Additive composition as a combustion improver for liquid and gaseous fuels

Abstract

This invention is related to an additive composition comprising metal-based quantum clusters (QCs) dispersed in a hydrocarbon medium. The additive composition is useful as a fuel additive, as it acts as a combustion improver for liquid and gaseous fuels. The invention describes a process for the synthesis of the additive composition comprising metal-based materials in atomic cluster form in hydrocarbon dispersible medium. The stable liquid dispersion of the QC has been doped into the hydrocarbon fuels at required concentrations. The measurable flame temperature of the fuels, e.g., commercial LPG on burner has been observed to increase by at least 60-80° C. The flame with high heat through put can be used for efficient cooking, heating, annealing and other high thermal applications. The additive composition may also be used to improve the fuel economy of the liquid hydrocarbon fuels.

Claims

1. An additive composition comprising: (a) 1-8 wt. % of metal-based quantum clusters (QCs) comprising: (i) an organic oxyacid salt or a mixture of salts of an organic oxyacid; and (ii) a metal salt, wherein at least five mole proportions of the salt or the mixture of salts of the organic oxyacid are required per mole of the metal salt; and (b) 92-99 wt. % of a hydrocarbon medium, wherein the metal-based quantum clusters (QCs) are dispersed in the hydrocarbon medium, wherein the additive composition is effective for improving combustion of a fuel.

2. The additive composition as claimed in claim 1, wherein the organic oxyacid is selected from a group consisting of carboxylic acid, organic sulfuric acid, sulfonic acid, phosphoric acid, or phosphonic acid.

3. The additive composition as claimed in claim 2, wherein acidity of the organic oxyacid ranges from 1-5 pKa.

4. The additive composition as claimed in claim 1, wherein the metal salt comprises a nitrate salt, a chloride salt, or a sulfate salt of a metal, and the metal is selected from the group consisting of cerium, iron, nickel, cobalt, manganese, zinc, and copper.

5. The additive composition as claimed in claim 1, wherein the hydrocarbon medium is a non-reacting medium, and wherein the hydrocarbon medium comprises an oil phase.

6. The additive composition as claimed in claim 5, wherein the hydrocarbon medium comprises pentane, isopentane, hexane, or heptane.

7. The additive composition as claimed in claim 1, wherein a size of the metal-based quantum clusters (QCs) ranges from 0.1-5 nanometer (nm).

8. The additive composition A fuel composition comprising the additive composition as claimed in claim 1, wherein the fuel comprises liquid and gaseous fuels.

9. The fuel composition as claimed in claim 8, wherein the fuel is doped with the additive composition in a concentration of 1-200 ppm of the fuel composition.

10. The fuel composition as claimed in claim 9, wherein the additive composition is present in the fuel in a form of dispersion or suspension.

11. A process for synthesis of the additive composition as claimed in claim 1, the process comprising: (a) preparing the salt or the mixture of salts of the organic oxyacid; (b) adding the hydrocarbon medium to the salt or the mixture of salts of the organic oxyacid to form a reaction mixture, wherein the hydrocarbon medium comprises an oil phase; (c) heating the reaction mixture to a temperature range of 25-80° C.; (d) adding the metal salt dissolved in water to the reaction mixture and continuing heating the reaction mixture for a period of 1-4 hours; and (e) recovering a product containing the oil phase and washing with water followed by filtration to obtain the additive composition.

12. The process as claimed in claim 11, wherein in step (a) the salt or the mixture of salts of the organic oxyacid is prepared in-situ by reacting the organic oxyacid with an oxide, hydroxide, hydrogen carbonate or carbonate of an alkali metal or an alkaline earth metal.

13. The additive composition as claimed in claim 1, wherein the quantum clusters (QCs) are free of any agglomeration.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 discloses X-ray powder diffraction (XRD) diffraction pattern of synthesized ceria after heat treatment at 350° C.

(2) FIG. 2 discloses ultraviolet-visible (UV-vis) spectra of ceria-based quantum clusters (QC) synthesized in different solvent.

