OSCILLATING NOZZLE FOR SINUSOIDAL DIRECT METAL DEPOSITION

Abstract

A system and a method for the rapid manufacturing of objects by direct metal deposition are disclosed. The system and method include an oscillating nozzle suspended by a gantry system or a robotic arm over a workpiece build. In some embodiments, the workpiece build is supported by a rotary stage, while in other embodiments the workpiece build is stationary. In embodiments including a rotary stage, the oscillating nozzle oscillates back and forth along the X-axis, and/or rotates clockwise and counter-clockwise about the Y-axis, as the rotary stage rotates about the Z-axis, resulting in a sinusoidal toolpath. In embodiments lacking a rotary stage, the oscillating nozzle is continuously rotated about the Z-axis by the gantry system or the robot arm. The sinusoidal toolpath results in a sinusoidal deposition track, which is particularly useful for building walled structures having rotational symmetry, including conical structures.

Claims

1. A method of performing direct material deposition upon a workpiece that has rotational symmetry about a vertical axis, comprising the steps of: providing a nozzle adapted to oscillate along a linear axis and adapted to pivot about a tilt axis that is orthogonal to the linear axis; causing the nozzle to project a laser beam and discharge a metal powder toward the workpiece while oscillating about the linear axis or the tilt axis; and causing the workpiece to rotate about the vertical axis as the nozzle is oscillating along the linear axis or pivoting about the tilt axis, such that the nozzle deposits a metal powder along a sinusoidal toolpath, thereby forming an additive layer on the surface of the workpiece by direct metal deposition.

2. The method set forth in claim 1, wherein the additive layer comprises a wall feature having a length and a width, further including causing relative movement of the nozzle along the length of the wall feature and causing the nozzle to trace the width of the wall feature.

3. The method set forth in claim 2, further including adjusting a speed of the nozzle during relative movement of the nozzle along the length of the wall feature.

4. The method set forth in claim 1, wherein causing the workpiece to rotate includes rotating the workpiece by a rotary stage.

5. The method set forth in claim 1, wherein the nozzle is mounted to a gantry system or a robotic arm.

6. The method set forth in claim 1, wherein the tilt axis of the oscillating nozzle positions the nozzle perpendicular to the workpiece.

7. The method set forth in claim 1, further including causing the workpiece to cease rotation as the nozzle oscillates along the linear axis or pivots about the tilt axis, such that the nozzle continues the additive layer of the workpiece without rotation of the workpiece.

8. A method of performing direct material deposition upon a stationary workpiece, comprising the steps of: providing a nozzle adapted to oscillate along a linear axis and adapted to pivot about a tilt axis that is orthogonal to the linear axis; causing the nozzle to project a laser beam and discharge a metal powder toward the stationary workpiece while oscillating about the linear axis or pivoting about the tilt axis; and causing the nozzle to move over the stationary workpiece in a linear direction that is perpendicular to the linear axis as the nozzle is oscillating along the linear axis or pivoting about the tilt axis, such that the nozzle deposits a metal powder along a sinusoidal toolpath, thereby forming an additive layer on the surface of the stationary workpiece by direct metal deposition.

9. The method set forth in claim 8, wherein the additive layer comprises a wall feature having a length and a width, further including causing relative movement of the nozzle along the length of the wall feature and causing the nozzle to trace the width of the wall feature.

10. The method set forth in claim 9, further including adjusting a speed of the nozzle during relative movement of the nozzle along the length of the wall feature.

11. The method set forth in claim 8, wherein the tilt axis of the oscillating nozzle positions the nozzle perpendicular to the workpiece.

12. The method set forth in claim 8, wherein the nozzle is driven by a gantry system or a robot arm.

13. The method set forth in claim 12, wherein the nozzle oscillates along the linear axis in a direction that is perpendicular to linear directional motion of the gantry system or a robot arm.

14. The method set forth in claim 12, further including moving the gantry system or robot art within a horizontal plane during formation of the additive layer.

