HOT BLOW FORMING METHOD FOR ALUMINUM ALLOY SHEET

Abstract

A hot blow forming method for the aluminum alloy sheet carries out a hot blow forming to an aluminum alloy sheet using a first metal mold being a female mold for forming having a protruding surface portion on an inside surface thereof and a second metal mold for gas introduction. Immediately prior to the hot blow forming, a temperature (T1) of the aluminum alloy sheet and a temperature (T2) of the first metal mold satisfy a relation (T1)−(T2)≧30° C. and the temperature (T2) is equal to or higher than 400° C. In the hot blow forming, the aluminum alloy sheet is made to be brought into contact with at least a part of the protruding surface portion of the first metal mold within 30 seconds from a start of the gas introduction from the second metal mold.

Claims

1. A hot blow forming method for an aluminum alloy sheet comprising: carrying out hot blow forming for the aluminum alloy sheet using a first metal mold, which is a female mold for forming having a protruding surface portion on an inside surface thereof, and a second metal mold for gas introduction, wherein, immediately prior to the hot blow forming, a temperature (T1) of the aluminum alloy sheet and a temperature (T2) of the first metal mold satisfy a relation (T1)−(T2)≧30° C., and the temperature (T2) is equal to or more than 400° C., and wherein, in the hot blow forming, the aluminum alloy sheet is brought into contact with at least a part of the protruding surface portion of the first metal mold within 30 seconds from a start of gas introduction from the second metal mold.

2. The hot blow forming method for an aluminum alloy sheet according to claim 1, wherein a temperature (T3) of the second metal mold immediately prior to the hot blow forming is lower than a melting point of the aluminum alloy sheet and is equal to or higher than the temperature (T1).

3. The hot blow forming method for an aluminum alloy sheet according to claim 1, wherein the aluminum alloy sheet is an aluminum alloy sheet comprising, by mass %, 1.1 to 6.5% Mg, 0.01 to 0.3% Fe, and a balance Al and inevitable impurities, and wherein the temperature (T1) is equal to or lower than 550° C.

4. The hot blow forming method for an aluminum alloy sheet according to claim 1, wherein the aluminum alloy sheet is an aluminum alloy sheet composed of, by mass %, 0.2 to 2.0% Si, 0.2 to 1.5% Mg, 0.01 to 0.3% Fe, and a balance Al and inevitable impurities, and wherein the temperature (T1) is equal to or lower than 550° C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0012] FIG. 1 is a perspective view illustrating an aluminum alloy sheet and a mold.

[0013] FIG. 2 is a cross-sectional view illustrating an aluminum alloy sheet and a mold for Experiment 1.

[0014] FIG. 3 is a schematic view illustrating a first mold for Experiment 1.

[0015] FIG. 4 is a cross-sectional view with respect to arrows IV to IV in FIG. 3.

[0016] FIG. 5 is a cross-sectional view illustrating the aluminum alloy sheet in contact with a forming surface of the first mold in Experiment 1.

[0017] FIG. 6 is a cross-sectional view illustrating the aluminum alloy sheet formed by the forming surface of the first mold in Experiment 1.

[0018] FIG. 7 is a cross-sectional view illustrating an aluminum alloy sheet and a mold for Experiment 2.

[0019] FIG. 8 is a schematic view illustrating a first mold for Experiment 2.

[0020] FIG. 9 is a cross-sectional view with respect to arrows IX to IX in FIG. 8.

[0021] FIG. 10 is a sectional view illustrating the aluminum alloy sheet in contact with a forming surface of the first mold in Experiment 2.

[0022] FIG. 11 is a cross-sectional view illustrating the aluminum alloy sheet formed by the forming surface of the first mold in Experiment 2.

EXPLANATION OF REFERENCE NUMERALS

[0023] 1 . . . aluminum alloy sheet, 21 . . . first metal mold, 210 . . . inside surface (inside surface of the first metal mold), 211 . . . protruding surface portion, 22 . . . second metal mold

MODE FOR CARRYING OUT THE INVENTION

[0024] The embodiments of the present invention will be described below. It is apparent that the present invention is not limited to the illustrative embodiments set forth herein and various modifications may be applicable without departing from the scope and spirit of the invention.

