PROCESS FOR POLYMERISING LACTIDE INTO POLYLACTIC ACID
20230174712 · 2023-06-08
Assignee
Inventors
Cpc classification
International classification
Abstract
The present invention relates to a process for polymerising lactide into polylactic acid. The present invention also relates to reactor configuration for polymerising lactide into polylactic acid.
Claims
1. A process for polymerising lactide into polylactic acid, the process comprising the steps of: feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or meso-lactide; and, wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed.
2. A process for polymerising lactide into polylactic acid, the process comprising the steps of: feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or meso-lactide; and, wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed.
3. The process according to claim 1, wherein the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at least 30% of the total residence time, preferably after at least 40%, preferably after at least 50%, preferably after at least 60%, preferably after at least 70%, preferably after at least 75% of the total residence time, preferably after at least 76%, preferably after at least 77%, preferably after at least 78%, preferably after at least 79%, preferably after at least 80%.
4. The process according to claim 1, wherein the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at most 90%, preferably after at most 85%, for example after at most 80% of the total residence time.
5. The process according to claim 1, wherein the first lactide feed is essentially free of D-lactide or essentially free of L-lactide.
6. The process according to claim 1, wherein the first lactide feed is essentially free of Meso-lactide.
7. The process according to claim 1, wherein the polylactic acid is not a stereo-block copolymer.
8. The process according to claim 1, wherein the second lactide feed comprises at least 90% by weight D-lactide, compared to the total weight of the second lactide feed, preferably at least 95% D-lactide, preferably at least 97% D-lactide, preferably at least 98% D-lactide, preferably at least 99% D-lactide.
9. The process according to claim 1, wherein the second lactide feed comprises at least 30% by weight Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 35% Meso-lactide, preferably at least 40% Meso-lactide, preferably at least 45% Meso-lactide, preferably at least 50% Meso-lactide, compared to the total weight of the second lactide feed.
10. A reactor configuration for polymerising lactide into polylactic acid, the reactor configuration comprising: a first polymerisation reactor section; a first lactide feeding line for feeding a first lactide feed into the first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; a second polymerisation section; a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or Meso-lactide; and, wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed.
11. A reactor configuration for polymerising lactide into polylactic acid, the reactor configuration comprising: a first polymerisation reactor section; a first lactide feeding line for feeding a first lactide feed into the first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; a second polymerisation section; a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or Meso-lactide; and, wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed.
12. The reactor configuration according to claim 10, wherein the first polymerisation reactor section comprises one or more CSTR type reactors.
13. The reactor configuration according to claim 10, wherein the first polymerisation reactor section comprises one or more CSTR type reactors and one or more PFR type reactors.
14. The reactor configuration according to claim 10, wherein the second polymerisation reactor section comprises one or more PFR type reactors.
15. The process according to claim 1 performed in a reactor configuration for polymerising lactide into polylactic acid, the reactor configuration comprising: a first polymerisation reactor section; a first lactide feeding line for feeding a first lactide feed into the first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; a second polymerisation section; a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or Meso-lactide; and, wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0041]
[0042]
[0043]
[0044]
DETAILED DESCRIPTION OF THE INVENTION
[0045] Before the present method used in the invention is described, it is to be understood that this invention is not limited to particular methods described, as such methods may, of course, vary. It is also to be understood that the terminology used herein is not intended to be limiting, since the scope of the present invention will be limited only by the appended claims.
[0046] When describing the processes and reactor configurations of the invention, the terms used are to be construed in accordance with the following definitions, unless a context dictates otherwise. As used herein, the singular forms “a”, “an”, and “the” include both singular and plural referents unless the context clearly dictates otherwise. By way of example, “a reactor” means one reactor or more than one reactor.
[0047] The terms “comprising”, “comprises” and “comprised of” as used herein are synonymous with “including”, “includes” or “containing”, “contains”, and are inclusive or open-ended and do not exclude additional, non-recited members, elements or method steps. The terms “comprising”, “comprises” and “comprised of” also include the term “consisting of”.
