ADDITIVE MANUFACTURING ANTIBACTERIAL COMPOSITE MATERIAL AND APPLICATION AND PREPARATION PROCESS THEREOF

Abstract

The present disclosure relates to antibacterial composite materials made by additive manufacturing (AM), and application and preparation process thereof.

Claims

1. An additive manufacturing antibacterial composite material, comprising: (a) a substrate, made of a substrate metal or alloy comprising at least one metal selected from the group consisting of titanium (Ti), zirconium (Zr), iron (Fe), cobalt (Co), copper (Cu) and magnesium (Mg); (b) an inorganic carrier, comprising a material selected from the group consisting of phosphates of an alkali earth metal(s) or a metal of Group 4 (IVB), carbonates of an alkali earth metal(s), sulfates of an alkali earth metal(s), zeolites, bentonites, diatomaceous earth, bioglass and any mixtures thereof; (c) an antibacterial metal, which is in elemental or ionic form and selected from the group consisting of silver (Ag), copper (Cu), zine (Zn), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), nickel (Ni), tantalum (Ta) and any mixtures thereof in non-alloy form; wherein the antibacterial metal is loaded within the inorganic carrier, and the inorganic carrier is presented within or embedded in the substrate metal or alloy.

2. The composite material according to claim 1, wherein the weight ratio of the antibacterial metal to the inorganic carrier is no greater than 0.03.

3. The composite material according to claim 1, wherein the antibacterial metal is presented within the inorganic carrier.

4. The composite material according to claim 1, wherein the substrate is porous.

5. The composite material according to claim 1, wherein the antibacterial metal in an ionic form is loaded in the inorganic carrier in the absence of ionic bonding between the antibacterial metal and the inorganic carrier.

6. The composite material according to claim 1, wherein the antibacterial metal in an ionic form is formed in situ during the additive manufacturing process.

7. The composite material according to claim 1, wherein the antibacterial metal is presented in an amount of at least 0.005 wt. % (50 ppm), based on the total weight of the composite material.

8. The composite material according to claim 1, wherein the antibacterial metal in combination with the inorganic carrier are presented in an amount of at least 0.1 wt. %, based on the total weight of the composite material.

9. The composite material according to claim 1, wherein relative density of the composite material to the components (a), (b) and (c) is at least 20%.

10. The composite material according to claim 1, wherein the substrate is made of Ti, Ti alloys (e.g., Ti-6Al-4V, Ti6242, etc.), Zr, Zr alloys (ZrCuAlNb, ZrCuNiAlTi, ZrCuNiAlNb), stainless steel, Co alloys (e.g., CoCrMo, CoCrW, etc.).

11. The composite material according to claim 1, wherein the inorganic carrier does not exhibit or provide an antibacterial effect.

12. A method of preparing an implant component, comprising a step of applying the composite material according to claim 1 to form a part of or the entirety of an implant component.

13. The method according to claim 12, wherein the implant component is a part of or the entirety of an artificial joint, an insert associated with an artificial joint, or a temporary anchorage device cosmetic implants such as facial implants, cranioplasty plates; cardiovascular implants such as pacemakers, stents, and artificial heart valves; or dental implants.

14. A process of preparing an additive manufacturing antibacterial composite material, the composite material comprising: (a) a substrate, made of a substrate metal or alloy comprising at least one metal selected from the group consisting of titanium (Ti), zirconium (Zr), iron (Fe), cobalt (Co), copper (Cu) and magnesium; (b) an inorganic carrier, comprising a material selected from the group consisting of phosphates of an alkali earth metal(s) or a metal of Group 4 (IVB), carbonates of an alkali earth metal(s), sulfates of an alkali earth metal(s), zeolites, bentonites, diatomaceous earth, bioglass and any mixtures thereof; (c) an antibacterial metal, which is in elemental or ionic form and selected from the group consisting of silver (Ag), copper (Cu), zine (Zn), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), nickel (Ni), tantalum (Ta) and any mixtures thereof in non-alloy form; the method comprising: (i) providing particles of the substrate metal or the substrate alloy, particles of the inorganic carrier and particles of the antibacterial metal; (ii) conducting powder bed fusion on the particles by selectively melting designated areas of the particles and fusing the particles into a solid layer; and (iii) repeating steps (i) and (ii) to build the additive manufacturing antibacterial composite material, layer-by-layer according to a digital design, such that the antibacterial metal is loaded within the inorganic carrier, and the inorganic carrier is presented within or embedded in the substrate metal or alloy.

