METHODS FOR METAL FLOW REACTOR MODULES AND MODULES PRODUCED

Abstract

A method for forming a metal flow module includes stacking together a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface with a second metal plate having opposing first and second major surfaces, the plates stacked together with their respective first major surfaces facing each other and with a layer of flux positioned in between contacting portions of the respective first major surfaces defined as those portions of the respective first and second major surfaces which would be in contact absent the flux; then heating the plates together in a non-oxidizing atmosphere to thermally bond the contacting portions of the respective first major surfaces of the first and second metal plates. Resulting modules are also disclosed.

Claims

1. A method for forming a metal flow module, the method comprising: stacking together a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface, with a second metal plate having opposing first and second major surfaces, the plates stacked together with their respective first major surfaces facing each other and with a layer of flux positioned in between contacting portions of the respective first major surfaces defined as those portions of the respective first and second major surfaces which would be in contact absent the flux; heating the plates together in a non-oxidizing atmosphere to thermally bond the contacting portions of the respective first major surfaces of the first and second metal plates.

2. The method of claim 1 wherein the second metal plate has one or more flow channels defined at least in part in the first major surface thereof.

3. The method of claim 1 wherein the flux comprises a carbide or nitride powder.

4. The method of claim 1 wherein the flux comprises a carbide powder.

5. The method of claim 4 wherein the flux comprises boron carbide powder.

6. The method of claim 1 wherein heating the plates is performed while pressing the plates together.

7. The method of claim 1 further comprising mechanically fastening the plates together prior to heating the plates.

8. The method of claim 7 wherein mechanically fastening the plates together comprises joining the plates with screws or bolts around the perimeter thereof.

9. The method of claim 7 wherein mechanically fastening the plates together comprises joining the plates with screws or bolts positioned around the perimeter thereof.

10. The method of claim 7 wherein mechanically fastening the plates together comprises joining the plates with screws or bolts positioned at locations around the perimeter thereof and in the center thereof.

11. The method according to claim 1 also comprising coating at least portions of the first major surfaces of the first and second plates with a chemically resistant coating prior to stacking the plates together.

12. The method according to claim 11 wherein the portions correspond, defined as align to, to locations of the flow channels.

13. The method according to claim 1 also comprising, after heating the plates together in a non-oxidizing atmosphere to thermally bond the contacting portions of the respective first major surfaces of the first and second metal plates, coating the flow channels with a chemically resistant coating.

14. The method of claim 1 further comprising forming in the first major surface of the first plate the one or more flow channels defined at least in part in the first major surface.

15. The method of claim 14 wherein forming is performed by machining.

16. A flow module useful in a flow reactor or for other fluidic processing, the flow module comprising: a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface; a second metal plate having opposing first and second major surfaces, the plates joined together with their respective first major surfaces facing each other by a flux bond.

17. A flow module useful in a flow reactor or for other fluidic processing, the flow module comprising: a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface; a second metal plate having opposing first and second major surfaces, the plates joined together with their respective first major surfaces facing each other by flux-assisted interdiffusion and/or co-melting of the facing surfaces.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] The following is a description of the figures in the accompanying drawings. The figures are not necessarily to scale, and certain features and certain views of the figures may be shown exaggerated in scale or in schematic in the interest of clarity and conciseness.

[0020] In the drawings:

[0021] FIG. 1 is flow diagram illustrating steps optional steps of embodiments of the present disclosure;

[0022] FIG. 2 is a digital photograph of an embodiment of a metal plate according to aspects of the current disclosure, the plate having one or more channels machined therein;

[0023] FIG. 3 is a digital photograph of an embodiment of a flow module according to aspects of the present disclosure;

[0024] FIG. 4 is a digital photograph of another embodiment of a flow module according to aspects of the present disclosure; and

[0025] FIG. 5 is a close up digital photograph of an edge of an embodiment of a flow module according to aspects of the present disclosure showing a seal between first and second plates of the module.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0026] Additional features and advantages will be set forth in the detailed description which follows and will be apparent to those skilled in the art from the description, or recognized by practicing the embodiments as described in the following description, together with the claims and appended drawings.

