SILICA GLASS MEMBER AND METHOD OF MANUFACTURING THE SAME

Abstract

Provided is a silica glass member which exhibits high optical transparency to vacuum ultraviolet light and has a low thermal expansion coefficient of 4.0−10.sup.−7/K or less at near room temperature, particularly a silica glass member which is suitable as a photomask substrate to be used in a double patterning exposure process using an ArF excimer laser (193 nm) as a light source. The silica glass member is used in a photolithography process using a vacuum ultraviolet light source, in which the fluorine concentration is 1 wt % or more and 5 wt % or less, and the thermal expansion coefficient at from 20° C. to 50° C. is 4.0×10.sup.−7/K or less.

Claims

1. A silica glass member that is used in a photolithography process using a vacuum ultraviolet light source, wherein a fluorine concentration is 1 wt % or more and 5 wt % or less, and a thermal expansion coefficient at from 20° C. to 50° C. is 4.0×10.sup.−7/K or less.

2. The silica glass member according to claim 1, wherein a density is 2.16 g/cm.sup.3 or more and 2.19 g/cm.sup.3 or less.

3. The silica glass member according to claim 1, wherein a concentration of an OH (hydroxyl) group is 10 ppm or less.

4. The silica glass member according to claim 1, wherein a fictive temperature is 1000° C. or lower.

5. The silica glass member according to claim 1, wherein concentrations of Fe, Cr, Ni, Cu, and Ti are each 1 wt ppm or less, and a viscosity coefficient at a temperature of 1000° C. is 10.sup.14.5 dPa.Math.s or less.

6. The silica glass member according to claim 1, wherein a linear transmittance of light having a wavelength of 193 nm is 90% or more.

7. The silica glass member according to claim 2, wherein a concentration of an OH (hydroxyl) group is 10 ppm or less.

8. The silica glass member according to claim 2, wherein a fictive temperature is 1000° C. or lower.

9. The silica glass member according to claim 2, wherein concentrations of Fe, Cr, Ni, Cu, and Ti are each 1 wt ppm or less, and a viscosity coefficient at a temperature of 1000° C. is 10.sup.14.5 dPa.Math.s or less.

10. The silica glass member according to claim 2, wherein a linear transmittance of light having a wavelength of 193 nm is 90% or more.

11. The silica glass member according to claim 3, wherein a fictive temperature is 1000° C. or lower.

12. The silica glass member according to claim 3, wherein concentrations of Fe, Cr, Ni, Cu, and Ti are each 1 wt ppm or less, and a viscosity coefficient at a temperature of 1000° C. is 10.sup.14.5 dPa.Math.s or less.

13. The silica glass member according to claim 3, wherein a linear transmittance of light having a wavelength of 193 nm is 90% or more.

14. The silica glass member according to claim 4, wherein concentrations of Fe, Cr, Ni, Cu, and Ti are each 1 wt ppm or less, and a viscosity coefficient at a temperature of 1000° C. is 10.sup.14.5 dPa.Math.s or less.

15. The silica glass member according to claim 4, wherein a linear transmittance of light having a wavelength of 193 nm is 90% or more.

16. The silica glass member according to claim 5, wherein a linear transmittance of light having a wavelength of 193 nm is 90% or more.

17. The silica glass member according to claim 1, wherein a density is 2.16 g/cm.sup.3 or more and 2.19 g/cm.sup.3 or less, a concentration of an OH (hydroxyl) group is 10 ppm or less, a fictive temperature is 1000° C. or lower, concentrations of Fe, Cr, Ni, Cu, and Ti are each 1 wt ppm or less, and a viscosity coefficient at a temperature of 1000° C. is 10.sup.14.5 dPa.Math.s or less, and a linear transmittance of light having a wavelength of 193 nm is 90% or more.

18. A method of manufacturing low thermal expansion silica glass, the method comprising: preparing silica glass having a fluorine concentration of 1 wt % or more and 5 wt % or less; heating the silica glass in a heating furnace to a temperature ranging from a temperature which is 1000° C. or higher and has a viscosity coefficient of 10.sup.14.5 dPa.Math.s or less, to 1500° or lower; taking out the silica glass from the heating furnace; and subjecting the silica glass to a quenching (rapidly cooling) treatment and to an annealing treatment again in a temperature range of 400° C. or higher and a temperature which is 1000° C. or lower and has a viscosity coefficient of the silica glass of 10.sup.14.5 dPa.Math.s or less.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0030] FIG. 1 illustrates the transmittance curve of Example 1.

