NATURAL PLANT FIBRE REINFORCED CONCRETE

Abstract

A plastinated plant material and method of preserving natural plant fibres. The plastinated plant material comprises reducing a plant material to a plant sample having a size smaller than the entire plant and plastinating said plant fibers by saturating said plant fibers in acetone to dehydrate said plant fibres, immersing said dehydrated plant fibres in a liquid polymer and subjecting said immersed plant fibres to a vacuum to replace acetone in said plant fibers with said liquid polymer.

Claims

1. A method of preserving natural plant fibres comprising: reducing a plant material to a plant sample having a size smaller than the entire plant; and plastinating said plant fibers by: saturating said plant fibers in acetone to dehydrate said plant fibres; immersing said dehydrated plant fibres in a liquid polymer; and subjecting said immersed plant fibres to a vacuum to replace acetone in said plant fibers with said liquid polymer.

2. The method of claim 1 wherein said plant sample are selected form the group consisting of bamboo, hemp and flax.

3. The method of claim 1 wherein the plant sample comprises at least a single plant fibre.

4. The method claim 3 wherein the plant sample comprise a single plant fibre.

5. The method of claim 3 wherein the plant sample comprises a plurality of individual plant fibres grouped together.

6. The method of claim 3 wherein said plant fibers are formed by crushing at least a portion of a plant.

7. The method of claim 3 wherein the plant sample is formed by cutting at least a portion of a plant.

8. A plastinated plant material comprising formed by removing all moisture within a quantity of a plant material plant sample and replacing said moisture with liquid polymer distributed.

9. The plastinated plant material of claim 8 wherein the plant material sample comprise at least a single plant fibre.

10. The plastinated plant material claim 8 wherein the plant material sample comprises a single plant fibre.

11. The plastinated plant material of claim 8 wherein the plant material sample comprises a plurality of individual plant fibres grouped together.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] In drawings which illustrate embodiments of the invention wherein similar characters of reference denote corresponding parts in each view,

[0013] FIG. 1 is a flow chart depicting a process for plastinating natural plant fibers.

[0014] FIG. 2 is a flow chart depicting a process for preparing elongate rods with palatinate natural plant fibers according to a first embodiment of the present invention.

[0015] FIG. 3 is a perspective view of a composite concrete body having elongate rods formed of plastinated natural plant fibers therein.

[0016] FIG. 4 is a cross sectional view of an apparatus for extruding the elongate rods with plastinated natural plant fibers in accordance with the method of FIG. 2.

DETAILED DESCRIPTION

[0017] The present invention provides a process for forming a reinforced bar (rebar) with plastinated natural plant fibers for use in concrete. According to a first embodiment of the present invention, plant fibers are plastinated by means as are commonly known, then the plastinated fibrers are combined with a plastic matrix and extruded to form elongate rods to be used as rebar within concrete, as is commonly known. Optionally, the plastinated fibers may be located within a concrete slurry to form a fiber-reinforced concrete mixture, increasing the structural integrity of the concrete.

[0018] Referring to FIG. 1, a process for plastinating natural plant fibers is illustrated generally at 10. Various plastination processes are commonly known, and described herein is one exemplary method. It will be appreciated that other plastination methods and techniques may also be useful as well. The plant fibers may be selected from a desired plant species, such as, by way of non-limiting example, bamboo, hemp and flax, although other plant species may be useful, as well. In particular, the bamboo species Guadua Angustifolia, has been found to have a higher tensile strength and may be particularly useful for the present methods.

[0019] The plant is harvested and prepared for plastination in step 12. The plant is dried, crushed and cut to prepare it into individual fibers or groups of fibres at this stage, although it will be appreciated that the plant may be crushed or cut into individual fibres following the plastination process, as well, such as, by way of non-limiting example, chipping shredding or the like. The plant fibers are immersed in a 100% acetone bath in step 14, which is brought to a temperature of between 13 and 77 degrees Fahrenheit (25 and 25 degrees Celsius) at which point the acetone replaces the water within the plant cells, thus dehydrating the plant material and eliminating moisture and mold concerns. In particular, it has been found that room temperature, such as, by way of non-limiting example, between 59 and 77 degrees Fahrenheit (15 and 25 degrees Celsius has been useful. The plant fibers remain in the acetone bath until they are saturated with acetone. Following dehydration, the dehydrated plant material is immersed in a liquid polymer bath in step 16. The liquid polymer bath may be formed of such as, by way of non-limiting example, silicone polymer (such a mixture of Biodur S10 and Biodur S3), polyester or epoxy resin, although other liquid polymers may be useful, as well. In particular, it has been found that a mixture of 100 parts S10 to 1 part S3 has been useful. The liquid polymer bath with the dehydrated plant material therein may be placed under vacuum, which vaporizes the acetone in the cells and draws the liquid polymer therein to replace the acetone. Step 16 continues until surface bubbles stop forming, at which point the vacuum is released and Biodur S6 is sprayed onto the fibers. Finally, in step 18 the plant material is removed from the liquid polymer bath and the liquid polymer within the cells may be cured to a hardened state. The curing process may include such as, by way of non-limiting example, drying at room temperature or applying heat, gas or ultraviolet light.