[0025] In the hot blow forming method for the aluminum alloy sheet, a hot blow forming is carried out to an aluminum alloy sheet by use of a first metal mold, which is a female mold for forming having a protruding surface portion on an inside surface, and a second metal mold for gas introduction.

[0026] The first metal mold is a recessed female mold for female forming an aluminum alloy sheet. The inside surface of the first metal mold is a forming surface which forms the aluminum alloy sheet to a predetermined shape. The protruding surface portion is provided at the inside surface of the first metal mold. The protruding surface portion may be configured with, for example, a curved surface (R surface and so on), multiple flat surfaces, or a combination thereof.

[0027] The second metal mold is a mold for gas introduction for introducing a high pressure gas for blow forming. It is good that the distance between the second metal mold and the aluminum alloy sheet at a time of hot blow forming is as close as possible in terms that a temperature ((T3) described later) of the second metal mold is made the same as or approximate to a temperature (T1) of the aluminum alloy sheet. For example, it is preferable that the distance between the gas introduction surface of the second metal mold and the aluminum alloy sheet is equal to or lower than 50 mm.

[0028] In the hot blow forming, forming is carried out by spraying a high pressure gas to the aluminum alloy sheet and pressing the aluminum alloy sheet to the inside surface (forming surface) of the first metal mold being the female mold for forming. In order that the reaction between the high pressure gas and the aluminum alloy sheet does not occur, for example, an inert gas, such as nitrogen gas and so on, is preferably used as the high pressure gas for blow forming.

[0029] According to the hot blow forming method for the aluminum alloy sheet, immediately prior to the hot blow forming, the temperature (T1) of the aluminum alloy sheet and the temperature (T2) of the first metal mold satisfy a relation (T1)−(T2)≧30° C., and the temperature (T2) is equal to or more than 400° C.

[0030] In order to inhibit cracking of the aluminum alloy sheet, which easily occurs at the protruding surface portion of the inside surface of the first metal mold being the female mold for forming, at the time of hot blow forming, it is necessary to set, during the hot blow forming, a deformation resistance of a portion of the aluminum alloy sheet in contact with the protruding surface of the inside surface of the first metal mold higher than a deformation resistance of a portion of the aluminum alloy sheet not in contact with the inside surface of the first metal mold. Accordingly, it is necessary that the temperature (T1) of the aluminum alloy sheet and the temperature (T2) of the first metal mold immediately prior to the hot blow forming satisfy the relation (T1)−(T2)≧30° C. It is more preferable that the two temperatures (T1) and (T2) satisfy the relation (T1)−(T2)≧50° C.

[0031] At a time of (T1)−(T2)<30° C., a difference between the deformation resistance of the portion of the aluminum alloy sheet in contact with the protruding surface portion on the inside surface of the first metal mold and the deformation resistance of the portion of the aluminum alloy sheet not in contact with the inside surface of the first metal mold becomes small during the hot blow forming. In this case, cracking of the aluminum alloy sheet at the protruding surface portion on the inside surface of the first metal mold may not be inhibited sufficiently.

[0032] Out of values aluminum alloys, for example, regarding an Al—Mg—Si based aluminum alloy (JIS6000-series aluminum alloy, hereinafter referred to as 6000-series aluminum alloy), which is a heat treatment type alloy, precipitation becomes remarkable and blow formability becomes remarkably lower in a temperature range lower than 400° C. Therefore, it is necessary for the temperature (T2) to be equal to or more than 400° C. in order to secure sufficient blow formability of aluminum alloy.

[0033] When the temperature (T2) is lower than 400° C., the ductility of the portion of the aluminum alloy in contact with the protruding surface portion on the inside surface of the first metal mold becomes extremely lower at the time of hot blow forming, and cracking of the aluminum alloy sheet at the protruding surface portion of the inside surface of the first metal mold is not sufficiently suppressed.

