Electrolytic solution and method for surface treatment of aluminum alloys for casting

Abstract

A method for surface treatment of aluminum alloys for forms an oxidation film in the aluminum alloys for casting by adding a metallic anion compound to an electrolytic solution. The method can prevent cracks from occurring on a surface of the aluminum alloys for casting at the time of applying an anodizing method.

Claims

1. A method for surface treatment of aluminum alloys for casting, comprising: forming an oxidation film in the aluminum alloys for casting by adding a metallic anion compound to an electrolytic solution, wherein the electrolytic solution is prepared using any one material selected from sulfuric acid and oxalic acid as a base, and wherein the metallic anion compound is NaAlO.sub.2.

2. The method of claim 1, wherein the aluminum alloys for casting includes Si ranging from 4.0 to 24.0 wt %, and the oxidation film has a thickness which is set to be equal to or more than 5 μm.

3. The method of claim 2, comprising steps of: coupling anions of the metallic anion compound included in the electrolytic solution with cracks formed on a surface of the aluminum alloys for casting by controlling a range of voltage, current, time, and temperature.

4. The method of claim 3, wherein the voltage is controlled to be within a range of 10 to 200 V, the current is controlled to be within a range of 0.2 to 10 A/cm.sup.2, and the time is controlled to be within a range of 1 to 24 h, and the metallic anion compound is added within a range of 0.02 to 0.4 M.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a diagram illustrating a process of forming cracks on a surface of an oxidation film by forming and island by lumps of Si during a conventional anodizing process.

(2) FIG. 2 is a diagram illustrating a surface treatment mechanism of aluminum alloys for casting in accordance with an exemplary embodiment of the present inventive concept.

(3) FIG. 3 is a diagram illustrating a crack prevention mechanism of aluminum alloys for casting to which a treatment method in accordance with an exemplary embodiment of the present inventive concept is applied.

(4) FIGS. 4A to 4D are photographs illustrating results obtained by observing a surface of aluminum alloy ingots ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 2 hours using an electron microscope.

(5) FIGS. 5A to 5D are photographs illustrating results obtained by observing a surface of ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 3 hours using an electron microscope.

(6) FIGS. 6A to 6D are photographs illustrating results obtained by observing a surface of ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 4 hours using an electron microscope.

(7) FIGS. 7A to 7C are diagrams illustrating anodizing film hardness of a surface of ADC12 alloy.

(8) FIG. 8 is a graph illustrating a polarization curve of ADC12 which is anodized for (a) 2 hours, (b) 3 hours, and (c) 4 hours using H.sub.2SO.sub.4 and H.sub.2SO.sub.4+0.2M NaAlO.sub.2.

DETAILED DESCRIPTION

(9) Hereinafter, an electrolytic solution and a method for surface treatment of aluminum alloys for casting in accordance with exemplary embodiments of the present inventive concept will be described with reference to the accompanying drawings.

(10) An electrolytic solution for surface treatment of aluminum alloys for casting in accordance with an exemplary embodiment of the present inventive concept is obtained by adding any one metallic anion compound selected from the group consisting of NaMoO.sub.4, Na.sub.2Ti.sub.3O.sub.7, and NaAlO.sub.2 to any one selected from a sulfuric acid solution and an oxalic acid solution to form an oxidizing film on a surface of aluminum alloys for casting including Si of 4.0 to 24.0 wt %.

(11) It is possible to prevent cracks from occurring at the time of anodizing the aluminum alloys for high Si casting by the surface treatment of the aluminum alloys for casting using the electrolytic solution, in which the Si ranges from 4.0 to 24.0 wt %.

(12) The method for surface treatment of the aluminum alloys for casting in accordance with the exemplary embodiment of the present inventive concept includes preparing an electrolytic solution by selecting any one of sulfuric acid and oxalic acid. Any one metallic anion compound selected from the group consisting of NaMoO.sub.4, Na.sub.2Ti.sub.3O.sub.7, and NaAlO.sub.2 is selected and the selected metallic anion compound is added to the electrolytic solution. Anions of the metallic anion compounds included in the electrolytic solution are coupled with the cracks formed on the surface of aluminum alloys for casting by controlling a range of voltage, current, time, and temperature.

(13) As illustrated in FIG. 2, by applying an anodizing method using the electrolytic solution in which any one metallic anion compound selected from the group consisting of NaMoO.sub.4, Na.sub.2Ti.sub.3O.sub.7, and NaAlO.sub.2 is added to any one of the sulfuric acid and the oxalic acid, Al.sub.2O.sup.− in the metallic anion compound is dissociated within an electrolyte and is then coupled with cracks on the surface of the aluminum alloys for casting which occurs at the time of the anodizing.