DESCRIPTION OF THE EMBODIMENTS

[0031] The silica glass member of the present invention is silica glass to be used in a photolithography process using vacuum ultraviolet light as a light source, in which the fluorine concentration is 1 wt % or more and 5 wt % or less, and the thermal expansion coefficient at from 20° C. to 50° C. is 4.0×10.sup.−7/K or less.

[0032] The above constitutional requirements of the present invention will be described in detail below.

[0033] In the present invention, the fluorine concentration in the silica glass member is 1 wt % or more and 5 wt % or less. It was widely known that fluorine-doped silica glass exhibits low thermal expansion property at 300° C. or higher when fluorine-doped optical fibers were studied in the past, and it is also reported that the thermal expansion coefficient thereof is 2.5×10.sup.−7/K at near 400° C. (Development of optical fibers in Japan, New York: Gordon and Breach Science Publishers, c 1989.). However, fluorine doping does not almost affect the thermal expansion coefficient at a temperature between 20° C. and 50° C. including room temperature even in such a fluorine-doped silica glass. For example, even in the silica glass doped with fluorine up to 1.5 wt %, the thermal expansion coefficient at from 5° C. to 65° C. is not almost different from that of silica glass that is not doped (Res. Reports Asahi Glass Co., Ltd., 57 (2007)).

[0034] As the principle, the fluorine doping replaces the OH group which is the terminal structure of the silica glass and cuts a part of the member ring structure (for example, a three-membered ring structure, a four-membered ring structure, or a six-membered ring structure) to form a new terminal group structure, and it is thus possible to dope fluorine to be 10-fold or more than other terminal groups (for example, an OH group and a Cl group) contained in the silica glass in a weight ratio depending on the doping conditions. Moreover, silica glass having a large number of terminal group structures has a feature to exhibit low viscosity.

[0035] To exhibit low viscosity means that the density of silica glass is low and the structural change occurs at a relatively low temperature. Moreover, this also means that the flowability of the molecules in the silica glass is great and the structural change is remarkable at a high temperature. In other words, the silica glass having a large number of terminal group structures has a wide temperature range in which the structure thereof changes. In this manner, in silica glass having a large number of fluorine groups, it is easy to set the fictive temperature in a wide temperature range and it is possible to control the density by combining the quenching treatment and the annealing treatment.

[0036] In the present invention, a silica glass member having a fluorine concentration of 1 wt % or more and 5 wt % or less, a decreased density, and a thermal expansion coefficient of 4.0×10.sup.−7/K or less at from 20° C. to 50° C. is obtained by subjecting silica glass to fluorine doping and a predetermined heat treatment.

[0037] Specifically, the silica glass member can be manufactured by, for example, the so-called VAD method in which a porous silica body (soot) is formed by flame hydrolysis of a silica glass forming raw material and then subjected to a transparentizing treatment (JP 2001-342027 A). In other words, the soot is formed, then doped with fluorine by being treated in a mixed gas atmosphere in which an inert gas such as helium and SiF.sub.4 gas are mixed, then transparentized in a fluorine-containing atmosphere (mixed gas atmosphere), and further subjected to a predetermined heat treatment, whereby a silica glass member is manufactured.

[0038] The fluorine concentration (concentration proportion of SiF.sub.4 gas) in the mixed gas is preferably from more than 5 vol % to 35 vol %, more preferably from 10 vol % to 35 vol %, and particularly preferably from 25 vol % to 35 vol %. In addition, the introduction temperature of the mixed gas is preferably from 1000° C. to 1300° C. and more preferably from 1100° C. to 1200° C. There is a case in which diffusion of fluorine into the glass structure is slow and fluorine is not sufficiently doped when the introduction temperature is lower than 1000° C. On the other hand, sintering of soot starts and diffusion of fluorine into the glass structure is hindered when the temperature exceeds 1300° C.

