RENDER COMPRISING HONEYCOMB AND CEMENTITIOUS OR CLAY OR GEOPOLYMER MATERIAL

Abstract

A render layer for a building comprises a honeycomb core of nonwoven polypropylene web, and a cementitious material fully filling the cells of the core, wherein (i) the nonwoven web has a porosity of from 5 microns to 600 microns, (ii) the core has a cell size of from 5 mm to 200 mm, (iii) the expansion and contraction across the plane of the core is greater than the expansion and contraction of the cementitious material filling the cells of the core, and (iv) the cementitious material is partly impregnated into the cell walls of the core.

Claims

1. A render layer for a building comprising (i) a honeycomb core of nonwoven polypropylene web, and (ii) a cementitious or clay or geopolymer material fully filling the cells of the core, wherein (a) the nonwoven web has a porosity of from 5 microns to 600 microns, (b) the core has a cell size of from 5 mm to 200 mm, and (c) the expansion and contraction across the plane of the core is greater than the expansion and contraction of the cementitious or clay or geopolymer material filling the cells of the core

2. The render layer of claim 1 wherein the honeycomb core has a cell size of from 5 mm to 50 mm.

3. The render layer of claim 1 wherein the cementitious material comprises plaster, mortar, concrete, mineral or organic binder.

4. The render layer of claim 1 wherein the nonwoven web has a porosity of from 80 microns to 120 microns.

5. The render layer of claim 1 wherein the expansion and contraction across the plane of the core is at least 10% greater than the expansion and contraction of the cementitious material filling the cells of the core.

6. The render layer of claim 1 wherein the cementitious or clay or geopolymer material is partly impregnated into the cell walls of the core.

7. The render layer of claim 2 wherein the honeycomb core has a cell size of from 11 mm to 22 mm.

8. A composite cladding structure for a building wall, comprising in order (i) an insulation layer, (ii) the render layer of claim 1, and (iii) at least one decorative layer, wherein the insulation layer is affixed to the building wall mechanically and/or with adhesive.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] FIGS. 1A and 1B are representations of views of a hexagonal shaped honeycomb.

[0011] FIG. 2 is a representation of another view of a hexagonal cell shaped honeycomb.

[0012] FIG. 3 is an illustration of a cladding structure on a building wall.

DETAILED DESCRIPTION

Render Layer

[0013] The render layer for a building comprising a honeycomb core of nonwoven polypropylene web, and a cementitious material fully filling the cells of the core,

Honeycomb Core

[0014] FIG. 1A is a plan view illustration of one honeycomb 1 of this invention and shows cells 2 formed by cell walls 3. FIG. 1B is an elevation view of the honeycomb shown in FIG. 1A and shows the two exterior surfaces, or faces 4 formed at both ends of the cell walls. The core also has edges 5. FIG. 2 is a three-dimensional view of the honeycomb. Shown is honeycomb 1 having hexagonal cells 2 and cell walls 3. The “T” dimension or the thickness of the honeycomb is shown in FIG. 2. Hexagonal cells are shown, however other geometric arrangements are possible with square, trapezoidal, over-expanded and flex-core cells being among the most common possible arrangements. Such cell types are well known in the art and reference can be made to Honeycomb Technology by T. Bitzer (Chapman & Hall, publishers, 1997) for additional information on possible geometric cell types.

[0015] The core has a cell size of from 5 to 200 mm, preferably from 5 to 50 mm and more preferably from 11 to 22 mm. The cell size is the diameter of an inscribed circle within the cell of the core that touches at least two cell walls.

[0016] In one embodiment, the core comprises a nonwoven polypropylene web having a porosity of from 5 microns to 600 microns. In another embodiment, the core comprises a nonwoven polypropylene web having a porosity of from 10 microns to 500 microns or even 80 to 120 microns. By porosity is meant the Apparent Opening Size (AOS) O.sub.95 as measured according to ASTM D4751-12. If the web porosity is less than 5 microns the cementitious material does not penetrate into the nonwoven web and thus there is no effective bond between those two materials. If the web porosity is greater than 600 microns the cementitious material can penetrate fully into the web and the cell walls lose its spring effect i. e. the ability of the cell walls to expand or contract. The core can be of any desired thickness but core thicknesses of from 5-12 mm are particularly useful.

