NI-BASED ALLOY MEMBER MANUFACTURING METHOD

Abstract

In an Ni-based alloy member manufacturing method, an Ni-based alloy casting material is casted, in which a -phase in an amount of 50 vol. % or more can be deposited in a -phase in the aging step. The Ni-based alloy casting material obtained after the casting step is heated for 1 hour or longer in a first strain removing temperature range of Ts0.90 C. to Ts C., when Ts C. represents the solid solution temperature of the -phase. The Ni-based alloy casting material obtained after the first strain removing heat treatment step is heated from the first strain removing temperature range to a solutionizing temperature range of higher than Ts+t1 C. but not higher than Tm C., when Tm C. represents the melting point of the -phase and t1 represents a temperature 10 C. or lower, and the temperature is held in the solutionizing temperature range for 2 hours or longer.

Claims

1. A Ni-based alloy member manufacturing method comprising: a casting step; a first strain removal heat treatment step; a solution heat treatment step; and an aging heat treatment step, wherein, in the casting step, a Ni-based alloy cast material having a chemical composition in which a phase is precipitable in an amount of 50 volume % or more in a phase in the aging heat treatment step is cast, in the first strain removal heat treatment step, when a solid-solution temperature of the phase is denoted by Ts C., the Ni-based alloy cast material after the casting step is heated in a first strain removal temperature range of Ts0.90 C. or higher and Ts C. or lower for one hour or longer, in the solution heat treatment step, when a melting point of the phase is denoted by Tm C., the Ni-based alloy cast material after the first strain removal heat treatment step is heated from the first strain removal temperature range to a solution heat treatment temperature range of higher than Ts+t1 C. and Tm C. or lower, and a temperature is held for two hours or longer in the solution heat treatment temperature range, and the t1 is 10 C. or lower.

2. The Ni-based alloy member manufacturing method according to claim 1, further comprising: a second strain removal heat treatment step between the first strain removal heat treatment step and the solution heat treatment step, wherein, when a temperature range of higher than Ts C. and Tm C. or lower, and lower than the solution heat treatment temperature range by the t1 C. is set as a second strain removal temperature range, in the second strain removal heat treatment step, the Ni-based alloy cast material after the first strain removal heat treatment step is heated from the first strain removal temperature range to the second strain removal temperature range, and the temperature is held for one hour or longer in the second strain removal temperature range, and in the solution heat treatment step, the Ni-based alloy cast material after the second strain removal heat treatment step is heated from the second strain removal temperature range to the solution heat treatment temperature range, and the temperature is held for two hours or longer in the solution heat treatment temperature range.

3. The Ni-based alloy member manufacturing method according to claim 1, wherein in the aging heat treatment step, the Ni-based alloy cast material after the solution heat treatment step is heated in an aging heat treatment temperature range of 850 C. or higher and 870 C. or lower for two hours to 20 hours.

4. The Ni-based alloy member manufacturing method according to claim 1, wherein in the first strain removal heat treatment step, a temperature rising rate from room temperature to the first strain removal temperature range is 50 C./min or slower.

5. The Ni-based alloy member manufacturing method according to claim 1, wherein in the solution heat treatment step, a temperature rising rate from the first strain removal temperature range to the solution heat treatment temperature range is 50 C./min or slower.

6. The Ni-based alloy member manufacturing method according to claim 1, wherein in the solution heat treatment step, after holding the temperature for two hours or longer, cooling from the solution heat treatment temperature range to room temperature is performed at a cooling rate of 10 C./min or faster.

7. The Ni-based alloy member manufacturing method according to claim 1, wherein a chemical composition of the Ni-based alloy cast material includes, by mass %, Cr: 5% to 15%, W: 3% to 10%, Al: 3.0% to 7.0%, Ta: 3% to 15%, Co: 0% to 15%, Mo: 0% to 5%, Ti: 0% to 5.0%, C: 0% to 0.10%, B: 0% to 0.05%, and a remainder including Ni and impurities.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0014] FIG. 1 is a flowchart of a Ni alloy member manufacturing method according to a first embodiment of the present invention.

[0015] FIG. 2 shows an electron micrograph of a Ni alloy member according to the first embodiment of the present invention.

[0016] FIG. 3 is a flowchart of a Ni alloy member manufacturing method according to a second embodiment of the present invention.

[0017] FIG. 4 is a view for describing an observation direction of a sample after a heat treatment test.

[0018] FIG. 5 is an appearance observation photograph after a heat treatment under a condition A.

[0019] FIG. 6 is an appearance observation photograph after the heat treatment under a condition B.

[0020] FIG. 7 is an appearance observation photograph after the heat treatment under a condition C.

DESCRIPTION OF EMBODIMENTS

[0021] As a result of intensive studies conducted by the present inventors, it was found that in a Ni-based alloy having a chemical composition with which a phase (for example, a NiAl phase) can be precipitated in an amount of 50 volume % or more, recrystallization can be significantly reduced by removing a strain that causes the recrystallization in a predetermined temperature range and then dissolving the phase without cooling. The present invention has been made based on the above-described findings. The Ni-based alloy is, for example, an alloy containing 50 mass % or more of Ni and one or more kinds of alloys selected from the group consisting of Cr, W, Al, Ta, Co, Mo, Ti, C, and B.

