GREASE COMPOSITION FOR CONSTANT-VELOCITY JOINT AND CONSTANT-VELOCITY JOINT FILLED THEREWITH

Abstract

A grease composition for a constant-velocity joint includes: (a) a base oil having a kinematic viscosity of 16.0 mm.sup.2/s or more at 100 C. and a viscosity index of 90 or more; (b) a diurea-based thickener, for example, an aliphatic diurea; (c) 0.2 to 2.0% by mass of zinc dialkyldithiophosphate; (d) 0.5 to 2.0% by mass of non-oil-soluble molybdenum dialkyl dithiocarbamate; (e) 0.5 to 3.0% by mass of oil-soluble molybdenum dialkyl dithiocarbamate; (f) 1.0 to 4.0% by mass of zinc dialkyldithiocarbamate; and (g) 0.1 to 1.5% by mass of a benzothiazole-thione or a derivative thereof, wherein (f):(g)=8:1 to 3:1 (mass ratio).

Claims

1. A grease composition for a constant-velocity joint, comprising: (a) a base oil having a kinematic viscosity of 16.0 mm.sup.2/s or more at 100 C. and a viscosity index of 90 or more; (b) a diurea-based thickener represented by the following formula (1) ##STR00011## wherein R.sup.1 and R.sup.1 are each independently an octyl group, a dodecyl group, a hexadecyl group, an octadecyl group, or a cyclohexyl group; (c) 0.2 to 2.0% by mass of a zinc dialkyldithiophosphate; (d) 0.5 to 2.0% by mass of a non-oil-soluble molybdenum dialkyl dithiocarbamate; (e) 0.5 to 3.0% by mass of an oil-soluble molybdenum dialkyl dithiocarbamate; (f) 1.0 to 4.0% by mass of a zinc dialkyldithiocarbamate; and (g) 0.1 to 1.5% by mass of a benzothiazole-thione or a derivative thereof, wherein a mass ratio between the component (f) and the component (g) is (f):(g)=8:1 to 3:1

2. The grease composition according to claim 1, wherein the component (c) is represented by the following formula (2): ##STR00012## wherein R.sup.2 is a primary or secondary alkyl group having 1 to 24 carbon atoms.

3. The grease composition according to claim 1, wherein the component (d) is represented by the following formula (3): ##STR00013## wherein R.sup.30 is a primary or secondary alkyl group having 1 to 4 carbon atoms, m is 0 to 3, n is 1 to 4, and m+n=4.

4. The grease composition according to claim 1, wherein the component (e) is represented by the following formula (4): ##STR00014## wherein R.sup.31 is a primary or secondary alkyl group having 5 to 24 carbon atoms, m is 0 to 3, n is 1 to 4, and m+n=4.

5. The grease composition according to claim 1, wherein the component (f) is represented by the following formula (5): ##STR00015## wherein R.sup.4 is a primary or secondary alkyl group having 1 to 24 carbon atoms.

6. A constant-velocity joint hermetically filled with the grease composition for a constant-velocity joint according to claim 1.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0028] FIG. 1 is a diagram of a tripod joint using a grease composition for a constant-velocity joint of the present invention in which a part thereof is cut out.

[0029] FIG. 2 is a diagram of a double-offset joint using the grease composition for a constant-velocity joint of the present invention in which a part thereof is cut out.

DESCRIPTION OF EMBODIMENTS

(a) Base Oil

[0030] A base oil of the present invention has a kinematic viscosity of 16.0 mm.sup.2/s or more at 100 C. and a viscosity index of 90 or more.

[0031] When the kinematic viscosity at 100 C. is 16.0 mm.sup.2/s or more, a sufficient oil film thickness can be secured even under a condition of a temperature of the surface of the CVJ of 90 to 100 C., and the lubricity at a high temperature can thus be maintained.

[0032] When the viscosity index is 90 or more, vibration can be suppressed by a reduction in sliding resistance at ordinary temperature and a reduction in agitation resistance in a low-temperature environment.

