LATEX COMPOSITION

Abstract

Provided are chlorosulfonated polyethylene latex having excellent film-forming properties, and a molded article (e.g., a thin film article) that is produced from the latex and has excellent tensile strength.

Claims

1. A chlorosulfonated polyethylene latex composition comprising (A) chlorosulfonated polyethylene, (B) a vulcanization accelerator, and (C) a glycol ether.

2. The composition according to claim 1, wherein (B) is at least one member selected from the group consisting of aldehyde-ammonia-based vulcanization accelerators, aldehyde-amine-based vulcanization accelerators, thiourea-based vulcanization accelerators, guanidine-based vulcanization accelerators, thiazole-based vulcanization accelerators, sulfenamide-based vulcanization accelerators, thiuram-based vulcanization accelerators, dithiocarbamate-based vulcanization accelerators, and xanthate-based vulcanization accelerators.

3. The composition according to claim 1, wherein (C) is at least one member selected from the group consisting of methyl glycol, methyl diglycol, methyl triglycol, methyl polyglycol, isopropyl glycol, isopropyl diglycol, butyl glycol, butyl diglycol, butyl triglycol, isobutyl glycol, isobutyl diglycol, hexyl glycol, hexyl diglycol, 2-ethylhexyl glycol, 2-ethylhexyl diglycol, allyl glycol, phenyl glycol, phenyl diglycol, benzyl glycol, benzyl diglycol, methyl propylene glycol, methyl propylene diglycol, methyl propylene triglycol, propyl propylene glycol, propyl propylene diglycol, butyl propylene diglycol, butyl propylene triglycol, phenyl propylene glycol, methyl propylene glycol acetate, dimethyl glycol, dimethyl diglycol, dimethyl triglycol, methyl ethyl diglycol, diethyl diglycol, dibutyl diglycol, and dimethyl propylene diglycol.

4. The composition according to claim 1, wherein (B) is contained in an amount of 0.1 to 10 parts by mass per 100 parts by mass of (A).

5. The composition according to claim 1, wherein (C) is contained in an amount of 1 to 30 parts by mass per 100 parts by mass of (A).

6. The composition according to claim 1, wherein (B) is contained in an amount of 0.1 to 10 parts by mass per 100 parts by mass of (A), and (C) is contained in an amount of 1 to 30 parts by mass per 100 parts by mass of (A).

7. A molded product obtained from the composition of claim 1.

Description

DESCRIPTION OF EMBODIMENTS

[0018] Embodiments encompassed by the present disclosure are described in more detail below. The present disclosure preferably encompasses, for example, a chlorosulfonated polyethylene latex composition comprising specific components, and its applications; however, the present disclosure is not limited to these and encompasses everything disclosed herein and recognizable to those skilled in the art.

[0019] The chlorosulfonated polyethylene latex composition encompassed by the present disclosure comprises (A) chlorosulfonated polyethylene, (B) a vulcanization accelerator, and (C) a glycol ether. As used herein, the chlorosulfonated polyethylene latex composition encompassed by the present disclosure may be referred to as “the composition of the present disclosure.” Further, the chlorosulfonated polyethylene, vulcanization accelerator, and glycol ether may be referred to as “component (A),” “component (B),” and “component (C),” respectively.

[0020] Chlorosulfonated polyethylene is produced by chlorination and chlorosulfonation of polyethylene. In other words, chlorosulfonated polyethylene is referred to as “chlorinated and chlorosulfonated polyethylene.” Although no structural limitation is intended, chlorosulfonated polyethylene may be represented by, for example, the following structural formula. (This structural formula is used only for convenience to facilitate understanding. For example, the continuity of each repeating unit (i.e., whether the repeating units are continuously or randomly linked) is not specified.)

—(CH.sub.2—CH.sub.2).sub.1—(CH.sub.2—CH(SO.sub.2Cl)).sub.m—(CH.sub.2—CH(Cl)).sub.n—

[0021] For example, component (A) is not limited and is preferably chlorosulfonated polyethylene obtained by introducing about 20 to 45 parts by mass of chlorine and about 0.1 to 5 parts by mass of sulfur, per 100 parts by mass of polyethylene.

