METHOD FOR DEPOSITING A COATING ON A SUBSTRATE

Abstract

A method for depositing a coating on a substrate (100), including a step of depositing a thin intermetallic layer (110) on the substrate (100), so as to obtain, at the end of this step, an external part (10) having a predetermined final colour.

Claims

1. A method for depositing a coating on a substrate (100), comprising: depositing a thin intermetallic layer (110) formed of an intermetallic compound on said substrate (100), so as to obtain, at the end of this step, an external part (10) of a timepiece, jewellery or fashion items having a predetermined final colour.

2. The method according to claim 1, wherein the step of depositing the thin intermetallic layer (110) is performed by implementing a PVD deposition method from cathodic or ionic sputtering, thermal evaporation, arc or electron beam evaporation, or pulsed laser beam ablation.

3. The method according to claim 2, wherein the deposition of the thin layer is performed from at least one target consisting of a composite of at least two metals or of at least two targets of different pure metals.

4. The method according to claim 1, wherein the step of depositing the thin intermetallic layer (110) is performed so that said thin intermetallic layer (110) has a thickness between 20 and 1000 nm, preferably between 200 and 500 nm, and more preferably of 300 nm.

5. The method according to claim 1, further comprising a localised annealing step on a predetermined area (111) of the thin intermetallic layer (110) so as to locally modify the final colour of the external part (10).

6. The method according to claim 5, wherein the localised annealing step is performed by means of a laser the beam of which has a diameter between 10 μm and 100 μm.

7. The method according to claim 5, wherein the localised annealing step is performed by means of a laser configured to emit pulses the duration of which is between 4 ns and 350 ns, of variable frequency between 10 kHz and 1 MHz.

8. The method according to claim 6, wherein the localised annealing step is performed by means of a laser configured to emit pulses the duration of which is between 4 ns and 350 ns, of variable frequency between 10 kHz and 1 MHz.

9. The method according to claim 5, wherein the step of depositing the thin intermetallic layer (110) is preceded by a surface structuring step wherein the surface (112) of the substrate (100) is structured.

10. The method according to claim 9, wherein the localised annealing step is performed by means of a laser configured to emit pulses the duration of which is between 4 ns and 350 ns, of variable frequency between 10 kHz and 1 MHz, and wherein during the structuring step, only one portion (113) of the surface (112) of the substrate (100) is structured, said portion (113) corresponding to the predetermined area (111) of the thin intermetallic layer (110) subjected to the localised annealing step.

11. The method according to claim 9, wherein during the structuring step, the structuring is performed on the entire surface (112) of the substrate (100).

12. The method according to claim 1, comprising, after the step of depositing the thin intermetallic layer (110) and the possible step of localised annealing, a step of depositing a protective layer (120).

13. The method according to claim 12, wherein during the step of depositing the protective layer (120), the thin intermetallic layer (110) is covered by a stack of thin dielectric layers and/or by a translucent polymer layer.

14. The method according to claim 12, wherein during the step of depositing the protective layer (120), the composition and the thickness of the thin dielectric layers of the protective stack (120) are specifically selected to conserve the original colour of the thin intermetallic layer (110) or to advantageously modify the colour of the thin intermetallic layer (110) in a chosen direction.

15. A timepiece component comprising a substrate (100), comprising a coating deposited by implementing a method according to claim 1, said timepiece component having a predetermined final colour.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0038] Other features and advantages of the invention will become apparent upon reading the following detailed description given by way of non-limiting example, with reference to FIG. 1 schematically showing a sectional view of a timepiece component, such as an external part, obtained by implementing a method for depositing an intermetallic layer according to the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0039] The present invention relates to a method for depositing a coating on a substrate 100, said method including a step of depositing a thin intermetallic layer 110 on the substrate 100 so as to obtain an external part 10 of a timepiece, jewellery or fashion items. In particular, such an external part 10 may advantageously form a timepiece component.

[0040] The substrate 100 may be produced in any suitable material, such as in metallic material, ceramic, etc.

[0041] The step of depositing the thin intermetallic layer 110 is implemented so that once completed, the colour of the thin layer deposited corresponds to a predetermined colour. More particularly, the step of depositing the thin intermetallic layer 110 is implemented so that at the end of this step, the external part 10 has a predetermined final colour corresponding to said predetermined colour of the thin intermetallic layer 110 deposited.

[0042] In other words, the method is implemented so that it is not necessary to perform a step of annealing the external part 10 to crystallise the intermetallic layer 110. More specifically, the composition of the thin intermetallic layer 110 is selected so that it has the predetermined colour directly in its mainly amorphous and slightly crystalline phase, such that deposited at a temperature below 100° C. with the deposition method selected.