15. The process according to claim 14, wherein the antibacterial metal in an ionic form is formed in situ during the additive manufacturing process.

16. The process according to claim 14, wherein the period of the materials (a), (b) and (c) being presented in a molten form and the period of the materials (a), (b) and (c) being presented in a solid form is controlled to reduce the oxidation of these materials.

17. The process according to claim 14, wherein the inorganic carrier does not exhibit or provide an antibacterial effect.

18. The process according to claim 14, wherein the additive manufacturing is conducted with powder bed fusion.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0032] In order to facilitate the understanding of the disclosure herein, terms as used herein are hereby defined as follows.

[0033] In the context of the specification and the claims, the singular forms a, an and the include plural referents, unless specifically indicated otherwise. Unless otherwise stated, any and all examples or exemplary language (e.g., such as) provided herein are merely used for better illustration of the present disclosure, instead of limiting the scope of the present disclosure.

[0034] It is to be understood that any numerical range recited in this specification is intended to include all sub-ranges encompassed therein. For example, a range from 50 to 70 C. includes all sub-ranges and specific values between the stated minimum value of 50 C. and the stated maximum value of 70 C., inclusive, e.g., from 58 C. to 67 C., and from 53 C. to 62 C., 60 C. or 68 C. Since the numerical ranges disclosed are continuous, they contain each numerical value between the minimum and maximum value. Unless otherwise specified, the various numerical ranges indicated in this specification are approximate.

[0035] In the present disclosure, the term about refers to an acceptable deviation of a given value measured by a person of ordinary skill in the art, depending, in part, on how to measure or determine the value.

[0036] In the present disclosure, the term alkali earth metal(s) refers to the elements of Group 2 in the periodic table.

[0037] In the present disclosure, the term zeolite(s) refers to microporous, crystalline aluminosilicate materials, which may be expressed by a general formula M.sup.n+.sub.1/n(AlO.sub.2).sup.(SiO.sub.2).sub.x.Math.yH.sub.2O, wherein M.sup.n+.sub.1/n is either a metal ion or H.sup.+, preferably M is H, Na or K.

[0038] In the present disclosure, the term bentonite(s) refers to a clay mainly consisting of montmorillonite (sheet silicates).

[0039] In the present disclosure, the term diatomaceous earth refers to a naturally occurring, soft, siliceous sedimentary rock, which mainly consists of the fossilized remains of diatoms; the chemical constitution mainly includes about 80 to 90% silica, with about 2 to 4% alumina and about 0.5 to 2% iron oxide.

[0040] In the present disclosure, the terms bioglass and bioactive glass may be interchangeable and refer to surface reactive glass-ceramic biomaterials, which are considered biocompatible to human, and the chemical constitution mainly includes silicate, calcium oxide, sodium oxide and/or phosphorous pentoxide, and optionally other metal oxides such as potassium oxide, magnesium oxide, etc.

[0041] In the present disclosure, the term biocompatible or biocompatibility means having an ability to be in contact with a living system without producing an adverse effect, e.g., (severe) allergic response, damage to cells, tissues or organs in a living body, etc.

[0042] In the present disclosure, the term antibacterial metal refers to those metals or metal ions exhibiting antibacterial effects.

[0043] In the present disclosure, the term porosity refers to the level of pore space in a material.