(3) FIG. 3 discloses Fourier transform infrared spectroscopy (FTIR) spectra of Ceria quantum clusters (QC) synthesized in (a) Hexane; (b) Pentane; (c) Bharat Stage IV (BSIV) Diesel and (d) (Bharat Stage VI) BSVI Diesel

(4) FIG. 4 discloses particle size distribution of ceria-based quantum cluster in organic solvent.

(5) FIG. 5 discloses D50 and D90 plot of ceria-based quantum cluster in organic solvent.

(6) FIG. 6 discloses transmission electron microscopy (TEM) image of ceria quantum cluster

(7) FIG. 7 discloses particle size distribution of iron-based quantum cluster in organic solvent

(8) FIG. 8 discloses D50 and D90 plot of iron-based quantum cluster in organic solvent

DETAILED DESCRIPTION OF THE INVENTION

(9) Those skilled in the art will be aware that the present disclosure is subject to variations and modifications other than those specifically described. It is to be understood that the present disclosure includes all such variations and modifications. The disclosure also includes all such steps of the process, features of the system, referred to or indicated in this specification, individually or collectively and all combinations of any or more of such steps or features.

Definitions

(10) For convenience, before further description of the present disclosure, certain terms employed in the specification, and examples are collected here. These definitions should be read in the light of the remainder of the disclosure and understood as by a person of skill in the art. The terms used herein have their meanings recognized and known to those of skill in the art, however, for convenience and completeness, particular terms and their meanings are set forth below.

(11) The articles “a”, “an” and “the” are used to refer to one or to more than one (i.e., to at least one) of the grammatical object of the article.

(12) The terms “comprise” and “comprising” are used in the inclusive, open sense, meaning that additional elements may be included. It is not intended to be construed as “consists of only”.

(13) Throughout this specification, unless the context requires otherwise the word “comprise”, and variations such as “comprises” and “comprising”, will be understood to imply the inclusion of a stated element or step or group of element or steps but not the exclusion of any other element or step or group of element or steps.

(14) The term “including” is used to mean “including but not limited to”. “Including” and “including but not limited to” are used interchangeably.

(15) Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the disclosure, the preferred methods, and materials are now described. All publications mentioned herein are incorporated herein by reference.

(16) The present disclosure is not to be limited in scope by the specific embodiments described herein, which are intended for the purposes of exemplification only. Functionally equivalent products and processes are clearly within the scope of the disclosure, as described herein.

(17) The present invention relates to an additive composition for improving fuel combustion. The additive composition comprises 1-8 wt. % of metal-based QCs dispersed in a 92-99 wt. % of a hydrocarbon medium. The metal-based QCs comprise a salt or a mixture of salts of an organic oxyacid; and a metal salt. The hydrocarbon medium is a non-reacting medium, and wherein the hydrocarbon medium comprises an oil phase. The hydrocarbon medium comprises pentane, isopentane, hexane, or heptane. The metal-based QCs are present in an atomic cluster form.

(18) In yet another embodiment, at least five mole proportions of the salt or the mixture of salts of the organic oxyacid are required per mole of the metal salt.

(19) In another embodiment, the metal salt comprises a nitrate salt, a sulfate salt, or a chloride salt of a metal selected from a group consisting of cerium, iron, nickel, cobalt, manganese, zinc, or copper. The metal salt is preferably water soluble. Preferably, it is ceric ammonium nitrate and iron chloride. The cerium (IV) and iron (III) salt may also react with the salt of the organic oxyacid in aqueous phase and simultaneously get stabilized in oil phase.

(20) In yet another embodiment, the organic oxyacid is selected from a group consisting of carboxylic acid, organic sulfuric acid, sulfonic acid, phosphoric acid, or phosphonic acid. The salt of the organic oxyacid is preferably an alkali metal salt, such as a sodium or potassium salt, or an ammonium salt. The organic oxyacid acts as a dispersant and comprises acidity in the range of 1-5 pKa.

(21) In another embodiment, the size of the metal-based QCs ranges from 0.1-5 nanometer (nm) without any agglomeration. Generally, particle size of the QCs will not exceed 5 nm, the size of the QC is especially below 2 nm.

(22) According to another embodiment, the present invention relates to in-situ synthesis of metal-based QCs. These metal-based QCs are dispersed in a non-reacting hydrocarbon medium.

