CARBON NANOTUBE THREAD Z-AXIS MULTIFUNCTIONAL STITCHING

Abstract

Carbon nanotube threads are coated with a coating solution such as dimethylformamide (DMF), ethylene glycol (EG), polyethylene glycol (PEG), PEG200 (PEG with a average molecular weight of approximately 200 grams per mole (g/mol)), PEG400 (PEG with a average molecular weight of approximately 400 g/mol), dimethyl sulfide (DMS 100 cP), HP1632, poly(methylhydrosiloxane), polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane 0 resin, platinum (0) -1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, moisture in air, acetic acid, water, poly(dimethylsiloxane) hydroxy terminated, (3-glycidyloxypropyl)-trimethoxysilane or a combination thereof. The coated carbon nanotubes may be used to stitch in a Z-direction into a composite such as a polymer prepreg to strengthen the composite. The stitching may occur using a sewing machine.

Claims

1. A method for coating a carbon nanotube thread, the method comprising: immersing a carbon nanotube thread in a coating solution to form a coated carbon nanotube thread, the coating solution comprising dimethylformamide (DMF), ethylene glycol (EG), polyethylene glycol (PEG), PEG200 (PEG with an average molecular weight of approximately 200 grams per mole (g/mol)), PEG400 (PEG with an average molecular weight of approximately 400 g/mol), dimethyl sulfide (DMS 100 cP), HP1632, poly(methylhydrosiloxane), polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane O resin, platinum (0) -1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, moisture in air, acetic acid, water, poly(dimethylsiloxane) hydroxy terminated, (3-glycidyloxypropyl)trimethoxysilane, petroleum based oils, synthetic oils, natural oils such as vegetable oil, coconut oil, palm oil or a combination thereof; and heating the coated carbon nanotube thread at a temperature from 50° C. to 230° C. to dry the coated carbon nanotube thread.

2. The method of claim 1, further comprising applying a lubricant to the coated carbon nanotube thread after the coated carbon nanotube thread is dry.

3. An article comprising a substrate stitched with a carbon nanotube thread in a Z-direction into the substrate, the carbon nanotube thread being coated with a coating solution chosen from dimethylformamide (DMF), ethylene glycol (EG), polyethylene glycol (PEG), PEG200 (PEG with a average molecular weight of approximately 200 grams per mole (g/mol)), PEG400 (PEG with a average molecular weight of approximately 400 g/mol), dimethyl sulfide (DMS 100 cP), HP1632, poly(methylhydrosiloxane), polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane O resin, platinum (0) -1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, moisture in air, acetic acid, water, poly(dimethylsiloxane) hydroxy terminated, (3-glycidyloxypropyl)trimethoxysilane, petroleum based oils, synthetic oils, and natural oils such as vegetable oil, coconut oil, palm oil, or a combination thereof.

4. A method for strengthening a composite, the method comprising: stitching a coated carbon nanotube thread with a sewing machine in a Z-direction into the composite.

5. The method of claim 4, further comprising: coating a carbon nanotube thread with a coating solution to form the coated carbon nanotube thread, the coating solution comprising dimethylformamide (DMF), ethylene glycol (EG), polyethylene glycol (PEG), PEG200 (PEG with a average molecular weight of approximately 200 grams per mole (g/mol)), PEG400 (PEG with a average molecular weight of approximately 400 g/mol), dimethyl sulfide (DMS 100 cP), HP1632, poly(methylhydrosiloxane), polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane O resin, platinum (0) -1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, moisture in air, acetic acid, water, poly(dimethylsiloxane) hydroxy terminated, (3-glycidyloxypropyl)trimethoxysilane, petroleum based oils, synthetic oils, and natural oils such as vegetable oil, coconut oil, palm oil, or a combination thereof; heating the coated carbon nanotube thread at a temperature from 50° C. to 230° C.; winding the coated carbon nanotube thread onto a spool; and loading the spool into the sewing machine.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] Though the specification concludes with claims particularly pointing out and distinctly claiming the invention, it is believed that the present invention will be better understood from the following description taken in conjunction with the accompanying drawings, in which:

[0012] The FIGURE includes synthetic schemes for preparing coated CNT thread according to embodiments described herein.

DETAILED DESCRIPTION

[0013] Features and advantages of the invention will now be described with occasional reference to specific embodiments. However, the invention may be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete and will fully convey the scope of the invention to those skilled in the art.

[0014] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention belongs. The terminology used in the description herein is for describing particular embodiments only and is not intended to be limiting. As used in the specification and appended claims, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.

