Copper hydroxide nitrate/calcium silicate/graphitic carbon nitride nanocomposite material based absorbent for wastewater treatment

Abstract

A method of absorption includes contacting a copper hydroxide nitrate/calcium silicate/graphite-phase carbon nitride [Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4] nanocomposite catalyst with a solution including one or more pollutants. Further, the method includes absorbing the one or more pollutants on the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite catalyst.

Claims

1. A method of absorbing one or more pollutants in wastewater, comprising: contacting a Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent with a solution comprising the one or more pollutants; thereby absorbing the one or more pollutants on the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

2. The method of claim 1, wherein the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent comprises: a graphite-phase carbon nitride (g-C.sub.3N.sub.4) in an amount of 20 to 40 percent by weight (wt. %), a copper hydroxide nitrate (Cu.sub.2(OH).sub.3NO.sub.3) in an amount of 20 to 40 wt. %, and a calcium silicate (CaSiO.sub.3) in an amount of 20 to 40 wt. %, based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

3. The method of claim 1, wherein the one or more pollutants is an organic pollutant.

4. The method of claim 1, wherein an absorption rate of the one or more pollutants onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent follows a pseudo-first order kinetic model.

5. The method of claim 1, wherein the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent has an absorption capacity of 100 to 115 mg of the one or more pollutants per gram of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

6. The method of claim 1, wherein the contacting occurs for 40 to 50 minutes.

7. The method of claim 1, wherein the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent is made by a process comprising: fabricating a calcium silicate CaSiO.sub.3; fabricating a graphite-phase carbon nitride g-C.sub.3N.sub.4; mixing the calcium silicate CaSiO.sub.3, the graphite-phase carbon nitride g-C.sub.3N.sub.4, and a copper salt in ethylene glycol monomethyl ether to form a mixture; microwaving the mixture to form the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

8. The method of claim 7, wherein the fabricating of the calcium silicate CaSiO.sub.3 is made by a process comprising: sonicating a mixture of a calcium salt and a silicate salt in an aqueous alcohol solution to form a calcium silicate mixture, followed by heating the calcium silicate mixture to a temperature of 160 to 200 C. for 1 to 3 hours to form the calcium silicate CaSiO.sub.3, wherein the calcium salt is selected from a group consisting of calcium nitrate, calcium chloride, calcium phosphate, calcium carbonate and calcium citrate, and wherein the silicate salt is selected from a group consisting of calcium silicate, sodium silicate, potassium silicate, zeolites and micas.

9. The method of claim 7, wherein the fabricating of the graphite-phase carbon nitride g-C.sub.3N.sub.4 comprises heating urea to a temperature of 550 to 650 C. for 30 to 60 minutes.

10. The method of claim 7, wherein the mixing comprises a copper salt selected from a group consisting of copper nitrate, copper chloride, copper sulfate, copper bromide and copper cyanide.

11. The method of claim 7, wherein the microwaving is performed at a temperature of 160 to 200 C. at a pressure of 4 to 6 bar for 30 to 90 minutes.

12. A Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite, comprising: a plurality of metal oxides nanorods; a plurality of g-C.sub.3N.sub.4 nanosheets, wherein the metal oxide nanorods comprises Cu.sub.2(OH).sub.3NO.sub.3 and CaSiO.sub.3.

13. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, wherein the metal oxides nanorods have an average length of 1 to 3 m.

14. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, wherein the metal oxides nanorods comprise nanowires having a length of 10 to 50 nm protruding perpendicularly to the nanorods.

15. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, wherein the metal oxides nanorods are dispersed on the g-C.sub.3N.sub.4 nanosheets with some aggregates.

16. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, having a mesoporous structure with a plurality of wide pores in the g-C.sub.3N.sub.4 nanosheets where the metal oxides nanorods deposit.

17. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, having an average pore diameter of 3 to 7 nm.

18. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, having a Brunauer-Emmett-Teller (BET) surface area of 140 to 160 m.sup.2.Math.g.sup.1.

19. The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite of claim 12, having an average pore volume of 0.3 to 0.4 cm.sup.3.Math.g.sup.1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) A more complete appreciation of this disclosure and many of the attendant advantages thereof may be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:

(2) FIG. 1A is a schematic diagram of a flowchart depicting a process to fabricate a copper hydroxide nitrate/calcium silicate/graphite-phase carbon nitride (Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4) nanocomposite-based absorbent, according to certain embodiments.

(3) FIG. 1B is a schematic diagram of a flowchart depicting a method of absorbing one or more pollutants in wastewater, according to certain embodiments.

(4) FIG. 2 depicts an X-ray diffraction (XRD) diffractogram of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(5) FIG. 3A depicts a transmission electron microscopy (TEM) image of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent at 200 nanometer (nm) magnification, according to certain embodiments.

(6) FIG. 3B depicts a TEM image of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent at 100 nm magnification, according to certain embodiments.

(7) FIG. 3C depicts a selected area electron diffraction (SAED) patterns of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(8) FIG. 4A is a graph depicting nitrogen (N.sub.2) adsorption-desorption isotherms of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(9) FIG. 4B is a graph depicting pore size distribution of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(10) FIG. 5 depicts a contact time investigation of basic fuchsin dye (BF) adsorption onto Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(11) FIG. 6 depicts a pseudo-first order (PF) investigation of BF adsorption onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(12) FIG. 7 depicts a pseudo-second order (PS) investigation of BF adsorption onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(13) FIG. 8 depicts a liquid film (LFD) investigation of BF adsorption onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

(14) FIG. 9 depicts intraparticle (IPD) investigation of BF adsorption onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, according to certain embodiments.

DETAILED DESCRIPTION

(15) Embodiments of the present invention will now be described fully hereinafter with reference to the accompanying drawings wherever applicable, in that some, but not all, embodiments of the disclosure are shown.

(16) In the drawings, like reference numerals designate identical or corresponding parts throughout the several views. Further, as used herein, the words a, an and the like generally carry a meaning of one or more, unless stated otherwise.

(17) When describing the present disclosure, the terms used are to be construed in accordance with the following definitions, unless a context dictates otherwise.

(18) Furthermore, the terms approximately, approximate, about, and similar terms generally refer to ranges that include the identified value within a margin of 20%, 10%, or preferably 5%, and any values therebetween.

(19) When amounts, concentrations, dimensions and other parameters are expressed in the form of a range, a preferable range, an upper limit value, a lower limit value or preferable upper and limit values, it should be understood that any ranges obtainable by combining any upper limit or preferable value with any lower limit or preferable value are also specifically disclosed, irrespective of whether the obtained ranges are clearly mentioned in the context.

(20) As used herein, the term amount refers to the level or concentration of one or more reactants, catalysts, or materials present in a reaction mixture.