[0034] When the temperature (T2) is lower than 400° C., the deformation resistance of the portion of the aluminum alloy in contact with the protruding surface portion of the inside surface of the first metal mold becomes higher. Especially when an Al—Mg based aluminum alloy having Mg content of 4 mass % or more (JIS5000-series aluminum alloy, hereinafter referred to as 5000-series aluminum alloy) is used, the aluminum alloy sheet is not able to be brought into contact with the protruding surface portion of the inside surface of the first metal mold within 30 seconds from a start of the gas introduction from the second metal mold at a gas pressure lower than 1 MPa that is not considered as a high pressure container in Japan.

[0035] According to the hot blow forming method for the aluminum alloy sheet, through the hot blow forming, the aluminum alloy sheet is made to be brought into contact with at least a part of the protruding surface portion of the first metal mold within 30 seconds from a start of the gas introduction from the second metal mold.

[0036] When the aluminum alloy sheet is not made to be brought into contact with the protruding surface portion of the inside surface of the first metal mold within 30 seconds from a start of the gas introduction using the second metal mold during the hot blow forming, the difference between the deformation resistance of the portion of the aluminum alloy sheet in contact with the protruding surface portion of the inside surface of the first metal mold and the deformation resistance of the portion of the aluminum alloy sheet not in contact with the inside surface of the first metal mold becomes small due to thermal diffusion from the aluminum alloy sheet to the first metal mold. In this case, cracking of the aluminum alloy sheet at the protruding surface portion of the inside surface of the first metal mold is not sufficiently inhibited.

[0037] During the hot blow forming, it is preferable that the temperature difference between the aluminum alloy sheet and the first metal mold is equal to or more than 30° C. until the compression of forming of a portion of the aluminum alloy sheet corresponding to the protruding surface portion of the inside surface of the first metal mold (until the contact of the aluminum alloy sheet with the entire protruding surface portion of the inside surface of the first metal mold.) That is, it is preferable to keep the temperature condition ((T1)−(T2)≧30° C.) immediately prior to the hot blow forming. In this case, it is possible to inhibit more stably cracking of the aluminum alloy sheet which may easily occur at the protruding surface portion of the inside surface of the first metal mold being the female mold for forming at the time of hot blow forming.

[0038] According to the hot blow forming method for the aluminum alloy sheet, the temperature (T3) of the second metal mold immediately before the hot blow forming may be lower than the melting point of the aluminum alloy sheet and equal to or higher than the temperature (T1). In this case, by controlling the temperature (T3) of the second metal mold immediately prior to hot blowing within a predetermined temperature range, it is possible to control the temperature (T1) of the aluminum alloy sheet immediately prior to hot blowing not to become low. Therefore, cracking of the aluminum alloy sheet, which easily occurs at the protruding surface portion of the inside surface of the first metal mold being the female mold for forming, is suppressed more stably at the time of hot blow forming.

[0039] In order not to melt the aluminum alloy sheet prior to hot blow forming, it is necessary, for example, to control the temperature (T3) of the second metal mold lower than the melting point of the aluminum alloy sheet while the aluminum alloy sheet is being held by the first and second metal molds.

[0040] The hot blow forming method for the aluminum alloy sheet is applicable to an aluminum alloy sheet having a melting point greater than 430° C. Aluminum alloys are selected depending upon usages, so aluminum alloys are not necessarily limited. However, when the hot blow forming is applied to a component for transporter such as automobile, to a component for a home electric appliance such as digital camera, personal computer, the formed product after the hot blow forming is required to have enough strength and appearance quality (surface quality). Therefore, such 5000-series aluminum alloy, 6000-series aluminum alloy and so on are considered to be appropriate aluminum alloy.

[0041] According to the hot blow forming method for the aluminum alloy sheet, the aluminum alloy sheet is an aluminum alloy sheet composed of, by mass %, 1.1 to 6.5% Mg, 0.01 to 0.3% Fe, and the balance Al and inevitable impurities, and the temperature (T1) may be equal to or lower than 550° C. In this case, usage of aluminum alloy sheet composed of the 5000-series aluminum alloy can secure enough strength and appearance quality (surface quality) for the formed product after being subjected to the hot blow forming.

