WELD METAL, WELD JOINT, AND WELD STRUCTURAL OBJECT

Abstract

A weld metal including C: 0.030% to 1.000%, Si: from 0.03% to 0.50%, Mn: 4.1% to 30.0%, P: 0% to 0.050%, S: 0% to 0.050%, Cu: 0% to 5.0%, Ni: 1.0% to 30.0%, Cr: 0% to 20.0%, Mo: 0% to 10.0%, Nb: 0% to 1.000%, V: 0% to 1.00%, Co: 0% to 1.00%, Pb: 0% to 1.00%, Sn: 0% to 1.00%, W: 0% to 20.0%, Mg: 0% to 5.0%, Al: 0% to 0.100%, Ca: 0% to 5.0%, Ti: 0% to 0.100%, B: 0% to 0.5000%, REM: 0% to 0.500%, Zr: 0% to 0.500%, N: 0% to 0.5000%, O: 0.0010% to 0.1500%, and balance: Fe and impurities, wherein, Mn+Ni: 5.0% or more, and Nb+Ti+V+Al: 0.005% or more.

Claims

1. A weld metal having a chemical component consisting of, in % by mass with respect to a total mass of the weld metal, C: from 0.030% to 1.000%, Si: from 0.03% to 0.50%, Mn: from 4.1% to 30.0%, P: from 0% to 0.050%, S: from 0% to 0.050%, Cu: from 0% to 5.0%, Ni: from 1.0% to 30.0%, Cr: from 0% to 20.0%, Mo: from 0% to 10.0%, Nb: from 0% to 1.000%, V: from 0% to 1.00%, Co: from 0% to 1.00%, Pb: from 0% to 1.00%, Sn: from 0% to 1.00%, W: from 0% to 20.0%, Mg: from 0% to 5.0%, Al: from 0% to 0.100%, Ca: from 0% to 5.0%, Ti: from 0% to 0.100%, B: from 0% to 0.5000%, REM: from 0% to 0.500%, Zr: from 0% to 0.500%, N: from 0% to 0.5000%, O: from 0.0010% to 0.1500%, and balance: Fe and impurities, wherein: a total (Mn+Ni) of a content of the Mn and a content of the Ni is 5.0% or more, and a total (Nb+Ti+V+Al) of a content of the Nb, a content of the Ti, a content of the V, and a content of the Al is 0.005% or more.

2. The weld metal according to claim 1, wherein a total (Mn+Ni+Cr) of the content of the Mn, the content of the Ni, and a content of the Cr is 15.0% or more.

3. The weld metal according to claim 1, wherein an fcc ratio obtained by a magnetic induction method is 70% or more.

4. The weld metal according to claim 1, wherein a mass ratio (Ni/Mn) of the content of the Mn and the content of the Ni is 0.10 or more.

5. The weld metal according to claim 4, wherein the mass ratio (Ni/Mn) is 1.00 or more.

6. The weld metal according to claim 1, wherein the content of the Ti is Ti: from 0.003% to 0.100%.

7. The weld metal according to claim 1, wherein a content of the C is C: from 0.110% to 1.000%.

8. A weld joint comprising the weld metal according to claim 1.

9. A weld structural object comprising the weld joint according to claim 8.

Description

DESCRIPTION OF EMBODIMENTS

[0048] Embodiments that is an example of the disclosure will be described.

[0049] In the present specification, a numerical range represented by to means a range including numerical values described before and after to as a lower limit value and an upper limit value when greater than and less than are not added to these numerical values. In addition, a numerical range when greater than or less than is attached to the numerical values described before and after to means a range not including these numerical values as the lower limit value or the upper limit value.

[0050] In numerical ranges described stepwise in the present specification, an upper limit value of a certain stepwise numerical range may be replaced with an upper limit value of a numerical range of another stepwise description, or may be replaced with a value shown in the examples. Further, a lower limit value of a certain stepwise numerical range may be replaced with a lower limit value of a numerical range of another stepwise description, or may be replaced with a value shown in the examples.

[0051] As for the content, % means % by mass.

[0052] 0 to as the content (%) means that the component is an optional component and need not be contained.

<Weld Metal>

[0053] In the weld metal according to the disclosure, the chemical component has a predetermined composition.

[0054] In the weld metal according to the disclosure, a weld metal that is inexpensive and has high toughness in low-temperature is obtained with the above configuration.

[0055] The weld metal according to the disclosure has been found from the following findings.

[0056] The inventors have studied a technique for obtaining a weld metal that can improve the toughness in low-temperature of the weld metal even when the Ni content is reduced and the Mn content is increased. As a result, the following findings were obtained.

[0057] In order to secure the toughness in low-temperature, it is preferable that the weld metal is an austenite single phase. Both Ni and Mn stabilize the austenite phase. However, when Ni is excessively reduced or Mn is excessively increased, stacking fault energy was lowered and the toughness was deteriorated. Therefore, by controlling the contents of Ni and Mn, the stacking fault energy was prevented from being lowered. As a result, the weld metal having high toughness in low-temperature was obtained even when the Ni content was reduced and the Mn content was increased in the entire weld metal.

[0058] From the above findings, it has been found that the weld metal according to the disclosure is inexpensive and has high toughness in low-temperature.

[0059] Hereinafter, the reasons for limiting the requirements (requirements including optional requirements) constituting the weld metal according to the disclosure will be specifically described.

(Chemical Component of Weld Metal)

[0060] Hereinafter, the chemical component of the weld metal will be described in detail.

[0061] In the description of the chemical component of the weld metal, % means % by mass with respect to the total mass of the weld metal unless otherwise specified.

[0062] The chemical component of the weld metal consists of [0063] C: from 0.030% to 1.000%, [0064] Si: from 0.03% to 0.50%, [0065] Mn: from 4.1% to 30.0%, [0066] P: from 0% to 0.050%, [0067] S: from 0% to 0.050%, [0068] Cu: from 0% to 5.0%, [0069] Ni: from 1.0% to 30.0%, [0070] Cr: from 0% to 20.0%, [0071] Mo: from 0% to 10.0%, [0072] Nb: from 0% to 1.000%, [0073] V: from 0% to 1.00%, [0074] Co: from 0% to 1.00%, [0075] Pb: from 0% to 1.00%, [0076] Sn: from 0% to 1.00%, [0077] W: from 0% to 20.0%, [0078] Mg: from 0% to 5.0%, [0079] Al: from 0% to 0.100%, [0080] Ca: from 0% to 5.0%, [0081] Ti: from 0% to 0.100%, [0082] B: from 0% to 0.5000%, [0083] REM: 0% to 0.500%, [0084] Zr: 0% to 0.500%, [0085] N: 0% to 0.5000%, [0086] O: from 0.0010% to 0.1500%, and [0087] balance: Fe and impurities.