First Embodiment

[0022] Hereinafter, a Ni-based alloy member manufacturing method S100 according to a first embodiment will be described with reference to FIG. 1. FIG. 1 is a flowchart of the Ni-based alloy member manufacturing method S100 according to the embodiment. The Ni-based alloy member manufacturing method S100 includes a casting step S10, a first strain removal heat treatment step S11, a solution heat treatment step S13, and an aging heat treatment step S14. Hereinafter, each step will be described. In the present specification, a numerical range represented using to refers to a range including numerical values before and after to as a lower limit and an upper limit. In the present specification, a temperature such as a heating temperature refers to a temperature of a surface of a Ni-based alloy cast material.

Casting Step S10

[0023] In the casting step S10, the Ni-based alloy cast material in which a phase can be precipitated in an amount of 50 volume % or more in a phase in the aging heat treatment step S14 is cast. A casting method is not particularly limited. The Ni-based alloy cast material can be manufactured, for example, by a lost-wax method. Since an active metal such as Al is contained, it is preferable to perform dissolution and casting in a vacuum. For example, the Ni-based alloy cast material is obtained by dissolving components constituting a Ni-based alloy, and injecting the obtained molten metal into a gap formed by a mold, a core, and the like.

[0024] A chemical composition of the Ni-based alloy cast material is not particularly limited as long as the phase can be precipitated in an amount of 50 volume % or more in the phase in the aging heat treatment step S14. Such a Ni-based alloy cast material is, for example, a Ni-based alloy having a chemical composition including, by mass %, Cr: 5% to 15%, W: 3% to 10%, Al: 3.0% to 7.0%, Ta: 3% to 15%, Co: 0% to 15%, Mo: 0% to 5%, Ti: 0% to 5.0%, C: 0% to 0.10%, B: 0% to 0.05%, and a remainder including Ni and impurities.

Cr: 5% to 15%

[0025] Cr is an element that generates M23C6 precipitates that improves strength at a high temperature. In addition, inclusion of Cr also improves oxidation resistance in a high temperature environment. In order to obtain the above-described effect, a Cr content is preferably 5% or more. The Cr content is preferably 8% or more. In a case where the Cr content is more than 15% m, precipitation of a harmful phase is caused, which leads to a decrease in strength and a decrease in ductility of a Ni-based alloy member. Therefore, the Cr content is preferably 15% or less.

W: 3% to 10%

[0026] W is an element that dissolves in the phase, which is a matrix of the Ni-based alloy, and contributes to an improvement of the strength of the Ni-based alloy member by solid solution strengthening. In order to obtain the above-described effect, a W content is preferably 3% or more. The W content is more preferably 4% or more. In a case where the W content is more than 10%, the precipitation of a harmful phase is caused, which leads to a decrease in strength and a decrease in ductility of the Ni-based alloy member. Therefore, the W content is preferably 10% or less. The W content is more preferably 8% or less.

Al: 3.0% to 7.0%

[0027] Al is an element that generates the phase that improves the strength of the Ni-based alloy member at a high temperature. Al is also an element having an effect of improving oxidation resistance and corrosion resistance at a high temperature. In order to obtain the above-described effect, an Al content is preferably 3.0% or more. The Al content is more preferably 3.5% or more. In a case where the Al content is more than 7.0%, weldability of the Ni-based alloy member decreases, and there is a concern that cracks occur during manufacturing or repair of the Ni-based alloy member. Therefore, the Al content is preferably 7.0% or less. The Al content is more preferably 5.5% or less.

Ta: 3% to 15%

[0028] Ta is an element that generates the phase which improves the strength of the Ni-based alloy member at a high temperature. In order to obtain the above-described effect, a Ta content is preferably 3% or more. The Ta content is more preferably 4% or more. In a case where the Ta content is more than 15%, MC carbides that are stable at a high temperature are generated within crystal grains, and M23C6 that contributes to the strength of the Ni-based alloy member at a high temperature is less likely to be generated. Therefore, the Ta content is preferably 15% or less. The Ta content is more preferably 11% or less.

Co: 0% to 15%

[0029] Co is an element having an effect of improving a solid-solution temperature of the phase that improves the strength of the Ni-based alloy member at a high temperature. Co is also an element that contributes to stabilization of the phase at a high temperature. In a case where the Co content is more than 15%, precipitation of a harmful phase in the Ni-based alloy member is caused, which leads to a decrease in strength and a decrease in ductility of the Ni-based alloy member. Therefore, the Co content is preferably 15% or less. The Co content is more preferably 10% or less. Since Co may not be contained, a lower limit of the Co content is 0%.

Mo: 0% to 5%

[0030] Mo is an element that dissolves in the phase, which is the matrix of the Ni-based alloy, and contributes to the improvement of the strength of the Ni-based alloy member by solid solution strengthening. In a case where a Mo content is more than 5%, precipitation of a harmful phase is caused, which leads to a decrease in strength and a decrease in ductility of the Ni-based alloy member. Therefore, the Mo content is preferably 5% or less. The Mo content is more preferably 3% or less. Since Mo may not be contained, a lower limit of the Mo content is 0%.

