Metal-based tris-bipyridyl complexes and uses thereof in electrochromic applications
09847494 · 2017-12-19
Assignee
Inventors
- Milko E. VAN DER BOOM (Rishon Lezion, IL)
- Michal LAHAV (Rehovot, IL)
- Sreejith Shankar Pooppanal (Rehovot, IL)
Cpc classification
B82Y10/00
PERFORMING OPERATIONS; TRANSPORTING
G11C7/00
PHYSICS
H10K85/331
ELECTRICITY
C07D403/06
CHEMISTRY; METALLURGY
C09B57/10
CHEMISTRY; METALLURGY
C07D401/06
CHEMISTRY; METALLURGY
International classification
B82Y10/00
PERFORMING OPERATIONS; TRANSPORTING
C07D401/06
CHEMISTRY; METALLURGY
C07D403/06
CHEMISTRY; METALLURGY
C09B57/10
CHEMISTRY; METALLURGY
G11C7/00
PHYSICS
Abstract
The present invention relates to metal-based tris-bipyridyl complexes, e.g., iron-based tris-bipyridyl complexes, and their use in fabrication of surface confined assemblies for electrochromic applications. Formulae I and II. ##STR00001##
Claims
1. A tris-bipyridyl complex of the general formula I: ##STR00017## wherein M is a transition metal selected from Mn, Fe, Co, Ni, Cu, Zn, Ti, V, Cr, Rh or Ir; n is the formal oxidation state of the transition metal, wherein n is 0-6; X is a counter anion such as Br.sup.−, Cl.sup.−, F.sup.−, I.sup.−, PF.sub.6.sup.−, BF.sub.4.sup.−, OH.sup.−, ClO.sub.4.sup.−, SO.sub.3.sup.2−, SO.sub.4.sup.2−, CF.sub.3COO.sup.−, CN.sup.−, alkylCOO.sup.−, arylCOO.sup.−, or a combination thereof; m is a number ranging from 0 to 6; R.sub.1 to R.sub.18 each independently is selected from H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —CON(R.sub.20).sub.2, —COOR.sub.20, —SR.sub.20, —SO.sub.3H, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, (C.sub.1-C.sub.10)alkoxy, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, protected carboxyl, or protected amino, wherein said (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, cycloalkyl, heterocycloalkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1 to A.sub.6 each independently is a group of the formula III or IV linked to the ring structure of the complex of general formula I via R.sub.19 ##STR00018## R.sub.19 each independently is selected from C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, phenylene, biphenylene, a peptide moiety consisting of 3 to 5 amino acid residues, ##STR00019## R.sub.x and R.sub.y each independently is selected from H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —CON(R.sub.20).sub.2, —COOR.sub.20, —SR.sub.20, —SO.sub.3H, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, (C.sub.1-C.sub.10)alkoxy, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, protected carboxyl, or protected amino, wherein said (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, cycloalkyl, heterocycloalkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl.
2. The complex of claim 1, wherein A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H.
3. The complex of claim 1, wherein R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, preferably C—C, C═C or C≡C.
4. The complex of claim 1, wherein A.sub.1 to A.sub.6 each is a group of the formula III wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C; or of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
5. The complex of claim 1, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N; and R.sub.20 each is H.
6. The complex of claim 5, wherein R.sub.1 to R.sub.18 each is H; A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; and R.sub.19 each independently is C—C, C═C or C≡C.
7. The complex of claim 6, wherein M is Fe; n and m each is 2 or 3; and A.sub.1 to A.sub.6 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C.
8. The complex of claim 7, wherein X is PF.sub.6.sup.−; and (i) R.sub.19 each is C—C, herein identified complex 2SB(Fe.sup.2+) or 2SB(Fe.sup.3+); (ii) R.sub.19 each is C═C, herein identified complex 2DB(Fe.sup.2+) or 2DB(Fe.sup.3+); or (ii) R.sub.19 each is C≡C, herein identified complex 2 TB(Fe.sup.2+) or 2 TB(Fe.sup.3+).
9. The complex of claim 6, wherein M is Fe; n and m each is 2 or 3; and A.sub.1 to A.sub.6 each is a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
10. The complex of claim 9, wherein X is PF.sub.6.sup.−; and (i) R.sub.19 each is C—C, herein identified complex 4SB(Fe.sup.2+) or 4SB(Fe.sup.3+); (ii) R.sub.19 each is C═C, herein identified complex 4DB(Fe.sup.2+) or 4DB(Fe.sup.3+); or (ii) R.sub.19 each is C≡C, herein identified complex 4TB(Fe.sup.2+) or 4TB(Fe.sup.3+).
11. An iron-based tris-bipyridyl complex of the general formula II: ##STR00020## wherein n is the formal oxidation state of the Fe, wherein n is 0-6; X is a counter anion such as Br.sup.−, Cl.sup.−, F.sup.−, I.sup.−, PF.sub.6.sup.−, BF.sub.4.sup.−, OH.sup.−, ClO.sub.4.sup.−, SO.sub.3.sup.2−, SO.sub.4.sup.2−, CF.sub.3COO.sup.−, CN.sup.−, alkCOO.sup.−, arylCOO.sup.−, or a combination thereof; m is a number ranging from 0 to 6; R.sub.1 to R.sub.18 each independently is selected from H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —CON(R.sub.20).sub.2, —COOR.sub.20, —SR.sub.20, —SO.sub.3H, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, (C.sub.1-C.sub.10)alkoxy, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, protected carboxyl, or protected amino, wherein said (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, cycloalkyl, heterocycloalkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III or IV linked to the ring structure of the complex of general formula II via R.sub.19 ##STR00021## R.sub.19 is selected from C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, phenylene, biphenylene, a peptide moiety consisting of 3 to 5 amino acid residues, ##STR00022## R.sub.x and R.sub.y each independently is selected from H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —CON(R.sub.20).sub.2, —COOR.sub.20, —SR.sub.20, —SO.sub.3H, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, (C.sub.1-C.sub.10)alkoxy, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, protected carboxyl, or protected amino, wherein said (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, cycloalkyl, heterocycloalkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; B.sub.1 to B.sub.3 each independently is selected from H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —CON(R.sub.20).sub.2, —COOR.sub.20, —SR.sub.20, —SO.sub.3H, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, (C.sub.1-C.sub.10)alkoxy, cycloalkyl, heterocycloalkyl, aryl, heteroaryl, protected carboxyl, or protected amino, wherein said (C.sub.1-C.sub.10)alkyl, (C.sub.2-C.sub.10)alkenyl, (C.sub.2-C.sub.10)alkynyl, cycloalkyl, heterocycloalkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20—(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl.
12. The complex of claim 11, wherein A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H.
13. The complex of claim 11, wherein R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, preferably C—C, C═C or C≡C.
14. The complex of claim 11, wherein A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C; or of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
15. The complex of claim 11, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; and R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N; B.sub.1 to B.sub.3 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH— pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each is H.
16. The complex of claim 15, wherein R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; R.sub.19 each independently is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is (C.sub.1-C.sub.4)alkyl, preferably methyl or ethyl.
17. The complex of claim 16, wherein A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is methyl.
18. The complex of claim 17, wherein X is PF.sub.6.sup.−; n and m each is 2 or 3; and (i) R.sub.19 each is C—C, herein identified complex 1SB(Fe.sup.2+) or 1SB(Fe.sup.3+); (ii) R.sub.19 each is C═C, herein identified complex 1DB(Fe.sup.2+) or 1DB(Fe.sup.3+); or (ii) R.sub.19 each is C≡C, herein identified complex 1TB(Fe.sup.2+) or 1TB(Fe.sup.3+).
19. The complex of claim 16, wherein A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C═C; and B.sub.1 to B.sub.3 each is methyl.
20. The complex of claim 19, wherein X is PF.sub.6.sup.−; n and in each is 2 or 3; and (i) R.sub.19 each is C—C, herein identified complex 3SB(Fe.sup.2+) or 3SB(Fe.sup.3+); (ii) R.sub.19 each is C═C, herein identified complex 3DB(Fe.sup.2+) or 3DB(Fe.sup.3+); or (ii) R.sub.19 each is C≡C, herein identified complex 3TB(Fe.sup.2+) or 3TB(Fe.sup.3+).
21. A device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have a predetermined oxidation state being changeable upon subjecting said layered structure to an electric field, wherein exposure of said device to a potential change causes reversible electron transfer, which results in a change in the electrochromic properties of said layered structure with high coloration efficiency, said device having high electrochemical stability when repeatedly exposed to a potential change, wherein said redox-active compound each independently is a tris-bipyridyl complex of claim 1.
22. The device of claim 21, wherein said coloration efficiency is higher than 500 cm.sup.2C.sup.−1, preferably higher than 800 cm.sup.2C.sup.−1, more preferably higher than 1000 cm.sup.2C.sup.−1.
23. The device of claim 21, wherein said substrate comprises glass, a doped glass, indium tin oxide (ITO)-coated glass, transparent conductive oxide, silicon, a doped silicon, Si(100), Si(111), SiO.sub.2, SiH, silicon carbide mirror, quartz, a metal, metal oxide, a mixture of metal and metal oxide, group IV elements, mica, a polymer such as polyacrylamide and polystyrene, a plastic, a zeolite, a clay, wood, a membrane, an optical fiber, a ceramic, a metalized ceramic, an alumina, an electrically-conductive material, a semiconductor, steel or a stainless steel and wherein said substrate is in the form of sheets, plates, columns, beads, microparticles, sub-microparticles, nanoparticles, quantum dots, metal-organic framework, or nanotubes and wherein said substrate is optically transparent to the ultraviolet (UV), infrared (IR), near-IR (NIR) and/or visible spectral ranges.
24. The device of claim 21, wherein said layered structure comprises (i) a monolayer of either one redox-active compound or two or more redox-active compounds, said redox-active compounds having identical or different metals; or (ii) a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compounds having identical or different metals.
25. The device of claim 24, wherein said layered structure comprises a monolayer of either one redox-active compound or two or more redox-active compounds, or a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is: a tris-bipyridyl complex of the general formula I in claim 1, wherein M is Fe; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; and A.sub.1 to A.sub.6 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
26. The device of claim 25, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or II, wherein X is PF.sub.6.sup.−.
27. The device of claim 21, for use in smart windows, electrochromic windows, smart mirrors, optical filters, frequency doubling devices, optical switches, modulators, spatial light modulators, phase masks, data transfer devices, data storage devices, pulse shapers, optical processors, electrochromic display devices, smart papers, electrochromic goggles, electrochromic helmets, electrochromic paints, or visors.