[0039] In the present invention, the concentration of fluorine in the obtained silica glass member is set to 1 wt % or more and 5 wt % or less by, for example, adjusting the concentration proportion of SiF.sub.4 gas in the mixed gas and the calcination temperature in the transparentizing treatment.

[0040] The predetermined heat treatment in the present invention refers to a process of subjecting the fluorine-doped silica glass at 1000° C. or higher to a quenching treatment after a transparentizing treatment and to an annealing treatment at 1000° C. or lower thereafter. Incidentally, the quenching treatment may be continuously conducted without once lowering the temperature after the transparentizing treatment.

[0041] The quenching treatment in the present invention refers to a treatment that the silica glass is heated in a temperature range of from 1000° C. to 1500° C. until the viscosity coefficient reaches 10.sup.14.5 dPa.Math.s or less and preferably 10.sup.13.0 dPa.Math.s or less and thereafter, the silica glass is rapidly cooled to 800° C. or lower, and it is more preferable as the temperature after rapid cooling is lower so that 600° C. is more preferable than 800° C. and 400° C. is more preferable than 600° C. In addition, with regard to the cooling rate, it is required to be rapid cooling to decrease 1000 K in about 1 second. Examples of rapid cooling may include to directly transfer the silica glass from the heating furnace to a low-temperature gas or liquid refrigerant that is present to be adjacent thereto. For example, a treatment may be conducted in which silica glass is heated to 1500° C. and then released into the atmospheric air, and the air is blown to the silica glass or the silica glass is dipped into the pool of pure water. It is possible to rapidly decrease the temperature of the silica glass to the refrigerant temperature as the air flow velocity after release into the atmospheric air is set to a value sufficient for cooling or the volume of the pure water pool is prepared in a sufficient amount with respect to the target silica glass by calculating the volume from the heat capacity at this time.

[0042] Incidentally, it is required to cool the silica glass as instantaneously as possible in the quenching treatment, it is thus preferable that the quenching treatment is conducted by forming the silica glass in a thin plate shape rather than a block shape, and also it is more preferable to conduct the quenching treatment in a liquid such as water or oil although it may be conducted in the air. In particular, it is preferable that large silica glass is thinned in order to uniformly rapidly cool the entire silica glass. In the present invention, the viscosity of the silica glass is determined mainly by the amount of fluorine and the temperature, but the properties of the silica glass before cooling are fixed and the thermal expansion coefficient at normal temperature can be decreased by rapidly cooling the silica glass after the silica glass is heated until the viscosity sufficiently decreases. Specifically, the object of the present invention that is a low thermal expansion coefficient can be achieved by rapidly cooling the silica glass from a temperature higher than a temperature at which the viscosity coefficient of the silica glass is 10.sup.14.5 dPa.Math.s by 200° C. or more to a temperature lower than the temperature by 100° C. or more while sandwiching the temperature therebetween.

[0043] The silica glass exhibits low viscosity when being doped with fluorine so that the molecular vibration in the glass is vigorous at 1000° C. or higher and it is presumed that the volume expansion is microscopically caused. By conducting the quenching treatment in this state, the glass structure is frozen while maintaining the volume expanded state, and the silica glass thus has a decreased density.

[0044] However, there is a case in which local strain due to the small member ring structure typified by a three-membered ring or a four-membered ring may remain in the structure by the quenching treatment, and in that case, an annealing treatment for removing the strain is required after the quenching treatment. It is required to conduct the annealing treatment at 1000° C. or lower and a viscosity coefficient in a range of 10.sup.14.5 dPa.Math.s or less. The annealing temperature is determined by the temperature characteristic of the silica glass. For example, the strain point of silica glass having a fluorine concentration of 1 wt % or more and 5 wt % or less is 1000° C. or lower, and thus the annealing temperature is usually 1000° C. or lower, preferably 800° C. or lower, and more preferably between 600° C. and 400° C. It is possible to eliminate the local strain of the silica glass while maintaining the low density state by conducting an annealing treatment that the silica glass after cooling is heated by a heater or the like and, for example, retained at a temperature of 400° C. for about 50 hours after being rapidly cooled in the quenching treatment. The effect of an annealing treatment cannot be expected at a temperature lower than 400° C.