[0042] In terms of strength, the 5000-series aluminum alloy composing the aluminum alloy sheet preferably contains 1.1 to 6.5% Mg. When the Mg content is lower than 1.1%, the strength required for components for transporters, home electric appliances, and so on, is not obtained, and shortage of strength is likely to occur. When the Mg content is more than 6.5%, cracking may occur by casting or hot rolling.

[0043] In terms of appearance quality, the 5000-series aluminum alloy composing the aluminum alloy sheet preferably contains 0.01 to 0.3% Fe so that crystal grain after the compression of hot blow forming becomes fine. When the Fe content is lower than 0.01%, coarsening of the crystal grain may occur during the hot blow forming and surface roughness called orange peel may easily occur, which may cause defects of outer appearance. When the Fe content is more than 0.3%, coarse crystalized products are easily generated by casting and cracking may occur at the time of hot rolling.

[0044] Coarsening of the crystal grain of the aluminum alloy sheet during the hot blow forming is influenced by the hot blow forming conditions as well as by chemical components of aluminum alloy (5000-series aluminum alloy). Especially, when the temperature of the aluminum alloy sheet during the hot blow forming is high, the crystal grain is likely to be coarsened. Therefore, it is preferable that the temperature (T1) of the aluminum alloy sheet immediately prior to the hot blow forming is equal to or lower than 550° C., further preferably equal to or lower than 530° C. When the temperature (T1) is more than 550° C., the crystal grain is likely to be coarsened during the hot blow forming and generation of orange peels on the surface of the formed product is likely to occur. This may result in poor appearance of the formed product.

[0045] According to the hot blow forming method for the aluminum alloy sheet, the aluminum alloy sheet is an aluminum alloy sheet composed of, by mass %, 0.2 to 2.0% Si, 0.2 to 1.5% Mg, 0.01 to 0.3% Fe, and the balance Al and inevitable impurities, and the temperature (T1) may be equal to or lower than 550° C. In this case, usage of an aluminum alloy sheet composed of the 6000-series aluminum alloy can secure enough strength and appearance quality (surface quality) for the formed product after being subjected to the hot blow forming.

[0046] In terms of strength, the 6000-series aluminum alloy composing the aluminum alloy sheet preferably contains 0.2 to 2.0% Si and 0.2 to 1.5% Mg. When the Si content is lower than 0.2% and/or when the Mg content is lower than 0.2%, it is likely that the strength required for components for transporters, home electric appliances, and so on, is not obtained, and that shortage of strength occur. When the Si content is more than 2.0% and/or when the Mg content is more than 1.5%, coarse crystalized products are likely to be created upon casting, which may lead to occurrence of cracking upon hot rolling.

[0047] In terms of appearance quality, the 6000-series aluminum alloy composing the aluminum alloy sheet preferably contains 0.01 to 0.3% Fe so that crystal grain after the compression of hot blow forming becomes fine. When the Fe content is lower than 0.01%, coarsening of the crystal grain may occur during the hot blow forming and surface roughness called orange peel may easily occur, which lead to defects of outer appearance. When the Fe content is more than 0.3%, coarse crystalized products are easily generated by casting and cracking may occur at the time of hot rolling.

[0048] Coarsening of the crystal grain of the aluminum alloy sheet during the hot blow forming is influenced by the hot blow forming conditions as well as by chemical components of aluminum alloy (6000-series aluminum alloy). Especially, when the temperature of the aluminum alloy sheet during the hot blow forming is high, the crystal grain is likely to be coarsened. Therefore, it is preferable that the temperature (T1) of the aluminum alloy sheet immediately prior to the hot blow forming is equal to or lower than 550° C., further preferably equal to or lower than 530° C. When the temperature (T1) is more than 550° C., crystal grain is likely to be coarsened during the hot blow forming and generation of orange peels on the surface of the formed product is likely to occur. This may result in poor appearance of the formed product.

Embodiments

[0049] Embodiments of the present invention will be described below compared with comparative examples. There embodiments illustratively describe the present invention and the present invention shall not be limited hereto.