(14) An ion reaction of the NaAlO.sub.2 of the metallic anion compound is represented as follows.
NaAlO.sub.2------>Na.sup.++Al2O.sup.−

(15) As illustrated in FIG. 3, the surface cracks occurring due to the Si are prevented by coupling the foregoing metal anions with the cracks on the Al.sub.2O.sub.3 oxidation film of the surface of aluminum alloys (Al based alloy) for casting and growing it.

(16) The method for surface treatment of aluminum alloys for casting in accordance with the exemplary embodiment of the present inventive concept embodies a surface treatment process to prepare the optimal electrolytic solution at the time of applying the anodizing method and apply the electrolytic solution to the surface treatment method, which will be described below.

(17) At the time of performing the surface treatment of aluminum alloys for casting, various conditions such as voltage, current, time, temperature, a kind of added metallic anion compounds, and the like need to be controlled. These conditions need to form a thick film of 5 μm in the aluminum alloys for casting including the high Si and be optimally maintained to enhance corrosion resistance, wear resistance, and film hardness by removing the cracks.

(18) Each of the voltage and the current needs to be applied at 10 to 200 V and 0.2 to 10 A/cm.sup.2, the surface treatment process needs to be performed within a range of 1 to 24 h, and the metallic anion compound needs to be added within a range of 0.02 to 0.4 M.

(19) Lower limits of the voltage, current, and time ranges are minimum values of the voltage, current, and time for anionization in the electrolytic solution for the surface treatment of aluminum alloys for casting, and upper limits thereof are maximum values of the voltage, current, and time to prevent a load from being excessively applied at the time of anodizing.

(20) The temperature of the electrolytic may range from 0 to 90° C., and as described above, the added metallic anion compound may be any one selected from the group consisting of NaMoO.sub.4, Na.sub.2Ti.sub.3O.sub.7, and NaAlO.sub.2.

(21) The amount of the metallic anion compound may not exceed 0.4 M since the metal anion compound needs to be added at an enough amount to be dissolved in the electrolytic solution.

(22) FIGS. 4A to 4D are photographs illustrating results obtained by observing a surface of ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 2 hours using an electron microscope. FIGS. 5A to 5D are photographs illustrating results obtained by observing a surface of ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 3 hours using an electron microscope. FIGS. 6A to 6D are photographs illustrating results obtained by observing a surface of ADC12 alloy anodized in (a) H.sub.2SO.sub.4 which is an electrolyte used in the conventional sulfuric method, (b) H.sub.2SO.sub.4+0.02M NaAlO.sub.2, (c) H.sub.2SO.sub.4+0.1 M NaAlO.sub.2, and (d) H.sub.2SO.sub.4+0.2M NaAlO.sub.2 for 4 hours using an electron microscope.

(23) It may be appreciated from FIG. 8 that except when the anodization is performed in a metal anion electrolyte to which 0.02M NaAlO.sub.2 is added, anodizing film hardness of ADC12 alloy is increased when the anodizing is performed in the metal anion electrolyte to which 0.1M and 0.2M NaAlO.sub.2 is added.

(24) FIGS. 7A to 7C are a graph illustrating a polarization curve of ADC12 which is anodized for (a) 2 hours, (b) 3 hours, and (c) 4 hours using H.sub.2SO.sub.4 and H.sub.2SO.sub.4+0.2M NaAlO.sub.2.

(25) It may be appreciated that a Tafel plot of the ADC12 alloy anodized in the electrolyte to which the 0.2M NaAlO.sub.2 is added moves to the right further than the ADC12 alloy anodized by using only the H.sub.2SO.sub.4 as the electrolyte, and as a result, it may be appreciated that corrosion resistance of the ADC12 alloy anodized in the electrolyte to which the 0.2M NaAlO.sub.2 is added is enhanced.

(26) In accordance with exemplary embodiments of the present inventive concept, various effects as follow may be obtained due to the above-mentioned technical configuration.

(27) First, it is possible to form a thick film of 5 μm or more in the aluminum alloys for casting including high Si by using metallic anion compounds.

(28) Second, it is possible to remove surface defects which occur at the time of forming the anodizing film on the aluminum alloys for casting.

(29) Third, it is possible to improve corrosion resistance, wear resistance, and film hardness of the anodized aluminum alloys for casting.

(30) Although the present inventive concept has been shown and described with respect to specific exemplary embodiments, it will be obvious to those skilled in the art that the present disclosure may be variously modified and altered without departing from the spirit and scope of the present invention as defined by the following claims.