[0045] Incidentally, the strain point is a temperature at which the viscosity coefficient is 10.sup.14.5 dPa.Math.s and a temperature at which viscous flow of silica glass cannot practically occur, and it corresponds to the lower limit temperature in the annealing range. Accordingly, the viscosity coefficient of the silica glass member of the present invention at 1000° C. is preferably 10.sup.14.5 dPa.Math.s or less and more preferably 10.sup.13.0 dPa.Math.s or less.

[0046] The thermal expansion coefficient of the silica glass member thus obtained at from 20° C. to 50° C. is 4.0×10.sup.−7/K or less, preferably 3.2×10.sup.−7/K or less, and more preferably 3.0×10.sup.−7/K or less. In addition, the density of the silica glass member at from 20° C. to 50° C. is 2.16 g/cm.sup.3 or more and 2.19 g/cm.sup.3 or less, specifically, 2.190 g/cm.sup.3 or less, preferably 2.185 g/cm.sup.3 or less, and more preferably 2.16 g/cm.sup.3 or more and 2.180 g/cm.sup.3 or less. When the density is less than 2.16 g/cm.sup.3, the hardness of the surface of the silica glass member tends to be insufficient, breakage occurs in the polishing step and the transportation step, and thus the silica glass member cannot be used in the photolithography process in some cases. Incidentally, the density of the silica glass member is related to the fluorine concentration as well, and thus the fluorine concentration is 1 wt % or more and 5 wt % or less, preferably 1.5 wt % or more and 5 wt % or less, and more preferably 3 wt % or more and 5 wt % or less.

[0047] It is known that the thermal expansion of silica glass varies depending on the fictive temperature (Journal of Non-Crystalline Solids vol. 5 (1970) p. 123). The fictive temperature corresponds to a temperature at which freezing of glass in which a structure in a supercooled liquid state at a high temperature is frozen occurs. It is known that the thermal expansion of silica glass varies depending on the density as well, and it is reported that the thermal expansion coefficient of densified glass increases (“Materials”, Vol. 32, No. 362, p. 64). In other words, the structure of silica glass varies depending on the density and freezing temperature, and, for example, in the case of densified glass, volume expansion is remarkable since the gap called the free volume between the glass network structures is small and the gaps to alleviate molecular vibration accompanying temperature rise are few.

[0048] It is known that the fictive temperature of silica glass can be changed by an annealing treatment. The fictive temperature also depends on the concentration of the OH group in the silica glass, and the fictive temperature is likely to decrease as the concentration of the OH group increases. This is because the OH group is present at the terminal portion in the glass structure, the member ring structure is cut by the annealing treatment, the flowability of the glass structure increases, and the structure freezing temperature thus decreases. However, there is limitation on a decrease in density by a change in fictive temperature of the silica glass, and it is reported that the thermal expansion coefficient of the silica glass in which the fictive temperature and the concentration of the OH group are changed is approximately from 6.0×10.sup.−7/K to 6.5×10.sup.−7/K between 20° C. and 400° C. (Journal of Non-Crystalline Solids, vol. 355 (2009) p. 323).

[0049] Meanwhile, it is conventionally known that the member ring structure is cut and the glass structure changes when silica glass is doped with fluorine, and, for example, it is reported that the bond angle of —Si—O—Si— in the member ring structure changes (Journal of the Ceramic Society of Japan vol. 120 (2012) p. 447). In other words, it is possible to change the fictive temperature and to decrease the density of silica glass by doping the silica glass with fluorine.

[0050] In the present invention, it is possible to control the fictive temperature of glass having a fluorine group by combining the quenching treatment and the annealing treatment, but the fictive temperature is preferably 1000° C. or lower and more preferably 900° C. or lower in order to set the thermal expansion coefficient at from 20° C. to 50° C. to 4.0×10.sup.−7/K or less. The silica glass is often in a state in which the local strain is not eliminated in a case in which the fictive temperature exceeds 1000° C., and in that case, a stable low thermal expansion property cannot be exerted in some cases. Incidentally, the fictive temperature can be determined on the basis of the calculation formula reported in Journal of Non-Crystalline Solids vol. 185 (1995) p. 191. It is reported that the fictive temperature correlates with the infrared absorption wavenumber of asymmetric stretching vibration of Si—O—Si of silica glass, but it is expected that the frequency changes as fluorine is doped in the glass structure. The fictive temperature of fluorine-doped glass can be calculated when glass having a known fluorine concentration is thermally treated at a predetermined temperature in advance, the temperature is regarded as a fictive temperature, and the difference between the fictive temperature and the value calculated by the basic formula is used as a correction coefficient. As these calculation formulas, several calculation formulas are reported, and in the present invention, the formula that is reported in JP 2002-316831 A and used in a case in which the fluorine concentration is 1 wt % or more is employed.

