METHOD FOR MANUFACTURE OF A MODIFIED ZSM-5 ZEOLITE IN THE PRESENCE OF ODSO

Abstract

A method for the preparation of a zeolite having MFI framework is provided that advantageously utilizes as a component oxidized disulfide oil, for example derived from a waste refinery stream of disulfide oil. The MFI framework zeolite is formed from an aqueous mixture of an aluminum source, a silica source, oxidized disulfide oil, an alkali metal source and a structure directing agent, which is heated under conditions and for a time effective to form the MFI framework zeolite.

Claims

1. A method for the preparation of a zeolite having MFI framework comprising: forming a homogeneous aqueous mixture of water soluble oxidized disulfide oil (ODSO), a silica source, an aluminum source, an alkali metal source, and a structure directing agent; heating the homogeneous aqueous mixture under conditions and for a time effective to form a crystalline zeolite as precipitate suspended in a supernatant as an intermediate suspension; recovering the precipitate from the intermediate suspension; and calcining the recovered precipitate is calcined at a suitable temperature, temperature ramp rate and for a suitable period of time at to realize porous MFI framework zeolite.

2. The method of claim 1, wherein the intermediate suspension has a pH of greater than about 9.

3. The method of claim 1, wherein the alkali metal source is sodium and the mass ratio of ODSO to sodium is less than about 9.

4. The method of claim 1, wherein the recovered porous MFI framework zeolite has a silica-to-alumina ratio in the range of about 20-1500.

5. The method as in claim 1, wherein the aluminum source comprises aluminates, alumina, other zeolites, aluminum colloids, boehmites, pseudo-boehmites, aluminum hydroxides, aluminum salts, aluminum alkoxides or alumina gels.

6. The method as in claim 1, wherein the silica source comprises sodium silicate (water glass), fumed silica, precipitated silica, colloidal silica, silica gels, zeolites, dealuminated zeolites, silicon hydroxides or silicon alkoxides.

7. The method as in claim 1, wherein the structure directing agent comprises quaternary ammonium cation compounds, bifunctional dicationic molecules containing a long aliphatic chain, dual-porogenic surfactants, silylated polyethylenimine polymers, amphiphilic organosilanes, or hydrophilic cationic polyelectroyltes/polymers.

8. The method as in claim 7, wherein the structure directing agent comprises quaternary ammonium cation compounds selected from the group consisting of tetramethylammonium (TMA) cation compounds, tetraethyl ammonium (TEA) cation compounds, tetrapropylammonium (TPA) cation compounds, tetrabutylammonium (TBA) cation compounds, cetyltrimethylammonium (CTA) cation compounds and combinations thereof.

9. The method as in claim 7, wherein the structure directing agent comprises bifunctional dicationic molecules selected from the group consisting of C.sub.22-6-6, C.sub.22-6-3, and poly(ethylene glycol).

10. The method of claim 1, wherein the ODSO comprises ODSO compounds having 3 or more oxygen atoms.

11. The method of claim 1, wherein the ODSO comprises ODSO compounds having 1 to 20 carbon atoms.

12. The method of claim 1, wherein the ODSO has an average density greater than about 1.0 g/cc.

13. The method of claim 1, wherein the ODSO has an average boiling point greater than about 80° C.

14. The method of claim 1, wherein the ODSO comprises ODSO compounds selected from the group consisting of (R—SOO—SO—R′), (R—SOO—SOO—R′), (R—SO—SOO—OH), (R—SOO—SOO—OH), (R—SO—SO—OH), (R—SOO—SO—OH), and mixtures thereof, where R and R′ can be the same or different and are alkyl groups comprising 1-10 carbon atoms.

15. The method of claim 1, wherein the homogeneous aqueous mixture is formed by: providing the silica source; and combining with the silica source the aluminum oxide source, the alkali metal source, and the structure directing agent; and the water soluble ODSO; wherein the water soluble ODSO is added after the aluminum oxide source, the alkali metal source, and the structure directing agent; or wherein the water soluble ODSO is first combined with the aluminum oxide source, the alkali metal source and the structure directing agent, and then combined with the silica source; and wherein an effective quantity of water for the homogeneous aqueous mixture is provided by using a water-containing silica source, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent.

