Magnesium-based raw material with low thermal conductivity and low thermal expansion and preparation method thereof

Abstract

The present disclosure relates to a magnesium-based raw material and a preparation method thereof. According to the technical solution, 40-60 wt % fused magnesia particles, 30-40 wt % fine monoclinic zirconia powder, 5-20 wt % fine zirconium oxychloride powder, 0.5-1.5 wt % calcium hydroxide nanopowder, 0.2-0.5 wt % calcium hydroxide nanopowder, and 0.1-0.3 wt % maleic acid are stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder is mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 250-400° C. for 0.5-3 h, and finally cooled to room temperature.

Claims

1. A method for preparing a magnesium-based raw material comprising: stirring 40-60 wt % fused magnesia particles, 30-40 wt % fine monoclinic zirconia powder, 5-20 wt % fine zirconium oxychloride powder, 0.5-2 wt % calcium hydroxide nanopowder, 0.2-0.5 wt % of fine light calcined magnesia powder, and 0.1-0.3 wt % maleic acid to mix well in a high-speed mixing mill at a constant temperature of 25° C. for 15 min to obtain a mixed powder; and mixing the mixed powder through a ball mill at a constant temperature of 25° C. for 3 min, roasting in a high temperature furnace at 250-400° C. for 0.5-3 h, and cooling to room temperature to form the magnesium-based raw material.

2. The method for preparing a magnesium-based raw material according to claim 1, wherein the fused magnesia particles is ≤1 mm in particle size, and MgO content in the fused magnesia particles is ≥96 wt %.

3. The method for preparing a magnesium-based raw material according to claim 1, wherein the fine monoclinic zirconia powder is ≤45 μm in particle size, and ZrO.sub.2 content in the fine monoclinic zirconia powder is ≥98 wt %.

4. The method for preparing a magnesium-based raw material according to claim 1, wherein the fine zirconium oxychloride powder is ≤45 μm in particle size.

5. The method for preparing a magnesium-based raw material according to claim 1, wherein the calcium hydroxide nanopowder has Ca(OH).sub.2 content of ≥98 wt % and a particle size of ≤0.1 μm.

6. The method for preparing a magnesium-based raw material according to claim 1, wherein the fine light calcined magnesia powder has MgO content of ≥95 wt % and a particle size of ≤45 μm.

Description

DETAILED DESCRIPTION OF THE EMBODIMENTS

(1) The present disclosure will be further described in detail below in combination with embodiments, without limiting the protection scope thereof.

(2) In order to avoid repetition, the materials involved in this DETAILED DESCRIPTION OF THE EMBODIMENTS are described in a unified manner as follows, which will not be repeated in the examples:

(3) The fused magnesia particles are ≤1 mm in particle size, and MgO content in the fused magnesia particles is ≥96 wt %.

(4) The fine monoclinic zirconia powder is ≤45 μm in particle size, and ZrO.sub.2 therein is ≥98 wt %.

(5) The fine zirconium oxychloride powder is ≤45 μm in particle size.

(6) The calcium hydroxide nanopowder has Ca(OH).sub.2 content of ≥98 wt % and a particle size of ≤0.1 μm.

(7) The fine light calcined magnesia powder has MgO content of ≥95 wt % and a particle size of ≤45 μm.

Example 1

(8) 40 wt % fused magnesia particles, 40 wt % fine monoclinic zirconia powder, 19 wt % fine zirconium oxychloride powder, 0.5 wt % calcium hydroxide nanopowder, 0.2 wt % fine light calcined magnesia powder, and 0.3 wt % maleic acid were stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder was mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 250° C. for 3 h, and cooled to room temperature to obtain a magnesium-based raw material with low thermal conductivity and low thermal expansion provided by the example.

Example 2

(9) 50 wt % fused magnesia particles, 35 wt % fine monoclinic zirconia powder, 13 wt % fine zirconium oxychloride powder, 1.4 wt % calcium hydroxide nanopowder, 0.5 wt % fine light calcined magnesia powder, and 0.1 wt % maleic acid were stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder was mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 400° C. for 0.5 h, and cooled to room temperature to obtain a magnesium-based raw material with low thermal conductivity and low thermal expansion provided by the example.

Example 3

(10) 60 wt % fused magnesia particles, 33 wt % fine monoclinic zirconia powder, 5 wt % fine zirconium oxychloride powder, 1.6 wt % calcium hydroxide nanopowder, 0.2 wt % fine light calcined magnesia powder, and 0.2 wt % maleic acid were stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder was mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 300° C. for 2.5 h, and cooled to room temperature to obtain a magnesium-based raw material with low thermal conductivity and low thermal expansion provided by the example.

Example 4

(11) 52 wt % fused magnesia particles, 40 wt % fine monoclinic zirconia powder, 5.2 wt % fine zirconium oxychloride powder, 2 wt % calcium hydroxide nanopowder, 0.5 wt % fine light calcined magnesia powder, and 0.3 wt % maleic acid were stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder was mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 350° C. for 2.5 h, and cooled to room temperature to obtain a magnesium-based raw material with low thermal conductivity and low thermal expansion provided by the example.