Ti: 0% to 5.0%

[0031] Ti is an element that generates the phase that improves the strength of the Ni-based alloy member at a high temperature. Ti is also an element that contributes to an improvement of oxidation resistance and corrosion resistance of the Ni-based alloy member at a high temperature. When a Ti content is more than 5%, weldability of the Ni-based alloy member decreases, and there is a concern that cracks occur in the Ni-based alloy member during manufacturing or repair. Therefore, the Ti content is preferably 5.0% or less. The Ti content is more preferably 3.5% or less. Since Ti may not be contained, a lower limit of the Ti content is 0%.

C: 0% to 0.10%

[0032] C is an element constituting M23C6 precipitates that contribute to the improvement of the strength of the Ni-based alloy member at a high temperature. In a case where a C content is more than 0.10%, the number of MC carbides precipitated in the crystal grains increases, and there is a concern that intragranular strength increases and the ductility decreases. Therefore, the C content is preferably 0.10% or less. Since C may not be contained, a lower limit of the C content is 0%.

B: 0% to 0.05%

[0033] B is an element having an effect of improving high-temperature creep strength of the Ni-based alloy member by strengthening grain boundaries when present at the grain boundaries. In a case where a B content is more than 0.05%, borides are generated, and there is a concern that the ductility of the Ni-based alloy member decreases. Therefore, the B content is preferably 0.05% or less. Since B may not be contained, a lower limit of the B content is 0%.

Remainder: Ni and Impurities

[0034] The remainder of the Ni-based alloy cast material of the present disclosure includes Ni and impurities. Here, the impurities are components that are mixed in the raw materials or during manufacturing steps when the Ni-based alloy cast material is cast. The impurities are allowed within a range in which the effects of the Ni-based alloy member of the present disclosure can be obtained.

[0035] The chemical composition of the Ni-based alloy cast material can be analyzed by using a known method. For example, the chemical composition of the Ni-based alloy cast material can be analyzed by an inductively coupled plasma mass spectrometry.

First Strain Removal Heat Treatment Step

[0036] In the first strain removal heat treatment step S11, when the solid-solution temperature of the phase is denoted by Ts C., the Ni-based alloy cast material after the casting step S10 is heated in a first strain removal temperature range of Ts0.90 C. or higher and Ts C. or lower for one hour or longer. It is possible to remove internal strain (internal strain accumulated due to a difference in thermal expansion between the Ni-based alloy cast material, and the mold and the core during cooling after casting) formed inside the Ni-based alloy cast material formed in the casting step S10. The solid-solution temperature of the phase refers to a temperature at which the phase is completely dissolved in a matrix phase. The solid-solution temperature of the phase can be obtained by performing calculation using thermodynamic calculation software (for example, JMatPro manufactured by Sente Software Ltd.) based on the chemical composition.

[0037] In a case where a first strain removal temperature is lower than Ts0.9 C., the temperature is low and a volume percentage of the phase becomes excessively high, so that the internal strain of the Ni-based alloy member cannot be sufficiently removed. Therefore, the first strain removal temperature is Ts0.9 C. or higher. In a case where the first strain removal temperature exceeds Ts C., the temperature is high, and the phase is (disappeared) dissolved, so that recrystallized grains are likely to be generated. Therefore, the first strain removal temperature is Ts C. or lower.

[0038] In the first strain removal heat treatment step S11, a heating time in the first strain removal temperature range is one hour or longer. In a case where the heating time is shorter than one hour, the internal strain of the Ni-based alloy cast material cannot be sufficiently removed.

[0039] A temperature rising rate from room temperature (5 C. to 35 C.) to the first strain removal temperature range is preferably 50 C./min or slower. In a case where the Ni-based alloy cast material is rapidly heated, there is a possibility that the temperature rises to the first strain removal temperature range or higher. In a case where the temperature exceeds the first strain removal temperature range, there is a possibility that recrystallized grains are generated. Therefore, the temperature rising rate from room temperature to the first strain removal temperature range is 50 C./min or slower.

Solution Heat Treatment Step

[0040] In the solution heat treatment step S13, when a melting point of the phase is denoted by Tm C., the Ni-based alloy cast material after the first strain removal heat treatment step S11 is heated from the first strain removal temperature range to a solution heat treatment temperature range of higher than Ts+t1 C. and Tm C. or lower, and the temperature is held for two hours or longer in the solution heat treatment temperature range. t1 is 10 C. or lower. t1 is preferably 1 C. or higher. t1 is more preferably 5 C. or higher. In the solution heat treatment step S13, the Ni-based alloy cast material is heated from the first strain removal temperature range to the solution heat treatment temperature range without being cooled. As a result, the phase can be dissolved without generating strain caused by a difference in thermal expansion between the phase and the phase. Therefore, the recrystallized grains can be significantly reduced. The melting point Tm of the phase can be obtained by performing calculation using thermodynamic calculation software (for example, JMatPro manufactured by Sente Software Ltd.) based on the chemical composition.

[0041] In addition, in the Ni-based alloy cast material after casting, the phase is precipitated in a coarse state, and uneven distribution of chemical components occurs. In the solution heat treatment step S13, the phase is dissolved, thereby achieving homogenization. In the solution heat treatment step S13, the phase preferably occupies 100%, but may contain another phase as long as the strength at a high temperature is not reduced. In a case where the Ni-based alloy cast material after completing the first strain removal heat treatment step S11 and the solution heat treatment step S13 is observed with a microscope, a single phase exhibiting a dendritic pattern with no recrystallized grains can be confirmed.