[0088] In the chemical component, [0089] a total (Mn+Ni) of a content of the Mn and a content of the Ni is 5.0% or more, and [0090] a total (Nb+Ti+V+Al) of a content of the Nb, a content of the Ti, a content of the V, and a content of the Al is 0.005% or more.

(C: From 0.030% to 1.000%)

[0091] C improves strength of the weld metal, and is an element for securing the strength of the weld metal.

[0092] However, when the C content in the weld metal is excessive, the influence of deterioration of the toughness due to an increase in the strength of the weld metal is large, and the toughness in low-temperature of the weld metal decreases.

[0093] Therefore, the C content in the weld metal is set from 0.030% to 1.000%.

[0094] A lower limit of the C content in the weld metal may be preferably set to 0.050%, 0.100%, 0.110%, 0.120%, 0.140%, 0.150%, 0.200%, or 0.250%.

[0095] An upper limit of the C content in the weld metal is preferably 0.900%, 0.800%, 0.700%, 0.600%, 0.550%, 0.500%, 0.450%, or 0.400%.

(Si: From 0.03% to 0.50%)

[0096] Si is a deoxidizing element. When the Si content in the weld metal is too low, the P content in the weld metal increases.

[0097] However, Si has a low solid solubility with respect to the austenite phase, and as Si is contained in a larger amount, an embrittlement phase such as an intermetallic compound or 8 ferrite is generated at a high temperature, and high temperature ductility is deteriorated.

[0098] Therefore, the Si content in the weld metal is set from 0.03% to 0.50%.

[0099] A lower limit of the Si content in the weld metal is preferably 0.04%, 0.05% or 0.08%.

[0100] An upper limit of the Si content in the weld metal is preferably 0.48%, 0.45%, 0.40%, 0.35%, 0.30%, or 0.20%.

(Mn: From 4.1% to 30.0%)

[0101] Mn stabilizes the austenite phase. When the Mn content in the weld metal is too low, austenitization of the weld metal hardly proceeds, and the toughness in low-temperature is deteriorated. Mn functions as a deoxidizing agent to improve the cleanness of the weld metal. Mn detoxifies S in the weld metal by forming MnS. It improve the toughness of the weld metal in low-temperature. In addition, Mn has an effect of preventing hot cracking.

[0102] However, when the Mn content in the weld metal is excessive, micro-segregation is likely to occur in the weld metal, and significant embrittlement occurs at the segregated portion. In addition, when Mn is excessively added, the stacking fault energy decreases and the toughness deteriorates.

[0103] Therefore, the Mn content in the weld metal is set from 4.1% to 30.0%.

[0104] A lower limit of the Mn content in the weld metal is preferably 4.2%, 4.5%, 5.0%, 7.0%, 9.0% or 10.0%.

[0105] An upper limit of the Mn content in the weld metal is preferably 28.0%, 25.0%, 23.0%, 20.0%, 18.0%, 15.0% or 14.5%.

(P: From 0% to 0.050%)

[0106] P is an impurity element and reduces the toughness, and thus it is preferable to reduce the P content in the weld metal as much as possible. Therefore, a lower limit of the P content in the weld metal is set to 0%. However, from the viewpoint of reducing the P removal cost, the P content in the weld metal is preferably 0.003% or more.

[0107] When the P content in the weld metal is 0.050% or less, the adverse effect of P on the toughness falls within an acceptable range.

[0108] Therefore, the P content in the weld metal is set from 0% to 0.050%.

[0109] In order to effectively suppress the decrease in the toughness, the P content in the weld metal is preferably 0.040% or less, 0.030% or less, 0.020% or less, 0.015% or less, or 0.010% or less.

(S: From 0% to 0.050%)

[0110] S is an impurity element and reduces the toughness, and thus it is preferable to reduce the S content in the weld metal as much as possible. Therefore, a lower limit of the S content in the weld metal is set to 0%. However, from the viewpoint of reducing the S removal cost, the S content in the weld metal is preferably 0.003% or more.

[0111] When the S content in the weld metal is 0.050% or less, the adverse effect of S on the toughness falls within an acceptable range.

[0112] Therefore, the S content in the weld metal is set from 0% to 0.050%.

[0113] In order to effectively suppress the decrease in the toughness, the S content in the weld metal is preferably 0.040% or less, 0.030% or less, 0.020% or less, 0.015% or less, or 0.010% or less.

(Cu: From 0% to 5.0%)

[0114] Cu is a precipitation strengthening element, and may be contained in the weld metal in order to improve the strength of the weld metal. Cu stabilizes the austenite phase. Cu may be contained in the weld metal in order to improve the toughness in low-temperature of the weld metal.

[0115] However, when the Cu content in the weld metal is excessive, the above effect is saturated.

[0116] Therefore, the Cu content in the weld metal is set from 0% to 5.0%.

[0117] A lower limit of the Cu content in the weld metal is preferably 0.3%, 0.5%, or 0.7%.

[0118] An upper limit of the Cu content in the weld metal is preferably 4.5%, 4.0%, or 3.5%.

(Ni: From 1.0% to 30.0%)

[0119] Ni stabilizes the austenite phase. When the Ni content in the weld metal is too low, the toughness is deteriorated by not stabilizing the austenite phase in the weld metals.

[0120] However, when the Ni content in the weld metal is increased, the cost of the weld metal increases.

[0121] Therefore, the Ni content in the weld metal is set from 1.0% to 30.0%.

[0122] A lower limit of the Ni content in the weld metal is preferably 2.0%, 3.0%, 3.2%, 3.7%, 5.0%, or 7.0%.

[0123] An upper limit of the Ni content in the weld metal is preferably 28.0%, 25.0%, 23.0%, 20.0%, 18.0%, or 15.0%.

(Cr: From 0% to 20.0%)

[0124] Cr stabilizes the austenite phase, and may be contained in the weld metal in order to improve the toughness in low-temperature of the weld metal.

[0125] However, when the Cr content in the weld metal is excessive, an amount of a low-melting-point compound in a molten metal increases, and a solid-liquid coexisting temperature range of the molten metal is widened, and thus the hot cracking is likely to occur.

[0126] Therefore, the Cr content in the weld metal is set from 0% to 20.0%.

[0127] A lower limit of the Cr content in the weld metal is preferably 1.0%, 2.0% or 3.0%.

[0128] An upper limit of the Cr content in the weld metal is preferably 18.0%, 15.8%, 15.3%, 15.0%, 13.3%, 13.0%, 10.0%, 9.0%, 8.0% or 7.0%.

(Mo: From 0% to 10.0%)

[0129] Mo is a precipitation strengthening element, and may be contained in the weld metal in order to improve the strength of the weld metal.

[0130] However, when the Mo content in the weld metal is excessive, the strength of the weld metal is excessive, and the toughness in low-temperature decreases.

[0131] Therefore, the Mo content in the weld metal is set from 0% to 10.0%.

[0132] A lower limit of the Mo content in the weld metal is preferably 1.0%, 2.0% or 3.0%.