[0044] In the present disclosure, the relative density has a specific meaning under the context of 3D printing and powder metallurgy, and it refers to the ratio of the actual density of a material to its theoretical maximum density. To determine the relative density of a metal sample, the following steps are typically involved: (a) the sample is sanded with abrasive paper (from 80 to 4,000) and polished using 0.05 um Al.sub.2O.sub.3; (b) a high-resolution micrograph of the sample is captured using Hitachi TM4000Plus; (c) the captured image is analyzed using ImageJ software; by carefully selecting appropriate threshold values, the pores within the microstructure can be accurately identified; (d) the built-in functions of ImageJ are utilized to determine the total black area within the micrograph, which corresponds to the porosity of the sample; and the relative density is calculated using the formula:

[00001]$\mathrm{Relative}\mathrm{Density}=1-\mathrm{Porosity}.$

[0045] A common cause of infection in implant surgery is abundant reproduction of bacteria adhering to the surface of the implant. Resulting severe complications can require additional surgery or removal of the implant, leading to surgical failure and increasing patient difficulty. To reduce bacterial reproduction, imparting antibacterial properties to implants has become an important medical issue.

[0046] Antibacterial materials can be organic or inorganic. The former is prone to microbial and poor heat resistance, so more attention and application have been devoted to inorganic antibacterial materials. Commonly, metal ions are adsorbed into the surface of bacterial cell walls to react with the functional groups thereof, affecting the structure or function of microbial cells and achieving bacteriostatic effect.

[0047] Currently, antibacterial metal ions can attach to the surface via electroplating, ion implantation, chemical deposition, or coating to form an antibacterial layer. However, shortcomings still need be overcome. For example, porous support or structure may be immersed into hydrogels comprising organic bioactive agents such as antibiotics and the hydrogels can be fixed on the support or structure. However, hydrogels, when being placed in organisms, are influenced by various environmental factors, such as temperature, pH, enzymes, etc., making them prone to degradation or denaturation and affecting the release effectiveness of antibiotics. Another approach is to anodize a bioactive substrate such as titanium alloy to form a layer of TiO.sub.2, e.g., in the form of nanotubes, with the treated substrate immersed in an antibacterial metal-containing solution (e.g., silver ions) to allow the metal ions to attach and form an antibacterial surface. However, since the surface treatment gives an oxide layer, under the influence of loading and friction, the limited bonding strength between the oxide layer and the metal body, or the impact of material brittleness may cause the antibacterial layer to peel off or fracture, resulting in premature loss of antibacterial effectiveness. Direct addition/mixing of the antibacterial metal (e.g., copper) and metal substrate, followed by an anodizing treatment and high-temperature nitridization may provide an antibacterial alloy substrate having a porous structure on the surface and the antibacterial metal ions can be released to exhibit an antibacterial effect. Nevertheless, the antibacterial metals in alloys do not possess ionic bonds or polarity, resulting in a weaker ability to release ions in an aqueous solution (e.g., biological conditions), and thus may reduce the antimicrobial effectiveness.

[0048] The present disclosure thus provides additive manufacturing antibacterial composite materials, applications thereof, and manufacturing process of the same to overcome these problems.

Additive Manufacturing Antibacterial Composite Materials

[0049] The additive manufacturing antibacterial composite material comprises (a) a substrate of metal or alloy, (b) an inorganic carrier, and (c) an antibacterial metal, wherein the antibacterial metal is loaded within the inorganic carrier presented within or embedded in the substrate metal or alloy. Details of the components and structure are as follows.

(a) Substrate Metal or Alloy

[0050] The antibacterial composite materials in the present disclosure are prepared via additive manufacturing (AM). Various metal and non-metal materials can be used in AM processes, and those being biocompatible are used herein, in particular, metals such as titanium (Ti), zirconium (Zr), iron (Fe), cobalt (Co), copper (Cu), magnesium (Mg) or alloys thereof. Preferably, Ti, Ti alloys (e.g., Ti-6Al-4V, Ti6242, etc.), Zr alloys (e.g., ZrCuAlNb, ZrCuNiAlTi, ZrCuNiAlNb), stainless steel, Co alloys (e.g., CoCrMo, CoCrW, etc.) are used.

[0051] Without being bound to theory, the substrate metals or alloys are not alloyed with the antibacterial metal used herein, or are alloyed at a minimum or trace level, to avoid hindering the release of the antibacterial metal.