[0042] In a case where the solution heat treatment temperature is Ts+t1 C. or lower, there may be cases where the phase cannot be sufficiently dissolved. Therefore, the solution heat treatment temperature is higher than Ts+t1 C. t1 is 10 C. or lower. t1 is preferably 1 C. or higher. t1 is more preferably 5 C. or higher. In a case where the solution heat treatment temperature exceeds the melting point Tm C. of the phase, the phase is dissolved. Therefore, the solution heat treatment temperature is Tm C. or lower.

[0043] A temperature rising rate from the first strain removal temperature range to the solution heat treatment temperature range is preferably 50 C./min or slower. In a case where the Ni-based alloy cast material is rapidly heated, there is a possibility that the temperature rises to the solution heat treatment temperature range or higher. In a case where the temperature exceeds the solution heat treatment temperature range, there is a possibility that the phase is dissolved. Therefore, the temperature rising rate from the first strain removal temperature range to the solution heat treatment temperature range is 50 C./min or slower.

[0044] After the temperature is raised to the solution heat treatment temperature range, the temperature is held for a certain period of time in the solution heat treatment temperature range. In a case where the time for holding the temperature is shorter than two hours, there is a possibility that the phase is not sufficiently dissolved. Therefore, in the solution heat treatment step S13, the time for holding the temperature is two hours or longer.

[0045] After holding the temperature in the solution heat treatment temperature range, the Ni-based alloy cast material is cooled from the solution heat treatment temperature range to room temperature. A cooling method is, for example, gas cooling. The volume percentage of the phase, which is a strengthening phase, is adjusted to a target volume percentage in the subsequent aging heat treatment step S14. Since there is a concern that an unexpected phase is precipitated during cooling after holding the temperature in the solution heat treatment temperature range, it is preferable to set a cooling rate to be as fast as possible. Therefore, the cooling rate is preferably 10 C./min or faster.

Aging Heat Treatment Step

[0046] By performing the aging heat treatment step S14 on the Ni-based alloy cast material after the solution heat treatment step S13, the phase can be precipitated, and the Ni-based alloy member of the present disclosure can be obtained. In the aging heat treatment step S14, it is preferable to heat the Ni-based alloy cast material after the solution heat treatment step S13 in an aging heat treatment temperature range of 850 C. or higher and 870 C. or lower for two hours to 20 hours. As a result, precipitation of the phase in an amount of 50 volume % or more in the phase is facilitated.

[0047] A temperature range (aging heat treatment temperature range) at which the Ni-based alloy cast material is aged after the solution heat treatment step S13 is preferably 850 C. or higher and 870 C. or lower. In this aging heat treatment temperature range, the volume percentage of the phase precipitated in the phase can be easily adjusted to 50 volume % or more, which is preferable.

[0048] A time for heating the Ni-based alloy cast material after the solution heat treatment step S13 in the aging heat treatment temperature range is preferably two hours to 20 hours. For this heating time, the volume percentage of the phase precipitated in the phase can be easily adjusted to 50 volume % or more, which is preferable.

[0049] The volume percentages of the phase and the phase after the aging heat treatment step S14 can be evaluated by observing a cross section of the Ni-based alloy member with a scanning electron microscope (SEM). FIG. 2 shows an electron micrograph obtained by the SEM observation of the Ni-based alloy member after the aging heat treatment step S14. As shown in FIG. 2, in the Ni-based alloy member of the present disclosure, rectangular phases and phases in a lattice pattern in gaps between the rectangular phases are observed. For example, an area percentage of the phase can be evaluated from the obtained observation image by using image processing software. The volume percentage of the phase can be set as the area percentage of the phase obtained from the electron micrographs of the cross section.

[0050] As described above, according to the Ni-based alloy member manufacturing method according to the present embodiment, it is possible to suppress recrystallized grains.

Second Embodiment

[0051] Next, a Ni-based alloy member manufacturing method S100B according to a second embodiment will be described with reference to FIG. 3. FIG. 3 is a flowchart of the Ni-based alloy member manufacturing method S100B according to the embodiment. The Ni-based alloy member manufacturing method S100B includes a casting step S10, a first strain removal heat treatment step S11, a second strain removal heat treatment step S12, a solution heat treatment step S13, and an aging heat treatment step S14. Hereinafter, each step will be described.

Casting Step S10

[0052] In the casting step S10, the Ni-based alloy cast material in which a phase can be precipitated in an amount of 50 volume % or more in a phase in the aging heat treatment step S14 is cast. A casting method is not particularly limited. The Ni-based alloy cast material can be manufactured, for example, by a lost-wax method. Since an active metal such as Al is contained, it is preferable to perform dissolution and casting in a vacuum. For example, the Ni-based alloy cast material is obtained by dissolving components constituting a Ni-based alloy, and injecting the obtained molten metal into a gap formed by a mold, a core, and the like.

[0053] A chemical composition of the Ni-based alloy cast material is not particularly limited as long as the phase can be precipitated in an amount of 50 volume % or more in the phase in the aging heat treatment step S14. Such a Ni-based alloy cast material is, for example, a Ni-based alloy having a chemical composition including, by mass %, Cr: 5% to 15%, W: 3% to 10%, Al: 3.0% to 7.0%, Ta: 3% to 15%, Co: 0% to 15%, Mo: 0% to 5%, Ti: 0% to 5.0%, C: 0% to 0.10%, B: 0% to 0.05%, and a remainder including Ni and impurities.