[0048] The recitation of numerical ranges by endpoints includes all integer numbers and, where appropriate, fractions subsumed within that range (e.g. 1 to 5 can include 1, 2, 3, 4 when referring to, for example, a number of elements, and can also include 1.5, 2, 2.75 and 3.80, when referring to, for example, measurements). The recitation of end points also includes the end point values themselves (e.g. from 1.0 to 5.0 includes both 1.0 and 5.0). Any numerical range recited herein is intended to include all sub-ranges subsumed therein.
[0049] Reference throughout this specification to “one embodiment” or “an embodiment” means that a particular feature, structure or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily all referring to the same embodiment, but may. Furthermore, the particular features, structures or characteristics may be combined in any suitable manner, as would be apparent to a person skilled in the art from this disclosure, in one or more embodiments. Furthermore, while some embodiments described herein include some but not other features included in other embodiments, combinations of features of different embodiments are meant to be within the scope of the invention, and form different embodiments, as would be understood by those in the art. For example, in the following claims and statements, any of the embodiments can be used in any combination.
[0050] Unless otherwise defined, all terms used in disclosing the invention, including technical and scientific terms, have the meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. By means of further guidance, definitions for the terms used in the description are included to better appreciate the teaching of the present invention.
[0051] Preferred statements (features) and embodiments of the methods of this invention are set herein below. Each statement and embodiment of the invention so defined may be combined with any other statement and/or embodiments unless clearly indicated to the contrary. In particular, any feature indicated as being preferred or advantageous may be combined with any other feature or features or statements indicated as being preferred or advantageous. Hereto, the present invention is in particular captured by any one or any combination of one or more of the below numbered statements 1 to 38 and/or embodiments with any other statement(s) and/or embodiment(s). [0052] 1. A process for polymerising lactide into polylactic acid, the process comprising the steps of: [0053] feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; [0054] feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, [0055] feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, preferably after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed. [0056] 2. A process for polymerising lactide into polylactic acid, the process comprising the steps of: [0057] feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; [0058] feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, [0059] feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, preferably after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed. [0060] 3. A reactor configuration for polymerising lactide into polylactic acid, the reactor configuration comprising: [0061] a first polymerisation reactor section; [0062] a first lactide feeding line for feeding a first lactide feed into the first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; [0063] a second polymerisation section; [0064] a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, [0065] a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines preferably configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or Meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed. [0066] 4. A reactor configuration for polymerising lactide into polylactic acid, the reactor configuration comprising: [0067] a first polymerisation reactor section; [0068] a first lactide feeding line for feeding a first lactide feed into the first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; [0069] a second polymerisation section; [0070] a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, [0071] a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines preferably configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or Meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed. [0072] 5. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at least 30% of the total residence time, preferably after at least 40%, preferably after at least 50%, preferably after at least 60%, preferably after at least 70%. [0073] 6. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at least 75% of the total residence time, preferably after at least 76%, preferably after at least 77%, preferably after at least 78%, preferably after at least 79%, preferably after at least 80%. [0074] 7. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at most 95% of the total residence time, preferably after at most 90%, preferably after at most 85%, for example after at most 80%. [0075] 8. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed comprises at most 5% by weight D-lactide, compared to the total weight of the lactide feed, preferably at most 4% D-lactide, preferably at most 3% D-lactide, preferably at most 2% D-lactide, preferably at most 1% D-lactide. [0076] 9. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed is essentially free of D-lactide. [0077] 10. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed comprises at most 5% by weight L-lactide, compared to the total weight of the lactide feed, preferably at most 4% L-lactide, preferably at most 3% L-lactide, preferably at most 2% L-lactide, preferably at most 1% L-lactide. [0078] 11. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed is essentially free of L-lactide. [0079] 12. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed comprises at most 5% by weight Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% Meso-lactide, preferably at most 3% Meso-lactide, preferably at most 2% Meso-lactide, preferably at most 1% Meso-lactide. [0080] 13. