HOLE ASSISTED OPTICAL FIBER

Abstract

An object of the present invention is to provide an HAF having a structure in which the number of air holes is decreased to be smaller than that of a PCF and Rayleigh scattering loss may be more reduced than that in the existing HAF. The HAF according to the present invention includes a core portion having a uniform optical refractive index; a cladding portion having a uniform optical refractive index and surrounding the core portion; and a plurality of air holes arranged in two layers at positions configuring hexagonal closest packing excluding the core portion within the cladding portion along a longitudinal direction of the hole-assisted fiber, wherein a center-to-center spacing of the air holes is a sum of a radius Rin of an inscribed circle inscribed in the air holes in an inner layer and a radius d/2 of the air hole, and a radius “a” of the core portion and a relative refractive index difference Δ between the core portion and the cladding portion are present within a range where Rn, which is a ratio of a Rayleigh scattering coefficient Rsmf of a single mode optical fiber and an effective Rayleigh scattering coefficient Reff of the hole-assisted fiber, is equal to or less than 0.92.

Claims

1. A hole-assisted fiber comprising: a core portion having a uniform optical refractive index; a cladding portion having a uniform optical refractive index and surrounding the core portion; and a plurality of air holes arranged at positions excluding the core portion within the cladding portion along a longitudinal direction of the hole-assisted fiber, wherein a center-to-center spacing between the plurality of air holes is a sum of a radius Rin of an inscribed circle inscribed to air holes of the plurality of air holes in an inner layer and a radius d/2 of an air hole of the plurality of air holes, and a radius “a” of the core portion and a relative refractive index difference Δ between the core portion and the cladding portion are present within a range where Rn, which is a ratio of a Rayleigh scattering coefficient Rsmf of a single mode optical fiber and an effective Rayleigh scattering coefficient Reff of the hole-assisted fiber, is equal to or less than 0.92.

2. The hole-assisted fiber according to claim 1, wherein a mode field diameter 2w of a fundamental mode at a wavelength of 1310 nm ranges from 7.8 μm to 9.2 μm, or from 9.3 μm to 11.7 μm.

3. The hole-assisted fiber according to claim 1, wherein Rin/a is equal to or greater than three.

4. The hole-assisted fiber according to claim 1, wherein in a cross-section of the hole-assisted fiber, an air hole occupancy ratio S, which is a ratio of an area of all of the air holes in the inner layer and the air holes in the outer layer to an area of a ring-shaped region that is formed by the inscribed circle and a circumscribed circle with a radius Rout circumscribing the air holes of the plurality of air holes in an outer layer, is represented by an expression of 0.001×exp(Rin/a/1.66)+0.19≤S≤−9.60×exp(−Rin/a/0.65)+0.30.

5. The hole-assisted fiber according to claim 1, wherein in a case where a reference optical fiber in which the plurality of air holes are not present and a structure other than the air holes is identical to the structure of the hole-assisted fiber is assumed, a mode field diameter of the hole-assisted fiber is 84% or more as large as a mode field diameter of the reference optical fiber, and the mode field diameter of the reference optical fiber ranges from 10.3 to 12.0 in a case where a V value of the reference optical fiber ranges from 1.25 to 1.76, or the mode field diameter of the reference optical fiber ranges from 12.3 to 13.6 in a case where the V value of the reference optical fiber ranges from 1.17 to 1.32.

6. The hole-assisted fiber according to claim 1, wherein the plurality of air holes are arranged in two layers at positions configuring hexagonal closest packing.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0026] FIG. 1 is a diagram for explaining a structure of a hole-assisted fiber according to the present invention.

[0027] FIG. 2 is a diagram for explaining characteristics of a hole-assisted fiber according to the present invention.

[0028] FIG. 3 is a diagram for explaining characteristics of a hole-assisted fiber according to the present invention.

[0029] FIG. 4 is a diagram for explaining characteristics of a hole-assisted fiber according to the present invention.

[0030] FIG. 5 is a diagram for explaining characteristics of a hole-assisted fiber according to the present invention.

[0031] FIG. 6 is a diagram for explaining a method for designing a hole-assisted fiber according to the present invention.