(23) In another embodiment, the present invention discloses a process for synthesis of the additive composition comprising the metal-based quantum clusters (QCs) dispersed in the hydrocarbon medium as a combustion improver for fuels, the process comprising:

(24) (a) preparing a salt or a mixture of salts of an organic oxyacid;

(25) (b) adding a hydrocarbon medium to the salt or the mixture of salts of the organic oxyacid to form a reaction mixture, wherein the non-reacting hydrocarbon medium comprises an oil phase;

(26) (c) heating the reaction mixture to a temperature range of 25-80° C., preferably to a range of 50-70° C.;

(27) (d) adding a metal salt dissolved in water to the reaction mixture and continuing heating the reaction mixture for a period of 1-4 hours; and

(28) (e) recovering the product containing the oil phase and washing with water followed by filtration to obtain the additive composition.

(29) In yet another embodiment, in step (a) the salt or the mixture of salts of the organic oxyacid is prepared in-situ by reacting the organic oxyacid with an oxide, hydroxide, hydrogen carbonate or carbonate of an alkali metal or an alkaline earth metal to form a mixture, to a pH in a range of 7 to 10, preferably about 8. The oil phase needs to be added in the reaction mixture after formation of the salt of organic oxyacid. Once the entire reaction mixture including oil phase reaches to the desired reaction mixture then only metal salt in water would be added. This chronology is very crucial to obtain metal-based QCs in oil phase.

(30) In another embodiment, the present invention also describes doping the fuels with the additive composition to catalyze the combustion process, thereby increasing the flame temperature and heat through put. The additive composition can be used in fuels to improve overall fuel economy and emission. Especially, no such effort has been reported for increasing the efficiency of the flames by using metal-based QCs dispersed in a hydrocarbon medium. The enhancement of the heat output and flame temperature through catalytic combustion is not reported so far. The present invention describes the catalytic combustion of gaseous hydrocarbon fuels in open flame and increases its heat output as well as flame temperature. The same can be extended to liquid fuel combustion improver in IC engines also.

(31) In yet another embodiment, the present invention discloses a synthetic method for the growth of catalyst which can be restricted in cluster level. These fuel borne catalysts (FBC) are basically metal oxo/hydroxo complexes stabilized by long-tail organic ligands. The inorganic content is in-situ transformed during the combustion process into the oxide and catalyze the process. The main advantage of the FBC is an effective dynamic intermingling of the nascent particles of the catalyst and soot in a gas phase which is beneficial for increasing of the number of their mutual contact points. As a result, the oxygen transfer from the catalyst toward the hydrocarbon fuel is facilitated, enhancing the combustion process.

(32) In another embodiment, the present invention provides that the additive composition comprising the metal-based QCs are dispersed in a non-reacting hydrocarbon medium compatible to the fuel. A bottom-up synthesis method is employed for the preparation of the additive composition. These clusters are functionalized to prevent agglomeration. A dispersant for stabilizing the particles has been used compatible to the matrix and fuel composition. The dispersant used is a non-reacting hydrocarbon medium, which comprises an oil phase

(33) In another embodiment, the present invention discloses a process for synthesis of an additive composition comprising metal-based QCs dispersed in a hydrocarbon medium, as a combustion improver for fuels. The metal-based QCs comprise ceria-based QCs and iron-based QCs.

(34) In a preferred embodiment, a process for synthesis of ceria-based QCs comprises—preparing a salt by reacting ethyl hexanoic acid with sodium hydroxide in water; followed by addition of an oil phase hydrocarbon medium and heating the solution to a temperature present in a range of 25-80° C.; adding 2.74 mole of ceric ammonium nitrate (CAN) salt dissolved in water to the reaction mixture to obtain the ceria-based QCs in a non-reacting hydrocarbon medium.

(35) In a preferred embodiment, a process for synthesis of iron-based QCs comprises—preparing a salt by reacting ethyl hexanoic acid with sodium hydroxide in water; followed by addition of an oil phase hydrocarbon medium and heating the solution to a temperature present in a range of 25-80° C.; adding 2.74 mole of FeCl.sub.3.6H.sub.2O salt dissolved in water to the reaction mixture to obtain the iron-based QCs in a non-reacting hydrocarbon medium.

