PREPARATION METHOD FOR INSTANTLY-PASTED PAINT NAILS

Abstract

The invention belongs to the technical field of manicure, and discloses a preparation method for instantly-pasted paint nails. The method specifically includes applying a Acrylic Powder glue on a plastic fake nail piece and curing to form a Acrylic Powder layer, using an ink to print a preset pattern layer on the Acrylic Powder layer, and applying a brightening glue on the pattern layer and curing to form a brightening layer, so as to obtain the instantly-pasted paint nails. Through fine process steps and material selection, the invention can effectively improve the thickness and transparency of paint nails.

Claims

1. A preparation method for instantly-pasted paint nails, comprising steps of: step one, applying 1-3 layers of Acrylic Powder glue on a clean plastic fake nail piece and curing at 20-25 C. for 5-6 minutes to form a Acrylic Powder layer of 0.1-0.3 mm, wherein the Acrylic Powder glue comprises a Acrylic Powder and a methyl methacrylate liquid with a mass volume ratio of 1 (g): 1 (mL); step two, using an ink to print a preset pattern layer on the Acrylic Powder layer of the step one; step three, applying a brightening glue on the pattern layer of the step two and curing with a UV curing lamp for 120 seconds to form a brightening layer, so as to prepare the instantly-pasted paint nail, wherein a thickness for applying is 0.1-0.4 mm.

2. The preparation method for instantly-pasted paint nails according to claim 1, wherein a particle size of the Acrylic Powder in the step one is 1-20 m.

3. The preparation method for instantly-pasted paint nails according to claim 1, wherein a roughness of the Acrylic Powder in the step one is 300-500 mesh.

4. The preparation method for instantly-pasted paint nails according to claim 1, wherein a method for applying in the step one comprises brushing or spraying.

5. The preparation method for instantly-pasted paint nails according to claim 1, wherein the Acrylic Powder in the step one comprises a mixture of a color powder, a shimmering powder and a transparent Acrylic resin powder.

6. The preparation method for instantly-pasted paint nails according to claim 5, wherein a mass ratio of the color powder, the simmering powder and the transparent acrylic resin powder is 2:2:6.

7. The preparation method for instantly-pasted paint nails according to claim 1, wherein in the step three, the brightening glue comprises a resin and a photoinitiator.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0016] The drawings described herein are intended to provide a further understanding of the invention, and are intended to be a part of this invention. The schematic embodiments of this invention and their descriptions are used to interpret this invention and do not constitute an undue limitation of this invention. In the drawings:

[0017] FIG. 1 is a plastic fake nail piece of the invention;

[0018] FIG. 2 shows the step one of forming a Acrylic Powder layer of the plastic fake nail piece according to the invention;

[0019] FIG. 3 shows instantly-pasted paint nails completed by the step three according to the invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0020] In order to make the purpose, technical solutions and advantages of the invention clearer, the technical solutions of the invention will be clearly and completely described below with reference to specific embodiments of the invention and corresponding drawings. Obviously, the described embodiments are only a part of the embodiments of the present invention, but not the whole. Based on the embodiments of the invention, all other embodiments obtained by a person skilled in the art without involving any inventive effort are within the scope of the invention.

Embodiment 1

[0021] A preparation method for instantly-pasted paint nails includes the following steps.

[0022] Step one, 2 layers of Acrylic Powder glue are applied on a clean plastic fake nail piece as shown in FIG. 1 and cured at 23 C. for 5 minutes to form a Acrylic Powder layer of 0.2 mm as shown in FIG. 2, wherein the Acrylic Powder glue includes a Acrylic Powder of 1000 g and a methyl methacrylate liquid of 1000 mL.

[0023] Step two, an ink is used to print a preset pattern layer on the Acrylic Powder layer of the step one.

[0024] Step three, a brightening glue is applied on the pattern layer of the step two and cured with a UV curing lamp for 120 seconds to form a brightening layer, so as to prepare the instantly-pasted paint nail as shown in FIG. 3, wherein a thickness for applying is 0.3 mm.

[0025] Further, a particle size of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 10 m.

[0026] Further, a roughness of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 400 mesh.

[0027] Further, a method for applying in the step one of the preparation method for instantly-pasted paint nails according to the embodiment includes brushing or spraying.

[0028] Further, the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the invention includes a mixture of a color powder, a shimmering powder and a transparent Acrylic resin powder.