(21) As used herein, the term particle refers to a small object that acts as a whole unit with regard to its transport and properties.

(22) As used herein, the term nanocomposite refers to a composite material in which at least one dimension of the component is in the nanometer size scale (<100 nm). The nanocomposite is a polyphase solid material made up of two or more nanomaterials. The term includes all types of multiphase solid materials in which one of the phases has one, two, or three dimensions of less than 100 nm, or structures having nanoscale repeat distances between the different phases that make up the material. The definition within the scope of the invention includes porous media, colloids, gels, copolymers, and solid combination of a bulk matrix and nano dimensional phase(s) differing in properties due to dissimilarities in structure and chemistry. Morphologies of the nanocomposite generally include phase separated systems, intercalated systems, and exfoliated systems. The nanocomposite includes ceramic matrix nanocomposites (CMNC), polymer matrix nanocomposites (PMNC), metal matrix nanocomposites (MMNC) or any combination thereof.

(23) As used herein, the term room temperature refers to a temperature range of 23 degrees Celsius ( C.)2 C. in the present disclosure. As used herein, ambient conditions means the temperature and pressure of the surroundings in which the substance, composition or article is located.

(24) As used herein the term disposed refers to being positioned, placed, deposited, arranged or distributed in a particular manner.

(25) As used herein, the term X-ray diffraction or XRD or X-ray crystallography refers to basic technique for obtaining information on the atomic structure of crystalline materials used as a standard laboratory technique. Unless otherwise specified, the XRD shall include an analytical technique based on the diffraction of X-rays by matter, especially crystalline materials.

(26) As used herein, the term Scanning Electron Microscopy or SEM refers to a surface-imaging technique that produces images of a sample by scanning the sample with a focused beam of electrons. Unless otherwise specified, the SEM shall include all imaging techniques using electron beams for imaging.

(27) In this application, a numerical value interval (i.e., a numerical value range) is involved, and, if not specifically stated, an optional numerical value distribution is considered continuous within the numerical value interval, and includes two numerical value endpoints (i.e., minimum and maximum values) of the numerical value range, and each numerical value between the two numerical value endpoints.

(28) The temperature parameters in the present disclosure, if not specifically limited, are both allowed to be constant temperature processing and also allowed to be varied within a certain temperature interval. It should be understood that the constant temperature processing allows the temperature to fluctuate within the precision range of the instrument control. It is allowed to fluctuate in the range of, for example, 5 C., 4 C., 3 C., 2 C., 1 C.

(29) A weight percent of a component, unless specifically stated to the contrary, is based on the total weight of the formulation or composition in which the component is included. For example, if a particular element or component in a composition or article is said to have 5 wt. %, it is understood that this percentage is in relation to a total compositional percentage of 100%.

(30) In addition, the present disclosure is intended to include all isotopes of atoms occurring in the present compounds and complexes. Isotopes include those atoms having the same atomic number but different mass numbers.

(31) Aspects of this disclosure pertain to a nanocomposite material of Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent fabricated for effective pollutant adsorption for wastewater remediation.

(32) A nanocomposite-based absorbent is described. The nanocomposite-based absorbent includes a graphite-phase carbon nitride (g-C.sub.3N.sub.4), a copper hydroxide nitrate (Cu.sub.2(OH).sub.3NO.sub.3), and a calcium silicate (CaSiO.sub.3). In some embodiments, the nanocomposite-based absorbent may include crystalline phases, but is not limited to quartz, calcite, hematite, magnetite, goethite, dolomite, albite, anorthite, pyrite, fluorite, halite, barite, apatite, rutile, and zircon. In a preferred embodiment, the nanocomposite-based absorbent includes a metallic nanosheet of Cu.sub.2(OH).sub.2NO.sub.3 as a major phase together with minor phases of Cu.sub.2O, CaSiO.sub.3, and g-C.sub.3N.sub.4. In a preferred embodiment, the nanocomposite-based absorbent includes the CaSiO.sub.3 monoclinic phase.

(33) In some embodiment, based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, a graphite-phase carbon nitride (g-C.sub.3N.sub.4) in an amount ranging from 20 to 40 percent by weight (wt. %), preferably 22 to 40 wt. %, preferably 25 to 40 wt. %, preferably 27 to 40 wt. %, preferably 30 to 40 wt. %, preferably 32 to 40 wt. %, preferably 35 to 40 wt. %, preferably 37 to 40 wt. %. In a preferred embodiment, the graphite-phase carbon nitride g-C.sub.3N.sub.4 is in an amount of 33.33 wt. % based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent. In some embodiment, based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, a copper hydroxide nitrate (Cu.sub.2(OH).sub.3NO.sub.3) in an amount ranging from 20 to 40 percent by weight (wt. %), preferably 22 to 40 wt. %, preferably 25 to 40 wt. %, preferably 27 to 40 wt. %, preferably 30 to 40 wt. %, preferably 32 to 40 wt. %, preferably 35 to 40 wt. %, preferably 37 to 40 wt. %. In a preferred embodiment, the copper hydroxide nitrate Cu.sub.2(OH).sub.3NO.sub.3 is in an amount of 33.33 wt. % based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent. In some embodiment, based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent, a calcium silicate (CaSiO.sub.3) in an amount ranging from 20 to 40 percent by weight (wt. %), preferably 22 to 40 wt. %, preferably 25 to 40 wt. %, preferably 27 to 40 wt. %, preferably 30 to 40 wt. %, preferably 32 to 40 wt. %, preferably 35 to 40 wt. %, preferably 37 to 40 wt. %. In a preferred embodiment, the calcium silicate CaSiO.sub.3 is in an amount of 33.33 wt. % based on a total weight of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

(34) In some embodiments, the nanocomposite comprises sheet morphologies, preferably nanosheets, although other morphologies such as nanowires, nanospheres, nanocrystals, nanorectangles, nanotriangles, nanopentagons, nanohexagons, nanoprisms, nanodisks, nanocubes, nanoribbons, nanoblocks, nanotoroids, nanodiscs, nanobarrels, nanogranules, nanowhiskers, nanoflakes, nanofoils, nanopowders, nanoboxes, nanobeads, nanobelts, nano-urchins, nanoflowers, nanostars, tetrapods, and their mixtures thereof. In a preferred embodiment, a Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite includes a plurality of metal oxides nanorods and a plurality of g-C.sub.3N.sub.4 nanosheets, where the metal oxide nanorods incudes a Cu.sub.2(OH).sub.3NO.sub.3 and CaSiO.sub.3. In a preferred embodiment, the metal oxides nanorods are dispersed on the g-C.sub.3N.sub.4 nanosheets with some aggregates.