[0027] As used herein, the term “and/or,” when used in a list of two or more items, means that any one of the listed items can be employed by itself, or any combination of two or more of the listed items can be employed. For example, if a composition is described as containing components A, B, and/or C, the composition can contain A alone; B alone; C alone; A and B in combination; A and C in combination; B and C in combination; or A, B, and C in combination.

[0028] In this document, relational terms, such as first and second, top and bottom, and the like, are used solely to distinguish one entity or action from another entity or action, without necessarily requiring or implying any actual such relationship or order between such entities or actions.

[0029] Modifications of the disclosure will occur to those skilled in the art and to those who make or use the disclosure. Therefore, it is understood that the embodiments shown in the drawings and described above are merely for illustrative purposes and not intended to limit the scope of the disclosure, which is defined by the following claims, as interpreted according to the principles of patent law, including the doctrine of equivalents.

[0030] For purposes of this disclosure, the term “coupled” (in all of its forms: couple, coupling, coupled, etc.) generally means the joining of two components directly or indirectly to one another. Such joining may be stationary in nature or movable in nature. Such joining may be achieved with the two components and any additional intermediate members being integrally formed as a single unitary body with one another or with the two components. Such joining may be permanent in nature, or may be removable or releasable in nature, unless otherwise stated.

[0031] As used herein, the term “about” means that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. When the term “about” is used in describing a value or an end-point of a range, the disclosure should be understood to include the specific value or end-point referred to. Whether or not a numerical value or end-point of a range in the specification recites “about,” the numerical value or end-point of a range is intended to include two embodiments: one modified by “about,” and one not modified by “about.” It will be further understood that the end-points of each of the ranges are significant both in relation to the other end-point, and independently of the other end-point.

[0032] The terms “substantial,” “substantially,” and variations thereof as used herein are intended to note that a described feature is equal or approximately equal to a value or description. For example, a “substantially planar” surface is intended to denote a surface that is planar or approximately planar. Moreover, “substantially” is intended to denote that two values are equal or approximately equal. In some embodiments, “substantially” may denote values within about 10% of each other, such as within about 5% of each other, or within about 2% of each other.

[0033] Directional terms as used herein—for example up, down, right, left, front, back, top, bottom—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.

[0034] As used herein the terms “the,” “a,” or “an,” mean “at least one,” and should not be limited to “only one” unless explicitly indicated to the contrary. Thus, for example, reference to “a component” includes embodiments having two or more such components unless the context clearly indicates otherwise.

[0035] As used herein, a “tortuous” passage refers to a passage having no line of sight directly through the module and with the central path of the passage tracing more than one radius of curvature, such that typical machining-based forming techniques are generally inadequate to form such a passage.

[0036] With reference to FIG. 1, a method 100 is represented in the flow diagram of the figure, the method comprising the step 10 of stacking together a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface, with a second metal plate having opposing first and second major surfaces, the plates stacked together with their respective first major surfaces facing each other and with a layer of flux positioned in between contacting portions of the respective first major surfaces defined as those portions of the respective first and second major surfaces which would be in contact absent the flux.

[0037] The presently preferred metal for the plates is 316L stainless steel, which has high corrosion performance and is readily available various thicknesses and sizes. Other stainless steel metals can be used as well including hastalloy, as well as still other metals.

[0038] The method further comprises the step 20 of then heating the plates together in a non-oxidizing atmosphere to thermally bond the contacting portions of the respective first major surfaces of the first and second metal plates.

[0039] The currently preferred flux is carbide powder for preserving chemical resistance of the finished modules. Any carbide powder (silicon carbide, boron carbide, hafnium carbide, etc.), or mixtures thereof, can be used. The preferred fluxing agent for lower sealing temperature is boron carbide as the bonding temperature (approximately 1210° C.) is significantly lower than other carbide powders (for example, silicon carbide requires a flux temperature of approximately 1340° C.). The carbide powder or carbide powder mixture is merely sprinkled onto the first surface of one of the plates so that there is complete coverage. It has been found that some nitride powders (silicon nitride) can bond as well, but carbide powder flux has better corrosion resistance relative to nitrides. The flux bonding process requires that it take place in an non-oxidizing or in an inert atmosphere (argon, vacuum, etc.). For carbide powders the bonding process can adequately take place in 90 minutes at peak temperature (for boron carbide that is 1210° C.).