[0022] The upper or lower limit of the amount range of chlorine (20 to 45 parts by mass) may be, for example, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, or 44 parts by mass. For example, this range may be 21 to 44 parts by mass. The upper or lower limit of the amount range of sulfur (0.1 to 5 parts by mass) may be, for example, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9, 3, 3.1, 3.2, 3.3, 3.4, 3.5, 3.6, 3.7, 3.8, 3.9, 4, 4.1, 4.2, 4.3, 4.4, 4.5, 4.6, 4.7, 4.8, or 4.9 parts by mass. For example, this range may be 0.2 to 4 parts by mass.

[0023] Also, without such a limitation, chlorosulfonated polyethylene has both elastomer characteristics and vulcanization characteristics, and contains no double bonds in the main chain, according to the classification of the standard of the American Society for Testing and Materials (ASTM D1418). Therefore, chlorosulfonated polyethylene has excellent chemical resistance, weather resistance, ozone resistance, heat resistance, and the like.

[0024] The composition of the present disclosure is a chlorosulfonated polyethylene latex composition, and chlorosulfonated polyethylene latex is latex in which chlorosulfonated polyethylene is dispersed in water to form a colloidal state (for example, by optionally using an emulsifier). The concentration of the chlorosulfonated polyethylene latex in the composition of the present disclosure is preferably, for example, 30 to 60 mass %. The upper or lower limit of this range may be, for example, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, 55, 56, 57, 58, or 59 mass %. For example, this range may be 35 to 55 mass %.

[0025] The chlorosulfonated polyethylene latex for use in the composition of the present disclosure is not limited and may be those produced by known methods (see, for example, PTL 2) or may be purchased commercial products. Examples of the known methods include a method comprising stirring an organic solvent solution of chlorosulfonated polyethylene synthesized by chlorosulfonation of high-pressure-processed polyethylene with chlorine and sulfurous acid gas, and an aqueous surfactant solution with a high-pressure homogenizer or other mixer to produce an emulsion, and subjecting the resulting emulsion to solvent removal and concentration. Examples of the commercial products include Sepolex CSM produced by Sumitomo Seika Chemicals Co., Ltd.

[0026] Examples of vulcanization accelerators contained in the composition of the present disclosure include, but are not limited to, aldehyde-ammonia-based vulcanization accelerators, aldehyde-amine-based vulcanization accelerators, thiourea-based vulcanization accelerators, guanidine-based vulcanization accelerators, thiazole-based vulcanization accelerators, sulfenamide-based vulcanization accelerators, thiuram-based vulcanization accelerators, dithiocarbamate-based vulcanization accelerators, and xanthate-based vulcanization accelerators.

[0027] Examples of aldehyde-ammonia-based vulcanization accelerators include hexamethylenetetramine.

[0028] Examples of aldehyde-amine-based vulcanization accelerators include n-butyraldehyde aniline.

[0029] Examples of thiourea-based vulcanization accelerators include N,N′-diphenylthiourea, trimethylthiourea, N,N′-diethylthiourea, and N,N′-dibutylthiourea.

[0030] Examples of guanidine-based vulcanization accelerators include 1,3-diphenylguanidine, di-o-tolylguanidine, 1-o-tolylbiguanide, and a di-o-tolylguanidine salt of dicatecholborate.

[0031] Examples of thiazole-based vulcanization accelerators include 2-mercaptobenzothiazole, dibenzothiazyl disulfide, a zinc salt of 2-mercaptobenzothiazole, a cyclohexylamine salt of 2-mercaptobenzothiazole, a dicyclohexylamine salt of 2-mercaptobenzothiazole, 2-(N,N-diethylthiocarbamoylthio)benzothiazole, and 2-(4′-morpholinodithio)benzothiazole.

[0032] Examples of sulfenamide-based vulcanization accelerators include N-cyclohexyl-2-benzothiazolylsulfenamide, N-tert-butyl-2-benzothiazolylsulfenamide, N-oxydiethylene-2-benzothiazolylsulfenamide, and N,N-dicyclohexyl-2 benzothiazolylsulfenamide.