(35) In some embodiments, the metal oxides nanorods of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite have an average length ranging from 1 to 3 m, preferably 1.2 to 3 m, preferably 1.5 to 3 m, preferably 2 to 3 m, preferably 2.5 to 3 m. In a preferred embodiment, the metal oxides nanorods of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite have an average length of 1.97 m. In some embodiments, the metal oxides nanorods of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite include nanowires having a length of 10 to 50 nm, preferably 15 to 50 nm, preferably 20 to 50 nm, preferably 25 to 50 nm, preferably 30 to 50 nm, preferably 35 to 50 nm, preferably 40 to 50 nm, preferably 45 to 50 nm protruding perpendicularly to the nanorods.

(36) In some embodiments, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite is porous. A porous material is the one that forms a porous bulk solid. Pores may be micropores, mesopores, macropores, and/or a combination thereof. The pores exist in the bulk material, not necessarily in the molecular structure of the material. The term microporous means that nanocomposite have pores with an average pore width (i.e. diameter) of less than 2 nm. The term mesoporous means the pores of the nanocomposite have an average pore width of 2-50 nm. The term macroporous means the pores of nanocomposite have an average pore width larger than 50 nm. Pore size may be determined by methods including, but not limited to, gas adsorption (e.g. N.sub.2 adsorption), mercury intrusion porosimetry, and imaging techniques such as scanning electron microscopy (SEM), and X-ray computed tomography (XRCT). In a preferred embodiment, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite have a mesoporous structure with a plurality of wide pores in the g-C.sub.3N.sub.4 nanosheets where the metal oxides nanorods deposit.

(37) In some embodiments, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite may have a Brunauer-Emmett-Teller (BET) surface area ranging from 140 to 160 m.sup.2.Math.g.sup.1, preferably 142 to 160 m.sup.2.Math.g.sup.1, preferably 145 to 160 m.sup.2.Math.g.sup.1, preferably 147 to 160 m.sup.2.Math.g.sup.1, preferably 150 to 160 m.sup.2.Math.g.sup.1, preferably 152 to 160 m.sup.2.Math.g.sup.1, preferably 155 to 160 m.sup.2.Math.g.sup.1, preferably 157 to 160 m.sup.2.Math.g.sup.1.

(38) In a preferred embodiment, the Brunauer-Emmett-Teller (BET) surface area of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite is 149.9 m.sup.2.Math.g.sup.1. In some embodiments, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite may have an average pore diameter ranging from 3 to 7 nm, preferably 3.5 to 7 nm, preferably 4 to 7 nm, preferably 4.5 to 7 nm, preferably 5 to 7 nm, preferably 5.5 to 7 nm, preferably 6 to 7 nm, preferably 6.5 to 7 nm. In a preferred embodiment, an average pore diameter of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite is 5 nm. In some embodiments, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite may have an average pore volume of 0.3 to 0.4 cm.sup.3.Math.g.sup.1, preferably 0.32 to 0.4 cm.sup.3.Math.g.sup.1, preferably 0.34 to 0.4 cm.sup.3.Math.g.sup.1, preferably 0.36 to 0.4 cm.sup.3.Math.g.sup.1, preferably 0.38 to 0.4 cm.sup.3.Math.g.sup.1. In a preferred embodiment, an average pore volume of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite is 0.354 cm.sup.3.Math.g.sup.1. FIG. 1A illustrates a schematic flow chart of a method 50 to fabricate the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent. The order in which the method 50 is described is not intended to be construed as a limitation, and any number of the method steps described can be combined to implement the method 50. Additionally, individual steps may be removed or skipped from the method 50 without departing from the spirit and scope of the present disclosure.

(39) At step 52, the method 50 includes fabricating a calcium silicate CaSiO.sub.3. The method of fabricating the calcium silicate CaSiO.sub.3 includes sonicating a mixture of a calcium salt and a silicate salt in an aqueous alcohol solution to form a calcium silicate mixture. The method further includes heating the calcium silicate mixture to a temperature of 160 to 200 C. for 1 to 3 hours to form the calcium silicate CaSiO.sub.3.

(40) In some embodiments, the calcium salt may include calcium chloride, calcium carbonate, calcium sulfate, calcium acetate, calcium lactate, calcium phosphate, calcium gluconate, calcium citrate, calcium formate, calcium propionate, calcium stearate, calcium oxide, calcium hydroxide, calcium bicarbonate, calcium bromide, calcium iodide, calcium hypochlorite, calcium chromate, calcium tungstate, and calcium molybdate. In some embodiments, the calcium salt is selected from a group consisting of calcium nitrate, calcium chloride, calcium phosphate, calcium carbonate and calcium citrate. In a preferred embodiment, calcium salt is calcium nitrate.

(41) In some embodiments, the silicate salt may include potassium silicate, lithium silicate, magnesium silicate, calcium silicate, aluminum silicate, barium silicate, zinc silicate, ammonium silicate, iron silicate, sodium orthosilicate, sodium disilicate, sodium hexafluorosilicate, sodium silicoaluminate, zirconium silicate, manganese silicate, strontium silicate, copper silicate, cobalt silicate, nickel silicate, and lead silicate. In some embodiments, the silicate salt is selected from a group consisting of calcium silicate, sodium silicate, potassium silicate, zeolites and micas. In a preferred embodiment, silicate salt is metasilicate.

(42) In some embodiments, the alcohol solution may include methanol, isopropanol, butanol, tert-butanol, propanol, isobutanol, pentanol, hexanol, heptanol, octanol, benzyl alcohol, cyclohexanol, allyl alcohol, phenol, ethylene glycol, diethylene glycol, triethylene glycol, glycerol, sorbitol, and xylitol. In a preferred embodiment, alcohol solution is ethanol and water of a equimolar ratio.

(43) In some embodiments, the calcium silicate mixture is heated to a temperature ranging from 160 to 200 C., preferably 165 to 200 C., preferably 170 to 200 C., preferably 175 to 200 C., preferably 180 to 200 C., preferably 185 to 200 C., preferably 190 to 200 C., preferably 195 to 200 C. In a preferred embodiment, the calcium silicate mixture is heated at a temperature of 180 C. In some embodiments, the calcium silicate mixture is heated for 1 to 3 hours, preferably 1.5 to 3 hours, preferably 2 to 3 hours, preferably 2.5 to 3 hours, preferably 1 to 2 hours. In a preferred embodiment, the calcium silicate mixture is heated for 2 hours.

(44) At step 54, the method 50 includes fabricating a graphite-phase carbon nitride g-C.sub.3N.sub.4. The fabricating of the graphite-phase carbon nitride g-C.sub.3N.sub.4 includes heating urea to a temperature of 550 to 650 C. for 30 to 60 minutes.