[0029] Preferably, a mass ratio of the color powder, the simmering powder and the transparent acrylic resin powder of the preparation method for instantly-pasted paint nails according to the embodiment is 2:2:6.

[0030] Further, in the step three of the preparation method for instantly-pasted paint nails according to the embodiment, the brightening glue includes a resin and a photoinitiator.

[0031] The instantly-pasted paint nails are tested for adhesion using a hundred-grid adhesive pull test. An adhesion level of the instantly-pasted paint nail according to the method of the embodiment is level 5.

Embodiment 2

[0032] A preparation method for instantly-pasted paint nails includes the following steps.

[0033] Step one, 1 layer of Acrylic Powder glue are applied on a clean plastic fake nail piece as shown in FIG. 1 and cured at 20 C. for 6 minutes to form a Acrylic Powder layer of 0.3 mm as shown in FIG. 2, wherein the Acrylic Powder glue includes a Acrylic Powder of 1000 g and a methyl methacrylate liquid of 1000 mL.

[0034] Step two, an ink is used to print a preset pattern layer on the Acrylic Powder layer of the step one.

[0035] Step three, a brightening glue is applied on the pattern layer of the step two and cured with a UV curing lamp for 120 seconds to form a brightening layer, so as to prepare the instantly-pasted paint nail as shown in FIG. 3, wherein a thickness for applying is 0.2 mm.

[0036] Further, a particle size of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 1 m.

[0037] Further, a roughness of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 300 mesh.

[0038] Further, a method for applying in the step one of the preparation method for instantly-pasted paint nails according to the embodiment includes brushing or spraying.

[0039] Further, the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the invention includes a mixture of a color powder, a shimmering powder and a transparent Acrylic resin powder.

[0040] Preferably, a mass ratio of the color powder, the simmering powder and the transparent acrylic resin powder of the preparation method for instantly-pasted paint nails according to the embodiment is 2:2:6.

[0041] Further, in the step three of the preparation method for instantly-pasted paint nails according to the embodiment, the brightening glue includes a resin and a photoinitiator.

[0042] The instantly-pasted paint nails are tested for adhesion using a hundred-grid adhesive pull test. An adhesion level of the instantly-pasted paint nail according to the method of the embodiment is level 5.

Embodiment 3

[0043] A preparation method for instantly-pasted paint nails includes the following steps.

[0044] Step one, 3 layers of Acrylic Powder glue are applied on a clean plastic fake nail piece as shown in FIG. 1 and cured at 20-25 C. for 6 minutes to form a Acrylic Powder layer of 0.1 mm as shown in FIG. 2, wherein the Acrylic Powder glue includes a Acrylic Powder of 1000 g and a methyl methacrylate liquid of 1000 mL.

[0045] Step two, an ink is used to print a preset pattern layer on the Acrylic Powder layer of the step one.

[0046] Step three, a brightening glue is applied on the pattern layer of the step two and cured with a UV curing lamp for 120 seconds to form a brightening layer, so as to prepare the instantly-pasted paint nail as shown in FIG. 3, wherein a thickness for applying is 0.4 mm.

[0047] Further, a particle size of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 20 m.

[0048] Further, a roughness of the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the embodiment is 500 mesh.

[0049] Further, a method for applying in the step one of the preparation method for instantly-pasted paint nails according to the embodiment includes brushing or spraying.

[0050] Further, the Acrylic Powder in the step one of the preparation method for instantly-pasted paint nails according to the invention includes a mixture of a color powder, a shimmering powder and a transparent Acrylic resin powder.

[0051] Preferably, a mass ratio of the color powder, the simmering powder and the transparent acrylic resin powder of the preparation method for instantly-pasted paint nails according to the embodiment is 2:2:6.

[0052] Further, in the step three of the preparation method for instantly-pasted paint nails according to the embodiment, the brightening glue includes a resin and a photoinitiator.

[0053] The instantly-pasted paint nails are tested for adhesion using a hundred-grid adhesive pull test. An adhesion level of the instantly-pasted paint nail according to the method of the embodiment is level 5.

[0054] The above is embodiments of the invention and is not intended to limit the invention. Various changes and modifications may be made to the present invention by those skilled in the art. Any modifications, equivalent substitutions, improvements and the like within the spirit and principles of the present invention are all intended to be included within the scope of the claims of the present invention.