Preparation method and use of two-dimensional MoS2 materials

Abstract

A preparation method and a use of 2D MoS.sub.2 materials are provided. Molybdenum source and sulfur powder are used as raw materials, and inert gas is used as carrier gas. Through an intermediate evaporation process, the raw materials are transported to the molten glass surface and deposited into solid molybdenum sulfide. In the subsequent etching-spreading-sulfurization-precipitation process, ultra-high quality and ultra-large area MoS.sub.2 single-crystal domains are obtained under normal pressure and without hydrogenation. The single-crystal domain size of the prepared 2D MoS.sub.2 material can reach 1.5 cm, and then grow into a wafer-level 2D MoS.sub.2 material with a size of 2 inches and a thickness of 1-2 layers.

Claims

1. A preparation method of 2D MoS.sub.2 materials, comprising following steps: using molybdenum source and sulfur as raw materials, using inert gas as carrier gas, transporting the raw materials to a molten sodium-calcium glass surface to deposit solid molybdenum sulfide through an intermediate evaporation process, and obtaining the 2D MoS.sub.2 materials by etching, spreading, sulfurization and precipitation; the step of transporting the raw materials to the molten sodium-calcium glass surface to deposit the solid molybdenum sulfide through the intermediate evaporation process comprises: placing the sulfur in a first temperature zone and placing the molybdenum source and the sodium-calcium glass in a second temperature zone; and heating the first temperature zone to 120-180 C., heating the second temperature zone to 500-1400 C., introducing the inert gas in a heating process, transporting the sulfur to the second temperature zone by the inert gas, and depositing on the sodium-calcium glass surface to obtain a solid molybdenum sulfide layer; steps of the etching and the spreading are: after obtaining the solid molybdenum sulfide layer, adjusting a temperature of the second temperature zone to 900-1400 C., introducing oxygen, and etching the solid molybdenum sulfide layer to obtain Na.sub.2Mo.sub.2O.sub.7, and steps of the sulfurization and precipitation are: after obtaining the Na.sub.2Mo.sub.2O.sub.7, stopping oxygen supply and carrying out a sulfurization and precipitation reaction to obtain the 2D MoS.sub.2 materials.

2. The preparation method according to claim 1, wherein in a process of depositing to obtain the solid molybdenum sulfide layer, a heating rate of the first temperature zone is 5-50 C./min; a heating rate of the second temperature zone is 5-50 C./min; and the inert gas is argon, and a flow rate is 200-500 sccm.

3. The preparation method according to claim 1, wherein in a process of the etching and the spreading, a flow rate of the oxygen is 1-10 sccm; and a temperature adjustment rate of the second temperature zone is 0-50 C./min.

4. The preparation method according to claim 1, wherein the sulfur is sublimated sulfur; the molybdenum source is one of MoO.sub.3, sodium molybdate, molybdenum sulfide and molybdenum foil; and a dosage of the molybdenum source is 1 mg to 20 mg.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The attached drawings, which constitute a part of this disclosure, are used to provide a further understanding of this disclosure. The illustrative embodiments and descriptions of this disclosure are used to explain this disclosure, and do not constitute an improper limitation of this disclosure. In the attached drawings:

(2) FIG. 1 is a schematic diagram of the growth of 2D MoS.sub.2.

(3) FIG. 2 is a flow chart of the preparation of the 2D MoS.sub.2 material of the present disclosure, where the substrate 1 is sodium-calcium glass and the substrate 2 is wafer.

(4) FIG. 3 is a single-crystal domain size diagram of the 2D MoS.sub.2 material prepared in Embodiment 1.

(5) FIG. 4 is a scanning tunneling microscope diagram of the 2D MoS.sub.2 prepared in Embodiment 1.

(6) FIG. 5 is a size diagram of the double-layer 2D MoS.sub.2 material prepared in Embodiment 2.

(7) FIG. 6 is a size diagram of the wafer-level 2D MoS.sub.2 material prepared in Embodiment 3.

(8) FIG. 7 is a single-crystal domain size diagram of a 2D MoS.sub.2 material prepared from molybdenum sulfide, sodium molybdate or molybdenum foil, where a is molybdenum sulfide, b is sodium molybdate and c is molybdenum foil.

