METHOD OF MANUFACTURING A COMPOSITE PANEL CONTAINING LAUAN OR OTHER MOISTURE-CARRYING OR MOISTURE-ABSORBING MATERIAL USING ADHESION PROMOTER AND PANEL MADE USING THE METHOD

Abstract

A method of manufacturing a composite panel with lauan or another moisture-carrying or moisture-absorbing material, and the panel so made, are provided. A layer of gel coat is formed on a mold surface, a wet laminate containing a resin is applied to the layer of gel coat on the mold surface, a substrate of lauan or another moisture-carrying or moisture-absorbing material is placed on the wet laminate, and the combination is cured. Prior to curing, there is provided a layer of a bonding promoter at the interface of the substrate with the wet laminate, additional to any amount of promoter(s) present in the resin of the wet laminate.

Claims

1. A method of manufacturing a composite panel, comprising: applying a layer of gel coat to a mold surface; applying a wet laminate to the layer of gel coat on the mold surface, the wet laminate comprising a resin; placing a substrate of lauan or other moisture-carrying or moisture-absorbing material on the wet laminate; providing a layer of a bonding promoter at an interface of the substrate of lauan or other moisture-carrying or moisture-absorbing material with the wet laminate, additional to any amount of promoter(s) present in the resin of the wet laminate; and curing the wet laminate and the gel coat to form a panel.

2. The method of claim 1, wherein said step of providing the layer of bonding promoter comprises applying the layer of bonding promoter to an exposed surface of the wet laminate.

3. The method of claim 2, wherein said step of providing the layer of bonding promoter is performed before said step of placing the substrate.

4. The method of claim 2, wherein said step of providing the layer of bonding promoter comprises spraying the bonding promoter onto an exposed surface of the wet laminate.

5. The method of claim 4, wherein said step of providing the layer of bonding promoter is performed before said step of placing the substrate.

6. The method of claim 1, wherein said step of providing the layer of bonding promoter comprises applying the layer of bonding promoter to an exposed surface of the substrate.

7. The method of claim 6, wherein said step of providing the layer of bonding promoter is performed before said step of placing the substrate.

8. The method of claim 6, wherein said step of providing the layer of bonding promoter comprises spraying the bonding promoter onto the exposed surface of the substrate.

9. The method of claim 6, wherein said step of providing the layer of bonding promoter comprises rolling the bonding promoter onto the exposed surface of the substrate.

10. The method of claim 1, wherein said step of providing the layer of bonding promoter comprises applying a solution of a promoter in a solvent, in a concentration of solvent to promoter in a range of 10:1 to 1000:1, inclusive.

11. The method of claim 10, wherein said step of providing the layer of bonding promoter comprises applying a solution of a material selected from the group consisting of copper, iron, cobalt and salts thereof.

12. The method of claim 10, wherein said step of providing the layer of bonding promoter comprises applying a solution of a material selected from the group consisting of amine accelerators, dimethyl aniline, dimethyl-p-toluidine, vanadium accelerators, vanadium monobutyl dihydrophosphite, 2,4-pentanedione and N,N-diethylacetoacetamide.

13. The method of claim 10, wherein said step of providing the layer of bonding promoter comprises applying a solution containing a material selected from the group consisting of mineral spirits, methyl ethyl ketone, styrene, acetone, methyl methacrylate and xylene as a solvent.

14. The method of claim 1, wherein the substrate is lauan.

15. The method of claim 1, wherein the substrate is plywood.

16. The method of claim 1, wherein the substrate is a wood other than lauan or plywood.

17. The method of claim 1, wherein the substrate placed on the wet laminate has a moisture content of up to 19 weight%.

18. The method of claim 1, wherein the substrate placed on the wet laminate has a moisture content of 13-18 weight%.

19. The method of claim 1, wherein the substrate placed on the wet laminate has a moisture content of 14-17 weight%.

20. A panel made by the method of claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] FIG. 1 is an illustration of one preferred embodiment of a method according to the present invention.

[0009] FIG. 2 is an illustration of a second preferred embodiment.

[0010] FIG. 3 is an illustration of a third preferred embodiment.

[0011] FIG. 4 is an illustration of a panel made according to the process of FIG. 1, 2 or 3.

[0012] FIG. 5 is a cross-sectional view of the panel shown in FIG. 4.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0013] As stated above, the conventional method of manufacturing a lauan composite panel involves forming a layer of gel coat on the surface of a mold of at least the size of the panel to be made. On the gel coat is formed a wet laminate, of a resin containing a promoter and possibly peroxide, and fiber glass fibers as a reinforcement. The wet laminate may be sprayed onto the gel coat, such as by spraying the resin onto the gel coat, followed by (or mixed with) the glass fibers, and then rolling the surface of the layer to achieve evenness. A sheet of lauan is then positioned on the wet laminate; for a typical panel, a number of pieces of lauan are actually used, and are placed abutting each other to cover the wet laminate.

[0014] The wet laminate is then cured. This may be done by encasing the entire mold in a vacuum bag, exposing the mold with the gel coat and other layers on it to a vacuum, and applying heat. Alternatively, heat alone may be used.

[0015] FIG. 1 illustrates one preferred embodiment of a method according to the present disclosure. A horizontal flat mold is provided, and is coated with a gel coat layer (not illustrated). A first spray head, shown toward the right in that Figure, is used to spray the mix of resin and glass fibers onto the gel coat. As in a conventional method, this mix may also include a promoter in an amount sufficient to achieve proper polymerization of the resin during curing, but should not contain so much as to change the curing time.

