RUBBER FILLER, RUBBER COMPOSITE COMPRISING THE SAME, AND PREPARATION METHOD THEREFOR AND USE THEREOF

Abstract

The present disclosure discloses a rubber filler, a rubber composite including the same, a preparation method therefor, and use thereof. The rubber filler includes polydivinylbenzene microspheres and polydopamine-modified white carbon black loaded on the polydivinylbenzene microspheres; wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(0.5-20). The rubber composite includes: a solution polymerized crude rubber and the rubber filler; wherein the rubber filler is added in an amount of 10-60 wt % of the dry basis mass of the solution polymerized crude rubber. The present disclosure uses polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black as the filler, solving the problem that the white carbon black is apt to agglomerate and the white carbon black has poor binding force with the rubber. The rubber composite obtained by the present disclosure is suitable for manufacturing green tires.

Claims

1. A rubber filler comprising: polydivinylbenzene microspheres and polydopamine-modified white carbon black loaded on the polydivinylbenzene microspheres, wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(0.5-20).

2. The rubber filler according to claim 1, wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(1-10); or the mass ratio of the white carbon black and polydopamine in the polydopamine-modified white carbon black is 1:(0.05-1).

3. The rubber filler according to claim 1, wherein the polydivinylbenzene microspheres have a particle size within the range of 0.1-1 m.

4. The rubber filler according to claim 1, wherein the white carbon black has a particle size within the range of 20-60 nm.

5. A method for preparing the rubber filler comprising: (1) carrying out a first reaction on the white carbon black and dopamine in a first buffer solution to obtain a polydopamine-modified white carbon black; (2) subjecting the polydivinylbenzene microspheres to a second reaction in a second buffer solution with the polydivinylbenzene microspheres obtained in step (1) to obtain the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(0.5-20).

6. The method according to claim 5, wherein step (1) specifically comprising: adding an inorganic acid or inorganic base into a weak alkalinity buffering agent solution to obtain a first buffer solution with a pH of 7.5-10.5, wherein the concentration of the buffering agent in the first buffer solution is within the range of 3-15 mmol/L; adding white carbon black and dopamine into the first buffer solution, carrying out the reaction for 0.5-2 h at room temperature, and then filtering, washing, and drying to obtain the polydopamine-modified white carbon black.

7. The method according to claim 6, wherein the mass ratio of the white carbon black and dopamine is 1:(0.05-1); or the mass ratio of the white carbon black to the first buffer solution is 1:(5-50); or the weak alkalinity buffering agent is one or more selected from the group consisting of trihydroxymethyl aminomethane, barbital, barbital-sodium chloride composite buffering agent, boric acid-potassium chloride composite buffering agent, borax-calcium chloride composite buffering agent, disodium hydrogen phosphate, and dipotassium hydrogen phosphate-potassium dihydrogen phosphate composite buffering agent; or the inorganic acid is one or more of hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid; or the inorganic base is potassium hydroxide and/or sodium hydroxide.

8. The method according to claim 5, wherein step (2) specifically comprising: adding an inorganic acid or inorganic base into a weak alkalinity buffering agent solution to obtain a second buffer solution with a pH of 7.5-10.5, wherein the concentration of the buffering agent in the second buffer solution is within the range of 3-15 mmol/L; adding polydivinylbenzene microspheres and the polydopamine-modified white carbon black obtained in step (1) into the second buffer solution, carrying out the reaction with magnetic stirring at room temperature for 1-4 h, then filtering, washing, and drying the reaction product to obtain the polydivinylbenzene microspheres loaded with the polydopamine-modified white carbon black.

9. The method according to claim 8, wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(1-10); or the mass ratio of the polydivinylbenzene microspheres and the second buffer solution is 1(50-500); or the weak alkalinity buffering agent is one or more selected from the group consisting of trihydroxymethyl aminomethane, barbital, barbital-sodium chloride composite buffering agent, boric acid-potassium chloride composite buffering agent, borax-calcium chloride composite buffering agent, disodium hydrogen phosphate, and dipotassium hydrogen phosphate-potassium dihydrogen phosphate composite buffering agent; or the inorganic acid is one or more of hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid; or the inorganic base is potassium hydroxide and/or sodium hydroxide.

10. A rubber composite comprising: a solution polymerized crude rubber, a first filler, and a second filler, wherein the first filler is the rubber filler according to claim 1, and the second filler is a polydopamine-modified white carbon black; the total addition amount of the first rubber filler and the second rubber filler is 10-60 wt % of the dry basis mass of the solution polymerized crude rubber.

11. The rubber composite according to claim 10, wherein the mass ratio of the first filler and the second filler is 1:(0.5-20).

12. The rubber composite according to claim 10, wherein the addition amount of the second rubber filler is 10-40 wt % of the dry basis mass of the solution polymerized crude rubber.

13. The rubber composite according to claim 10, wherein the rubber composite further comprises an auxiliary agent.

14. The rubber composite according to claim 13, wherein the auxiliary agent is one or more selected from the group consisting of a vulcanizing agent, an anti-aging agent, an accelerant, and an activator.

15. The rubber composite according to claim 10, wherein the solution-polymerized crude rubber is one or more selected from the group consisting of solution-polymerized styrene-butadiene rubber, polyisoprene rubber, cis-butadiene rubber, and butyl rubber.

16. A method for preparing the rubber composite comprising: mixing the solution polymerized crude rubber with a first filler and a second filler, and then vulcanizing the mixture to prepare a rubber composite; wherein the first filler is the rubber filler according to claim 1, and the second filler is a polydopamine-modified white carbon black; the total addition amount of the first rubber filler and the second rubber filler is 10-60 wt % of the dry basis mass of the solution polymerized crude rubber.