[0051] In the silica glass member of the present invention, the concentration of an OH group is preferably 10 ppm or less. There is a case in which it is difficult to set the fluorine concentration to 1 wt % or more in a case in which the concentration of an OH group exceeds 10 ppm. This is due to the trade-off relationship that fluorine concentration is low when the concentration of an OH group is high since fluorine is exchanged with the OH group.

[0052] The concentrations of Fe, Cr, Ni, Cu, and Ti contained in the silica glass member thus obtained are each 1 wt ppm or less, and the viscosity coefficient at a temperature of 1000° C. is preferably 10.sup.14.5 dPa.Math.s or less.

[0053] In order to use a silica glass member in a photolithography process using an ArF excimer laser light source, optical transparency at an exposure wavelength of 193 nm is required. At this time, metal impurities in the glass cause deterioration in transparency. In particular, the metal impurities typified by transition metals such as Fe, Cr, Ni, Cu, and Ti cause the d-d transition between the d orbitals that are the excited level of electrons, have an absorption edge in the visible region, and thus remarkably deteriorate transparency in the ultraviolet region. Hence, the concentrations of these metal impurities are each preferably 1 wt ppm or less in the silica glass member as described above.

[0054] The silica glass member can be used in photolithography using vacuum ultraviolet light as a light source. Here, the vacuum ultraviolet light refers to an electromagnetic wave having a wavelength in the vicinity of from 10 nm to 200 nm, and the vacuum ultraviolet laser includes an ArF excimer laser (193 nm), an F.sub.2 laser (157 nm), and the like.

[0055] In the silica glass member, the optical transparency of the ArF excimer laser at an exposure wavelength of 193 nm is 85% or more, preferably 90% or more, and more preferably 91% or more as a linear transmittance, and it is equivalent to or higher than the light transmittance of conventional silica glass.

EXAMPLES

[0056] Hereinafter, the present invention will be specifically described based on Examples, but the present invention is not limited by the following Examples.

Example 1

[0057] SiCl.sub.4 as a glass forming raw material was hydrolyzed in oxyhydrogen flame, the silica fine particles thus produced were deposited on a quartz glass target, thereby obtaining porous silica (soot) having a diameter of 200 mm and a length of 500 mm. Subsequently, the soot was inserted in a furnace the temperature thereof was raised to 1200° C. at a rate of temperature rise of 400° C./h in a He gas atmosphere having a flow rate of 20 L/min, the atmosphere gas was then switched to a mixed gas of SiF.sub.4: 20 vol %+He: 80 vol % (flow rate: 15 L/min), and the soot was retained at 1200° for 3 hours, thereby conducting a fluorine doping treatment.

[0058] After the fluorine doping treatment was completed, the atmosphere was maintained as it was, and the temperature of the fluorine-doped soot was raised to 1400° C. at a rate of temperature rise of 400° C./h, and the fluorine-doped soot was retained at 1400° for 2 hours to conduct a transparentizing treatment, thereby obtaining a silica glass ingot having a diameter of 120 mm and a length of 230 mm.

[0059] The ingot was once returned to normal temperature and was sliced to be formed into a thin plate having a thickness of 6.4 mm, the thin plate was put in an electric furnace, the temperature was raised in the atmospheric air atmosphere, and the thin plate was retained at 1100° C. for 1 hour, then taken out from the furnace, and subjected to a quenching treatment to rapidly cool the thin plate to 20° C. by blowing a large amount of air thereto. After the quenching treatment, the thin plate was further reheated to 1000° C. at a rate of temperature rise of 100° C./h in the atmospheric air atmosphere again and left to be naturally cooled to conduct an annealing treatment, thereby obtaining a silica glass member.

