METHOD FOR PRODUCING GRAMOPHONE RECORDS BY INJECTION MOULDING

Abstract

A method for producing gramophone records by injection moulding, comprises the steps of heating polymeric material to liquefy said material, supplying liquid polymeric material under pressure from a feed zone to a space between two mould parts via a nozzle. The liquid polymeric material is passed through a single passage located in one of the mould parts and forced under pressure through the nozzle into said space. Polyethylene terephthalate isophthalic acid modified copolymer is used as said polymeric material.

Claims

1. Gramophone records, comprising polymeric material injected into a space with an injection nozzle; wherein said injection nozzle is provided with a nozzle piece and an inlet opening and a pouring channel extending between said inlet opening and said nozzle piece such that the polymeric material is provided with a single stream from the inlet opening into the space and does not split into sub-streams, and wherein said polymeric material is supplied in a direction perpendicular to the moulding surfaces of the mould parts; and wherein said polymeric material consists mainly of a polyethylene terephthalate isophthalic acid modified copolymer; and wherein the amount of monopolymer isophthalic acid in the polyethylene terephthalate isophthalic acid modified copolymer is between 1.5 and 2.5%.

2. The gramophone records according to claim 1, further comprising a label printed directly on the polyethylene terephthalate isophthalic acid modified copolymer material by means of a UV-printer.

3. The gramophone records according to claim 1, wherein the polymeric material is supplied through a completely straight line along said pouring channel.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] The invention will be further elucidated below on the basis of drawings. These drawings show an embodiment of an injection moulding device for injection moulding a gramophone record according to the invention. In the drawings:

[0018] FIG. 1 is a diagrammatically representation of a mould of an injection moulding device for manufacturing a gramophone record according to the invention with closed injection channel;

[0019] FIG. 2 is the injection moulding device with open injection channel;

[0020] FIG. 3 is the injection nozzle of the injection moulding device with closed injection canal; and

[0021] FIG. 4 is the injection nozzle of the injection moulding device with open injection canal.

DETAILED DESCRIPTION OF THE DRAWINGS

[0022] An injection moulding device for injection moulding a gramophone record has a mould 1. In FIG. 1 this mould is schematically shown. The mould 1 is composed of two mould parts 3 and 5 with a space 7 in between. When the mould parts are in contact with each other the space 7 defines a mould cavity 8 (see FIG. 2) with the shape of a gramophone record. In the mould part 5 is an inset piece 9 for receiving an injection nozzle 11. Only the front part of the injection nozzle is shown. In the mould part 3 there is a central bush 15 in which an ejector 17 is displaceable for ejecting a remaining central injection piece which is not part of the gramophone record. A further ejector 19 is slidable over the bush for ejecting the gramophone record. Between the mould parts 3 and 5 there is a venting ring 21. The mould cavity 8 is bounded by two mirror parts 23 and 25 which are each provided with a pusher 27 and 29.

[0023] The injection nozzle 11 is shown in detail in FIG. 3. The injection nozzle is provided with a nozzle piece 31 and an inlet opening 33 being part of a feed zone. A pouring channel 35 is present in the injection nozzle 11 between the inlet opening and the nozzle piece. The pouring channel 35 is completely straight and is closed by a rotatable valve 37. This valve can be adjusted by an arm 39. In FIG. 4 the injection nozzle 11 is shown with the valve 37 in the open position.

[0024] When spraying a gramophone record, moulding material (usually in the form of a granulate) of PET, with some additives to give the moulding material the 20 optimum properties, is heated to a liquid state. The liquid material is injected under pressure into the space 7 between the mould parts 3 and 5 via a single passage 12, the material stream of the moulding material from the place where the moulding material melts into this space does not split into sub-streams which later come together again. The liquid material flows in one flow through the injection nozzle 11 into the space 7. While injecting the polymeric material into the space 7 between the two mould parts 3 and 5, the mould parts are at a distance of about 3 mm from each other, see FIG. 1. Immediately after injection these mould parts 3 and 5 are moved against each other creating a mould cavity 8 having a shape of a gramophone record, see FIG. 2.

[0025] The polymeric material 2 used for injection moulding is a polyethylene terephthalate isophthalic acid modified copolymer. Conventional additives for improvement can be added to this base polymeric material.

[0026] Although the present invention is elucidated above on the basis of the given drawings, it should be noted that this invention is not limited whatsoever to the embodiments shown in the drawings. The invention also extends to all embodiments deviating from the embodiments shown in the drawings within the scope of the invention defined by the appended claims.