CATHODE SHEET AND METHOD FOR PREPARING SAME, AND LITHIUM-ION BATTERY

Abstract

The present invention relates to the technical field of lithium-ion batteries, and particularly provides a positive electrode sheet and a preparation method therefor, and a lithium-ion battery comprising the positive electrode sheet. The positive electrode sheet comprises a positive electrode active material layer, and the positive electrode active material layer comprises a positive electrode material, a negative thermal expansion material, a conductive agent, and a binder, wherein the characteristic value J of the positive electrode sheet satisfies: 0.001J0.005. wherein J=R(F)/, R(F) represents the peak intensity ratio between the main peak (F) of the negative thermal expansion material and the (003) characteristic peak of the positive electrode material in the XRD pattern of the positive electrode sheet, and p represents the surface density of the positive electrode sheet, with a unit of mg/cm.sup.2.

Claims

1. A cathode sheet, comprising a cathode active material layer, wherein the cathode active material layer comprises a cathode material, a negative thermal expansion material, a conductive agent, and a binder, wherein the cathode sheet has a characteristic value J satisfying: 0.001J0.005, J=R(F)/, where: R(F) represents a ratio of a peak intensity of a main peak (F) of the negative thermal expansion material to a peak intensity of a (003) characteristic peak of the cathode material in an X-Ray Diffraction (XRD) pattern of the cathode sheet; and represents an areal density of the cathode sheet, in the unit of mg/cm.sup.2.

2. The cathode sheet according to claim 1, wherein the characteristic value J of the cathode sheet satisfies: 0.00125J0.004.

3. The cathode sheet according to claim 1, wherein R(F)=I(F)/I(003), where: I(F) represents the peak intensity of the main peak (F) of the negative thermal expansion material in the XRD pattern of the cathode sheet; and I(003) represents the peak intensity of the (003) characteristic peak of the cathode material in the XRD pattern of the cathode sheet; and wherein: 0.005R(F)0.1, and preferably, 0.02R(F)0.05.

4. The cathode sheet according to claim 1, wherein the areal density of the cathode sheet satisfies: 8 mg/cm.sup.225 mg/cm.sup.2, and preferably, 10 mg/cm.sup.216 mg/cm.sup.2.

5. The cathode sheet according to claim 1, wherein in the XRD pattern of the cathode sheet, the cathode material has the (003) characteristic peak at 2=182 and a (101) characteristic peak at 2=372; and wherein: in the XRD pattern of the cathode sheet, the main peak (F) of the negative thermal expansion material is located between the (003) characteristic peak and the (101) characteristic peak of the cathode material.

6. The cathode sheet according to claim 1, wherein the negative thermal expansion material has an average particle size D.sub.50(F) satisfying: D.sub.50(F)0.42D.sub.50, where D.sub.50 represents an average particle size of the cathode material, in the unit of m.

7. The cathode sheet according to claim 1, wherein the cathode material has an average particle size D.sub.50 ranging from 1 m to 20 m, and preferably, ranging from 1 m to 10 m.

8. The cathode sheet according to claim 1, wherein the negative thermal expansion material has an average particle size D.sub.50(F) ranging from 0.1 m to 10 m, and preferably, ranging from 0.1 m to 3 m.

9. The cathode sheet according to claim 1, wherein the cathode material is a lithium-containing layered compound.

10. The cathode sheet according to claim 1, wherein the cathode material has a composition represented by Formula I: Li.sub.1+Ni.sub.xCo.sub.yMn.sub.zM.sub.mM.sub.nO.sub.2 (I), where 0.50.4, 0<x<1, 0y<1, 0z<1, 0m0.1, 0n0.1, x+y+z+m+n=1, and M and M are each independently selected from at least one element of Al, Y, Ti, Zr, V, Nb, Ta, Cr, Mo, W, La, Ce, Er, Mg, Sr, Ba, P, or B, preferably, in the Formula I, 00.1, 0.6x0.9, 0.01y0.2, 0.01z0.3, m and n are not both zero, and 0.001m+n0.1; preferably, in the Formula I, M and M are different elements; and more preferably, in the Formula I, M is selected from at least one element of Al, Y, Ti, Zr, La, Sr, or B, and M is selected from at least one element of Nb, Mo, W, or P.

11. The cathode sheet according to claim 1, wherein the negative thermal expansion material has a composition represented by Formula II: Q.sub.aQ.sub.bO.sub.c (II), where: a, b, and c are each independently selected from a natural number from 1 to 15; Q and Q are each independently selected from at least one element of Zr, W, Hf, Al, Sc, In, Y, Mo, V, Sn, Ti, or P; and Q and Q are different elements.

12. The cathode sheet according to claim 1, wherein the negative thermal expansion material is selected from at least one of tungstates, molybdates, vanadates, or pyrophosphates, and preferably, the negative thermal expansion material is selected from at least one of ZrW.sub.2O.sub.8, HfW.sub.2O.sub.8, Al.sub.2W.sub.3O.sub.12, Sc.sub.2W.sub.3O.sub.12, In.sub.2W.sub.3O.sub.12, Y.sub.2W.sub.3O.sub.12, ZrMo.sub.2O.sub.8, HfMo.sub.2O.sub.8, ZrV.sub.2O.sub.7, HfV.sub.2O.sub.7, SnV.sub.2O.sub.7, TiV.sub.2O.sub.7, ZrP.sub.2O.sub.7, HfP.sub.2O.sub.7, SnP.sub.2O.sub.7, or TiP.sub.2O.sub.7.

13. The cathode sheet according to claim 1, wherein the cathode active material layer has a thickness ranging from 20 m to 85 m, and preferably, from 25 m to 60 m.

14. The cathode sheet according to claim 1, wherein based on a total weight of the cathode active material layer: a content of the cathode material ranges from 85.5 wt % to 94.52 wt %, and preferably, from 90 wt % to 94.5 wt %; a content of the negative thermal expansion material ranges from 0.48 wt % to 9.5 wt %, and preferably, from 0.5 wt % to 5 wt %; a content of the conductive agent ranges from 2 wt % to 4 wt %, and preferably, from 2.5 wt % to 3.5 wt %; and a content of the binder ranges from 1 wt % to 3 wt %, and preferably, from 1.5 wt % to 2.5 wt %.

15. The cathode sheet according to claim 1, wherein the cathode sheet has an initial discharge impedance value R(d), satisfying R(d)20, and preferably, R(d)18.

16. A method for preparing the cathode sheet according to claim 1, the method comprising: (1) mixing a cathode material, a negative thermal expansion material, a conductive agent, a binder, and a solvent to obtain a cathode slurry; and (2) coating the cathode slurry on a surface of a cathode current collector, and performing drying and roller pressing sequentially, to load a cathode active material layer on the surface of the cathode current collector for obtaining the cathode sheet, wherein: the cathode material is a lithium-containing layered compound; and the negative thermal expansion material has a composition represented by Formula II: Q.sub.aQ.sub.bO.sub.c (II), where: a, b, and c are each independently selected from a natural number from 1 to 15; Q and Q are each independently selected from at least one element of Zr, W, Hf, Al, Sc, In, Y, Mo, V, Sn, Ti, or P; and Q and Q are different elements.