[0133] An upper limit of the Mo content in the weld metal is preferably 9.0%, 8.0%, or 7.0%.

(Nb: From 0% to 1.000%)

[0134] Nb forms a carbide in the weld metal and increases the strength of the weld metal, and thus may be contained in the weld metal.

[0135] However, when the Nb content in the weld metal is excessive, there is a concern that the hot cracking of the weld metal may occur.

[0136] Therefore, the Nb content in the weld metal is set from 0% to 1.000%.

[0137] A lower limit of the Nb content in the weld metal is preferably 0.010%, 0.050%, 0.100%, 0.150%, or 0.200%.

[0138] An upper limit of the Nb content in the weld metal is preferably 0.950%, 0.900%, 0.850%, or 0.800%.

(V: From 0% to 1.00%)

[0139] V forms a carbonitride in the weld metal and increases the strength of the weld metal, and thus may be contained in the weld metal.

[0140] However, when the V content in the weld metal is excessive, the hot cracking of the weld metal may occur.

[0141] Therefore, the V content in the weld metal is set from 0% to 1.00%.

[0142] A lower limit of the V content in the weld metal is preferably 0.01%, 0.05%, 0.10%, 0.15%, or 0.20%.

[0143] An upper limit of the V content in the weld metal is preferably 0.95%, 0.90%, 0.85%, or 0.80%.

(Co: From 0% to 1.00%)

[0144] Co increases the strength of the weld metal by solid solution strengthening, and thus may be contained in the weld metal.

[0145] However, when the Co content in the weld metal is excessive, ductility of the weld metal decreases, and the toughness cannot be secured.

[0146] Therefore, the Co content in the weld metal is set from 0% to 1.00%.

[0147] A lower limit of the Co content in the weld metal is preferably 0.01%, 0.05%, 0.10%, 0.15%, or 0.20%.

[0148] An upper limit of the Co content in the weld metal is preferably 0.95%, 0.90%, 0.85%, or 0.80%.

(Pb: From 0% to 1.00%)

[0149] Pb improves toe formability between a steel material that is a base material and the weld metal and improving a cutting property of the weld metal. Therefore Pb may be contained in the weld metal.

[0150] However, when the Pb content in the weld metal is excessive, the hot cracking occurs.

[0151] Therefore, the Pb content in the weld metal is set from 0% to 1.00%.

[0152] A lower limit of the Pb content in the weld metal is preferably 0.01%, 0.05%, 0.10%, 0.15%, or 0.20%.

[0153] An upper limit of the Pb content in the weld metal is preferably 0.95%, 0.90%, 0.85%, or 0.80%.

(Sn: From 0% to 1.00%)

[0154] Sn improves corrosion resistance of the weld metal, and thus may be contained in the weld metal.

[0155] However, when the Sn content in the weld metal is excessive, there is a concern that cracking may occur in the weld metal.

[0156] Therefore, the Sn content in the weld metal is set from 0% to 1.00%.

[0157] A lower limit of the Sn content in the weld metal is preferably 0.01%, 0.05%, 0.10%, 0.15%, or 0.20%.

[0158] An upper limit of the Sn content in the weld metal is preferably 0.95%, 0.90%, 0.85%, or 0.80%.

(W: From 0% to 20.0%)

[0159] W is a solid solution strengthening element, and may be contained in the weld metal in order to improve the strength.

[0160] However, when the W content in the weld metal is excessive, the strength of the weld metal is excessive, and the toughness may be reduced.

[0161] Therefore, the W content in the weld metal is set from 0% to 20.0%.

[0162] A lower limit of the W content in the weld metal is preferably 0.5%, 1.0%, or 2.0%.

[0163] An upper limit of the W content in the weld metal is preferably 19.0%, 18.0%, 17.0%, 16.0%, or 15.0%.

(Mg: From 0% to 5.0%)

[0164] Mg is a deoxidizing element, and has an effect of reducing oxygen and improving the toughness, and thus may be contained in the weld metal.

[0165] However, when the Mg content in the weld metal is excessive, an arc is destabilized during a welding work for obtaining the weld metal, sputtering and blow holes increase, and the welding workability is deteriorated.

[0166] Therefore, the Mg content in the weld metal is set from 0% to 5.0%.

[0167] A lower limit of the Mg content in the weld metal is preferably 0.02%, 0.05%, 0.1%, or 0.2%.

[0168] An upper limit of the Mg content in the weld metal is preferably 4.8%, 4.5%, 4.3%, or 4.0%.

(Al: From 0% to 0.100%)

[0169] Al is a deoxidizing element, and may be contained in the weld metal in order to suppress welding defects and improve the cleanness of the weld metal.

[0170] However, when the Al content in the weld metal is excessive, Al may form a nitride or an oxide in the weld metal, and the toughness in low-temperature of the weld metal may be reduced.

[0171] Therefore, the Al content in the weld metal is set from 0% to 0.100%.

[0172] A lower limit of the Al content in the weld metal is preferably 0.010%, 0.020%, or 0.030%.

[0173] An upper limit of the Al content in the weld metal is preferably 0.090%, 0.080%, or 0.070%.

(Ca: From 0% to 5.0%)

[0174] Ca has a function of changing the structure of a sulfide and refining the sizes of the sulfide and an oxide in the weld metal, and thus is effective for improving the ductility and the toughness of the weld metal. Therefore, Ca may be contained in the weld metal.

[0175] However, when the content in Ca in the weld metal is excessive, coarsening of the sulfide and the oxide may occur, leading to deterioration of the toughness in low-temperature of the weld metal.

[0176] Therefore, the Ca content in the weld metal is set from 0% to 5.0%.

[0177] A lower limit of the Ca content in the weld metal is preferably 0.01%, 0.02%, or 0.03%.

[0178] An upper limit of the Ca content in the weld metal is preferably 4.8%, 4.5%, 4.3%, or 4.0%.

(Ti: From 0% to 0.100%)

[0179] Ti is a deoxidizing element, and may be contained in the weld metal in order to suppress welding defects and improve the cleanness of the weld metal.

[0180] However, when the Ti content in the weld metal is excessive, carbide is generated in the weld metal, and the toughness of the weld metal may be deteriorated.

[0181] Therefore, the Ti content in the weld metal is set from 0% to 0.100%.

[0182] A lower limit of the Ti content in the weld metal is preferably 0.003%, 0.010%, 0.020%, or 0.030%.

[0183] An upper limit of the Ti content in the weld metal is preferably 0.090%, 0.080%, or 0.070%.

(B: From 0% to 0.5000%)

[0184] B stabilizes the austenite phase. B is also an interstitial solid solution strengthening element, and may be contained in the weld metal in order to improve the toughness in low-temperature and the strength of the weld metal.

[0185] However, when the B content in the weld metal is excessive, M.sub.23(C,B).sub.6 is precipitated, which causes toughness deterioration.