First Strain Removal Heat Treatment Step

[0054] In the first strain removal heat treatment step S11, when the solid-solution temperature of the phase is denoted by Ts C., the Ni-based alloy cast material after the casting step S10 is heated in a first strain removal temperature range of Ts0.90 C. or higher and Ts C. or lower for one hour or longer. It is possible to remove internal strain (internal strain accumulated due to a difference in thermal expansion between the Ni-based alloy cast material, and the mold and the core during cooling after casting) formed inside the Ni-based alloy cast material formed in the casting step S10. The solid-solution temperature of the phase refers to a temperature at which the phase is completely dissolved in a matrix phase. The solid-solution temperature of the phase can be obtained by performing calculation using thermodynamic calculation software (for example, JMatPro manufactured by Sente Software Ltd.) based on the chemical composition.

[0055] In a case where a first strain removal temperature is lower than Ts0.9 C., the temperature is low and a volume percentage of the phase becomes excessively high, so that the internal strain of the Ni-based alloy member cannot be sufficiently removed. Therefore, the first strain removal temperature is Ts0.9 C. or higher. In a case where the first strain removal temperature exceeds Ts C., the temperature is high, and the phase is (disappeared) dissolved, so that recrystallized grains are likely to be generated. Therefore, the first strain removal temperature is Ts C. or lower.

[0056] In the first strain removal heat treatment step S11, a heating time in the first strain removal temperature range is one hour or longer. In a case where the heating time is shorter than one hour, the internal strain of the Ni-based alloy cast material cannot be sufficiently removed.

[0057] A temperature rising rate from room temperature (5 C. to 35 C.) to the first strain removal temperature range is preferably 50 C./min or slower. In a case where the Ni-based alloy cast material is rapidly heated, there is a possibility that the temperature rises to the first strain removal temperature range or higher. In a case where the temperature exceeds the first strain removal temperature range, there is a possibility that recrystallized grains are generated. Therefore, the temperature rising rate from room temperature to the first strain removal temperature range is 50 C./min or slower.

Second Strain Removal Heat Treatment Step

[0058] In the second strain removal heat treatment step S12, when a temperature range of higher than Ts C. and Tm C. or lower, and lower than a solution heat treatment temperature range by t1 C. is set as a second strain removal temperature range, the Ni-based alloy cast material after the first strain removal heat treatment step S11 is heated from the first strain removal temperature range to the second strain removal temperature range. Thereafter, the Ni-based alloy cast material is held at a temperature in the second strain removal temperature range for one hour or longer. In the second strain removal heat treatment step, the Ni-based alloy cast material is heated from the first strain removal temperature range to the second strain removal temperature range without being cooled. As a result, it is possible to remove internal strain remaining after the first strain removal heat treatment step S11.

[0059] In the second strain removal heat treatment step S12, a heating time in the second strain removal temperature range is one hour or longer. In a case where the heating time is shorter than one hour, there may be cases where the internal strain of the Ni-based alloy cast material cannot be sufficiently removed.

[0060] A temperature rising rate from the first strain removal temperature range to the second strain removal temperature range is preferably 50 C./min or slower. In a case where the Ni-based alloy cast material is rapidly heated, there is a possibility that the temperature rises to the second strain removal temperature range or higher. In a case where the temperature exceeds the second strain removal temperature range, there is a possibility that the strain cannot be sufficiently removed. Therefore, the temperature rising rate from the first strain removal temperature range to the second strain removal temperature range is preferably 50 C./min or slower.

Solution Heat Treatment Step

[0061] In the solution heat treatment step S13, when a melting point of the phase is denoted by Tm C., the Ni-based alloy cast material after the second strain removal heat treatment step S12 is heated from the second strain removal temperature range to a solution heat treatment temperature range, and the temperature is held for two hours or longer in the solution heat treatment temperature range. In the solution heat treatment step S13, the Ni-based alloy cast material is heated from the second strain removal temperature range to the solution heat treatment temperature range without being cooled. As a result, the phase can be dissolved without generating strain caused by a difference in thermal expansion between the phase and the phase. Therefore, the recrystallized grains can be significantly reduced. The melting point Tm of the phase can be obtained by performing calculation using thermodynamic calculation software (for example, JMatPro manufactured by Sente Software Ltd.) based on the chemical composition.

[0062] In addition, in the Ni-based alloy cast material after casting, the phase is precipitated in a coarse state, and uneven distribution of chemical components occurs. In the solution heat treatment step S13, the phase is dissolved, thereby achieving homogenization. In the solution heat treatment step S13, the phase preferably occupies 100%, but may contain another phase as long as the strength at a high temperature is not reduced. In a case where the Ni-based alloy cast material after completing the first strain removal heat treatment step S11, the second strain removal heat treatment step S12, and the solution heat treatment step S13 is observed with a microscope, a single phase exhibiting a dendritic pattern with no recrystallized grains can be confirmed.

[0063] In a case where the solution heat treatment temperature is Ts+t1 C. or lower, there may be cases where the phase cannot be sufficiently dissolved. Therefore, the solution heat treatment temperature is higher than Ts+t1 C. Here, t1 is 10 C. or lower. t1 is preferably 1 C. or higher. t1 is more preferably 5 C. or higher. In a case where the solution heat treatment temperature exceeds the melting point Tm C. of the phase, the phase is dissolved. Therefore, the solution heat treatment temperature is Tm C. or lower.

