperature at ° C. 1258 1289 1268 1268 1246 1247 1249 1228 1228 1261 10.sup.4.5 dPa .Math. s Liquidus ° C. 1241 1283 1288 1270 1289 1265 1293 1260 1285 1262 temperature Liquidus viscosity dPa .Math. s 4.7 4.6 4.3 4.5 4.1 4.3 4.1 4.2 4.0 4.5 (log η at TL)

TABLE-US-00013 TABLE 13 No. 121 No. 122 No. 123 No. 124 No. 125 No. 126 Glass SiO.sub.2 mol % 68.81 67.29 67.30 67.25 65.83 65.86 composition Al.sub.2O.sub.3 mol % 12.50 12.50 12.50 12.55 12.48 12.48 B.sub.2O.sub.3 mol % 0.00 0.00 0.00 0.00 0.00 0.00 Na.sub.2O mol % 0.010 0.010 0.010 0.010 0.010 0.010 K.sub.2O mol % 0.001 0.001 0.001 0.001 0.001 0.001 MgO mol % 8.03 11.03 9.55 8.00 11.00 9.52 CaO mol % 10.04 8.56 10.03 11.57 10.06 11.52 SrO mol % 0.51 0.51 0.51 0.51 0.50 0.51 BaO mol % 0.00 0.01 0.00 0.00 0.01 0.00 TiO.sub.2 mol % 0.007 0.007 0.007 0.007 0.007 0.006 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.085 0.080 0.084 0.084 0.084 0.084 Fe.sub.2O.sub.3 mol % 0.010 0.011 0.009 0.010 0.010 0.010 β-OH /mm 0.15 0.13 0.13 0.15 0.13 0.13 Density g/cm.sup.3 2.527 2.540 2.544 2.548 2.561 2.565 Thermal expansion ×10.sup.−7/ 38.7 38.7 39.9 41.1 41.1 42.3 coefficient ° C. Young's modulus GPa 88.1 89.7 89.1 88.4 90.2 89.5 Strain point ° C. 754 748 747 746 740 738 Temperature at ° C. 1262 1243 1242 1238 1220 1222 10.sup.4.5 dPa .Math. s Liquidus ° C. 1268 1250 1251 1273 1241 1260 temperature Liquidus viscosity dPa .Math. s 4.5 4.4 4.4 4.2 4.3 4.1 (log η at TL) No. 127 No. 128 No. 129 No. 130 No. 131 Glass SiO.sub.2 mol % 68.75 68.76 67.24 67.29 65.79 composition Al.sub.2O.sub.3 mol % 14.54 14.54 14.53 14.52 14.52 B.sub.2O.sub.3 mol % 0.00 0.00 0.00 0.00 0.00 Na.sub.2O mol % 0.010 0.010 0.010 0.010 0.010 K.sub.2O mol % 0.001 0.001 0.001 0.001 0.001 MgO mol % 8.52 7.00 10.04 8.51 10.01 CaO mol % 7.56 9.05 7.56 9.05 9.05 SrO mol % 0.51 0.52 0.51 0.51 0.51 BaO mol % 0.00 0.01 0.01 0.00 0.00 TiO.sub.2 mol % 0.007 0.007 0.007 0.007 0.007 ZrO.sub.2 mol % 0.001 0.001 0.001 0.001 0.001 SnO.sub.2 mol % 0.086 0.086 0.081 0.085 0.081 Fe.sub.2O.sub.3 mol % 0.008 0.009 0.010 0.009 0.009 β-OH /mm 0.14 0.13 0.15 0.13 0.13 Density g/cm.sup.3 2.520 2.523 2.535 2.539 2.555 Thermal expansion ×10.sup.−7/ 34.8 36.0 36.0 37.2 38.4 coefficient ° C. Young's modulus GPa 89.5 88.8 90.6 90.0 91.0 Strain point ° C. 767 769 761 761 754 Temperature at ° C. 1273 1278 1254 1256 1236 10.sup.4.5 dPa .Math. s Liquidus ° C. 1316 1280 1321 1286 1289 temperature Liquidus viscosity dPa .Math. s 4.1 4.5 3.9 4.2 4.0 (log η at TL)

[0061] Each sample was prepared as follows. First, a glass batch obtained by mixing glass raw materials so as to have a glass composition shown in the tables was put into a platinum crucible and melted at 1600° C. for 24 hours. When melting the glass batch, the glass batch was stirred using a platinum stirrer for homogenization. Next, the molten glass was poured onto a carbon sheet, formed into a flat sheet shape, and then cut into a disk shape. For each of the obtained samples, a β-OH value, a density, a thermal expansion coefficient, a Young's modulus, a strain point, a temperature at 10.sup.4.5 dPa.Math.s, a liquidus temperature, a liquidus viscosity, and a thermal shrinkage were evaluated.

[0062] The β-OH value is a value calculated by the above equation.

[0063] The density is a value measured by a known Archimedes method.

[0064] The thermal expansion coefficient is an average thermal expansion coefficient measured with a dilatometer in a temperature range of 30° C. to 380° C.

[0065] The Young's modulus is a value measured by a dynamic elastic modulus measurement method (a resonance method) based on JIS R1602.

[0066] The strain point is a value measured based on a method of ASTM C336.

[0067] The temperature at a viscosity in high temperature of 10.sup.4.5 dPa.Math.s is a value measured by a platinum sphere pull up method.

[0068] The liquidus temperature is a temperature at which each sample is grinded, a glass powder that passes through a standard sieve of 30 mesh (500 μm) and remains on a sieve of 50 mesh (300 μm) is put into a platinum boat, the platinum boat is held in a temperature gradient furnace set at 1100° C. to 1350° C. for 24 hours, then the platinum boat is taken out, and devitrified crystals (crystal foreign substances) are observed in a glass. The liquidus viscosity is a value obtained by measuring a viscosity of a glass at a liquidus temperature by a platinum sphere pull up method.

[0069] As is clear from the tables, Sample Nos. 1 to 131 have a strain point of 715° C. or higher, a temperature at 10.sup.4.5 dPa.Math.s of 1290° C. or lower, and a Young's modulus of 81.7 GPa or higher, and thus are suitable as a glass disk for a magnetic recording medium.

[0070] A glass batch obtained by mixing glass raw materials so as to have a glass composition of each of Sample Nos. 1 to 131 in the tables was put into a melting kiln, melted at 1500° C. to 1700° C. for 24 hours, fined, homogenized, formed into a sheet shape by an overflow down-draw method so as to have a thickness of 0.675 mm, and then processed into a disk shape. A surface roughness Ra of a surface of the obtained glass disk was measured by an atomic force microscope (AFM) and found to be 0.10 nm to 0.20 nm. A total thickness variation (TTV) was 1.0 μm. Further, an average linear transmittance of the obtained glass disk in an optical path length of 1 mm and a wavelength range of 350 nm to 1500 nm was measured with a spectrophotometer UV-3100 manufactured by Shimadzu Corporation, and found to be 85% or more in each case.