[0015] As used in this disclosure, the term “preforms” are three-dimensional fabric forms designed to conform to a specific shape to meet specific mechanical and structural requirements. Carbon nanotube (CNT) thread can be sewn in to the Z-direction of a composite preform using a standard sewing machines, industrial sewing machines (one or two-sided), or a LayStich system. CNT thread may be any CNT thread made by any suitable method. Various kinds of CNT thread are available commercially from Nanocomp Technologies, Inc (NTI). The CNT thread may have a single ply or multiple plies and standard production strength or high strength. The CNT thread is electrically conductive.

[0016] The Z-direction stitching significantly improves Z-direction mechanical, thermal, and electrical properties. The CNT thread electrical properties may be exploited further by designing stitched patterns and using these as embedded composites as antennas, heaters, sensors, or general wiring for any type of electrical connection for various applications—this concept is referred to as enabling multifunctionality into composite structures.

[0017] A LayStitch system allows for novel fiber architectures through the computer controlled deposition of fiber tows and threads in a layer-by-layer process. The CNT thread can be used as either (or both) the sewing thread or the tow material to construct may types of optimized strength or multifunctional composite preforms including all CNT preforms. The CNT yarn enables this type of application, because carbon fiber tows are too brittle to be used as a thread and have a denier that is much too large for many applications.

[0018] In the aerospace field, the most common form of composite fabrication is through a lay-up of prepreg plies, which are then cured to form a composite structure. Prepreg plies are used because the toughened matrix resin can be uniformly coated onto each laminate. The prepreg lay-up approach is not suitable to making complex composite parts. Complex parts are easy to make using dry preforms however. Dry preforms require subsequent resin infusion to make a finished composite, and this process may restrict the use of most tougheners used in prepreg systems.

[0019] Conventional prepreg-based composite structures can be Z-pinned to improve damage tolerance; however, Z-pinning is expensive and damages the prepreg fibers. With the advent of Z-stitching, high strength CNT threads can be stitched into dry laminates, damage-free, providing superior toughening versus traditional toughened resins in prepregs or Z-pinning. Also the CNT thread can with stand higher temperatures than polymer-based threads enabling use for BMI's polyimides, carbon/carbon, and ceramic matrix composites. Additionally, CNT threads are electrically and thermally conductive thereby enabling various multifunctionalities. Overall, CNT threads Z-stitching enables complex and tougher composite preforms and resulting structures that cannot be fabricated today with state-of-the-art technologies.

[0020] Using combinations of solvents and solutions, the CNT thread is coated and then treated. In one embodiment, the coating solution is selected from the Hydrosize® line of products, which includes sizing solutions designed for use in the manufacturing of glass fiber, carbon fiber and natural fiber, using chopped strand or continuous strand fiber glass. These are in turn used to manufacture composite products and components. This solution offers excellent adhesion properties and abrasion resistance. In one embodiment, the solution is HP 1632, which is a polyimide solution.

[0021] In another embodiment, the coating solution comprises DMF, ethylene glycol (EG), polyethylene glycol (PEG), PEG200 (PEG with an average molecular weight of approximately 200 grams per mole (g/mol)), PEG400 (PEG with an average molecular weight of approximately 400 g/mol), dimethyl sulfide (DMS100 cP), HP1632, poly(methylhydrosiloxane), polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane O resin, platinum (0) -1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, moisture in air, acetic acid, water, poly(dimethylsiloxane) hydroxy terminated, (3-glycidyloxypropyl)trimethoxysilane or a combination thereof. However, other acids stronger and weaker than acetic acid may be substituted for acetic acid. In addition, other chemicals with similar chemical properties may be substituted for other reagents in the coating solution.

[0022] Depending on the type of coating in which a CNT thread is immersed, different treatments yield better or worse results, with the desired result being a lower coefficient of friction. A lower friction coefficient allows the CNT thread to be used in a sewing machine, similar to normal thread, which encompasses winding the thread on a spool, loading the spool into a sewing machine, and sewing the coated CNT thread into a substrate without the thread breaking.

[0023] In further embodiments, the coating solution may comprise DMS, AMSG, HPM, or PAWG. DMS is an aminopropyl terminated polydimethylsiloxane and is also a lubricant that has amino group for matrix compatibility. AMSG is a three-ingredient mixture. The AMSG offers amino group for matrix interaction and is believed to generate hydroxyl groups when the coated threads are left in air for sufficient long storage time (by moisture in air). The AMSG interacts with carboxylic and hydroxyl groups of the fiber surface if they are available. The AMSG has polyalkylene glycol and silicone for lubrication. HPM is a two-ingredient mixture that is believed to generate hydroxyl groups when the coated yarns are left in air for sufficient long storage time). The HPM interacts with carboxylic and hydroxyl groups of the fiber surfaces if they are available. The HPM has silicone section for lubrication. PAWG is a three-ingredient mixture. The PAWG offers epoxy groups for matrix interaction and is believed to interact with carboxylic and hydroxyl groups of the fiber surfaces if they are available. The PAWG has polyalkylene glycol for lubrication.