[0033] Examples of thiuram-based vulcanization accelerators include tetramethylthiuram disulfide, tetraethylthiuram disulfide, tetrabutylthiuram disulfide, tetrakis(2-ethylhexyl)thiuram disulfide, tetrabenzylthiuram disulfide, tetramethylthiuram monosulfide, and dipentamethylenethiuram tetrasulfide.

[0034] Examples of dithiocarbamate-based vulcanization accelerators include a pentamethylene dithiocarbamate piperidine salt, a pipecolyl dithiocarbamate pipecoline salt, zinc dimethyldithiocarbamate, zinc diethyldithiocarbamate, zinc dibutyldithiocarbamate, zinc N-ethyl-N-phenyldithiocarbamate, zinc N-pentamethylenedithiocarbamate, zinc dibenzyldithiocarbamate, sodium diethyldithiocarbamate, sodium dibutyldithiocarbamate, copper dimethyldithiocarbamate, ferric dimethyldithiocarbamate, and tellurium diethyldithiocarbamate.

[0035] Examples of xanthate-based vulcanization accelerators include zinc butyl xanthate and zinc isopropyl xanthate.

[0036] The vulcanization accelerators may be used alone or in a combination of two or more.

[0037] Examples of a method for incorporating the vulcanization accelerator into the composition of the present disclosure include a method comprising blending the vulcanization accelerator with chlorosulfonated polyethylene latex. The blending method is not limited. For example, the vulcanization accelerator may be blended directly. Alternatively, a vulcanization accelerator formed into an aqueous solution or aqueous dispersion may be blended.

[0038] The content of the vulcanization accelerator in the composition of the present disclosure is preferably 0.1 to 10 parts by mass, and more preferably 1 to 5 parts by mass, per 100 parts by mass of chlorosulfonated polyethylene in the composition. The upper or lower limit of this range (0.1 to 10 parts by mass) may be, for example, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2 .7, 2.8, 2.9, 3, 3.1, 3.2, 3.3, 3.4, 3.5, 3.6, 3.7, 3.8, 3.9, 4, 4.1, 4.2, 4.3, 4.4, 4.5, 4.6, 4.7, 4.8, 4.9, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, or 9.5 parts by mass. For example, the range may be 0.5 to 7.5 parts by mass.

[0039] Examples of the glycol ether contained in the composition of the present disclosure include, but are not limited to, methyl glycol, methyl diglycol, methyl triglycol, methyl polyglycol, isopropyl glycol, isopropyl diglycol, butyl glycol, butyl diglycol, butyl triglycol, isobutyl glycol, isobutyl diglycol, hexyl glycol, hexyl diglycol, 2-ethylhexyl glycol, 2-ethylhexyl diglycol, allyl glycol, phenyl glycol, phenyl diglycol, benzyl glycol, benzyl diglycol, methyl propylene glycol, methyl propylene diglycol, methyl propylene triglycol, propyl propylene glycol, propyl propylene diglycol, butyl propylene diglycol, butyl propylene triglycol, phenyl propylene glycol, methyl propylene glycol acetate, dimethyl glycol, dimethyl diglycol, dimethyl triglycol, methyl ethyl diglycol, diethyl diglycol, dibutyl diglycol, and dimethyl propylene diglycol. Of these, phenyl glycol, butyl triglycol, phenyl diglycol, methyl propylene triglycol, and the like are preferred. The glycol ethers may be used alone or in a combination of two or more.

[0040] The glycol ether contained in the composition of the present disclosure is preferably, for example, a compound represented by formula (I): R.sup.1—O—CH.sub.2—CH(R.sup.2)).sub.n—OH (I), wherein R.sup.1 is a linear or branched alkyl group having 1, 2, 3, 4, 5, or 6 carbon atoms or a phenyl group, R.sup.2 is a hydrogen atom or a linear or branched alkyl group having 1, 2, or 3 carbon atoms, and n is 1, 2, 3, 4, 5, or 6.