(9) FIG. 8 is a single-crystal domain size diagram of 2D MoS.sub.2 prepared in Comparative Embodiment 1.

(10) FIG. 9 is a single-crystal domain size diagram of a pseudo-single-crystal TMDCs wafer prepared in Comparative Embodiment 2.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(11) A number of exemplary embodiments of the present disclosure will now be described in detail, and this detailed description should not be considered as a limitation of the present disclosure, but should be understood as a more detailed description of certain aspects, characteristics and embodiments of the present disclosure.

(12) It should be understood that the terminology used in the present disclosure is only for describing specific embodiments and is not used for limiting the present disclosure. In addition, for the numerical range in the present disclosure, it should be understood that each intermediate value between the upper limit and the lower limit of the range is also specifically disclosed. Intermediate values within any stated value or stated range, as well as each smaller range between any other stated value or intermediate values within the stated range are also included in the present disclosure. The upper and lower limits of these smaller ranges can be included or excluded independently.

(13) Unless otherwise specified, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure relates. Although the present disclosure only describes the preferred methods and materials, any methods and materials similar or equivalent to those described herein can also be used in the practice or testing of the present disclosure. All documents mentioned in this specification are incorporated by reference to disclose and describe methods and/or materials related to the documents. In case of conflict with any incorporated document, the contents of this specification shall prevail.

(14) It is obvious to those skilled in the art that many improvements and changes can be made to the specific embodiments of the present disclosure without departing from the scope or spirit of the present disclosure. Other embodiments obtained from the description of the present disclosure are obvious to the skilled person. The description and embodiment of the present disclosure are exemplary only.

(15) The terms including, comprising, having and containing used herein are all open terms, which means including but not limited to.

(16) Unless otherwise specified, the room temperature and normal temperature in the specific embodiment of the present disclosure are both 20-30 degrees Celsius ( C.).

(17) In a specific embodiment of the present disclosure, the inert gas is argon.

(18) FIG. 1 is a schematic diagram of the growth of 2D MoS.sub.2.

(19) FIG. 2 is a flow chart of the preparation of the 2D MoS.sub.2 material of the present disclosure, where the substrate 1 is sodium-calcium glass and the substrate 2 is a wafer.

Embodiment 1

(20) The preparation steps of the centimeter-level 2D MoS.sub.2 single-crystal domain material are as follows. S1, treatment of growth substrate: the sodium-calcium glass surface is ultrasonically cleaned with acetone, isopropanol and water for 5 minutes (min), respectively, and then the glass substrate with clean surface is obtained by oxygen ion etching after being dried by nitrogen; S2, oven drying and inert gas protection: heating the tube furnace to 500 C. for heat preservation, and introducing inert protective gas to expel air; S3, double-temperature zone heating growth: putting sublimated sulfur in the first temperature zone, pushing 5 mg of MoO.sub.3 powder and sodium-calcium glass in the second temperature zone in turn (sodium-calcium glass is set off by wafer, in order to keep the shape of sodium-calcium glass at high temperature), the distance between molybdenum source and sodium-calcium glass is about 12-15 cm, and heating the first temperature zone to 130 C. at a heating rate of 50 degrees Celsius per minute ( C./min). Heating the second temperature zone to 1000 C. at a heating rate of 20 C./min, transporting the sublimated sulfur in the first temperature zone to the second temperature zone in the form of steam under the flow of inert gas (100 standard cubic centimeter per minute (sccm)), and depositing on the sodium-calcium glass surface to obtain a solid molybdenum sulfide layer; S4, after obtaining a solid molybdenum sulfide layer, introducing oxygen (1-10 sccm) at 1000 C., and etching the solid molybdenum sulfide layer to obtain a Na.sub.2Mo.sub.2O.sub.7 precursor; and S5, after obtaining the Na.sub.2Mo.sub.2O.sub.7 precursor, stopping oxygen supply, carrying out sulfurization and precipitation reaction, and cooling to room temperature to obtain the centimeter-level 2D MoS.sub.2 material.