[0033] As long as the kinematic viscosity and the viscosity index are within such ranges, the type of base oil used in the present invention is not particularly limited. For example, such base oils include mineral oils represented by a naphthene-based oil and a paraffin-based oil, synthetic hydrocarbon oils represented by polybutene, ether-based synthetic oils represented by alkyl diphenyl ether, and various synthetic oils such as silicone oil and fluorinated oil. The synthetic oil may be a so-called biomass oil produced by using a biological resource produced from an animal, a plants, or the like as a raw material. For example, biomass ester oils synthesized from various fatty acids using vegetable oils as raw materials and alcohols, and biomass hydrocarbon oils using vegetable oils such as palm oil, corn oil, and soybean oil can also be used. One base oil may be used alone, or two or more base oils may be mixed. A mineral oil is preferable from the viewpoint of cost, and a paraffin-based mineral oil is preferable to a naphthene-based oil from the viewpoint of viscosity index.

[0034] The kinematic viscosity at 100 C. is preferably 18.0 mm.sup.2/s or more from the viewpoint of securing an oil film thickness at a high temperature. In addition, the kinematic viscosity at 100 C. is preferably 24.0 mm.sup.2/s or less, and more preferably 22.0 mm.sup.2/s or less, from the viewpoint of suppressing vibration at ordinary temperature and reducing an agitation resistance in a low-temperature environment.

[0035] The viscosity index is preferably 93 or more from the viewpoint of suppressing vibration at ordinary temperature and reducing an agitation resistance in a low-temperature environment. In addition, the viscosity index is preferably 120 or less, and more preferably 110 or less, from the viewpoint of compatibility with a boot material.

[0036] As the base oil of the present invention, a mineral oil having a kinematic viscosity of 18.0 mm.sup.2/s or more at 100 C. and a viscosity index of 95 or more is preferable from the viewpoint of securing an oil film thickness at a high temperature, reducing a sliding resistance at ordinary temperature, and reducing an agitation resistance in a low-temperature environment. A mineral oil having a kinematic viscosity of 19.0 to 20.0 mm.sup.2/s at 100 C. and a viscosity index of 95 to 105 is more preferable.

[0037] Note that the kinematic viscosity of the base oil can be measured in accordance with JIS K 2283. The viscosity index of the base oil can be obtained from measured values of the kinematic viscosities at 40 C. and 100 C. of the base oil in accordance with a calculation formula specified in JIS.

[0038] The content of the base oil is preferably 80 to 94% by mass, more preferably 83 to 92% by mass, and further preferably 85 to 90% by mass, based on the total mass of the composition, from the viewpoint of the fluidity of the grease.

(b) Thickener

[0039] A thickener of the present invention is a diurea-based thickener represented by the following formula (1).

##STR00006## [0040] wherein R.sup.1 and R.sup.1 are each independently an octyl group, a dodecyl group, a hexadecyl group, an octadecyl group, or a cyclohexyl group.

[0041] The diurea-based thickener of the formula (1) includes an aliphatic diurea in which both R.sup.1 and R.sup.1 are each an octyl group, a dodecyl group, a hexadecyl group, or an octadecyl group, an alicyclic aliphatic diurea containing a diurea compound in which one of R.sup.1 and R.sup.1 is an octyl group, a dodecyl group, a hexadecyl group, or an octadecyl group and the other thereof is a cyclohexyl group, and an alicyclic diurea in which both R.sup.1 and R.sup.1 are each a cyclohexyl group.