[0064] A temperature rising rate from the second strain removal temperature range to the solution heat treatment temperature range is preferably 50 C./min or slower. In a case where the Ni-based alloy cast material is rapidly heated, there is a possibility that the temperature rises to the solution heat treatment temperature range or higher. In a case where the temperature exceeds the solution heat treatment temperature range, there is a possibility that the phase is dissolved. Therefore, the temperature rising rate from the second strain removal temperature range to the solution heat treatment temperature range is 50 C./min or slower.

[0065] After the temperature is raised to the solution heat treatment temperature range, the temperature is held for a certain period of time in the solution heat treatment temperature range. In a case where the time for holding the temperature is shorter than two hours, there is a possibility that the phase is not sufficiently dissolved. Therefore, in the solution heat treatment step S13, the time for holding the temperature is two hours or longer.

[0066] After holding the temperature in the solution heat treatment temperature range, the Ni-based alloy cast material is cooled from the solution heat treatment temperature range to room temperature. A cooling method is, for example, gas cooling. The volume percentage of the phase, which is a strengthening phase, is adjusted to a target volume percentage in the subsequent aging heat treatment step S14. Since there is a concern that an unexpected phase is precipitated during cooling after holding the temperature in the solution heat treatment temperature range, it is preferable to set a cooling rate to be as fast as possible. Therefore, the cooling rate is preferably 10 C./min or faster.

Aging Heat Treatment Step

[0067] By performing the aging heat treatment step S14 on the Ni-based alloy cast material after the solution heat treatment step S13, the phase can be precipitated, and the Ni-based alloy member of the present disclosure can be obtained. In the aging heat treatment step S14, it is preferable to heat the Ni-based alloy cast material after the solution heat treatment step S13 in an aging heat treatment temperature range of 850 C. or higher and 870 C. or lower for two hours to 20 hours. As a result, precipitation of the phase in an amount of 50 volume % or more in the phase is facilitated.

[0068] A temperature range (aging heat treatment temperature range) at which the Ni-based alloy cast material is aged after the solution heat treatment step S13 is preferably 850 C. or higher and 870 C. or lower. In this aging heat treatment temperature range, the volume percentage of the phase precipitated in the phase can be easily adjusted to 50 volume % or more, which is preferable.

[0069] A time for heating the Ni-based alloy cast material after the solution heat treatment step S13 in the aging heat treatment temperature range is preferably two hours to 20 hours. For this heating time, the volume percentage of the phase precipitated in the phase can be easily adjusted to 50 volume % or more, which is preferable.

[0070] As described above, according to the Ni-based alloy member manufacturing method according to the second embodiment, it is possible to suppress recrystallized grains. By the second strain removal heat treatment step S12, the internal strain remaining after the first strain removal heat treatment step S11 can be removed, and recrystallization can be further suppressed.

[0071] The technical scope of the present invention is not limited to the above-mentioned embodiment, and various changes can be made within a range not departing from the scope of the present invention. In addition, the components of the above-mentioned embodiment can be appropriately replaced with well-known components within a range not departing from the scope of the present invention.

EXAMPLES

[0072] Next, examples of the present invention will be described, but conditions in the examples are examples of one condition adopted to confirm the feasibility and effects of the present invention, and the present invention is not limited to the examples of one condition. The present invention can adopt various conditions without departing from the scope of the present invention as long as the gist of the present invention is achieved.

Example 1

[0073] A Ni-based alloy cast material having a chemical composition including, by mass %, Cr: 8%, W: 8%, Al: 5.5%, Ta: 11%, and a remainder including Ni and impurities was cast. A solid-solution temperature Ts of a phase obtained by performing thermodynamic calculation from the chemical composition was 1,305 C., Ts0.9 C. was 1,175 C., and a melting point Tm of a phase was 1,336 C.

[0074] The obtained Ni-based alloy cast material was heated to a first strain removal temperature range of 1,175 C. or higher and 1,305 C. or lower at a temperature rising rate of 50 C./min or slower, and subjected to a first strain removal heat treatment in the first strain removal temperature range for one hour or longer. Thereafter, without cooling, the temperature was raised from the first strain removal temperature range to a solution heat treatment temperature range of higher than 1,305 C. and 1,336 C. or lower at a temperature rising rate of 50 C./min or slower. After the temperature was raised, the temperature was held in the solution heat treatment temperature range for two hours, and then cooling was performed at 10 C./min. In a case where the Ni-based alloy cast material after the cooling was observed with a microscope, a single phase exhibiting a dendritic pattern with no recrystallized grains could be confirmed.

[0075] After the cooling, the Ni-based alloy cast material was heated in an aging heat treatment temperature range of 850 C. to 870 C. for two hours to 20 hours, thereby obtaining a Ni-based alloy member of Example 1.

Example 2

[0076] A Ni-based alloy cast material having a chemical composition including, by mass %, Cr: 15%, W: 4%, Al: 3.5%, Ta: 4%, Co: 10%, Mo: 3%, Ti: 3.5%, C: 0% to 0.10%, B: 0% to 0.03%, and a remainder including Ni and impurities was cast. A solid-solution temperature Ts of a phase obtained by performing thermodynamic calculation from the chemical composition was 1,136 C., Ts0.9 C. was 1,022 C., and a melting point Tm of a phase was 1,274 C.