[0041] Examples of a method for incorporating the glycol ether into the composition of the present disclosure include a method comprising blending the glycol ether with chlorosulfonated polyethylene latex. The blending method is not limited. For example, the glycol ether may be blended directly. Alternatively, glycol ether formed into an aqueous solution or aqueous dispersion may be blended.

[0042] The content of the glycol ether in the composition of the present disclosure is preferably 1 to 30 parts by mass, and more preferably 5 to 20 parts by mass, per 100 parts by mass of chlorosulfonated polyethylene in the composition. The upper or lower limit of this range (1 to 30 parts by mass) may be, for example, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, or 29 parts by mass. For example, the range may be 2 to 29 parts by mass.

[0043] The composition of the present disclosure is a chlorosulfonated polyethylene latex composition, and is a composition in which fine particles of chlorosulfonated polyethylene are dispersed in an aqueous medium, as described above. The composition of the present disclosure thus also comprises an aqueous medium. The aqueous medium for use is preferably water and may be various types of water, such as tap water, industrial water, ion-exchanged water, deionized water, and pure water. Particularly preferred is deionized water or pure water.

[0044] In addition to components (A) to (C), the composition of the present disclosure may also comprise additional components as long as the above effects are not impaired. Examples of such components include thickeners, tackifiers, pH adjusters, plasticizers, film-forming aids, crosslinking agents, crosslinking aids, fillers, anti-aging agents, metal oxides, defoamers, and stabilizers. Surfactants (emulsifiers) may also be contained to aid dispersion. Latex other than chlorosulfonated polyethylene latex may also be contained. Examples of such latex include butadiene latex, butadiene-styrene copolymer latex, dicarboxylated butadiene-styrene copolymer latex, vinylpyridine-butadiene-styrene terpolymer latex, isoprene rubber latex, acrylonitrile-butadiene copolymer latex, hydrogenated acrylonitrile-butadiene copolymer latex, and polyolefin emulsion. The latex other than chlorosulfonated polyethylene latex may be used alone or in a combination of two or more.

[0045] Examples of methods for producing the composition of the present disclosure include a method comprising preparing chlorosulfonated polyethylene latex by a known method or a method obvious from a known method, and adding component (B) and component (C) (and optionally other components) thereto, followed by mixing. These components may be mixed in advance before being added or may be added individually in sequence to the chlorosulfonated polyethylene latex. These components may be added directly, or aqueous solutions or aqueous dispersions of these components may be prepared in advance and added.

[0046] By using the composition of the present disclosure, a molded product, such as a thin film article, can be formed by, for example, applying the composition of the present disclosure to the surface of a target coating object or the surface of a mold for a molded product, followed by drying.

[0047] The materials and shapes of the target coating object and the mold for a molded product in terms of the composition of the present disclosure are not limited. Examples of the materials include paper, glass, wood, various metals, cement, resins, and rubbers. Examples of the shapes include flat plates, spheres, human handprints, fibers, and woven fabrics.

[0048] The method for applying the composition of the present disclosure to the surface of a target coating object or the surface of a mold for a molded product is not limited. Examples include brush coating, spraying, bar coating, and dipping.

[0049] The drying method after the composition of the present disclosure is applied to the surface of a target coating object or the surface of a mold for a molded product is not limited. Examples include natural drying at room temperature, air drying, drying by heating, drying under reduced pressure, and freeze drying. From the standpoint of workability and time required for drying, drying by heating is preferred.

[0050] The temperature for drying by heating of the composition of the present disclosure is not limited as long as the water in the chlorosulfonated polyethylene latex contained in the chlorosulfonated polyethylene latex composition is volatilized. From the standpoint of workability and time required for drying, the temperature is preferably, for example, 20 to 200° C., and more preferably 70 to 150° C. The temperature for drying by heating may be constant or may be changed during the drying process. Alternatively, the drying may be performed while changing the drying temperature.

[0051] The time for drying by heating the composition of the present disclosure is not limited as long as the water in the chlorosulfonated polyethylene latex contained in the chlorosulfonated polyethylene latex composition is volatilized. From the standpoint of workability and the time required for drying, the time is preferably 5 minutes to 24 hours, and more preferably 1 hour to 12 hours.