[0042] The thickener is preferably an aliphatic diurea thickener or an alicyclic aliphatic diurea thickener which is easily softened by shear, and more preferably an alicyclic aliphatic diurea thickener because when the grease easily flows in the CVJ, the grease can be easily supplied to a sliding portion, which leads to an improvement in durability. As the aliphatic diurea thickener, one of R.sup.1 and R.sup.1 in the formula (1) is preferably an octyl group. The alicyclic aliphatic diurea thickener is preferably a mixture of a diurea compound in which one of R.sup.1 and R.sup.1 in the formula (1) is an octadecyl group and the other thereof is a cyclohexyl group, a diurea compound in which both R.sup.1 and R.sup.1 in the formula (1) are each an octadecyl group, and a diurea compound in which both R.sup.1 and R.sup.1 in the formula (1) are each a cyclohexyl group is preferable. The molar ratio between a cyclohexyl group and an octadecyl group of the alicyclic aliphatic diurea thickener is preferably 1:9 to 3:7, and more preferably 1:9 to 2:8, from the viewpoint of securing the fluidity of the grease.

[0043] The content of the thickener may be an amount with which the penetration of the grease can be adjusted to 300 to 350, and specifically, is preferably 3 to 10% by mass, more preferably 4 to 9% by mass, and further preferably 5 to 8% by mass, based on the total mass of the composition. Note that in the Specification, the penetration means 60-stroke worked penetration measured in accordance with JIS K 2220.7.

(c) As a Zinc Dialkyldithiophosphate (ZnDTP), One Represented by the Following Formula (2) is Preferable

##STR00007## [0044] wherein R.sup.2 is a primary or secondary alkyl group having 1 to 24 carbon atoms or aryl group having 6 to 30 carbon atoms. R.sup.2 is particularly preferably a primary or secondary alkyl group having 3 to 8 carbon atoms.

[0045] The content of the component (c) is 0.2 to 2.0% by mass, preferably 0.5 to 1.8% by mass, and more preferably 0.8 to 1.5% by mass, based on the total mass of the composition. Adding the component (c) in such a range is preferable because sufficient initial conformability can be obtained.

(d) As a Non-Oil-Soluble Molybdenum Dialkyl Dithiocarbamate (Non-Oil-Soluble MoDTC), One Represented by the Following Formula (3) is Preferable

##STR00008## [0046] wherein R.sup.30 is a primary or secondary alkyl group having 1 to 4 carbon atoms, and preferably a primary or secondary alkyl group having 2 to 4 carbon atoms, m is 0 to 3, n is 1 to 4, and m+n=4.

[0047] The content of the component (d) is 0.5 to 2.0% by mass, preferably 0.5 to 1.5% by mass, and more preferably 0.5 to 1.0% by mass, based on the total mass of the composition, from the viewpoint of low friction properties. Adding the component (d) in such a range is preferable because sufficient low friction properties can be obtained.

(e) As an Oil-Soluble Molybdenum Dialkyl Dithiocarbamate (Oil-Soluble MoDTC), One Represented by the Following Formula (4) is Preferable

##STR00009## [0048] wherein R.sup.31 is a primary or secondary alkyl group having 5 to 24 carbon atoms, and preferably a primary or secondary alkyl group having 5 to 18 carbon atoms, m is 0 to 3, n is 1 to 4, and m+n=4.

[0049] The content of the component (e) is 0.5 to 3.0% by mass, preferably 0.5 to 2.5% by mass, and more preferably 0.5 to 2.0% by mass, based on the total mass of the composition, from the viewpoint of low friction properties. Adding the component (e) in such a range is preferable because sufficient low friction properties can be obtained.

(f) As a Zinc Dialkyldithiocarbamate (ZnDTC), One Represented by the Following Formula (5) is Preferable

##STR00010## [0050] wherein R.sup.4 is a primary or secondary alkyl group having 1 to 24 carbon atoms or aryl group having 6 to 30 carbon atoms. R.sup.4 is preferably an alkyl group having 3 to 8 carbon atoms.

[0051] The content of the component (f) is 1.0 to 4.0% by mass, preferably 1.2 to 3.8% by mass, and more preferably 1.5 to 3.5% by mass, based on the total mass of the composition, from the viewpoint of initial conformability. Adding the component (f) in such a range is preferable because sufficient initial conformability can be obtained.