28. The device of claim 27, for use in smart windows or electrochromic windows, wherein said layered structure comprises a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is: a tris-bipyridyl complex of the general formula I in claim 1, wherein M is Fe; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; and A.sub.1 to A.sub.6 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
29. The device of claim 28, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or II, wherein X is PF.sub.6.sup.−.
30. A memory device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have at least one a predetermined electronic property, including at least one of electrodensity and oxidation state, said predetermined electronic property being changeable upon subjecting said layered structure to an electric field, wherein said redox-active compound each independently is a tris-bipyridyl complex of claim 1.
31. A device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have a predetermined oxidation state being changeable upon subjecting said layered structure to an electric field, wherein exposure of said device to a potential change causes reversible electron transfer, which results in a change in the electrochromic properties of said layered structure with high coloration efficiency, said device having high electrochemical stability when repeatedly exposed to a potential change, wherein said redox-active compound each independently is a tris-bipyridyl complex of claim 11.
32. The device of claim 31, wherein said coloration efficiency is higher than 500 cm.sup.2C.sup.−1, preferably higher than 800 cm.sup.2C.sup.−1, more preferably higher than 1000 cm.sup.2C.sup.−1.
33. The device of claim 31, wherein said substrate comprises glass, a doped glass, indium tin oxide (ITO)-coated glass, transparent conductive oxide, silicon, a doped silicon, Si(100), Si(111), SiO.sub.2, SiH, silicon carbide mirror, quartz, a metal, metal oxide, a mixture of metal and metal oxide, group IV elements, mica, a polymer such as polyacrylamide and polystyrene, a plastic, a zeolite, a clay, wood, a membrane, an optical fiber, a ceramic, a metalized ceramic, an alumina, an electrically-conductive material, a semiconductor, steel or a stainless steel and wherein said substrate is in the form of sheets, plates, columns, beads, microparticles, sub-microparticles, nanoparticles, quantum dots, metal-organic framework, or nanotubes and wherein said substrate is optically transparent to the ultraviolet (UV), infrared (IR), near-IR (NIR) and/or visible spectral ranges.
34. The device of claim 31, wherein said layered structure comprises (i) a monolayer of either one redox-active compound or two or more redox-active compounds, said redox-active compounds having identical or different metals; or (ii) a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compounds having identical or different metals.
35. The device of claim 34, wherein said layered structure comprises a monolayer of either one redox-active compound or two or more redox-active compounds, or a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is: a tris-bipyridyl complex of the general formula II in claim 11, wherein n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is methyl.
36. The device of claim 35, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or II, wherein X is PF.sub.6.sup.−.
37. The device of claim 31, for use in smart windows, electrochromic windows, smart mirrors, optical filters, frequency doubling devices, optical switches, modulators, spatial light modulators, phase masks, data transfer devices, data storage devices, pulse shapers, optical processors, electrochromic display devices, smart papers, electrochromic goggles, electrochromic helmets, electrochromic paints, or visors.
38. The device of claim 37, for use in smart windows or electrochromic windows, wherein said layered structure comprises a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is: a tris-bipyridyl complex of the general formula II in claim 11, wherein n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is methyl.
39. The device of claim 31, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or II, wherein X is PF.sub.6.sup.−.
40. A memory device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have at least one a predetermined electronic property, including at least one of electrodensity and oxidation state, said predetermined electronic property being changeable upon subjecting said layered structure to an electric field, wherein said redox-active compound each independently is a tris-bipyridyl complex of claim 11.
Description
BRIEF DESCRIPTION OF DRAWINGS
(1)
(2)
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
(14)
(15)
(16)
(17)
(18)
(19)
(20)
(21)
(22)
(23)
(24)
(25)
(26)
(27)
(28)
(29)
(30)
(31)
(32)
(33)
(34)
(35)
(36)
(37)
(38)
(39)
(40)
(41)
(42)
(43)
(44)
(45)
(46)
(47)
(48)
(49)
DETAILED DESCRIPTION OF THE INVENTION
(50) The present invention relates to a tris-bipyridyl complex of the general formula I and to an iron-based tris-bipyridyl complex of the general formula II as defined above.
(51) The term “oxidation state” also known as “oxidation number” is an indicator of the degree of oxidation of an atom in a chemical compound. As used herein, this term refers to the oxidation state of the tris-bipyridyl complexes of the present invention, more particularly to the oxidation state of the metal atom in the complex which may be either the electrically neutral state of said metal atom or any state other than said neutral state produced/caused by the gain or loss of electrons, i.e., reduction or oxidation, respectively.
(52) The term “optical properties”, as used herein, refers to the absorption spectrum of the tris-bipyridyl complex of the present invention, wherein the change in the optical properties is caused electrochemically by addition or withdrawal of one or more electrons to or from said tris-bipyridyl complex, more particularly, to or from the metal atom in the complex.
(53) The counter anion “X” in the tris-bipyridyl complexes of the present invention may be any suitable anion having a negative charge of, e.g., −1 or −2, such as Br.sup.−, Cl.sup.−, F.sup.−, I.sup.−, PF.sub.6.sup.−, BF.sub.4.sup.−, OH.sup.−, ClO.sub.4.sup.−, SO.sub.3.sup.2−, SO.sub.4.sup.2−, CF.sub.3COO.sup.−, CN.sup.−, alkylCOO.sup.−, arylCOO.sup.−, or a combination thereof. The value of “m” represents the ratio between the oxidation state of the transition metal and the valence of said anion, and may thus be, e.g., 0.5, 1, 1.5, 2, 2.5, 3, 4, 5 or 6.
(54) The term “halogen”, as used herein, includes fluoro, chloro, bromo, and iodo.
(55) The term “alkyl”, as used herein, typically means a straight or branched hydrocarbon radical having preferably 1-10 carbon atoms, and includes, e.g., methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, isopentyl, 2,2-dimethylpropyl, n-hexyl, n-heptyl, n-octyl, n-nonyl, n-decyl, and the like. The alkyl may be substituted, e.g., with one or more substituents each independently selected from halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, —N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H, wherein R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl. The term “alkylCOO” particularly refers to an alkyl group substituted by a carboxyl group on any one of its carbon atoms, e.g., CH.sub.3COO.sup.− or C.sub.2H.sub.5COO.sup.−. The term “alkylene” refers to a linear divalent hydrocarbon chain having preferably 1-10 carbon atoms and includes, e.g., methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, and the like.
(56) The terms “alkenyl” and “alkynyl” typically mean straight or branched hydrocarbon radicals having preferably 2-10 carbon atoms and at least one double or triple bond, respectively. Non-limiting examples of such alkenyls are ethenyl, propenyl, 3-buten-1-yl, 2-ethenylbutyl, 3-octen-1-yl, and the like, and propynyl, 2-butyn-1-yl, 3-pentyn-1-yl, and the like. Each one of the alkenyl and alkynyl may be substituted, e.g., with one or more substituents each independently selected from halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, —N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H, wherein R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl.
(57) The term “alkoxy” refers to the group —OR, wherein R is an alkyl group.
(58) The term “cycloalkyl” typically means a mono- or bicyclic saturated hydrocarbyl group having preferably 3-10 carbon atoms such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclodecyl, bicyclo[3.2.1]octyl, 10 bicyclo[2.2.1]heptyl, and the like. The term “heterocycloalkyl” refers to a cycloalkyl, in which at least one of the carbon atoms of the ring is replaced by a heteroatom selected from N, O or S. Each one of the cycloalkyl and heterocycloalkyl may be substituted, e.g., with one or more substituents each independently selected from halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, —N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H, wherein R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl.
(59) The term “aryl” denotes an aromatic carbocyclic group, preferably having 6-14 carbon atoms, consisting of a single ring or multiple rings either condensed or linked by a covalent bond such as, but not limited to, phenyl, naphthyl, phenanthryl, and biphenyl. The aryl group may be substituted by any known substituent. The aryl may be substituted, e.g., with one or more substituents each independently selected from halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, —N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H, wherein R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl. The term “arylCOO” refers to such a substituted aryl, in this case being substituted by a carboxylate group.
(60) The term “heteroaryl” refers to a radical derived from a mono- or polycyclic heteroaromatic ring containing one to three, preferably 1-2, heteroatoms selected from the group consisting of N, O and S. When the heteroaryl is a monocyclic ring, it is preferably a radical of a 5-6-membered ring such as, but not limited to, pyrrolyl, furyl, thienyl, thiazinyl, pyrazolyl, pyrazinyl, imidazolyl, oxazolyl, isoxazolyl, thiazolyl, isothiazolyl, pyridyl, pyrimidinyl, 1,2,3-triazinyl, 1,3,4-triazinyl, and 1,3,5-triazinyl. Polycyclic heteroaryl radicals are preferably composed of two rings such as, but not limited to, benzofuryl, isobenzofuryl, benzothienyl, indolyl, quinolinyl, isoquinolinyl, imidazo[1,2-a]pyridyl, benzimidazolyl, benzthiazolyl, benzoxazolyl, pyrido[1,2-a]pyrimidinyl and 1,3-benzodioxinyl. The heteroaryl may be substituted, e.g., with one or more substituents each independently selected from halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, —N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H, wherein R.sub.20 each independently is H, (C.sub.1-C.sub.6)alkyl or aryl. It is to be understood that when a polycyclic heteroaryl is substituted, the substitution may be in any of the carbocyclic and/or heterocyclic rings.
(61) The term “amino” refers to the group —NH.sub.2 or to substituted amino including secondary, tertiary and quaternary substitutions wherein the substituents are alkyl or aryl. The term “protected amino” refers to such groups which may be converted to the amino group.
(62) The term “carboxyl” refers to the group —COOH. The term “protected carboxyl” refers to such groups which may be converted into the carboxyl group, e.g., esters such as —COOR, wherein R is an alkyl group or an equivalent thereof, and others which may be known to a person skilled in the art of organic chemistry.
(63) The term “amino acid” as used herein refers to an organic compound comprising both amine and carboxylic acid functional groups, which may be either a natural or non-natural amino acid. The twenty two natural amino acids are aspartic acid (Asp), tyrosine (Tyr), leucine (Leu), tryptophan (Trp), arginine (Arg), valine (Val), glutamic acid (Glu), methionine (Met), phenylalanine (Phe), serine (Ser), alanine (Ala), glutamine (Gln), glycine (Gly), proline (Pro), threonine (Thr), asparagine (Asn), lysine (Lys), histidine (His), isoleucine (Ile), cysteine (Cys), selenocysteine (Sec), and pyrrolysine (Pyl). Non-limiting examples of non-natural amino acids include diaminopropionic acid (Dap), diaminobutyric acid (Dab), omithine (Orn), aminoadipic acid, β-alanine, 1-naphthylalanine, 3-(1-naphthyl)alanine, 3-(2-naphthyl)alanine, γ-aminobutiric acid (GABA), 3-(aminomethyl) benzoic acid, p-ethynyl-phenylalanine, p-propargly-oxy-phenylalanine, m-ethynyl-phenylalanine, p-bromophenylalanine, p-iodophenylalanine, p-azidophenylalanine, p-acetylphenylalanine, azidonorleucine, 6-ethynyl-tryptophan, 5-ethynyl-tryptophan, 3-(6-chloroindolyl)alanine, 3-(6-bromoindolyl)alanine, 3-(5-bromoindolyl)alanine, azidohomoalanine, p-chlorophenylalanine, α-aminocaprylic acid, O-methyl-L-tyrosine, N-acetylgalactosamine-α-threonine, and N-acetylgalactosamine-α-serine. The term “peptide” as used herein refers to a short chain of amino acid monomers linked by peptide bonds, i.e., the covalent bond formed when a carboxyl group of one amino acid reacts with an amino group of another amino acid. Particular peptides comprise 2, 3, 4, 5, 6, 7, 8 or more, preferably 3-5, amino acid monomers.