(45) In some embodiments, the graphite-phase carbon nitride g-C.sub.3N.sub.4 is achieved by microwave-assisted synthesis, solvothermal method, hydrothermal synthesis, chemical vapor deposition, ultrasonic exfoliation, electrochemical synthesis, plasma-enhanced chemical vapor deposition, microwave irradiation, mechanochemical synthesis, ionothermal synthesis, template-assisted synthesis, photochemical synthesis, arc-discharge method, electrospinning, wet chemical method, laser ablation, microwave-polymerization, sol-gel technique, supercritical fluid synthesis, and solution combustion synthesis. In a preferred embodiment, graphite-phase carbon nitride product is achieved by thermal condensation process. In some embodiments, the graphite-phase carbon nitride g-C.sub.3N.sub.4 is achieved by thermal condensation process by heating dicyandiamide, melamine, thiourea, cyanamide, guanidine hydrochloride, biguanide, ammonium thiocyanate, guanidine carbonate, creatinine, guanidine sulfate, ammonium cyanate, biuret, semicarbazide, hydrazine derivatives, thiobiuret, cyanoguanidine, formamidine acetate, ammonium carbamate, melam, and ammeline. In a preferred embodiment, the graphite-phase carbon nitride g-C.sub.3N.sub.4 is achieved by thermal condensation by heating urea.

(46) In some embodiments, urea is heated to a temperature ranging from 550 to 650 C., preferably 570 to 650 C., preferably 590 to 650 C., preferably 600 to 650 C., preferably 620 to 650 C., preferably 640 to 650 C. In a preferred embodiment, urea is heated at a temperature of 600 C. In some embodiments, urea may be heated for 30-60 min, preferably 31-59 min, preferably 32-58 min, preferably 33-57 min, preferably 34-56 min, preferably 35-55 min, preferably 36-54 min, preferably 37-53 min, preferably 38-52 min, preferably 39-51 min, preferably 40-50 min, preferably 41-49 min, preferably 42-48 min, preferably 43-47 min, preferably 44-46 min. In a preferred embodiment, urea is heated at 600 C. for 45 min.

(47) At step 56, the method 50 includes mixing the calcium silicate CaSiO.sub.3, the graphite-phase carbon nitride g-C.sub.3N.sub.4, and a copper salt in ethylene glycol monomethyl ether to form a mixture.

(48) In some embodiments, the copper salt may include, but is not limited to, copper (II) sulfate, copper (I) chloride, copper (II) chloride, copper (II) acetate, copper (I) oxide, copper (II) oxide, copper (I) bromide, copper (II) bromide, copper (I) iodide, copper (II) iodide, copper (II) carbonate, copper (II) phosphate, copper (II) fluoride, copper (II) citrate, copper (II) tartrate, copper (II) formate, copper (II) stearate, copper (II) laurate, copper (II) thiocyanate, and copper (II) arsenate. In some embodiments, the mixing includes a copper salt selected from a group consisting of copper nitrate, copper chloride, copper sulfate, copper bromide and copper cyanide. In a preferred embodiment, the copper salt is Cu(NO.sub.3) 2.3H.sub.2O

(49) In some embodiments, the ether may include diethyl ether, dimethyl ether, methyl tert-butyl ether, ethyl tert-butyl ether, diisopropyl ether, dipropyl ether, dibutyl ether, tetrahydrofuran, dioxane, anisole, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, butyl vinyl ether, phenetole, methyl phenyl ether, benzyl methyl ether, allyl phenyl ether, and tert-amyl methyl ether. In a preferred embodiment, the ether is ethylene glycol monomethyl ether.

(50) At step 58, the method 50 includes microwaving the mixture to form the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent. In some embodiments, the microwaving is performed at a temperature ranging from 160 to 200 C., preferably 165 to 200 C., preferably 170 to 200 C., preferably 175 to 200 C., preferably 180 to 200 C., preferably 185 to 200 C., preferably 190 to 200 C., preferably 195 to 200 C. In a preferred embodiment, the microwave temperature is 180 C. In some embodiments, the microwaving is performed at a pressure ranging from 4 to 6 bar, preferably 4.2 to 6 bar, preferably 4.5 to 6 bar, preferably 5 to 6 bar, preferably 5.2 to 6 bar, preferably 5.5 to 6 bar. In a preferred embodiment, a microwave pressure is 5 bar. In some embodiments, a microwave duration ranges from 30 to 90 minutes, preferably 30 to 90 minutes, preferably 30 to 90 minutes, preferably 30 to 90 minutes, preferably 30 to 90 minutes, preferably 30 to 90 minutes. In a preferred embodiment, a microwave duration is 60 minutes.

(51) FIG. 1B illustrates a schematic flow chart of a method 90 of absorbing one or more pollutants in wastewater. The order in which the method 90 is described is not intended to be construed as a limitation, and any number of the described method steps can be combined to implement the method 90. Additionally, individual steps may be removed or skipped from the method 90 without departing from the spirit and scope of the present disclosure.

(52) At step 92, the method 90 includes contacting a Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent with a solution including one or more pollutants. In some embodiments, the contacting occurs for 40 to 50 minutes, preferably 42 to 50 minutes, preferably 44 to 50 minutes, preferably 46 to 50 minutes, preferably 48 to 50 minutes.

(53) The Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent can be used as an effective absorbent for water remediation. In some embodiments, the nanocomposite-based absorbent can be used to remove organic contaminants including pesticides, pharmaceuticals, dyes, and other synthetic or natural organic substances that can pose environmental or health risks. In some embodiments, the one or more pollutants is an organic pollutant.

(54) In some embodiments, the organic contaminant may be a dye, a phenol, a polycyclic aromatic hydrocarbon, an herbicide, a pesticide, a persistent organic contaminant, or the like.