16. The method of claim 1, wherein the homogeneous aqueous mixture is formed by: providing the aluminum oxide source, the alkali metal source and the structure directing agent as a first mixture; and combining the first mixture with the silica source and the water soluble ODSO; wherein the water soluble ODSO is added after the silica source; or wherein the water soluble ODSO is first combined with the silica source, and then combined with the first mixture, wherein an effective quantity of water for the homogeneous aqueous mixture is provided by using a water-containing silica source, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent.

17. The method of claim 1, wherein the homogeneous aqueous mixture is formed by: combining the water soluble ODSO with the silica source to form a first mixture; and combining the first mixture with the aluminum oxide source, alkali metal source and the structure directing agent; wherein an effective quantity of water for the homogeneous aqueous mixture is provided by using a water-containing silica source, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent.

18. The method of claim 1, wherein the homogeneous aqueous mixture is formed by: combining the water soluble ODSO with the aluminum oxide source, the alkali metal source and the structure directing agent to form a first mixture; and combining the first mixture with the silica source; wherein an effective quantity of water for the homogeneous aqueous mixture is provided by using a water-containing silica source, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent.

19. The method of claim 1, wherein an effective quantity of water for the homogeneous aqueous mixture is provided by using a water-containing silica source, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0024] The invention will be described in further detail below and with reference to the attached drawings in which the same or similar elements are referred to by the same number, and where:

[0025] FIG. 1 shows X-ray diffraction patterns of calcined ZSM-5 zeolites synthesized using ODSO, wherein diffractograms are provided for different ratios of ODSO/Na;

[0026] FIG. 2 is a plot of relative crystallinity as a function of ODSO/Na ratios, indicating crystalline or amorphous material;

[0027] FIG. 3 is a plot of thermogravimetric (TGA) and derivative thermogravimetric (DTG) mass loss profiles of the ZSM-5 zeolites synthesized in the presence of ODSO and water as in Examples 1-2 and the ZSM-5 zeolite of comparative Example 1 synthesized in the absence of ODSO (water only);

[0028] FIG. 4 is a plot of normalized yield as a function of ODSO/Na ratios, indicating crystalline or amorphous material;

[0029] FIG. 5 is a plot of ODSO/Na ratios against ODSO mass demonstrating transition between crystalline products and amorphous products;

[0030] FIG. 6 shows scanning electron microscopy images of the ZSM-5 zeolites synthesized in the presence of ODSO and water, and the ZSM-5 zeolite of comparative Example 1 synthesized in the absence of ODSO (water only);

[0031] FIG. 7 are diagrams representative of the crystallographic nature of the ZSM-5 zeolites synthesized in the presence of ODSO and water as in Examples 1-2.

DETAILED DESCRIPTION

[0032] Methods for the preparation of zeolites having MFI framework, such as a ZSM-5 zeolite, are provided. Effective quantities of water soluble ODSO, an aluminum source, a silica source, an alkali metal source, and a structure directing agent are formed as a homogeneous aqueous mixture. The components are mixed for an effective time and under conditions suitable to form the homogeneous aqueous mixture. The chronological sequence of mixing can vary, with the objective being a highly homogenous distribution of the components in an aqueous mixture. The homogeneous aqueous mixture is heated under conditions and for a time effective to form a precipitate suspended in a supernatant. The precipitate is recovered, for example by filtration, washing and drying. The recovered precipitate is calcined at a suitable temperature, temperature ramp rate and for a suitable period of time at to realize porous ZSM-5 zeolite having WI framework.

[0033] In certain embodiments, the homogeneous aqueous mixture is formed by: providing the silica source; combining the aluminum oxide source, the alkali metal source and the structure directing agent; and combining the water soluble ODSO. Alternatively, the water soluble ODSO is combined with the aluminum oxide source, the alkali metal source and the structure directing agent, and that mixture is combined with the silica source.