[0052] (g) A benzothiazole-thione or a derivative thereof is normally used as an extreme pressure agent for a grease. For example, a compound of amines, C16 to 22-tert-alkyl, and 2 (3H)-benzothiazole-thione (1:1) (a compound represented by Amines, C16-22-tert-alkyl, compds. with 2 (3H)-benzothiazolethione (1:1)) (for example, Vanlube (registered trademark) 601 produced by Vanderbilt) can be used, and among these, one having a sulfur content of 5 to 20% by mass and a nitrogen content of 1 to 10% by mass is preferable.

[0053] The content of the component (g) is 0.1 to 1.5% by mass, preferably 0.2 to 1.2% by mass, and more preferably 0.3 to 1.0% by mass, based on the total mass of the composition, from the viewpoint of initial conformability. Setting the content of the component (g) in such a range is preferable because sufficient initial conformability can be obtained.

[0054] The mass ratio between the component (f) and the component (g) is (f):(g)=8:1 to 3:1, and preferably 6:1 to 3.5:1. Setting the mass ratio between the component (f) and the component (g) in such a range is preferable because sufficient initial conformability can be obtained.

[0055] The grease composition of the present invention may contain an additive normally used for a grease composition, such as another extreme pressure additive, an antioxidant, or a rust inhibitor in addition to the above-described components. The other extreme pressure additive includes phosphoric acid ester and the like. The antioxidant includes amine-based and phenol-based antioxidants and the like. The rust inhibitor includes sulfonate-based, carboxylic acid-based, and amine-based rust inhibitors. The content of such an optional additive is, for example, 0.1 to 2.0% by mass, and preferably 0.3 to 1.0% by mass based on the total mass of the composition.

[0056] The grease composition for a constant-velocity joint of the present invention can be used for any constant-velocity joints without limitation, but the expression of the advantageous effects is particularly significant in the case where the grease composition for a constant-velocity joint of the present invention is used for constant-velocity joints in which components conduct rolling sliding motions, for example, plunging constant-velocity joints such as tripod joints and double-offset joints.

[0057] The structures of plunging constant-velocity universal joints preferable as the present embodiments are given below.

[0058] (A) A structure including: an outer joint member in which three straight track grooves that extend in an axial direction are formed in an inner peripheral surface thereof; a tripod member as an inner joint member having three leg shafts protruding in a radial direction; and rollers as rolling elements rotatably supported on the leg shafts of the tripod member, wherein the rollers are arranged to be rollable along the track grooves of the outer joint member.

[0059] (B) A structure including: an outer joint member in which a plurality of straight track grooves that extend in an axial direction are formed in a cylindrical inner peripheral surface thereof; an inner joint member in which a plurality of straight track grooves paired with the track grooves of the outer joint member are formed in a spherical outer peripheral surface thereof; (3 to 8) balls as rolling elements disposed between the track grooves of the outer joint member and the track grooves of the inner joint member; and a cage holding the balls between the outer joint member and the inner joint member.

[0060] First and second specific embodiments of the constant-velocity universal joint of the present invention will be described based on FIG. 1 and FIG. 2. FIG. 1 shows a partially-cut sectional view of a tripod joint (hereinafter, referred to as TJ) and FIG. 2 shows a partially-cut sectional view of a double-offset joint (hereinafter, referred to as DOJ). These are sliding constant-velocity universal joints and are used for drive shaft for automobiles and the like.

[0061] As shown in FIG. 1, a TJ 1 includes three straight track grooves 3 formed in an axial direction in an inner surface of an outer joint member 2. A tripod member (inner joint member) 4 incorporated inside the outer joint member 2 is provided with three leg shafts 5. A spherical roller 6 is inserted on an outer side of each leg shaft 5, and a needle 7 is incorporated between the spherical roller 6 and the leg shaft 5 to support the spherical roller 6 such that the spherical roller 6 is rotatable and slidable in the axial direction. The spherical roller 6 is rollably inserted in the above-described track groove 3. A boot 9 is mounted from the outer joint member 2 over a shaft 8 joined to the tripod member 4.