17. The preparation method according to claim 16, wherein in the step (1): the cathode material, the negative thermal expansion material, the conductive agent, and the binder are mixed at a mass ratio of (85.5 to 94.52):(0.48 to 9.5):(2 to 4):(1 to 3), and preferably, (90 to 94.5):(0.5 to 5):(2.5 to 3.5):(1.5 to 2.5); and said mixing is performed under the conditions of: a temperature ranging from 15 C. to 40 C., and preferably, from 20 C. to 30 C.; a duration ranging from 10 min to 120 min, and preferably, from 20 min to 60 min; and a rotational speed ranging from 500 rpm to 2,000 rpm, and preferably, from 800 rpm to 1,500 rpm.

18. The method according to claim 16, wherein the cathode material has a composition represented by Formula I: Li.sub.1+Ni.sub.xCo.sub.yMn.sub.zM.sub.mM.sub.nO.sub.2(I), where 0.50.4, 0<x<1, 0y<1, 0z<1, 0m0.1, 0n0.1, x+y+z+m+n=1, and M and M are each independently selected from at least one element of Al, Y, Ti, Zr, V, Nb, Ta, Cr, Mo, W, La, Ce, Er, Mg, Sr, Ba, P, or B, preferably, in the Formula I, 00.1, 0.6x0.9, 0.01y0.2, 0.01z0.3, m and n are not both zero, and 0.001m+n0.1, preferably, in the Formula I, M and M are different elements, and more preferably, in the Formula I, M is selected from at least one element of Al, Y, Ti, Zr, La, Sr, or B, and M is selected from at least one element of Nb, Mo, W, or P.

19. The method according to claim 16, wherein in the step (2): said drying is performed at a temperature ranging from 80 C. to 150 C., and preferably, from 120 C. to 150 C.; and the roller pressing is performed under a pressure P satisfying 5T<P<20T.

20. A lithium-ion battery, comprising: the cathode sheet according to claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] FIGURE is an XRD pattern of cathode sheet S1 prepared in Example 1.

DETAILED DESCRIPTION

[0011] The endpoint values or any values of the ranges disclosed in the present disclosure are not limited to the precise ranges or values. These ranges or values should be understood to include values close to these ranges or values. For numerical ranges, one or more new numerical ranges can be obtained by combining the endpoint values of the respective ranges, an endpoint value and an individual point value within the respective ranges, and individual point values within the respective ranges, and these numerical ranges should be regarded as specifically disclosed in the present disclosure.

[0012] An objective of the present disclosure is to overcome the above technical problems. The present disclosure provides a cathode sheet and a method for preparing same, and a lithium-ion battery. The cathode sheet possesses low volume expansion, high structural stability, and high-temperature stability. In addition, the lithium-ion battery including the cathode sheet exhibits satisfactory capacity performance, rate capability, cycling performance, and energy density.

[0013] In a first aspect of the present disclosure, a cathode sheet is provided. The cathode sheet includes a cathode active material layer. The cathode active material layer includes a cathode material, a negative thermal expansion material, a conductive agent, and a binder. The cathode sheet has a characteristic value J satisfying: 0.001J0.005. J=R(F)/, where R(F) represents a ratio of a peak intensity of a main peak (F) of the negative thermal expansion material to a peak intensity of a (003) characteristic peak of the cathode material in an X-Ray Diffraction (XRD) pattern of the cathode sheet, and p represents an areal density of the cathode sheet, in the unit of mg/cm.sup.2.

[0014] It was found by the inventor that: by adding the negative thermal expansion material to the cathode active material layer, the negative thermal expansion material can absorb heat generated during cycling of the cathode material in situ and undergo a volume reduction, providing a space for a volume expansion of the cathode active material, and helping to alleviate a stress and avoid a material deformation. In addition, by incorporating the negative thermal expansion material and the cathode material into the cathode active material layer, the negative thermal expansion material maintains its original material structure and is uniformly distributed in the cathode active material layer, forming inter-particle contact with the cathode material. In this way, at a level of the cathode sheet, the negative thermal expansion material can be ensured to optimally counteract a volume expansion of the cathode active material layer caused by a thermal expansion of the cathode material during charge-discharge cycles. Since a lattice parameter of the cathode material (especially a lithium nickel cobalt manganese oxide cathode material) varies within a predetermined range due to different doping modifications, differences also exist in heat generation during charging and discharging when the cathode material is applied in sheets.

[0015] Further, when cathode sheets are processed using a same formulation for a same cathode material, differences in areal densities of coating lead to variations in internal resistances of the sheets, resulting in different heat generation situations of the sheets during the charge-discharge cycles.

[0016] Therefore, in the present disclosure, by reasonably controlling the characteristic value J of the cathode sheet, i.e., by properly controlling a composition of the cathode active material layer in the cathode sheet, the cathode sheet made of the cathode material incorporating the negative thermal expansion material is realized, effectively mitigating the deformation of the cathode sheet caused by the thermal expansion during the charge-discharge cycles without affecting lithium-ion transport performance and electrical conductivity.

[0017] In the present disclosure, J=R(F)/ ranges from 0.001 to 0.005, which defines a relative numerical ratio relationship between R(F) and when the unit of the areal density of the cathode sheet is mg/cm.sup.2. That is, when either R(F) or of the cathode sheet is specified, the other parameter must fall within an appropriate range to obtain the cathode sheet of the present disclosure.

[0018] In the present disclosure, unless otherwise specified, the cathode sheet further includes a cathode current collector. The cathode active material layer is disposed on a surface of the cathode current collector. In the present disclosure, the cathode current collector includes, but is not limited to, an aluminum foil and the like.

[0019] In some embodiments of the present disclosure, the characteristic value J of the cathode sheet satisfies: 0.001J0.005, e.g., 0.001, 0.00125, 0.0015, 0.0018, 0.002, 0.0023, 0.0025, 0.003, 0.0035, 0.004, 0.005, and any value within a range formed by any two of these values. Preferably, 0.00125J0.004.

[0020] In the present disclosure, by reasonably controlling the characteristic value J of the cathode sheet, lithium-ion transport from a bulk to a surface of the cathode material in the cathode active material layer is ensured to be unrestricted, achieving satisfactory rate capability and capacity utilization. In addition, due to a combination of the negative thermal expansion material and the cathode material, an expansion of the cathode sheet during cycling is suppressed, which avoids an impact of the expansion of the cathode sheet on electrical performance, enhancing high-temperature stability and cycle life of the cathode sheet, and improving safety of the battery.