[0017] It is a requirement of this invention that the expansion and contraction across the plane of the core is greater than the expansion and contraction of the cementitious material filling the cells of the core. In some embodiments the expansion and contraction across the plane of the core is at least 10% greater than the expansion and contraction of the cementitious material filling the cells of the core.

Cementitious Material

[0018] Cementitious material is a component of the render layer. Suitable cementitious materials include plaster, mortar or concrete. In other embodiments, the cementitious material may include mineral or a binder. The render may be organic or mineral in nature. In some embodiments, an organic render is preferred. Renders of clay or geopolymer concrete are also suitable materials. Typically a geopolymer concrete is characterized by long chains or networks of inorganic molecules.

[0019] The filled core structure may be produced by dispensing the wet cementitious material over the core so as to fill the cell walls followed by scraping off surplus cement or by placing the core into a wet slab of cement or by a combination of both. The cementitious material is then allowed to cure (set). In a preferred embodiment, the cementitious material fully fills the cells of the core.

[0020] Preferably the cementitious material is partly impregnated into the cell walls of the core. This partial impregnation, which is facilitated by the selected porosity of the web material, provides enhanced cohesive adhesion between the core and the cementitious material without the need for additional binding agents.

[0021] The greater expansion characteristics (dilatation capability) across the plane of the core when compared to the expansion characteristics of the cementitious material prevents micro-cracking of the render.

Cladding Structure

[0022] FIG. 3 is a schematic of a composite cladding structure for a building wall, comprising in order

[0023] (i) an insulation layer,

[0024] (ii) the render layer of claim 1, and

[0025] (iii) at least one decorative layer,

[0026] wherein the insulation layer is affixed to the building wall mechanically and/or with adhesive.

[0027] In FIG. 3, the building wall is shown as 31, the insulation layer as 33, the render (honeycomb core filled with cementitious material) layer as 34 and the at least one decorative layer is 35. For purposes of clarity, the figure is shown in a partly exploded view and the render is not shown inside the cells of the core.

[0028] Exemplary means of mechanically fixing the insulation layer to the building wall include bolts, nails, pins, screws, or staples. Exemplary adhesive materials for fixing the insulation layer to the building wall are liquids, films, powders or pastes. In some embodiments the adhesive may be supported by a lightweight scrim. An example of an adhesive bond is shown as 32 in FIG. 3.

[0029] Examples of insulation materials are glass, aerogel or mineral fiber batts and foam such as expanded polystyrene or polyurethane foams.

[0030] Typically, the decorative layer is a thin render layer which is organic in nature, is pigmented and may optionally contain some hydrophobic agents. However, other materials may sometimes be used.

[0031] The compressive resistance of the honeycomb core helps to reduce impact damage to a cladded structure.

Test Methods

[0032] Experimental samples were tested according to the protocol of ETAG 004, Edition 2000, Amended February 2013—External Thermal Insulation Composite Systems (ETICS) with Rendering. Two types of evaluation were completed (i) weathering in a climatic chamber to observe microcracking during curing and (ii) a shock or impact test with 10 Joules of energy from a 63.5 mm steel ball dropped from a height of 1.02 m (ISO 7892 issued 1998).

EXAMPLES

Shrinkage Evaluation

[0033] The render was a mineral material SM700 available from Knauf Insulation, Shelbyville, Ind.

[0034] The render was poured to fully fill the cells of the core and allowed to harden. All examples were left for 30 days after pouring of the render in ambient conditions to allow shrinkage to develop. The temperatures generally ranged from 17 to 22 degrees C. although temperature drops to as low as 14 degrees C. occurred at weekends when the heating was turned off. Relative humidity was between 25 to 43% with one spike at 55%. Shrinkage was evaluated in the long and short directions of the trapezoidal shaped cells.

Comparative Example A

[0035] This example comprised a 10 mm thick slab of render without honeycomb core or any other reinforcement material.

Comparative Example B

[0036] This comprised a 10 mm thick slab of render having a backing of fiberglass net type Gittex (mesh size 5 mm) from Knauf.

Example 1

[0037] The core was made from 190 gsm Typar® polypropylene sheet available from E. I. DuPont de Nemours and Company, Wilmington, Del. The core thickness was 10 mm. The cell shape approximated to a trapezoidal shape with a longest dimension of about 17 mm and a shortest dimension of about 12 mm. This gave a core that was more rigid in one direction, the long direction.

[0038] The core was filled to the top with render.