(64) In certain embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each is H. Preferred such embodiments are those wherein R.sub.1 to R.sub.18 each is H.
(65) In certain embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I, wherein A.sub.1 to A.sub.6 each independently is a pyridine moiety, i.e., a group of the formula III wherein R.sub.x is H, or a pyrimidine moiety, i.e., a group of the formula IV wherein R.sub.y is H.
(66) In certain embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I, wherein R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, preferably C—C, C═C or C≡C.
(67) In certain embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I, wherein A.sub.1 to A.sub.6 each is a pyridine moiety, i.e., a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C; or a pyrimidine moiety, i.e., a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
(68) In certain embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I as defined in any one of the embodiments above, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; R.sub.9 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N; and R.sub.20 each is H.
(69) In particular such embodiments, the tris-bipyridyl complex of the present invention is a complex of the general formula I, wherein R.sub.1 to R.sub.18 each is H; A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; and R.sub.19 each independently is C—C, C═C or C≡C. More particular such complexes are those wherein M is Fe, i.e., iron-based tris-bipyridyl complexes, most particularly wherein n is 2 or 3.
(70) In certain specific embodiments, the tris-bipyridyl complex of the invention is a complex of the general formula I, wherein M is Fe; n and m each is 2 or 3; X is PF.sub.6.sup.−; R.sub.1 to R.sub.18 each is H; A.sub.1 to A.sub.6 each independently is a group of the formula III, wherein R.sub.x is H; and (i) R.sub.19 each is C—C, i.e., [tris[4,4′-bis(2-(4-pyridyl)ethyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyridyl)ethyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 2SB(Fe.sup.2+) or 2SB(Fe.sup.3+), respectively; (ii) R.sub.19 each is C═C, i.e., [tris[4,4′-bis(2-(4-pyridyl)ethenyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyridyl)ethenyl)-2,2′-bipyridine]iron(II)] tris(hexafluoro-phosphate), herein identified complex 2DB(Fe.sup.2+) or 2DB(Fe.sup.3+), respectively; or (ii) R.sub.19 each is C≡C, i.e., [tris[4,4′-bis(2-(4-pyridyl)ethynyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyridyl)ethynyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 2TB(Fe.sup.2+) or 2TB(Fe.sup.3+), respectively (see Appendix).
(71) In other specific embodiments, the tris-bipyridyl complex of the invention is a complex of the general formula I, wherein M is Fe; n and m each is 2 or 3; X is PF.sub.6.sup.−; R.sub.1 to R.sub.18 each is H; A.sub.1 to A.sub.6 each independently is a group of the formula IV, wherein R.sub.y is H; and (i) R.sub.19 each is C—C, i.e., [tris[4,4′-bis(2-(4-pyrimidinyl)ethyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyrimidinyl)ethyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 4SB(Fe.sup.2+) or 4SB(Fe.sup.3+), respectively; (ii) R.sub.19 each is C═C, i.e., [tris[4,4′-bis(2-(4-pyrimidinyl)ethenyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyrimidinyl)ethenyl)-2,2′-bipyridine] iron(III)] tris(hexafluoro-phosphate), herein identified complex 4DB(Fe.sup.2+) or 4DB(Fe.sup.3+), respectively; or (iii) R.sub.19 each is C≡C, i.e., [tris[4,4′-bis(2-(4-pyrimidinyl)ethynyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4,4′-bis(2-(4-pyrimidinyl)ethynyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 4TB(Fe.sup.2+) or 4TB(Fe.sup.3+), respectively (see Appendix).
(72) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, preferably H, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each is H. Preferred such embodiments are those wherein R.sub.1 to R.sub.18 each is H.
(73) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein A.sub.1, A.sub.3 and A.sub.5 each independently is a pyridine moiety, i.e., a group of the formula III wherein R.sub.x is H, or a pyrimidine moiety, i.e., a group of the formula IV wherein R.sub.y is H.
(74) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N, preferably C—C, C═C or C≡C.
(75) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein A.sub.1, A.sub.3 and A.sub.5 each is a pyridine moiety, i.e., a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C; or a pyrimidine moiety, i.e., a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C.
(76) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein B.sub.1 to B.sub.3 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, preferably (C.sub.1-C.sub.4)alkyl, more preferably methyl or ethyl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each is H.
(77) In certain embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II as defined in any one of the embodiments above, wherein R.sub.1 to R.sub.18 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; R.sub.19 each independently is C—C, C═C, C≡C, N═N, C═N, N═C, C—N, N—C, —COO—, —CONH—, —CON(OH)—, —NR.sub.20—, —Si(R.sub.20).sub.2—, or an alkylene optionally interrupted by one or more heteroatoms selected from O, S or N; B.sub.1 to B.sub.3 each independently is H, halogen, —OH, —N.sub.3, —NO.sub.2, —CN, —N(R.sub.20).sub.2, —SR.sub.20, —CH═CH-pyridyl, (C.sub.1-C.sub.10)alkyl, aryl, or heteroaryl, wherein said (C.sub.1-C.sub.10)alkyl, aryl and heteroaryl may optionally be substituted with halogen, —OR.sub.20, —COR.sub.20, —COOR.sub.20, —OCOOR.sub.20, —OCON(R.sub.20).sub.2, —(C.sub.1-C.sub.8)alkylene-COOR.sub.20, —CN, N(R.sub.20).sub.2, —NO.sub.2, —SR.sub.20, —(C.sub.1-C.sub.8)alkyl, —O—(C.sub.1-C.sub.8)alkyl, —CON(R.sub.20).sub.2, or —SO.sub.3H; and R.sub.20 each is H.
(78) In particular such embodiments, the iron-based tris-bipyridyl complex of the present invention is a complex of the general formula II, wherein R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each independently is a group of the formula III, wherein R.sub.x is H, or of the formula IV, wherein R.sub.y is H; R.sub.19 each independently is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is (C.sub.1-C.sub.4)alkyl, preferably methyl or ethyl. Preferred such embodiments are those wherein n is 2 or 3.
(79) In certain specific embodiments, the iron-based tris-bipyridyl complex of the invention is a complex of the general formula II, wherein X is PF.sub.6.sup.−; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H; B.sub.1 to B.sub.3 each is methyl; and R.sub.19 each is C—C, i.e., [tris[4′-methyl-4-(2-(4-pyridyl)ethyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(4-pyridyl)ethyl)-2,2′-bipyridine] iron(III)] tris(hexafluoro-phosphate), herein identified complex 1SB(Fe.sup.2+) or 1SB(Fe.sup.3+), respectively; (ii) R.sub.19 each is C═C, i.e., [tris[4′-methyl-4-(2-(4-pyridyl)ethenyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(4-pyridyl)ethenyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 1DB(Fe.sup.2+) or 1DB(Fe.sup.3+), respectively; or (iii) R.sub.19 each is C≡C, i.e., [tris[4′-methyl-4-(2-(4-pyridyl)ethynyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(4-pyridyl)ethynyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 1TB(Fe.sup.2+) or 1TB(Fe.sup.3+), respectively (see Appendix).
(80) In other specific embodiments, the iron-based tris-bipyridyl complex of the invention is a complex of the general formula II, wherein X is PF.sub.6.sup.−; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula IV, wherein R.sub.y is H; B.sub.1 to B.sub.3 each is methyl; and R.sub.19 each is C—C, i.e., [tris[4′-methyl-4-(2-(5-pyrimidinyl)ethyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(5-pyrimidinyl) ethyl)-2,2′-bipyridine] iron(III)] tris(hexafluoro-phosphate), herein identified complex 3SB(Fe.sup.2+) or 3SB(Fe.sup.3+), respectively; (ii) R.sub.19 each is C═C, i.e., [tris[4′-methyl-4-(2-(5-pyrimidinyl)ethenyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(5-pyrimidinyl) ethenyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 3DB(Fe.sup.2+) or 3DB(Fe.sup.3+), respectively; or (iii) R.sub.19 each is C≡C, i.e., [tris[4′-methyl-4-(2-(5-pyrimidinyl)ethynyl)-2,2′-bipyridine]iron(II)] bis(hexafluoro-phosphate), or [tris[4′-methyl-4-(2-(5-pyrimidinyl) ethynyl)-2,2′-bipyridine]iron(III)] tris(hexafluoro-phosphate), herein identified complex 3TB(Fe.sup.2+) or 3TB(Fe.sup.3+), respectively (see Appendix).
(81) The complexes of the present invention, i.e., both the tris-bipyridyl complex of the general formula I and the iron-based tris-bipyridyl complex of the general formula II, can be prepared using any suitable procedure or technique known in the art, e.g., as described in Materials and Methods hereinafter for the various iron-based tris-bipyridyl complexes exemplified. This procedure may of course be extended for the preparation of any tris-bipyridyl complex of the general formula I wherein the metal atom is Fe or one of the other metal atoms represented by the group M in the general formula I.
(82) The tris-bipyridyl complex of the general formula I and the iron-based tris-bipyridyl complex of the general formula II, e.g., the complexes exemplified herein, are chiral complexes and consequently exist as enantiomers, i.e., optically pure isomers (Δ (delta) and Λ (lambda)), racemate, or a mixture wherein a certain enantiomer is enantiomerically enriched. Particular tris-bypyridyl complexes of the general formula II, e.g., complex 1DB(Fe.sup.2+), consist of facial and/or meridional isomers, depending on the ligand geometry with respect to the central metal ion, and may occur either as single isomers or as mixtures composed of any ratio of isomers. It should be understood that the present invention encompasses all such enantiomers, isomers, and mixtures thereof.
(83) Optically active forms of the tris-bipyridyl complexes of the invention may be prepared/obtained using any method known in the art. Non-limiting examples of such methods include chiral chromatography including simulated moving bed chromatography, resolution of the racemic form by recrystallization techniques, resolution using optically pure reagents which form pairs of diastereomers which can be separated by any technique known in the art, and extraction with chiral solvents. A wide variety of chiral stationary phases are commercially available.