[0077] The obtained Ni-based alloy cast material was heated to a first strain removal temperature range of 1,022 C. or higher and 1,136 C. or lower at a temperature rising rate of 50 C./min or slower, and subjected to a first strain removal heat treatment in the first strain removal temperature range for one hour or longer. Thereafter, without cooling, the temperature was raised from the first strain removal temperature range to a solution heat treatment temperature range of higher than 1,136 C. and 1,274 C. or lower at a temperature rising rate of 50 C./min or slower. After the temperature was raised, the temperature was held in the solution heat treatment temperature range for two hours, and then cooling was performed at 10 C./min. In a case where the Ni-based alloy cast material after the cooling was observed with a microscope, a single phase exhibiting a dendritic pattern with no recrystallized grains could be confirmed.

[0078] After the cooling, the Ni-based alloy cast material was heated in an aging heat treatment temperature range of 850 C. to 870 C. for two hours to 20 hours, thereby obtaining a Ni-based alloy member of Example 2.

Example 3

[0079] A Ni-based alloy cast material having a chemical composition including, by mass %, Cr: 8%, W: 8%, Al: 5.5%, Ta: 11%, and a remainder including Ni and impurities was cast. A solid-solution temperature Ts of a phase obtained by performing thermodynamic calculation from the chemical composition was 1,305 C., Ts0.9 C. was 1,175 C., and a melting point Tm of a phase was 1,336 C.

[0080] The obtained Ni-based alloy cast material was heated to a first strain removal temperature range of 1,175 C. or higher and 1,305 C. or lower at a temperature rising rate of 50 C./min or slower, and subjected to a first strain removal heat treatment in the first strain removal temperature range for one hour or longer. Thereafter, without cooling, the temperature was raised from the first strain removal temperature range to a second strain removal temperature range (a temperature of 1,305 C. or higher and 1,336 C. or lower, and lower than solution heat treatment temperature range by 10 C.) at a temperature rising rate of 50 C./min or slower, and a second strain removal heat treatment was performed for one hour or longer. Next, the temperature was raised from the second strain removal temperature range to the solution heat treatment temperature range (a temperature range of higher than 1,305 C. and 1,336 C. or lower, and higher than the second strain removal temperature range by 10 C.) at a temperature rising rate of 50 C./min or slower. After the temperature was raised, the temperature was held in the solution heat treatment temperature range for two hours, and then cooling was performed at 10 C./min. In a case where the Ni-based alloy cast material after the cooling was observed with a microscope, a single phase exhibiting a dendritic pattern with no recrystallized grains could be confirmed.

[0081] After the cooling, the Ni-based alloy cast material was heated in an aging heat treatment temperature range of 850 C. to 870 C. for two hours to 20 hours, thereby obtaining a Ni-based alloy member of Example 3.

Volume Percentage of Phase

[0082] From the thermodynamic calculation, a volume percentage of the phase of Example 1 was 70%, a volume percentage of the phase of Example 2 was 51%, and a volume percentage of the phase of Example 3 was 70%. In addition, in all of Example 1, Example 2, and Example 3, no recrystallized grains were observed.

Pre-Strain Imparting Experiment

[0083] Bending deformation was applied to simulate internal strain that occurs during casting. A chemical composition of test piece subjected to the bending deformation was the same as the chemical composition of Example 1. After applying bending deformation to the sample, the sample was heated under each of conditions A, B, and C, and sizes of recrystallized grains were evaluated by revealing a metallurgical structure by etching and taking appearance observation photographs. The other conditions such as temperature raising, which are not described above, were the same as those in Example 1.

[0084] Condition A: First strain removal heat treatment step (heating at Ts0.9 C. or higher and Ts C. or lower for one hour or longer), second strain removal heat treatment step (heating at a temperature of higher than Ts C. and Tm C. or lower, and lower than a solution heat treatment step by 10 C. for one hour or longer), and solution heat treatment step (heating at higher than Ts+10 C. and Ts C. or lower for two hours or longer).

[0085] Condition B: Heat treatment step in a first strain removal heat treatment temperature range or lower (heating at lower than Ts0.9 C. for one hour or longer) and solution heat treatment step (heating at higher than Ts C. and Tm C. or lower for two hours or longer).

[0086] Condition C: Solution heat treatment step (heating at higher than Ts C. and Tm C. or lower for two hours or longer).

[0087] FIG. 4 is a view for describing an observation direction of the sample after the heat treatment. Appearance observation photographs of the samples after the heat treatments were taken in a direction of an arrow in FIG. 4. The obtained photographs are shown in FIGS. 5 to 7. The metallurgical structure was revealed by etching in each photograph. FIG. 5 is an appearance observation photograph after the heat treatment under the condition A. FIG. 6 is an appearance observation photograph after the heat treatment under the condition B. FIG. 7 is an appearance observation photograph after the heat treatment under the condition C. As shown in FIG. 5, in the sample that was subjected to the heat treatment satisfying temperature conditions of the present disclosure, no recrystallized grains were generated. As shown in FIG. 6, under the condition B in which the heat treatment was performed in the first strain removal heat treatment temperature range or lower, a recrystallized structure was generated at a bent portion. As shown in FIG. 7, under the condition C in which the first strain removal heat treatment was not performed, a noticeable recrystallized structure was generated at the bent portion. From the above results, it was confirmed that, by using the Ni-based alloy member manufacturing method of the present disclosure, the generation of recrystallized grains can be significantly reduced even in a case where the phase occupies 50 volume % or more.