[0020] At this stage, the plastinated fibers 54 may be combined with a concrete slurry to produce a fiber-reinforced concrete product. Concrete with fibrous material therein has been shown to have improved structural integrity, helping to control cracking and providing greater impact, abrasion and shatter-resistance. As the water content of the plant fibers has been replaced by a liquid polymer, the fibers will not decay, attract insects or expand due to moisture absorption. Such fibers may be utilized within a matrix of another material, such as by way of non limiting example plastics or concrete as described herein and may also be utilized as a non decaying fiber which may be used in place of any other commonly known fibers. In particular it will be appreciated that such plastinated fibers may be stronger than the unplastinated fibers as well as being resistant to moisture, mildew and rot due to near 0% moisture in such plastinated fibers. Such fibers may also be less subject to deterioration when exposed to ultra violet light. By way of non-limiting example such plastinated fibers may be useful as a substitute for organic or inorganic fibers in composite material. It will also be appreciated the whole plant or any portion thereof such as, by way of non-limiting example, dimensioned lumber may be plastinated in the above manner to provide the above advantages. It has also been found that including plastinated fibers within other composite materials such as fiberglass may provide improved impact and noise dampening properties.

[0021] Turning now to FIG. 2, a process for preparing plastinated plant fiber rods is illustrated generally at 20. Plastic material 56 such as, by way of non-limiting example, Polyethylene Terephthalate (PET) plastic, such as from reclaimed water, soda and juice bottles, is washed and shredded in step 22. The washing and shredding process may be performed on site or locally available PET plastic facilities may be used, providing local employment and an incentive for environmental reclamation by removal of discarded PET plastic. The PET plastic material 56 may be shredded by any known means, such as, by way of non-limiting example, through a shredder, grinder, wood chipper, pelletizer or the like. The plastinated fibers prepared in the process 10 are then combined with the prepared PET plastic in step 24 and fed into an extrusion machine as illustrated in FIG. 4 and further described below. The combined material is brought to a temperature in the range of such as, by way of non-limiting example, 475 to 536 degrees Fahrenheit (246 to 280 degrees Celsius) and extruded into elongate rods 50 in step 26. The combined material is kept within this temperature range for up to 20 seconds prior to being extruded. Upon exit from the extrusion machine, while the elongate rods 50 are at an elevated temperature in the range such as, by way of non-limiting example, 86 to 275 Fahrenheit (30 to 135 Celsius), they may have adhesion agent 52 applied thereto while a ribbing surface texture is imprinted thereon in step 28. The adhesion agent 52 may be such as, by way of non-limiting example, lime, recycled concrete or sand, although other adhesion agents may be useful as well. The combination of a ribbed surface, as is commonly known, and the embedded adhesion agent improves adhesion to concrete over conventional methods.

[0022] The prepared elongate rods 50 may now be used for concrete reinforcement in the same manner as typical rebar is used, as is commonly known as illustrated in FIG. 3 by embedding within or otherwise forming a concrete structure 40 therearound according to known methods.

[0023] Turning now to FIG. 4, an exemplary extrusion apparatus is illustrated generally at 60. The extrusion apparatus includes a hopper 62 adapted to receive the plastinated natural plant fibres 54 and PET plastic material 56. The extrusion apparatus 60 may include an auger 64 having a spiralled driving surface or fin 66 extending therefrom such that rotation of the auger 64 by a motor 68 will move the plastinated natural plant fibres 54 and PET plastic material 56 along the extrusion housing towards and through an extrusion die 72. A heater 70 may be provided to increase the temperature of the combined plastinated natural plant fibres 54 and PET plastic material 56 to the desired temperature. Upon exit from the extrusion apparatus 60, the elongate rod 50 may have an adhesion agent 52 applied thereto, as described above. It will be appreciated that although a single screw style extrusion machine is illustrated, any other suitable extrusion machine may also be useful such as, by way of non-limiting example, a twin screw design. It will be appreciated that the hopper 62 may receive PET plastic material 56 without the addition of plastinated natural fibres 54 to form an elongate rod 50 which does not include plastinated natural fibres 54 therein, or the hopper may receive PET plastic material 56 with the addition of alternate fibrous material, such as, by way of non-limiting example, glass, carbon, aramid or boron fibers.

[0024] While specific embodiments of the invention have been described and illustrated, such embodiments should be considered illustrative of the invention only and not as limiting the invention as construed in accordance with the accompanying claims.