[0024] In still further embodiments, the coating solution may include any type of oil such as, for example, petroleum based oils, synthetic oils, and natural oils such as vegetable oil, coconut oil, palm oil, or combinations thereof.

[0025] In some embodiments, while the coated nanotube thread is being used to stitch or sew, the a solvent such as water, alcohol, or acetone, for example, may be dripped or sprayed onto the carbon nanotube thread. The benefits of using a solvent in this manner is that the solvent can be dried away, leaving no residue after sewing. In some embodiments, dry graphite powder may be used to lubricate the coated carbon nanotube thread during sewing.

[0026] The CNT thread is treated by immersing the thread in a coating solution, and then drying the thread. There are different combinations of coating solutions, as previously described. Depending on the coating solution, the immersion and drying step may be repeated two or three times. Once the thread has been immersed in the coating solution, the CNT thread is heated at a temperature from 50° C. to 230° C.

[0027] After the CNT thread is coated, an additional lubricant may increase the functionality of the thread. Siloxane, polyalkylene glycol, or combinations thereof were typical lubricants used for various trials.

EXAMPLES

[0028] The following examples are offered by way of illustration only and are not intended to limit the scope of the preceding disclosure or the appended claims.

[0029] Tables 1 and 2 include the results of different tests, when CNT thread was immersed in a coating solution and then dried. As the results show, for CNT threads coated with DMF (dimethylformamide) the coefficient of friction was less after treatment than it was before treatment.

[0030] The tests included a coefficient of friction (COF) test and a sewing test. A test sample was given a “Pass” in the COF test if either (a) the coefficient of friction of a coated/size carbon nanotube thread was determined to be less than that of a neat (uncoated/unsized) carbon nanotube thread; or (b) the coefficient of friction of the coated/size carbon nanotube thread was determined to be similar to (±10%) that of a regular polyester or cotton sewing thread conventionally used in a sewing machine. A test sample was given a “Pass” in the sewing test if, on loading a spool of the coated carbon nanotube thread into a conventional home sewing machine and using the carbon nanotube thread to sew according to the manufacturer instructions of the conventional home sewing machine, the coated carbon nanotube thread sews properly, i.e., does not tangle, jam the sewing machine, or miss stitches.

[0031] Table 2 describes results from applying different treatments and coatings to CNT thread and testing in the same manner as described in Table 1. In trials 4-6, the treatments were repeated, and two after-treatment coefficients of friction are reported: the COF measured before the treatment was repeated (Heat 1), and the COF measured after the second treatment (Heat 2).

TABLE-US-00001 TABLE 1 Solvent Based Investigation Before Coating Treatment After Treatment COF Sewing No Description Treatment COF* SD** COF SD Test Test 1 DMF Immersion & 50° C. 0.264 10.11 0.254 0.018 Pass N/T Dry 2 DMF Immersion & 0.211 0.004 0.201 0.002 Pass N/T 160° C. Dry 3 DMF Immersion & 50° C. 0.218 0.077 0.202 0.003 Pass Pass Dry 4 DMF/HP1632 Immersion & 0.267 0.005 Heat 1 = 0.280 Heat 1 = 0.280 Fail N/T (90/10 v/v) 230° C. Dry (x2) Heat 2 = 0.288 Heat 2 = 0.288 5 DMF/HP1632 Immersion & 0.252 0.033 Heat 1 = 0.314 Heat 1 = 0.314 Fail N/T (75/25 v/v) 230° C. Dry (x2) Heat 2 = 0.297 Heat 2 = 0.297 6 DMF/HP1632 Immersion & 0.266 0.004 Heat 1 = 0.327 Heat 1 = 0.327 Fail N/T (50/50 v/v) 230° C. Dry (x2) Heat 2 = 0.323 Heat 2 = 0.323 *Coefficient of Friction **Standard Deviation

TABLE-US-00002 TABLE 2 Lubrication Based Investigation Before Coating Treatment After Treatment COF Sewing No Description Treatment COF SD COF*** SD Test Test 1 DMS100cP Immersion & 0.203 0.012 0.199 0.018 Pass Pass 16 plies 200° C. Dry of fiberglass 2 DMS100cP Immersion & 0.264 0.011 0.265 0.040 Fail N/T 200° C. Dry (yarn defects) 3 PEG200 Immersion & 0.208 0.009 Heat 1 = 0.382 Heat 1 = 0.160 Fail Pass 200° C. Dry (x2) Heat 2 = 0.419 Heat 2 = 0.202 4 EG Immersion & 0.202 0.007 Heat 1 = 0.259 Heat 1 = 0.029 Fail N/T 50° C. Dry Heat 2 = 0.256 Heat 2 = 0.030 5 PEG200 Immersion & 0.265 0.010 Heat 1 = 0.358 Heat 1 = 0.194 Pass N/T 200° C. Dry (x2) Heat 2 = 0.244 Heat 2 = 0.019 6 PEG400 Immersion & 0.203 0.012 Heat 1 = 0.403 Heat 1 = 0.036 Fail N/T 200° C. Dry (x2) Heat 2 = 0.444 Heat 2 = 0.087