(36) In another embodiment, the liquid and gaseous fuels are doped with the additive composition to improve the combustion process. The additive composition may be present in form of suspension or dispersion in the liquid or gaseous fuels.

(37) In yet another embodiment, the liquid and gaseous fuels are doped with the additive composition in a concentration range of 1-200 μm, preferably in a range of 10-100 ppm, more preferably in a range of 10-40 ppm of the fuel composition. The amount of additive composition may vary depending upon the nature and composition of the fuel. For LPG fuels, 2 ppm doping with the additive composition is enough to get satisfactory performance enhancement. For diesel fuel, the doping of the additive composition may be around 40 ppm. The additive composition is readily dispersible in fuels with or without co-surfactant depending on the nature of the fuel. The measurable flame temperature of the fuels, for instance commercial LPG on burner has been observed to increase at least by 60 to 80° C. The flame with high heat through put can be used for efficient cooking, heating, annealing and related high thermal applications.

(38) In another embodiment, the gaseous fuel may be propane, butane, or a mixture thereof at different ratio (such as LPG). The fuel under subject may be liquefied natural gas (LNG) or compressed natural gas (CNG) at different composition. The liquid fuel may be diesel, gasoline, motor spirit, mineral turpentine oil (MTO) and others.

(39) In another embodiment, the application of fuels doped with the additive composition include but are not limited to high temperature applications such as metal cutting, brazing, soldering, etc., where a high flame temperature is desirable. The additized fuel is also suitable for LPG/propane fired boilers, automotive applications, etc. The additized LPG will reduce cooking time, consumption of gas in cooking and enhance heating significantly.

(40) In another embodiment, the additive composition containing liquid fuels may also be suitable for internal combustion (IC) engines based on diesel and motor spirit (MS).

EXAMPLES

(41) Having described the basic aspects of the present invention, the following non-limiting examples illustrate specific embodiments thereof. Those skilled in the art will appreciate that many modifications may be made in the invention without changing the essence of the invention.

Example 1: Preparation of Additive Composition Comprising Cerium (IV)-Based QCs

(42) The large-scale production of an additive composition comprising cerium (IV) based QCs was carried out as follows: 2.74 mole ceric ammonium nitrate (CAN) was dissolved in 1 liter water. 10.4 mole Ethyl hexanoic acid was mixed with 5-liter water followed by addition of 4-liter of 45M NaOH solution in water. Then addition of 10-liter oil was done and the solution was heated to a temperature range of 60° C. Finally, the CAN solution was added, and the reaction was continued for heating for a time of 2 hours. On completion of the reaction, the product containing oil layer was recovered and washed thoroughly with water and the additive composition was collected after filtration. The ceria concentration measured with ICP analysis was found to be 5 wt. % and particle size was measured around 1 nanometer (nm). The final concentration of Ce can be increased by changing the salt amount accordingly. The final concentration of quantum clusters in the additive composition varies depending upon oil used and source of metal salt.

(43) UV-vis spectrophotometry of ceria is of particular interest as it provides quantitative information about the type of oxidation state and rate of reaction. It is known that Ce(III) absorbs both the UV and the Visible region while Ce(IV) absorbs the Visible region. Here cerium oxide exhibits strong absorption bands at 260 nm in the UV range in different solvents. Usually, CeO.sub.2 absorbs around 300 to 340 nm range. Due to size reduction (below 2 nm) the UV-vis spectra have been shifted to blue region.

(44) Infrared spectrum (FTIR) of the synthesized ceria-based additive composition to be in the range of 500-4000 cm.sup.−1 wave number and identifies the chemical bonds, as well as functional groups in the compound. The sharp band at 3650 cm.sup.−1 is ascribed to the O—H stretching vibration in OH.sup.− groups or Ce—O—H.sub.2. The broad peak in the range 3,400-2,400 cm.sup.−1 indicates OH of free carboxylic acid. Very sharp peak at 1707 cm-1 represents the C═O of carboxylic acid. The strong sharp peak at 1580-1550 cm.sup.−1 represents the C═O of carboxylate. The weak peaks in the range of 700-500 cm.sup.−1 represent the complex framework of Ce—O clusters.