[0186] Therefore, the B content in the weld metal is set from 0% to 0.5000%.

[0187] A lower limit of the B content in the weld metal is preferably 0.0005%, 0.0010%, or 0.0020%.

[0188] An upper limit of the B content in the weld metal is preferably 0.4800%, 0.4500%, 0.4300%, or 0.4000%.

(REM: From 0% to 0.500%)

[0189] REM stabilizes an arc during the welding for obtaining the weld metal, and thus may be contained in the weld metal.

[0190] However, when the REM content in the weld metal is excessive, sputtering becomes severe during the welding work for obtaining the weld metal, and welding workability may be poor.

[0191] Thus, the REM content in the weld metal is set from 0% to 0.500%.

[0192] A lower limit of the REM content in the weld metal is preferably 0.001%, 0.002%, or 0.005%.

[0193] An upper limit of the REM content in the weld metal is preferably 0.480%, 0.450%, 0.430%, or 0.400%.

(Zr: From 0% to 0.500%)

[0194] Zr can stabilize a bead shape of the welding work for obtaining the weld metal, and thus may be contained in the weld metal.

[0195] However, when the Zr content in the weld metal is excessive, an oxygen amount of the weld metal is increased, and the toughness in low-temperature may be deteriorated.

[0196] Therefore, the Zr content in the weld metal is set from 0% to 0.500%.

[0197] A lower limit of the Zr content in the weld metal is preferably 0.001%, 0.002%, or 0.005%.

[0198] An upper limit of the Zr content in the weld metal is preferably 0.480%, 0.450%, 0.430%, or 0.400%.

(N: From 0% to 0.5000%)

[0199] N stabilizes the austenite phase. N is also an interstitial solid solution strengthening element, and may be contained in the weld metal in order to improve the toughness in low-temperature and the strength of the weld metal.

[0200] However, when the N content in the weld metal is excessive, the occurrence of blowing increases, which causes welding defects.

[0201] Therefore, the N content in the weld metal is set from 0% to 0.5000%.

[0202] A lower limit of the N content in the weld metal is preferably 0.0010%, 0.0100% or 0.0500%.

[0203] An upper limit of the N content in the weld metal is preferably 0.4500%, 0.4000%, or 0.3500%.

(O: From 0.0010% to 0.1500%)

[0204] O is contained in the weld metal as an impurity. However, when the O content is excessive, the toughness and the ductility are deteriorated, and thus an upper limit of the O content in the weld metal is set to 0.1500% or less.

[0205] However, an extreme reduction in the O content leads to an increase in manufacturing cost, and thus a lower limit of the O content in the weld metal is set to 0.0010% or less.

[0206] The lower limit of the O content in the weld metal is preferably 0.0020% or 0.0030%.

[0207] An upper limit of the O content in the weld metal is preferably 0.1300% or 0.1000%.

(Balance: Fe and Impurities)

[0208] The other components of a balance in the chemical component of the weld metal are Fe and impurities.

[0209] The impurity means a raw material such as ore or scrap, or a component mixed due to various factors in the manufacturing process when the weld metal is industrially manufactured, and is acceptable within a range not adversely affecting the characteristics of the weld metal.

(Total (Mn+Ni) of Mn Content and Ni Content)

[0210] Each of Mn and Ni stabilizes the austenite phase. Each of Mn and Ni improves the toughness in low-temperature of the weld metal. However, since Ni is an expensive metal, in order to improve the toughness in low-temperature of the weld metal while suppressing the cost of the weld metal, while the Mn content and the Ni content in the weld metal satisfy the above ranges, respectively, the total (Mn+Ni) of the Mn content and the Ni content is set to 5.0% or more.

[0211] The total (Mn+Ni) of the Mn content and the Ni content in the weld metal is preferably 5.2% or more, 6.2% or more, 6.7% or more, 7.0% or more, 10.0% or more, or 15.0% or more.

[0212] When Mn is excessively increased, the stacking fault energy is lowered and the toughness is deteriorated. Therefore, from the viewpoint of suppressing the cost of the weld metal and improving the toughness in low-temperature of the weld metal, it is preferable that while each of the Mn content and the Ni content in the weld metal satisfies the above range, the total (Mn+Ni) of the Mn content and the Ni content is set to 37.0% or less.

[0213] The total (Mn+Ni) of the Mn content and the Ni content in the weld metal is more preferably 35.0% or less, 32.0% or less, or 30.0% or less.

(Total (Mn+Ni+Cr) of Mn Content, Ni Content and Cr Content)

[0214] Each of Mn, Ni and Cr stabilizes the austenite phase. Each of Mn, Ni and Cr improves the toughness in low-temperature of the weld metal. However, since Ni is an expensive metal, in order to improve the toughness in low-temperature of the weld metal while suppressing the cost of the weld metal, it is preferable that while each of the Mn content, the Ni content, and the Cr content satisfies the above range, the total (Mn+Ni+Cr) of the Mn content, the Ni content, and the Cr content in the weld metal is set to 15.0% or more

[0215] The total (Mn+Ni+Cr) of the Mn content, the Ni content, and the Cr content in the weld metal is more preferably 17.0% or more, 19.0% or more, 20.0% or more, 22.0% or more, 24.0% or more, 26.0% or more, 28.0% or more, or 30.0% or more.

[0216] When the Mn content is not excessive, the stacking fault energy is not excessively lowered, and the toughness can be secured. When the Cr content is not excessive, the amount of the low-melting-point compound in the molten metal can be reduced, and the expansion of the solid-liquid coexisting temperature range of the molten metal can be suppressed, and thus the occurrence of the hot cracking can be suppressed. Therefore, from the viewpoint of suppressing the cost of the weld metal, improving the toughness in low-temperature of the weld metal, reducing the generation amount of the low-melting-point compound in the molten metal, and suppressing the occurrence of the hot cracking, it is preferable that while each of the Mn content, the Ni content, and the Cr content in the weld metal satisfies the above range, the total (Mn+Ni+Cr) of the Mn content, the Ni content, and the Cr content is set to 47.0% or less.

[0217] The total (Mn+Ni+Cr) of the Mn content, the Ni content, and the Cr content in the weld metal is more preferably 45.0% or less, 42.0% or less, or 40.0% or less.

(Mass Ratio (Ni/Mn) of Mn Content to Ni Content)

[0218] Each of Mn and Ni stabilizes the austenite phase. Each of Mn and Ni improves the toughness in low-temperature of the weld metal. However, Ni is an expensive metal, and when Mn is further excessively increased, the stacking fault energy is lowered and the toughness is deteriorated.

[0219] Therefore, from the viewpoint of improving the toughness in low-temperature of the weld metal while suppressing the cost of the weld metal, a mass ratio (Ni/Mn) of the Mn content to the Ni content in the weld metal is preferably set to 0.10 or more.