[0039] All examples showed continued shrinkage for the first three days with no further deterioration during the remaining 27 days of the evaluation. This latter level is referred to as the Steady State Shrinkage which is presented in Table 1.

TABLE-US-00001 TABLE 1 Steady State Example Shrinkage (microns) Comparative A 7500 Comparative B 3700 Example 1 3200 (long direction) Example 1 4250 (short direction)

[0040] The results showed that the incorporation of a honeycomb structure into cementitious material as in Example 1 gave a product that significantly reduced the shrinkage of the render when compared to the honeycomb-free render of Example A and was comparable to that of the fabric backed render of Example B. This demonstrates the use of honeycomb having a web porosity as defined above to control shrinkage during curing of the cementitious material.

Impact Evaluation

[0041] Two series of test were carried out to evaluate impact resistance. The first series of tests were Comparative Examples C and D and inventive Examples 2-5. In all these examples the render was SM 700. All the examples were tested for impact resistance by measurement of residual deformation and a visual observation as to the extent of cracking. All examples were prepared on a 1 m×0.5 m expanded polystyrene (EPS) plate that was 50 mm thick unless indicated otherwise. The EPS plate for Comparative Examples A-B and Examples 3-5 was placed in a metal frame representative of a window frame.

[0042] All samples were placed in a climatic chamber at 20 degrees C. and 50% relative humidity for 4 weeks to allow full curing of the cementitious material. The samples were then tested for impact resistance.

Comparative Example C

[0043] This consisted solely of a layer of a nominal 7 mm thick layer of SM700 render.

Comparative Example D

[0044] This example was a 7 mm thick fiberglass net type Gittex (mesh size 5 mm) from Knauf that was fully impregnated with SM700 render.

Example 2

[0045] This sample comprised a 7 mm thick core having a cell size of 11 mm made from 150 gsm Typar® polypropylene sheet. The core was filled with SM700 render.

Example 3

[0046] This was as Example 2 except that there was a 1 mm thick SM700 render layer on one outer surfaces of the core.

Example 4

[0047] This was as Example 3 except that the 1 mm thick render layer was a finishing render of SKAP 1.7 mm grain from Knauf.

Example 5

[0048] This was as Example 2 except that there was an additional 1 mm thick finishing render layer of SKAP 1.7 mm grain from Knauf on top of the 1 mm thick SM700 render layer.

[0049] The results of the impact test are shown in Table 2. All samples cracked after impact.

TABLE-US-00002 TABLE 2 Residual Deformation Sample (mm) Comparative C 4.8 Comparative D 3.4 Example 2 3.6 Example 3 4.4 Example 4 5.0 Example 5 3.4

[0050] All the deformation values showed a relatively deep ball penetration and were considered to be statistically similar showing that the honeycomb containing examples performed no worse than the comparative examples.

[0051] The second series of tests were inventive Examples 6-16. All of these examples had core made from 190 gsm Typar® polypropylene sheet. The core thickness was either 7 mm or 10 mm and the cell size was 11 mm. The renders filling the core cells were both organic renders either type ZF-SIL 3585 from Brillux GmbH, Muenster, Germany or Plastol P394 from Knauf. In some examples there was also a 3 mm thick fiberglass net on top of the render filled core. In some other examples there was also a decorative layer as an outer surface. The decorative material was either Rausan KR K#3517 from Brillux or SKA P311 from Knauf.

[0052] The results are summarized in Table 3.

TABLE-US-00003 TABLE 3 Core EPS Total Residual Thickness Thickness Glass Deco thickness Deformation Example (mm) (mm) Render Layer Layer (mm) (mm) 6 10 10 Brillux Yes Rausan 14 2.2 7 10 10 Brillux Yes Rausan 14 2.4 8 10 10 Brillux Yes Rausan 14 2.1 9 10 50 Brillux Yes Rausan 14 2.0 10 10 50 Brillux Yes Rausan 14 3.0 11 7 50 Brillux No Rausan 8 2.8 12 7 50 Brillux No Rausan 8 2.2 13 10 50 Pastol No Skap 11 3.0 14 10 50 Pastol No Skap 11 2.7 15 7 50 Pastol No Skap 8 1.7 16 7 50 Pastol No Skap 8 2.6

[0053] The residual deformation of all Examples 6-16 was lower than those reported in Table 2. Further, none of the samples had cracks as a result of the impact.