(b) Inorganic Carriers

[0052] In the present disclosure, the inorganic carrier is used for carrying (loading) the antibacterial materials and presented in the substrate metal or alloy and/or embedded in the substrate metal or alloy. The inorganic carrier can also prevent or hinder oxidation/reduction reaction or alloy between the antibacterial metal and the substrate metal/alloy. In addition, the inorganic carrier is advantageous in the release of antibacterial metal over existing antibacterial composite materials of implants. For example, in one embodiment, the antibacterial metal in an ionic form is loaded in the inorganic carrier in the absence of ionic bonding between the antibacterial metal and the inorganic carrier. In any preceding embodiments, the antibacterial metal in an ionic form is loaded in the inorganic carrier via electrostatic force. In another embodiment, the inorganic carrier is presented within the substrate metal or alloy. In yet another embodiment, the inorganic carrier is presented within and embedded in the substrate metal or alloy.

[0053] In particular, phosphates of an alkali earth metal or a metal of Group 4 (IVB), carbonates of an alkali earth metal, sulfates of an alkali earth metal(s) or an alkali metal(s), zeolites, bentonites, diatomaceous earth, bioglass and any mixture thereof, can be used as the inorganic carrier herein.

[0054] Examples of phosphates include, but are not limited to, apatites (e.g., hydroxy-/chloro-/fluoro-apatites) or pure phosphates (e.g., those without hydroxy/chloro/flouro in the crystals). Examples of alkali earth metal(s) include, but are not limited to, magnesium (Mg) and calcium (Ca), preferably Ca. The metal of Group 4 (IVB) is preferably zirconium (Zr). Examples of phosphates of an alkali earth metal(s) or a metal of Group 4 (IVB) include, but are not limited to, calcium phosphate, calcium hydroxyapatite, or zirconium phosphate.

[0055] Examples of carbonates of an alkali earth metal include, but are not limited to, calcium carbonate.

[0056] Examples of sulfates of an alkali earth metal(s) or an alkali metal(s), include, but are not limited to, sodium sulfate, potassium sulfate, magnesium sulfate and calcium sulfate, preferably calcium sulfate.

[0057] Examples of zeolites include, but are not limited to, LTA (Linde Type A), MOR-type, HEU-type and ANA-typ.

[0058] Examples of bentonites include, but are not limited to, Na-montmorillonite and Ca-montmorillonite.

[0059] Examples of bioglass include, but are not limited to, Bioglass 45S5 or derivative forms of Bioglass 45S5, e.g., having different CaO/P.sub.2O.sub.5 ratios.

[0060] In one embodiment, the inorganic carriers are presented in an amount of no greater than 1.0 wt. %, e.g., no greater than 0.8 wt. %, no greater than 0.6 wt. %, no greater than 0.5 wt. %, no greater than 0.4 wt. %, no greater than 0.3 wt. %, based on the total weight of the composite material.

(c) Antibacterial Metals

[0061] Antibacterial metals exhibit strong inhibition of adhesion and growth and/or proliferation of bacteria. In the present disclosure, antibacterial metals are in elemental or ionic, rather than alloy, form.

[0062] Examples of antibacterial metal include, but are not limited to, silver (Ag), copper (Cu), zine (Zn), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), nickel (Ni), tantalum (Ta), and ionic form(s) thereof, preferably Ag, Cu, Zn, Co and ionic form(s) thereof, and any mixtures thereof in non-alloy form.

[0063] In one embodiment, the antibacterial metal is at least presented in an amount to exhibit the antibacterial effect, e.g., of at least 0.005 wt. % (50 ppm), e.g., at least 0.01 wt. % (100 ppm), at least 0.1 wt. %, at least 0.2 wt. %, at least 0.3 wt. %, at least 0.4 wt. %, at least 0.5 wt. %, at least 0.75 wt. %, at least 1 wt. %, at least 2 wt. %, at least 3 wt. %, at least 4 wt. %, at least 5 wt. %, based on the total weight of the composite material.

[0064] In one embodiment, the antibacterial metal in an ionic form is formed in situ during the additive manufacturing process. In one embodiment, the antibacterial metal in an ionic form is released under specific conditions, e.g., biological conditions.

[0065] In one embodiment, the antibacterial metal in combination with the inorganic carrier is presented in an amount of at least 0.1 wt. %, e.g., at least 0.2 wt. %, at least 0.3 wt. %, at least 0.4 wt. %, at least 0.5 wt. %, at least 1 wt. %, at least 2 wt. %, at least 3 wt. %, at least 3.5 wt. %, at least 4 wt. %, at least 5 wt. %, at least 7.5 wt. %, based on the total weight of the composite material.