(45) Another aspect of the present invention is to dope the hydrocarbon fuels with additive composition comprising ceria clusters and evaluate the efficiency. For this, liquefied propane and LPG have been used. The flame was generated and the temperature of inner core of the flame was measured by a thermocouple. The experimental flame temperature obtained was found to be at least 50° C. more than the gaseous fuel under study.

Example 2: Preparation of Additive Composition Comprising Iron (III)-Based QCs

(46) The large-scale production of an additive composition comprising Iron (III)-based QCs was carried out as follows: 2.74 mole FeCl.sub.3.6H.sub.2O was dissolved in 1-liter water. 10.4 mole Ethyl hexanoic acid was mixed with 5-liter water followed by addition of 4-liter of 45M NaOH solution in water. Then addition of 10-liter oil was done and the solution was heated to a desired temperature of 60° C. Finally, the iron chloride solution was added, and the reaction was continued for heating for a time of 2 hours. On completion of the reaction, the product containing oil layer was recovered and washed thoroughly with water and the additive composition was collected after filtration. The iron concentration measured with ICP analysis was found to be 2 wt. % and particle size was measured to be around 1 nm. The final concentration of quantum clusters in the additive composition can be increased by changing the salt amount accordingly.

Example 3: Doping of Gaseous Fuel with the Additive Composition

(47) Additive composition comprising Ce and Fe-based QC are synthesized by dispersing in a hydrocarbon medium having a concentration of 5 and 2 wt. % respectively. For doping in LPG, the QCs were dispersed in hydrocarbon solvents like pentane, Isopentane, hexane, heptanes, etc. The additive composition can be directly doped in LPG without any co-surfactant as per required amount. LPG were doped with the additive composition in different concentrations ranging from 2-40 ppm.

Example 4: Flame Temperature Measurement

(48) This method covers measurement of flame temperature of an open flame on LPG gas burner. The use of this method aims at ascertaining the presence of catalyst in differentiated LPG cylinder by measuring the enhancement in flame temperature (FT) on a domestic stove.

(49) Equipment for the Test:

(50) 1. Domestic two burners stove (IS marked)

(51) 2. Type ‘K’ rigid thermocouple

(52) 3. Digital data logger

(53) 4. Clamp and stand for holding thermocouple

(54) 5. Gas lighter

(55) 6. LPG cylinder

(56) Procedure for the Test:

(57) 1. Connecting the thermocouple to the data logger and setting the thermocouple's type and channel position in the data logger before starting of measurement

(58) 2. Connecting the LPG cylinder to the domestic burner for the FT measurement purpose

(59) 3. Generating the flame in a suitable place to avoid drift/flow of wind that may disturb the flame sturdiness. The flame must be generated on Big Burner (rating: 189 gph) of domestic stove. The cleanliness of burner must be ensured before flame generation

(60) 5. Setting the thermocouple position horizontally at a height of 2 centimeter (cm) from outer edge of the burner nozzle (hole) of outer circle using clamp and stand

(61) 6. Switching on the flame of the burner at max position of knob and adjusting the thermocouple position at the outer edge of the blue flame very minutely to get highest temperature and recording the data when the temperature stabilizes within ±5° C. Please note that placing the thermocouple for longer time in the flame may damage it
7. Switching off the burner and switching off the data logger
8. Waiting for thermocouple and burner to cool down up to ambient temperature
9. Switching on the data logger first and repeating the step 1-6 to record the second reading for highest temperature measurement.

(62) The procedure was adopted for LPG and additized LPG (LPG doped with additive composition comprising metal-based QCs in hydrocarbon medium). The flame temperature for different additized LPG and blank LPG has been given in table 1.