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed is essentially free of Meso-lactide. [0081] 14. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed comprises at most 5% by weight D/Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% D/Meso-lactide, preferably at most 3% D/Meso-lactide, preferably at most 2% D/Meso-lactide, preferably at most 1% D/Meso-lactide. [0082] 15. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed is essentially free of D/Meso-lactide. [0083] 16. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed comprises at most 5% by weight L/Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% L/Meso-lactide, preferably at most 3% L/Meso-lactide, preferably at most 2% L/Meso-lactide, preferably at most 1% L/Meso-lactide. [0084] 17. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first lactide feed is essentially free of L/Meso-lactide. [0085] 18. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 90% by weight D-lactide, compared to the total weight of the second lactide feed, preferably at least 95% D-lactide, preferably at least 97% D-lactide, preferably at least 98% D-lactide, preferably at least 99% D-lactide. [0086] 19. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 90% by weight L-lactide, compared to the total weight of the second lactide feed, preferably at least 95% L-lactide, preferably at least 97% L-lactide, preferably at least 98% L-lactide, preferably at least 99% L-lactide. [0087] 20. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 30% by weight Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 35% Meso-lactide, preferably at least 40% Meso-lactide, preferably at least 45% Meso-lactide, preferably at least 50% Meso-lactide. [0088] 21. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 50% D/Meso-lactide, preferably at least 60% D/Meso-lactide, preferably at least 70% D/Meso-lactide, preferably at least 80% D/Meso-lactide. [0089] 22. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 50% L/Meso-lactide, preferably at least 60% L/Meso-lactide, preferably at least 70% L/Meso-lactide, preferably at least 80% L/Meso-lactide. [0090] 23. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 90% by weight D/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 95% D/Meso-lactide, preferably at least 97% D/Meso-lactide, preferably at least 98% D/Meso-lactide, preferably at least 99% D/Meso-lactide. [0091] 24. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second lactide feed comprises at least 90% by weight L/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 95% L/Meso-lactide, preferably at least 97% L/Meso-lactide, preferably at least 98% L/Meso-lactide, preferably at least 99% L/Meso-lactide. [0092] 25. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the polylactic acid has a weight average molecular weight (M.sub.w) of at least 50 kDa to at most 500 kDa, preferably at least 75 kDa to at most 400 kDa, for example at least 100 kDa to at most 300 kDa, for example about 200 kDa. [0093] 26. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the polylactic acid has a ratio of the weight average molecular weight (M.sub.w) to the number average molecular weight (M.sub.n) from 1.0 to 4.0, preferably from 1.2 to 3.6, preferably from 3.2 to 2.8, preferably from 1.6 to 2.4, preferably from 1.8 to 2.0. [0094] 27. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the polylactic acid has a density of at least 1.16 g/cm.sup.3 to at most 1.40 g/cm.sup.3, for example at least 1.18 g/cm.sup.3 to at most 1.35 g/cm.sup.3, preferably at least 1.20 g/cm.sup.3 to at most 1.30 g/cm.sup.3, preferably at least 1.22 g/cm.sup.3 to at most 1.28 g/cm.sup.3, preferably at least 1.23 g/cm.sup.3 to at most 1.26 g/cm.sup.3, for example about 1.24 g/cm.sup.3, as determined in accordance with ASTM D1505 at 23° C. [0095] 28. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first polymerisation reactor section comprises one or more CSTR type reactors. [0096] 29. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first polymerisation reactor section comprises only CSTR type reactors. [0097] 30. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second polymerisation reactor section comprises one or more PFR type reactors. [0098] 31. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the second polymerisation reactor section comprises only PFR type reactors. [0099] 32. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first polymerisation reactor section comprises one or more CSTR type reactors and one or more PFR type reactors. [0100] 33. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first polymerisation reactor section comprises one or more CSTR type reactors, and wherein the second polymerisation reactor section comprises one or more PFR type reactors. [0101] 34. The process or reactor configuration according to any of the above statements, or in some embodiments described herein, wherein the first polymerisation reactor section comprises one or more CSTR type reactors and one or more PFR type reactors, and wherein the second polymerisation reactor section comprises one or more PFR type reactors. [0102] 35. The process according to any of the above statements, or in some embodiments described herein, performed in a reactor configuration according to any of the above statements, or in some embodiments described herein. [0103] 36. Use of the reactor configuration according to any of the above statements, or in some embodiments described herein, in a process according to any of the above statements, or in some embodiments described herein. [0104] 37. Polylactic acid formed by the process according to any of the above statements, or in some embodiments described herein. [0105] 38. Polylactic acid formed in a reactor configuration according to any of the above statements, or in some embodiments described herein.