[0066] In one embodiment, the weight ratio of the antibacterial metal to the inorganic carrier is no greater than 0.03, e.g., no greater than 0.025, no greater than 0.02, no greater than 0.019, no greater than 0.018, or no greater than 0.015. Without being bound to theory, this weight ration may reflect the efficacy or limitation of protection of the inorganic carrier.

[0067] In one embodiment, the antibacterial metal comprises less than 0.05 molar %, preferably less than 0.025 molar % of its oxide form. Without being bound to theory, the release of an oxide form of the antibacterial metal may be slower than that of the antibacterial metal in an elemental form or in an ionic form, in particular under certain specific conditions.

[0068] In one embodiment, relative density of the composite material to the components (a), (b) and (c) is at least 20%.

[0069] The antibacterial composite materials are prepared via additive manufacturing processes and details are described herein.

[0070] In one embodiment, the component (b) is in an amount of 0.05 wt. % to 0.3 wt. % and the component (c) is in an amount of 0.005 wt. % (50 ppm) to 0.015 wt. % (150 ppm), based on the total weight of the composite material. In any previous embodiment, the component (c) is silver. In any preceding embodiment, the component (b) is bioglass. In any preceding embodiment, the component (a) is titanium or titanium alloy.

Additive Manufacturing Processes for Manufacturing Antibacterial Composite Materials

[0071] Traditional powder metallurgy, metal injection molding (MIM), binder jetting, and material extrusion modeling (MEX) can all be used to manufacture metal and non-metal composites. The common feature of these processes is the use of a binder (usually organic) to preform the powder, followed by debinding at high temperatures to remove the binder, and then sintering the metal particles together while retaining the non-metal in the metal substrate. Nevertheless, the sintering process is typically more complex and the finished product usually has lower relative density (e.g., 85 to 93%) than additive manufacturing products, resulting in decreased mechanical strength.

[0072] Hence, the present disclosure provides a method of preparing an additive manufacturing antibacterial composite material, the composite material comprising: [0073] (a) a substrate of a substrate metal or alloy comprising at least one metal selected from the group consisting of titanium (Ti), zirconium (Zr), iron (Fe), cobalt (Co), copper (Cu) and magnesium (Mg), [0074] (b) an inorganic carrier comprising a material selected from the group consisting of phosphates of an alkali earth metal(s) or a metal of Group 4 (IVB), carbonates of an alkali earth metal(s), sulfates of an alkali earth metal(s), zeolites, bentonites, diatomaceous earth, bioglass and any mixtures thereof, or; [0075] (c) an antibacterial metal in elemental or ionic form and selected from the group consisting of silver (Ag), copper (Cu), zine (Zn), cobalt (Co), chromium (Cr), iron (Fe), manganese (Mn), nickel (Ni), tantalum (Ta) and any mixtures thereof in non-alloy form; and

[0076] The method comprises: [0077] (i) providing particles of the substrate metal or the substrate alloy, particles of the inorganic carrier and particles of the antibacterial metal; [0078] (ii) conducting powder bed fusion on the particles by selectively melting designated areas of the particles and fusing the particles into a solid layer, and [0079] (iii) repeating steps (i) and (ii) to build the additive manufacturing antibacterial composite material, layer-by-layer according to a digital design; such that the antibacterial metal is loaded within the inorganic carrier, and the inorganic carrier is presented within or embedded in the substrate metal or alloy.

[0080] In one embodiment, step (i) includes ball milling of the particles. In a specific embodiment, the ball milling process comprising (1) sequentially charging a ball mill chamber with the inorganic carrier, substrate metal or alloy powder, and grinding media, (2) rotating the chamber at a controlled speed for a designated period to achieve intimate contact between materials through collisions and shearing, and (3) discharging the homogenized mixture upon reaching the predetermined level of uniformity. In one embodiment, step (i) includes spreading a thin layer of the (fresh) particles on a platform.