15. The method set forth in claim 12, further including rotating the gantry system or robot arm about a vertical axis during formation of the additive layer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIG. 1 is a schematic of the rotating symmetrical workpiece and oscillating nozzle making the sinusoidal toolpath deposition when tilt axis at home position (hollow cylinder).

[0010] FIG. 2 is a schematic of the rotating symmetrical workpiece and oscillating nozzle making the sinusoidal toolpath deposition when tilt axis at positive angle (hollow expanding cone).

[0011] FIG. 3 is a schematic of the rotating symmetrical workpiece and oscillating nozzle making the sinusoidal toolpath deposition when tilt axis at negative angle (hollow tapering cone).

[0012] FIG. 4 shows the nozzle moving linearly towards inner wall of the stationary workpiece.

[0013] FIG. 5 shows the nozzle moving linearly towards outer wall of the stationary workpiece.

[0014] FIG. 6 shows the top view schematic of the stationary workpiece and oscillating nozzle making of the sinusoidal toolpath.

[0015] FIG. 7 shows the top view schematic of the rotating workpiece and oscillating nozzle making of the sinusoidal toolpath.

[0016] FIG. 8 shows an oscillating nozzle mounted onto a gantry or a robotic arm which moves in one direction to deposit a wall feature on a stationary workpiece.

[0017] FIG. 9 shows an oscillating nozzle mounted onto a gantry or a robotic arm which rotates to maintain the oscillating nozzle at a perpendicular axis to the linear directional motion of the nozzle over a stationary workpiece.

DETAILED DESCRIPTION OF THE CURRENT EMBODIMENTS

[0018] The current embodiments include a system and a method for direct metal deposition of a workpiece build, the workpiece build optionally having rotational symmetry. The system and the method include an oscillating nozzle supported above a workpiece build for generating a sinusoidal toolpath. The sinusoidal toolpath decreases the build time for hollow workpieces having vertical and angled wall features. The workpieces are completely or partially formed by DMD, while in other embodiments the workpieces are rebuilt or repaired by DMD.

[0019] Referring to FIG. 1, a rotating symmetrical workpiece 10 and oscillating nozzle 12 is illustrated. The workpiece 10 includes complete rotational symmetry about the Z-axis in the present embodiment, while in other embodiments only a portion of the workpiece 10 is symmetrical about the Z-axis. The workpiece 10 includes a sidewall 14 formed in successive layers according to a direct metal deposition process. As noted above, direct metal deposition is a laser-based additive manufacturing process in which metal alloy powder is directly blown into a melt pool. The laser energy beam and the metal alloy powder interact at or slightly above the workpiece surface, and the metal allow powder is absorbed into the laser-induced melt pool, which rapidly solidifies. The nozzle 12 deposits a track in a sinusoidal pattern, multiple overlapping tracks form a layer, and multiple layers form the three-dimensional workpiece 10. The oscillating nozzle 12 is adapted for performing DMD, for example the nozzle disclosed in U.S. Pat. No. 6,534,745 entitled “Nozzle Particularly Suited to Direct Metal Deposition,” the disclosure of which is incorporated by reference in its entirety. The oscillating nozzle 12 is suspended over a build platform, for example a rotary stage 16, and the oscillating nozzle 12 is pivotable about a tilt axis via a rotary motor 18 and is translatable along a linear axis via a linear motor 20.