[0220] A lower limit of the mass ratio (Ni/Mn) of the Mn content to the Ni content in the weld metal is more preferably 0.20, 0.30, 0.50, 0.70, 0.73, 1.00, 1.10, or 1.20.

[0221] An upper limit of the mass ratio (Ni/Mn) of the Mn content to the Ni content in the weld metal is preferably 10.00, 8.00, or 5.00.

(Total (Nb+Ti+V+Al) of Nb Content, Ti Content, V Content, and Al Content)

[0222] Nb, Ti, V, and Al are all elements that improve the strength of the weld metal by precipitation strengthening, and thus the weld metal contains one or more of Nb, Ti, V, and Al, and the total (Nb+Ti+V+Al) thereof is set to 0.005% or more.

[0223] A lower limit of the total (Nb+Ti+V+Al) of Nb, Ti, V, and Al in the weld metal is preferably 0.010%, 0.020%, 0.050%, 0.100%, 0.300%, or 0.500%.

[0224] An upper limit of the total (Nb+Ti+V+Al) of Nb, Ti, V, and Al in the weld metal is not particularly limited, but is preferably 2.000%, 1.800%, 1.500%, or 1.300% in order to prevent toughness deterioration due to excessive precipitation.

(Fcc Ratio Obtained by Magnetic Induction Method)

[0225] In order to increase the toughness in low-temperature in the weld metal, it is preferable to increase a ratio of austenite in the structure of the weld metal. Therefore, the fcc ratio in the weld metal is preferably set to 70% or more. The fcc ratio is more preferably 80% or more, or 90% or more, and may be 100%. The balance of the structure is bcc.

[0226] The fcc ratio in the structure of the weld metal can be measured by the following method.

[0227] A sample is collected from the weld metal, bcc ratios (%) are measured on a surface of the sample by a magnetic induction method by using FERITSCOPE (registered trademark) FMP30 (manufactured by Fischer Instruments K.K.) and using a probe (FGAB 1.3 Fe) manufactured by Fischer Instruments K.K. as a probe of the measuring instrument, and an arithmetic average value of the measured bcc ratios is determined. Using the obtained average value of the bcc ratios, the fcc ratio (%) in the structure of the weld metal is determined by the following equation.

fcc ratio=100bcc ratio

(Tensile Strength)

[0228] The tensile strength of the weld metal is preferably set to from 590 MPa to 1200 MPa, for example. The tensile strength can be measured by performing a tensile test of the weld metal in accordance with JIS Z3111:2005.

<Weld Joint and Weld Structural Object>

[0229] Next, a weld joint and a weld structural object according to the disclosure will be described.

[0230] A weld joint according to the disclosure includes the weld metal according to the disclosure. For example, the weld joint according to the disclosure includes a steel material that is a base material and a welded portion including the weld metal and a weld heat-affected portion.

[0231] The weld structural object according to the disclosure includes the weld joint according to the disclosure.

[0232] The weld joint according to the disclosure includes the weld metal according to the disclosure, and thus the weld joint is inexpensive and has high toughness in low-temperature.

[0233] Here, a method of manufacturing the weld joint according to the disclosure will be described.

[0234] The method of manufacturing described below is an example, and the method of manufacturing the weld joint according to the disclosure is not limited to the following method.

[0235] The weld joint according to the disclosure can be manufactured by welding the steel material that is the base material by using the weld material.

[0236] For example, the method of manufacturing the weld joint according to the disclosure is obtained by performing gas metal arc welding on the steel material by using a flux-cored wire. In this case, the chemical component of the weld metal include components derived from the flux-cored wire that is the weld material and the steel material that is the base material.

[0237] The method of manufacturing the weld joint according to the disclosure is obtained by performing submerged arc welding using a solid wire and a flux. For example, in the submerged arc welding, it is possible to apply a general submerged arc welding apparatus in which a granular flux is sprayed on a weld line in advance, the solid wire is fed into the flux, and welding is performed by arc heat generated from an arc between the solid wire and the steel material in the flux. In this case, the chemical component of the weld metal include components derived from the solid wire and the flux that are the weld material and the steel material that is the base material.

[0238] Further, the method of manufacturing the weld joint according to the disclosure can be obtained by, for example, a welding method such as shielded metal arc welding, simple electrogas arc welding, electroslag welding, TIG welding, or gas metal welding by using the solid wire. In this case, the chemical component of the weld metal include components derived from the weld material and the steel material that is the base material.

[0239] The type of the base material included in the weld joint according to the disclosure, that is, the steel material (welding target material) used in the method of manufacturing the weld joint is not particularly limited, but for example, Ni-based low temperature steel containing from 6% to 9% Ni with a plate thickness of 20 mm or more can be suitably used.

EXAMPLES

[0240] Next, the feasibility and effects of the disclosure will be described in more detail with reference to the disclosure examples and the comparative examples, but the following examples do not limit the disclosure, and any design change dedicated to the gist of the preceding and following description is included in the technical scope of the disclosure.

[0241] The weld metal was obtained by shielded metal arc welding (SMAW) using a shielded metal arc welding rod, gas metal arc welding (GMAW) using the flux-cored wire, and the submerged arc welding (SAW) using the solid wire and the flux by the methods described below.

<1. Shielded Metal Arc Welding (SMAW) Using Shielded Metal Arc Welding Rod>

(Manufacturing of Shielded Metal Arc Welding Rod)

[0242] The shielded metal arc welding rod was manufactured by the method described below.

[0243] First, the shielded metal arc welding rod was experimentally produced by applying a flux including components shown in Table 2-C to a core wire including the chemical component shown in Table 2-A and Table 2-B and firing the core wire in a temperature range of from 300 C. to 500 C. for a range from 1 hour to 3 hours. The final welding rod diameter of the obtained shielded metal arc welding rod was 6.0 mm, and the average thickness of the flux was 1.0 mm. The configurations of these shielded metal arc welding rods (No. 1 to 3, 15, A1, A4) are shown in Tables 2-A to 2-C.

[0244] The unit of the contents of the chemical component of the core wire shown in Tables 2-A and 2-B is % by mass with respect to the total mass of the core wire. The unit of the contents of the components (oxide, fluoride, and metal carbonate) of the flux shown in Table 2-C is % by mass with respect to the total mass of the flux.

[0245] In Table 2-C, TiO.sub.2 represents the total of Ti oxides in terms of TiO.sub.2, SiO.sub.2 represents the total of Si oxides in terms of SiO.sub.2, Al.sub.2O.sub.3 represents the total of Al oxides in terms of Al.sub.2O.sub.3, MgO represents the total of Mg oxides in terms of MgO, Na.sub.2O represents the total of Na oxides in terms of Na.sub.2O, and K.sub.2O represents the total of K oxides in terms of K.sub.2O.

[0246] The balance (that is, components other than the respective components shown in the tables) of the core wire shown in Tables 2-A and 2-B is iron and impurities.