(84) The facial and meridional isomers of the tris-bipyridyl complexes of the invention may be prepared/obtained using any method known in the art, e.g., by chemical synthesis using tethers and/or protective groups, or by chromatographic separation using suitable stationary phases (e.g., silica, alumina or sephadex), including simulated moving bed chromatography.
(85) In study 1 hereinafter, pyridine terminated template layers were generated from silane based coupling layers covalently attached to silicon, quartz and glass substrates, and subsequently, two different multi-component molecular assemblies, herein identified MA1DB and MA2DB, were constructed, layer by layer, via iterative immersion of these functionalized substrates in a 1 mM solution of PdCl.sub.2(PhCN).sub.2 in THF and 0.2 mM solution of the respective iron-based tris-bypiridyl complex 1DB(Fe.sup.2+) (for the construction of MA1DB) or 2DB(Fe.sup.2+) (for the construction of MA2DB) in CH.sub.2Cl.sub.2/MeOH (1:1, v/v) with sonication-wash cycles in between, thereby controlling the electrochemical and photophysical properties of the surface confined architectures. Introducing symmetric 4,4′-bis(vinyl pyridine) bipyridyl ligands on Fe(II), due to its steric constraints, resulted in a slower and linear growth of the assemblies, whereas the one with non-symmetric (4-methyl-4′-vinyl pyridine) bipyridyl analogue grew exponentially. The trend in growth was also reflected on their properties allowing a fine-control of thickness, optical properties, electrochemistry and chromophorism.
(86) The electrochromic behavior of the molecular assemblies was investigated by SEC, wherein the electro-optical response during the switching of potential in a stepwise manner between the oxidized (transmissive) and reduced (colored) states was recorded at the corresponding absorption maxima (λ.sub.max=575 nm for MA1DB and 591 nm for MA2DB) as percentage transmittance (% T) over time, and a superior degree of electro-optic response was evidenced for MA2DB, suggesting an enhanced electrochromic performance and efficiency (Δ% T [MA1DB.sub.8].sub.λmax=574 nm (41.3); Δ% T [MA2DB.sub.8].sub.λmax=591 nm (33.8)). In view of their vibrant switching from coloured to transmissive states, and consequently their potential for applications in ECDs, the electrochemical stability of the assemblies were followed by CV and SEC in TBAPF.sub.6-propylene carbonate electrolyte solution over time. The CV of MA2DB after every few thousands of continuous spectroelectrochemical switching cycles confirmed its ultra-high stability. No detectable decrease in the maximum current (in both oxidative and reductive directions) was observed at least until 112,000 cycles. The decrease in Δ% T was found to be negligible (compared to maximum Δ% T) after 30,000 redox cycles. MA1DB was found to electrochemically less stable compared to MA2DB. The electrochemical stability of MA2DB was further proved by repeating the same experiments (for 30,000 cycles) over 6 days with continuous exposure to UV/vis light and intentional stoppage of cycling for periods ranging from a few minutes to 10 hours, and leaving the assembly in the electrolyte solution for the whole duration. The extra stability of MA2DB over MA1DB could be justified by the larger number of binding sites; and the extended delocalization of electrons and the positive charge over a larger chain of the ligands, which in turn reduces the susceptibility of coordination based systems to dissociate, as explained by the anodic shift in the E.sub.1/2 of MA2DB.
(87) We also fabricated various gel electrolyte-based SELDs of multi-component metal-organic CPNFs capable of switching colors efficiently, with applied potential difference.
(88) One of the key parameters determining the performance and power efficiency of any ECD is its coloration efficiency (CE), which is defined as the change in optical density (ΔOD) per unit charge injected/ejected per unit area of the electrode, and calculated as:
(89)
where T.sub.colored and T.sub.bleached are the transmittance in colored (reduced) and bleached (oxidized) states, respectively, and Q.sub.d is the total injected or ejected charge per unit area.
(90) The coloration efficiency of the assemblies MA1DB and MA2DB after 8 deposition cycles were calculated at their MLCT λ.sub.max and were found to be 955 and 1488 cm.sup.2C.sup.−1, respectively, which are exceptionally high for surface confined coordination-based metal-organic assembles.
(91) In Study 2, pyridine terminated template layers were generated from silane based coupling layers covalently attached to silicon, quartz and glass substrates, and subsequently, four different multi-component MAs, herein identified MA2SB, MA2DB, MA2TB and MA2Mix, were constructed as described in Study 1, via iterative immersion of those functionalized substrates in a solution of the iron-based tris-bypiridyl complex 2SB(Fe.sup.2+) (for the construction of MA2SB); 2DB(Fe.sup.2+) (for the construction of MA2DB); 2TB(Fe.sup.2+) (for the construction of MA2TB); or an equimolar mixture of 2SB(Fe.sup.2+), 2DB(Fe.sup.2+) and 2TB(Fe.sup.2+) (for the construction of MA2Mix). Using different ligands that coordinate to the Fe centers, the electro-optical properties of the assemblies were controlled. All these assemblies grew linearly and showed electrochemical switchings between colored (reduced) and transmissive (oxidized) states upon application of the right potential. Combined effect of the ligands and experimental parameters (temperature, switching time (=pulse width), overpotential, etc.) modulates the electro-optical signature of these assemblies. The assemblies showed better optical and electrochemical responses at higher temperature (up to 50° C.) and on application of higher overpotential. Higher the temperature, smaller was the response time for all the MAs. At higher switching times (=pulse width), the MAs showed superior electro-optical response. Application of overpotential at low temperature or smaller pulse width also resulted in better spectroelectrochemical properties.
(92) In Study 3, the effect of the molecular structure of the ligands in determining the stability and coloration efficiencies of the coordination based assemblies was determined. MA2DB was found to be electrochemically the most stable in the family and exhibited the highest coloration efficiency. MA2DB was electrochemically stable at lower temperature (10° C.) and at RT, eventhough showed a slightly diminished stability at 40° C. The thermal stability of MA1DB and MA2DB was also very high as no detectable loss in the intensity of MLCT band was observed after 60 days at 70° C. The coloration efficiency for MA2DB (1488 cm.sup.2C.sup.−1) and MA1DB (955 cm.sup.2C.sup.−1) are amongst the highest reported values for such coordination based assemblies. The uniformity and color intensity of the assemblies was also found to be superlative.
(93) In a further aspect, the present invention provides a device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have a predetermined oxidation state being changeable upon subjecting said layered structure to an electric field, wherein exposure of said device to a potential change causes reversible electron transfer, which results in a change in the electrochromic properties of said layered structure with high coloration efficiency, said device having high electrochemical stability when repeatedly exposed to a potential change, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or an iron-based tris-bipyridyl complex of the general formula II as defined above. Such a device may be used, e.g., in smart windows, electrochromic window, smart mirrors, electrochromic display devices, smart paper, electrochromic goggles, electrochromic helmet, electrochromic paint, or visors.
(94) The term “high electrochemical stability”, as used herein with respect to the device of the present invention, refers to the capability of the device to retain high values of % ΔT, i.e., >90%, >95% or >97%, after at least 1,000 but preferably more than 3,000, 5,000 or 10,000, more preferably more than 20,000 or 30,000, electrochemical switching cycles as immersed in an electrolyte solution, and exposed to air and UV light over a period of a few hours to a few days.
(95) In certain embodiments, exposure of the device of the present invention to a potential change causes reversible electron transfer, which results in a change in the electrochromic properties of said layered structure with coloration efficiency higher than 500 cm.sup.2C.sup.−1, preferably higher than 600 cm.sup.2C.sup.−1, 700 cm.sup.2C.sup.−1, 800 cm.sup.2C.sup.−1, or 900 cm.sup.2C.sup.−1, more preferably higher than 1000 cm.sup.2C.sup.−1.
(96) In certain embodiments, the substrate comprised within the device of the present invention is hydrophilic, hydrophobic or a combination thereof.
(97) In certain embodiments, the substrate comprised within the device of the present invention includes a material selected from glass, a doped glass, ITO-coated glass, TCO, silicon, a doped silicon, Si(100), Si(111), SiO.sub.2, SiH, silicon carbide mirror, quartz, a metal, metal oxide, a mixture of metal and metal oxide, group IV elements, mica, a polymer such as polyacrylamide and polystyrene, a plastic, a zeolite, a clay, wood, a membrane, an optical fiber, a ceramic, a metalized ceramic, an alumina, an electrically-conductive material, a semiconductor, steel or a stainless steel. In particular such embodiments, said substrate is in the form of beads, microparticles, sub-microparticles, nanoparticles, quantum dots, metal-organic framework, or nanotubes. In more particular such embodiments, said substrate is optically transparent to the ultraviolet (UV), infrared (IR), near-IR (NIR) and/or visible spectral ranges.
(98) As stated above, the device of the present invention comprises a substrate having an electrically conductive surface and carrying a layered structure comprising at least one redox-active compound configured to have a predetermined oxidation state, wherein each redox-active compound independently a transition metal-based tris-bipyridyl complex of the general formula I or an iron-based tris-bipyridyl complex of the general formula II as defined above.
(99) In certain embodiments, the layered structure comprises (i) a monolayer of either one redox-active compound as defined above or two or more, i.e., two, three, four or more, redox-active compounds each as defined above, said redox-active compounds having identical or different metals; or (ii) a plurality of layers each comprising either one redox-active compound as defined above or two or more, i.e., two, three, four or more, redox-active compounds each as defined above, said redox-active compounds having identical or different metals. In particular such devices, said redox-active compound each independently is an iron-based tris-bipyridyl complex of the general formula I or II as defined above, wherein n is 2 or 3.
(100) In particular such embodiments, the layered structure comprises a monolayer of either one redox-active compound or two or more redox-active compounds, or a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is (i) a tris-bipyridyl complex of the general formula I as defined above, wherein M is Fe; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; and A.sub.1 to A.sub.6 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; or (ii) an iron-based tris-bipyridyl complex of the general formula II as defined above, wherein n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is methyl. In more particular such embodiments, X is PF.sub.6.sup.−.
(101) The device of the present invention, in any one of the embodiments defined above, can be used in smart windows, electrochromic windows, smart mirrors, optical filters, frequency doubling devices, optical switches, modulators, spatial light modulators, phase masks, data transfer devices, data storage devices, pulse shapers, optical processors, electrochromic display devices, smart papers, electrochromic goggles, electrochromic helmets, electrochromic paints, or visors.
