Abstract

The invention relates to a refractory dry vibratable mix which sets at room temperature when water is added, for use in metallurgical vessels and comprising a refractory main component, a binder and a retarder.

Claims

1. A refractory dry vibratable mix that is formulated to set at room temperature when water is added to said refractory dry vibratable mix; said refractory dry vibratable mix includes a refractory main component, a binder and a retardant; said refractory main component constitutes 5-95 wt. % of said refractory dry vibratable mix; said refractory main component is formed of one or more of sintered magnesia, fused magnesia, olivine, quartz, and sintered dolomite; said binder constitutes >1-<5 wt. % of said refractory dry vibratable mix; said binder includes ammonium dihydrogen phosphate; said retardant constitutes >1-<5 wt. % of said refractory dry vibratable mix; said retardant includes carboxylic acid; said refractory dry vibratable mix includes less than 1 wt. % SiO.sub.2.

2. A refractory dry vibratable mix that is formulated to set at room temperature when water is added to said refractory dry vibratable mix; said refractory dry vibratable mix includes a refractory main component, a binder and a retardant; said refractory main component constitutes 5-95 wt. % of said refractory dry vibratable mix; said refractory main component is formed of one or more of sintered magnesia, fused magnesia, olivine, quartz, and sintered dolomite; said binder constitutes >1-<5 wt. % of said refractory dry vibratable mix; said binder includes a) ammonium dihydrogen phosphate, b) magnesium oxide and potassium dihydrogen phosphate, and wherein said magnesium oxide is absent sintered magnesia, fused magnesia, olivine, quartz, and sintered dolomite, or c) magnesium oxide and alkali polyphosphate, and wherein said magnesium oxide is absent sintered magnesia, fused magnesia, olivine, quartz, and sintered dolomite; said retardant constitutes >1-<5 wt. % of said refractory dry vibratable mix; said retardant includes carboxylic acid; said refractory dry vibratable mix includes less than 1 wt. % SiO.sub.2.

Description

DESCRIPTION OF THE INVENTION

(1) From the foregoing, the objective of the invention is to provide an improved dry vibratable mix for use in metallurgical vessels, which sets at room temperature when water is added, characterized by a refractory main component, a binder and a retardant.

(2) This objective is achieved by means of a refractory dry vibratable mix for use in metallurgical vessels, which sets at room temperature when water is added, characterized by a refractory main component, a binder and a retardant.

(3) The dry vibratable mix in accordance with the invention advantageously contains the binder components in the powdered form and can set at room temperature when water is added as a solvent or reactant, but does not suffer from the disadvantages described above.

(4) In one embodiment, a binder consisting of magnesium oxide and an alkali phosphate (for example potassium dihydrogen phosphate or an alkali polyphosphate) or ammonium dihydrogen phosphate or mixtures of these phosphates is provided. Preferably, the phosphate which is used is a potassium dihydrogen phosphate. Magnesium oxide and potassium dihydrogen phosphate react by taking in water to form crystalline potassium magnesium phosphate hexahydrate (set product). The water which is added acts both as a solvent and as a reactant in which it is taken up as water of crystallization. Upon heating, annealing-resistant magnesium pyrophosphate is formed at approximately 250 C. Beyond approximately 1000 C., this is converted into magnesium phosphate.

(5) Furthermore, the refractory mass in accordance with the invention is characterized in that it contains at least one retardant in the form of a carboxylic acid. The carboxylic acid used is, for example, citric acid, tartaric acid, malic acid, maleic acid, etc.

(6) Further features and embodiments of the invention are a refractory dry vibratable mix for use in metallurgical vessels, which sets at room temperature when water is added, characterized by a refractory main component, a binder and a retardant. The main component can comprise or can be a sintered magnesia, fused magnesia, olivine, quartz, sintered dolomite and/or secondary raw materials based on MgO. The binder can be based on magnesium oxide and an alkali phosphate and/or ammonium dihydrogen phosphate. The alkali phosphate can comprise or can be potassium dihydrogen phosphate and/or alkali polyphosphate. The retardant can be in the form of a carboxylic acid, in particular citric acid, tartaric acid, malic acid, maleic acid or malonic acid. The dry vibratable mix can comprise (as a % by weight): 5-95% of MgO or olivine, and/or amorphous SiO2, <1%, and/or carboxylic acid, >1%<5%, and/or alkali phosphate, >1%<5%. The refractory component can be magnesia and no additional MgO. The refractory component can be magnesia and in particular additional MgQ, <2% by weight, <1% by weight, <0.1% by weight MgO.