[0034] In certain embodiments, the homogeneous aqueous mixture is formed by: providing the aluminum oxide source, the alkali metal source and the structure directing agent as a mixture; combining the silica source; and combining the water soluble ODSO. Alternatively, the water soluble ODSO is combined with the silica source, and that mixture is combined with the aluminum oxide source, the alkali metal source and the structure directing agent.

[0035] In certain embodiments, the homogeneous aqueous mixture is formed by: combining the water soluble ODSO with the silica source to form a mixture; and that mixture is combined with the aluminum oxide source, the alkali metal source and the structure directing agent.

[0036] In certain embodiments, the homogeneous aqueous mixture is formed by: combining the water soluble ODSO with the aluminum oxide source, the alkali metal source and the structure directing agent to form a mixture; and that mixture is combined with the silica source.

[0037] The homogeneous aqueous mixture of the aluminum source, silica source, ODSO and structure directing agent, formed from any of the above chronological sequences of component addition, is heated under conditions and for a time effective to form a precipitate suspended in a supernatant. The precipitate is recovered, for example by filtration, washing and drying. The recovered precipitate is calcined at a suitable temperature, temperature ram rate and for a suitable period of time at to realize porous ZSM-5 zeolite.

[0038] An effective quantity of water for the aqueous environment compound can be provided by using a water-containing silica source such as colloidal silica, and/or by using an aqueous mixture of the aluminum oxide source, the alkali metal source and the structure directing agent. These components are added with water to the reaction vessel prior to heating. Typically, water allows for adequate mixing to realize a more homogeneous distribution of the sol-gel components, which ultimately produces a more desirable product because each crystal is more closely matched in properties to the next crystal. Insufficient mixing could result in undesirable “pockets” of highly concentrated sol-gel components and this may lead to impurities in the form of different structural phases or morphologies. Water also determines the yield per volume.

[0039] Certain ratios of materials are provided to attain the effective quantities of components. An effective SAR in the synthesized ZSM-5 includes but is not limited to ratios in the range of about 20-1500, 20-1000, 20-500, 25-1500, 25-1000, 25-500, 50-1500, 50-1000, 50-500, 100-1500, 100-1000 or 100-500. An effective amount of structure directing agent is used, for example at a molar ratio (normalized to 1 mole of Al.sub.2O.sub.3) in the range of about 0.1-75, 0.1-50, 0.1-30, 2.5-75, 2.5-50, 2.5-30, 5-75, 5-50 or 5-30. In addition, an effective amount of alkali metal is used so as to maintain a pH level of greater than or equal to about 9, for example in the range of about 9-14, 9-13, 10-14, 10-13, 11-14 or 11-13 in the intermediate suspension of the precipitate suspended in the supernatant. It is noted that in the process herein, the pH is reduced by the presence of ODSO, therefore, the quantity of the alkali metal source, such as sodium in the form of NaOH, can be adjusted accordingly to give the desired added to provide the desired pH. An effective mass ratio of ODSO/Na is less than or equal to about 9, for example in the range of about 0.01-9.

[0040] The aluminum source can comprise, without limitation, one or more of aluminates, alumina, other zeolites, aluminum colloids, boehmites, pseudo-boehmites, aluminum salts such as aluminum sulfate and alumina chloride, aluminum hydroxides and alkoxides, alumina gels. For example, suitable materials as aluminum sources are commercially available from Sasol, for instance high purity aluminas (CERALOX) and alumina hydrates (PURAL and CAPITAL), boehmites (DISPERSAL and DISPAL), and silica-alumina hydrates (SIRAL) and the corresponding oxides (SIRALOX).

[0041] The silica source can comprise, without limitation, one or more of silicates including sodium silicate (water glass), fumed silica, precipitated silica, colloidal silica, silica gels, other zeolites, dealuminated zeolites, and silicon hydroxides and alkoxides. Silica sources resulting in a high relative yield are preferred. For instance, suitable materials as silica sources are commercially from Cabot (for example, fumed silica) and Ludox (for example, colloidal silica).

