SLURRY AND HUMID-HEAT-ATTENUATION-RESISTANT PHOTOVOLTAIC CELL

Abstract

A paste and a damp-heat (DH) attenuation resistant photovoltaic cell. The paste comprises a paste body, into which an inert metal element and an oxide thereof are added, so that a barrier layer having a certain thickness can be formed on the surface of an electrode after sintering, and the barrier layer can resist oxidation and corrosion so as to enhance the oxidation resistance and the acid corrosion resistance of the metallized electrode. The electrode of the photovoltaic cell is made of the paste, and the DH attenuation resistant photovoltaic cell made of the paste can reduce DH attenuation and power loss, and has the enhanced environmental protection property and reliability.

Claims

1. A paste, comprising a paste body, wherein the paste body includes an inert metal element and an oxide thereof.

2. The paste according to claim 1, wherein the paste body further includes a non-active rare-earth element fluoride.

3. The paste according to claim 1, wherein the paste body further includes a non-active rare-earth element.

4. The paste according to claim 1, wherein the inert metal element is at least one of a titanium element, a platinum element, or a gold element.

5. The paste according to claim 4, wherein a mass percentage of the inert metal element is in a range of 0.01% to 1%.

6. The paste according to claim 2, wherein the non-active rare-earth element fluoride is at least one of yttrium fluoride or lanthanum fluoride.

7. The paste according to claim 3, wherein the non-active rare-earth element is at least one of an yttrium element, a lanthanum element, or a cerium element.

8. The paste according to claim 7, wherein a mass percentage of the non-active rare-earth element is in a range of 0.01% to 1%.

9. A damp-heat (DH) attenuation resistant photovoltaic cell, wherein an electrode of the photovoltaic cell is made of a paste comprising a paste body, wherein the paste body includes an inert metal element and an oxide thereof.

10. The DH attenuation resistant photovoltaic cell according to claim 9, wherein the electrode of the photovoltaic cell comprises both a finger and a busbar, and both the finger and the busbar are made of the paste.

11. The DH attenuation resistant photovoltaic cell according to claim 9, wherein the paste body further includes a non-active rare-earth element fluoride.

12. The paste according to claim 5, wherein the inert metal element includes titanium element in a mass percentage range of 0.01% to 0.02%, and gold element in a mass percentage range of 0.005% to 0.015%.

13. The paste according to claim 8, wherein the non-active rare-earth element includes yttrium element in a mass percentage range of 0.005% to 0.01%, a lanthanum element in a mass percentage range of 0.005% to 0.01%, and a cerium element in a mass percentage range of 0.005% to 0.01%.

14. The DH attenuation resistant photovoltaic cell according to claim 1, wherein the paste body further includes a non-active rare-earth element.

15. The DH attenuation resistant photovoltaic cell according to claim 1, wherein the inert metal element is at least one of a titanium element, a platinum element, or a gold element.

16. The DH attenuation resistant photovoltaic cell according to claim 15, wherein a mass percentage of the inert metal element is in a range of 0.01% to 1%.

17. The DH attenuation resistant photovoltaic cell according to claim 11, wherein the non-active rare-earth element fluoride is at least one of yttrium fluoride or lanthanum fluoride.

18. The DH attenuation resistant photovoltaic cell according to claim 14, wherein the non-active rare-earth element is at least one of an yttrium element, a lanthanum element, or a cerium element.

19. The DH attenuation resistant photovoltaic cell according to claim 18, wherein a mass percentage of the non-active rare-earth element is in a range of 0.01% to 1%.

20. A method for preparing a photovoltaic cell, comprising: preparing a nano-powder material of inert metal and an oxide thereof and sieving; mixing a glass material and an organic or inorganic system to form an even paste; forming good ohmic contact through a sintering process; and preparing a photovoltaic cell, and testing acid resistance and oxidation resistance of an electrode.

Description

DRAWINGS

[0019] In order to better illustrate the technical solutions in the embodiments of the present disclosure or the related art, the accompanying drawings used in the description of the embodiments or the related art will be introduced below. It is apparent that, the accompanying drawings in the following description are only some embodiments of the present disclosure, and other drawings can be obtained by those of ordinary skill in the art from the provided drawings without creative efforts.

[0020] FIG. 1 is a schematic flowchart of implementation of a paste according to one or more embodiments of the present disclosure.

[0021] The drawings described herein are for illustration purposes only and are not intended to limit the scope of the present disclosure in any way.

DETAILED DESCRIPTION

[0022] The following description is merely exemplary in nature and is not intended to limit the present disclosure, application, or uses. It should be understood that throughout the drawings, corresponding reference numerals indicate like or corresponding parts and features.