[0081] In one embodiment, the period of the materials (a), (b) and (c) being presented in a molten form and (a), (b) and (c) being presented in a solid form is controlled to reduce oxidation thereof. Without being bound to theory, controlling the periods of melting/solidification during the process prevents or reduces oxidation-reduction between the inorganic carrier, antibacterial metal, and metal substrate. This allows the inorganic carrier and antibacterial metal to be retained and evenly dispersed within the metal substrate, and even when the composite material is subjected to wear during use, antibacterial properties can still be maintained.

[0082] In addition, additive manufacturing processes may provide metal substrates having high specific surface area and porous structures, which lead to increase in the release of metal ions, and the processes can be adjusted to modify or improve the mechanical strength of the product. Last but not least, additive manufacturing processes may reduce tedious post-processing and minimize the risk of bacterial contamination during transfer.

[0083] In one embodiment, the antibacterial metal in an ionic form is formed in situ during the additive manufacturing process, in particular during melting.

[0084] In one embodiment, the inorganic carrier does not exhibit or provide an antibacterial effect.

[0085] In one embodiment, the additive manufacturing is conducted with laser powder bed fusion.

[0086] In the additive manufacturing process, one or more of the following process parameters can adopted or adjusted: [0087] (1) laser power of 1 W to 300 W, e.g., 5 W to 15 W, 10 W to 250 W, 15 W to 35 W, 50 W to 75 W, about 100 W, 40 W to 180 W, 25 W to 275 W, about 150 W, 60 W to 90 W, 80 W to 200 W, 120 W to 130 W, 20 W to 30 W, 175 W to 225 W, or any single point or a reasonable numeric range constituted by above-mentioned point values, e.g., 275 W to 300 W, 30 W to 80 W, etc.; [0088] (2) scanning rate of 3 m/s or less, e.g., 2.5 m/s or less, 2 m/s or less, 1 m/s or less; [0089] (3) scanning strategy selected from the group consisting of chess, stripes, contour and meander; [0090] (4) pre-heated temperature of a platform in additive manufacturing: 50 C. to 200 C., e.g., about 175 C., 65 C. to 70 C., 60 C. to 120 C., 55 C. to 100 C., about 150 C., 80 C. to 130 C., or any single point or a reasonable numeric range constituted by above-mentioned point values, e.g., 120 C. to 130 C., about 80 C., etc.; [0091] (5) thickness of each layer: 20 m to 100 m, e.g., about 25 m, about 50 m, about 75 m, 30 m to 40 m, 80 m to 90 m, 35 m to 60 m, or any single point or a reasonable numeric range constituted by above-mentioned point values, e.g., 40 m to 50 m, about 80 m, etc.; [0092] (6) oxygen content (v/v): 0.05% to 3% (v/v) of the total volume in the build chamber, e.g., about 0.5%, about 1.5%, about 0.15%, 0.075% to 0.1%, less than 2.5%, 0.25% to 0.75%, less than 2%, or any single point or a reasonable numeric range constituted by above-mentioned point values; and [0093] (7) inert gas flow rate: 0.1 m/s to 3 m/s, e.g., about 1.75 m/s, 0.3 m/s to 0.5 m/s, 1.5 to 2.5 m/s, 1 m/s to 2 m/s, or any single point or a reasonable numeric range constituted by above-mentioned point values.

Applications of the Additive Manufacturing Antibacterial Composite Materials

[0094] The additive manufacturing antibacterial composite materials man be applied in an implant component, e.g., a part of or the entirety of an artificial joint, an insert associated with an artificial joint, or a temporary anchorage device; cosmetic implants such as facial implants, cranioplasty plates; cardiovascular implants such as pacemakers, stents, and artificial heart valves; or dental implants, etc.

[0095] Without being bound to theory, as noted herein, even when the implant component comprising the composite material is subjected to wear during use, antibacterial properties can be maintained and lifetime and durability of the implant component prolonged.

Examples

[0096] The following examples are provided to illustrate the present invention to those of ordinary skill in the art without limiting the scope thereof.

Materials, Methodologies and Test Models

[0097] Ti64 powders having particle size from 15 to 53 m (available from Shandong Lianhong new material Technology CO. LTD) were used. Silver-containing glass powders can be obtained from Ishizuka CO. LTD.