(63) TABLE-US-00001 TABLE 1 Flame temperature observation for additized and blank LPG Sr. No. Sample Flame Temperature (° C.) 1 Blank LPG 852-856 2 10 ppm (Ce-QC) additized LPG 930-935 3  5 ppm (Ce-QC) additized LPG 918-926 4 10 ppm (Fe-QC) additized LPG 921-925 5  5 ppm (Fe-QC) additized LPG 912-918

(64) It was clearly observed that for QC additized LPG (LPG doped with additive composition comprising metal-based QCs in hydrocarbon medium), the flame temperatures were 60-80° C. higher than regular LPG (not additized). The flame temperatures are reported in a range as a little variation was observed in flame temperature during measurement because of manual handling of the thermocouple.

Example 5: Fuel Saving Experiment Using 10 ppm Additized LPG (Iron-Based QC and Ceria-Based QC)

(65) A comparative LPG consumption study for regular LPG and additized LPG (LPG doped with additive composition comprising metal-based QCs in hydrocarbon medium) were also performed as per below mentioned test protocol.

(66) Materials Required for Experiment Set Up:

(67) 1. One ISO approved LPG Gas Stove (two burners).

(68) 2. One thermocouple (preferably Type ‘K’) and data logger for measuring data continuously against time in covering temperature range from ambient to 300° C.

(69) 3. One overhead stirrer (PTFE).

(70) 4. Two Flat bottom Pans (Steel) with lid having two holes (one for stirrer and other for thermocouple). One bigger flat bottom pan with lid for big burner and one small flat bottom pan with lid for small burner. These pans should cover the flame of the burner completely for better heat transfer. Details of the Pan is described in table 2.

(71) TABLE-US-00002 TABLE 2 Materials required for experiment set up Big Flat Bottom Small Flat Bottom Pan with lid Pan with lid having having two holes two holes for Small Sr. No. Details for Big Burner Burner 1 Material of Pan and lid Stainless Steel Stainless Steel 2 Capacity of Pan, liters 5.0 2.0 3 Diameter, millimeter (mm 215 130 4 Height, mm 120 90 5 Heating medium (Mustard 3.0 1 Oil), liters 6 RPM 90 50

(72) Experimental Process:

(73) 1) Taking a pan with lid. Taking recommended amount (3.0/1 L) of mustard oil in pre-weighed pan suitable for respective burners and noting the weight of the respective vessel.

(74) 2) Fixing LPG cylinder with stove and switching on the LPG cylinder regulator. Taking initial weight of LPG cylinder with regulator and tube as reference.

(75) 3) Putting the pan with oil on the burner first. Then fixing the stirrer and thermocouple through the holes in lid of the pan and marking the depth of both stirrer and thermocouple insertion in oil. After that switching on the stirrer (90/50 RPM) and data logger.
4) Switching on the stove knob and igniting the LPG simultaneously. The knob was fixed for the maximum position.
5) Heating the oil with constant stirring till the temperature reaches 200° C. and switching off the stove knob immediately after the temperature is reached.
6) Noting the final weight of LPG cylinder with regulator and tube (reference) immediately after the test without disturbing any set up.
7) Repeating above exercise three times with reference LPG and every time fresh mustard oil was taken. The LPG cylinder weight was taken before start of test and just after the test every time to avoid chances of minor leakages, if any.
8) After this, repeating the same exercise 3 times by replacing the LPG cylinder with QC-additized LPG cylinder and keeping other points same as with reference LPG.

(76) Average reading of the three data points was taken for calculation of the difference in gas consumption. Fuel consumption data has been depicted in table 3.

(77) TABLE-US-00003 TABLE 3 Calculation of difference in gas consumption Additized Additized LPG LPG (Iron- (Ceria- Sr. No Parameter based QC) based QC) 1 LPG savings in small −7.70 −8.20 burner of domestic stove 2 LPG savings in big burner −5.29 −6.1 of domestic stove

(78) Overall, it was observed that by using iron-based QC-additized cylinders 7.7% and 5.29% fuel can be saved as compared to normal LPG in small and big burner respectively. Similarly in case of ceria-based QC-additized cylinders 8.2% and 6.1% fuel savings were observed in small and big burner respectively.