[0247] In Tables 2-A to 2-C, blanks in the table regarding the contents of the chemical component of the core wire and the components of the flux mean that the contents of the components and the like are less than the number of significant digits. These components and the like may be unavoidably mixed or generated in a content less than the number of significant digits.

(Manufacturing of Weld Joint)

[0248] The weld joint including the weld metal was manufactured by performing shielded metal arc welding with vertical upward welding using the obtained shielded metal arc welding rod (No. 1 to 3, 15, A1, A4). 9% Ni steel (steel sheet in accordance with JIS G 3127:2013 SL9N 590) having a sheet thickness of 50 mm was used as a steel sheet to be welded. All the welding currents at the time of welding were set to an alternating current, and welding conditions were set to the conditions of shielded metal arc welding (SMAW) described in Table 5.

[0249] The chemical component of the weld metal in the manufactured weld joint are shown in Tables 1-A to 1-C(No. 1 to 3, 15, A1, A4). In Tables 1-A to 1-C, numerical values outside the range defined in the disclosure are underlined.

<2. Gas Shielded Arc Welding (GMAW) Using Flux-Cored Wire>

(Manufacturing of Flux-Cored Wire)

[0250] The flux-cored wire was manufactured by the method described below.

[0251] First, while feeding a steel strip in the longitudinal direction, the steel strip was formed using a forming roll to obtain an open tube having a U shape. The flux was supplied into the open tube through an opening of the open tube, and edge portions of the opening of the open tube facing each other were butt-welded to obtain a seamless tube. The seamless tube was wire drawn to obtain the flux-cored wire including no slit-like gap.

[0252] In this way, the flux-cored wire having a final wire diameter of @1.2 mm was experimentally produced.

[0253] In the middle of the wire drawing operation of these flux-cored wires, the flux-cored wires were annealed in a temperature range of from 650 C. to 950 C. for 4 hours or more. After the experimental production, a lubricant was applied to the wire surface. The configurations (the chemical component of the entire wire, components of the flux) of these flux-cored wires (No. 4 to 9, A2) are shown in Tables 3-A to 3-C.

[0254] The unit of the contents of the chemical component of the entire wire and the contents of the components (oxides and fluorides) of the flux shown in Tables 3-A to 3-C is % by mass with respect to the total mass of the flux-cored wire. In the table, chemical component of the entire wire means chemical component of the wire excluding oxides and fluorides.

[0255] The balance (that is, components other than the respective components shown in the table) of the chemical component of the entire wire shown in Tables 3-A and 3-B includes iron and impurities.

[0256] The elements contained in the flux-cored wires shown in Tables 3-A and 3-B are in the form of steel outer skins or metal powders.

[0257] In Tables 3-A to 3-C, blanks in the table regarding the contents of the chemical component of the entire wire and the components of the flux mean that the contents of the components and the like are less than the number of significant digits. These components and the like may be unavoidably mixed or generated in a content less than the number of significant digits.

(Manufacturing of Weld Joint)

[0258] The weld joint including the weld metal was manufactured by performing gas shielded arc welding with vertical upward welding using the obtained flux-cored wire (No. 4 to 9, A2). 9% Ni steel (steel sheet in accordance with JIS G 3127: SL9N 590) having a sheet thickness of 50 mm was used as a steel sheet to be welded. The type of the welding gas at the time of welding was Ar-20% CO.sub.2 gas. All the welding current at the time of welding was set to a direct current, and all the polarity of the wire was positive. Welding conditions were set to the conditions of flux-cored wire (GMAW) described in Table 5.

[0259] The chemical component of the weld metal in the manufactured weld joint is shown in Tables 1-A to 1-C(No. 4 to 9, A2). In Tables 1-A to 1-C, numerical values outside the range defined in the disclosure are underlined.

<3. Submerged Arc Welding (SAW) Using Solid Wire and Flux>

(Manufacturing of Solid Wire)

[0260] The solid wire was manufactured by the method described below.

[0261] First, steel including the chemical component shown in Tables 4-A and 4-B was melted, and then subjected to forging processing. Thereafter, the steel was processed into a rod shape through rolling processing, and the steel having the rod shape was wire drawn to obtain the solid wire. In this way, solid wires (No. 10 to 14, 16 to 17, A3, A5) each having a final wire diameter of 2.4 mm were experimentally produced.

[0262] When the chemical component of the obtained solid wires were analyzed, the solid wires included the chemical component shown in Tables 4-A and 4-B. After the experimental production, a lubricant was applied to the wire surface.

[0263] The unit of the contents of the chemical component of the wire shown in Tables 4-A and 4-B is % by mass with respect to the total mass of the solid wire.

[0264] The balance (that is, components other than the respective components shown in the table) of the wire shown in Tables 4-A and 4-B includes iron and impurities.

[0265] In Tables 4-A and 4-B, blanks in the table regarding the contents of the chemical component of the wire mean that the contents of the chemical component are less than the number of significant digits. These chemical components and the like may be unavoidably mixed or generated in a content less than the number of significant digits.

(Manufacturing of Weld Joint)

[0266] The weld joint including the weld metal was manufactured by welding downward by the submerged arc welding using the obtained solid wires (No. 10 to 14, 16 to 17, A3, A5). Specifically, the submerged arc welding was performed using the solid wires in combination with NITTETSU FLUX 10 H manufactured by NIPPON STEEL WELDING & ENGINEERING CO., LTD., which is a flux for the submerged arc welding.

[0267] 9% Ni steel (steel sheet in accordance with JIS G 3127: SL9N 590) having a sheet thickness of 40 mm was used as a steel sheet to be welded. All the welding current at the time of welding was set to a direct current, and all the polarity of the wire was positive. Welding conditions were set to the conditions of submerged arc welding (SAW) described in Table 5.

[0268] The chemical component of the weld metal in the manufactured weld joint are shown in Tables 1-A to 1-C(No. 10 to 14, 16 to 17, A3, A5). In Tables 1-A to 1-C, numerical values outside the range defined in the disclosure are underlined.

<Evaluation Test>

(Evaluation of Toughness in Low-Temperature)

[0269] Three impact test pieces (V-notch test pieces each having a notch depth of 2 mm) were taken from the center in a plate thickness direction of the weld metal (No. 1 to 17, A1 to A5) obtained in the disclosure example and the comparative example.

[0270] The three impact test pieces were subjected to a Charpy impact test in accordance with JIS Z2242:2005 at 196 C.

[0271] Then, the case in which the Charpy absorbed energy average value of the three impact test pieces at 196 C. was 34 J or more was rated as excellent, the case in which the average value was 27 J or more and less than 34 J was rated as passed, and the case in which the average value was less than 27 J was rated as failed.