Example 5

(12) 45 wt % fused magnesia particles, 37 wt % fine monoclinic zirconia powder, 16 wt % fine zirconium oxychloride powder, 1.5 wt % calcium hydroxide nanopowder, 0.3 wt % fine light calcined magnesia powder, and 0.2 wt % maleic acid were stirred for 15 min to mix well in a high-speed mixing mill at a constant temperature of 25° C. to obtain a mixed powder; and the mixed powder was mixed through a ball mill at a constant temperature of 25° C. for 3 min, roasted in a high temperature furnace at 400° C. for 1.5 h, and cooled to room temperature to obtain a magnesium-based raw material with low thermal conductivity and low thermal expansion provided by the example.

Comparative Examples 1 to 5

(13) In Comparative Examples 1 to 5, the fused magnesia particles, fine monoclinic zirconia powder, fine zirconium oxychloride powder, calcium hydroxide nanopowder, fine light calcined magnesia powder, and maleic acid were subject to the weight ratio and process conditions in Table 1.

(14) TABLE-US-00001 TABLE 1 The ratio of raw materials in Comparative Examples 1 to 5 Comparative Comparative Comparative Comparative Comparative Example 1 Example 2 Example 3 Example 4 Example 5 Fused magnesia particles 75 20 10 65 35 Fine monoclinic zirconia 21 50 60 27 45 powder Fine zirconium 2 24 30 3 18 oxychloride powder Calcium hydroxide 0.2 4 0 4 0.1 nanopowder Fine light calcined 0.8 1 0 1 1.9 magnesia powder Maleic acid 1 1 0 0 0 Temperature (° C.) 300 250 300 350 400 Roasting time (h) 3 2.5 2 2 1.5

(15) TABLE-US-00002 TABLE 2 Comparison of performance indexes of raw materials in the examples of the present disclosure and Comparative Examples 1 to 5 Thermal conductivity Thermal expansion Solution (W/mk) .Math. (800° C.) coefficient (° C..sup.−1) Comparative Example 1 8.6 13.5 × 10.sup.−6 Comparative Example 2 8.8 13.8 × 10.sup.−6 Comparative Example 3 9.2 14.3 × 10.sup.−6 Comparative Example 4 9.0 14.2 × 10.sup.−6 Comparative Example 5 8.7 13.9 × 10.sup.−6 Example 1 5.8  9.8 × 10.sup.−6 Example 2 5.9  9.9 × 10.sup.−6 Example 3 6.0   10 × 10.sup.−6 Example 4 5.9  9.8 × 10.sup.−6 Example 5 6.0  9.8 × 10.sup.−6

(16) The comparison of performance indexes of magnesium-based raw materials in all examples of the present disclosure versus traditional magnesium-based raw materials is shown in Table 2. From Tables 1 and 2, 40-60 wt % fused magnesia particles, 30-40 wt % fine monoclinic zirconia powder, 5-20 wt % fine zirconium oxychloride powder, 0.5-2 wt % calcium hydroxide nanopowder, 0.2-0.5 wt % fine light calcined magnesia powder, and 0.1-0.3 wt % maleic acid are stirred to mix well in a high-speed mixing mill at a constant temperature of 25° C. for 15 min to obtain a mixed powder, and both thermal conductivity and thermal expansion coefficient of the raw material obtained finally are far lower than those of traditional magnesium-based raw materials. There are the following reasons. The present disclosure adopts a millimeter-micron-nano-sized particle composite system and a mixed milling and ball milling process. Combined with the pyrolysis of the fine zirconium oxychloride powder and calcium hydroxide nanopowder, the present disclosure may introduce and uniformly distribute micro-nano zirconia and calcium oxide (CaO) around the magnesia grain boundary. When the magnesium-based raw material is used at a high temperature, the phase change of zirconia and the stress generated by the reaction of zirconia with calcium oxide may promote the close contact of the micro-nano zirconia with the magnesia grain boundary, and in grain boundary impurities thereof, CaO may take priority over SiO.sub.2 to react with these active ZrO.sub.2 to form CaZrO.sub.3 at the grain boundary; an appropriate amount of nano-sized ZrO.sub.2 particles are coated with CaO with similar particle size and MgO micropowder with larger activity, hindering the aggregation reaction of the nano-sized ZrO.sub.2 particles with CaO impurities in the grain boundary, stabilizing the structure of the magnesia, and having a sustained-release effect; these intercrystalline CaZrO.sub.3 phases generated continuously may enhance the binding force of magnesia particles, effectively reduce the thermal conductivity and thermal expansion coefficient of the magnesia, and improve slag resistance.

(17) Therefore, the present disclosure has the characteristics of simple process and convenient industrial production; the prepared magnesium-based raw material with low thermal conductivity and low thermal expansion is characterized by relatively low thermal conductivity, low thermal expansion coefficient, excellent dispersibility, and strong resistance to slag penetration and erosion.

(18) The present disclosure has been described in detail above with reference to general descriptions and specific examples, but it will be apparent to those skilled in the art that some modifications or improvements can be made based on the present disclosure. Therefore, all these modifications or improvements made without departing from the spirit of the present disclosure fall within the scope of the present disclosure.