[0021] In some embodiments of the present disclosure, preferably, R(F)=I(F)/I(003), where I(F) represents the peak intensity of the main peak (F) of the negative thermal expansion material in the XRD pattern of the cathode sheet; and I(003) represents the peak intensity of the (003) characteristic peak of the cathode material in the XRD pattern of the cathode.

[0022] In the present disclosure, unless otherwise specified, I(003) represents the peak intensity of the (003) characteristic peak of the cathode material near 2=182, and I(F) represents the peak intensity of the main peak (F) of the negative thermal expansion material.

[0023] In the present disclosure, by adjusting the ratio R(F) of the peak intensity I(F) of the negative thermal expansion material to the peak intensity I(003) of the cathode material in the cathode sheet, high-temperature performance and cycling stability of the sheet can be improved. An R(F) value being too low indicates that the negative thermal expansion material in the processed cathode sheet fails to maintain its original crystal structure, and thus a property of contracting upon heating and expanding upon cooling of the negative thermal expansion material cannot be effectively utilized. However, the R(F) value being too high indicates that an excessive amount of negative thermal expansion material is added, which affects capacity utilization of the cathode sheet.

[0024] In some embodiments of the present disclosure, preferably, 0.005R(F)0.1, e.g., 0.005, 0.01, 0.015, 0.02, 0.025, 0.03, 0.035, 0.04, 0.045, 0.05, 0.08, 0.1, and any value within a range formed by any two of these values. More preferably, 0.02R(F)0.05.

[0025] In the present disclosure, the R(F) value falling within the above range, particularly the preferred range, on the one hand, indicates that the applied negative thermal expansion material possesses satisfactory crystallinity and can maintain its structure within the sheet, thereby exhibiting the characteristic peak (F) in an XRD diffraction pattern. On the other hand, the R(F) value falling within the above range, particularly the preferred range, shows that a proportion of the negative thermal expansion material capable of exerting a negative thermal expansion effect in the cathode active material layer can match a sheet process, thereby achieving optimal performance.

[0026] In the present disclosure, the parameter areal density of the cathode sheet affects performance of the cathode sheet. When the areal density of the cathode sheet is relatively lower, the cathode sheet is relatively thinner, and the battery has a relatively smaller internal resistance. Further, during charge-discharge cycles, a change of a structure of the sheet caused by continuous intercalation and deintercalation of lithium ions in the lithium-ion battery is relatively smaller, which is beneficial for lithium-ion migration. Furthermore, the sheet has a relatively smaller thermal expansion. Conversely, when the areal density of the cathode sheet is relatively higher, the lithium ions have a relatively longer migration path, the battery has a relatively greater internal resistance, and the sheet has a relatively greater thermal expansion.

[0027] In the present disclosure, if the areal density of the cathode sheet is too low, very little active material is available in the battery for fast charging, and a gram capacity of the cathode sheet is relatively low. In addition, during processing of the cathode sheet, cathode active particles are prone to fracture, affecting a service life of the battery. If the areal density p of the cathode sheet is too high, not only stability of the cathode active material layer and a surface quality of the cathode sheet are affected, but also charge transfer impedance and polarization are increased, leading to increased internal resistance of the battery, reduced discharge specific capacity, inferior rate capability, and shortened cycle life. Therefore, reasonably controlling the areal density of the cathode sheet is of great significance for battery performance.

[0028] In some embodiments of the present disclosure, preferably, the areal density of the cathode sheet satisfies: 8 mg/cm.sup.225 mg/cm.sup.2, e.g., 8 mg/cm.sup.2, 10 mg/cm.sup.2, 12 mg/cm.sup.2, 14 mg/cm.sup.2, 16 mg/cm.sup.2, 20 mg/cm.sup.2, 25 mg/cm.sup.2, and any value within a range formed by any two of these values. Preferably, 10 mg/cm.sup.216 mg/cm.sup.2.

[0029] In the present disclosure, unless otherwise specified, the areal density of the cathode sheet refers to a coating weight of the cathode active material layer per unit area of the battery sheet. The parameter areal density of the cathode sheet is measured by the following method: areal density =coating weight m of the cathode active material layer/coating area S. The coating weight m of the cathode active material layer may be obtained by subtracting a weight of the cathode current collector (aluminum foil) from a weight of the coated cathode sheet. The coating area S is an area of the cathode current collector corresponding to the cathode sheet, i.e., an area of the circular aluminum foil, which can be calculated from a diameter of the aluminum foil.

[0030] In the present disclosure, due to a strong orientation of a crystal structure of the cathode material, distinct and separate diffraction peaks appear within a predetermined angular range in the XRD pattern. For example, the (003) characteristic peak of the cathode material corresponds to 2=182, and a (101) characteristic peak of the cathode material corresponds to 2=372, with no other peaks of the cathode material appearing between the (003) characteristic peak and the (101) characteristic peak.

[0031] In some embodiments of the present disclosure, preferably, in the XRD pattern of the cathode sheet, the cathode material has the (003) characteristic peak at 2=182 and the (101) characteristic peak at 2=372.

[0032] In the present disclosure, for the cathode active material layer modified with the negative thermal expansion material, the negative thermal expansion material existing in its original crystal structure can display corresponding lines in the XRD diffraction pattern of the cathode sheet. These lines appear between the (003) characteristic peak and the (101) characteristic peak of the cathode material. One or more characteristic peaks of the negative thermal expansion material may appear in this interval, in which a peak with a highest peak intensity is defined as the main peak (F). An XRD peak intensity of the main peak (F) is defined as I(F).

[0033] In some embodiments of the present disclosure, preferably, in the XRD pattern of the cathode sheet, the main peak (F) of the negative thermal expansion material is located between the (003) characteristic peak and the (101) characteristic peak of the cathode material. Meeting the above feature indicates that the negative thermal expansion material incorporated in the cathode sheet can maintain its original structure and exhibits satisfactory negative thermal expansion performance.

[0034] In a specific embodiment of the present disclosure, in the XRD pattern of the cathode sheet, diffraction peaks of the negative thermal expansion material, especially the main peak (F), are distributed between the (003) characteristic peak and the (101) characteristic peak of the cathode material, i.e., between 2=180 and 2=37.

[0035] In some embodiments of the present disclosure, preferably, the negative thermal expansion material has an average particle size D.sub.50(F) satisfying: D.sub.50(F)0.42D.sub.50, where D.sub.50 represents an average particle size of the cathode material, in the unit of m. In the present disclosure, selecting the negative thermal expansion material with an appropriate D.sub.50(F) helps fill voids in the cathode material of the cathode sheet, allowing the negative thermal expansion material to function more effectively.

[0036] In some embodiments of the present disclosure, preferably, the average particle size D.sub.50 of the cathode material ranges from 1 m to 20 m, e.g., 1 m, 2 m, 5 m, 8 m, 10 m, m, 20 m, and any value within a range formed by any two of these values, and preferably, from 1 m to 10 m.