DESCRIPTION OF EMBODIMENTS

[0032] Embodiments of the present invention will be described with reference to the accompanying drawings. The embodiments described below are examples of the present invention and the present invention is not limited to the embodiments described below. Note that constituent elements with the same reference signs in the specification and the drawings are assumed to be the same constituent elements.

[0033] FIG. 1 is a diagram for explaining a cross-sectional structure of an HAF of the present embodiment. The HAF includes a core portion 11 having a uniform optical refractive index; a cladding portion 12 having a uniform optical refractive index and surrounding the core portion 11; and a plurality of air holes 13 arranged in two layers at positions configuring hexagonal closest packing excluding the core portion 11 within the cladding portion 12 along a longitudinal direction of the optical fiber.

Note that in the present specification, a case is described in which the air holes are arranged at the positions configuring hexagonal closest packing, but the air holes may be arranged differently as long as the air holes are arranged within a range of an air hole occupancy ratio S to be described below.

[0034] The core portion 11 is located in the center of the HAF and has a radius “a”. In the cladding portion 12, N air holes 13 each having a diameter d are arranged in two layers in a hexagonal closest structure (one cell structure) excluding the core portion 11. N is equal to 18 in the present example, where six air holes 13 are arranged in an inner layer while 12 air holes 13 are arranged in an outer layer. An air hole occupancy ratio S in a region obtained by excluding an inscribed circle C1 of the air holes 13 in the inner layer from a circumscribed circle C2 of the air holes 13 in the outer layer is represented by Equation 1.

S=N×(d/2){circumflex over ( )}2/(Rout{circumflex over ( )}2−Rin{circumflex over ( )}2)  [Equation 1]

Note that Rin is the radius of the inscribed circle C1 and Rout is the radius of the circumscribed circle C2.

[0035] A center-to-center spacing t of the air holes 13 is a sum of a radius Rin of the inscribed circle C1 inscribed with respect to the air holes 13 in the inner layer and a radius d/2 of the air hole 13.

t=Rin+d/2  [Equation 2]

[0036] In the HAF, the radius a of the core portion and a relative refractive index difference Δ between the core portion and the cladding portion are present within a range where Rn, which is a ratio of a Rayleigh scattering coefficient Rsmf of a single mode optical fiber and an effective Rayleigh scattering coefficient Reff of the hole-assisted fiber, is equal to or less than 0.92. To determine the core radius a of the HAF and the relative refractive index difference Δ between the core portion 11 and cladding portion 12, graphs in FIGS. 2 to 4 are used.

[0037] FIG. 2 is a diagram illustrating a relationship of the air hole occupancy ratio S, a mode field diameter 2w at a wavelength of 1310 nm, and a normalized Rayleigh scattering coefficient Rn. A procedure of obtaining the graph in FIG. 2 is described below. First, while varying core parameters in FIG. 1 (the radius a and the relative refractive index difference Δ) in a range of 1.5<a<5 (μm) and 0.1<Δ<0.4 and also varying air hole parameters (the radius Rin of the inscribed circle C1 and the air hole occupancy ratio S) in a range of 3<Rin<65 (mm) and 0.1<S<0.4, cutoff wavelengths, bending loss, and confinement loss of all combinations of the parameters are calculated (see NPL 5, in which a method for calculating the mode field diameter (2w), cutoff wavelength, bending loss, and confinement loss with four parameters (a, Δ, Rin, and S) is described).

[0038] Subsequently, the calculated cutoff wavelengths, bending loss, and confinement loss are compared with each requirement described below to extract a parameter group PG satisfying all of the requirements from all the parameters, and the extracted parameter group PG is plotted on a graph where the horizontal axis represents the air hole occupancy ratio S while the vertical axis represents the mode field diameter 2w.

[0039] The requirements are as follows.

(1) Cutoff wavelength: bending loss of a first high order mode of a 1260 nm wavelength is 1 dB/m or more when a bending radius is 140 mm.
(This requirement is set to allow the propagation of a fundamental mode of the 1260 nm wavelength)
(2) Bending loss: bending loss of a fundamental mode of a 1625 nm wavelength at a bending radius R of 30 mm is 0.5 dB/100 turns or less.
(3) Confinement loss: confinement loss is 1×10.sup.−6 dB/m or less at a 1550 nm wavelength (fundamental mode).