[0043] The step of depositing the thin intermetallic layer 110 is performed by implementing a PVD deposition method and more particularly by implementing one of the following methods: ionic or cathodic sputtering, thermal evaporation, arc or electron beam evaporation, or pulsed laser beam ablation.

[0044] The deposition of the thin intermetallic layer 110 is performed from at least two targets each consisting of a specific metal and/or from at least one target consisting of a composite of at least two metals.

[0045] Preferably, to simplify the implementation of the step of depositing the thin intermetallic layer 110, it is produced from a target consisting of a composite of at least two metals. Moreover, the results obtained during tests demonstrate that the composition of the thin intermetallic layer 110 is more reproducible when the step of depositing the thin intermetallic layer 110 is implemented from a single target consisting of a metal composite.

[0046] By way of non-limiting example, the metals used are selected from Pt, Al, Cu, In and Au, or from composites of these metals.

[0047] More specifically, the metals are for example selected so that the thin intermetallic layer 110 includes an Au—Al, Au—In, Pt—Al, or Pt—Al—Cu intermetallic combination.

[0048] The deposition step is performed so that said thin intermetallic layer 110 measures between 20 and 1000 nm of thickness, preferably between 200 and 500 nm, and more preferably 300 nm. Thus, the thin intermetallic layer 110 is advantageously opaque and has a good compromise between a thickness thick enough in order that the thin intermetallic layer 110 is adapted to withstand mechanical stresses that it is likely to undergo, and a thickness thin enough in order that the consumption of noble metals and that the duration for depositing the thin intermetallic layer 110 are not too high.

[0049] The method of depositing the thin intermetallic layer 110 is implemented so that said thin intermetallic layer 110 has a mainly amorphous and slightly crystalline phase after its deposition.

[0050] The parameters of the PVD deposition method, particularly the powers applied simultaneously on the various sources, as well as the composition of the composite target if applicable, are selected so that the thin intermetallic layer 110 obtained has a composition that has a desired final colour after the step of depositing the thin intermetallic layer 110.

[0051] By way of non-limiting example, the thin intermetallic layer 110 may be made of Pt—Al—Cu composite the composition of which is Pt 48.2% by weight, Al 11.2% by weight and Cu 40.6% by weight, the deposition step being performed by cathodic co-sputtering from 3 pure targets respectively of Pt, Al and Cu. At the end of the deposition step, an external part is obtained, including a thin intermetallic layer slightly crystallised and a colour characterised by the parameters (L*, a*, b*)=(81.2, 6.6, 14.8). It therefore has a final orange colour.

[0052] Similarly, by way of non-limiting example, the thin intermetallic layer 110 may be made of Pt—Al—Cu composite the composition of which is Pt 36.7% by weight, Al 14.3% by weight and Cu 49.0% by weight, the deposition step being performed by cathodic co-sputtering from 3 pure targets respectively of Pt, Al and Cu. At the end of the deposition step, an external part is obtained, including a thin intermetallic layer slightly crystallised and a colour characterised by the parameters (L*, a*, b*)=(78.3, 6.5, 4.4). It therefore has a final pink colour.

[0053] In another non-limiting example, the thin intermetallic layer 110 may be made of Pt—Al—Cu composite the composition of which is Pt 54.6% by weight, Al 12.8% by weight and Cu 32.7% by weight, the deposition step being performed by cathodic co-sputtering from 3 pure targets respectively of Pt, Al and Cu. At the end of the deposition step, an external part is obtained, including a thin intermetallic layer slightly crystallised and a colour characterised by the parameters (L*, a*, b*)=(81.8, 4.3, 12.8). It therefore has a final yellow colour.

[0054] Advantageously, although the method does not require the implementation of an annealing step on the entire external part to obtain a predetermined colour, it may include a localised annealing step on a predetermined area 111 of the thin intermetallic layer 110.

[0055] This localised annealing step has the effect of locally modifying the final colour of the thin intermetallic layer 110, in order to generate a decoration, for example in the form of indices of dials, digits, logos, etc. Indeed, the annealing has the effect of locally modifying the phase of the thin intermetallic layer 110, by making it change from a mainly amorphous and slightly crystalline state to a crystalline state, which changes its colour, typically from its original hue to grey.