(55) In alternate embodiments, the organic contaminant is a dye. A dye is a colored substance that chemically binds to a material it may be intended to color. Generally, a dye is applied in solution, typically aqueous solution. Examples of dyes include, but are not limited to: acridine dyes, which are acridine and its derivatives such as acridine orange, acridine yellow, acriflavine, and gelgreen; anthraquinone dyes, which are anthroaquinone and its derivatives such as acid blue 25, alizarin, anthrapurpurin, carminic acid, 1,4-diamno-2,3-dihydroanthraquinone, 7,14-dibenzypyrenequinone, dibromoanthrone, 1,3-dihydroxyanthraquinone, 1,4-dihydroxyanthraquinone, disperse red 9, disperse red 11, indanthrone blue, morindone, oil blue 35, parietin, quinizarine green SS, remazol brilliant blue R, solvent violet 13, 1,2,4-trihydroxyanthraquinone, vat orange 1, and vat yellow 1; diaryl methane dyes such as auramine O, triarylmethane dyes such as acid fuchsin, aluminon, aniline blue WS, aurin, aurintricarboxylic acid, brilliant blue FCF, brilliant green, bromocresol green, bromocresol purple, bromocresol blue, bromophenol blue, bromopyrogallol red, chlorophenol red, coomassie brilliant blue, cresol red, O-cresolphthalein, crystal violet, dichlorofluorescein, ethyl green, fast green FCT, FIAsH-EDT2, fluoran, fuchsine, green S, light green SF, malachite green, merbromin, metacresol purple, methyl blue, methyl violet, naphtholphthalein, new fuchsine, pararosaniline, patent blue V, phenol red, phenolphthalein, phthalein dye, pittacal, spirit blue, thymol blue, thymolphthalein, Victoria blue BO, Victoria blue R, water blue, xylene cyanol, and xylenol orange; azo dyes such as acid orange 5, acid red 13, alican yellow, alizarine yellow R, allura red AC, amaranth, amido black 10B, aniline yellow, arylide yellow, azo violet, azorubine, basic red 18, biebrich scarlet, Bismarck brown Y, black 7984, brilliant black BN, brown FK, chrysoine resorcinol, citrus red 2, congo red, D&C red 33, direct blue 1, disperse orange 1, eriochrome black T, evans blue, fast yellow AB, orange 1, hydroxynaphthol blue, janus green B, lithol rubine BK, metanil yellow, methyl orange, methyl red, methyl yellow, mordant brown 33, mordant red 19, naphthol AS, oil red O, oil yellow DE, orange B, orange G, orange GGN, para red, pigment yellow 10, ponceau 2R, prontosil, red 2G, scarlet GN, Sirius red, solvent red 26, solvent yellow 124, sudan black B, sudan I, sudan red 7B, sudan stain, tartrazine, tropaeolin, trypan blue, and yellow 2G; phthalocyanine dyes such as phthalocyanine blue BN, phthalocyanine Green G, Alcian blue, and naphthalocyanine, azin dyes such as basic black 2, mauveine, neutral red, Perkin's mauve, phenazine, and safranin; indophenol dyes such as indophenol and dichlorophenolindophenol; oxazin dyes; oxazone dyes; thiazine dyes such as azure A, methylene blue, methylene green, new methylene blue, and toluidine blue; thiazole dyes such as primuline, stains-all, and thioflavin; xanthene dyes such as 6-carboxyfluorescein, eosin B, eosin Y, erythosine, fluorescein, rhodamine B, rose bengal, and Texas red; fluorone dyes such as calcein, carboxyfluorescein diacetate succinimidyl ester, fluo-3, fluo-4, indian yellow, merbromin, pacific blue, phloxine, and seminaphtharhodafluor; or rhodamine dyes such as rhodamine, rhodamine 6G, rhodamine 123, rhodamine B, sulforhodamine 101, and sulforhodamine B.

(56) A phenol is an organic compound including a hydroxyl group (OH) bonded directly to an aromatic hydrocarbon group. Examples of phenols may include phenol (the namesake of the group of compounds), bisphenols (including bisphenol A), butylated hydroxytoluene (BHT), 4-nonylphenol, orthophenyl phenol, picric acid, phenolphthalein and its derivatives mentioned above, xylenol, diethylstilbestrol, L-DOPA, propofol, butylated hydroxyanisole, 4-tert-butylcatechol, tert-butylhydroquinone, carvacrol, chloroxyleol, cresol (including M, O, and P-cresol), 2,6-di-tert-butylphenol, 2,4-dimethyl-6-tert-butylphenol, 2-ethyl-4,5-dimethylphenol, 4-ethylguaiacol, 3-ethylphenol, 4-ethylphenol, flexirubin, mesitol, 1-nonyl-4-phenol, thymol, 2,4,6-tri-tert-butylphenol, chlorophenol (including 2-, 3-, and 4-chlorophenol), dichlorophenol (including 2,4- and 2,6-dichlorophenol), bromophenol, dibromophenol (including 2,4-dibromophenol), nitrophenol, norstictic acid, oxybenzone, and paracetamol (also known as acetoaminophen).

(57) A polycyclic aromatic hydrocarbon (PAH) is an aromatic hydrocarbon composed of multiple aromatic rings. Examples of polycyclic aromatic hydrocarbons include naphthalene, anthracene, phenanthrene, phenalene, tetracene, chrysene, triphenylene, pyrene, pentacene, benzo[a]pyrene, corannulene, benzo[g,h,i]perylene, coronene, ovalene, benzo[c]fluorine, acenaphthene, acenaphthylene, benz [a]anthracene, benzo[b]fluoranthene, benzo[j]fluoranthene, benzo[k]fluoranthene, benzo[e]pyrene, cyclopenta [c,d]pyrene, dibenz [a,h]anthracene, dibenzo[a,e]pyrene, dibenzo[a,h]pyrene, dibenzo[a,i]pyrene, dibenzo[a,l]pyrene, fluoranthene, fluorine, indeno[1,2,3-c,d]pyrene, 5-methylchrysene, naphthacene, pentaphene, picene, and biphenylene.

(58) An herbicide (also known as weedkiller) is a substance that is toxic to plants and may kill, inhibit the growth of, or prevent the germination of plants. Herbicides are typically used to control the growth of or remove unwanted plants from an area of land, particularly in an agricultural context. Examples of herbicides include, but are not limited to, 2,4-D, aminopyralid, chlorsulfuron, clopyralid, dicamba, diuron, glyphosate, hexazinone, imazapic, imazapyr, methsulfuron methyl, picloram, sulfometuron methyl, triclopyr, fenoxaprop, fluazifop, quizalofop, clethodim, sethoxydim, chlorimuron, foramsulfuron, halosulfuron, nicosulfuron, primisulfuron, prosulfuron, rimsulfuron, thofensulfuron, tribenuron, imazamox, imazaquin, flumetsulam, cloransulam, thiencarbazone, fluoxpyr, diflufenzopyr, atrazine, simazine, metribuzin, bromoxynil, bentazon, linuron, glufosinate, clomazone, isoxaflutole, topramezone, mesotrione, tembotrione, acifluorfen, formesafen, lactofen, flumiclorac, flumioxazin, fulfentrazone, carfentrazone, fluthiacet-ethyl, falufenacil, paraquat, ethalfluralin, pendimethalin, trifluralin, butylate, EPTC, ecetochlor, alachlor, metolachlor, dimethenamid, flufenacet, and pyroxasulfone.

(59) A pesticide is a substance meant to prevent, destroy, or control pests including, but not limited to algae, bacteria, fungi, plants, insects, mites, snails, rodents, and viruses.

(60) A pesticide intended for use against algae is known as an algicide. Examples of algicides include benzalkonium chloride, bethoxazin, cybutryne, dichlone, dichlorophen, diuron, endothal, fentin, isoproturon, methabenthiazuron, nabam, oxyfluorfen, pentachlorophenyl laurate, quinoclamine, quinonamid, simazine, terbutryn, and tiodonium.

