MATERIAL FOR A POLYSTYRENE-BASED FOOD PACKAGING AND PREPARATION METHOD

Abstract

A material for food packaging, includes a polystyrene and 0.1 to 50% by weight of a halloysite essentially in the form of empty nanotubes, relative to the weight of the material, a method for preparing such a material, as well as the applications of this material, in particular for the manufacture of a food packaging.

Claims

1. A material for food packaging, the material comprising: a polystyrene and 0.1 to 50% by weight of a halloysite essentially in the form of empty nanotubes, relative to the weight of the material.

2. The material according to claim 1, the material further comprising at least one additive selected from the group consisting of antioxidants, colourants, pigments, and mineral fillers.

3. A food packaging comprising a material according to claim 1.

4. The food packaging according to claim 3, wherein the food packaging is multilayer and comprises at least one layer made of a material comprising a polystyrene and 0.1 to 50% by weight of a halloysite essentially in the form of empty nanotubes, relative to the weight of the material.

5. The food packaging according to claim 4, wherein the food packaging comprises several layers, identical or different, made of a material comprising a polystyrene and 0.1 to 50% by weight of a halloysite essentially in the form of empty nanotubes, relative to the weight of the material.

6. A method for preparing a polystyrene-based material for food packaging, wherein a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes is homogenized, to obtain said material.

7. The method according to claim 6, characterized in that it the method including the following steps of: a) Homogenizing a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes to obtain a primary mixture, and b) Homogenizing the primary mixture a) with a polystyrene in particulate form to obtain said material.

8. A method for limiting, and possibly inhibiting, the migration of styrene from a polystyrene-based material for food packaging, wherein a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes is homogenized, to obtain said material.

9. The method according to claim 8, the method including the following steps: a) Homogenizing a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes to obtain a primary mixture, and b) Homogenizing the primary mixture a) with a polystyrene in particulate form to obtain said material.

10. The method according to claims, wherein the halloysite is entirely in the form of empty nanotubes.

11. The method according to claims, wherein the halloysite is dried.

12. The method according to claim 6, wherein the, one or all homogenizations are carried out in a twin-screw extruder.

13. The method according to claim 7, wherein the polystyrene of step a) and the polystyrene of step b) are identical or different.

14. The method according to claim 6, wherein the particulate polystyrene(s) are in the form of particles having a size smaller than or equal to 1 cm.

15. The method according to claim 6, wherein the content of halloysite essentially in the form of empty nanotubes in said material is from 0.1 to 50% by weight, relative to the weight of the material.

16. The method according to claim 6, wherein at least one additive selected from the group consisting of antioxidants, colourants, pigments, and mineral fillers is added.

17. A use of a halloysite in the form of hollow nanotubes, to manufacture a polystyrene-based material with low styrene release, for food packaging.

Description

DETAILED DESCRIPTION OF THE DISCLOSURE

[0021] As previously indicated, an object of the disclosure relates to a material for food packaging, comprising a polystyrene and a halloysite essentially in the form of empty nanotubes, the halloysite being present in a content of 0.1 to 50% by weight relative to the weight of the material. Preferably, the halloysite content is 0.1 to 30%, and possibly 0.1 to 20%, and possibly 0.1 to 10%. Beyond the value of 50% of the halloysite content, the qualities of the packaging are altered, and below a value of 0.1%, the halloysite content is too low to prevent the migration of styrene.

[0022] As will be demonstrated later on in the examples, the inventors have identified, among several clays, the halloysite as an additive to polystyrene to overcome the aforementioned problem. Even if a mechanism could be considered, it would appear that halloysite acts by catalyzing the polymerization of styrene monomers, dimers and trimers into stable oligomers of at least 4 units, preventing the migration of said monomers, dimers and trimers; this result is completely unexpected.

[0023] By “essentially in the form of empty nanotubes”, it should be understood that most of halloysite tubes are empty, or in any case that the existence of some tubes which would not be empty that could be considered as present in the form of traces, in no way affects the effectiveness of the additive of the disclosure. According to a variant of the disclosure, the halloysite of mixture a) is entirely in the form of empty nanotubes.