(21) The single-crystal domain size diagram of the centimeter-level 2D MoS.sub.2 material prepared in S5 step is shown in FIG. 3; and the scanning tunneling microscope (STM) diagram of the centimeter-level 2D MoS.sub.2 material prepared in S5 step is shown in FIG. 4, where the bright spots are molybdenum atoms (Mo) and the dark spots are sulfur atoms(S).

Embodiment 2

(22) The preparation steps of the double-layer 2D MoS.sub.2 material are as follows. S1, treatment of growth substrate: the sodium-calcium glass surface is ultrasonically cleaned with acetone, isopropanol and water for 5 min, respectively, and then the glass substrate with clean surface is obtained by oxygen ion etching after being dried by nitrogen; S2, oven drying and inert gas protection: heating the tube furnace to 500 C. for heat preservation, and introducing inert protective gas to expel air; S3, double-temperature zone heating growth: putting sublimated sulfur in the first temperature zone, pushing 8 mg of MoO.sub.3 powder and sodium-calcium glass in the second temperature zone in turn (sodium-calcium glass is set off by wafer, in order to keep the shape of sodium-calcium glass at high temperature), the distance between molybdenum source and sodium-calcium glass is about 12-15 cm, and heating the first temperature zone to 160 C. at a heating rate of 50 C./min. Heating the second temperature zone to 1000 C. at a heating rate of 20 C./min, transporting the sublimated sulfur in the first temperature zone to the second temperature zone in the form of steam under the flow of inert gas (150 sccm), and depositing on the sodium-calcium glass surface to obtain a solid molybdenum sulfide layer; S4, after obtaining a solid molybdenum sulfide layer, introducing oxygen (1-10 sccm) at 1100 C., and etching the solid molybdenum sulfide layer to obtain a Na.sub.2Mo.sub.2O.sub.7 precursor; and S5, after obtaining the Na.sub.2Mo.sub.2O.sub.7 precursor, stopping oxygen supply, carrying out sulfurization and precipitation reaction, and cooling to room temperature to obtain the centimeter-level 2D MoS.sub.2 material.

(23) The single-crystal domain size diagram of the double-layer 2D MoS.sub.2 material prepared in S5 step is shown in FIG. 5.

Embodiment 3

(24) The preparation steps of the wafer-level 2D MoS.sub.2 material are as follows. S1, treatment of growth substrate: the sodium-calcium glass surface is ultrasonically cleaned with acetone, isopropanol and water for 5 min, respectively, and then the glass substrate with clean surface is obtained by oxygen ion etching after being dried by nitrogen; S2, oven drying and inert gas protection: heating the tube furnace to 500 C. for heat preservation, and introducing inert protective gas to expel air; S3, double-temperature zone heating growth: putting sublimated sulfur in the first temperature zone, pushing 10 mg of MoO.sub.3 powder and sodium-calcium glass in the second temperature zone in turn (sodium-calcium glass is set off by wafer, in order to keep the shape of sodium-calcium glass at high temperature), the distance between molybdenum source and sodium-calcium glass is about 12-15 cm, and heating the first temperature zone to 150 C. at a heating rate of 50 C./min. Heating the second temperature zone to 1100 C. at a heating rate of 20 C./min, transporting the sublimated sulfur in the first temperature zone to the second temperature zone in the form of steam under the flow of inert gas (100 sccm), and depositing on the sodium-calcium glass surface to obtain a solid molybdenum sulfide layer; S4, after obtaining a solid molybdenum sulfide layer, introducing oxygen (1-10 sccm) at 1100 C., and etching the solid molybdenum sulfide layer to obtain a Na.sub.2Mo.sub.2O.sub.7 precursor; and S5, after obtaining the Na.sub.2Mo.sub.2O.sub.7 precursor, stopping oxygen supply, carrying out sulfurization and precipitation reaction, and cooling to room temperature to obtain the centimeter-level 2D MoS.sub.2 material. After the wafer-level 2D MoS.sub.2 material is transferred to a wafer, the sizes are measured, as shown in FIG. 6.