[0040] Furthermore, for each parameter included in the parameter group PG, the effective Rayleigh scattering coefficient Reff is calculated from an electric field amount applied to the core portion using the mode field diameter 2w when the air holes are given. Note that the electric field amount applied to the core portion is determined from the structure and the wavelength. The calculation method uses an equation described below in which a calculation equation for the Rayleigh scattering coefficient that depends on the dopant concentration described in NPL 4 is multiplied by the electric field amount applied to the core portion.

Reff=0.8+0.50[GeO.sub.2]−0.50[GeO.sub.2]exp(2a.sup.2/(MFD/2){circumflex over ( )}.sup.2)  [Equation 3]

Note that [GeO.sub.2] means Δ of the dopant concentration.
Then, the normalized Rayleigh scattering coefficient Rn for each parameter is calculated by an equation of Rn=Reff/Rsmf from the calculated effective Rayleigh scattering coefficient Reff and the Rayleigh scattering coefficient Rsmf (equals to 0.89) of a single mode fiber (SMF) such as G.652B, 652D or the like of ITU-T. The calculated normalized Rayleigh scattering coefficient Rn is displayed on the parameter group PG. The procedure of obtaining the graph in FIG. 2 has been described above.

[0041] Note that the normalized Rayleigh scattering coefficient Rn has the following meanings. When the Rayleigh scattering loss can be reduced by 0.02 dB/km compared to the SMF at a wavelength of 1310 nm. Rn is equal to 0.92. Note that Rn of pure quartz glass is 0.85.

[0042] Even when dopant is contained as in an HAF, a low loss property may be achieved with a structure capable of making the Rn approach 0.85. Accordingly, in the present embodiment, it is intended to find a structure in which the normalized Rayleigh scattering coefficient Rn is 0.92 or less. Then, it may be understood from FIG. 2 that there exist parameters that bring a relation of Rn≤0.92 in a region where the air hole occupancy ratio S is greater than or equal to 0.2 and the mode field diameter 2w is 9.6 to 11.7 μm, and in a region where the air hole occupancy ratio S is greater than or equal to 0.25 and the mode field diameter 2w is 7.8 to 9.2 μm.

[0043] FIG. 3 is a diagram for explaining a lower limit of Rin/a in a low Rn region. For each parameter included in the parameter group PG, 2w/MFD is calculated and plotted on a graph where the horizontal axis represents Rin/a while the vertical axis represents 2w/MFD. Note that the “low Rn region” refers to a region of Rn≤0.92. In a case of being 0.92 or less compared to the Rayleigh scattering coefficient of the SMF, it is possible to reduce the transmission loss at a wavelength of 1550 nm by 0.02 dB/km or more.

[0044] Here, Rin/a is a parameter that directly determines an effect of the air holes on MFD (for example, see NPL 5). For example, when Rin/a becomes smaller, 2w is reduced and the effect of the increase in loss due to unevenness of the air hole interface becomes apparent. In addition, “2w” represents the mode field diameter of the present HAF, and “MFD” represents the mode field diameter of a “reference optical fiber” with no air hole 13 in the structure illustrated in FIG. 1. In other words, “2w/MFD” refers to a mode field diameter reduction rate when the air holes 13 are given to the reference optical fiber.

[0045] From FIG. 2, it may be understood that each parameter included in the parameter group PG is present within a region of Rin/a≥3 and 2w/MFD≥0.84.

[0046] FIG. 4 is a diagram for explaining a v value in the low Rn region. The wavelength is 1310 nm. The horizontal axis represents the v value of the reference optical fiber while the vertical axis represents the mode field diameter MFD of the reference optical fiber. A relationship between the v value of the reference optical fiber (step type optical fiber) and the mode field diameter MFD may be represented by Equation 4. Equation 4 is an empirical equation described in NPL 5.

MFD/2=a×(0.65+1.619v{circumflex over ( )}−1.5+2.879v{circumflex over ( )}−6)  [Equation 4]

The v value is determined by the core radius a, a refractive index n.sub.1 of the core portion, and the relative refractive index difference Δ.

v=(2πan1√(2Δ))/λ  [Equation 5]

[0047] FIG. 4 is a graph in which the v value and the MFD are calculated and plotted using Equation 3 and Equation 4 for each parameter included in the parameter group PG. From FIG. 4, the following may be recognized. There are two parameter groups; one of them is a parameter group in which the MFD becomes 10.3 to 12.0 when the v value of the reference optical fiber is 1.25 to 1.76, and the other one is a parameter group in which the MFD becomes 12.3 to 13.6 when the v value is 1.17 to 1.32.