[0024] Said material of the disclosure is intended for food packaging, and it may include any usually used additive. Thus, it may comprise at least one or more additive(s) selected from antioxidants, colourants, pigments, mineral fillers, fibers whether natural or synthetic. Any other additive well known to those skilled in the art can be added. The proportion of each of the additives is highly variable depending on the nature and function of the additive and can easily be determined by those skilled in the art with regards to the expected properties. For illustration, the proportion of the antioxidant(s) is preferably smaller than or equal to 1% by weight relative to the weight of the material. The proportion of pigments and/or colourants can reach 20% by weight relative to the weight of the material. That of the mineral fillers and/or fibers can amount to 40%, and possibly 50% by weight relative to the weight of the material. This material may be in various forms, thus it may be in the form of a flexible film.

[0025] Another object of the disclosure relates to a food packaging comprising at least one material as defined above. By “at least”, it should be understood that the food packaging may comprise two or more materials, said materials being as defined above and different. It may also comprise any other appropriate material which is compatible with the material of the disclosure. Thus, a food packaging of the disclosure may be multilayer and may comprise at least one layer of a material according to the disclosure. It may comprise or consist of several layers at least two, or more, or even all, of which are each made of a material of the disclosure, said materials of each layer may be identical or different.

[0026] The disclosure also concerns a method for preparing a polystyrene-based material for food packaging, comprising the step according to which a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes is homogenized, to obtain said material.

[0027] According to a variant of such a method, it comprises the following steps of:

[0028] a) Homogenizing a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes to obtain a primary mixture, and

[0029] b) Homogenizing the primary mixture a) with a polystyrene in particulate form to obtain said material.

[0030] In another aspect, the disclosure concerns a method for limiting, and possibly inhibiting, the migration of styrene from a polystyrene-based material for food packaging, this method comprising the step according to which a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes is homogenized, to obtain said material.

[0031] According to a variant, the method comprises the following steps of:

[0032] a) Homogenizing a mixture of a polystyrene in particulate form and at least one halloysite essentially in the form of empty nanotubes to obtain a primary mixture, and

[0033] b) Homogenizing the primary mixture a) with a polystyrene in particulate form to obtain said material.

[0034] Implementations of the disclosure are described below, the features set out below may be considered individually or in any combination.

[0035] The halloysite according to the disclosure is favorably used in powder form. This form is commercially available. A preferred particle size distribution of the halloysite powder is as follows: d90:10.00 μm; d50:0.19 μm, d100:18 μm. Preferably, the halloysite is dried before use thereof, for example in a dryer for 2 hours at 120° C.

[0036] According to an advantageous variant, the homogenization step of a method of the disclosure, or step a) and/or step b) of the above methods is carried out in a twin-screw extruder; preferably steps a) and b) are carried out in a twin-screw extruder.

[0037] The choice of polystyrene is adapted to the food packaging and those skilled in the art have no difficulty in making it using their general knowledge. Steps a) and b) make use of particulate polystyrenes, which may be identical or different.

[0038] By particulate polystyrene in step a) and/or step b), it should be advantageously understood a polystyrene in the form of particles of which at least 95% have a size smaller than 1 cm. The homogenization of polystyrene particles with halloysite must be optimal to obtain maximum efficiency of the halloysite. And according to the variant defined above of a method of the disclosure, it is preferable that the homogenization of polystyrene particles with halloysite to obtain the primary mixture of step a) but also that the homogenization of the primary mixture with a polystyrene in step b) are as thoroughly as possible. Such particulate polystyrenes are commercially available; they can also be obtained by any grinding technique from a polystyrene for example in the form of granules.

[0039] To obtain the primary mixture, in step a), 50-99.9% by weight of polystyrene and 0.1-50% by weight of halloysite, relative to the weight of the expected final material, are mixed. In step b), 1-60% by weight of primary mixture and 40-99% by weight of polystyrene are mixed to obtain the secondary mixture.

[0040] According to the method, at least one additive can be added. These are those previously identified and optionally any other appropriate additive well known to those skilled in the art. Advantageously, the additive(s) are added in step a).

[0041] The disclosure also concerns the manufacture of a packaging of the disclosure. This comprises a step of shaping a material of the disclosure by heat treatment. It can be performed by any shaping technique such as thermoforming, injection, extrusion. Preferably, it is carried out by extrusion in a single-screw or twin-screw extruder.