[0106] In an aspect, the present invention relates to a process for polymerising lactide into polylactic acid. The process preferably comprises the steps of: [0107] feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; [0108] feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, [0109] feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, preferably after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed.
[0110] Alternatively, the process preferably comprises the steps of: [0111] feeding a first lactide feed into a first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; [0112] feeding the output of the first polymerisation reactor section into a second polymerisation reactor section; and, [0113] feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, preferably after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed.
[0114] In an aspect, the present invention relates to a reactor configuration for polymerising lactide into polylactic acid. The reactor configuration preferably comprises: [0115] a first polymerisation reactor section; wherein the first lactide feed comprises L-lactide; [0116] a second polymerisation section; [0117] a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, [0118] a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines preferably configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises D and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed.
[0119] Alternatively, the reactor configuration preferably comprises: [0120] a first polymerisation reactor section; wherein the first lactide feed comprises D-lactide; [0121] a second polymerisation section; [0122] a feeding line for feeding the output of the first polymerisation reactor section into the second polymerisation reactor section; and, [0123] a second lactide feeding line for feeding a second lactide feed into the second polymerisation reaction section between the first polymerisation reactor section and the second polymerisation reactor section, the feeding lines preferably configured to feed the second lactide feed after at most 95% of the total residence time; wherein the second lactide feed comprises L and/or meso-lactide; preferably wherein the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed.
[0124] The present invention also relates to a process as described herein or embodiments thereof, performed in a reactor configuration as described herein or embodiments thereof.
[0125] The present invention also relates to the use of a reactor configuration as described herein or embodiments thereof, in a process as described herein or embodiments thereof.
[0126] The processes as described herein provide an improved lactide polymerization process by injection of D-lactide (or alternatively L-lactide) and/or purified meso-lactide in a relatively more downstream portion of the reaction section.
[0127] Lactic acid is chiral such that (R)-lactic acid (or D-lactic acid) and (S)-lactic acid (or L-lactic acid) exist. Furthermore, these enantiomers do not racemise readily. Thus, formation of lactide from two equivalents of lactic acid gives rise to three stereoisomers: (R,R)-lactide (or D-lactide), (S,S)-lactide (or L-lactide) and (R,S)-lactide (or Meso-lactide). As used herein, the terms D-lactide and Meso-lactide may be jointly referred to as “D/Meso-lactide”; and the terms L-lactide and Meso-lactide may be jointly referred to as “L/Meso-lactide”;
[0128] PLA as produced in the present invention can be prepared according to any method known in the state of the art. The PLA is preferably prepared by ring-opening polymerization of lactide, which is a cyclic dimer of lactic acid, and optionally glycolide, which is a cyclic dimer of glycolic acid, or caprolactone and the like.
[0129] The lactide used in the present invention includes L-lactide, which is a cyclic dimer of L-lactic acid, D-lactide, which is a cyclic dimer of D-lactic acid, Meso-lactide, which is a cyclic dimer of D-lactic acid and L-lactic acid. According to some embodiments of the present invention, when the first lactide feed comprises L-lactide, the second lactide feed comprises at least D and/or Meso-lactide. According to some alternative embodiments of the present invention, when the first lactide feed comprises D-lactide, the second lactide feed comprises at least L and/or Meso-lactide.
[0130] Co-polymeric components other than lactic acid may be used and include dicarboxylic acid, polyhydric alcohol, hydroxycarboxylic acid, lactone, or the like, which have two or more functional groups each capable of forming an ester bonding. These are, for example, polyester, polyether, polycarbonate, or the like which have the two or more unreacted functional groups in a molecule.
[0131] The hydroxycarboxylic acids may be selected from the list comprising glycolic acid, hydroxybutyric acid, hydroxyvaleric acid, hydroxypentanoic acid, hydroxycaproic acid, and hydroxyheptanoic acid.