[0032] To assess how certain lubrication components affected the COF, three different tests were performed, the data for which are provided in Table 3. The lubrication test was chosen to assess compatibility with certain other functional groups. In the three tests, three different sizings of CNT thread, three different coatings, two different treatments, and three different lubrication components were used.

[0033] In Test 1, the coating solution included a combination of polyalkylene glycol, (3-aminopropyl)trimethoxysilane, hydride functional siloxane O resin, and platinum (0) -1,3-divinyl-1,1,3,3-tetramethyldisiloxane. This coating was chosen to yield an interface comprising the following CNT/sizing interface:

##STR00001##

[0034] These interface substituent groups created a matrix that was compatible to binding hydroxyl groups and amine groups. The CNT thread source was Lot. #271, 4-ply consisting of sizing AMSG. The CNT thread was coated as described in this paragraph by immersing the thread into the coating solution, then drying the thread at 140° C., and then repeating these two steps (immersing the CNT thread and drying the CNT thread).

[0035] In Test 2, the coating solution included hydride-functional siloxane O resin, platinum (0)-1,3-divinyl-1,1,3,3-tetramethyl-disiloxane, and the moisture in air. This coating was chosen to yield interface 1 and interface 2. The designed lubrication component consisted of siloxane. The interface substituent groups and the lubrication component created a matrix that was compatible to binding hydroxyl groups. The CNT thread source was Lot. #271, 4-ply consisting of sizing HPM. The CNT thread was treated by immersing the CNT thread in the coating described in this paragraph, and then drying the CNT thread at 140° C. The immersing and drying steps were only performed once.

[0036] In Test 3, the coating solution included a combination of polyalkylene glycol, acetic acid, water, and (3-glycidyloxypropyl)trimethoxysilane. This coating was chosen to yield interface 1 and interface 2. The designed lubrication component consisted of PAG. The interface substituent groups and the lubrication component created a matrix that was compatible to binding hydroxyl groups and epoxide groups. The CNT thread source was Lot. #271, 4-ply consisting of sizing PAWG. The CNT thread was treated by immersing the CNT thread in the coating described in this paragraph, and then drying the CNT thread at 140° C. The immersing and drying steps were only performed once.

[0037] The results to the three tests mentioned above are recorded in Table 3. All three strands of CNT thread passed the sewing test.

TABLE-US-00003 TABLE 3 Custom Synthesis Before Treatment After Treatment No. COF SD COF SD COF Test Sewing Test 1 0.227 0.003 0.207 0.012 Pass Pass 2 0.223 0.023 0.217 0.011 Pass Pass 3 0.242 0.009 0.208 0.047 Pass Pass

[0038] Additional synthetic schemes that may be used in embodiments are provided in the FIGURE.

[0039] Various composites were sewn or stitched in the Z-direction with coated carbon nanotube threads according to embodiments of this disclosure. Mechanical testing performed on the stitched composites showed that the Z-stitching improves interlaminar composite properties such as the results of Mode I fracture toughness testing.

[0040] For assessing fracture toughness, twelve-ply carbon fiber cloth test specimens with untoughened epoxy SR-4-86 matrices or toughened RM2005 epoxy matrices were fabricated and tested. The results in the Table 4 show that 0.125-inch pitch stitches resulted in a tougher composite than aerospace grade toughened epoxy matrix composites. The results also show that sparser 0.25-inch pitch stitches out performed both untoughened epoxy matrix and nano-particle enhanced epoxy matrix composites.

[0041] Stitched composites were tested for fracture toughness. Results of various tests for fracture toughness are provided in Table 4.

TABLE-US-00004 TABLE 4 Results of Mode I Fracture Toughness Testing Automated Calculation Manual Calculation Test Specimen Type (lbs/in) (lbs/in) SR-4-86 0.125-inch Stitched Panel 7.061 7.985 RM2005 Toughened Baseline Panel 5.468 5.895 SR-4-86 0.25-inch Stitched Panel 4.633 5.085 SR-4-86 Untoughened Baseline Panel 3.550 3.856 S4-4-86 Nano-enhanced Panel 3.416 3.846

[0042] It should be apparent to those skilled in the art that modifications and variations can be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Thus, it is intended that the specification cover the modifications and variations of the various embodiments described herein, provided such modifications and variations come within the scope of the appended claims and their equivalents.