<Aluminum Alloy Sheet (Blank Member)>

[0050] Aluminum alloys having chemical compositions summarized in Table 1 were ingot-made by DC casting and cooled to a room temperature after being subjected to homogenization treatment under the conditions summarized in Table 1. “Bal.” in Table 1 denotes the balance (Balance). The melting points of the aluminum alloys 5023, 5083, and 6016 are 562° C., 574° C., and 588° C., respectively.

[0051] The obtained aluminum alloy ingots were then heated again to 400° C., and then the ingots were subjected to hot rolling, so that hot rolled sheets with the thickness 5.0 mm were obtained. The hot rolling end temperature was 250° C. Further, the obtained hot rolled sheets were subjected to cool rolling to have 1.0 mm in thickness and to annealing at 400° C. for an hour, so that aluminum alloy sheets (blank members) for hot blow forming were obtained.

TABLE-US-00001 TABLE 1 Homogenization Contained Components (mass %) Treatment Alloy Si Fe Cu Mn Mg Cr Zn Ti Al (Temp. - Time) 5023 0.03 0.04 0.2 0.01 5.2 <0.01 <0.01 0.03 Bal. 450° C. - 12 h 5083 0.03 0.05 <0.01 0.67 4.6 0.15 <0.01 0.02 Bal. 500° C. - 12 h 6016 1.10 0.13 <0.01 0.10 0.6 <0.01 0.0 0.03 Bal. 550° C. - 12 h

Embodiment 1

<Metal Mold for Forming>

[0052] As illustrated in FIGS. 1 and 2, a metal mold for forming 2 has a recessed first metal mold 21 being a female mold for forming and a second metal mold 22 for gas introduction. The metal mold for forming 2 is configured so that an aluminum alloy sheet 1 is held by the first metal mold 21 and the second metal mold 22. The second metal mold 22 has a gas introduction conduit 221 to introduce high pressure gas for blow forming.

[0053] As illustrated in FIGS. 3 and 4, provided on an inside surface (forming surface) 210 of the first metal mold 21 is a protruding surface portion 211 protruding towards the inside of the first metal mold 21. The protruding surface portion 211 has 60 mm in height from the bottom surface of the first metal mold 21. A top 212 of the protruding surface portion 211 is formed into a curved surface having a curvature radius of 5 mm.

[0054] <Blow Formability>

[0055] As illustrated in FIGS. 5 and 6, hot blow formings having various conditions were carried out to the aluminum alloy sheet 1 by use of the aforementioned metal mold for forming 2. Table 2 summarizes various conditions including the temperature (T1) of the aluminum alloy sheet immediately prior to the hot blow forming, the temperature (T2) of the first metal mold immediately prior to the hot blow forming, the temperature (T3) of the second metal mold immediately prior to the hot blow forming, and the gas pressure. When the gas pressure is 0.98 to 0.99 MPa, the gas pressure is rounded and described as 1 MPa.

[0056] As illustrated in FIG. 5, for the hot blow forming, in a state where the aluminum alloy sheet 1 has been held by the first metal mold 21 and the second metal mold 22 of the metal mold for forming 2, a high pressure gas G was introduced into the metal mold for forming 2 from the gas introduction conduit 221 of the second metal mold 22 and was sprayed to the aluminum alloy sheet 1 from the side of the second metal mold 22. As illustrated in FIG. 6, the aluminum alloy sheet 1 was pressed to the inside surface (forming surface) 210 of the first metal mold 21 so as to be formed to a predetermined shape. A distance D between the gas introduction surface of the second metal mold 22 and the aluminum alloy sheet 1 was 50 mm, and nitrogen gas was employed as the gas G.

[0057] The pass/fail assessment of the blow formability was made for the occurrence of cracking of aluminum alloy sheet at the protruding surface portion (especially, the top) of the inside surface (forming surface) of the first metal mold during the hot blow forming. The aluminum alloy sheet with no cracking passed (◯: no cracking) and the one with cracking failed (×: with cracking).