[0037] In some embodiments of the present disclosure, preferably, the average particle size D.sub.50(F) of the negative thermal expansion material ranges from 0.1 m to 10 m, e.g., 0.1 m, 0.5 m, 1 m, 2 m, 3 m, 5 m, 10 m, and any value within a range formed by any two of these values, and preferably, from 0.1 m to 3 m.

[0038] In some embodiments of the present disclosure, preferably, the cathode material is a lithium-containing layered compound.

[0039] In the present disclosure, a wide selection range is available for the type of the cathode material. Preferably, the cathode material has a composition represented by Formula I: Li.sub.1+Ni.sub.xCo.sub.yMn.sub.zM.sub.mM.sub.nO.sub.2(I), where 0.50.4, 0<x<1, 0y<1, 0z<1, 0m0.1, 0n0.1, x+y+z+m+n=1, and M and M are each independently selected from at least one element of Al, Y, Ti, Zr, V, Nb, Ta, Cr, Mo, W, La, Ce, Er, Mg, Sr, Ba, P, or B.

[0040] In some specific embodiments of the present disclosure, in the Formula I, -0.50.4, e.g., 0.5, 0.2, 0.1, 0, 0.02, 0.03, 0.05, 0.1, 0.2, 0.4, and any value within a range formed by any two of these values, and preferably, 00.1.

[0041] In some specific embodiments of the present disclosure, in the Formula I, 0<x<1, e.g., 0.2, 0.5, 0.6, 0.7, 0.8, 0.83, 0.9, 0.95, and any value within a range formed by any two of these values, and preferably, 0.6x0.9.

[0042] In some specific embodiments of the present disclosure, in the Formula I, 0y<1, e.g., 0, 0.01, 0.05, 0.1, 0.11, 0.15, 0.2, 0.3, 0.4, and any value within a range formed by any two of these values, and preferably, 0.01y0.2.

[0043] In some specific embodiments of the present disclosure, in the Formula I, 0z<1, e.g., 0, 0.01, 0.05, 0.08, 0.1, 0.15, 0.2, 0.25, 0.3, 0.4, and any value within a range formed by any two of these values, and preferably, 0.01z0.3.

[0044] In some specific embodiments of the present disclosure, in the Formula I, 0m0.1, e.g., 0, 0.001, 0.002, 0.005, 0.01, 0.018, 0.05, 0.06, 0.08, 0.1, and any value within a range formed by any two of these values; 0n0.1, e.g., 0, 0.001, 0.002, 0.005, 0.01, 0.018, 0.05, 0.06, 0.08, 0.1, and any value within a range formed by any two of these values; preferably, 0.001m+n0.1, e.g., 0.001, 0.006, 0.01, 0.02, 0.05, 0.06, 0.08, 0.09, 0.1, and any value within a range formed by any two of these values.

[0045] In some specific embodiments of the present disclosure, in the Formula I, M and M are each independently selected from at least one element of Al, Y, Ti, Zr, V, Nb, Ta, Cr, Mo, W, La, Ce, Er, Mg, Sr, Ba, P, or B; preferably, M and M are different elements; more preferably, M is selected from at least one element of Al, Y, Ti, Zr, La, Sr, or B, and M is selected from at least one element of Nb, Mo, W, or P.

[0046] In a specific embodiment of the present disclosure, the cathode material includes, but is not limited to, Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2, Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2, Li.sub.1.03Ni.sub.0.6Co.sub.0.1Mn.sub.0.3O.sub.2, Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05Al.sub.0.018W.sub.0.002O.sub.2, Li.sub.1.03Ni.sub.0.83Co.sub.0.104Mn.sub.0.06Zr.sub.0.005Nb.sub.0.001O.sub.2, and the like.

[0047] In some embodiments of the present disclosure, preferably, the negative thermal expansion material has a composition represented by Formula II: Q.sub.aQ.sub.bO.sub.c (II), where a, b, and c are each independently selected from a natural number from 1 to 15, Q and Q are each independently selected from at least one element of Zr, W, Hf, Al, Sc, In, Y, Mo, V, Sn, Ti, or P, and Q and Q are different elements.

[0048] In some embodiments of the present disclosure, more preferably, the negative thermal expansion material is selected from at least one of tungstates, molybdates, vanadates, or pyrophosphates.

[0049] In a specific embodiment of the present disclosure, when the negative thermal expansion material is selected from the tungstates, the tungstates include, but are not limited to, ZrW.sub.2O.sub.8, HfW.sub.2O.sub.8, Al.sub.2W.sub.3O.sub.12, Sc.sub.2W.sub.3O.sub.12, In.sub.2W.sub.3O.sub.12, Y.sub.2W.sub.3O.sub.12, and the like.

[0050] In a specific embodiment of the present disclosure, when the negative thermal expansion material is selected from the molybdates, the molybdates include, but are not limited to, ZrMo.sub.2O.sub.8, HfMo.sub.2O.sub.8, and the like.

[0051] In a specific embodiment of the present disclosure, when the negative thermal expansion material is selected from the vanadates, the vanadates include, but are not limited to, ZrV.sub.2O.sub.7, HfV.sub.2O.sub.7, SnV.sub.2O.sub.7, TiV.sub.2O.sub.7, and the like.

[0052] In a specific embodiment of the present disclosure, when the negative thermal expansion material is selected from the pyrophosphates, the pyrophosphates include, but are not limited to, ZrP.sub.2O.sub.7, HfP.sub.2O.sub.7, SnP.sub.2O.sub.7, TiP.sub.2O.sub.7, and the like.

[0053] In some embodiments of the present disclosure, preferably, the cathode active material layer has a thickness ranging from 20 m to 85 m, e.g., 20 m, 25 m, 30 m, 40 m, 50 m, 60 m, 75 m, 85 m, and any value within a range formed by any two of these values, and preferably, from 25 m to 60 m.

[0054] In the present disclosure, for the cathode sheet, the thickness of the cathode active material layer is related to a characteristic and weight of the coated active material and a pressure for roller pressing. The active material refers to a mixture formed by the cathode material, the negative thermal expansion material, the conductive agent, and the binder. A high coating weight of the active material, low compaction performance of the cathode sheet, and a low pressure for the roller pressing during processing result in a thicker active material layer, which lengthens a charge transport path, adversely affecting charge transport, and causing increased impedance. Thus, a pronounced thermal effect occurs during charging and discharging, which negatively impacts cycling performance.