[0042] In another aspect, the disclosure concerns a method for preserving food in a polystyrene-based packaging, comprising the following steps of:

[0043] manufacturing a polystyrene-based packaging by a method of the disclosure described above, and

[0044] packaging said food in the packaging and storing the food thus packaged under conditions adapted to said food.

[0045] Compared to conventional polystyrene-based packaging, the migration of styrene into the preserved food is substantially reduced and the risk of toxicity related thereto is thus significantly reduced, and possibly eliminated.

[0046] The disclosure also concerns the use of halloysite in the form of hollow nanotubes, to manufacture a polystyrene-based material for food packaging, with low styrene release. Advantageously, halloysite is used in the previously indicated contents.

[0047] The features and advantages of some aspects of the disclosure will appear from the examples below, which illustrate the influence of different clays on the migration of styrene from a polystyrene composition.

Example 1: Experimental Protocol

[0048] 1.1) Clays

[0049] The tested clays are as follows:

[0050] {circle around (1)} A clay of the disclosure, a Dragonite HP halloysite commercialized by APPLIED MINERALS INC and meeting the following characteristics:

[0051] chemical formulation AlSi.sub.2O.sub.5(OH).sub.2.nH.sub.2O, with n ranging from 0-3

[0052] % of metal oxides by weight relative to the total weight of the composition

TABLE-US-00001 Na.sub.2O and K.sub.2O <0.10% CaO <0.20% MgO <0.05% Fe.sub.2O.sub.3  0.3-1% TiO.sub.2 <0.05% P.sub.2O.sub.5 <0.75%,

[0053] nanotube morphology:

TABLE-US-00002 length (L)  0.2-2 μm outer diameter (D) 50-70 nm inner diameter 15-30 nm with L/D 10-20,

[0054] cation exchange capacity (in milliequivalents per 100 g): 11,

[0055] particle size distribution (μm):

TABLE-US-00003 d90 10.00 d50 0.19 d10 0.18, pH 3.7-5.0

[0056] {circle around (2)} A montmorillonite commercialized under the name “Polargel HV” by MINERAL TECHNOLOGY;

[0057] {circle around (3)} An attapulgite commercialized under the name “Actigel 208” by ACTIVE MINERALS;

[0058] {circle around (4)} A silicalite commercialized under the name “Asorbio ZSM 5” by SILKEM

[0059] {circle around (5)} A zeolite having a pore size of 13 Å commercialized under the name “Asorbio ZAP 13X” by SILKEM (zeolite having a pore size of 13 Å); and

[0060] {circle around (6)} Another zeolite having a pore size of 4 Å commercialized under the name “Zeoflair 1000” by ZEOCHEM.

[0061] 1.2) Preparation of a Packaging Type Polystyrene Sample

[0062] Commercial granules of crystal polystyrene (General Purpose PolyStyrene, GPPS) of the Edistir® N 1840 type are ground until obtaining a powder less than 5% of the particles of which are larger than 1,000 μm.

[0063] The clays and zeolites are dried in a dryer for 2 hours at 120° C.

[0064] The ground GPPS is then mixed for one minute at high speed in a turbo-mixer with clays and zeolites {circle around (1)} to {circle around (6)} and an antioxidant additive Irganox® 1076.

[0065] The powder mixtures thus obtained are extruded at 190° C. into pellets using a twin-screw extruder of the TSA 21-40D type so that each mixture contains 30% of mineral clay by weight in the samples 1-6. A control sample is prepared in the same way with the only difference that it does not contain clay or antioxidant.

[0066] Each of the mixtures is then combined with a mixture having a weight ratio of 50/50 of crystal polystyrene (GPPS) of the Edistir® N 1840 type and high impact polystyrene (HIPS) of the Edistir® R 850 E type, to reach a final clay or zeolite content of 3% by weight relative to the weight of the mixture.

[0067] The mixtures are then extruded at 200° C. into 800 μm thick sheets with a single-screw extruder.

Example 2: Miciration Test and Results

[0068] The sheets thus obtained are tested for the migration of styrene monomers according to the Commission Regulation (EU) No. 10/2011 of Jan. 14, 2011 on plastic materials and articles intended to come into contact with food. The foodstuff simulant D1 of said regulation has been retained, it corresponds to an ethanol aqueous solution at 50% (v/v). Each sheet is immersed in such a solution for 10 days at 40° C., at the end of which the styrene concentration is measured by gas chromatography coupled with mass spectrometry CG/MS.