TABLE-US-00002 TABLE 2 Aluminum First Second Alloy Sheet Metal Mold Metal Mold Gas Forming Temp. (T1) Temp. (T2) Temp. (T3) Pressure Time Blow Sample Alloy (° C.) (° C.) (° C.) (MPa) (second) Formability EMBODIMENT 1 5023 430 400 430 1 30 ∘ 2 5023 500 450 520 1 15 ∘ 3 5083 430 400 430 1 30 ∘ 4 5083 540 400 550 1 20 ∘ 5 6016 430 400 430 1 30 ∘ 6 6016 550 500 550 0.5 10 ∘ COMPARATIVE 7 5023 425 400 425 1 30 x 8 5023 500 475 500 1 30 x 9 5023 430 400 430 0.5 60 x 10 5083 425 400 425 1 30 x 11 5083 520 500 520 1 25 x 12 5083 430 400 430 0.5 60 x 13 5083 390 360 390 1 70 x 14 6016 425 400 425 1 30 x 15 6016 540 525 540 0.5 10 x 16 6016 430 400 430 0.2 50 x 17 6016 400 370 400 1 30 x

[0058] Table 2 summarizes the results of blow formabilities for the respective samples. The forming time in Table 2 is a period of time from the start of gas introduction to the moment when the aluminum alloy sheet contacts the protruding surface portion of the first metal mold (a period of time from the start of gas introduction to the moment when the aluminum alloy sheet is shifted to the state illustrated in FIG. 5).

[0059] Samples 1 to 6 satisfy the relation (T1)−(T2)≧30° C., the temperatures (T2) thereof are equal to or more than 400° C., and the forming times thereof are within 30 seconds. For Samples 1 to 6, no cracking occurred at the protruding surface portion of the first metal mold, and preferable blow formabilities were obtained.

[0060] Samples 7, 8, 10, 11, 14, and 15 do not satisfy the relation (T1)−(T2)≧30° C. The temperature (T2) of Sample 17 is lower than 400° C. For Samples 7, 8, 10, 11, 14, 15, and 17, cracking occurred at the protruding surface portion of the first metal mold.

[0061] Samples 9, 12, 13, and 16 did not contact the protruding surface portion of the first metal mold within 30 seconds of the forming time and contacted the protruding surface portion of the first metal mold in the forming time over 30 seconds of the forming time. The temperature (T2) of Sample 13 is lower than 400° C. For samples 9, 12, 13, and 16, cracking occurred at the protruding surface portion of the first metal mold.

Embodiment 2

[0062] <Metal Mold for Forming>

[0063] As illustrated in FIG. 7, a metal mold for forming 2 has a recessed first metal mold 21 being a female mold for forming and a second metal mold 22 for gas introduction. The metal mold for forming 2 is configured so that the aluminum alloy sheet 1 is held by the first metal mold 21 and the second metal mold 22. The second metal mold 22 has a gas introduction conduit 221 to introduce high pressure gas for blow forming.

[0064] As illustrated in FIGS. 8 and 9, provided on an inside surface (forming surface) 210 of the first metal mold 21 is a protruding surface portion 211 protruding towards the inside of the first metal mold 21. The protruding surface portion 211 has 70 mm in height from the bottom surface of the first old 21. A top 212 of the protruding surface portion 211 is formed into a curved surface having a curvature radius of 6 mm.

[0065] <Blow Formability>

[0066] As illustrated in FIGS. 10 and 11, hot blow formings having various conditions were carried out to an aluminum alloy sheet 1 by use of the aforementioned metal mold for forming 2. Table 3 summarizes various conditions including the temperature (T1) of the aluminum alloy sheet immediately prior to the hot blow forming, the temperature (T2) of the first metal mold immediately prior to the hot blow forming, the temperature (T3) of the second metal mold immediately prior to the hot blow forming, and the gas pressure. When the gas pressure is 0.98 to 0.99 MPa, the gas pressure was rounded and described as 1 MPa.

[0067] As illustrated in FIG. 10, for the hot blow forming, in a state where the aluminum alloy sheet 1 has been held by the first metal mold 21 and the second metal mold 22 of the metal mold for forming 2, a high pressure gas G was introduced into the metal mold for forming 2 from the gas introduction conduit 221 of the second metal mold 22 and was sprayed to the aluminum alloy sheet 1 from the side of the second metal mold 22. As illustrated in FIG. 11, the aluminum alloy sheet 1 was pressed to the inside surface (forming surface) 210 of the first metal mold 21 so as to be formed to a predetermined shape. A distance D between the gas introduction surface of the second metal mold 22 and the aluminum alloy sheet 1 was 50 mm, and nitrogen gas was employed as the gas G.