TABLE-US-00001 TABLE 1-A Welding Chemical component (% by mass) (balance is Fe and impurities) No. Classification method C Si Mn P S Cu Ni Cr Mo Nb V 1 Disclosure example SMAW 0.570 0.32 16.8 0.017 0.010 24.5 4.7 6.9 1.00 2 Disclosure example SMAW 0.120 0.25 22.8 0.024 0.009 1.9 9.2 7.2 0.937 3 Disclosure example SMAW 0.340 0.30 8.0 0.009 0.009 12.0 7.0 3.0 0.020 4 Disclosure example GMAW 0.510 0.29 22.0 0.036 0.010 1.3 27.5 18.0 0.596 5 Disclosure example GMAW 0.380 0.36 24.3 0.012 0.042 12.2 2.0 5.4 0.115 6 Disclosure example GMAW 0.357 0.43 9.1 0.009 0.009 17.1 7.4 3.4 0.018 7 Disclosure example GMAW 0.770 0.36 15.5 0.017 0.032 1.5 14.6 0.6 0.4 0.56 8 Disclosure example GMAW 0.450 0.17 14.2 0.045 0.028 18.9 6.4 0.15 9 Disclosure example GMAW 0.590 0.43 28.0 0.026 0.036 11.5 7.4 0.40 10 Disclosure example SAW 0.720 0.32 24.9 0.027 0.039 21.9 6.5 9.4 0.720 11 Disclosure example SAW 0.390 0.23 27.3 0.013 0.004 17.8 4.3 0.352 12 Disclosure example SAW 0.430 0.25 12.5 0.009 0.009 12.8 2.1 0.028 13 Disclosure example SAW 0.950 0.13 5.0 0.014 0.001 21.9 7.2 0.3 0.138 0.70 14 Disclosure example SAW 0.130 0.12 27.4 0.034 0.048 3.3 2.7 2.2 0.586 0.83 15 Disclosure example SMAW 0.340 0.05 5.0 0.009 0.009 4.0 7.0 3.0 0.020 16 Disclosure example SAW 0.670 0.08 15.2 0.014 0.001 28.0 7.2 0.3 17 Disclosure example SAW 0.200 0.20 4.5 0.007 0.008 15.0 5.0 5.0 0.12 A1 Comparative example SMAW 0.910 0.41 8.7 0.004 0.046 23.5 A2 Comparative example GMAW 0.090 0.30 1.0 0.045 0.016 2.0 6.3 6.9 A3 Comparative example SAW 0.090 0.19 35.0 0.024 0.029 5.8 7.3 0.89 A4 Comparative example SMAW 0.340 0.30 3.0 0.009 0.009 5.0 8.0 3.0 A5 Comparative example SAW 0.510 0.29 29.0 0.036 0.010 1.3 0.5 0.125

TABLE-US-00002 TABLE 1-B Chemical component (% by mass) (balance is Fe and impurities) No. Classification Co Pb Sn W Mg Al Ca Ti B REM Zr N 1 Disclosure example 0.55 0.08 4.3 4.6 0.016 0.1021 2 Disclosure example 0.24 0.15 13.8 0.0979 3 Disclosure example 0.09 0.015 0.010 0.0180 4 Disclosure example 0.35 0.66 0.3273 0.045 0.3850 5 Disclosure example 0.76 0.058 1.5 0.028 0.0880 6 Disclosure example 0.009 0.054 0.0010 0.0145 7 Disclosure example 0.06 0.018 0.057 0.0182 8 Disclosure example 0.97 4.7 0.026 0.046 0.0175 9 Disclosure example 10.2 0.3406 0.0082 10 Disclosure example 10.1 1.2 0.2640 0.1314 11 Disclosure example 0.80 0.41 2.5 0.0902 12 Disclosure example 0.01 0.030 0.0098 13 Disclosure example 4.2 0.095 0.045 0.0169 14 Disclosure example 5.0 0.031 0.0480 0.044 0.0197 15 Disclosure example 0.015 0.010 0.0180 16 Disclosure example 0.009 0.054 0.0169 17 Disclosure example 0.0245 A1 Comparative example 0.25 6.8 2.8 0.003 2.4 0.035 0.0182 A2 Comparative example 0.19 0.096 0.033 0.090 0.100 0.1314 A3 Comparative example 5.8 0.0102 A4 Comparative example 0.09 0.010 0.0180 A5 Comparative example 0.3850

TABLE-US-00003 TABLE 1-C Chemical component (% by mass) (balance is Fe and impurities) fcc Nb + Ti + Mn + ratio No. Classification O Mn + Ni V + Al Mn/Ni Ni + Cr (%) 1 Disclosure example 0.0188 41.3 1.016 0.69 46.0 100 2 Disclosure example 0.0200 24.7 0.937 12.00 33.9 100 3 Disclosure example 0.0239 20.0 0.045 0.67 27.0 100 4 Disclosure example 0.0455 49.5 0.596 0.80 67.5 100 5 Disclosure example 0.0413 36.5 0.201 1.99 38.5 100 6 Disclosure example 0.0471 26.2 0.081 0.53 33.6 100 7 Disclosure example 0.0587 30.1 0.578 1.06 30.7 100 8 Disclosure example 0.0606 33.1 0.176 0.75 33.1 100 9 Disclosure example 0.0686 39.5 0.400 2.43 39.5 100 10 Disclosure example 0.0097 46.8 0.720 1.14 53.3 100 11 Disclosure example 0.0094 45.1 0.352 1.53 49.4 100 12 Disclosure example 0.0195 25.3 0.058 0.98 25.3 100 13 Disclosure example 0.0233 26.9 0.838 0.23 34.1 100 14 Disclosure example 0.0153 30.1 1.447 10.15 32.3 98 15 Disclosure example 0.0239 9.0 0.045 1.25 16.0 89 16 Disclosure example 0.0283 43.2 0.063 0.54 50.4 100 17 Disclosure example 0.0215 19.5 0.120 0.30 24.5 72 A1 Comparative example 0.0195 32.2 0.003 0.37 32.2 100 A2 Comparative example 0.0307 3.0 0.129 0.50 9.3 0 A3 Comparative example 0.0041 40.8 0.890 6.03 40.8 100 A4 Comparative example 0.0239 8.0 0.010 0.60 16.0 65 A5 Comparative example 0.0455 29.5 0.125 58.00 29.5 100

TABLE-US-00004 TABLE 2-A Welding Chemical component of core wire (% by mass) (balance is Fe and impurities) No. Classification method C Si Mn P S Cu Ni Cr Mo Nb V 1 Disclosure example SMAW 0.570 0.400 21.000 0.002 0.010 24.500 4.700 6.900 1.000 2 Disclosure example SMAW 0.120 0.313 28.500 0.002 0.009 1.900 9.200 7.200 0.937 3 Disclosure example SMAW 0.340 0.375 10.000 0.001 0.009 12.000 7.000 3.000 0.020 15 Disclosure example SMAW 0.340 0.063 6.250 0.001 0.009 4.000 7.000 3.000 0.020 A1 Comparative example SMAW 0.200 0.250 5.625 0.001 0.008 15.000 5.000 5.000 0.120 A4 Comparative example SMAW 0.340 0.375 3.750 0.001 0.009 5.000 8.000 3.000