17. The method according to claim 16, wherein the mass ratio of the first filler and the second filler is 1:(0.5-20); or the addition amount of the second rubber filler is 10-40 wt % of the dry basis mass of the solution polymerized crude rubber.

18. (canceled)

19. The method according to claim 16, wherein an auxiliary agent is further added in the mixing step: or the auxiliary agent is one or more selected from the group consisting of a vulcanizing agent, an anti-aging agent, an accelerant, and an activator.

20. (canceled)

21. The method according to claim 16, wherein the solution-polymerized crude rubber is one or more selected from the group consisting of solution-polymerized styrene-butadiene rubber, polyisoprene rubber, cis-butadiene rubber, and butyl rubber.

22. A tire comprising the rubber composite according to claim 10.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIG. 1 illustrates the infrared spectrogram of the white carbon black, the polydopamine-modified white carbon black, and the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black, respectively; wherein curve a illustrates the infrared spectrogram of the white carbon black; curve b illustrates the infrared spectrogram of the polydopamine-modified white carbon black; and curve c illustrates the infrared spectrogram of the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0020] The terminals and any value of the ranges disclosed herein are not limited to the precise ranges or values, such ranges or values shall be comprehended as comprising the values adjacent to the ranges or values. As for numerical ranges, the endpoint values of the various ranges, the endpoint values and the individual point values of the various ranges, and the individual point values may be combined with one another to produce one or more new numerical ranges, which should be deemed to have been specifically disclosed herein.

[0021] The first aspect of the present disclosure provides a rubber filler comprising polydivinylbenzene microspheres and polydopamine-modified white carbon black loaded on the polydivinylbenzene microspheres, wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(0.5-20), such as 1:0.5, 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10, 1:12, 1:14, 1:16, 1:18, 1:20, and a random value within the range consisting of any two numerical values, preferably is 1:(1-10).

[0022] The present disclosure uses polydivinylbenzene microspheres with high adsorption capacity, primarily for loading, the present disclosure does not impose limitations to the specific loading patterns of the polydopamine-modified white carbon black, as long as it can be loaded on the polydivinylbenzene microspheres. When the polydopamine-modified white carbon black is loaded on the polydivinylbenzene microspheres (DVB), it may be loaded on the surface of the polydivinylbenzene microspheres, or loaded in the interior pores and channels of the polydivinylbenzene microspheres, or both. It has been found in research that the polydopamine-modified white carbon black mainly deposits on the surface of microspheres.

[0023] The present disclosure uses the polydopamine to modify white carbon black, which can prevent the white carbon black from self-agglomerating, and improve the dispersibility of the white carbon black. The catecholamine structure of polydopamine has a higher affinity which can tightly bind with rubber, thereby improving the mechanical strength of the white carbon black/rubber. The dispersibility of the white carbon black is improved more efficiently by using polydivinylbenzene microspheres as the carriers, and the microspheres are desirably compatible with rubber, the microspheres having a high adsorption capacity can be used as a loading filler, during a process of using the rubber filler is used for preparing the rubber composite, the polydivinylbenzene microspheres also function as physical entanglement of the cross-linking points, its physical cross-linking with blended rubber can effectively enhance the physical and mechanical properties of the material, the rubber composite is suitable for manufacturing the green tires.

[0024] In some embodiments of the present disclosure, the mass ratio of the white carbon black and polydopamine in the polydopamine-modified white carbon black is 1:(0.05-1), such as 1:0.05, 1:0.08, 1:0.1, 1:0.2, 1:0.3, 1:0.4, 1:0.5, 1:0.6, 1:0.7, 1:0.8, 1:0.9, 1:1, and a random value within the range consisting of any two numerical values, preferably is 1:(0.1-0.6).

[0025] In some embodiments of the present disclosure, the polydivinylbenzene microspheres have a particle size within the range of 0.1-1 m, for example, 0.1 m, 0.2 m, 0.3 m, 0.4 m, 0.5 m, 0.6 m, 0.7 m, 0.8 m, 0.9 m, 1 m, and a random value within the range consisting of any two numerical values, preferably within the range of 0.2-0.5 m.

[0026] In some embodiments of the present disclosure, the white carbon black has a particle size within the range of 20-60 nm, e.g., 20 nm, 30 nm, 40 nm, 50 nm, 60 nm, and a random value within the range consisting of any two numerical values, preferably within the range of 30-50 nm.

[0027] The second aspect of the present disclosure provides a method for preparing the rubber filler comprising: [0028] (1) carrying out a first reaction on the white carbon black and dopamine in a first buffer solution to obtain a polydopamine-modified white carbon black; [0029] (2) subjecting the polydivinylbenzene microspheres to a second reaction in a second buffer solution with the polydivinylbenzene microspheres obtained in step (1) to obtain the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres to the polydopamine-modified white carbon black is 1:(0.5-20), such as 1:0.5, 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10, 1:12, 1:14, 1:16, 1:18, 1:20, and a random value within the range consisting of any two numerical values, preferably is 1:(1-10).

[0030] As shown in FIG. 1, curve a illustrates the infrared spectrogram of the white carbon black; curve b shows the infrared spectrogram of the polydopamine-modified white carbon black; and curve c exhibits the infrared spectrogram of the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black, wherein curve a exhibits an asymmetric stretching vibration absorption peaks of SiOSi at a wave number of 1099 cm.sup.1, a symmetric stretching vibration absorption peak of SiOSi at a wave number of 804 cm.sup.1, and a bending vibration absorption peaks of SiOSi at a wave number of 465 cm.sup.1. Curve b shows a weak absorption peak of the benzene ring (1600-1450 cm.sup.1), which can be attributed to the absorption of the benzene ring in polydopamine; in curve c, the broadening and enlargement of the absorption peak around 3450 cm.sup.1 is caused by the phenolic hydroxyl group and NH bond carried by the loaded polydopamine, indicating the successful loading of the polydopamine-modified white carbon black on the polydivinylbenzene microspheres.