[0060] The silica glass member thus obtained was cut, processed into a cylindrical shape, and then subjected to the measurement of thermal expansion by an optical interference type thermal expansion meter (LIX-2 manufactured by ADVANCE RIKO, Inc.). Furthermore, a strip-shaped sample of 20 mm×40 mm×6.4 mm was cut out and subjected to optical polishing, then the measurement of linear transmittance at a wavelength of 193 nm by a vacuum ultraviolet measuring device (JASCO VUV-200), and the measurement of fictive temperature and OH concentration attributed to the OH absorption peak by an infrared spectrometer (Nicolet 6700). The strip-shaped sample was also subjected to the analysis of F concentration by ion chromatography, the measurement of density by the Archimedes method (JIS R 1634), the analysis of metal impurities by a mass spectrometer, and the measurement of viscosity coefficient by a beam bending method (ISO 7884-4).

Example 2

[0061] A silica glass member was obtained in the same manner as in Example 1 except that the fluorine doping treatment was conducted by setting the ratio of SiF.sub.4 to He in the mixed gas to 30 vol %: 70 vol % in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Examples 3 and 4

[0062] Silica glass members were obtained in the same manner as in Example 1 except that the fluorine doping treatment was conducted by setting the ratio of SiF.sub.4 to He in the mixed gas to 30 vol %: 70 vol % and the annealing treatment was conducted at 800° C. (Example 3) or 600° C. (Example 4) after the quenching treatment of the obtained thin plates at 1300° C. for 1 hour in Example 1. Thereafter, the silica glass members were subjected to the same tests and evaluations as in Example 1.

Example 5

[0063] A silica glass member was obtained in the same manner as in Example 1 except that the fluorine doping treatment was conducted by setting the ratio of SiF.sub.4 to He in the mixed gas to 8 vol %: 92 vol % in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Example 6

[0064] A silica glass member was obtained in the same manner as in Example 1 except that the fluorine doping treatment was conducted by setting the ratio of SiF.sub.4 to He in the mixed gas to 8 vol %: 92 vol % and the annealing treatment of the thin plate was conducted at 800° C. after the quenching treatment in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Example 7

[0065] A silica glass member was obtained in the same manner as in Example 1 except that the thin plate was dropped from the furnace to be immersed in water at normal temperature at the time of the quenching treatment in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Example 8

[0066] The soot fabricated in the same manner as in Example 1 was put into a furnace and the temperature thereof was raised to 1200° C. at a rate of temperature rise of 400° C./h in a He gas atmosphere having a flow rate of 20 L/min, the atmosphere gas was then switched to a mixed gas of SiF.sub.4: 25 vol %+He: 75 vol % (flow rate: 15 L/min), and the soot was retained at 1200° for 3 hours to conduct fluorine doping.

[0067] After the fluorine doping treatment was completed, the atmosphere was switched to a mixed gas of SiF.sub.4: 20 vol %+He: 80 vol %, and the temperature of the fluorine-doped soot was raised to 1400° C. at a rate of temperature rise of 400° C./h, and the fluorine-doped soot was retained at 1400° for 2 hours to conduct a transparentizing treatment, thereby obtaining a silica glass ingot having a diameter of 120 mm and a length of 230 mm.

[0068] A thin plate (thickness 6.4 mm) sliced from the silica glass ingot thus obtained was retained at 1300° C. for 1 hour in the atmospheric air atmosphere, and then dropped from the furnace to be immersed in water at normal temperature to conduct a quenching treatment. After the quenching treatment, the silica glass thin plate was further reheated to 600° C. at a rate of temperature rise of 100° C./h in the atmospheric air atmosphere again and left to be naturally cooled to conduct an annealing treatment, thereby obtaining a silica glass member.

Example 9

[0069] The soot fabricated in the same manner as in Example 1 was put into a furnace and the temperature thereof was raised to 1200° C. at a rate of temperature rise of 400° C./h in a He gas atmosphere having a flow rate of 20 L/min, the atmosphere gas was then switched to a mixed gas of SiF.sub.4: 35 vol %+He: 65 vol % (flow rate: 15 L/min), and the soot was retained at 1200° for 3 hours to dope fluorine.