[0052] Additionally, for example, a molded product of a second layer may be provided on the molded product of the first layer formed by the method described above.

[0053] The composition of the present disclosure is particularly suitable for, for example, paints and outdoor coatings, and for preparing thin film articles.

[0054] The term “comprise” or “contain” as used herein includes the meanings of consisting essentially of and consisting of. Further, the present disclosure includes any combination of the constituent requirements described in the present specification.

[0055] In addition, the various characteristics (properties, structures, functions, etc.) described in each embodiment of the present disclosure described above may be combined in any way in specifying the subjects encompassed by the present disclosure. In other words, the present disclosure encompasses all the subjects comprising all combinations of the combinable characteristics described in the present specification.

EXAMPLES

[0056] The embodiments of the present disclosure are more specifically explained below with reference to Examples; however, the embodiments are not limited to the Examples below.

Evaluation Method

[0057] Each measurement was performed according to the following methods.

(1) Film-Forming Properties

[0058] Chlorosulfonated polyethylene latex compositions were produced under the conditions described in each Example and each Comparative Example, and molded articles were formed according to the following process. The thus-obtained molded articles were visually observed to evaluate the film-forming properties. Specifically, a molded article without cracking was determined to be “A” while a molded article with cracking was determined to be “B.”

[0059] A glass container (length: 14 cm×width: 14 cm×height: 2 cm) was placed horizontally in an oven (model: PVH-231, produced by ESPEC Corp.), and 20 g of the chlorosulfonated polyethylene latex composition was gently poured into the glass container.

[0060] The internal temperature of the oven was set to 70° C., and the product was dried by heating for 5 hours. Further, the internal temperature of the oven was changed to 120° C., and the product was dried by heating for 2 hours.

[0061] The glass container was removed from the oven and allowed to cool to room temperature to thus obtain a molded article of the chlorosulfonated polyethylene latex composition.

(2) Tensile Strength of Molded Article

[0062] Chlorosulfonated polyethylene latex compositions were produced under the conditions described in each Example and each Comparative Example, and molded articles of the compositions were formed in the same manner as described in “(1) Film-forming Properties” above. The tensile strength of the molded articles was then measured. The tensile strength of the molded articles was measured in accordance with JIS K6251:2010. Specifically, the obtained molded article was punched into a No. 4 dumbbell shape, and the measurement was performed using a tensile tester (Autograph AGS-X, 10 kN, produced by Shimadzu Corporation) at a tensile rate of 200 mm/min. Molded articles preferably have a tensile strength measured in this manner of about 30 to 40 MPa.

Example 1

[0063] A chlorosulfonated polyethylene latex composition was obtained by adding 0.8 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (1 part by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 2.0 g of phenyl glycol as a glycol ether (5 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 2

[0064] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 2.0 g of phenyl glycol as a glycol ether (5 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 3

[0065] A chlorosulfonated polyethylene latex composition was obtained by adding 0.8 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (1 part by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of phenyl glycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 4

[0066] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of phenyl glycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 5

[0067] A chlorosulfonated polyethylene latex composition was obtained by adding 4.0 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (5 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of phenyl glycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 6

[0068] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of butyl triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 7

[0069] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of phenyl diglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 8

[0070] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of methyl propylene triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 9

[0071] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 6.0 g of butyl triglycol as a glycol ether (15 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 10

[0072] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 8.0 g of butyl triglycol as a glycol ether (20 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 11

[0073] A chlorosulfonated polyethylene latex composition was obtained by adding 1.2 g of zinc N-ethyl-N-phenyldithiocarbamate (trade name: Nocceler PX, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of butyl triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 12

[0074] A chlorosulfonated polyethylene latex composition was obtained by adding 1.2 g of dipentamethylenethiuram tetrasulfide (trade name: Nocceler TRA, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of butyl triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Example 13

[0075] A chlorosulfonated polyethylene latex composition was obtained by adding 1.2 g of a zinc salt of 2-mercaptobenzothiazole (trade name: Nocceler MZ, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex), and 4.0 g of butyl triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Comparative Example 1

[0076] A chlorosulfonated polyethylene latex composition was obtained without adding anything to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.).