[0031] In some embodiments of the present disclosure, step (1) specifically comprises: [0032] adding an inorganic acid or inorganic base into a weak alkalinity buffering agent solution to obtain a first buffer solution with a pH of 7.5-10.5, wherein the concentration of the buffering agent in the first buffer solution is within the range of 3-15 mmol/L; [0033] adding white carbon black and dopamine into the first buffer solution, carrying out the reaction for 0.5-2 h at room temperature, then filtering, washing, and drying to obtain the polydopamine-modified white carbon black.

[0034] In the present disclosure, the dried white carbon black is used during the modification process of the white carbon black. The dried white carbon black may be obtained by using the drying techniques commonly used in the art, such as drying the white carbon black in a vacuum at the temperature of 100-120 C.

[0035] Further, the mass ratio of the white carbon black and dopamine is 1:(0.05-1), such as 1:0.05, 1:0.08, 1:0.1, 1:0.2, 1:0.3, 1:0.4, 1:0.5, 1:0.6, 1:0.7, 1:0.8, 1:0.9, 1:1, and a random value within the range consisting of any two numerical values, preferably is 1:(0.1-0.6).

[0036] Furthermore, the mass ratio of the white carbon black to the first buffer solution is 1:(5-50), for example, 1:5, 1:10, 1:15, 1:20, 1:25, 1:30, 1:40, 1:45, 1:50, and a random value within the range consisting of any two numerical values, preferably is 1:(10-40).

[0037] Moreover, the weak alkalinity buffering agent is one or more selected from the group consisting of trihydroxymethyl aminomethane, barbital, barbital-sodium chloride composite buffering agent, boric acid-potassium chloride composite buffering agent, borax-calcium chloride composite buffering agent, disodium hydrogen phosphate, and dipotassium hydrogen phosphate-potassium dihydrogen phosphate composite buffering agent; preferably trihydroxymethyl aminomethane or barbital.

[0038] Further, the inorganic acid is one or more of hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid.

[0039] Further, the inorganic base is potassium hydroxide and/or sodium hydroxide.

[0040] In some embodiments of the present disclosure, step (2) specifically comprises: [0041] adding an inorganic acid or inorganic base into a weak alkalinity buffering agent solution to obtain a second buffer solution with a pH of 7.5-10.5, wherein the concentration of the buffering agent in the second buffer solution is within the range of 3-15 mmol/L; [0042] adding polydivinylbenzene microspheres and the polydopamine-modified white carbon black obtained in step (1) into the second buffer solution, carrying out the reaction with magnetic stirring at room temperature for 1-4 h, then filtering, washing, and drying to obtain the polydivinylbenzene microspheres loaded with the polydopamine-modified white carbon black.

[0043] Further, the mass ratio of the polydivinylbenzene microspheres and the second buffer solution is 1:(50-500), such as 1:50, 1:100, 1:150, 1:200, 1:250, 1:300, 1:400, 1:450, 1:500, and a random value within the range consisting of any two numerical values, preferably is 1:(100-400).

[0044] Further, the weak alkalinity buffering agent is one or more selected from the group consisting of trihydroxymethyl aminomethane, barbital, barbital-sodium chloride composite buffering agent, boric acid-potassium chloride composite buffering agent, borax-calcium chloride composite buffering agent, disodium hydrogen phosphate, and dipotassium hydrogen phosphate-potassium dihydrogen phosphate composite buffering agent; preferably trihydroxymethyl aminomethane or barbital.

[0045] Furthermore, the inorganic acid is one or more of hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid.

[0046] Further, the inorganic base is potassium hydroxide and/or sodium hydroxide.

[0047] The third aspect of the present disclosure provides a rubber composite comprising a solution polymerized crude rubber, a first filler, and a second filler, wherein the first filler is the rubber filler according to the first aspect, or the rubber filler produced with the aforementioned method according to the second aspect, and the second filler is a polydopamine-modified white carbon black, wherein the total addition amount of the first rubber filler and the second rubber filler is 10-60 wt % of the dry basis mass of the solution polymerized crude rubber, such as 10 wt %, 15 wt %, 20 wt %, 25 wt %, 30 wt %, 35 wt %, 40 wt %, 45 wt %, 50 wt %, 55 wt %, 60 wt %, and a random value within the range consisting of any two numerical values, preferably 20-40 wt %.

[0048] In some embodiments of the present disclosure, the mass ratio of the first filler and the second filler is 1:(0.5-20), e.g., 1:0.5, 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10, 1:12, 1:14, 1:16, 1:18, 1:20, and a random value within the range consisting of any two numerical values, preferably is 1:(1-10).

[0049] In some embodiments of the present disclosure, the addition amount of the second rubber filler is 10-40 wt % of the dry basis mass of the solution polymerized crude rubber, such as 10 wt %, 15 wt %, 20 wt %, 25 wt %, 30 wt %, 35 wt %, 40 wt %, and a random value within the range consisting of any two numerical values, preferably 20-30 wt %.

[0050] In some embodiments of the present disclosure, the rubber composite further comprises an auxiliary agent.

[0051] Further, the auxiliary agent is one or more selected from the group consisting of a vulcanizing agent, an anti-aging agent, an accelerant, and an activator.

[0052] The types, functions, and addition amounts of the auxiliary agents in the invention are well-known among those skilled in the art, for instance, the relevant content is described in the textbook Practical Rubber Formulation Technology, it will not be repeatedly described herein.