(61) A pesticide intended for use against bacteria is known as a bactericide. Examples of bactericides include antibiotics such as: aminoglycosides such as amikacin, gentamicin, kanamycin, neomycin, netilmicin, tobramycin, paromomycin, streptomycin, and spectinomycin; ansamycins such as geldanamycin, herbimycin, and rifaximin; carbacephems such as loracarbef; carbapenems such as ertapenem, doripenem, imipenem, and meropenem; cephalosporins such as cefadroxil, cefazolin, cephradine, cephapirin, cephalothin, cephalexin, cefaclor, cefoxitin, cefotetan, cefamandole, cefmetazole, cefonicid, cefprozil, cefuroxime, cefixime, cefdinir, cefditoren, cefoperazone, cefotaxime, cefpodoxime, cefazidime, ceftibuten, ceftizoxime, moxalactam, ceftriaxone, cefepime, cefaroline fosamil, and ceftobiprole; glycopeptides such as teicoplanin, vancomycin, telavancin, dalbavancin, and oritavancin; lincosamides such as clindamycin and lincomycin; lipopeptides such as daptomycin; macrolides such as azithromycin, clarithromycin, erythromycin, roxithromycin, telithromycin, spiramycin, and fidoxamicin; monobactams such as aztreonam; nitrofurans such as furazolidone and nitrofurantoin; oxazolidinones such as linezolid, posizolid, radezolid, and torezolid; penicillins such as amoxicillin, ampicillin, azlocillin, dicloxacillin, flucloxacillin, mezlocillin, methicillin, nafcillin, oxacillin, penicillins (including penicillin G and V), piperacillin, temocillin, and ticarcillin; polypeptides such as bacitracin, colistin, and polymyxin B; quinolones such as ciproflaxacin, enoxacin, gatifloxacin, gemifloxacin, levofloxacin, lomefloxacin, moxifloxacin, nadifloxacin, nalidixic acid, norfloxacin, ofloxacin, trovafloxacin, gepafloxacin, sparfloxacin, and temafloxacin; sulfonamides such as mafenide, sulfacetamide, sulfadiazine, sulfadithoxine, sulfamethizole, sulfamethoxazole, sulfanilamide, sulfasalazine, sulfisoxazole, and sulfonamidochrysoidine; tetracyclines such as demeclocycline, doxycycline, metacycline, minocycline, oxytetracycline, and tetracycline.

(62) A pesticide intended for use against fungi is known as a fungicide. Examples of fungicides include acibenzolar, acypetacs, aldimorph, anilazine, aureofungin, azaconazole, azithiram, azoxystrobin, benalaxyl, benodanil, benomyl, benquinox, benthiavalicarb, binapacryl, biphenyl, bitertanol, bixafen, blasticidin-S, boscalid, bromuconazole, captafol, captan, carbendazim, carboxin, carpropamid, chloroneb, chlorothalonil, chlozolinate, cyazofamid, cymoxanil, cyprodinil, dichlofluanid, diclocymet, dicloran, diethofencarb, difenoconazole, diflumetorim, dimethachlone, dimethomorph, diniconazole, dinocap, dodemorph, edifenphos, enoxastrobin, epoxiconazole, etaconazole, ethaboxam, ethirimol, etridiazole, famoxadone, fenamidone, fenarimol, fenbuconazole, fenfuram, fenhexamid, fenoxanil, fenpropidin, fenpropimorph, ferbam, fluazinam, fludioxonil, flumorph, fluopicolide, fluopyram, fluoroimide, fluoxastrobin, flusilazole, flutianil, flutolain, flopet, fthalide, furalaxyl, guazatine, hexaconazole, hymexazole, imazalil, imibenconazole, iminoctadine, iodocarb, ipconazole, iprobenfos, iprodione, iprovalicarb, siofetamid, isoprothiolane, isotianil, kasugamycin, laminarin, mancozeb, mandestrobin, mandipropamid, maneb, mepanypyrim, mepronil, meptyldinocap, mealaxyl, metominostrobin, metconazole, methafulfocarb, metiram, metrafenone, myclobutanil, naftifine, nuarimol, octhilinone, ofurace, orysastrobin, oxadixyl, oxathiapiprolin, oxolinic acid, oxpoconazole, oxycarboxin, oxytetracycline, pefurazate, penconazole, pencycuron, penflufen, penthiopyrad, phenamacril, picarbutrazox, picoxystrobin, piperalin, polyoxin, probenzole, prochloraz, procymidone, propamocarb, propiconazole, propineb, proquinazid, prothiocarb, prothioconazole, pydiflumetofen, pyraclostrobin, pyrametostrobin, pyraoxystrobin, pyrazophos, pyribencarb, pyributicarb, pyrifenox, pyrimethanil, pyrimorph, pyriofenone, pyroquilon, quinoxyfen, quintozene, sedaxane, silthiofam, simeconazole, spiroxamine, streptomycin, tebuconazole, tebufloquin, teclofthalam, tecnazene, terbinafine, tetraconazole, thiabendazole, thifluzamide, thiphanate, thiram, tiadinil, tolclosfos-methyl, folfenpyrid, tolprocarb, tolylfluanid, triadimefon, triadimenol, triazoxide, triclopyricarb, tricyclazole, tridemorph, trifloxystrobin, triflumizole, triforine, validamycin, and vinclozolin.

(63) A pesticide intended for use against plants is known as an herbicide as described above.

(64) A pesticide intended for use against insects is known as an insecticide. Examples of insecticides are: organochlorides such as Aldrin, chlordane, chlordecone, DDT, dieldrin, endofulfan, endrin, heptachlor, hexachlorobenzene, lindane, methoxychlor, mirex, pentachlorophenol, and TDE; organophosphates such as acephate, azinphos-methyl, bensulide, chlorethoxyfos, chlorpyrifos, diazinon, chlorvos, dicrotophos, dimethoate, disulfoton, ethoprop, fenamiphos, fenitrothion, fenthion, malathion, methamdophos, methidathion, mevinphos, monocrotophos, naled, omethoate, oxydemeton-methyl, parathion, phorate, phosalone, phosmet, phostebupirim, phoxim, pirimiphos-methyl, profenofos, terbufos, and trichlorfon; carbamates such as aldicarb, bendiocarb, carbofuran, carbaryl, dioxacarb, fenobucarb, fenoxycarb, isoprocarb, methomyl; pyrethroids such as allethrin, bifenthrin, cyhalothrin, cypermethrin, cyfluthrin, deltamethrin, etofenprox, fenvalerate, permethrin, phenothrin, prallethrin, resmethrin, tetramethrin, tralomethrin, and transfluthrin; neonicotinoids such as acetamiprid, clothiandin, imidacloprid, nithiazine, thiacloprid, and thiamethoxam; ryanoids such as chlorantraniliprole, cyanthaniliprole, and flubendiamide.