[0062] The boot 9 includes an outer tubular end portion (large-diameter attachment portion) 9a which is fitted and fixed onto the outer joint member 2, an inner tubular end portion (small-diameter attachment portion) 9b which is fitted and fixed onto the shaft 8 coupled to the inner joint member 4, and a bellows-shaped bent portion (hereinafter also referred to as bellows portion) 9c which connects the outer tubular end portion 9a and the inner tubular end portion 9b and has a plurality of mountains and valleys, and covers the constant-velocity universal joint in a sealing manner. This sealed space is hermetically filled with the grease as a lubricant. The boot 9 is such that the outer tubular end portion 9a is fitted onto the outer joint member 2 and fixed with a fastening band 10a or the like, and the inner tubular end portion 9b is fixed onto the shaft 8 with a fastening band 10b or the like. A boot groove 8a is formed in an outer peripheral surface where the inner tubular end portion 9b of the shaft 8 is fixed, and the inner tubular end portion 9b is fitted into the boot groove 8a. Note that by providing annular protruding portions 8b on both sides of the boot groove 8a, the fixation of the inner tubular end portion 9b, which is fitted in the boot groove 8a, to the shaft 8 can be further strengthened.

[0063] As shown in FIG. 2, a DOJ 11 includes a plurality of straight track grooves 14, 15 formed in an axial direction in an inner surface of an outer joint member 12 and an outer surface of an inner race (inner joint member) 13. A ball 16 incorporated between the track grooves 14, 15 is supported with a cage 17, and an outer periphery of this cage 17 is formed into a spherical surface 17a and an inner periphery thereof is formed into a spherical surface 17b that matches an outer periphery of the inner race 13. The centers (A) and (B) of the respective spherical surfaces 17a, 17b are displaced in the axial direction on the axis of the outer joint member 12. A boot 19 is mounted from the outer joint member 12 over a shaft 18 joined to the inner race 13. The structure of the boot 19 and the attachment structure thereof are the same as those of the boot 9 in FIG. 1. In addition, the space sealed by the boot 19 is hermetically filled with the grease as a lubricant.

[0064] The constant-velocity universal joint used for a drive shaft for automobiles, that is hermetically filled with the grease of the present embodiment, can maintain an excellent durability at a high temperature.

[0065] Therefore, various constant-velocity joints hermetically filled with the above-described grease composition, particularly plunging constant-velocity joints, are also encompassed within the scope of the present invention.

EXAMPLES

[0066] Grease compositions of Examples and Comparative Examples were prepared by using components described below. Specifically, 1 mol of 4,4-diphenylmethane diisocyanate and 2 mol of a certain amine were reacted in a base oil, and the temperature was increased and cooled, then followed by kneading with a three roll mill to obtain a base grease. To the base grease, additives were blended in ratios shown in Table 1 (the numbers in Table are % by mass based on the total mass of the composition), and the base oil is further added to obtain the amounts of the thickener in ratios shown in Table 1, followed by dispersing with a three roll mill to obtain the grease compositions of Examples and Comparative Examples. Note that the penetrations were measured and all adjusted to 325 in accordance with JIS K2220 7.

(a) Base Oil

[0067] Mineral oil

(b) Thickener

[0068] For the aliphatic diurea, octylamine was used as an amine. [0069] For the alicyclic aliphatic diurea, cyclohexylamine and octadecylamine were used in a molar ratio of cyclohexylamine: octadecylamine=2:8 as amines. [0070] For the alicyclic aromatic diurea, cyclohexylamine and aniline were used in a molar ratio of cyclohexylamine: aniline=7:3 as amines.