[0053] In some embodiments of the invention, the solution-polymerized crude rubber is one or more selected from the group consisting of solution-polymerized styrene-butadiene rubber, polyisoprene rubber, cis-butadiene rubber, and butyl rubber.

[0054] Further, the number average molecular weight Mn of the solution polymerized styrene-butadiene rubber before coupling is within the range of 100,000-400,000 g/mol, and the content of vinyl is within the range of 30-70 wt %.

[0055] Further, the weight average molecular weight Mw of the polyisoprene rubber is within the range of 150,000-300,000 g/mol.

[0056] Further, the weight average molecular weight Mw of the cis-butadiene rubber is within the range of 200,000-300,000 g/mol.

[0057] Further, the weight average molecular weight Mw of the butyl rubber is within the range of 100,000-500,000 g/mol.

[0058] The fourth aspect of the present disclosure provides a method for preparing the rubber composite comprising: [0059] mixing the solution polymerized crude rubber with a first filler and a second filler, and then vulcanizing the mixture to obtain a rubber composite; wherein the first filler is the rubber filler according to the first aspect, or the rubber filler produced with the aforementioned preparation method according to the second aspect, and the second filler is a polydopamine-modified white carbon black; the total addition amount of the first rubber filler and the second rubber filler is 10-60 wt % of the dry basis mass of the solution polymerized crude rubber, e.g., 10 wt %, 15 wt %, 20 wt %, 25 wt %, 30 wt %, 35 wt %, 40 wt %, 45 wt %, 50 wt %, 55 wt %, 60 wt %, and a random value within the range consisting of any two numerical values, preferably is 20-40 wt %.

[0060] The present disclosure uses the polydopamine-modified white carbon black loaded polydivinylbenzene microspheres as a first rubber filter, which can prevent the white carbon black from self-agglomerating, and improve dispersibility and stability of the white carbon black; in addition, the polydopamine-modified white carbon black can prevent the white carbon black from self-agglomerating, improve dispersity of the white carbon black and enhance the mechanical strength of the white carbon black/rubber, during the preparation process of the rubber composite, the polydivinylbenzene microspheres can also function as physical entanglement of the cross-linking points, its physical cross-linking action with blended rubber can effectively enhance the physical and mechanical properties of the material, mainly improve the strength, hardness, and wear resistance of the rubber material, the two rubber fillers produce a synergistic effect, the polydivinylbenzene microspheres are used as the carriers, such that the polydopamine-modified white carbon black is more effectively dispersed and obtain an improved stability, the overall performance of the material is improved more effectively than a single filler, and the obtained rubber composite is suitable for manufacturing the green tires.

[0061] In the present disclosure, a conventional mixing method may be employed in the rubber mixing process, for example, mixing by an open mill and mixing by an internal mixer.

[0062] In some embodiments of the present disclosure, the mass ratio of the first filler and the second filler is 1:(0.5-20), e.g., 1:0.5, 1:1, 1:2, 1:3, 1:4, 1:5, 1:6, 1:7, 1:8, 1:9, 1:10, 1:12, 1:14, 1:16, 1:18, 1:20, and a random value within the range consisting of any two numerical values, preferably is 1:(1-10).

[0063] In some embodiments of the present disclosure, the addition amount of the second rubber filler is 10-40 wt % of the dry basis mass of the solution polymerized crude rubber, e.g., 10 wt %, 15 wt %, 20 wt %, 25 wt %, 30 wt %, 35 wt %, 40 wt %, and a random value within the range consisting of any two numerical values, preferably is 20-30 wt %.

[0064] In some embodiments of the present disclosure, an auxiliary agent is further added in the mixing step.

[0065] Further, the auxiliary agent is one or more selected from the group consisting of a vulcanizing agent, an anti-aging agent, an accelerant, and an activator.

[0066] One or more auxiliary agents of a vulcanizing agent, an anti-aging agent, an accelerant, and an activator may be added in the rubber mixing process, and the addition amount and the function of the auxiliary agents are well-known among those skilled in the art, for example, the relevant content is described in the textbook Practical Rubber Formulation Technology, it will not be repeatedly described herein.

[0067] In some embodiments of the present disclosure, the solution-polymerized crude rubber is one or more selected from the group consisting of solution-polymerized styrene-butadiene rubber, polyisoprene rubber, cis-butadiene rubber, and butyl rubber.

[0068] Further, the number average molecular weight Mn of the solution polymerized styrene-butadiene rubber before coupling is within the range of 100,000-400,000 g/mol, and the content of vinyl is within the range of 30-70 wt %.

[0069] Further, the weight average molecular weight Mw of the polyisoprene rubber is within the range of 150,000-300,000 g/mol.

[0070] Further, the weight average molecular weight Mw of the cis-butadiene rubber is within the range of 200,000-300,000 g/mol.

[0071] Further, the weight average molecular weight Mw of the butyl rubber is within the range of 100,000-500,000 g/mol.

[0072] The fifth aspect of the present disclosure provides a use of the aforementioned rubber composite or the rubber composite produced with the aforementioned preparation method in a tire.

[0073] The rubber composite of the present disclosure solves the dispersibility problem of white carbon black and addresses the problem that the white carbon black has poor binding force with the rubber, thereby improving the comprehensive operational performance of the tires.

[0074] Further, the aforementioned rubber composite is used in green tires.

[0075] The present disclosure solves the problem that the white carbon black is apt to agglomerate and the white carbon black has poor binding force with the rubber. In addition, the polydivinylbenzene microspheres are used as the carriers, so that the dispersibility of the white carbon black can be more effectively improved, the polydivinylbenzene microspheres can also function as physical entanglement of the cross-linking points, its physical cross-linking action with blended rubber can effectively enhance the physical and mechanical properties of the material, and the polydivinylbenzene microspheres can be used for manufacturing the green tires. Moreover, the method of the present disclosure has the advantages of fewer reaction steps and simple operations.