[0055] In the present disclosure, to achieve optimal electrical performance of the cathode sheet, when the negative thermal expansion material is present in the cathode sheet, matching the areal density of the cathode sheet is also necessary. When the areal density of the cathode sheet is low, a content of the cathode material is relatively low, heat generation is low, and processability of the cathode sheet is unsatisfactory. Thus, a content of the negative thermal expansion material in the cathode sheet needs to be reduced to match the thermal expansion of the cathode active material layer in the cathode sheet. Conversely, when the areal density of the cathode sheet is high, the content of the cathode material is high, leading to high heat generation. Therefore, during the processing, the crystal structure of the negative thermal expansion material in the cathode sheet needs to be preserved intact, and a greater amount of negative thermal expansion material is required to counteract the volume expansion of the sheet during charging and discharging.

[0056] In some embodiments of the present disclosure, preferably, based on a total weight of the cathode active material layer, a content of the cathode material ranges from 85.5 wt % to 94.52 wt %, and preferably, from 90 wt % to 94.5 wt %; and a content of the negative thermal expansion material ranges from 0.48 wt % to 9.5 wt %, and preferably, from 0.5 wt % to 5 wt %.

[0057] In some embodiments of the present disclosure, more preferably, based on a total weight of the cathode active material layer, a content of the conductive agent ranges from 2 wt % to 4 wt %, and preferably, from 2.5 wt % to 3.5 wt %; and a content of the binder ranges from 1 wt % to 3 wt %, and preferably, from 1.5 wt % to 2.5 wt %.

[0058] In the present disclosure, the conductive agent includes, but is not limited to, acetylene black, carbon fiber, carbon nanotubes, graphite, Ketjen black, and the like, and the binder includes, but is not limited to, PVDF and the like.

[0059] The cathode sheet provided by the present disclosure features a low internal resistance. Impedance testing performed on the cathode sheet shows that the cathode sheet has an initial discharge impedance value R(d), satisfying R(d)20, and preferably, R(d)18.

[0060] In a second aspect of the present disclosure, a method for preparing a cathode sheet is provided. The method includes: (1) mixing a cathode material, a negative thermal expansion material, a conductive agent, a binder, and a solvent to obtain a cathode slurry; and (2) coating the cathode slurry on a surface of a cathode current collector, and performing drying and roller pressing sequentially, to load a cathode active material layer on the surface of the cathode current collector for obtaining the cathode sheet. The cathode material is a lithium-containing layered compound. The negative thermal expansion material has a composition represented by Formula II: Q.sub.aQ.sub.bO.sub.c (II), where a, b, and c are each independently selected from a natural number from 1 to 15, Q and Q are each independently selected from at least one element of Zr, W, Hf, Al, Sc, In, Y, Mo, V, Sn, Ti, or P, and Q and Q are different elements.

[0061] In some embodiments of the present disclosure, preferably, in the step (1), the cathode material, the negative thermal expansion material, the conductive agent, and the binder are mixed at a mass ratio of (85.5 to 94.52):(0.48 to 9.5):(2 to 4):(1 to 3), and preferably, (90 to 94.5):(0.5 to 5):(2.5 to 3.5):(1.5 to 2.5).

[0062] In some embodiments of the present disclosure, preferably, in the step (1), the cathode material has a composition represented by Formula I: Li.sub.1+Ni.sub.xCo.sub.yMn.sub.zM.sub.mM.sub.nO.sub.2 (I), where 0.50.4, 0<x<1, 0y<1, 0z<1, 0m0.1, 0n0.1, x+y+z+m+n=1, and M and M are each independently selected from at least one element of Al, Y, Ti, Zr, V, Nb, Ta, Cr, Mo, W, La, Ce, Er, Mg, Sr, Ba, P, or B.

[0063] In some embodiments of the present disclosure, preferably, in the Formula I, 00.1, 0.6x0.9, 0.01y0.2, 0.01z0.3, m and n are not both zero, and 0.001m+n0.1.

[0064] In some embodiments of the present disclosure, preferably, in the Formula I, M and Mare different elements, and more preferably, in the Formula I, M is selected from at least one element of Al, Y, Ti, Zr, La, Sr, or B, and M is selected from at least one element of Nb, Mo, W, or P.

[0065] In some embodiments of the present disclosure, preferably, in the step (1), the negative thermal expansion material has an average particle size D.sub.50(F) satisfying: D.sub.50(F)0.42D.sub.50, where D.sub.50 represents an average particle size of the cathode material, in the unit of m. More preferably, the cathode material has an average particle size D.sub.50 ranging from 1 m to 20 m, and preferably, from 1 m to 10 m. The average particle size D.sub.50(F) of the negative thermal expansion material ranges from 0.1 m to 10 m, and preferably, from 0.1 m to 3 m.

[0066] In the present disclosure, in the step (1), the solvent is intended merely to enable uniform mixing of the cathode material, the negative thermal expansion material, the conductive agent, and the binder. The solvent includes, but is not limited to, NMP, methanol, ethanol, etc.

[0067] In some embodiments of the present disclosure, preferably, in the step (1), said mixing is performed under the conditions of: a temperature ranging from 15 C. to 40 C., and preferably, from 20 C. to 30 C.; a duration ranging from 10 min to 120 min, and preferably, from 20 min to 60 min; and a rotational speed ranging from 500 rpm to 2,000 rpm, and preferably, from 800 rpm to 1,500 rpm.

[0068] In some embodiments of the present disclosure, preferably, a solid content of the cathode slurry ranges from 40 wt % to 60 wt %.

[0069] In the present disclosure, in the step (2), the coating is intended to uniformly coat the cathode slurry on the surface of the cathode current collector to form a cathode slurry coating layer, and the drying is intended to remove the solvent from the cathode slurry coating layer to form the cathode active material layer. Preferably, the drying is performed at a temperature ranging from 80 C. to 150 C., and preferably, from 120 C. to 150 C.

[0070] In some embodiments of the present disclosure, preferably, a pressure P for the roller pressing ranges from 5 T to 20 T. In the present disclosure, the roller pressing operation is generally carried out using a roller pressing machine. A roller pressing product is cut to obtain the cathode sheet.

[0071] With the method for preparing the cathode sheet provided by the present disclosure, the negative thermal expansion material is blended and incorporated into interstices between particles of the cathode material, which can balance the volume expansion of the material during charging and discharging, improving the cycling stability of the sheet. Specifically, by controlling the type, addition amount, and D.sub.50 of the cathode material, the type, addition amount, and D.sub.50(F) of the negative thermal expansion material, and the pressure P for the roller pressing, the characteristic value J of the cathode sheet is regulated. In this way, the cathode sheet possesses low volume expansion, high structural stability, and high-temperature stability.

[0072] In a third aspect of the present disclosure, a lithium-ion battery is provided. The lithium-ion battery includes the cathode sheet in the first aspect, or the cathode sheet prepared by the method in the second aspect.

[0073] In a specific embodiment of the present disclosure, the lithium-ion battery includes the cathode sheet provided by the present disclosure, an anode sheet, a separator disposed between the cathode sheet and the anode sheet, and an electrolyte.

[0074] Compared with the related art, the present disclosure has the following advantages.