(102) In particular embodiments, the device is used in smart or electrochromic windows, wherein said layered structure comprises a plurality of layers each comprising either one redox-active compound or two or more redox-active compounds, said redox-active compound each independently is (i) a tris-bipyridyl complex of the general formula I as defined above, wherein M is Fe; n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; and A.sub.1 to A.sub.6 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; or (ii) an iron-based tris-bipyridyl complex of the general formula II as defined above, wherein n and m each is 2 or 3; R.sub.1 to R.sub.18 each is H; A.sub.1, A.sub.3 and A.sub.5 each is a group of the formula III, wherein R.sub.x is H and R.sub.19 is C—C, C═C or C≡C, or a group of the formula IV, wherein R.sub.y is H and R.sub.19 is C—C, C═C or C≡C; and B.sub.1 to B.sub.3 each is methyl. In more particular such embodiments, X is PF.sub.6.sup.−.
(103) The device of the present invention, in any one of the embodiments defined above, can also be used as a memory device.
(104) In yet another aspect, the present invention thus provides a memory device comprising a substrate having an electrically conductive surface and a layered structure disposed thereon, said layered structure comprising at least one redox-active compound configured to have at least one a predetermined electronic property, including at least one of electrodensity and oxidation state, said predetermined electronic property being changeable upon subjecting said layered structure to an electric field, wherein said redox-active compound each independently is a tris-bipyridyl complex of the general formula I or an iron-based tris-bipyridyl complex of the general formula II as defined above.
(105) The term “electrodensity”, as used herein and also known as “electron density”, refers to the measure of the probability of an electron being present at a specific location.
(106) The invention will now be illustrated by the following non-limiting Examples.
Examples
(107) Materials and Methods
(108) Most reagents were purchased from Sigma Aldrich, BDH or Merck. All chemicals were used as received. Solvents (Reagent Grade) were purchased from Bio-Lab (Jerusalem), Sigma Aldrich, and Merck. Toluene was dried using an M. Braun solvent purification system and degased with argon for 30 minutes before introducing into a nitrogen filled glove box. All reaction vessels were cleaned with piranha solution (7:3 (v/v) H.sub.2SO.sub.4:30% H.sub.2O.sub.2) for 20 minutes (caution: piranha is an extremely dangerous oxidizing agent and should be handled with care using appropriate personal protection), washed with excess of water, acetone and dried for at least 5 hours in an air oven at 130° C. Monolayers were prepared and characterized as previously reported (Motiei et al., 2008) with slight changes in the cleaning procedure. Single crystal silicon (100) substrates were purchased from Wafernet (San Jose, Calif.) and were cleaned (10×20 mm) by sonication for 8 minutes each in CH.sub.2Cl.sub.2, n-hexane, acetone and ethanol followed by drying under a flow of nitrogen and subsequent treatment in a UVOCS cleaning system (Montgomery, Pa.) for 30 minutes, washings with ethanol and sonication. ITO coated glass slides (unpolished Float Glass, 7×50×0.5 mm, SiO.sub.2 passivated/ITO coated two surfaces, R.sub.s=8-12Ω) were purchased from Delta Technologies Ltd. (Loveland, Colo.) and were cleaned via exactly the same procedure as described above. Quartz slides were purchased from Chemglass Life Sciences (USA) and were cleaned by washing several times with deionized (DI) water, followed by immersion in a piranha solution (7:3 (v/v) H.sub.2SO.sub.4: 3% H.sub.2O.sub.2) for 1 hour. Thereafter, the glass substrates were rinsed with deionized water and cleaned for 1 hour using the Radio Corporation of America (RCA) cleaning protocol (1:5:1 (v/v) NH.sub.4OH:H.sub.2O:30% H.sub.2O.sub.2). Subsequently, the substrates were rinsed with ethanol, dried under a N.sub.2 flow and all the substrates (Silicon, ITO coated glass and quartz) oven dried for at least 3 hours at 130° C.
(109) UV/vis spectra were recorded at RT, unless stated otherwise, on a Cary 100 spectrophotometer in transmission mode (200-800 nm). The functionalised quartz substrates were fixed in a Teflon holder (1.5×0.75 cm window) and an identical quartz substrate without monolayer was used to compensate for the background absorption.
(110) .sup.1H, .sup.13C (.sup.1H), .sup.19F and .sup.31P NMR spectra were recorded on a Bruker 300 MHz NMR spectrometer. Atomic Force Microscope (P47 Solver AFM (NT-MDT, Zelenograd, Russia)) in intermittent contact/tapping mode, using AC240 probes (Olympus) in intermittent contact/tapping mode) was used to estimate the roughness of the MAs as well as film morphologies. Film thickness was estimated on silicon substrates using a J.A. Woollam (Lincoln, Nebr.) model M-2000 V variable angle spectroscopic ellipsometer with the VASE32 software. XRR measurements were performed at BeamlineX6B of the National Synchrotron Light Source, Brookhaven (Upton, N.Y.) using a four-circle Huber diffractometer in the specular reflection mode (i.e., incident angle I was equal to the exit angle).
(111) Electrochemical measurements, unless otherwise stated, were performed using a potentiostat (CHI660A) and a three-electrode cell configuration consisting of (a) an ITO modified substrate (working electrode), (b) Ag/Ag.sup.+ (reference electrode) and (c) a Pt wire (counter electrode), at RT using 0.1 M solution of tetrabutylammoniumhexafluoro phosphate (Bu.sub.4NPF.sub.6) in anhydrous CH.sub.3CN or propylene carbonate (H.sub.2O<0.001% v/v) (both were purchased from Sigma Aldrich).
(112) The experimental data were fitted to the expression y=y.sub.0+c.sub.1exp(c.sub.2x) or y=y.sub.0+c.sub.1exp(c.sub.2x)+c.sub.3exp(c.sub.4x), for exponential fits and y=a+bx, for linear fits, where y is the measured absorption, thickness, current, charge or intensity after x deposition steps or at a particular experimental condition, c.sub.1, c.sub.2, c.sub.3 and c.sub.4 are fitting parameters, a is a constant and b is the slope of the linear fit. Similar fitting models have earlier been used.
Synthesis of 4-[2-(4-pyridyl)ethenyl]-4′-methyl-2,2′-bipyridine (ligand L1DB)
(113) As demonstrated in Scheme 1, ligand L1DB was synthesized from 4,4′-dimethyl-2,2′-bipyridine 1 in a two-step reaction involving its deprotonation and attack on pyridine-4-carboxaldehyde, followed by dehydration (Choudhury el al., 2010). In particular, to a solution of di-isoproplylamine (2.83 ml, 20 mmol) in freshly distilled THF (10 ml) was added dropwise nBuLi (12.5 ml, 20 mmol, 1.6 M solution in hexanes) at −20° C. under an inert atmosphere. The solution was stirred for an additional 15 min, where after 4,4′-dimethyl-2,2′-bipyridine (3.7 g, 20 mmol) in 120 ml THF was added drop wise, where upon the color changed to dark red-brown. After 2 h, a solution of pyridine-4-carboxyaldehyde (1.89 ml, 20 mmol) in 15 ml THF was added which resulted in a color change from red-brown to yellow-green. The solution was stirred for 2 h at −20° C., and allowed to warm to RT overnight. The reaction was quenched with water (20 ml) and the THF evaporated under reduced pressure. The resulting solution was extracted with CH.sub.2Cl.sub.2 (3×150 ml). The organic fractions were pooled together, dried with Na.sub.2SO.sub.4 and the solvent was removed under reduced pressure to yield a crude yellow solid (5.04 g). The yellow solid was dissolved in dry pyridine (50 ml) at 0° C. and a solution of POCl.sub.3 (2.25 ml, 0.25 mmol) in 16 ml dry pyridine was added during the course of 30 min. Upon addition, the mixture turned dark red. An additional amount of POCl.sub.3 (0.75 ml) was added, and the mixture was stirred for an additional 4 hours at RT. The pyridine was removed under reduced pressure, and ice-water was added to destroy any excess of POCl.sub.3. The aqueous solution was stirred for 30 min., before the pH was adjusted to 7-8. The solution was extracted with CH.sub.2Cl.sub.2 (4×150 ml). The extracts were pooled together and dried with Na.sub.2SO.sub.4. The solvent was removed under reduced pressure and the crude product was purified by column chromatography (neutral alumina, G-II) to afford 4-[2-(4-pyridyl)-2-ethenyl]-4′-methyl-2,2′-bipyridine (L1DB) as an off white solid (4.06 g, 74%). .sup.1H NMR (400 MHz, CDCl.sub.3) δ 8.68 (d, J=5.1 Hz, 1H), 8.6 (dd, J=1.6, 4.6 Hz, 2H), 8.56-8.59 (m, 2H), 8.28 (s, 1H), 7.42 (dd, J=1.6, 4.6 Hz, 2H), 7.39 (dd, J=1.7, 5.1 Hz, 1H), 7.34 (AB ethenyl, J=16.5 Hz, 2H), 7.18 (d, J=5.0 Hz, 1H), 2.46 (s, 3H); ESI-MS 274.46 [M+H].sup.+, 296.54 [M+Na].sup.+.
Synthesis of 4,4′-bis((E)-2-(pyridin-4-yl)vinyl)-2,2′-bipyridine (ligand L2DB)
(114) Two different routes have been envisaged for the synthesis of ligand L2DB, both starting from the commercially available 4,4′-dimethyl-2,2′-bipyridine. The initial synthetic strategy consists of two steps as in the synthesis of L1DB, but with low overall yield (Choudhury et al., 2010); and the second one is a multi-step protocol with higher overall yields (Oki and Morgan, 1995; Gillaizeau-Gauthier et al., 2001; Coe et al., 2010). Route 1: Deprotonation of the methyl groups in 4,4′-dimethyl-2,2′-bipyridine 1, followed by nucleophilic attack on pyridine-4-carboxaldehyde gave the corresponding diol in 71% yield. The crude diol was then double-dehydrated using pyridine-POCl.sub.3 to yield the ligand L2DB in 6-8% overall yield. Route 2: Oxidation of the methyl groups in 4,4′-dimethyl-2,2′-bipyridine 1 using chromic acid yielded the diacid 3 in 95% yield, which was esterified and subsequently reduced to give the corresponding diol 5. The diol on reaction with HBr—H.sub.2SO.sub.4 gave the dibromide 6 in 85% yield, which on further treatment with triethyl phosphite gave the corresponding bisphosphonate 7. The addition of pyridine-4-carboxaldehyde 2 in presence of a base under anhydrous conditions yielded the ligand L2DB in near quantitative yield (overall yield 46% over 6 steps).