[0040] According to embodiments of the method, the second metal plate can also have one or more flow channels defined at least in part in the first major surface thereof.

[0041] According to embodiments, the heating step can be performed while pressing the plates together, although it can also be successful without external pressing. As the plates become relatively larger, however, it is currently preferred to mechanically fasten the plates together prior to heating, such as by joining the plates with screws or bolts positioned around the perimeter thereof.

[0042] FIG. 2 shows a plate 200 for use in the disclosed method. The plate is stainless steel with a channel 210 formed in a first major surface 201 of the plate, such as by machining. A second major surface 202 of the plate 200, the surface 202 not being directly visible in the photograph of FIG. 2, is positioned opposite the first major surface 201. The channel 210 has two inputs 230 and an output 232.

[0043] FIG. 3 shows a finished (sealed) module 300 after the heating step. Metal fluid connectors 240 have been added.

[0044] FIG. 4 shows another finished (sealed) module 300 after the heating step. Bolts were used at locations around the perimeter of the module 300 to hold the first and second plates together and prevent warping or separation during heating. Metal fluid connectors 240 have again been added.

[0045] According to another aspect of the present method, the threads of the fluid connectors 240 (such as Swagelok® fittings) used for fluid inputs and outputs can be coated with a flux material prior to threading them into the respective plate, prior to the heating step. This produces a permanent and durable seal between the fluid connectors 240 and the module 300. Without thermal flux-assisted bonding of the connectors into the plate, leaks can occur under high pressure. The flux for this purpose may take the form of a water based paint mixture including silicon carbide and boron carbide powder.

[0046] For some applications, additional corrosion resistance is needed even relative to stainless steel. For such applications, a carbide film (silicon carbide is preferred) can be first deposited on the open face of the milled channel plate prior to plate stacking and heating and bonding process. Alternatively, the channels within the finished module may be coated after heating and bonding.

[0047] As another aspect of the present disclosure, a flow module useful in a flow reactor or for other fluidic processing is provided, the flow module comprising a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface and a second metal plate having opposing first and second major surfaces, the plates joined together with their respective first major surfaces facing each other by a flux bond.

[0048] As yet another aspect of the present disclosure, a flow module useful in a flow reactor or for other fluidic processing is provided, the flow module comprising a first metal plate having opposing first and second major surfaces and one or more flow channels defined at least in part in the first major surface and a second metal plate having opposing first and second major surfaces, the plates joined together with their respective first major surfaces facing each other by flux-assisted interdiffusion and/or co-melting of the facing surfaces.

[0049] FIG. 5 is a close up digital photograph of an edge of an embodiment of a flow module according to aspects of the present disclosure showing a seal between first and second plates 200a, 200b, of a module 300. As may be seen in the figure, flux-assisted interdiffusion and/or co-melting of the facing (“first”) surfaces of the plates 200a, 200b, has occurred at the interface 260, producing a robust seal.

[0050] The methods and modules of the present disclosure provide a low-cost method to produce a metal or stainless steel flow reactor module. If embedded fluid couplers are included, users have a simple way of connecting to the module, and the process of embedding is likewise simple and produces a robust seal between the couplers and the consolidated plate. The method also provides a flow reactor module which is sealed or enclosed without the use of organic materials such as gaskets or O-rings, allowing for performance high temperature processes or reactions, or other processes or reactions incompatible with organic materials.

[0051] While exemplary embodiments and examples have been set forth for the purpose of illustration, the foregoing description is not intended in any way to limit the scope of disclosure and appended claims. Accordingly, variations and modifications may be made to the above-described embodiments and examples without departing substantially from the spirit and various principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.