[0075] (1) The cathode sheet provided by the present disclosure incorporates the negative thermal expansion material and is configured with the specific characteristic value J, which achieves satisfactory rate capability and capacity utilization while ensuring unrestricted lithium-ion transport from a bulk to a surface of the cathode material in the cathode active material layer. In addition, due to a combination of the negative thermal expansion material and the cathode material, the expansion of the cathode sheet during cycling is suppressed, which avoids an impact of the expansion of the cathode sheet on electrical performance, enhancing structural stability, thermal stability, and cycle life of the cathode sheet, and improving safety of the battery.

[0076] (2) In the cathode sheet provided by the present disclosure, the negative thermal expansion material with a specific content is added, which not only has almost no effect on a discharge capacity, but also contributes to high rate capability to some extent, for a reason that a volume thermal expansion effect of the cathode material under high-rate and high-current conditions can be partially offset by a volume contraction of the negative thermal expansion material.

[0077] (3) The method provided by the present disclosure offers advantages such as simple process, green and pollution-free preparation process, and low production costs, facilitating large-scale industrial production.

[0078] (4) Applying the cathode sheet provided by the present disclosure in the lithium-ion battery can effectively improve electrochemical performance of the lithium-ion battery, especially in terms of capacity performance, rate capability, and cycling performance.

[0079] The present disclosure will be described in detail below through examples.

[0080] Process parameters for preparing the cathode sheets in Examples and Comparative Examples, and physical property parameters of the prepared cathode sheets, are all listed in Table 1.

Example 1

[0081] (1) The cathode material (Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2, D.sub.50=3.5 m), the negative thermal expansion material (ZrW.sub.2O.sub.8, D.sub.50(F)=0.4 m), the conductive agent (acetylene black), the binder (PVDF), and the solvent (NMP) were mixed (at a temperature of 25 C. and a rotation speed of 1,000 rpm for 40 min) to obtain the cathode slurry with the solid content of 40 wt %.

[0082] The above cathode material, negative thermal expansion material, conductive agent, and binder were mixed at the mass ratio of 91.2:3.8:3:2.

[0083] (2) The above cathode slurry was coated on a surface of the aluminum foil serving as the cathode current collector to form the cathode slurry coating layer on the surface of the aluminum foil. After drying at 135 C., roller pressing was performed using the roller pressing machine (at a pressure of 15 T) to form the cathode active material layer on the surface of the aluminum foil, obtaining cathode sheet S1.

[0084] The XRD pattern of the above cathode sheet S1 is illustrated in FIG. 1. FIG. 1 reveals that, the above cathode material has the (003) characteristic peak at 2=18 and the (101) characteristic peak at 2=37, and the main peak (F) of the above negative thermal expansion material is located between the (003) characteristic peak and the (101) characteristic peak of the cathode material.

Example 2 to Example 6

[0085] Example 2 to Example 6 adopted the method of Example 1. Example 2 to Example 6 differed from Example 1 in that: in the step (1), the mass ratio of the above cathode material, negative thermal expansion material, conductive agent, and binder was adjusted based on data in Table 1, and all other conditions remained identical. In this way, cathode sheets S2 to S6 were obtained.

Example 7 to Example 11

[0086] Example 7 to Example 11 adopted the method of Example 1. Example 7 to Example 11 differed from Example 1 in that: in the step (1), the type and D.sub.50 of the above cathode material, the type and D.sub.50(F) of the negative thermal expansion material, and the mass ratio of the above cathode material, negative thermal expansion material, conductive agent, and binder were adjusted based on the data in Table 1, and in the step (2), the pressure for the roller pressing was adjusted based on the data in Table 1; and all other conditions remained identical. In this way, cathode sheets S7 to S11 were obtained.

Example 12

[0087] Example 12 adopted the method of Example 1. Example 12 differed from Example 1 in that: in the step (1), the type and D.sub.50 of the above cathode material, and the mass ratio of the above cathode material, negative thermal expansion material, conductive agent, and binder were adjusted based on the data in Table 1, and in the step (2), the pressure for the roller pressing was adjusted based on the data in Table 1; and all other conditions remained identical. In this way, cathode sheet S12 was obtained.

Example 13

[0088] Example 13 adopted the method of Example 12. Example 13 differed from Example 12 in that: in the step (1), D.sub.50(F) of the above negative thermal expansion material was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet S13 was obtained.

Example 14

[0089] Example 14 adopted the method of Example 1. Example 14 differed from Example 1 in that: in the step (1), the type of the above cathode material was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet S14 was obtained.

Example 15

[0090] Example 15 adopted the method of Example 14. Example 15 differed from Example 14 in that: in the step (2), the pressure for the roller pressing was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet S15 was obtained.

Example 16

[0091] Example 16 adopted the method of Example 14. Example 16 differed from Example 14 in that: in the step (1), the type of the above negative thermal expansion material was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet S16 was obtained.

Example 17

[0092] Example 17 adopted the method of Example 7. Example 17 differed from Example 7 in that: the type of the above cathode material was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet S17 was obtained.

Comparative Example 1

[0093] Comparative Example adopted the method of Example 1. Comparative Example 1 differed from Example 1 in that: in the step (1), the mass ratio of the above cathode material, negative thermal expansion material, conductive agent, and binder was adjusted based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet DS1 was obtained.

Comparative Example 2

[0094] Comparative Example 2 adopted the method of Example 1. Comparative Example 2 differed from Example 1 in that: in the step (1), D.sub.50(F) of the above negative thermal expansion material was adjusted based on the data in Table 1, resulting in D.sub.50(F)>0.42D.sub.50, and all other conditions remained identical. In this way, cathode sheet DS2 was obtained.

Comparative Example 3

[0095] Comparative Example 3 adopted the method of Example 1. Comparative Example 3 differed from Example 1 in that: in the step (2), the pressure for the roller pressing was replaced with 4 T based on the data in Table 1, and all other conditions remained identical. In this way, cathode sheet DS3 was obtained.