[0016] A second spray head sprays promoter onto the wet laminate, as shown to the left of the first spray head. This promoter may be the same as is included in the wet laminate itself, but that need not be the case, as discussed below. The wet laminate, coated with the promoter by the second spraying head, is then covered with the required number of pieces of lauan. (To be more precise, the wet laminate may not be exactly and completely covered by the lauan, as a peripheral portion of the laminate may remain uncovered.)

[0017] When the entire mold has been provided with each of the mentioned layers, it is enclosed in a vacuum bag (not illustrated), and the resin of the wet laminate is cured under vacuum and heat. Alternatively, other techniques of curing may be used. The finished panel is then released from the mold and cut to size if necessary.

[0018] An example of a panel manufactured in this fashion is shown in FIGS. 4 and 5. As may be seen, one surface of the panel is formed by the lauan substrate, which is bonded to the fiberglass laminate. The other side of the laminate is bonded to the high-gloss gel coat. In both Figures the interface layer between the lauan substrate and the fiberglass laminate is labeled, and the thin layer of adhesion promoter is illustrated as well (see FIG. 4).

[0019] While reference has been made above simply to a promoter being applied to the lauan-laminate interface, in practice of course what is applied is a solution of the promoter(s), so that what is applied includes one or more promoters, a solvent, and if needed a material to dilute the concentration of the promoter(s) to the desired value. It is believed that the following may be used as suitable promoters, although it should be understood that neither this list nor the following list of solvents is intended to be exhaustive: [0020] Promotors, including but not limited to: [0021] Copper salts [0022] Manganese salts [0023] Iron salts [0024] Cobalt salts [0025] Amine accelerators [0026] Dimethyl aniline [0027] Dimethyl-p-toluidine [0028] Vanadium accelerators [0029] Vanadium monobutyl dihydrophosphite [0030] 2,4-Pentanedione [0031] N,N-Diethylacetoacetamide [0032] Solvents, including but not limited to: [0033] Mineral spirits [0034] Methyl ethyl ketone [0035] Styrene [0036] Acetone [0037] Methyl methacrylate [0038] Xylene

[0039] The mixture ratio of solvent to promotor can range, for example, from 10:1 to 1000:1, or more particularly from 20:1 to 800:1, or from 50:1 to 500:1, or from 100:1 to 300:1.

[0040] One preferred embodiment applies 1% cobalt-acetone drying solution as the solvent-promoter mixture, applied to the lauan with target coverage of 3 grams/square foot (about 32 grams/square meter). Another example uses cobalt with mineral spirits. Other mixtures, as stated, may be used.

[0041] Also, the promoter used in the solvent-promoter mixture may be one (or more) also used in the resin, or instead may include one or more not used in the resin.

[0042] While the embodiment described above with reference to FIG. 1 is particularly preferred due to the ease of manufacturing the product using that embodiment, other embodiments are also contemplated. A second example of a preferred embodiment of the method is illustrated in FIG. 2. In that embodiment, instead of spraying the promoter onto the wet laminate, the promoter is sprayed onto one surface of the lauan shortly before the lauan is positioned on the wet laminate. Each sheet of lauan, after being sprayed with the proper amount of promoter solution, is turned over and placed with the sprayed surface in contact with the wet laminate.

[0043] Another example is illustrated in FIG. 3, in which the promoter solution is again applied to the lauan rather than to the wet laminate, but the application is done using a roller rather than a spray head. Similarly, to FIG. 2, after application of the promoter, each sheet of lauan is inverted and positioned with the coated surface in contact with the wet laminate. In both variants (FIGS. 2 and 3), the rest of the procedure is the same as in that illustrated in FIG. 1.

[0044] Additional variations in the method are within the broad scope of the present invention. For example, while only application by spraying or by use of a roller have been mentioned, any other mechanized or manual method of application of the promoter that may be found convenient may be used. Also, an individual mold may be used for each panel, or a continuous mold may be used. Again, the mold may be moved past each work station in turn for application of the gel coat, of the wet laminate, of the promoter and of the lauan, and then for the curing, or alternatively the mold may be stationary.

[0045] Results obtained have been good, based on testing including for regularity of product surface or surface profile, and mechanical, such as flex, tensile and, block pull tests, with moisture contents from 0 to 19% (and, particularly, with high moisture content, of e.g., 13-18% and especially 14-17%; all % are weight-%). Moreover, the inventor has found that advantageous results may be obtained regardless of whether the lauan used is sanded or not, and for different thicknesses of lauan. Additionally, the method may yield advantageous results whether the resin used contains a filler, such as mica, or not. Further, it is believed that this method may produce satisfactory results with any moisture content up to the level at which the lauan would be unacceptable based on other criteria.

[0046] Furthermore, while this method has been described with particular relation to the manufacture of a panel having a lauan substrate bonded to a resin-fiberglass layer that is bonded to a gel coat, the method is applicable as well to the manufacture of other types of article in which it is desired to bond lauan or a similar material to a resin layer, whether containing glass fibers or not. The method is also applicable to other woods than lauan, such as plywood, and to other substrates that may carry or absorb moisture.

[0047] While various example embodiments of the present invention have been described above, it should be understood that they have been presented by way of example, and not limitation. It will be apparent to persons skilled in the relevant art(s) that various changes in form and detail can be made therein. Thus, the present invention should not be limited by any of the above described example embodiments, but should be defined only in accordance with the following claims and their equivalents.

[0048] Further, the purpose of the following Abstract is to enable the U.S. Patent and Trademark Office and the public generally, and especially the scientists, engineers and practitioners in the art who are not familiar with patent or legal terms or phraseology, to determine quickly from a cursory inspection the nature and essence of the technical disclosure of the application. The Abstract is not intended to be limiting as to the scope of the example embodiments presented herein in any way. It is also to be understood that the procedures recited in the claims need not be performed in the order presented.