[0042] Effective structure directing agents include one or more of quaternary ammonium cation compounds (including one or more of tetramethylammonium (TMA) cation compounds, tetraethylammonium (TEA) cation compounds, tetrapropylammonium (TPA) cation compounds, tetrabutylammonium (TBA) cation compounds, cetyltrimethylammonium (CTA) cation compounds. The cation can be paired with one or more of a hydroxide anion (for example, TPAOH or CTAOH), a bromide anion (for example, TPAB or CTAB), or an iodide anion. In certain embodiments the structure directing agents include bifunctional dicationic molecules containing a long aliphatic chain (for example C.sub.22H.sub.45—N.sup.+(CH.sub.3).sub.2—C.sub.6H.sub.12—N.sup.+(CH.sub.3).sub.2—C.sub.6H.sub.13, denoted C.sub.22-6-6, C.sub.22H.sub.45—N.sup.+(CH.sub.3).sub.2—C.sub.6H.sub.12—N.sup.+(CH.sub.3).sub.2—C.sub.3H.sub.7, denoted C.sub.22-6-3, or a poly(ethylene glycol)), dual-porogenic surfactants, silylated polyethylenimine polymers, amphiphilic organosilanes, or hydrophilic cationic polyelectroyltes/polymers such as poly(diallyldimethylammonium chloride) (PDADMAC).

[0043] The disclosed process for synthesizing ZSM-5 can occur in the absence or presence of seed materials comprising zeolite structures such as ZSM-5 (MFI), ZSM-8 (MFI), ZSM-11 (MEL) and Silicalite-1 (MFI).

[0044] The disclosed processes for synthesizing ZSM-5 can occur in the presence of a mineralizer as the alkali metal source selected from the group consisting of NaOH, KOH, RbOH, LiOH, CsOH and combinations thereof. In certain embodiments a Na-based mineralizer is selected. Note that the alkali metal source is provide as a hydroxide, but in embodiments herein where the ratio is expressed based on the mass of the alkali, it is the metal itself. For instance, when the alkali is NaOH, the ODSO/Na ratio is determined by dividing the mass of the ODSO by the mass of the Na portion of NaOH, that is, about 57.5% of the NaOH mass.

[0045] The use of ODSO has the effect to modify the morphology of the ZSM-5 crystals (for example, increasing the epitaxial growth along the (100) direction, varying the ratio of the (101) to (001) planes, and increasing the length-to-diameter ratios), as described herein.

[0046] The use of ODSO has the effect to produce ZSM-5 crystals are formed having a dimension up to about 5, 15, 20 or 30 μm.

[0047] The use of ODSO has the effect to produce ZSM-5 zeolites with improved crystallinity, in the range of about 1.2-1.8 (120-180% increase), for instance about 1.5 times (150%), as comparted to ZSM-5 synthesized in the absence of ODSO (water only).

[0048] The use of ODSO has the effect to increase the production yield of ZSM-5 zeolite up to about 170 wt %, for example in the range of about 150-170 wt %, as compared to ZSM-5 synthesized in the absence of ODSO (water only).

[0049] In the process herein, one or more ODSO compounds are used in the synthesis of ZSM-5. The one or more ODSO compounds can include compounds of the general formulae R—SOO—SO—R′, R—SOO—SOO—R′, R—SO—SOO—OH, R—SOO—SOO—OH, R—SO—SO—OH, R—SOO—SO—OH, and mixtures thereof, where R and R′ can be the same or different and are alkyl groups comprising 1-10 carbon atoms. In certain embodiments, the R and R′ are methyl and/or ethyl groups. The one or more ODSO compounds used in the synthesis of ZSM-5 generally include ODSO compounds having 3 or more oxygen atoms. In certain embodiments, one or more ODSO compounds used in the synthesis of ZSM-5 include ODSO compounds having 1 to 20 carbon atoms. In certain embodiments, one or more ODSO compounds used in the synthesis of ZSM-5 include ODSO compounds having an average density greater than about 1.0 g/cc. In certain embodiments, one or more ODSO compounds used in the synthesis of ZSM-5 include ODSO compounds having an average boiling point greater than about 80° C.