TABLE-US-00001 TABLE 1 Negative thermal Cathode material expansion material D.sub.50, D.sub.50(F), D.sub.50(F) Type m Type m 0.42D.sub.50 Mass ratio* Example 1 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 91.2:3.8:3:2 Example 2 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 90.2:4.8:3:2 Example 3 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 92.1:2.9:3:2 Example 4 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 93.1:1.9:3:2 Example 5 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 94.1:0.9:3:2 Example 6 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 94.3:0.7:3:2 Example 7 Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2 10 Al.sub.2W.sub.3O.sub.12 0.4 92.1:2.9:3:2 Example 8 Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2 10 Al.sub.2W.sub.3O.sub.12 1 92.1:2.9:3:2 Example 9 Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2 10 ZrV.sub.2O.sub.7 2 92.1:2.9:3:2 Example 10 Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2 10 ZrMo.sub.2O.sub.8 3 92.1:2.9:3:2 Example 11 Li.sub.1.03Ni.sub.0.83Co.sub.0.11Mn.sub.0.06O.sub.2 10 TiP.sub.2O.sub.7 4 87.5:7.5:3:2 Example 12 Li.sub.1.03Ni.sub.0.6Co.sub.0.1Mn.sub.0.3O.sub.2 4 ZrW.sub.2O.sub.8 0.4 90.3:4.7:3:2 Example 13 Li.sub.1.03Ni.sub.0.6Co.sub.0.1Mn.sub.0.3O.sub.2 4 ZrW.sub.2O.sub.8 0.8 90.3:4.7:3:2 Example 14 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.03Al.sub.0.018W.sub.0.002O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 91.2:3.8:3:2 Example 15 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.03Al.sub.0.018W.sub.0.002O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 91.2:3.8:3:2 Example 16 Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.03Al.sub.0.018W.sub.0.002O.sub.2 3.5 Fe[Co(CN).sub.6] 0.4 91.2:3.8:3:2 Example 17 Li.sub.1.03Ni.sub.0.83Co.sub.0.104Mn.sub.0.06Zr.sub.0.005Nb.sub.0.001O.sub.2 10 Al.sub.2W.sub.3O.sub.12 0.4 92.1:2.9:3:2 Comparative Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 94.9.0.1:3:2 Example 1 Comparative Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 2 X 91.2:3.8:3:2 Example 2 Comparative Li.sub.1.02Ni.sub.0.9Co.sub.0.05Mn.sub.0.05O.sub.2 3.5 ZrW.sub.2O.sub.8 0.4 91.2:3.8:3:2 Example 3 Note: indicates that D.sub.50(F) of the negative thermal expansion material is 0.42D.sub.50; otherwise, X is marked; *mass ratio of the cathode material, the negative thermal expansion material, the conductive agent, and the binder. Cathode active material layer Mixing, Roller Cathode Negative thermal C. Drying, pressing, Thickness, material, expansion rpm min C. T m wt % material, wt % Example 1 25 1000 40 135 15 35 91.2 3.8 Example 2 25 1000 40 135 15 35 90.2 4.8 Example 3 25 1000 40 135 15 35 92.1 2.9 Example 4 25 1000 40 135 15 35 93.1 1.9 Example 5 25 1000 40 135 15 45 94.1 0.9 Example 6 25 1000 40 135 15 35 94.3 0.7 Example 7 25 1000 40 135 12 35 92.1 2.9 Example 8 25 1000 40 135 10 40 92.1 2.9 Example 9 25 1000 40 135 10 55 92.1 2.9 Example 10 25 1000 40 135 12 45 92.1 2.9 Example 11 25 1000 40 135 10 63 87.5 7.5 Example 12 25 1000 40 135 18 33 90.3 4.7 Example 13 25 1000 40 135 18 27 90.3 4.7 Example 14 25 1000 40 135 15 35 91.2 3.8 Example 15 25 1000 40 135 18 20 91.2 3.8 Example 16 25 1000 40 135 15 39 91.2 3.8 Example 17 25 1000 40 135 12 40 92.1 2.9 Comparative 25 1000 40 135 15 35 94.9 0.1 Example 1 Comparative 25 1000 40 135 15 35 91.2 3.8 Example 2 Comparative 25 1000 40 135 4 88 91.2 3.8 Example 3 Cathode sheet Peak intensity Areal density , Characteristic Initial discharge ratio R(F) mg/cm.sup.2 value J impedance R(d), Example 1 0.035 12 0.0029 16.8 Example 2 0.048 12 0.0040 17.1 Example 3 0.018 12 0.0015 16.5 Example 4 0.024 16 0.0015 16.3 Example 5 0.012 12 0.0010 17.3 Example 6 0.0081 8 0.0010 17.3 Example 7 0.028 12 0.0023 15.9 Example 8 0.035 14 0.0025 16.2 Example 9 0.03 16 0.0019 16.5 Example10 0.028 12 0.0023 16.3 Example 11 0.082 20 0.0041 17.8 Example 12 0.048 12 0.0040 17.6 Example 13 0.036 10 0.0036 17.5 Example 14 0.039 13 0.0030 16.9 Example 15 0.008 8 0.0010 18.9 Example 16 0.033 12 0.0028 18.6 Example 17 0.038 14 0.0027 16.3 Comparative 0.0048 12 0.0004 20.4 Example 1 Comparative 0.0049 7 0.0007 20.1 Example 2 Comparative 0.0018 30 0.0001 21.5 Example 3 Note: peak intensity ratio R(F) = I(F)/I(003), i.e., the ratio of the peak intensity of the main peak (F) of the negative thermal expansion material to the peak intensity of the (003) characteristic peak of the cathode material; characteristic value J = R(F)/.

Test Examples

[0096] The cathode sheets prepared in the above Examples and Comparative Examples were evaluated using 2025-type coin cells. An assembly process was specifically as follows.

[0097] Cell assembly: in an argon-filled glove box with both a water content and an oxygen content below 5 ppm, the above cathode sheet, a separator, an anode sheet, and an electrolyte were assembled into a 2025-type coin cell, which was then let stand for 6 hours. The anode sheet was a lithium metal sheet having a diameter of 16 mm and a thickness of 0.5 mm. The separator was a 25 m-thick porous polyethylene membrane (Celgard 2325). The electrolyte was an equimolar mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) containing 1 mol/L LiPF.sub.6.

[0098] Electrochemical performance of the 2025-type coin cells assembled from the above Examples and Comparative Examples was tested using a Shenzhen Neware battery testing system. All test results are listed in Table 1 and Table 2.

[0099] (1) Initial impedance test method: the coin cell was subjected to capacity conditioning at 25 C. and 0.1 C (when a nickel content in the cathode material of the cathode sheet was >80 mol %, a charge/discharge current density for 0.1 C during testing was 20 mA/g; when the nickel content in the cathode material of the cathode sheet was <80 mol %, the charge/discharge current density for 0.1 C during the testing was 18 mA/g). After the capacity conditioning, the coin cell rested for 10 minutes, was charged to 4.35 V at a constant current of 0.33 C and constant voltage, and then rested for another 10 minutes. Subsequently, the coin cell was discharged to 3.0 V at a constant current of 0.33 C, followed by another 10-minute rest. The cell after the capacity conditioning was recharged and re-discharged to 50% Depth Of Discharge (DOD), rested for 3 minutes, and then discharged at a constant current of 1 C for 18 seconds. A voltage and a current before and after the discharge process were recorded to calculate the impedance value.

[0100] (2) First-cycle charge/discharge specific capacity and first-cycle charge/discharge efficiency at 0.1 C test: at 25 C., the coin cell was subjected to charge/discharge testing at 0.1 C. When the nickel content in the cathode material of the cathode sheet was >80 mol %, the charge/discharge current density for 0.1 C during the testing was 20 mA/g, and a charge/discharge voltage was controlled to range from 3.0 V to 4.3 V. When the nickel content in the cathode material of the cathode sheet was <80 mol %, the charge/discharge current density for 0.1 C during the testing was 18 mA/g, and the charge/discharge voltage was controlled to range from 3.0 V to 4.4 V.