TABLE-US-00005 TABLE 2-B Chemical component of core wire (% by mass) (balance is Fe and impurities) No. Classification Co Pb Sn W Mg Al Ca Ti B REM Zr N 1 Disclosure example 0.550 0.080 4.300 9.200 1.600 0.085 2 Disclosure example 0.240 0.150 13.800 0.082 3 Disclosure example 0.090 1.500 0.014 0.015 15 Disclosure example 1.500 0.014 0.015 A1 Comparative example 0.020 A4 Comparative example 0.090 0.014 0.015

TABLE-US-00006 TABLE 2-C Components of flux No. Classification TiO.sub.2 SiO.sub.2 Al.sub.2O.sub.3 MgO Na.sub.2O K.sub.2O CaF.sub.2 CaCO.sub.3 1 Disclosure example 6.3 4.6 0.1 1.3 1.3 23.0 63.4 2 Disclosure example 10.0 10.0 7.5 2.5 70.0 3 Disclosure example 6.3 4.6 0.1 1.3 1.3 23.0 63.4 15 Disclosure example 10.0 10.0 7.5 2.5 70.0 A1 Comparative example 6.3 4.6 0.1 1.3 1.3 23.0 63.4 A4 Comparative example 10.0 10.0 7.5 20.0 52.6

TABLE-US-00007 TABLE 3-A Welding Chemical component of entire wire (% by mass) (balance is Fe and impurities) No. Classification method C Si Mn P S Cu Ni Cr Mo Nb V 4 Disclosure example GMAW 0.510 0.363 27.500 0.003 0.010 1.300 27.500 18.000 0.596 5 Disclosure example GMAW 0.380 0.450 30.375 0.001 0.042 12.200 2.000 5.400 0.115 6 Disclosure example GMAW 0.357 0.538 11.425 0.001 0.009 17.100 7.400 3.400 0.018 7 Disclosure example GMAW 0.770 0.450 19.375 0.002 0.032 1.500 14.600 0.600 0.400 0.560 8 Disclosure example GMAW 0.450 0.213 17.750 0.004 0.028 18.900 6.400 0.150 9 Disclosure example GMAW 0.590 0.538 35.000 0.002 0.036 11.500 7.400 0.400 A2 Comparative example GMAW 0.090 0.375 1.250 0.004 0.016 2.000 6.300 6.900

TABLE-US-00008 TABLE 3-B Chemical component of entire wire (% by mass) (balance is Fe and impurities) No. Classification Co Pb Sn W Mg Al Ca Ti B REM Zr N 4 Disclosure example 0.350 0.660 0.385 0.090 0.321 5 Disclosure example 0.760 5.800 3.000 0.040 0.073 6 Disclosure example 0.900 0.077 0.001 0.012 7 Disclosure example 0.060 0.026 0.114 0.015 8 Disclosure example 0.970 9.400 0.037 0.092 0.015 9 Disclosure example 10.200 0.401 0.007 A2 Comparative example 0.190 9.600 0.047 0.180 0.200 0.110

TABLE-US-00009 TABLE 3-C Components of flux No. Classification TiO.sub.2 SiO.sub.2 Al.sub.2O.sub.3 MgO Na.sub.2O K.sub.2O CaF.sub.2 4 Disclosure example 5.0 1.0 0.1 0.1 0.1 5 Disclosure example 0.1 7.5 6 Disclosure example 5.0 1.0 0.1 0.1 0.1 7 Disclosure example 0.1 7.5 8 Disclosure example 5.0 1.0 0.1 0.1 0.1 9 Disclosure example 0.1 7.5 A2 Comparative example 5.0 1.0 0.1 0.1 0.1

TABLE-US-00010 TABLE 4-A Wire Welding Chemical component of wire (% by mass) (balance is Fe and impurities) No. Classification method C Si Mn P S Cu Ni Cr Mo Nb V 10 Disclosure example SAW 0.864 0.480 37.350 0.003 0.047 26.280 7.800 10.890 0.650 11 Disclosure example SAW 0.468 0.345 40.950 0.001 0.005 21.360 5.160 0.422 12 Disclosure example SAW 0.516 0.375 18.750 0.001 0.011 15.360 2.520 0.034 13 Disclosure example SAW 1.140 0.195 7.500 0.002 0.001 26.280 8.640 0.360 0.166 0.840 14 Disclosure example SAW 0.156 0.180 41.100 0.004 0.058 3.960 3.240 2.640 0.703 0.996 16 Disclosure example SAW 0.240 0.300 6.750 0.001 0.010 18.000 6.000 6.000 0.144 17 Disclosure example SAW 0.240 0.300 6.750 0.001 0.010 18.000 6.000 6.000 0.144 A3 Comparative example SAW 0.108 0.285 52.500 0.003 0.035 6.960 8.760 1.068 A5 Comparative example SAW 0.612 0.435 43.500 0.004 0.012 1.560 0.600 0.150

TABLE-US-00011 TABLE 4-B Wire Chemical component of wire (% by mass) (balance is Fe and impurities) No. Classification Co Pb Sn W Mg Al Ca Ti B REM Zr N 10 Disclosure example 12.120 2.880 0.373 0.131 11 Disclosure example 0.960 0.492 3.000 0.090 12 Disclosure example 0.012 3.600 0.010 13 Disclosure example 10.080 0.228 0.108 0.017 14 Disclosure example 12.000 0.053 0.068 0.106 0.020 16 Disclosure example 0.025 17 Disclosure example 0.025 A3 Comparative example 6.960 0.010 A5 Comparative example 0.385

TABLE-US-00012 TABLE 5 Current Voltage Speed Heat input Welding method A V mm/mm kJ/mm Shielded metal arc welding 140 22 160 1.2 (SMAW) Flux-cored wire (GMAW) 200 31 350 1.1 Submerged arc welding (SAW) 360 30 350 1.9

TABLE-US-00013 TABLE 6 No. Classification Toughness in low-temperature 1 Disclosure example Passed 2 Disclosure example Excellent 3 Disclosure example Passed 4 Disclosure example Passed 5 Disclosure example Excellent 6 Disclosure example Passed 7 Disclosure example Excellent 8 Disclosure example Passed 9 Disclosure example Excellent 10 Disclosure example Excellent 11 Disclosure example Excellent 12 Disclosure example Passed 13 Disclosure example Passed 14 Disclosure example Excellent 15 Disclosure example Excellent 16 Disclosure example Passed 17 Disclosure example Passed A1 Comparative example Failed A2 Comparative example Failed A3 Comparative example Failed A4 Comparative example Failed A5 Comparative example Failed

[0272] It can be seen that the weld metal of the disclosure examples have high toughness in low-temperature.

[0273] However, comparative examples did not satisfy any of the requirements specified in the disclosure, and therefore failed in the toughness in low-temperature.