[0050] In certain embodiments ODSO compounds used in the synthesis of ZSM-5 comprise all or a portion of water-soluble ODSO compounds contained in an oxidation effluent stream that is obtained by oxidation of DSO compounds from a MEROX process, as disclosed in U.S. Pat. Nos. 10,807,947 and 10,781,168 and as incorporated herein by reference above. Table 2 identifies certain water-soluble ODSO compounds that are formed by oxidation of DSO obtained from MEROX by-products.

TABLE-US-00002 TABLE 2 ODSO Name Formula Structure Examples Dialkyl- sulfonesulfoxide Or 1,2-alkyl-alkyl- disulfane 1,1,2-trioxide (R—SOO—SO—R′) [00001] Dialkyl-disulfone Or 1,2 alkyl-alkyl- disulfane 1,1,2,2-tetraoxide (R—SOO—SOO—R′) [00002] Alkyl- sulfoxidesulfonate (R—SO—SOO—OH) [00003] Alkyl- sulfonesulfonate (R—SOO—SOO—OH) [00004] Alkyl- sulfoxidesulfinate (R—SO—SO—OH) [00005] Alkyl- sulfonesulfinate (R—SOO—SO—OH) [00006] R and R′ can be the same or different alkyl groups comprising 1-10 carbon atoms.

[0051] In certain embodiments, the ODSO compounds are contained in a mixture from oxidation of DSO compounds, comprising alkyl-sulfoxidesulfonate (R—SO—SOO—OH), alkyl-sulfonesulfonate (R—SOO—SOO—OH), alkyl-sulfoxidesulfinate (R—SO—SO—OH) and alkyl-sulfonesulfinate (R—SOO—SO—OH), for example, similar to those obtained as “Composition 2” in U.S. Pat. No. 10,781,168 as incorporated herein by reference above.

[0052] The below examples and data are exemplary. It is to be understood that other aluminum sources, silica sources, bases and structure directing agents can be used as compared to the example.

[0053] In the synthesis steps for producing ZSM-5 herein, the sequence of adding the components is described above, but can be varied. In certain embodiments, the aluminum source, the alkali metal source and the structure directing agent are formed into an aqueous solution, to which the ODSO is added, and then the silica, since addition of the silica source forms a thick gel. In other embodiments, the ODSO can be added to the silica source, and that mixture is added to an aqueous solution of the aluminum source, the alkali metal source and the structure directing agent.

[0054] The temperature and pressure conditions, and residence time, for the mixing steps described herein to produce the intermediate suspension of precipitate in the supernatant that is used for producing MFI framework (ZSM-5) zeolite are similar to those used in typical ZSM-5 synthesis, for example, where the sol-gel is prepared at ambient temperature and pressure (for instance about 20° C. and about 1 standard atmosphere). The mixing time is sufficient to realize a homogeneous distribution of the sol-gel components. In certain embodiments the sol-gel can be aged before being subjected to subsequent hydrothermal treatment, for example for a period of about 0-24, 0-5, 0.5-24 orf 0.5-5 hours. Hydrothermal treatment is then carried out at a temperature in the range of about 100-180° C. and at atmospheric or autogenous pressure, and for a time period within the range of about 3 hours to 5 days.

[0055] The products are washed, for example with water at a suitable quantity, for example at about twice the volume of the sol-gel solution. The wash can be at a temperature of from about 20-80° C. at atmospheric pressure or under vacuum. The wash can continue until the pH of the filtrate approaches 7. The solids are recovered by filtration, for instance, using known techniques such as centrifugation, gravity, vacuum filtration, filter press, or rotary drums, and dried, for example at a temperature of up to about 110 or 150° C.