Example 6: Doping of Liquid Fuel with the Additive Composition

(79) For doping of liquid fuels like diesel with an additive composition, an additional co-surfactant is required for long term stability. A nonionic co-surfactant sorbitan oleate (SPAN-80) was used in different mole ratio with respect to the additive composition to get them stabilized in diesel fuel. Details of the stability study done by ICP analysis for different mole ratio of Ce-based and Fe-based additive composition have been depicted in Tables 4 & 5.

(80) TABLE-US-00004 TABLE 4 Stability observation for (Ce-based QC) additized BSVI diesel (Ce-based QC) Additized BSVI Diesel Molar Ratio Result as ) Result after Ce: SPAN80 prepared (ppm 60 days (ppm) 1:5 270 270 1:10 263 262 1:15 275 274 1:20 285 285 1:25 290 288

(81) TABLE-US-00005 TABLE 5 Stability observation for (Fe-based QC) additized BSVI diesel (Fe-based QC) Additized BSVI Diesel Molar Ratio Result as Result after Fe: SPAN80 prepared (ppm) 60 days (ppm) 1:5 142 140 1:10 143 142 1:15 147 144 1:20 153 150 1:25 155 152

(82) Detail fuel specification after doping with the additive composition (Ce-based and Fe-based QCs) in diesel were performed and found compliance with BSIV and BSVI norms (depicted in Tables 6 & 7).

(83) TABLE-US-00006 TABLE 6 No harm test with 40 parts per million (ppm) (Ce-based QC) additized BSIV and BSVI diesel Sample Details CD/FRD CQC BSIV- CQC BSVI- DIESEL DIESEL S. Test Unit of (F-09-04) (F-09-05) No. Properties Methods measurement Test Results 1 Appearance — — Clear, bright, Clear, bright, free from free from sediments sediments 2 Density at 15° C. ASTM Kg/m.sup.3 827.3 819.5 D4052 3 Distillation: ASTM D86 Deg C 363 355.7 95% volume/volume recovery, Max 4 Flash point, Abel, Min IS: 1448 (P: ° C. 47.0 53.0 20) 5 Total sulphur, Max ASTM PPm 30 2 D5453 6 K. V. at 40° C. ASTM cSt 2.635 2.767 D445 7 Cu strip corrosion 50 IS: 1448 (P: — No. 1 No. 1 8 Cetane Index, Min ASTM — 55.7 61.0 D4737 9 Cold filter plugging ASTM ° C. 0 -1.0 point, Max D6371 ° C. Winter Summer 10 Water content, Max ISO 12937 mg/kg 120 50 11 Lubricity, corrected ISO 12156 μm 414 406 WSD @ 60° C., Max 12 Total Contamination, DIN 51419 mg/kg 6 4 Max 13 Acidity, Inorganic IS 1448, P:2 Nil Nil Nil 14 Acidity, total, mg of ASTMD To report 0.04 0.03 KOH/g, Max 974 15 Carbon residue IS 1448, P:8 0.30 <0.1 <0.1 (Ramsbottom) on 10% residue, % mass, Max 16 Ash, % mass, Max IS 1448, P:4 % By mass <0.001 <0.001 17 PAH ASTM % By mass 1.3 <0.2 D6591 18. Cetane number, Min. ASTM — — — D613 19 FAME Content Max ASTMD % v/v 0.0 0.0 7371 20 Pour Point Max — −6.0 −6.0 Winter — ° C. Summer ° C. 21 Oxidation stability ASTM Minutes 51 57 D7545

(84) TABLE-US-00007 TABLE 7 No harm test with 40 ppm (Fe-based QC) additized BSVI diesel Sample Details CD/Location/FRD BSVI HSD QC-40/BSVI Units of F-08-03 F-08-04 S. No. Characteristics Test Methods measurement Test Results 1 Density@ 15° C. ASTMD 4052 Kg/m.sup.3 819.2 821.0 2 Flash point, Abel, Min IS 1448 (P:20) ° C. 46.5 46.0 3 Calorific Value ASTMD 240 Cal/gm 11041 11014 4 K.V. at 40° C. ASTMD 445 cSt 2.755 2.844 5 Pour Point ASTMD 97 ° C. −3.0 −3.0 6 Water Content Max ISO 12937 Mg/kg 60 6.4 7 Total Sulphur, Max ASTMD ppm 4 4 D2622