[0076] Unless otherwise specified in the present disclosure, % refers to mass percent.

[0077] The technical solutions in the present disclosure will be clearly and completely described below with reference to examples, it is obvious that the examples described herein are a portion of examples in the present disclosure, instead of the entire examples of the present disclosure. All other examples, which can be obtained by those skilled in the art without paying any creative labor based on the examples in the present disclosure, fall into the protection scope of the present disclosure.

[0078] If the specific conditions are not indicated in the following examples and comparative examples, the reactions are performed according to the conventional conditions or the conditions suggested by the manufacturers. If the manufacturers of the reagent or instrument are not specified, both the reagent and the instrument pertain to the commercially available conventional products.

[0079] In the following examples of the present disclosure, [0080] (1) The sources of raw materials were as follows: [0081] The white carbon black was purchased from Weifang Wanli Additive Co., Ltd.; [0082] Dopamine and trihydroxymethyl aminomethane with a purity of 99.5% were commercially available from Acros Organics Corporation; [0083] Barbital, sodium chloride, borax, calcium chloride, boric acid, potassium chloride, dipotassium phosphate, potassium dihydrogen phosphate, and disodium hydrogen phosphate, with a purity of 99%, were commercially available from the Sinopharm Group Chemical Reagent Co., Ltd.; [0084] Polydivinylbenzene microspheres with a particle size of 0.2-0.5 m were purchased from Suzhou Zhiwei Nano Technology Co., Ltd.; [0085] The solution polymerized styrene-butadiene rubber glue solution was purchased from Lanzhou Chemical Research Center and Dushanzi Petrochemical Company; [0086] The polyisoprene rubber was commercially available from PetroChina Jilin Petrochemical Company and Lanzhou Chemical Research Center; [0087] The butyl rubber was commercially available from Bayer Corporation in Germany.

[0088] The addition amount of the first rubber filler and the second rubber filler calculated is based on the dry basis mass of the solution polymerized crude rubber. Taking the first buffer in Example 1 as an example, the method of preparing the first buffer solution comprises: preparing a solution with a concentration of 9 mmol/L of trihydroxymethyl aminomethane, then adding hydrochloric acid or sodium hydroxide into the solution to adjust the pH of the solution to 8.5. [0089] (2) The analysis and test methods:

[0090] Infrared spectrum analysis of the samples: the functional group analysis was performed on the nanometer white carbon black samples before and after modification with the infrared spectrometer manufactured by BRUKER OPTICS GMBH in Germany. Samples were dried in a vacuum oven at 100 C., and subjected to tablet pressing with potassium bromide, the collected wave number range was from 400 cm.sup.1 to 4000 cm.sup.1.

[0091] Differential thermal analysis of polymer deposition: the deposition amount of polydopamine was assayed by using the synchronous thermal analyzer (TG/DSC, STA 449C) manufactured by NETZSCH GMBH in Germany. The samples were subjected to drying in a vacuum oven at 100 C., and the weight loss data of the samples in the temperature range of 20-600 C. was collected.

[0092] Glass-transition temperature analysis: the glass-transition temperature was determined by using a synchronous thermal analyzer (TG/DSC, STA449C) manufactured by NETZSCH GMBH in Germany.

[0093] Dynamical and mechanical properties analysis: the mechanical properties of the samples were tested by using a universal material testing machine with a model 5567, manufactured by Instron Corporation in the United States of America (USA).

[0094] Tensile strength, and elongation at break: tested according to the China National Standard GB/T528-2009;

[0095] Shore A hardness: measured according to the China National Standard GB/T531.1-2008.

Example 1

[0096] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 100 C.; the dried white carbon black and dopamine were added into a prepared trihydroxymethyl aminomethane buffer solution with a pH of 8.5 (the concentration of trihydroxymethyl aminomethane was 9 mmol/L), carried out the reaction at room temperature for 1.5 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified white carbon black, which was marked as polydopamine-modified white carbon black-1; wherein the mass ratio of the white carbon black and dopamine was 1:0.1, and the mass ratio of the white carbon black and the buffer solution was 1:20; [0097] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-1 prepared in step (1) was subjected to drying under vacuum at 100 C.; polydivinylbenzene microspheres with a particle size of 0.2 m, the dried polydopamine-modified white carbon black-1, and the prepared trihydroxymethyl aminomethane buffer solution with a pH of 8.5 (the concentration of trihydroxymethyl aminomethane was 9 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 3 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-1 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-1 was 1:5; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:300; [0098] (3) Preparation of a rubber composite: the solution polymerized styrene-butadiene rubber-1 (the parameters were shown in Table 1), the polydopamine-modified white carbon black-1 obtained in step (1), the polydivinylbenzene microspheres-1 loaded with polydopamine-modified white carbon black obtained in step (2), and other auxiliary agents were mixed, wherein the formula of the solution polymerized crude rubber and the other auxiliary agents were shown in Table 2, the addition amount of the polydopamine-modified white carbon black-1 was 17 wt % of the solution polymerized styrene-butadiene rubber-1, and the addition amount of the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black-1 was 3 wt % of the solution polymerized styrene-butadiene rubber-1; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/solution polymerized butadiene-styrene rubber composite, which was denoted as A-1, and the test results were shown in Table 7.