Additives

[0071] (c) ZnDTP: a zinc dialkyldithiophosphate [0072] (LUBRIZOL 1395, produced by Lubrizol)

[0073] (d) MoDTC (non-oil-soluble): a molybdenum dialkyl dithiocarbamate [0074] (ADEKA SAKURA-LUBE 600, produced by ADEKA)

[0075] (e) MoDTC (oil-soluble): a molybdenum dialkyl dithiocarbamate [0076] (ADEKA SAKURA-LUBE 525, produced by ADEKA)

[0077] (f) ZnDTC: a zinc dialkyldithiocarbamate [0078] (Vanlube AZ, produced by Vanderbilt)

[0079] (g) A benzothiazole-thione derivative [0080] (Vanlube 601, produced by Vanderbilt)

Test Methods

[0081] Each grease composition of Examples and Comparative Examples was tested by methods described below. Results are shown in Table 1.

Roll Stability Test

(In Compliance with ASTM D 1831)

[0082] This test is a test for evaluating how easily the grease is softened by shear. [0083] Test conditions [0084] Ambient temperature: 100 C. [0085] Roll rotation speed: 165 rpm [0086] Rotation time: 24 h [0087] Evaluation criteria [0088] Worked penetration of the grease after the test [0089] : 400 or more [0090] x: less than 400

SRV Test-Evaluation of Initial Conformability

(In Compliance with ASTM D5706)

[0091] This test is a test for evaluating the degree of smoothing of plate surface roughness after the test. [0092] Test conditions: [0093] Surface pressure: 2.8 GPa [0094] Sliding speed: 20 mm/s (3.0 mm3.3 Hz) [0095] Plate temperature: 95 C. [0096] Ball diameter: 17.5 mm [0097] Plate roughness Ra before the test: 0.7 m [0098] Evaluation criteria [0099] Plate roughness Ra after the test [0100] : less than 0.35 m [0101] x: 0.35 m or more

Evaluation of Durability at a High Temperature

[0102] Each grease composition of Examples and Comparative Examples was put into an actual tripod CVJ, and a joint durability test was conducted by using this under conditions described below, and the durability at a high temperature was evaluated by measuring the time when flaking occurred. [0103] Test conditions [0104] Rotation speed: 200 rpm [0105] Torque: 800 Nm [0106] Angle: 6 [0107] Temperature of the surface of the joint: 90 to 100 C. [0108] Evaluation method

[0109] The joint was dismantled and checked every 50 hours after the start of the test, and the time when the flaking area in the outer race, the inner race, or the trunnion or the needle reached 20 mm.sup.2 was measured. Note that after the flaking area exceeds 20 mm.sup.2, the operation becomes difficult to continue. [0110] Evaluation criteria [0111] : 250 h or more [0112] x: less than 250 h

Evaluation of Induced Thrust-Vibration Resistance

[0113] Each grease composition of Examples and Comparative Examples was put into an actual tripod CVJ, and vibration resistance was evaluated by using this CVJ and measuring the force generated in the axial direction as an induced thrust when this CVJ was rotated at an operating angle and torque. [0114] Measurement conditions [0115] Rotation speed: 150 rpm [0116] Torque: 300 Nm [0117] Angle: 0 to 12 deg [0118] Evaluation criteria [0119] Third-order component [0120] : 110 N.sub.rms or less [0121] X: more than 110 N.sub.rms