[0048] FIG. 6 is a flowchart illustrating a design method for determining the structure of an HAF. The design method determines a core radius “a” and a relative refractive index difference Δ of the HAF by using FIGS. 2 to 4.

[0049] First, for specifications of the HAF, a normalized Rayleigh scattering coefficient Rn and a mode field diameter 2w are determined (step S01). Rn is approximately 0.92, and 2w is determined from a connection target device or the like of the HAF.

[0050] Subsequently, a range of an air hole occupancy ratio S satisfying the Rn and 2w is detected from FIG. 2 (step S02).

[0051] Then, any parameter is selected from the parameters included in the range of the S, and Rin/a and 2w/MFD are detected from FIG. 3 (step S03).

[0052] The MFD is calculated from the detected 2w/MFD and the 2w determined in step S01 (step S04), and a v value corresponding to the MFD is detected from FIG. 4 (step S05).

[0053] The MFD and the v value are substituted into Equation 4 to calculate the core radius a (step S06). Furthermore, the calculated core radius a, the v value, a desired wavelength λ (equals to 1310 nm), and a refractive index n.sub.2 of the cladding portion (1.455, which is a refractive index of quartz) is substituted into Equation 5 to calculate the relative refractive index difference Δ (step S07).

[0054] A specific design example will be described below.

Example 1

[0055] It is considered to design an HAF with low Rayleigh scattering loss capable of propagating single mode light at a wavelength of 1260 nm to 1625 nm. The HAF structure is the same as that in FIG. 1. The design is carried out in such a manner that Rn is 0.92 or less, and 2w is 11 μm at a 1310 nm wavelength.

[0056] From FIG. 2, a relationship of (S, 2w, Rn)=(0.2, 11, 0.92) may be selected. Under this condition, from FIG. 3, a relationship of Rin/a=3.3 is selected to suppress the effect of the loss increase due to unevenness of the air hole interface, and a relationship of 2w/MFD=0.95 is selected to suppress the reduction rate to be 5% from the MFD accompanying the provision of the air holes. At this point of time, air hole parameters (Rin/a and S) may be determined. At this time, from 2w and 2w/MFD, the MFD is 11.5 when there is no air hole (reference optical fiber). From FIG. 4, the v value that satisfies this condition is 1.76. A combination of the core radius a and the relative refractive index difference Δ that satisfies the MFD and v value may be calculated by Equation 4 and Equation 5, and core parameters may be determined to have a relationship of (a, Δ)=(4, 0.2). By designing in the manner described above, an HAF capable of reducing Rn to 0.92 may be designed.

Example 2

[0057] It is considered to design an HAF with low Rayleigh scattering loss capable of propagating single mode light at a wavelength of 1260 nm to 1625 nm. The HAF structure is the same as that in FIG. 1. The design is carried out in such a manner that Rn is 0.92 or less, and 2w is 8.9 μm at a 1310 nm wavelength.

[0058] From FIG. 2, a relationship of (S, 2w, Rn)=(0.25, 8.9, 0.92) may be selected. Under this condition, from FIG. 3, a relationship of Rin/a=4.5 is selected to suppress the effect of the loss increase due to the unevenness of the air hole interface, and a relationship of 2w/MFD=0.86 is selected to suppress the reduction rate to be 14% from the MFD accompanying the provision of the air holes. At this point of time, air hole parameters (Rin/a and S) may be determined. At this time, from 2w and 2w/MFD, the MFD is 10.3 when there is no air hole (reference optical fiber). From FIG. 4, the v value that satisfies this condition is 1.25. A combination of the core radius a and the relative refractive index difference Δ that satisfies the above MFD and v value may be calculated by Equation 3 and Equation 4, and core parameters may be determined to have a relationship of (a, Δ)=(2, 0.4). By designing in the manner described above, the HAF capable of reducing Rn to 0.92 may be designed.

