PROCESS FOR MAKING AMMONIUM NITRATE

Abstract

A process of making ammonium nitrate from nitric acid and ammonia in a tubular reactor internally coated with a ceramic coating.

Claims

1-14. (canceled)

15. A process of making ammonium nitrate, the process comprising: introducing nitric acid and ammonia in a tubular reactor; and withdrawing a solution containing ammonium nitrate from the tubular reactor; wherein the tubular reactor is made of a metal material and has an internal coating that includes a ceramic coating.

16. The process according to claim 15, wherein the ceramic coating includes or is made of any of the following: titanium nitride; chromium carbide; hafnium carbide; hafnium carbide; silicon carbide; tantalum carbide; zirconium carbide; oxides of any of hafnium, zirconium, aluminum, silica, tantalum, or combinations thereof; or combinations thereof.

17. The process according to claim 15, wherein the ceramic coating has a roughness that is not greater than 0.20 times a roughness of an uncoated internal surface of the tubular reactor.

18. The process according to claim 17, wherein the roughness of the ceramic coating is in a range 0.10 to 0.01 times the roughness of the uncoated internal surface of the tubular reactor.

19. The process according to claim 15, wherein a hardness of the ceramic coating is greater than a hardness of an uncoated internal surface of the tubular reactor.

20. The process according to claim 19, wherein the hardness of the ceramic coating is at least 3 times greater than the hardness of the uncoated internal surface of the tubular reactor.

21. The process according to claim 19, wherein the hardness of the ceramic coating is 3 to 6 times greater than the hardness of the uncoated internal surface of the tubular reactor.

22. The process according to claim 15, wherein the internal coating is provided on an entire inner surface of the tubular reactor, or only a portion of the inner surface of the tubular reactor.

23. The process according to claim 15, wherein the internal coating is provided at least from an inlet point where nitric acid and ammonia are introduced, to an outlet point where the solution containing ammonium nitrate is withdrawn, or the internal coating is provided on a coated portion of the tubular reactor starting from the inlet point and the coated portion has a length of 2 to 40 times the inner diameter of the tubular reactor.

24. The process according to claim 23, wherein the length is 4 to 35 times the inner diameter of the reactor.

25. The process according to claim 15, wherein a thickness of the ceramic coating is constant in the tubular reactor, or selected regions of an internal surface of the tubular reactor have a differentiated thickness of coating.

26. The process according to claim 15, wherein an increased thickness of the ceramic coating is provided over a portion starting from a point of introduction of ammonia and nitric acid and having a length of 2 to 40 times the inner diameter of the tubular reactor.

27. The process according to claim 26, wherein the length is between 4 and 35 times the inner diameter of the tubular reactor.

28. The process according to claim 15, wherein a thickness of the coating is 30 μm to 300 μm.

29. The process according to claim 15, wherein the tubular reactor is made of steel.

30. The process according to claim 29, wherein the steel includes austenitic steel.

31. The process according to claim 15, wherein the ceramic coating is chemically bonded to an internal surface of the tubular reactor.

32. The process according to claim 15, wherein the tubular reactor has the shape of an elongated tube or elongated pipe.

33. The process according to claim 32, wherein the elongated tube or the elongated pipe has a ratio between a length and an inner diameter that is in a range of 20 to 80.

34. The process according to claim 33, wherein the range of the ratio is 35 to 65.

35. The process according to claim 15, wherein a specific mass flow in the tubular reactor is 80 kg/h per cm.sup.2 to 300 kg/h per cm.sup.2 of the cross-section.

Description

PREFERRED EMBODIMENTS

[0014] Preferred ceramic materials include: Titanium nitride, Chromium carbide, Hafnium carbide, Hafnium carbide, silicon carbide, tantalum carbide, zirconium carbide; oxides of any of Hafnium, Zirconium, Aluminum, Silica and Tantalum; combinations of the above materials. The ceramic coating may include, or be made of, any of the above materials and combinations thereof.

[0015] The internal coating has a surface roughness which is smaller than the surface roughness of the uncoated internal surface of the tubular reactor. Preferably the surface roughness of the coating is not greater than 0.20 times the surface roughness of the uncoated internal surface, more preferably not greater than 0.10 times. Preferably the surface roughness of the coating is to 0.20 to 0.01 and more preferably 0.10 to 0.01 times the roughness of the uncoated surface.

[0016] The reduced roughness will limit the product particle adhesion to the internal surface of the reaction and enforce the erosion resistance of the equipment.

[0017] The surface roughness may be determined according to the ISO 4287:1997 standard as arithmetical mean deviation of the assessed profile, commonly denoted with the symbol Ra.

[0018] The hardness of the ceramic coating may be greater than the hardness of the uncoated material of the pipe reactor. The surface hardness of the ceramic is preferably at least 3 times and more preferably 3 to 6 times the hardness of the uncoated internal surface of the tubular reactor.

[0019] The internal coating may be provided on the entire inside surface of the tubular reactor, or only a portion thereof.

[0020] The thickness of the internal coating may be constant or suitably differentiated.

[0021] The internal coating may be arranged to provide increased protection to selected critical regions found to be more exposed to the above described erosion. This increased protection may be the result of the presence itself of the internal coating in partial coating embodiments, and/or of an increased thickness of the coating.

[0022] The internal ceramic coating is provided, in a preferred embodiment, at least from an inlet point where ammonia and nitric acid are introduced, to an outlet point where the ammonium nitrate solution is withdrawn from the reactor. The inlet point and outlet point may be an inlet flange and outlet flange, respectively.

[0023] In other embodiments the coated portion may be determined in terms of the length of the coated portion compared to the inner diameter of the tubular reactor. In a preferred embodiment the coated portion extends from the above mentioned inlet point (e.g. inlet flange) over a length between 2 to 40 times the inner diameter and more preferably between 4 to 35 times the inner diameter.

[0024] A variable thickness of the internal coating may be provided in some embodiments. In a preferred embodiment an increased thickness of ceramic coating is provided over a determined length starting from said inlet point of the tubular reactor. Said length is more preferably 2 to 40 times the inner diameter of the tubular reactor, particularly preferably 4 to 35 times the inner diameter.

[0025] The thickness of the coating is preferably 30 to 300 microns. Also in embodiments with variable thickness, the variable thickness may be comprised in the above range.

[0026] The tubular reactor may be made of steel, preferably austenitic steel.

[0027] The coating may be provided with a mechanical, physical or chemical deposition process.

[0028] The ceramic coating may be chemically bonded to the internal surface of the tubular reactor. For example the ceramic coating may be chemically bonded to the stainless steel over the internal surface of the tubular reactor.

[0029] The tubular reactor may have the shape of an elongated tube or elongated pipe. Accordingly the length of the tubular reactor is several times greater than its diameter. The size of the tubular reactor may be defined in terms of the ratio between length and diameter, e.g. the inner diameter. In a preferred embodiment the tubular reactor has a ratio L/D of length over inner diameter which is comprised between 20 and 100. More preferably said ratio L/D is 35 to 65.

[0030] The specific mass flow in the tubular reactor may be 80 to 300 kg/h per cm.sup.2 of the cross section.

[0031] Another aspect of the invention is an ammonium nitrate pipe reactor, for use in the production of ammonium nitrate by reacting nitric acid and ammonia, said reactor being a tubular reactor made of a metal material and having an internal ceramic coating.

[0032] All the above described preferred embodiments are applicable to the pipe reactor. An ammonium nitrate pipe reactor with features recited in the attached claims is also disclosed.