(65) A pesticide intended for use against mites is known as a miticide. Examples of miticides are permethrin, ivermectin, carbamate insecticides as described above, organophosphate insecticides as described above, dicofol, abamectin, chlorfenapyr, cypermethrin, etoxazole, hexythiazox, imidacloprid, propargite, and spirotetramat.

(66) A pesticide intended for use against snails and other mollusks is known as a molluscicide. Examples of molluscicides are metaldehyde and methiocarb.

(67) A pesticide intended for use against rodents is known as a rodenticide. Examples of rodenticides are warfarin, coumatetralyl, difenacoum, brodifacoum, flocoumafen, bromadiolone, diphacinone, chlorophacinone, pindone, difethialone, cholecalciferol, ergocalciferol, ANTU, chloralose, crimidine, 1,3-difluoro-2-propanol, endrin, fluroacetamide, phosacetim, pyrinuron, scilliroside, strychnine, tetramethylenedisulfotetramine, bromethalin, 2,4-dinitrophenol, and uragan D2.

(68) A pesticide intended for use against viruses is known as a virucide. Examples of virucides are cyanovirin-N, griffithsin, interferon, NVC-422, scytovirin, urumin, virkon, zonroz, and V-bind viricie.

(69) A persistent organic contaminant is a toxic organic chemical that adversely affects human and environmental health, can be transported by wind and water, and can persist for years, decades, or centuries owing to resistance to environmental degradation by natural chemical, biological, or photolytic processes. Persistent organic contaminants are regulated by the United Nations Environment Programme 2001 Stockholm Convention on Persistent Organic Contaminants. Examples of persistent organic contaminants are Aldrin, chlordane, dieldrin, endrin, heptachlor, hexachlorobenzene, mirex, toxaphene, polychlorinated biphenyl (PCBs), dichlorodiphenyltrichloroethane (DDT), dioxins, polychlorinated dibenzofurans, chlordecone, hexachlorocyclohexane (- and -), hexabromodiphenyl ether, lindane, pentachlorobenzene, tetrabromodiphenyl ether, perfluorooctanesulfonic acid, endosulfans, and hexabromocyclododecane.

(70) At step 94, the method 90 includes absorbing the one or more pollutants on the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent.

(71) In some embodiments, an adsorption rate of pollutant onto the absorbent may include, but is not limited to, pseudo-second order kinetic model, intraparticle diffusion model, Elovich model, Bangham model, Avrami kinetic model, Boyd model, film diffusion model, fractional power model, external diffusion model, and Langmuir-Hinshelwood kinetic model. In a preferred embodiment, an absorption rate of the one or more pollutants onto the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent follows a pseudo-first order kinetic model.

(72) In some embodiments, the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent has an absorption capacity ranging from 100 to 115 mg of the one or more pollutants per gram, preferably 102 to 115 mg/g, preferably 104 to 115 mg/g, preferably 106 to 115 mg/g, preferably 108 to 115 mg/g, preferably 110 to 115 mg/g, preferably 112 to 115 mg/g, preferably 114 to 115 mg/g of the Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite-based absorbent. In a preferred embodiment, the absorption capacity is 106.9 mg/g.

(73) The following examples are provided solely for illustration and are not to be construed as limitations of the present disclosure, as many variations thereof are possible without departing from the spirit and scope of the present disclosure.

EXAMPLES

(74) The following examples demonstrate a method of absorption and a Cu.sub.2(OH).sub.3NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite. The examples are provided solely for illustration and are not to be construed as limitations of the present disclosure, as many variations thereof are possible without departing from the spirit and scope of the present disclosure.

Example 1: Fabricating Calcium Silicate (CaSiO.SUB.3.)

(75) According to the present disclosure, equal moles of calcium nitrate and sodium metasilicate were dispersed in 100 milliliter (mL) of ethanol:water (1:1) in a 150 ml glass beaker and sonicated for 15 minutes. The mixture was transferred to a 200 mL autoclave and then placed in an oven operated at 180 degrees Celsius ( C.) for 2.0 hour (h). The product was dispersed in 500 ml distilled water with an ultrasonic bath for 10 minutes, filtered via a buchner system, rinsed with distilled water, and dried at 120 C. for 1.0 h.

Example 2: Fabricating Graphite-Phase Carbon Nitride (g-C.SUB.3.N.SUB.4.)

(76) About 30.0 gram (g) of urea was placed in a 250 mL porcelain crucible, covered with its porcelain cover, then the hall crucible and cover were wrapped with three layers of aluminum foil to reduce the urea loss of evaporation. The crucible was heated via a furnace set at 600 C. for 45 minutes.

Example 3: Fabricating Copper Hydroxide Nitrate/Calcium Silicate/Graphite-Phase Carbon nitride (Cu.SUB.2.(OH).SUB.2.NO.SUB.3./CaSiO.SUB.3./g-C.SUB.3.N.SUB.4.)

(77) 2.0 g of CaSiO.sub.3, 2.0 g of g-C.sub.3N.sub.4 and the amount of Cu (NO.sub.3) 2.3H.sub.2O enough to produce 2.0 g of Cu.sub.2(OH).sub.2NO.sub.3 were transferred to a mono wave-200 vial (G30), dispersed in 20 ml ethylene glycol monomethyl ether via an ultrasonic bath for 30 minutes. The vial was closed with its teflon cover and placed in the Anton-Baar Monowave-200 operated at 180 C. and 5.0 bar pressure for one hour. The product was dispersed in 1 liter (L) distilled water with an ultrasonic bath for 30 minutes, filtered via a buchner system, rinsed with distilled water, and dried at 150 C. for 2.0 h.

(78) The crystallinity and phases identification present in Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite was analyzed by XRD and the results are given in FIG. 2. The intense peaks and high intensity values indicate that the powder is highly crystalline in nature. In addition, the peak broadening indicates the small particle size of the prepared composites. Examination of the diffraction patterns with the standard JCPDS cards reveals the presence of metallic nanosheet of Cu.sub.2(OH).sub.2NO.sub.3 as a major phase together with minor phases of cupric oxide (Cu.sub.2O), CaSiO.sub.3, and g-C.sub.3N.sub.4. The Cu.sub.2(OH).sub.2NO.sub.3 phase was indexed to the strong reflections at 2 values of 12.9, 25.7, 33.8, 36.7, and 43.4 (JCPDS No. 00-003-0061). The CaSiO.sub.3 monoclinic phase (JCPDS No. 00-001-0720) was detected at 2 values of 27.3, 32.3 and 62.6. The Cu.sub.2O was characterized by a strong reflection at 2 value of 36.4 (JCPDS No. 01-078-2076). The diffractions related to g-C.sub.3N.sub.4 were observed at 33.2, and 58.0 (COD No. 1534042 and JCPDS No. 00-050-0848). The weak diffractions of both CaSiO.sub.3 and g-C.sub.3N.sub.4 may be attributed to the semi-crystalline nature of these phases and the high crystalline phases of Cu.sub.2O and Cu.sub.2(OH).sub.2NO.sub.3 phases in the prepared composite. No other phases were detected indicating the successful fabrication of Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4.