(115) Synthesis of Ligand L2DB According to Route 1
(116) As demonstrated in Scheme 1, to a solution of di-isoproplylamine (11.8 ml, 83.6 mmol) in freshly distilled THF (50 ml) was added dropwise nBuLi (52.2 ml, 83.6 mmol, 1.6 M solution in hexanes) at −20° C. under an inert atmosphere. The solution was stirred for an additional 15 min, where after 4,4′-dimethyl-2,2′-bipyridine (7 g, 38 mmol) in 250 ml THF was added drop wise, where upon the color changed to dark red-brown. After 2 h, a solution of pyridine-4-carboxyaldehyde 2 (7.9 ml, 83.6 mmol) in 40 ml THF was added which resulted in a color change from red-brown to yellow-green. The solution was stirred for 2 h at −20° C., and allowed to warm to RT overnight. The reaction was quenched with water (100 ml) and THF evaporated under reduced pressure. The resulting solution was extracted with CH.sub.2Cl.sub.2 (3×400 ml). The organic fractions were pooled together, dried with Na.sub.2SO.sub.4 and the solvent was removed under reduced pressure to yield a crude yellow solid (10.79 g, 71%) and was used in the next step without further purification or characterization. The yellow solid (10.79 g, 23.1 mmol) was dissolved in dry pyridine (100 ml) and a solution of POCl.sub.3 (7.6 ml, 81.2 mmol) in 40 ml dry pyridine was added during the course of 30 min. Upon addition, the mixture turned dark red. An additional amount of POCl.sub.3 (2.5 ml, 27.1 mmol) was added, and the mixture was stirred for another 4 hours. Pyridine was removed under reduced pressure, and ice was added to quench excess POCl.sub.3. The aqueous solution was stirred for 30 min., before the pH was adjusted to 7-8 using NaOH. The solution was extracted with CH.sub.2Cl.sub.2 (4×250 ml). The extracts were pooled together and dried with Na.sub.2SO.sub.4. The solvent was removed under reduced pressure and the crude product was purified by column chromatography (3-5% MeOH/CHCl.sub.3+0.5% Et.sub.3N as eluent) to afford L2DB as an off white solid (1.01 g, 12%). .sup.1H NMR (CDCl.sub.3) δ: 8.72 (2H, d, J=5.1 Hz), 8.64 (4H, d, J=6.1 Hz), 8.60 (s, 2H), 7.45-7.41 (6H, m), 7.39 (2H, d, J=16.5 Hz), 7.32 (2H, d, J=16.4 Hz). ESI-MS 363.13 [M+H].sup.+, 385.13 [M+Na].sup.+, 747.07 [2M+Na].sup.+ (For complete data, see Coe et al., 2010).
(117) Synthesis of Ligand L2DB According to Route 2
(118) As demonstrated in Scheme 2, to a stirred solution of 4,4′-dimethyl-2,2′-bipyridine 1 (10 g, 41 mmol) in sulfuric acid (95-98%, 250 ml) at 0° C. was added potassium dichromate (48 g, 163 mmol) in small portions over 20 min. The inside temperature of the mixture was maintained at 70-80° C. by occasional cooling using ice/water bath. The resultant mixture was stirred at RT until the inside temperature fell below 40° C. (3-4 h) while the color turned deep green. The reaction mixture was poured into ice, filtered and washed with cold water until the filtrate became colorless. The solid was dried, refluxed in 50% HNO.sub.3 for 4 h and the solution was poured over ice and diluted with water (2 l). The aqueous mixture was cooled to <5° C. and the precipitate was filtered, washed with water (4×100 ml), acetone (3×30 ml) and dried to give [2,2′-bipyridine]-4,4′-dicarboxylic acid 3 as an off-white solid (9.51 g, 95%). The crude product obtained was used in the next step without further characterization or purification.
(119) To a suspension of the diacid 3 (9.51 g, 39 mmol) in 1 l of absolute ethanol was added concentrated sulfuric acid (20 ml, 95-98%). The suspension was kept under reflux for 2 days to obtain a clear solution and then cooled to RT. The mixture was poured into ice was added and excess ethanol removed under vacuum. The pH was adjusted to neutral with 2M NaOH solution, and the resulting precipitate was filtered, washed with water (5×200 ml) and dried to obtain the diester diethyl [2,2′-bipyridine]-4,4′-dicarboxylate 4 as a yellowish-white solid (10.41 g, 89%). .sup.1H NMR (300 MHz, CDCl.sub.3) δ 8.98-8.92 (m, 2H), 8.87 (d, J=4.9 Hz, 2H), 7.91 (dd, J=5.0, 1.6 Hz, 2H), 4.45 (q, J=7.1 Hz, 4H), 1.44 (t, J=7.1 Hz, 6H). .sup.13C NMR (75 MHz, CDCl.sub.3) δ 165.4, 156.7, 150.4, 139.4, 123.7, 121.0, 62.3, 14.6. ESI-MS 301.11 [M+H].sup.+, 323.11 [M+Na].sup.+, 623.14 [2M+Na].sup.+.
(120) To a suspension of the diester 4 (10.0 g, 33.3 mmol) in 300 ml of absolute ethanol was added sodium borohydride (25.19 g, 665.9 mmol) in one portion. The mixture was refluxed for 3 h and cooled to RT, and excess borohydride was decomposed by the dropwise addition saturated ammonium chloride solution (300 ml). Ethanol was removed under vacuum and the precipitated solid was filtered and the solid was dissolved in ethyl acetate (400 ml), washed with water (100 ml), dried over anhy. Na.sub.2SO.sub.4 and the solvent was removed under vacuum to yield the diol [2,2′-bipyridine]-4,4′-diyldimethanol 5 as a white powder (5.9 g, 82%). .sup.1H NMR (300 MHz, CD.sub.3OD) δ 8.63-8.56 (m, 2H), 8.30-8.21 (m, 2H), 7.53-7.38 (m, 2H), 4.76 (s, 4H). .sup.13C NMR (75 MHz, CD.sub.3OD) δ 157.2, 154.3, 150.2, 122.7, 120.2, 63.6. ESI-MS 217.08 [M+H].sup.+, 239.02 [M+Na].sup.+, 455.20 [2M+Na].sup.+.
(121) A solution of the diol 5 (10.0 g, 46.2 mmol) in a mixture of HBr (48%, 200 ml) and concentrated H.sub.2SO.sub.4 (95-98%, 67 ml) was refluxed for 6 h and then allowed to cool to RT. Water (400 ml) was then added to the mixture and the pH was adjusted to neutral with 2M NaOH solution. The resulting precipitate filtered, washed with water (4×100 ml), and dried. The solid was dissolved in chloroform (200 ml) and filtered. The solution was dried over anhy. Na.sub.2SO.sub.4 and the solvent was removed under vacuum, yielding the dibromide 4,4′-bis(bromomethyl)-2,2′-bipyridine 6 (13.5 g, 85.4%) as an off-white powder. .sup.1H NMR (300 MHz, CDCl.sub.3) δ 8.72 (d, J=5.1 Hz, 2H), 8.58 (s, 2H), 7.47 (d, J=5.1 Hz, 2H), 4.52 (s, 4H). .sup.13C NMR (75 MHz, CDCl.sub.3) δ 154.2, 149.2, 149.0, 124.8, 122.2, 30.4. ESI-MS 342.90 [M+H].sup.+, 364.84 [M+Na].sup.+, 706.63 [2M+Na].sup.+.
(122) To a solution of the dibromide 6 (12.0 g, 35.1 mmol) in dry chloroform (100 ml) was added triethyl phosphite (100 ml) and the resulting mixture was refluxed for 3 h under nitrogen. The excess phosphite was removed under high vacuum, and the remaining solid was purified by flash chromatography (Silica gel, 4-8% MeOH/CHCl.sub.3 as eluent) yielding the bisphosphonate tetraethyl ([2,2′-bipyridine]-4,4′-diylbis(methylene))bis(phosphonate) 7 as a yellowish-white solid (13.0 g, 81%). .sup.1H NMR (300 MHz, CDCl.sub.3) δ 8.60 (d, J=5.1 Hz, 2H), 8.38 (s, 2H), 7.37-7.32 (m, 2H), 4.05 (dq, J=14.2, 7.1 Hz, 8H), 3.23 (d, J=22.3 Hz, 4H), 1.24 (t, J=7.1 Hz, 12H). .sup.13C NMR (75 MHz, CDCl.sub.3) δ 154.9, 148.8, 143.4, 125.5, 125.4, 123.1, 123.0, 62.6, 62.53, 34.7, 32.8, 16.5, 16.4. .sup.31P NMR (121 MHz, CDCl.sub.3) δ 25.40. ESI-MS 457.10 [M+H].sup.+, 479.04 [M+Na].sup.+, 935.07 [2M+Na].sup.+, 1391.10 [3M+Na].sup.+, 455.20 [M−H].sup.−.
(123) To a stirred solution of the bisphosphonate 7 (11.8 g, 25.8 mmol) in dry THF (400 ml) under N.sub.2, potassium tert-butoxide (7.25 g, 64.6 mmol) was added, followed by pyridine-4-carboxaldehyde (5.5 ml, 58.2 mmol). The mixture was stirred in the dark at RT for 3 h. after which triple distilled water (400 ml) was added, and was stirred for another 2 min. The solid was filtered off, washed with water (5×100 ml) and diethyl ether (3×50 ml), and dried under vacuum to give ligand L1DB (9.0 g, 96%) as an off-white solid. .sup.1H NMR (300 MHz, CD.sub.3OD) δ 8.71-8.67 (m, 2H), 8.56 (dd, J=4.7, 1.6 Hz, 4H), 8.54 (d, J=0.9 Hz, 2H), 7.59 (dd, J=4.8, 1.6 Hz, 4H), 7.52 (dd, J=5.2, 1.7 Hz, 2H), 7.44 (s, 4H). .sup.13C NMR (75 MHz, CD.sub.3OD) δ 156.2, 149.9, 148.7, 146.0, 145.2, 132.3, 130.8, 122.4, 122.3, 119.4. ESI-MS 363.13 [M+H].sup.+, 385.13 [M+Na].sup.+, 747.07 [2M+Na].sup.+.
(124) Synthesis of Ligand L2SB and L2TB
(125) The synthesis of ligands L2SB and L2TB was carried out as demonstrated in Scheme 3, starting from ligand L2DB and based on the procedure for the synthesis of 1,2-bis(4-pyridyl)acetylene (Nugent et al., 2013).
(126) To a solution of L2DB (1.0 g, 2.76 mmol) in MeOH—AcOEt (1:1 v/v, 15 ml) inside a Fisher-Porter tube, was added 5 wt % Pd—C (50 mg). The resulting mixture was stirred under H.sub.2 (8 bar) for 12 h. with the exclusion of light. The mixture was then filtered over celite, and washed with MeOH—AcOEt (1:1 v/v, 15 ml). The filtrate was evaporated under reduced pressure to obtain L2SB as an off-while solid (990 mg, 98%). .sup.1H NMR (300 MHz, CDCl.sub.3) δ 8.47 (d, J=5.0 Hz, 2H), 8.36 (dd, J=4.7, 1.2 Hz, 4H), 8.14 (s br, 2H), 7.20-7.07 (m, 4H), 7.06 (dd, J=5.0, 1.5 Hz, 2H), 2.98 (s, 8H). .sup.13C NMR (75 MHz, CDCl.sub.3) δ 155.9, 151.0, 150.6, 149.1, 149.0, 124.2, 124.1, 121.4, 35.8, 35.6. ESI MS 367.18 [M+H], 389.19 [M+Na], 755.25 [2M+Na].