Example 3

[0059] It is considered to design an HAF with low Rayleigh scattering loss capable of propagating single mode light at a wavelength of 1260 nm to 1625 nm. The HAF structure is the same as that in FIG. 1. The design is carried out in such a manner that Rn is 0.89 or less, and MFD is 11.7 μm at a 1310 nm wavelength.

[0060] From FIG. 2, a relationship of (S, 2w, Rn)=(0.25, 11.7, 0.89) may be selected. Under this condition, from FIG. 3, a relationship of Rin/a=4 is selected to suppress the effect of the loss increase due to the unevenness of the air hole interface, and a relationship of 2w/MFD=0.86 is selected to suppress the reduction rate to be 14% from the MFD accompanying the provision of the air holes. At this point of time, air hole parameters (Rin/a and S) may be determined. At this time, from 2w and 2w/MFD, the MFD is 13.6 when there is no air hole (reference optical fiber). From FIG. 4, the v value that satisfies this condition is 1.32. A combination of the core radius a and the relative refractive index difference Δ that satisfies the MFD and v value may be calculated by Equation 3 and Equation 4, and core parameters may be determined to have a relationship of (a, Δ)=(3, 0.2). By designing in the manner described above, the HAF capable of reducing Rn to 0.89 may be designed.

[0061] An HAF of Rn≤0.92 may be designed from the parameter group PG as in Example 1 to Example 3. FIG. 5 is a graph on which the above-discussed Rin/a and S of the HAF are plotted. From FIG. 5, it may be understood that the HAF of Rn≤0.92 is present in a range surrounded by a curved line A and a curved line B. Thus, in a case of an HAF of the structure having the air hole occupancy ratio S, core radius a, and inscribed circle Rin of the air holes that are plotted in the range surrounded by the curved line A and the curved line B, it is possible to achieve a relation of Rn≤0.92 even in the HAF in which 10 air holes are arranged in a ring shape in such a manner that, for example, the number of air holes in the first layer is 10 and the number of air holes in the second layer is 10, regardless of the hexagonal closest structure.

Curved line A: −9.60×exp(−Rin/a/0.65)+0.30

Curved line B: 0.001×exp(Rin/a/1.66)+0.19

Effects of the Invention

[0062] The present invention provides an HAF structure where Rayleigh scattering loss is low over a wide wavelength region and the number of air holes is reduced to enhance manufacturability. In the present invention, a hybrid structure of the existing HAF and PCF is used. By at least one of a reduction in the core radius of the existing HAF (a reduced core) and a reduction in the relative refractive index difference Δ of the core (a reduced Δ), the Rayleigh scattering loss by the core is suppressed. In order to suppress increases in the confinement loss, bending loss, and the like of the optical fiber due to the reduced core and reduced Δ of the HAF, air holes are arranged in two layers.

[0063] In other words, the present invention intends to provide a core to suppress the increase in loss due to the impurities entering into the inner surface during the production, the unevenness, or the like, which is a problem of the existing PCF, and intends to achieve the reduced core or reduced Δ to suppress Rayleigh scattering loss derived from the core, which is a problem of the HAF.

[0064] As for the increase in loss due to the impurities entering into the inner surface during the production, the unevenness, or the like, which is a problem of the PCF, achieving the reduced core or reduced Δ makes it possible to confine the light with both the core and a small number of air holes, so that it is possible to enhance the manufacturability by suppressing the increase in loss during the production and reducing the number of air holes.

[0065] Rin/a, which is expressed by using the radius Rin of the air hole inscribed circle and the core radius a, is a parameter that directly determines the effect of the air holes on the MFD (NPL 5), and when Rin/a decreases, the effect of the loss increase by the air hole interface becomes noticeable in addition to the MFD reduction. In the present invention, by using the hybrid structure of the existing HAF and PCF, there is provided an HAF structure where Rayleigh scattering loss is low over a wide wavelength region, and the number of air holes is reduced to enhance the manufacturability. In the HAF of the present invention, Rin/a expressed by using the radius Rin of the inscribed circle C1 and the core radius a is three or greater, and the reduction rate of the MFD accompanying the provision of the air holes is at least 84%.

INDUSTRIAL APPLICABILITY

[0066] The HAF of the present invention may be applied to optical fibers for communication that utilize a wavelength division multiplexing (WDM) technique using a large number of multiple pieces of signal light having different wavelengths, a multi-level modulation technique, and the like.