TABLE-US-00001 TABLE 1 Parameters of the solution polymerized butadiene-styrene rubber-1 Sample name Styrene Vinyl Mn (before coupling) Tg Solution polymerized 25% 55% 300,000 g/mol 30 C. styrene-butadiene rubber-1

TABLE-US-00002 TABLE 2 Formulation of rubber materials Parts by Category of Name of raw materials weight raw materials Solution polymerized 100 Synthetic rubber crude rubber Rubber filler 10-60 Reinforcing agent Other Zinc oxide 3 Activator auxiliary Stearic acid 2 Activator agents Anti-aging 1 Anti-aging agent agent 4020 Sulfur 1.5 Vulcanizing agent Accelerant NZ 0.9 Accelerant

[0099] In table 2, the weight part of Solution polymerized crude rubber is based on the dry basis mass of the solution polymerized crude rubber, the weight part of rubber filler means the total weight parts of the first rubber filler and the second rubber filler.

Example 2

[0100] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared trihydroxymethyl aminomethane buffer solution with a pH of 9 (the concentration of trihydroxymethyl aminomethane was 6 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-2; wherein the mass ratio of the white carbon black and dopamine was 1:0.2, and the mass ratio of the white carbon black and the buffer solution was 1:30; [0101] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-2 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.4 m, the dried polydopamine-modified white carbon black-2, and the prepared trihydroxymethyl aminomethane buffer solution with a pH of 9 (the concentration of trihydroxymethyl aminomethane was 6 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-2 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-2 was 1:7; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:400; [0102] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-2 obtained in step (1), the polydivinylbenzene microspheres-2 loaded with polydopamine-modified white carbon black obtained in step (2), the solution polymerized butadiene-styrene rubber-2 (its parameters were shown in Table 3), and other auxiliary agents were mixed, wherein the formula of the solution polymerized crude rubber and the other auxiliary agents were shown in Table 2, the addition amount of the polydopamine-modified white carbon black-2 in step (1) was 20 wt % of the solution polymerized styrene-butadiene rubber-2, and the addition amount of the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black-2 was 5 wt % of the solution polymerized styrene-butadiene rubber-2; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/solution polymerized butadiene-styrene rubber composite, which was denoted as A-2, and the test results were shown in Table 7.

TABLE-US-00003 TABLE 3 Parameters of the solution polymerized butadiene-styrene rubber-2 Mn (before Sample name Styrene Vinyl coupling) Tg Solution polymerized 25% 65% 260,000 g/mol 25 C. styrene-butadiene rubber-2

Example 3

[0103] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared trihydroxymethyl aminomethane buffer solution with a pH of 9 (the concentration of trihydroxymethyl aminomethane was 10 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-3; wherein the mass ratio of the white carbon black and dopamine was 1:0.3, and the mass ratio of the white carbon black and the buffer solution was 1:30; [0104] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-3 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.3 m, the dried polydopamine-modified white carbon black-3, and the prepared trihydroxymethyl aminomethane buffer solution with a pH of 9 (the concentration of trihydroxymethyl aminomethane was 10 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-3 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-3 was 1:8; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:400; [0105] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-3 obtained in step (1), the polydivinylbenzene microspheres-3 loaded with polydopamine-modified white carbon black obtained in step (2), solution polymerized styrene-butadiene rubber-3 (its parameters were shown in Table 4), and other auxiliary agents were mixed, wherein the formula of the solution polymerized crude rubber and the other auxiliary agents were shown in Table 2, the addition amount of the polydopamine-modified white carbon black-3 in step (1) was 25 wt % of the solution polymerized styrene-butadiene rubber-3, and the addition amount of the polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black-3 was 5 wt % of the solution polymerized styrene-butadiene rubber-3; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/solution polymerized butadiene-styrene rubber composite, which was denoted as A-3, and the test results were shown in Table 7.

TABLE-US-00004 TABLE 4 Parameters of solution polymerized styrene-butadiene rubber-3 Mn (before Sample name Styrene Vinyl coupling) Tg Solution polymerized 25% 70% 230,000 g/mol 23 C. styrene-butadiene rubber-3

Example 4

[0106] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared barbital/sodium chloride buffer solution with a pH of 8.5 (the concentration of barbital/sodium chloride was 6 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-4; wherein the mass ratio of the white carbon black and dopamine was 1:0.1, and the mass ratio of the white carbon black and the buffer solution was 1:20; [0107] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-4 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.3 m, the dried polydopamine-modified white carbon black-4, and the prepared barbital/sodium chloride buffer solution with a pH of 8.5 (the concentration of barbital/sodium chloride was 6 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-4 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-4 was 1:5; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:300; [0108] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-4 obtained in step (1), the polydivinylbenzene microspheres-4 loaded with polydopamine-modified white carbon black obtained in step (2), polyisoprene rubber-1, and other auxiliary agents were mixed, wherein the formula of the solution polymerized crude rubber and the other auxiliary agents were shown in Table 2, the parameters of polyisoprene rubber-1 were shown in Table 5; wherein the addition amount of the polydopamine-modified white carbon black-4 in step (1) was 17 wt % of the polyisoprene rubber, and the addition amount of the polydivinylbenzene microspheres-4 loaded with polydopamine-modified white carbon black in step (2) was 3 wt % of the polyisoprene rubber; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/polyisoprene rubber composite, which was denoted as A-4, and the test results were shown in Table 7.