[0020] In particular, a robotic arm or an overhead gantry 100 a controls movement of the oscillating nozzle 12 in accordance with a toolpath for the workpiece 10. The oscillating nozzle 12 is moveable along the X-axis, shown in FIG. 1, and the oscillating nozzle 12 is rotatable about the Y-axis, shown in FIGS. 2 and 3. In one embodiment, a rotary stage 16 causes the workpiece 10 to continuously rotate about the Z-axis during this back-and-forth movement of the nozzle 12, such that the nozzle 12 deposits a track of additive material in a sinusoidal pattern. The rotary stage 16 receives rotational movement from a rotary servo motor. In other embodiments the workpiece 10 is stationary, and the oscillating nozzle 12 continuously orbits the workpiece about the Z-axis. The amplitude of the sinusoidal pattern determines the thickness of the sidewall 14, such that the thickness of the sidewall 14 can increase or decrease with successive layers of the workpiece build. The peaks of the sinusoidal pattern (the portion of the sinusoidal pattern having zero slope) form the inner and outer contours of the sidewall 14, and the remainder of the sinusoidal pattern (the portion of the sinusoidal pattern having a non-zero slope) determine the inner quality of the sidewall 14.

[0021] As shown in FIG. 1, the tilt axis of the oscillating nozzle 12 is in the home position for forming successive layers of a hollow cylinder. The tilt axis of the oscillating nozzle 12 includes a positive angle in FIG. 2 for forming successive layers of a hollow expanding cone. The tilt axis of the oscillating nozzle 12 includes a negative angle in FIG. 3 for forming successive layers of a hollow tapering cone. In FIGS. 2 and 3, the oscillating nozzle 12 is oriented normal to the workpiece feature, providing a perpendicular additive build. FIGS. 4 and 5 depict the toolpath for a stationary workpiece build. As shown in FIG. 4, the oscillating nozzle 12 is depicted as moving linearly towards the inner wall of the stationary workpiece 10, while in FIG. 5 the oscillating nozzle 12 is depicted as moving linearly towards the outer wall of the stationary workpiece 10. In these embodiments, the gantry (or the robot arm) rotate the nozzle about the Z-axis while the nozzle oscillates in the manner set forth above. FIG. 6 shows the top view schematic of the stationary workpiece 10 and oscillating nozzle 12 making of the sinusoidal toolpath. As noted above, the peaks of the sinusoidal toolpath form the inner and outer contours of the sidewall 14, and the remainder of the sinusoidal toolpath determine the inner quality of the sidewall 14. The sinusoidal toolpath deposits a sinusoidal track of metal alloy to form a layer of the workpiece build, and multiple layers form the completed three-dimensional workpiece. This is further illustrated in FIG. 7, which shows the top view schematic of the rotating workpiece 10 and oscillating nozzle 12 making of the sinusoidal toolpath.

[0022] In another embodiment, the oscillating nozzle is mounted to a gantry or robotic arm and deposits onto a stationary workpiece. In FIG. 8, the gantry or robotic arm moves in a linear motion, carrying the oscillating nozzle 12, which deposits a wall feature 14 onto a stationary workpiece or build platform. In particular, the oscillating nozzle 12 is mounted onto a gantry or a robotic arm which moves in a linear direction as the oscillating nozzle 12 pivots about the tilt axis and/or translates along the linear axis. In FIG. 9, the gantry or robotic arm moves in two directional motion, carrying the oscillating nozzle 12, which deposits a rectangle 14 on a stationary workpiece. In particular, the gantry or a robotic arm rotates to maintain the oscillating nozzle 12 at a perpendicular axis to the linear directional motion of the nozzle 12 over a stationary workpiece 14. The gantry or robotic arm may move in multi-directional toolpath motion, carrying the oscillating nozzle to create sinusoidal deposition on a stationary workpiece.

[0023] The above description is that of current embodiments. Various alterations can be made without departing from the spirit and broader aspects of the invention as defined in the claims, which are to be interpreted in accordance with the principles of patent law including the doctrine of equivalents. This disclosure is presented for illustrative purposes and should not be interpreted as an exhaustive description of all embodiments of the invention or to limit the scope of the claims to the specific elements illustrated or described in connection with these embodiments. The present invention is not limited to only those embodiments that include all of these features or that provide all of the stated benefits, except to the extent otherwise expressly set forth in the issued claims. Any reference to claim elements in the singular, for example, using the articles “a,” “an,” “the” or “said,” is not to be construed as limiting the element to the singular.