[0056] The conditions for calcination to produce MFI framework (ZSM-5) zeolite herein can include temperatures in the range of about 450-700, 450-600, 500-700 or 500-600° C., atmospheric pressure, and a time period of about 3-24, 3-18, 6-24 or 6-18 hours. Calcining can occur with ramp rates in the range of from about 0.1-10, 0.1-5, 0.1-3, 1-10, 1-5 or 1-3° C. per minute. In certain embodiments calcination can have a first step ramping to a temperature of between about 100-150° C. with a holding time of from about 2-24 hours (at ramp rates of from about 0.1-5, 0.1-3, 1-5 or 1-3° C. per min) before increasing to a higher temperature with a final holding time in the range of about 2-24 hours.

EXAMPLES

Comparative Example 1

[0057] Aluminum nitrate nonahydrate (0.2633 g) was weighed into a Teflon liner (45 ml). Thereafter, 0.7750 g of a 50 wt. % sodium hydroxide solution and 7.0469 g tetrapropylammonium hydroxide (TPAOH) were added and the mixture stirred. Next, distilled water (3.3005 g) was added and the mixture was maintained under stirring. Finally, the silica source, 5.2430 g of Ludox AS-50, SiO.sub.2 content of 40 wt. %, was added and the mixture stirred until homogeneous.

[0058] The Teflon liner was positioned within an autoclave and transferred to an oven and heated to a temperature of 175° C. whilst rotating the autoclave. The autoclave was maintained at isothermal conditions for 18 hours.

[0059] The product was filtered and washed with distilled water before drying at 110° C. The dry mass was 1.3906 g. The inorganic content determined by thermogravimetric (TGA) analysis was 87.78%. Hence, a product (zeolite) yield of 1.2207 g was obtained.

[0060] The as-made sample from Comparative Example 1 was calcined at 550° C. (1° C./min ramp rate) for 8 hours to realize a porous ZSM-5 zeolite.

Example 1

[0061] Aluminum nitrate nonahydrate (0.2609 g) was weighed into a Teflon liner (45 ml). Thereafter, 0.7502 g of a 50 wt. % sodium hydroxide solution and 7.0361 g tetrapropylammonium hydroxide (TPAOH) were added and the mixture stirred. Next, distillated water (1.5546 g) and ODSO (1.7545 g) were added and the mixture was maintained under stirring. The ODSO used in this example are those obtained as “Composition 2” in U.S. Pat. No. 10,781,168, incorporated herein by reference above. Finally, the silica source, 5.2325 g of Ludox AS-50, SiO.sub.2 content of 40 wt. %, was added and the mixture stirred until homogeneous.

[0062] The Teflon liner was positioned within an autoclave and transferred to an oven and heated to a temperature of 175° C. whilst rotating the autoclave. The autoclave was maintained at isothermal conditions for 18 hours.

[0063] Thereafter, the product was filtered and washed with distilled water before drying at 110° C. The dry mass was 2.3206 g. The inorganic content determined by thermogravimetric (TGA) analysis was 87.74%. Hence, a zeolite yield of 2.0361 g was obtained.

Example 2

[0064] Aluminum nitrate nonahydrate (0.2601 g) was weighed into a Teflon liner (45 ml). Thereafter, 0.7455 g of a 50 wt. % sodium hydroxide solution and 7.0196 g tetrapropylammonium hydroxide (TPAOH) were added and the mixture stirred. Next, distilled water (1.4826 g) and ODSO (1.7905 g) were added and the mixture was maintained under stirring. Finally, the silica source, 5.5561 g of Ludox AS-50, SiO.sub.2 content of 40 wt. %, was added and the mixture stirred until homogeneous.

[0065] The Teflon liner was positioned within an autoclave and transferred to an oven and heated to a temperature of 175° C. whilst rotating the autoclave. The autoclave was maintained at isothermal conditions for 18 hours.

[0066] Thereafter, the product was filtered and washed with distilled water before drying at 110° C. The dry mass was 2.3387 g. The inorganic content determined by thermogravimetric (TGA) analysis was 88.32%. Hence, a zeolite yield of 2.0655 g was obtained.