TABLE-US-00005 TABLE 5 Parameters of polyisoprene rubber-1 Mooney Content of cis- Content of Mw viscosity 1,4 structure 3,4-structure (10,000 ML (1 + 4) Sample name (wt %) (wt %) g/mol) 100 C. Polyisoprene 96.1 4.4 23 73 rubber-1

Example 5

[0109] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared barbital/sodium chloride buffer solution with a pH of 8 (the concentration of barbital/sodium chloride was 9 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-5; wherein the mass ratio of the white carbon black and dopamine was 1:0.3, and the mass ratio of the white carbon black and the buffer solution was 1:25; [0110] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-5 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.4 m, the dried polydopamine-modified white carbon black-5, and the prepared barbital/sodium chloride buffer solution with a pH of 8 (the concentration of barbital/sodium chloride was 9 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-5 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-5 was 1:8; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:400; [0111] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-5 obtained in step (1), the polydivinylbenzene microspheres-5 loaded with polydopamine-modified white carbon black obtained in step (2), polyisoprene rubber-2, and other auxiliary agents were mixed, wherein the formula of the solution polymerized crude rubber and the other auxiliary agents were shown in Table 2, the parameters of polyisoprene rubber-2 rubber were shown in Table 6; wherein the addition amount of the polydopamine-modified white carbon black-5 in step (1) was 24 wt % of the polyisoprene rubber-2, and the addition amount of the polydivinylbenzene microspheres-5 loaded with polydopamine-modified white carbon black in step (2) was 6 wt % of the polyisoprene rubber-2; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/polyisoprene rubber composite, which was denoted as A-5, and the test results were shown in Table 7.

TABLE-US-00006 TABLE 6 Parameters of polyisoprene rubber-2 Mooney Content of cis- Content of Mw viscosity 1,4 structure 3,4-structure (10,000 ML (1 + 4) Sample name (wt %) (wt %) g/mol) 100 C. Polyisoprene 95.9 4.4 25 75 rubber-2

Example 6

[0112] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared barbital/sodium chloride buffer solution with a pH of 8.5 (the concentration of barbital/sodium chloride was 8 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-6; wherein the mass ratio of the white carbon black and dopamine was 1:0.1, and the mass ratio of the white carbon black and the buffer solution was 1:20; [0113] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-6 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.2 m, the dried polydopamine-modified white carbon black-6, and the prepared barbital/sodium chloride buffer solution with a pH of 8.5 (the concentration of barbital/sodium chloride was 8 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-6 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-6 was 1:5; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:300; [0114] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-6 obtained in step (1), the polydivinylbenzene microspheres-6 loaded with polydopamine-modified white carbon black obtained in step (2), butyl rubber and other auxiliary agents were mixed, wherein the formula of the solution polymerized rubber crude rubber and the other auxiliary agents were shown in Table 2, wherein the addition amount of the polydopamine-modified white carbon black-6 in step (1) was 20 wt % of the butyl rubber, and the addition amount of the polydivinylbenzene microspheres-6 loaded with polydopamine-modified white carbon black in step (2) was 5 wt % of the butyl rubber; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/butyl rubber composite, which was denoted as A-6, and the test results were shown in Table 7.

Example 7

[0115] (1) Modification of the white carbon black: the white carbon black was subjected to drying under vacuum at 110 C.; the dried white carbon black and dopamine were added into a prepared barbital/sodium chloride buffer solution with a pH of 7.8 (the concentration of barbital/sodium chloride was 9 mmol/L), carried out the reaction at room temperature for 2 h, the reaction product was then subjected to filtering, washing, and drying to obtain a polydopamine-modified nanometer white carbon black, which was marked as polydopamine-modified white carbon black-7; wherein the mass ratio of the white carbon black and dopamine was 1:0.2, and the mass ratio of the white carbon black and the buffer solution was 1:25; [0116] (2) Preparation of polydivinylbenzene microspheres (DVB) loaded with the polydopamine-modified white carbon black: the polydopamine-modified white carbon black-7 prepared in step (1) was subjected to drying under vacuum at 110 C.; polydivinylbenzene microspheres with a particle size of 0.4 m, the dried polydopamine-modified white carbon black-7, and the prepared barbital/sodium chloride buffer solution with a pH of 7.8 (the concentration of barbital/sodium chloride was 9 mmol/L) were added into a round-bottomed flask, the reaction was performed with a magnetic stirring at room temperature for 4 h, the reaction product was then subjected to filtering, washing, and drying to obtain the polydivinylbenzene microspheres-7 loaded with polydopamine-modified white carbon black; wherein the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-7 was 1:8; the mass ratio of the polydivinylbenzene microspheres and the buffer solution was 1:400; [0117] (3) Preparation of a rubber composite: the polydopamine-modified white carbon black-7 obtained in step (1), the polydivinylbenzene microspheres-7 loaded with polydopamine-modified white carbon black obtained in step (2), butyl rubber, and other auxiliary agents were mixed, wherein the formula of the solution polymerized rubber crude rubber and the other auxiliary agents were shown in Table 2, wherein the addition amount of the polydopamine-modified white carbon black-7 in step (1) was 30 wt % of the butyl rubber, and the addition amount of the polydivinylbenzene microspheres-7 loaded with polydopamine-modified white carbon black in step (2) was 10 wt % of the butyl rubber; the mixture was then subjected to vulcanizing to prepare a rubber composite, namely polydivinylbenzene microsphere filler loaded with polydopamine-modified white carbon black/butyl rubber composite, which was denoted as A-7, and the test results were shown in Table 7.

Example 8

[0118] The rubber composite was prepared according to the method of Example 7, except that the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-7 in step (2) was 1:1; a rubber composite was prepared, which was denoted as A-8, and the test results were shown in Table 7.

Example 9

[0119] The rubber composite was prepared according to the method of Example 7, except that the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-7 in step (2) was 1:0.5; a rubber composite was prepared, which was denoted as A-9, and the test results were shown in Table 7.

Example 10

[0120] The rubber composite was prepared according to the method of Example 7, except that the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-7 in step (2) was 1:10; a rubber composite was prepared, which was denoted as A-10, and the test results were shown in Table 7.