[0098] Porosity can be measured by Hitachi TM4000Plus.

[0099] Scanning electronic microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) were adopted for imaging and elemental analysis for positioning of the materials.

[0100] Antibacterial effect was evaluated by JIS Z 2801, and Staphylococcus aureus (strain BCRC 10451) was used. Mechanical properties were evaluated based on ASTM E8, including tensile strength, percentage of elongation, etc. Surface characteristics were evaluated by using ULVAC-PHI PHI 5000 Versaprobe II.

[0101] Additive manufacturing is conducted by using Trumpf lasers (e.g., Truprint 2000).

Example

[0102] Ti64 powders were used as the substrate metal/alloy; silver-containing glass powders loaded in an inorganic carrier were used as the antibacterial metal in combination with the inorganic carrier. The powders were mixed and used for additive manufacturing or being processed by arc melting under vacuum. Different proportions or level of the materials were used. The parameters are listed in Table 1 below:

TABLE-US-00001 TABLE 1 Antibacterial Inorganic metal (Ag) carrier level Processing Sample No. level (wt. %) manner Sample 1 15 ppm 0.3 PBF Sample 2 27 ppm 0.15 PBF Sample 3 36 ppm 0.2 PBF Sample 4 38 ppm 0.3 PBF Sample 5 48 ppm 0.3 PBF Sample 6 54 ppm 0.3 PBF Sample 7 90 ppm 0.5 PBF Sample 8 450 ppm 2.5 PBF Sample 9 54 ppm 0.3 Vacuum arc remelting Sample 10 0.2% 11 Vacuum arc remelting Sample 11 0.2% 11 PBF Control 0 0

[0103] The constitution of the powders (wt. %): P(2030), Al(210), Mg(15), Na(15), Si(0.11.0), Ag(15), remainder being O.

[0104] Characteristics of the products are summarized in Table 2 below:

TABLE-US-00002 TABLE 2 Sample No. Characteristics 1 2 3 4 5 6 Relative density 99.6 99.8 99.8 99.7 99.6 99.7 (%) Ultimate tensile 1320 1280 1315 1311 1379 1348 stress(MPa) Elongation (%) 3.4 6 4.6 3.3 3.5 3.5 Antibacterial 0 <90 76.56 62.85 96.37 efficacy (%) XPS Ag3d peak (eV) Sample No. Characteristics 7 8 9 10 11 Control Relative density 99.2 97.6 99.9 (%) Ultimate tensile 1388 1413 1240 stress(MPa) Elongation (%) 2.2 0.8 6.8 Antibacterial >99.0 <90.0 <90.0 0 efficacy (%) XPS Ag3d peak 367.0~ 367.0~ (eV) 369.0 369.0

[0105] In order to determine the dispersion of the antibacterial metal/inorganic carrier within the substrate, the sample was polished and ground and examined by SEM; samples at specific locations were selected and images were obtained. Through the contrast between light and dark zones, the distribution of the inorganic carrier can be preliminarily observed and confirmed.

[0106] Further analysis of the element distribution was conducted using EDS. Through the element distribution map, the position of the inorganic carrier and whether the antibacterial metal is retained in the inorganic carrier can be confirmed; homogeneity of the material can also be evaluated.

[0107] The invention exhibits superior effects over the existing objects, for example, providing sufficient antibacterial effects while maintaining comparable mechanical properties. Without being bond to the theory, in traditional metal forming processes, high-temperature metals have high reactivity, which may reduce the release of antibacterial metals in inorganic oxides through reduction or alloying. However, according to the subject disclosure, by optimizing the process parameters of powder bed laser, the reaction time of antibacterial metals with the metal substrate at high temperatures can be reduced, thereby reducing the reaction at high temperatures. The unalloyed antibacterial metals that are retained can be more easily released to the surface, achieving better antibacterial effects.

[0108] A person of ordinary skill in the art of the subject invention should understand that variations and modification may be made to the teaching and the disclosure of the subject invention without departing from the spirit and scope of the subject application. Based on the contents above, the subject application intends to cover any variations and modifications thereof with the proviso that the variations or modifications or their equivalents fall within the scope as defined in the appended claims.