Comparative Example 2

[0077] A chlorosulfonated polyethylene latex composition was obtained by adding 2.4 g of a 50% aqueous solution of sodium dibutyldithiocarbamate (trade name: Nocceler TP, produced by Ouchi Shinko Chemical Industrial Co., Ltd.) as a vulcanization accelerator (3 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.), without adding any glycol ether.

Comparative Example 3

[0078] A chlorosulfonated polyethylene latex composition was obtained by adding 4.0 g of butyl triglycol as a glycol ether (10 parts by mass per 100 parts by mass of the solids content of chlorosulfonated polyethylene latex) to 100 g of chlorosulfonated polyethylene latex with a solids content of 40% (trade name: Sepolex CSM, produced by Sumitomo Seika Chemicals Co., Ltd.), without adding any vulcanization accelerator.

[0079] Table 1 below shows the film-forming properties of the chlorosulfonated polyethylene compositions obtained in the Examples and Comparative Examples, and the tensile strength of the molded articles obtained from these compositions.

TABLE-US-00001 TABLE 1 Film- Tensile Vulcanization forming strength accelerator Glycol ether properties (MPa) Ex. 1 Nocceler TP Phenyl glycol A 31.3 1 part by mass 5 parts by mass Ex. 2 Nocceler TP Phenyl glycol A 31.5 3 parts by mass 5 parts by mass Ex. 3 Nocceler TP Phenyl glycol A 32.6 1 part by mass 10 parts by mass Ex. 4 Nocceler TP Phenyl glycol A 40.0 3 parts by mass 10 parts by mass Ex. 5 Nocceler TP Phenyl glycol A 35.1 5 parts by mass 10 parts by mass Ex. 6 Nocceler TP Butyl triglycol A 40.5 3 parts by mass 10 parts by mass Ex. 7 Nocceler TP Phenyl diglycol A 38.6 3 parts by mass 10 parts by mass Ex. 8 Nocceler TP Methyl propylene triglycol A 35.0 3 parts by mass 10 parts by mass Ex. 9 Nocceler TP Butyl triglycol A 37.5 3 parts by mass 15 parts by mass Ex. 10 Nocceler TP Butyl triglycol A 38.0 3 parts by mass 20 parts by mass Ex. 11 Nocceler PX Butyl triglycol A 32.2 3 parts by mass 10 parts by mass Ex. 12 Nocceler TRA Butyl triglycol A 31.1 3 parts by mass 10 parts by mass Ex. 13 Nocceler MZ Butyl triglycol A 33.2 3 parts by mass 10 parts by mass Comp. Ex. 1 None None B 22.3 Comp. Ex. 2 Nocceler TP None A 23.7 3 parts by mass Comp. Ex. 3 None Butyl triglycol A 24.2 10 parts by mass Nocceler TP (dithiocarbamate-based): sodium dibutyldithiocarbamate Nocceler PX (dithiocarbamate-based): zinc N-ethyl-N-phenyldithiocarbamate Nocceler TRA (thiuram-based): dipentamethylenethiuram tetrasulfide Nocceler MZ (thiazole-based): zinc salt of 2-mercaptobenzothiazole

[0080] As shown in Table 1, the chlorosulfonated polyethylene latex compositions obtained in the Examples had excellent film-forming properties, and the molded articles obtained using these compositions had remarkably improved tensile strength. In contrast, although some of the chlorosulfonated polyethylene latex compositions obtained in the Comparative Examples had improved film-forming properties, the molded articles obtained using these compositions did not have improved tensile strength.

[0081] The above results demonstrate that the chlorosulfonated polyethylene latex compositions comprising chlorosulfonated polyethylene latex, a vulcanization accelerator, and a glycol ether have excellent film-forming properties, and that the molded products produced by using these chlorosulfonated polyethylene latex compositions have a tensile strength that greatly exceeds the tensile strength of the original chlorosulfonated polyethylene (e.g., 24 MPa as disclosed in Example 1 of PTL 1).