[0023] The purpose of the present disclosure is to provide a paste and a DH attenuation resistant photovoltaic cell, which can enhance the oxidation resistance and the acid corrosion resistance of the metallized electrode, reduce DH attenuation and power loss, and thus enhance environmental protection property and reliability.

[0024] The technical solutions in the embodiments of the present disclosure will be described below with reference to the accompanying drawings in the embodiments of the present disclosure. It is appreciated that, the described embodiments are merely some of rather than all of the embodiments of the present disclosure. All other embodiments acquired by those skilled in the art without creative efforts based on the embodiments of the present disclosure shall fall within the protection scope of the present disclosure.

[0025] In some embodiments of the present disclosure, a paste is provided, including a paste body, into which an inert metal element and an oxide thereof are added. The inert metal used herein may be, but is not limited to, titanium, platinum, and gold. Taking titanium element as an example, after sintering, the titanium element reacts with a glass material in the paste to form a titanium oxide, so that a certain barrier layer is formed on the surface of the electrode, which can resist acid corrosion of silver and aluminum of the electrode. Titanium has good stability in acidic, alkaline, and neutral saline solutions and an oxidizing medium, and the titanium element is not easily corroded in low-concentration non-oxidizing acid. In addition to a single type of inert metal, a combination of two or more inert metals may also be used, which is not limited herein. Such inert metal elements and oxides thereof are more stable and may be sintered to form a barrier layer with a thickness between 2 microns and 5 microns on the surface of the electrode. A specific manufacturing process may be shown in FIG. 1. FIG. 1 is a schematic flowchart of implementation of a paste according to one or more embodiments of the present disclosure. The process includes the following steps.

[0026] In S1, a nano-powder material of inert metal and an oxide thereof is prepared and sieved.

[0027] Nanoparticles may have particle sizes between 15 nm and 40 nm, with excellent dispersion. Further, a preparation method for a nano-metallic material may be a physical method or a chemical method. The chemical method includes a chemical reduction method, a chemical precipitation method, a sol-gel method, a hydrothermal method, a template synthesis method, a solvothermal synthesis method, a high-temperature combustion synthesis method, an electrolysis method, and so on. The physical method is a high-energy ball milling method in some embodiments. A glass material and inorganic and organic additives can be mixed without delamination, with an advantage that an average particle size of the nanoparticles obtained is relatively small, the printing may not cause blockage to screen meshes, and printing requirements on a line width below 20 μm can be met.

[0028] In S2, a glass material and an organic or inorganic system are mixed to form an even paste.

[0029] In S3, good ohmic contact is formed by using a sintering process.

[0030] After sintering in this way, the inert metal and the oxide thereof can form a barrier layer on the surface of the electrode.

[0031] In S4, a photovoltaic cell is prepared, and acid resistance and oxidation resistance of an electrode are tested.

[0032] As can be known through the above descriptions, in the paste according to the present disclosure, an inert metal element and an oxide thereof are added into the paste body, so that a barrier layer having a certain thickness can be formed on the surface of an electrode after sintering, and the barrier layer can resist oxidation and corrosion, so as to enhance the oxidation resistance and the acid corrosion resistance of the metallized electrode.

[0033] In some embodiments of the paste, a non-active rare-earth element fluoride is further added into the paste body. The non-active rare-earth element fluoride has good acid corrosion resistance, thus reducing the corrosion of the electrode of the photovoltaic cell by acid.

[0034] In some embodiments of the paste, a non-active rare-earth element is further added into the paste body. The non-active rare-earth element may consume certain organic acid, for example, it can form complexes with citric acid, acetic acid, ammonia triacetic acid (NTA), and ethylenediamine tetraacetic acid (EDTA) to inhibit electrochemical corrosion within the electrode. Further, the non-active rare-earth element may be at least one of an yttrium element, a lanthanum element, and a cerium element. The yttrium element and the lanthanum element have good anti-sulfur and anti-oxidation effects, and can form complexes with the organic acid to reduce the corrosion of the silver-aluminum electrode by the organic acid, while the cerium element can reduce a corrosion rate of aluminum in a silver-aluminum paste, and one or more of the elements may be used, which is not limited herein.

[0035] In some embodiments of the paste, a mass percentage of the inert metal element may be in a range of 0.01% to 1%. In this case, the surface of the electrode can be protected with a lower dosage, thereby achieving the purpose of reducing the corrosion of the electrode on the basis of low costs.

[0036] In some embodiments of the paste, the non-active rare-earth element fluoride may be at least one of yttrium fluoride and lanthanum fluoride. Rare-earth fluoride and oxalate have low solubility in water and dilute inorganic acid.