(79) TEM images of Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3/g-C.sub.3N.sub.4 nanocomposite were presented in FIGS. 3A-3B. The TEM images showed that a two-dimensional porous structure constructed with curled and wrinkled nanosheets and platelets of the g-C.sub.3N.sub.4, as shown in FIG. 3A. The image also shows well dispersion of rods metal oxides nanoparticles with size 1.97 micrometer (m) and some aggregates on nanosheets of g-C.sub.3N.sub.4. The corresponding selected area electron diffraction (SAED) pattern reveals diffraction spots with interplanar spacing of 0.365 nanometer (nm), 0.242 nm, 0.141 nm, and 0.124 nm due to (CaSiO.sub.3: 2-12, Cu.sub.2(NO.sub.3)(OH).sub.3: -111), (CaSiO.sub.3: -2-12, Cu.sub.2(NO.sub.3)(OH).sub.3: -211), (CaSiO.sub.3: 322, Cu.sub.2(NO.sub.3)(OH).sub.3:00-5), and (CaSiO.sub.3: -125) diffraction plane, as shown in FIG. 3C.

(80) FIG. 4A displays the nitrogen adsorption-desorption isotherms of Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite. The nitrogen sorption isotherm of the composite belonging to type IV with noticed hysteresis loop, indicating the formation of mesoporous structures. However, shifting the loop to a relatively higher pressure (P/P.sub.o=0.62-1) suggests the presence of wide mesopores, which may result from the deposition of metal oxides particles in the wide pores of g-C.sub.3N.sub.4. Furthermore, the Brunauer-Emmett-Teller (BET) surface area of the Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 sample was calculated to be 149.9 square meter per gram (m.sup.2g-1). The marked high specific surface area reflects the good dispersion of these metal oxides nanoparticles on g-C.sub.3N.sub.4 and CaSiO.sub.3. Moreover, the pore size distribution curves, plotted using the barrett-joyner-halenda (BJH) method, for the Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 sample exhibited unimodal distribution with average pore diameters maximized at 5 nm and pore volume of 0.354 cubic centimeter per gram (cm.sup.3g.sup.1), as shown in FIG. 4B. All the isotherms fall under the H.sub.3 pore type category, which is characterized by the absence of a limiting adsorption plateau at high relative pressure (P/P.sub.o). This behavior is typically associated with the aggregation of plate-like particles, resulting in the formation of slit-shaped pores. This indicates that the assembly of Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 composite provoked a mesoporous structure.

(81) 0.05 g of sorbent was measured in a separate 150 ml beaker. 100 mL of the 100 milligram per liter (mgL.sup.1) basic fuchsin dye (BF) solution was poured into each beaker. A portion of the mixture was withdrawn till the BF sorption reached the equilibrium. The aliquots were filtered via a 0.22 m syringe filter, and the absorbance was measured utilizing a UV-Vis-spectrophotometer (=550 nm). The contact time study of BF and sorption onto the as-prepared nanocomposite was studied. The BF and absorbance measured during the study were employed for calculating the remaining concentrations (unabsorbed) at each time interval via Eq. 1. Using Eq. 2 was utilized to calculate the adsorption capacity at each period [the BF or milligrams adsorbed onto one gram of sorbent, q.sub.t, milligram per gram (mg.Math.g.sup.1)].

(82) $\begin{array}{cc}{C}_t=\frac{{\mathrm{Absorbance}}_{\mathrm{sample}}}{{\mathrm{Absorbance}}_{\mathrm{standard}}}\mathrm{conc}{.}_{\mathrm{standard}}& \left(1\right)\end{array}$$\begin{array}{cc}{q}_t=\frac{\left(C_0-C_t\right)V}{m}& \left(2\right)\end{array}$

(83) FIG. 5 demonstrates the adsorption trend of BF onto prepared nanocomposite. The Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@gC.sub.3N.sub.4 showed q.sub.t values of 106.9 milligram per gram (mg/g); the results reflected the capability of the Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 for treating water contaminated by organic pollutants. Notably, almost 90% of the gained q.sub.t value was acquired within the first 30 minutes, and the overall sorption processes reached equilibrium within 90 minutes, presenting the Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 as fast treatment sorbent.

(84) The adsorption rate order of BF removal by Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 was studied via pseudo-first order (PF, Eq. 3) and pseudo-second order (PS, Eq. 4) kinetic models.

(85) $\begin{array}{cc}\ln \left(q_e-q_t\right)=\ln q_e-k_1.Math.t& \left(3\right)\end{array}$$\begin{array}{cc}\frac{1}{q_t}=\frac{1}{k_2.Math.q_e^{2}t}+\frac{1}{q_e}& \left(4\right)\end{array}$

(86) The symbol q.sub.e (mg/g) represents the equilibrium adsorption capacity. The PF and PS constants are also time dependent, with the former represented as k.sub.1 (min.sup.1) and the latter as k.sub.2 [gram per milligram per minute (g mg.sup.1 min.sup.1)]. The PF plot of the BF adsorption onto Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite is depicted in FIG. 6. Additionally, FIG. 7 illustrates the PS plots of BF sorption onto Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4. The rate-order output of BF removal illustrated that the sorption on Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 showed better fitting to the PF model.

(87) The rate-control mechanism of BF removal by Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 was studied using the intraparticle (IPD, Eq. 5) and the liquid-film (LFD, Eq. 6) diffusion model.

(88) $\begin{array}{cc}{q}_t=K_{\mathrm{IP}}*t^{\frac{1}{2}}+C_i& \left(5\right)\end{array}$$\begin{array}{cc}\ln \left(1-F\right)=-K_{\mathrm{LF}}*t& \left(6\right)\end{array}$

(89) The IPD constant is denoted by K.sub.IPD [milligrams per gram per square root of minute (mg g.sup.1 min.sup.1/2)], and the LFD constant is designated by K.sub.LFD (min.sup.1). C.sub.i: the boundary layer factor, expressed as mg g.sup.1

(90) The LFD plot of the BF adsorption onto Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite was depicted in FIG. 8. Additionally, FIG. 9 illustrated the IPD plots of BF sorption onto Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4. The rate-control output of BF removal illustrated that the sorption of BF on the fabricated Cu.sub.2(OH).sub.2NO.sub.3/CaSiO.sub.3@g-C.sub.3N.sub.4 nanocomposite was mostly controlled by the LF model.

(91) Numerous modifications and variations of the present disclosure are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.