[0067] The as-made samples from Examples 1 and 2 were calcined at 550° C. (1° C./min ramp rate) for 8 hours to realize porous ZSM-5 zeolite having MFI framework.

[0068] FIG. 1 shows the x-ray diffraction patterns of the calcined zeolites from Examples 1 and 2 and the comparative example. All diffractograms show that ZSM-5 (MFI) has been produced, however, the peak intensities are clearly observed to be different. For the ZSM-5 zeolite synthesized in water only, the peak intensity is lower than that of the ZSM-5 zeolite synthesized when the ODSO/Na mass ratios are 8.14 and 8.36. When normalizing the degree of crystallinity, this is based on the peak intensity of the (051) peak reflection for the calcined ZSM-5 zeolite synthesized in water only. For the ZSM-5 zeolites synthesized using ODSO/Na mass ratios of 8.14 and 8.36, the relative crystallinity is approx. 1.26 and 1.21 times higher, respectively (Table 3, FIG. 2).

[0069] Additionally, the zeolite yield is increased as a function of increasing the ODSO/Na mass ratio for crystalline materials. Zeolite yield is calculated based on the dry-mass of the as-made zeolite multiplied by the percentage of inorganic content determined from thermogravimetric analysis (FIG. 3, FIG. 4 and Table 4).

[0070] FIG. 5 shows the transition between crystalline products and amorphous products as a function of the ODSO/Na mass ratio; with the proportions of alumina and silica, the ODSO/Na mass ratio of less than about 9 produces crystalline material whereas higher ratios produce amorphous material ASA.

[0071] The morphology of the zeolite is also observed to change as a function of the ODSO/Na mass ratio (FIG. 6). For the ZSM-5 zeolite synthesized in water only the morphology is not so well defined. Increasing the ODSO/Na mass ratio to 8.14 shows a dramatic change to the morphology of a type of twinned octagonal crystals in the region of 5 μm. The crystals appear to be consistent with respect to their relative dimensions and also there appears to be a high ratio between the (001) and (101) planes to give the impression of a curved surface at opposing ends. The (100) plane appears to be the largest side of the crystal, however, the length-to-diameter ratio is close to 1 (see FIG. 7 for structural information).

[0072] However, further increasing the ODSO/Na mass ratio to 8.36 results in further changes to the crystal morphology. The first observation is that of larger crystals, in the region of 15 μm, hence, three times that of the ZSM-5 crystals produced for an ODSO/Na mass ratio of 8.14. The second observation is epitaxial growth along the (100) plane resulting in a length-to-diameter of approx. 2.5. The third observation is that the opposing ends are no longer curved but pointed as a result of the dominant (101) planes over that of the (001) plane.

[0073] The data obtained shows that a higher yield of ZSM-5 can be obtained when synthesized in the presence of an effective quantity of ODSO and that the said ZSM-5 is more crystalline with tuned and well-defined morphology.

TABLE-US-00003 TABLE 3 Relative crystallinity of the calcined ZSM-5 as a function of the ODSO/Na ratio. ODSO/Na Ratio (w/w) Relative Crystallinity 0 1.00 8.14 1.26 8.36 1.21 Relative crystallinity based on peak intensity of the (051) peak reflection at approx. 26.9° (2θ). An ODSO/Na ratio = 0 is a water-only synthesis in the absence of ODSO.

TABLE-US-00004 TABLE 4 Normalized zeolite yield as a function of the ODSO/Na ratio. ODSO/Na Ratio (w/w) Normalized Yield 0 1.00 8.14 1.67 8.36 1.69 Normalized zeolite yield is based on the dry mass of the as-made zeolite multiplied by the inorganic content determined from thermogravimetric analysis. An ODSO/Na ratio = 0 is a water-only synthesis in the absence of ODSO.

[0074] The methods and compositions of the present invention have been described above and in the attached drawings; however, modifications will be apparent to those of ordinary skill in the art and the scope of protection for the invention is to be defined by the claims that follow.