[0068] The pass/fail assessment of the blow formability is made for the occurrence of cracking of aluminum alloy sheet at the protruding surface portion (especially top) of the inside surface (forming surface) of the first metal mold during the hot blow forming. The aluminum alloy sheet with no cracking passed (◯: no cracking) and the one with cracking failed (×: with cracking).

[0069] <Orange Peel Occurrence>

[0070] For the surfaces of the formed products after being subjected to the hot blow forming, the surface roughness was measured by a contact-type surface roughness meter. The formed product passed (◯: no occurrence) when it was Rz≧20 μm (Rz: Maximum Height Roughness) and failed (×: with occurrence) when it was Rz>20 μm (Rz: Maximum Height Roughness).

TABLE-US-00003 TABLE 3 Aluminum First Second Alloy Sheet Metal Mold Metal Mold Gas Forming Temp. (T1) Temp. (T2) Temp. (T3) Pressure Time Blow Orange Peel Sample Alloy (° C. ) (° C. ) (° C. ) (MPa) (second) Formability Occurrence EMBODIMENT 18 5023 430 400 430 1 30 ∘ ∘ 19 5023 520 420 530 1 20 ∘ ∘ 20 5083 430 400 430 1 30 ∘ ∘ 21 5083 530 400 545 1 20 ∘ ∘ 22 6016 430 400 430 1 30 ∘ ∘ 23 6016 540 480 545 0.5 10 ∘ ∘ COMPARATIVE 24 5023 425 400 425 1 30 x ∘ 25 5023 520 500 520 1 30 x ∘ 26 5023 430 400 430 0.6 50 x ∘ 27 5083 425 400 425 1 30 x ∘ 28 5083 555 530 560 1 20 x x 29 5083 430 400 430 0.6 50 x ∘ 30 5083 390 360 390 1 60 x ∘ 31 6016 425 400 425 1 30 x ∘ 32 6016 560 545 560 0.7 5 x x 33 6016 430 400 430 0.3 40 x ∘ 34 6016 410 380 410 1 30 x ∘

[0071] Table 3 summarizes the results of blow formabilities and orange peel occurrences for the respective samples. The forming time in Table 3 is a period of time from the start of gas introduction to the moment when the aluminum alloy sheet contacts the protruding surface portion of the first metal mold (a period of time from the start of gas introduction to the moment when the aluminum alloy sheet is shifted to the state illustrated in FIG. 10).

[0072] Samples 18 to 23 satisfied the relation (T1)−(T2)≧30° C., the temperatures (T2) thereof were equal to or more than 400° C., and the forming times in which the aluminum alloy sheets contacted the protruding surface portion of the inside surface of the first metal mold were within 30 seconds. For Samples 18 to 23, no cracking occurred at the protruding surface portion of the first metal mold, and preferable blow formabilities were obtained. In addition, no orange peel occurred on the surfaces of the formed products after being subjected to forming.

[0073] Samples 24, 25, 27, 28, 31, and 32 do not satisfy the relation (T1)−(T2)≧30° C. The temperature (T2) of Sample 34 is lower than 400° C. For Samples 24, 25, 27, 28, 31, 32, and 34, cracking occurred at the protruding surface portion of the first metal mold.

[0074] Samples 26, 29, 30, and 33 did not contact the protruding surface portion of the first metal mold within 30 seconds of the forming time and contacted the protruding surface portion of the first metal mold in the forming time over 30 seconds of the forming time. The temperature (T2) of Sample 30 is lower than 400° C. For Samples 26, 29, 30, and 33, cracking occurred at the protruding surface portion of the first metal mold.

[0075] The temperatures (T1) of Samples 28 and 32 are higher than 550° C. For Samples 28 and 32, orange peels occurred on the surfaces of the formed products after being subjected to the forming.