[0037] In the above paste, a mass percentage of the non-active rare-earth element is in a range of 0.01% to 1%. The following solution may be adopted: the cerium element accounts for 0.005%, the yttrium element accounts for 0.002%, and the lanthanum element accounts for 0.005%.

[0038] In some embodiments of a DH attenuation resistant photovoltaic cell according to the present disclosure, an electrode of the photovoltaic cell is made of the paste according to the above embodiments. The finger of the photovoltaic cell may be made of the paste separately, or the busbar of the photovoltaic cell may be made of the paste separately, which is not limited herein. The electrode of the photovoltaic cell may also include both the finger and the busbar. In other words, the busbar and the finger of the photovoltaic cell are made of the paste at the same time. The DH attenuation resistant photovoltaic cell made of the paste can reduce DH attenuation and power loss, and achieve enhanced environmental protection property and reliability.

[0039] The above solutions and technical effects are described below with three detailed embodiments.

Embodiment 1

[0040] A titanium element with a mass percentage in a range of 0.02% to 0.05% was added to a metallized paste and sintered to form, along with a glass material in the metallized paste, a certain amount of titanium dioxide, which covers a surface of an electrode to form a protective layer, thereby preventing reduction of power of the photovoltaic module finally caused by partial loss of the electrode, increase of series resistance, and decrease of the filling factor due to corrosion of the silver element in the electrode by acidic substances produced by decomposition of polymer materials in materials of the photovoltaic module or long-term infiltration of oxygen.

Embodiment 2

[0041] In view of the situation that the infiltration of oxygen in the photovoltaic module and sulfide produced by decomposition of silica gel in a packaging material may cause the corrosion of silver in the paste and the loss of the electrode, 0.01% to 0.05% yttrium, lanthanum, and cerium by mass percentage were added into the metallized paste. After sintering, the rare-earth elements were diffused into the electrode and combined with silver or silver-aluminum to slow the corrosion caused by the oxygen and sulfur elements. It should be noted that the cerium element can reduce the corrosion of the aluminum element and better protect the electrode of the photovoltaic cell using a silver-aluminum paste.

Embodiment 3

[0042] Still in view of the situation that the infiltration of oxygen in the photovoltaic module and sulfide produced by decomposition of silica gel in a packaging material may cause the corrosion of silver in the paste and the loss of the electrode, the combination of an inert metal element and a rare-earth element was added into a metallized paste, including a titanium element with a mass percentage in a range of 0.01% to 0.02%, a gold element with a mass percentage in a range of 0.005% to 0.015%, rare-earth elements yttrium and lanthanum with mass percentages in a range of 0.005% to 0.01%, and a cerium element with a mass percentage in a range of 0.005% to 0.01%. Better usage effect may be brought by combining the above two manners.

[0043] No polyolefin elastomer (POE) material or EVA containing rare-earth elements was used as the packaging material of the photovoltaic module. DH attenuation data after different periods of time was shown in Table 1:

TABLE-US-00001 TABLE 1 DH1000 DH2000 DH4000 attenuation attenuation attenuation Basic solution 3.52% 4.78% 9.87% Embodiment 1 2.84% 3.75% 5.82% Embodiment 2 1.94% 3.16% 4.41% Embodiment 3 1.36% 2.74% 3.86%

[0044] The above data shows that, after the application of the paste according to the present application, amplitude of attenuation of the photovoltaic module after a DH process is reduced.

[0045] The above descriptions of the disclosed embodiments are provided to enable those skilled in the art to implement or use the present disclosure. Various modifications to these embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be implemented in other embodiments without departing from the scope of the present disclosure. Therefore, the present disclosure will not be limited to the embodiments shown herein, but is to conform to the broadest scope consistent with the principles and novel features disclosed herein.

[0046] Unless otherwise expressly indicated herein, all numerical values indicating mechanical/thermal properties, compositional percentages, dimensions and/or tolerances, or other characteristics are to be understood as modified by the word “about” or “approximately” in describing the scope of the present disclosure. This modification is desired for various reasons including industrial practice, material, manufacturing, and assembly tolerances, and testing capability.

[0047] As used herein, the phrase at least one of A, B, and C should be construed to mean a logical (A OR B OR C), using a non-exclusive logical OR, and should not be construed to mean “at least one of A, at least one of B, and at least one of C.”

[0048] The description of the disclosure is merely exemplary in nature and, thus, variations that do not depart from the substance of the disclosure are intended to be within the scope of the disclosure. Such variations are not to be regarded as a departure from the spirit and scope of the disclosure.