Example 11

[0121] The rubber composite was prepared according to the method of Example 7, except that the mass ratio of the polydivinylbenzene microspheres and the polydopamine-modified white carbon black-7 in step (2) was 1:15; a rubber composite was prepared, which was denoted as A-11, and the test results were shown in Table 7.

Example 12

[0122] The rubber composite was prepared according to the method of Example 7, except that in step (3) preparation process of rubber composite, the addition amount of the polydopamine-modified white carbon black-7 in step (1) was 20 wt % of the butyl rubber, and the addition amount of the polydivinylbenzene microspheres-7 loaded with polydopamine-modified white carbon black in step (2) was 40 wt % of the butyl rubber; a rubber composite was prepared, which was denoted as A-12, and the test results were shown in Table 7.

Example 13

[0123] The rubber composite was prepared according to the method of Example 7, except that in in step (3) preparation process of rubber composite, the addition amount of the polydopamine-modified white carbon black-7 in step (1) was 40 wt % of the butyl rubber, and the addition amount of the polydivinylbenzene microspheres-7 loaded with polydopamine-modified white carbon black in step (2) was 20 wt % of the butyl rubber; a rubber composite was prepared, which was denoted as A-13, and the test results were shown in Table 7.

Comparative Example 1

[0124] The rubber composite was prepared according to the method of Example 1, except that step (2) was not carried out, and step (3) preparation of a rubber composite: the white carbon black occupied 17 wt % of the solution polymerized styrene-butadiene rubber, the polydopamine-modified white carbon black-1 occupied 13 wt % of the solution polymerized styrene-butadiene rubber, the solution polymerized crude rubber and other auxiliary agents as shown in Table 2 were mixed; the mixture was then subjected to vulcanizing to prepare a sample of the white carbon black/solution polymerized butadiene-styrene rubber composite, which was denoted as D-1, and the test results were shown in Table 7.

Comparative Example 2

[0125] The rubber composite was prepared according to the method of Example 1, except that in step (3) preparation of a rubber composite, the polydopamine-modified white carbon black-1 of step (1) was not added, the addition amount of the polydivinylbenzene microspheres-1 loaded with the polydopamine-modified white carbon black of step (2) was 10 wt % of the solution polymerized styrene-butadiene rubber-1; a rubber composite was obtained, which was denoted as D-2, and the test results were shown in Table 7.

Comparative Example 3

[0126] The rubber composite was prepared according to the method of Example 1, except that in step (3) preparation of a rubber composite, the polydivinylbenzene microspheres-1 loaded with the polydopamine-modified white carbon black in step (2) was not added, the addition amount of the polydopamine-modified white carbon black-1 in step (1) was 40 wt % of the solution polymerized styrene-butadiene rubber-1; a rubber composite was obtained, which was denoted as D-3, and the test results were shown in Table 7.

Comparative Example 4

[0127] The rubber composite was prepared according to the method of Example 3, except that the step (2) was not carried out, and step (3) preparation of a rubber composite: the white carbon black occupied 25 wt % of the solution polymerized styrene-butadiene rubber, the polydopamine-modified white carbon black-3 obtained in step (1) occupied 5 wt % of the solution polymerized styrene-butadiene rubber, the solution polymerized crude rubber and other auxiliary agents as shown in Table 2 were mixed; the mixture was then subjected to vulcanizing to prepare a sample of the white carbon black/solution polymerized butadiene-styrene rubber composite, which was denoted as D-4, and the test results were shown in Table 7.

TABLE-US-00007 TABLE 7 Test results of the rubber composite Tensile Elongation Shore A Tear Glass-transition Sample strength at break hardness strength temperature name (MPa) (%) (degree) (kN/m) ( C.) A-1 15.5 561 56 23.5 22.7 A-2 16.6 571 57 22.5 21.6 A-3 17.5 493 57 23.7 19.2 A-4 26.3 776 46 32 71.3 A-5 27.5 796 49 34 68.3 A-6 15.5 470 56 23.1 66.2 A-7 17.6 480 62 25.1 64.6 A-8 18.7 490 64 26.1 63.4 A-9 18.4 487 63 25.2 61.5 A-10 18.5 492 53 23.7 60.7 A-11 18.3 493 51 23.2 59.4 A-12 18.9 510 65 27.1 64.6 A-13 16.9 479 60 23.6 63.7 D-1 9.9 501 52 15.3 19.7 D-2 11.5 507 54 17.5 21.9 D-3 10.2 503 52 16.3 20.5 D-4 9.7 438 56 16.7 17.3

[0128] As can be seen from the results of Table 7, the Examples have significantly better effects than the Comparative Examples. The polydivinylbenzene microspheres loaded with polydopamine-modified white carbon black are used in the present disclosure as a filler to replace a part of the polydopamine-modified white carbon black, and uses the polydivinylbenzene microspheres as a carrier, so that the modified white carbon black is not apt to agglomerate, the dispersibility of the modified white carbon black is improved, the dispersity and stability of the modified white carbon black can be more effectively enhanced; in addition, the modified polydivinylbenzene microspheres can also play a role in an entanglement of crosslinking points, may generate an interaction force with the white carbon black due to the polar functional groups on their surface; moreover, the modified polydivinylbenzene microspheres improve the physical and mechanical properties of the material through the vulcanization and cross-linking effects.

[0129] The above content describes in detail the preferred embodiments of the present disclosure, but the present disclosure is not limited thereto. A variety of simple modifications can be made in regard to the technical solutions of the present disclosure within the scope of the technical concept of the present disclosure, including a combination of individual technical features in any other suitable manner, such simple modifications and combinations thereof shall also be regarded as the content disclosed by the present disclosure, each of them falls into the protection scope of the present disclosure.