[0101] (3) Cycling performance test: with the charge/discharge voltage controlled to range from 3.0 V to 4.3 V, the coin cell was subjected to 2 charge-discharge cycles at 0.1 C and then 80 charge-discharge cycles at 1 C, all under a constant temperature of 45 C.

[0102] (4) Rate capability test: with the charge/discharge voltage controlled to range from 3.0 V to 4.3 V, at 25 C., the coin cell was subjected to 2 charge-discharge cycles at 0.1 C, followed by one cycle each at 0.2 C, 0.33 C, 0.5 C, 1 C, and 2 C. The rate capability of the multi-element cathode material was evaluated based on a ratio of a first-cycle discharge specific capacity at 0.1 C to a discharge specific capacity at 2 C. The first-cycle discharge specific capacity at 0.1 C corresponds to a 1-st cycle of the coin cell, and the specific discharge capacity at 2 C corresponds to a 7-th cycle of the coin cell.

TABLE-US-00002 TABLE 2 First-cycle discharge Discharge specific First-cycle specific capacity discharge capacity 2.0 C/ Cycle at 0.1 C, efficiency, at 2 C, 0.1 C, retention mAh/g % mAh/g % rate, % Example 1 213.9 90.8 192.4 89.9 92.1 Example 2 213.5 90.1 192.3 90.1 92.3 Example 3 215.1 90.5 191.7 89.1 91.2 Example 4 214.9 90.5 191.9 89.3 91.0 Example 5 215.4 90.0 191.8 89.0 90.8 Example 6 216.0 89.8 190.5 88.2 89.3 Example 7 207.3 93.2 193.0 93.1 91.5 Example 8 207.6 92.9 192.6 92.8 91.6 Example 9 207.5 93.1 190.9 92.0 91.2 Example 10 206.8 92.8 192.8 93.2 91.3 Example 11 201.9 91.2 188.6 93.4 92.0 Example 12 192.9 90.8 171.9 89.1 95.4 Example 13 193.2 90.6 172.1 89.1 95.5 Example 14 214.2 90.9 192.4 90.2 92.9 Example 15 213.5 90.9 191.9 89.9 90.3 Example 16 211.9 89.8 186.5 88.0 89.3 Example 17 207.1 91.8 192.1 92.8 92.0 Comparative 213.3 90.6 184.8 86.6 85.1 Example 1 Comparative 212.5 90.0 186.4 87.7 86.0 Example 2 Comparative 211.1 88.8 182.3 86.4 84.9 Example 3

[0103] Data in Table 1 and Table 2 reveal that, compared with Comparative Example 1 to Comparative Example 3, Example 1 to Example 17 achieved cathode sheets whose peak intensity ratio R(F), areal density , and characteristic value J fall within preferred ranges by controlling the type and D.sub.50 of the cathode material, the type and D.sub.50(F) of the negative thermal expansion material, the mass ratio between the cathode material and the negative thermal expansion material, and the pressure for the roller pressing. Thus, the layered active material in the cathode sheet can be ensured to exhibit excellent electrical performance, with satisfactory lithium-ion deintercalation ability and high rate capability for the capacity. In addition, adding the negative thermal expansion material to the sheet can counteract the volume expansion occurring during charging and discharging of the sheet, which reduces the volume expansion of the sheet during charging and discharging, avoiding an adverse effect of the volume expansion of the sheet on battery performance. Thus, the battery can be ensured to have satisfactory cycling performance. As a result, the battery has comprehensive performance characterized by high capacity, satisfactory rate capability, and long cycle life.

[0104] In Comparative Example 1, the amount of negative thermal expansion material used was relatively low, which resulted in a lower R(F) value of the cathode sheet, and a relatively high areal density of the cathode sheet that led to a correspondingly lower characteristic value J. Thus, a proportion of the negative thermal expansion material capable of exerting a negative thermal expansion effect in the cathode sheet was too low to sufficiently counteract a volume change of the cathode material during charging and discharging. The relatively high areal density led to increased internal resistance of the battery, reducing the discharge specific capacity, and affecting the rate capability and the cycle life. Moreover, during charging and discharging, cathode particles had relatively significant volume expansion and thermal effect, which deteriorates the cycling performance of the sheet.

[0105] In Comparative Example 2, D.sub.50(F) of the negative thermal expansion material used was excessively large, causing a mismatch between the negative thermal expansion material and the cathode material. Consequently, the R(F) value of the sheet was also relatively low. Although the areal density of the sheet was moderate, the corresponding characteristic value J of the sheet was relatively low. This indicated that although a predetermined amount of negative thermal expansion material was added during sheet preparation, the mismatch between the negative thermal expansion material and the cathode material prevented the negative thermal expansion material and the cathode material from functioning synergistically after the sheet was prepared. As a result, the capacity utilization of the sheet was reduced. Further, the negative thermal expansion material failed to counteract the thermal effect, impairing the rate capability and the cycling performance.

[0106] In Comparative Example 3, the sheet obtained after the processing had a relatively large thickness and a relatively high areal density, causing the value of J to deviate from an optimal range. Thus, the negative thermal expansion material in the active layer of the cathode material was unable to fully exert its counteracting effect during cycling, leading to inferior sheet performance.

[0107] Example 1 to Example 13 demonstrate electrical performance of sheets fabricated using a preferred design. Example 1 to Example 13 indicate that, for different combinations of the cathode material and the negative thermal expansion material, batteries assembled from sheets meeting characteristic value requirements of the sheets exhibited satisfactory rate capability and satisfactory cycling performance. In Example 11, the relatively high amount of the negative thermal expansion material added caused the characteristic value J of the sheet to deviate somewhat from the preferred range, resulting in a predetermined degree of reduction in the electrical performance.

[0108] Example 14, Example 15, and Example 17 employed preferred cathode materials in the cathode sheet. By utilizing ternary cathode materials modified with elements M and M, inherent stability of the cathode material was enhanced. Further, by controlling processing conditions, the resulting cathode sheets met the characteristic value requirements of the sheets, improving the cycling performance. In Example 16, a non-preferred negative thermal expansion material was used, which causes the characteristic value J of the sheet to deviate from the preferred range, reducing the rate capability and the cycling performance of the sheet.

[0109] While preferred implementations of the present disclosure have been described in detail above, the present disclosure is not limited in this regard. A variety of simple variants of the technical solutions of the present disclosure can be made within technical concepts of the present disclosure, including combinations of individual technical features in any other suitable manner. Such simple variants and combinations shall also be construed as disclosed in the present disclosure and fall within the protection scope of the present disclosure.