(127) To a stirred solution of L2DB (1.0 g, 2.76 mmol) in HBr (48%, 15 ml) at 0° C., Br.sub.2 (1.05 ml, 19.3 mmol) was added dropwise. The mixture was then heated to 120° C. and stirred for 2 hours. Subsequent cooling to room temperature yielded a dark orange precipitate. After chilling in an ice-acetone bath for 1 h, the solid was filtered, washed with water (3×50 ml). An aqueous solution of NaOH (2 M, 50 ml) was added to the solid and was stirred for 30 min. The resulting off-white solid was filtered, washed with water (3×100 ml), and dried under vacuum for 24 hours to give the dibromo adduct 8 (1.6 g, 85%). .sup.1H NMR (300 MHz, DMSO) δ 8.87 (d, J=5.1 Hz, 2H), 8.78-8.71 (m, 6H), 7.83 (d, J=6.2 Hz, 6H), 6.39 (dd, J=28.4, 11.9 Hz, 4H). .sup.13C NMR (75 MHz, DMSO) δ 155.5, 150.2, 150.0, 149.6, 123.5, 123.4, 123.1, 119.9, 51.1, 51.0. MS (Maldi-TOF) 683.2 [M+H], 682.21 [M], 599.25, 601.26, 603.26, 605.27, 606.27, 609.31 [M-Br], 517.14, 520.17, 521.17, 523.33, 525.33, 526.34, 527.34, 529.37, 532.39 [M-2Br].
(128) Finely cut pieces of Na (454 mg, 19.7 mmol) was added t-BuOH (20 ml, dried over 4 Å molecular sieves for 3 days) and was heated to 80° C. under nitrogen for 24 h until complete dissolution. The dibromo adduct obtained above (897 mg, 1.3 mmol) was added in four portions over 15 min and the mixture was stirred at 80° C. for 6 hrs. The mixture was then allowed to cool to RT and dry EtOH (10 ml) was added dropwise, followed by water (10 ml, caution: any left-over sodium can react violently with water) using a dropping funnel. The resultant mixture was extracted with CHCl.sub.3 (50 ml) until the extracts became colorless (6×). The combined extracts were dried over Na.sub.2SO.sub.4 and then evaporated under reduced pressure. The light brown solid was dissolved in CH.sub.2Cl.sub.2 (10 ml) and Et.sub.3N (300 □l) was added and evaporated to dryness to obtain L2DB as an off-white solid (300 mg, 64%). .sup.1H NMR (400 MHz, CDCl.sub.3+MeOD) δ 8.67 (dd, J=5.0, 0.7 Hz, 2H), 8.55 (dd, J=4.5, 1.6 Hz, 4H), 8.48 (dd, 0.1=1.3, 0.8 Hz, 2H), 7.45-7.40 (m, 6H). .sup.13C NMR (101 MHz, CDCl.sub.3+MeOD) δ 155.6, 149.8, 149.5, 131.5, 130.9, 126.0, 125.9, 123.6, 91.2, 90.7. ESI-MS 359.13 [M+H], 381.14 [M+Na], 739.15 [2M+Na].
(129) Synthesis of Iron Polypyridyl Complexes 1DB(Fe.sup.2−), 2DB(Fe.sup.2+), 2SB(Fe.sup.2+) and 2TB(Fe.sup.2+)
(130) To a solution of FeCl.sub.2.4H.sub.2O (1.1 equiv., 0.36 mmol) in MeOH (10 ml) was added a solution of the corresponding ligand L1DB, L2DB, L2SB or L2TB (3 equiv., 0.98 mmol) in MeOH (10 ml). The solution was then stirred for 30 minutes, with occasional warming to 50° C. (every 10 minutes) and filtered. The filtrate was then concentrated to half its initial volume and an aqueous solution (50 ml) of NH.sub.4PF.sub.6 (320 mg, 1.96 mmol, 6 equiv.) was added. The precipitate was filtered and washed with water (3×25 ml) and ether (25 ml), and was dried to obtain the corresponding Fe complex as its PF.sub.6 salt in near quantitative yield. Complex 1DB(Fe.sup.2+) ([Fe(L1DB).sub.3](PF.sub.6).sub.2): .sup.1H NMR (400 MHz, (CD.sub.3).sub.2CO) δ 9.09 (t, J=4.1 Hz, 1H), 8.82 (br s, 1H), 8.67-8.62 (m, 2H), 7.86 (dd, J=12.8, 5.8 Hz, 1H), 7.81 (d, J=4.4 Hz, 1H), 7.77-7.68 (m, 3H), 7.64-7.60 (m, 2H), 7.47 (br d, J=4.9 Hz, 1H), 2.64 (d, J=4.5 Hz, 3H); ESI/MS: 1020.44 [MPF.sub.6].sup.+, 144.71 (PF.sub.6.sup.−). Elemental Analysis: Calc. C, 52.40; H, 4.32; N, 10.18. Found C, 51.81; H, 3.98; N, 10.20. Complex 2DB(Fe.sup.2+) ([Fe(L2DB).sub.3](PF.sub.6).sub.2): .sup.1H NMR (400 MHz, MeOD+CD.sub.2Cl.sub.2) δ 8.97 (s, 2H), 8.52 (d, J=5.7 Hz, 4H), 7.71 (d, 0.1=16.4 Hz, 2H), 7.61-7.58 (m, 6H), 7.53 (d, J=16.5 Hz, 2H), 7.45 (d, J=6.1 Hz, 2H). .sup.13C NMR (101 MHz, MeOD+CD.sub.2Cl.sub.2) δ 160.1, 154.2, 150.3, 147.7, 144.5, 134.9, 129.4, 125.6, 122.6, 122.1. .sup.19F{.sup.1H} NMR (282 MHz, CDCl.sub.3+MeOD) δ −76.09 (d, 0.1=710.3 Hz); ESI/MS: 1143.52 [M-2PF.sub.6+H].sup.+, 144.90 [PF.sub.6]. Complex 2SB(Fe.sup.2+) ([Fe(L2SB).sub.3](PF.sub.6).sub.2): .sup.1H NMR (400 MHz, MeOD+CD.sub.2Cl.sub.2) δ 8.42 (d, 0.1=1.0 Hz, 2H), 8.34 (dd, J=4.5, 1.5 Hz, 4H), 7.23 (dd, J=4.7, 1.4 Hz, 6H), 7.10 (d, 0.1=5.9 Hz, 2H), 3.17-3.13 (m, 4H), 3.07-3.03 (m, 4H). .sup.13C NMR (101 MHz, MeOD+CD.sub.2Cl.sub.2) δ 159.6, 154.5, 153.7, 151.3, 149.6, 128.4, 125.0, 124.9, 35.9, 35.4. .sup.19F NMR (282 MHz, MeOD) δ −73.59 (d, J=710.8 Hz). ESI MS 577.62 [M-2PF.sub.6].sup.2+, 1299.6 [M-PF.sub.6], 1154.73 [M-2PF.sub.6], 144.90 [PF.sub.6]. Complex 2TB(Fe.sup.2+) ([Fe(L2TB).sub.3](PF.sub.6).sub.2): 1H NMR (400 MHz, MeOD+CD.sub.2Cl.sub.2) δ 8.85 (d, J=1.1 Hz, 2H), 8.59 (dd, J=4.6, 1.6 Hz, 4H), 7.61 (dd, J=6.0, 1.6 Hz, 2H), 7.54 (dd, J=4.5, 1.7 Hz, 4H), 7.50 (d, 1=5.8 Hz, 2H). .sup.13C NMR (101 MHz, MeOD+CD.sub.2Cl.sub.2) δ 158.9, 154.57, 150.1, 134.3, 130.3, 130.2, 126.7, 126.6, 96.2, 89.1. .sup.19F NMR (282 MHz, MeOD+CD.sub.2Cl.sub.2) δ −74.12 (d, J=710.2 Hz). ESI MS 565.32 [M-2PF.sub.6].sup.2+, 1275.96 [M-PF.sub.6], 144.84 [PF.sub.6].
(131) A complex similar to complex 2DB(Fe.sup.2+), in which each one of the nitrogen atoms of the six terminal pyridine groups (each represented by the group A in the general formula I) is substituted by methyl ([FeII(Me.sub.2bbpe.sub.2.sup.+).sub.3][PF.sub.6].sub.8), has already been disclosed (Coe et al., 2010). According to Coe et al., FeII(BF.sub.4).sub.2.6H.sub.2O was added to a solution of [Me.sub.2bbpe.sub.2.sup.+]-[PF.sub.6].sub.2.0.8H.sub.2O in DMF (10 ml), and the deep blue solution was stirred at RT for 2 hours in the dark. Addition of aqueous NH.sub.4PF.sub.6 afforded a dark blue precipitate, which was filtered off, washed with water, and dried. Purification was effected by column chromatography to afford a dark blue solid.
(132) Nevertheless, complexes as disclosed in Coe et al. are completely different both in structure and electronic, optical and electrochemical properties from the complex of the formula I. In particular, while the complex reported in Coe et al. consists of six pyridinium salts, wherein the overall charge of the complex is 8.sup.+, the tris-bypiridyl complex of the general formula I has free pyridine (or pyrimidine) groups, wherein the overall charge is 2.sup.+. Moreover, a complex as described in Coe et al. cannot form a network structure as it has no free binding sites for metal salts.
(133) Furthermore, prima facie, it seems that a tris-bypiridyl complex of the general formula I such as complex 2DB(Fe.sup.2+) cannot even be synthesized according to the procedure of Coe et al., considering that this complex is not very stable in DMF and some sort of ligand exchange may occur if left in DMF for some time. Moreover, while the complex of Coe et al. should be purified by column chromatography, the procedure described herein for the synthesis of a complex of the general formula I gives the product instantaneously, wherein the yield is quantitative and no further purification is required.
(134) Single Electrochrome Laminated Devices (SELD)
(135) Preparation of the gel electrolyte. Polymethylmethacrylate (PMMA, 700 mg), trifluoromethylsulfonamide lithium salt (300 mg), acetonitrile (dry, 7 g, ˜8.9 ml) and propylene carbonate (dry, 2 g, 1.7 ml), in a weight percentage composition of 70:20:7:3, were added to an oven-dried glass vessel under inert atmosphere and stirred vigorously for 12 hours, giving a homogeneous casting electrolyte solution.
(136) Device Fabrication and Measurements.