[0056] The localised annealing step is performed with the aid of a laser the beam of which may have a diameter for example between 10 μm and 100 μm, or even between 50 μm and 100 μm. The movement of the laser beam is advantageously controlled by a scanning system specific to the laser and based on mechanical or optical axes or by a scanning system specific to the substrate based on mechanical axes providing a high precision of the position of the point of impact of the laser beam on the thin intermetallic layer 110.

[0057] The laser beam has the effect of generating locally, at the point of impact with the thin intermetallic layer 110, a local rise of the temperature resulting in a local phase change of said thin intermetallic layer 110, and consequently in a local change of colour.

[0058] The laser beam may be generated by a nanosecond pulsed or microsecond pulsed laser, or optionally by a continuous laser.

[0059] More specifically, during the localised annealing step, the laser may emit pulses of a duration between 4 ns and 350 ns, of variable frequency between 10 kHz and 1 MHz, and that may reach an average power in the order of 40 W.

[0060] Alternatively, the localised annealing step may also be implemented by using picosecond or femtosecond pulsed lasers, by using the heat accumulation effect at high rate in frequencies ranging from 100 to 200 kHz up to 10 MHz, or pulse series in bursts, as known by the person skilled in the art, spaced apart from one another from a few picoseconds to a few nanoseconds.

[0061] The wavelength of the laser beam is determined so as to favour the absorbance of the material of the thin intermetallic layer 110 that the beam is intended to impact.

[0062] By way of example, the laser beam may have a wavelength in the infra-red spectrum, in the visible spectrum or in the ultraviolet spectrum.

[0063] During the localised annealing step, the variation of the energy of the pulses of the laser beam, their repetition frequency as well as their degree of superposition result in modifying the colour of the intermetallic layer 110.

[0064] It is thus possible to create multicoloured or contrasted decorations based on a single deposition of thin intermetallic layer 110 of homogeneous composition.

[0065] Advantageously, the steps of depositing and localised annealing the thin intermetallic layer may be preceded by a step of structuring the surface 112 of the substrate 100 wherein a portion 113 of the surface 112 of the substrate 100 is structured so as to generate a surface structure contrast on said surface 112.

[0066] In particular, the structured portion 113 of the surface 112 of the substrate 100 may correspond to the predetermined area 111 of the intermetallic layer 110 that is subjected to the heat treatment during the localised annealing step. This has the advantageous effect of reinforcing the difference between the visual appearance of said predetermined area 111 and that of the rest of the thin intermetallic layer 110.

[0067] Alternatively, in an alternative embodiment of the invention, the structuring is performed on the entire surface 112 of the substrate 100.

[0068] Such a surface structuring step may consist for example in polishing, matt finishing or satin finishing partially or totally the surface 112 of the substrate 100, according to the alternative embodiment considered.

[0069] In order to facilitate the localised annealing step and reduce the local contribution of heat needed to carry out the phase transformation of the thin intermetallic layer, the external part 10 may be preheated to a temperature that is close to the phase transition temperature. Thus the supplementary energy contribution by laser may be reduced.

[0070] Advantageously, the thin intermetallic layer 110 obtained after the deposition step may be covered with a protective layer 120, for example formed by a stack of dielectric layers intended to protect the thin intermetallic layer 110 against environmental hazards, during a subsequent deposition step that may advantageously be performed with the same deposition equipment as that used to implement the step for depositing the thin intermetallic layer 110. This stack of thin dielectric layers may also have the effect of modifying the visual appearance of the external part 10, for example by increasing the brightness thereof, and/or by modifying the colour of the intermetallic layer 110 by an advantageous interference effect.

[0071] The step of depositing a protective layer 120 is advantageously the last step of the method according to the invention.

[0072] The stack of thin dielectric layers may be formed of various oxides, nitrides, oxynitrides, such as TiO.sub.2, Al.sub.2O.sub.3, SiO.sub.2, SiN, Si3N4 and may be deposited by an ALD and/or PVD and/or CVD deposition method.

[0073] Alternatively, the step of depositing a protective layer 120 may consist in depositing a varnish layer, for example a polymer varnish layer of the zapon or parylene type.

[0074] Globally, if the method according to the invention includes all of the aforementioned steps, they are implemented successively by starting with the step of structuring the surface of the substrate 100, then the step of depositing a thin intermetallic layer 110 is performed, followed by the localised annealing step, and finally the step of depositing the protective layer 120.

[0075] The invention thus proposes a solution for the use of intermetallic compounds, particularly based on noble metals, offering a wide range of new colours for aesthetic applications in watchmaking, jewellery and any other luxury product.

[0076] More generally, it should be noted that the implementations and embodiments considered above have been described by way of non-limiting examples, and that other variants are consequently possible.