[0070] After the fluorine doping treatment was completed, the atmosphere was switched to a mixed gas of SiF.sub.4: 20 vol %+He: 80 vol %, and the temperature of the fluorine-doped soot was raised to 1400° C. at a rate of temperature rise of 400° C./h, and the fluorine-doped soot was retained at 1400° for 2 hours to conduct a transparentizing treatment, thereby obtaining a silica glass ingot having a diameter of 120 mm and a length of 230 mm.

[0071] The silica glass ingot thus obtained was gradually cooled and retained for 1 hour when the temperature thereof reached 1300° C., and then dropped from the furnace to be immersed in water at normal temperature to conduct a quenching treatment. After the quenching treatment, the silica glass ingot was further reheated to 400° C. at a rate of temperature rise of 100° C./h in the atmospheric air atmosphere again and left to be naturally cooled to conduct an annealing treatment, thereby obtaining a silica glass member.

Comparative Example 1

[0072] A silica glass member was obtained in the same manner as in Example 1 except that the fluorine doping treatment was conducted by setting the ratio of SiF.sub.4 to He in the mixed gas to 5 vol %: 95 vol % in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Comparative Examples 2 and 3

[0073] Silica glass members were obtained in the same manner as in Comparative Example 1 except that the thin plate was retained at 1300° C. for 1 hour, then subjected to a quenching treatment, and the annealing treatment was conducted at 1000° C. (Comparative Example 2) or 800° C. (Comparative Example 3). Thereafter, the silica glass members were subjected to the same tests and evaluations as in Example 1.

Comparative Example 4

[0074] A silica glass member was obtained in the same manner as in Example 1 except that the quenching treatment was omitted in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Comparative Example 5

[0075] A silica glass member was obtained in the same manner as in Example 1 except that the annealing treatment was omitted in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

Comparative Example 6

[0076] A silica glass member was obtained in the same manner as in Example 1 except that the quenching treatment and the annealing treatment were omitted in Example 1. Thereafter, the silica glass member was subjected to the same tests and evaluations as in Example 1.

[0077] The results of Examples 1 to 9 and Comparative Examples 1 to 6 are presented in Table 1. In addition, the transmittance curve of Example 1 is illustrated in FIG. 1.

[0078] In Examples, the silica glass was described for those obtained by hydrolysis in oxyhydrogen flame, but the silica glass may be those manufactured by other methods. For example, silica glass obtained by addition of fluorine and a sol-gel method or the like may be subjected to a quenching treatment and then a heat treatment.

TABLE-US-00001 TABLE 1 Concentration of Thermal metal impurity expansion Fictive Concentration Concentration (maximum content of coefficient Transmittance temperature of OH group of F any of Fe, Cr, Ni, [×10.sup.−7] (25° C.) at 193 nm [%] [° C.] [ppm] [wt %] Density Cu, or Ti) [wt ppm] Example 1 3.1 90 942 2 2 2.18 0.1 Example 2 2.3 91 880 1 3.3 2.18 0.1 Example 3 2.5 91 880 1 3.4 2.18 0.1 Example 4 1.9 91 876 1 3.8 2.18 0.1 Example 5 3.7 90 980 5 1 2.19 0.1 Example 6 3.5 90 962 4 1.1 2.19 0.1 Example 7 2.9 90 940 2 2 2.18 0.1 Example 8 1.7 91 870 1 3.8 2.18 0.1 Example 9 2.5 90 800 1 4 2.16 0.1 Comparative 4.7 90 1104 7 0.6 2.2 0.1 Example 1 Comparative 4.5 90 1082 6 0.7 2.2 0.1 Example 2 Comparative 4.2 90 1046 6 0.8 2.2 0.1 Example 3 Comparative 5 90 810 2 2 2.2 0.1 Example 4 Comparative 4.8 90 1100 4 2 2.18 0.1 Example 5 Comparative 5.2 91 1051 2 2 2.2 0.1 Example 6

INDUSTRIAL APPLICABILITY

[0079] The silica glass member of the present invention can be suitably used in photolithography using vacuum ultraviolet light such as an ArF excimer laser (193 nm) or a F.sub.2 laser (157 nm) as a light source.