(137) The modified ITO substrate was cleaned by rinsing in ethanol and drying under a flow of nitrogen. The electrolyte solution was then carefully drop-casted on to the corresponding modified ITO substrate and was kept in an air oven at 55° C. for 10 minutes. This ITO substrate was placed on top of a clean bare ITO coated glass substrate in such a way that the gel electrolyte was sandwiched between the substrates and was held tight with an insulating 2-sided sticking tape at each ends (to prevent short circuits as well as to hold the setup together). The ends were then connected to a potentiostat and the electrochromic property of the solid-state set-up was studied.
(138) Study 1. Molecular Assemblies Based on Complexes 1DB(Fe.sup.2+) and 2DB(Fe.sup.2+), and their Electrochromic Behavior
(139) Pyridine terminated template layers (TLs) were generated from silane based coupling layers (CLs) covalently attached to silicon, quartz and glass substrates (
(140) The characteristic MLCT band of MA1DB and MA2DB at λ=574 nm and 591 nm, respectively (see
(141) A linear correlation between the film thickness and absorption intensities (R.sup.2>0.99) confirms the formation of thin films with uniform composition irrespective of the substrate used (
(142) TABLE-US-00001 TABLE 1 Root mean square roughness of the MAs measured using AFM Roughness (nm) Deposition cycle MA1DB MA2DB 2 0.4 0.4 4 0.6 0.4 6 0.7 0.4 8 0.9 0.5
(143) The observed trends in growth of the assemblies are consistent with those reported in Moieti et al. (2008) on the exponential growth of the SPMAs, resulting from the porous nature of the assemblies capable of trapping excess Pd salt, which could later be used for subsequent coordination with more metal complex, via migration to the solid-solution interface. For a fully formed network, in which Pd bridges all the pyridines of one metal complex to another, the expected Pd/Fe ratio is 1.5 for MA1DB and 3 for MA2DB, and a reasonably higher ratio could be ascribed to a faster, non-linear growth of the assemblies using the trapped excess Pd via a diffusion controlled mechanism as described above. XPS analysis of our assemblies confirmed the Pd/Fe ratio in MA1DB was ˜2.6 (>73% excess Pd) and that in MA2DB was 3.6-3.7 (˜20% excess Pd) after 3-5 deposition cycles, which justifies the faster growth of the former compared to the slower growth of latter. This effect could presumably be due to the structural features of the complexes 1DB(Fe.sup.2+) and 2DB(Fe.sup.2+)—and clearly, sterically more demanding 2DB(Fe.sup.2+) allows a little excess of Pd to be trapped, moreover, its migration back to the surface would also be hindered.
(144) As previously reported, multicomponent assemblies constructed from pyridine based complexes of ruthenium and osmium, and PdCl.sub.2 are redox active (Motiei et al., 2008; de Ruiter et al., 2013a; de Ruiter et al., 2013b). Reversible redox processes characteristic of Fe.sup.2+/3+ couple was revealed by CV measurements of MA1DB and MA2DB on ITO coated glass. The half wave potentials (E.sub.1/2, Vs Ag/Ag.sup.+) of 0.958 V and 1.079 V respectively at a scan rate of 100 mVs.sup.−1. This anodic shift of E.sub.1/2 by 121 mV in MA2DB could obviously be attributed to the comparably higher electron delocalization in the bipyridine derived ligands due to extended conjugation. The peak current and total charge (obtained by the integration of the voltammetric peaks) increase exponentially with increasing deposition cycles for MA1DB and linearly for MA2DB (
(145) This single electron oxidation/reduction process is accompanied by a reversible change in color of the molecular assemblies assigning them with electrochromic properties. For instance, MA1DB (Fe.sup.2+) is purple and MA2DB (Fe.sup.2+) is grey-blue, which on oxidation (Fe.sup.3+) turns more or less transmissive due to the bleaching of the MLCT bands (
(146) The electrochromic behavior of the assemblies was investigated by SEC using a square wave potential step method involving chronoamperometry coupled to optical spectroscopy. The optical response during the switching of potential in a stepwise manner between the oxidized (transmissive) and reduced (colored) states was recorded at the corresponding absorption maxima (λ.sub.max=575 nm for MA1DB and 591 nm for MA2DB) as percentage transmittance (Δ% T) over time, with the active area of the assemblies on the substrate fixed at 3.36 cm.sup.2. The Δ% T at a pulse width of 5 sec. was found to be larger for MA2DB compared to MA1DB for films of ˜17 nm thickness (5 deposition cycles), even though the total injected charge for the same films were found to be higher for MA1DB. In fact, a superior degree of electro-optic response was evidenced for MA2DB compared to their MA1DB counterparts, suggesting an enhanced electrochromic performance and efficiency (Δ% T [MA1DB.sub.8].sub.λmax=574 nm (41.3); Δ% T [MA2DB.sub.8].sub.λmax=591 nm (33.8)).
(147) Benefiting from their vibrant switching from coloured to transmissive states, these solution processable, electrochemically active molecular assemblies imply themselves as promising candidates for applications in ECDs. Nonetheless, coordination based molecular assemblies immobilised on surfaces do come with a stability concern and rational device design demands a judicious combination of both performance and robustness.
(148) The electrochemical stability of the assemblies was followed by CV and SEC in TBAPF.sub.6-propylene carbonate electrolyte solution over time. The CV of MA2DB after every few thousands of continuous spectroelectrochemical switching cycles confirmed its ultra-high stability. No detectable decrease in the maximum current (in both oxidative and reductive directions) was observed aleaset until 112,000 cycles (
(149) The electrochemical stability of MA2DB was also proved by repeating the same experiments (for 30,000 cycles) over 6 days with continuous exposure to UV/vis light and intentional stoppage of cycling for periods ranging from a few minutes to 10 hours, and leaving the assembly in the electrolyte solution for the whole duration. Thereafter, analysis of the electrolyte solution showed presence of traces of complex 2DB(Fe.sup.2+) with no free ligand or Fe salt in the detection limits (
(150) MA1DB and MA2DB were confirmed to have excellent switching efficiencies as the assemblies switched at a pulse width ranging from 0.1 s to 10 s (
(151) One of the key parameters determining the performance and power efficiency of any ECD is its coloration efficiency (CE), which is defined as the change in optical density (ΔOD) per unit charge injected/ejected per unit area of the electrode and was calculated as described above. The CEs of the assemblies MA1DB and MA2DB after 8 deposition cycles were calculated at their MLCT λ.sub.max and were found to be 955 and 1488 cm.sup.2C.sup.−1, respectively (
(152) Electrochromic devices in solid state has attracted tremendous attention due to their intended applications and long term stability and we fabricated one of the first SELD of its kind using our molecular assemblies (
(153) In a further experiment the versatility of the SELD set-up was illustrated using the electrolyte systems (a) MeCN:PC:PMMA:(CF.sub.3SO.sub.2).sub.2N.sup.−Li.sup.+ 70:20:7:3 wt % composition; (b) MeCN:PC:PMMA:Bu.sub.4N.sup.+PF.sub.6.sup.− 70:20:7:3 wt % composition; and (c) MeCN:PC:PMMA:Bu.sub.4N.sup.+BPh.sub.4.sup.− 70:20:7:3 wt % composition. The switching was found to be efficient in the different electrolytes, wherein the Bu.sub.4N.sup.+PF.sub.6.sup.− system being the most promising.
(154) Study 2. Modulation of Electrochemical and Electro-Optical Signatures of MA2SB, MA2DB, MA2TB and MA2Mix
(155) In this study, pyridine terminated template layers were generated from silane based coupling layers covalently attached to silicon, quartz and glass substrates via a slight modification of the procedure previously reported (Motiei et al., 2008). Subsequently, four different multi-component MAs, herein identified MA2SB, MA2DB, MA2TB and MA2Mix, were constructed as described in Study 1, via iterative immersion of these functionalized substrates in a solution of the iron polypyridyl complex 2SB(Fe.sup.2+) (for the construction of MA2SB); 2DB(Fe.sup.2+) (for the construction of MA2DB); 2TB(Fe.sup.2+) (for the construction of MA2TB); or an equimolar mixture of 2SB(Fe.sup.2+), 2DB(Fe.sup.2+) and 2TB(Fe.sup.2+) (for the construction of MA2Mix). Using different ligands that coordinate to the Fe centers, the electro-optical properties of the assemblies were controlled.
(156) All these assemblies grew linearly and showed electrochemical switchings between colored (reduced) and transmissive (oxidized) states upon application of the right potential. Combined effect of the ligands and experimental parameters (temperature, switching time (=pulse width), overpotential, etc.) modulates the electro-optical signature of these assemblies. The assemblies showed better optical and electrochemical responses at higher temperature (up to 50° C.,
(157) Study 3. Stability and Coloration Efficiency of MA2DB Based Electrochromics
(158) In this study, the effect of the molecular structure of the ligands in determining the stability and coloration efficiencies of the coordination based assemblies was determined. MA2DB was found to be electrochemically the most stable (
APPENDIX
(159) ##STR00008##
(160) ##STR00009##
(161) ##STR00010##
Structures: Specific Complexes of the General Formulas I and II
(162) TABLE-US-00002
REFERENCES
(163) Choudhury, J., Kaminker, R., Motiei, L., de Ruiter, G., Morozov, M., Lupo, F., Gulino, A., van der Boom, M. E., J. Am. Chem. Soc., 2010, 132, 9295-9297 Coe, B. J., Fielden, J., Foxon, S. P., Brunschwig, B. S., Asselberghs, I., Clays, K., Samoc, A. Samoc, M., J. Am. Chem. Soc., 2010, 132, 3496-3513 de Ruiter, G., Lahav, M., Keisar, H., van der Boom, M. E., Angew. Chem., Int. Ed., 2013a, 52, 704-709 de Ruiter, G., Lahav, M., Evmenenko, G., Dutta, P., Cristaldi, D. A., Gulino, A., van der Boom, M. E., J. Am. Chem. Soc., 2013b, 135, 16533-16544 Gillaizeau-Gauthier, I., Odobel, F., Alebbi, M., Argazzi, R., Costa, E., Bignozzi, C. A., Qu, P., Meyer, G. J., Inorg. Chem., 2001, 40, 6073-6079 Motiei, L., Altman, M., Gupta, T., Lupo, F., Gulino, A., Evmenenko, G., Dutta, P., van der Boom, M. E., J. Am. Chem. Soc., 2008, 130, 8913-8915 Nugent, P., Belmabkhout, Y., Burd, S. D., Cairns, A. J., Luebke, R., Forrest, K., Pham. T., Ma. S., Space, B., Wojtas, L., Eddaoudi, M., Zaworotko, M. J., Nature, 2013, 495, 80-84 Oki, A. R., Morgan, R. J., Synthetic Commun., 1995, 25, 4093-4097