TABLE-US-00001 TABLE 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 (a) Base oil Amount Bal. Bal. Bal. Bal. Bal. Bal. Kinematic 16.1 19.4 21.6 16.1 19.4 21.6 viscosity at 100 C. [mm.sup.2/s] Viscosity 98 102 103 98 102 103 index (b) Thickener Aliphatic 6.0 6.0 diurea Alicyclic 6.0 6.0 6.0 6.0 aliphatic diurea Alicyclic aromatic diurea (c) ZnDTP 1.0 1.0 1.0 1.0 1.0 1.0 (d) Non-oil-soluble 0.75 0.75 0.75 0.75 0.75 0.75 MoDTC (e) Oil-soluble MoDTC 1.0 1.0 1.0 1.0 1.0 1.0 (f) ZnDTC 3.0 3.0 3.0 3.0 3.0 3.0 (g) Benzothiazole- 0.6 0.6 0.6 0.6 0.6 0.6 thione or a derivative thereof Roll stability test 100 C. 24 h 400 400 400 400 400 400 Plate roughness Ra after SRV test m Anti- Constant- High flaking velocity temperture 250 350 400 250 350 400 properties joint Ordinary temperature 800 >1000 >1000 800 >1000 >1000 Inducced Ordinary thrust temperature Comp. Comp. Comp. Comp. Comp. Comp. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 (a) Base oil Amount Bal. Bal. Bal. Bal. Bal. Bal. Kinematic 13.5 13.5 13.5 13.5 21.6 13.5 viscosity at 100 C. [mm.sup.2/s] Viscosity 80 96 80 96 82 80 index (b) Thickener Aliphatic 6.0 6.0 diurea Alicyclic 6.0 6.0 6.0 aliphatic diurea Alicyclic 13.0 aromatic diurea (c) ZnDTP 1.0 1.0 1.0 1.0 1.0 1.0 (d) Non-oil-soluble 0.75 0.75 0.75 0.75 0.75 0.75 MoDTC (e) Oil-soluble MoDTC 1.0 1.0 1.0 1.0 1.0 1.0 (f) ZnDTC 3.0 3.0 3.0 3.0 3.0 3.0 (g) Benzothiazole- 0.6 0.6 0.6 0.6 0.6 0.6 thione or a derivative thereof Roll stability test 100 C. 24 h 400 400 400 400 400 340 Plate roughness Ra after SRV test m Anti- Constant- High x x x x x flaking velocity temperture 150 150 150 150 350 50 properties joint Ordinary temperature 600 600 600 600 Inducced Ordinary x x thrust temperature Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Comp. Ex. 7 Ex. 8 Ex. 9 Ex. 10 Ex. 11 Ex. 12 Ex. 13 Ex. 14 Ex. 15 Ex. 16 Ex. 17 (a) Base oil Amount Bal. Bal. Bal. Bal. Bal. Bal. Bal. Bal. Bal. Bal. Bal. Kinematic 13.5 16.1 19.4 21.6 16.1 16.1 16.1 16.1 13.2 13.2 13.2 viscosity at 100 C. [mm.sup.2/s] Viscosity 96 98 102 103 98 98 98 98 index (b) Thickener Aliphatic 5.0 5.0 5.0 diurea Alicyclic 6.0 6.0 6.0 6.0 aliphatic diurea Alicyclic 13.0 13.0 13.0 13.0 aromatic diurea (c) ZnDTP 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 (d) Non-oil-soluble 0.75 0.75 0.75 0.75 0.75 0.75 0.75 0.5 0.5 0.75 MoDTC (e) Oil-soluble MoDTC 1.0 1.0 1.0 1.0 1.0 1.0 1.0 0.5 0.5 1.25 (f) ZnDTC 3.0 3.0 3.0 3.0 3.0 3.0 3.0 1.0 2.0 1.0 (g) Benzothiazole- 0.6 0.6 0.6 0.6 0.6 0.6 0.6 1.0 1.0 1.0 thione or a derivative thereof Roll stability test 100 C. 24 h 340 340 340 340 400 400 400 400 425 425 425 Plate roughness Ra after x x x x x x x SRV test m Anti- Constant- High x x x x x x x x x x x flaking velocity temperture 100 100 100 100 100 50 50 100 50 100 100 properties joint Ordinary temperature >1000 Inducced Ordinary x x x x x thrust temperature

REFERENCE SIGNS LIST

[0122] 1 TJ [0123] 2 outer joint member [0124] 3 track groove [0125] 4 tripod member (inner joint member) [0126] 5 leg shaft [0127] 6 spherical roller [0128] 7 needle [0129] 8 shaft [0130] 9 boot [0131] 10a, 10b fastening band [0132] 11 DOJ [0133] 12 outer joint member [0134] 13 inner race (inner joint member) [0135] 14, 15 track groove [0136] 16 ball [0137] 17 cage [0138] 18 shaft [0139] 19 boot