Supplementary Notes

[0088] The Ni-based alloy member manufacturing method described in the above embodiments can be understood as follows.

[0089] (1) A Ni-based alloy member manufacturing method according to a first aspect of the present disclosure includes: a casting step S10; a first strain removal heat treatment step S11; a solution heat treatment step S13; and an aging heat treatment step S14, in which, in the casting step S10, a Ni-based alloy cast material having a chemical composition in which a phase is precipitable in an amount of 50 volume % or more in a phase in the aging heat treatment step S14 is cast, in the first strain removal heat treatment step S11, when a solid-solution temperature of the phase is denoted by Ts C., the Ni-based alloy cast material after the casting step S10 is heated in a strain removal temperature range of Ts0.90 C. or higher and Ts C. or lower for one hour or longer, in the solution heat treatment step S13, when a melting point of the phase is denoted by Tm C., the Ni-based alloy cast material after the strain removal heat treatment step S11 is heated from the strain removal temperature range to a solution heat treatment temperature range of higher than Ts+t1 C. and Tm C. or lower, and a temperature is held for two hours or longer in the solution heat treatment temperature range, and t1 is 10 C. or lower.

[0090] In this manner, the generation of recrystallized grains in the solution heat treatment step can be suppressed.

[0091] (2) A Ni-based alloy member manufacturing method according to a second aspect of the present disclosure is the Ni-based alloy member manufacturing method according to the first aspect further including: a second strain removal heat treatment step S12 between the first strain removal heat treatment step S11 and the solution heat treatment step S13, in which when a temperature range of higher than Ts C. and Tm C. or lower, and lower than the solution heat treatment temperature range by t1 C. is set as a second strain removal temperature range, in the second strain removal heat treatment step S12, the Ni-based alloy cast material after the first strain removal heat treatment step S11 is heated from the first strain removal temperature range to the second strain removal temperature range, and the temperature is held for one hour or longer in the second strain removal temperature range, and in the solution heat treatment step S13, the Ni-based alloy cast material after the second strain removal heat treatment step S12 is heated from the second strain removal temperature range to the solution heat treatment temperature range, and the temperature is held for two hours or longer in the solution heat treatment temperature range.

[0092] By providing the second strain removal heat treatment step, the strain can be further removed.

[0093] (3) A Ni-based alloy member manufacturing method according to a third aspect of the present disclosure is the Ni-based alloy member manufacturing method according to the first or second aspect, in which, in the aging heat treatment step S14, the Ni-based alloy cast material after the solution heat treatment step S13 is heated in an aging heat treatment temperature range of 850 C. or higher and 870 C. or lower for two hours to 20 hours.

[0094] In this manner, a volume percentage of the phase can be adjusted.

[0095] (4) A Ni-based alloy member manufacturing method according to a fourth aspect of the present disclosure is the Ni-based alloy member manufacturing method according to any one of the first to third aspects, in which, in the first strain removal heat treatment step S11, a temperature rising rate from room temperature to the first strain removal temperature range is 50 C./min or slower.

[0096] In this manner, the generation of recrystallized grains in the solution heat treatment step can be suppressed.

[0097] (5) A Ni-based alloy member manufacturing method according to a fifth aspect of the present disclosure is the Ni-based alloy member manufacturing method according to any one of the first to fourth aspects, in which, in the solution heat treatment step S13, a temperature rising rate from the strain removal temperature range to the solution heat treatment temperature range is 50 C./min or slower.

[0098] In this way, it is possible to suppress the dissolution of the phase in the solution heat treatment step.

[0099] (6) A Ni-based alloy member manufacturing method according to a sixth aspect of the present disclosure is the Ni-based alloy member manufacturing method according to any one of the first to fifth aspects, in which, in the solution heat treatment step S13, after holding the temperature for two hours or longer, cooling from the solution heat treatment temperature range to room temperature is performed at a cooling rate of 10 C./min or faster.

[0100] In this manner, the precipitation of an unexpected phase during cooling can be suppressed.

[0101] (7) A Ni-based alloy member manufacturing method according to a seventh aspect of the present disclosure is the Ni-based alloy member manufacturing method according to any one of the first to sixth aspects, in which, a chemical composition of the Ni-based alloy cast material includes, by mass %, Cr: 5% to 15%, W: 3% to 10%, Al: 3.0% to 7.0%, Ta: 3% to 15%, Co: 0% to 15%, Mo: 0% to 5%, Ti: 0% to 5.0%, C: 0% to 0.10%, B: 0% to 0.05%, and a remainder including Ni and impurities.

[0102] In this manner, precipitation of the phase in an amount of 50 volume % or more in the phase is facilitated.

Industrial Applicability

[0103] Since the recrystallized grains can be reduced by the Ni-based alloy member manufacturing method of the present disclosure, the Ni-based alloy member manufacturing method of the present disclosure is highly industrially applicable.

Reference Signs List

[0104] S100: Ni-based alloy member manufacturing method [0105] S10: casting step [0106] S11: first strain removal heat treatment step [0107] S12: second strain removal heat treatment step [0108] S13: solution heat treatment step [0109] S14: aging heat treatment step