[0069] The results are shown in Table 1 below.

TABLE-US-00004 TABLE 1 Formulations F1 F2 F3 F4 F5 F6 Constituents Control Invention Comparative Comparative Comparative Comparative Comparative {circle around (1)} — 3 — — — — — {circle around (2)} — — 3 — — — — {circle around (3)} — — — 3 — — — {circle around (4)} — — — — 3 — — {circle around (5)} — — — — — 3 — {circle around (6)} — — — — — — 3 GPPS 50 48.49 48.49 48.49 48.49 48.49 48.49 HIPS 50 48.49 48.49 48.49 48.49 48.49 48.49 Antioxidant — 0.02 0.02 0.02 0.02 0.02 0.02 Specific migration of styrene (ppm) 0.066 0.006 0.060 0.078 0.059 0.078 0.078

[0070] It is observed that the formulation F1 allows reducing the migration by a ratio of more than 90% compared to the control formulation. It is also noticed that at equal concentrations three of the tested clays increase the migration of styrene compared to the control formulation. Among the comparative tests, only two clays have the capability of limiting the migration of styrene compared to the control formulation, yet the reduction rate does not exceed 10%.

[0071] Halloysite proves to be surprisingly effective.

[0072] The aforementioned document WO2004/012998A2 provides an illustration of the expected effect which seems to concern nanoparticles of any platy mineral filler. It arises from the present example that among various clays, halloysite is indeed the only one to have this capability of substantially reducing the migration of styrene.

Example 3

[0073] Two polystyrene formulations are prepared, one is a control formulation containing no clay and the other one according to the disclosure.

[0074] Control Formulation:

[0075] Commercial granules of crystal polystyrene (GPPS) of the Edistir® N 1840 type and high impact polystyrene (HIPS) of the Edistir® R 850 E type in a ratio of 50:50, are ground until obtaining a powder which is extruded at 200° C. into pellets using a twin-screw extruder of the TSA 21-40D type.

Formulation According to the Disclosure

[0076] Commercial granules of crystal polystyrene (GPPS) of the Edistir® N 1840 type are ground until obtaining a powder less than 5% of the particles of which are larger than 1,000 μm.

[0077] The used clay is a Dragonite HP halloysite. It is dried beforehand in a dryer for 2 hours at 120° C., and then added to ground GPPS in a proportion of 30% by weight relative to the weight of the mixture, as well as an antioxidant additive Irganox® 1076. The whole is then mixed for one minute at high speed in a turbo-mixer.

[0078] The powder mixture thus obtained is extruded at 190° C. into pellets using a twin-screw extruder of the TSA 21-40D type.

[0079] The pellets are then combined with a mixture having a weight ratio of 50/50 of crystal polystyrene (GPPS) of the Edistir® N 1840 type and high impact polystyrene (HIPS) of the Edistir® R 850 E type, to reach a final clay content of 3% by weight relative to the weight of the mixture.

[0080] Aliquots of 0.2 g of each of the formulations are sampled and dissolved in 8 ml of tetrahydrofuran. The samples are filtered and then analyzed by GC/MS in order to determine the volatile organic compounds not trapped by the clay.

[0081] The results are shown in Table 2 below.

TABLE-US-00005 TABLE 2 Formulations Constituents Control Disclosure Halloysite (% w/w) — 3 GPPS (% w/w) 50 48.49 HIPS (% w/w) 50 48.49 Antioxidant (% w/w) — 0.02 Detected volatile organic compounds Styrene monomer (ppm) 846 112.9 Styrene dimer (ppm) 3288 815 Styrene trimer (ppm) 13465 293 Styrene tetramer (ppm) 340 4302

[0082] From these results, the following observations emerge:

[0083] Compared to the control formulation, a much lower content of styrene monomers, dimers and trimers is detected for a formulation of the disclosure, only the tetramers are in high proportion; this suggests that halloysite catalyzes the formation of oligomers of at least 4 units from styrene mono-, di- and tri-mers; [0084] generally, that is to say including mono- and oligo-mers, a much lower rate of released styrene units, for a formulation of the disclosure, is measured; this indisputably demonstrates the positive effect of a halloysite by considerably reducing the degradation of polystyrene.