Embodiment 4

(25) The only difference from Embodiment 1 is that MoO.sub.3 powder is replaced by molybdenum sulfide, sodium molybdate or molybdenum foil with the same mass.

(26) FIG. 7 is a single-crystal domain size diagram of a 2D MoS.sub.2 material prepared from molybdenum sulfide, sodium molybdate or molybdenum foil, where a is molybdenum sulfide, b is sodium molybdate and c is molybdenum foil.

Comparative Embodiment 1

(27) The steps of preparing 2D MoS.sub.2 by conventional CVD are as follows.

(28) S1, the precursor is evaporated/sublimated into gas at high temperature and transported to the substrate area under the action of carrier gas.

(29) S2, on the surface of the substrate, at first, some precursor gas molecules break through the adsorption potential barrier and are adsorbed on the surface of the glass substrate, and then break through the nucleation barrier to undergo chemical reaction to obtain nucleation. At the same time, a part of gas molecules is desorbed and leave the substrate surface.

(30) S3, after the nucleation is completed, the precursor continues to grow near the nucleation point in two ways: 1. breaking through E1 and directly adsorbing on the edge of the nucleation point, and completing the bonding and growth along the edge; 2. breaking through E2 and firstly adsorbing on the substrate surface, and then completing aggregation, bonding and growth at the edge of nucleation point through diffusion on the substrate surface. In fact, E1 is much larger than E2, so the adsorption and diffusion on the substrate surface are very important factors affecting the growth of 2D materials.

(31) FIG. 8 is a single-crystal domain size diagram of 2D MoS.sub.2 prepared in Comparative Embodiment 1. As can be seen from FIG. 8, the 2D MoS.sub.2 material prepared by this method has a small area with a size side length of only 2.6 mm, which is quite different from that prepared in Embodiment 1 of this disclosure.

Comparative Embodiment 2

(32) The steps of splicing micron-sized particles to synthesize a pseudo-single-crystal TMDCs wafer with a large number of crystal boundaries are as follows.

(33) S1, by increasing the mass flux greatly, the nucleation barrier is broken, and a large number of nucleation sites are gathered on the substrate surface.

(34) S2, using high-quality flux to break through the diffusion barrier and complete the growth of a large number of micron-sized crystal domains on the substrate surface.

(35) S3, when the micron-sized crystal domains grow to be in contact with the adjacent domains, the randomly oriented crystal domains will generate crystal boundaries during the splicing process.

(36) FIG. 9 is a single-crystal domain size diagram of the pseudo-single-crystal TMDCs wafer prepared in Comparative Embodiment 2. As can be seen from FIG. 9, there are obvious crystal boundaries in the crystal domain of the pseudo-single-crystal TMDCs wafer prepared in Comparative Embodiment 2, thus affecting the stability as a channel material.

(37) By improving the growth method and controlling the growth conditions, the defect density of the prepared material is lower than 1.010.sup.13 cm.sup.2, and low defect density means high uniformity and stability of the material, which is beneficial to the preparation of large-scale high-quality integrated circuits.

(38) In this disclosure, the transfer mode of molybdenum source is as follows: after sublimation, molybdenum sulfide solid is carried away by carrier gas to complete the gas-solid process, after oxygen is introduced, the solid-liquid process is completed; and after stopping oxygen supply, the liquid-solid process is completed to form 2D MoS.sub.2. Under the condition of increasing the amount of molybdenum source, more competition will occur between crystal domains, and the final product will be a wafer-level crystal domain splicing film, so that the substrate surface is fully spliced with splicing films, and when the dosage is low, a centimeter-level single-crystal domain is formed.

(39) The various embodiments in this specification are described in a progressive way, and each embodiment focuses on the differences from other embodiments, and the same and similar parts among the embodiments can only be referred to each other.

(40) The above description of the disclosed embodiments enables those skilled in the art to make or use the disclosure. Many modifications to these embodiments will be obvious to those skilled in the art, and the general principles defined herein can be implemented in other embodiments without departing from the spirit or scope of the disclosure. Therefore, the present disclosure is not to be limited to the embodiments shown herein, but is to be accorded the widest scope consistent with the principles and novel features disclosed herein.