[0132] As used herein, the term “residence time” refers to the mean residence time as calculated pro rata based on the volume. For example, the mean residence time RT.sub.1 of the first polymer reactor section is calculated as V.sub.1/Q.sub.1, whereby V.sub.1 is the volume of the first reactor section and Q.sub.1 is the output volumetric flow rate of the first reactor zone. The mean residence time RT.sub.2 of the second polymer reactor section is calculated as V.sub.2/Q.sub.2, whereby V.sub.2 is the volume of the second reactor section and Q.sub.2 is the output volumetric flow rate of the second reactor section. For example, in some embodiments, Q.sub.2 may be calculated as Q.sub.1+Q′, whereby Q′ is the input volumetric flow rate of the second lactide feed. The total mean residence time RT is calculated as RT.sub.1+RT.sub.2. Typically, the productivity will reduce along the process (due to less monomer), which means that the % residence time is not equivalent to % conversion ratio. For example, an 80% residence time allows to reach a conversion higher than 80% of the targeted 95% final conversion.
[0133] The second lactide feed is preferably injected as much downstream of the reaction section as possible, which will give the highest gain on grade change transition time and fine-tuning optimization. However, preferably the first lactide feed has not been completely converted into PLA to avoid formation of a stereo-block copolymer. A stereo-block copolymer is a completely different polymer in nature and has different mechanical properties. The present invention allows to produce standard copolymer PLA, which is a copolymer of L- and D-lactide, and not stereo-block copolymer, which is a copolymer of PLLA and PDLA. Standard copolymer PLA typically has a fusion temperature (or melting point) that is lower than PLA made from 100% L or D (pure PLLA or PDLA). The irregular chains do not crystallize well and have a reduced heat resistance, while homopolymer chains crystallize fast and provide good heat stability. Stereo-block PLA typically has a fusion temperature (or melting point) that is higher than PLA made from 100% L or D (pure PLLA or PDLA), since the stereo-complex may show interlocking structures. Preferably, the PLA formed in the present invention has a fusion temperature (or melting point) that is lower than homopolymer PLA made from 100% L or D (pure PLLA or PDLA).
[0134] In some preferred embodiments, the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at least 30% of the total residence time, preferably after at least 40%, preferably after at least 50%, preferably after at least 60%, preferably after at least 70%. In some preferred embodiments, the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at least 75% of the total residence time, preferably after at least 76%, preferably after at least 77%, preferably after at least 78%, preferably after at least 79%, preferably after at least 80%.
[0135] Preferably, there is still a minimum residence time in the reaction section downstream of the injection point so as to properly incorporate the second lactide feed (preferably D/meso lactide) into the PLA macromolecules. Therefore, in some preferred embodiments, the second lactide feed is fed between the first polymerisation reactor section and the second polymerisation reactor section after at most 95% of the total residence time, preferably after at most 90%, preferably after at most 85%, for example after at most 80%.
[0136] In some embodiments, the first lactide feed comprises little to no D-lactide and/or little to no Meso-lactide. In such embodiments, the second lactide feed comprises mainly D-lactide and/or Meso-lactide. Therefore, in some preferred embodiments, the first lactide feed comprises at most 5% by weight D-lactide, compared to the total weight of the lactide feed, preferably at most 4% D-lactide, preferably at most 3% D-lactide, preferably at most 2% D-lactide, preferably at most 1% D-lactide. In some preferred embodiments, the first lactide feed is essentially free of D-lactide.
[0137] In some embodiments, the first lactide feed comprises little to no L-lactide and/or little to no Meso-lactide. In such embodiments, the second lactide feed comprises mainly L-lactide and/or Meso-lactide. Therefore, in some embodiments, the first lactide feed comprises at most 5% by weight L-lactide, compared to the total weight of the lactide feed, preferably at most 4% L-lactide, preferably at most 3% L-lactide, preferably at most 2% L-lactide, preferably at most 1% L-lactide. In some embodiments, the first lactide feed is essentially free of L-lactide.
[0138] In some preferred embodiments, the first lactide feed comprises at most 5% by weight Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% Meso-lactide, preferably at most 3% Meso-lactide, preferably at most 2% Meso-lactide, preferably at most 1% Meso-lactide. In some preferred embodiments, the first lactide feed is essentially free of Meso-lactide.
[0139] In some preferred embodiments, the first lactide feed comprises at most 5% by weight D/Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% D/Meso-lactide, preferably at most 3% D/Meso-lactide, preferably at most 2% D/Meso-lactide, preferably at most 1% D/Meso-lactide. In some preferred embodiments, the first lactide feed is essentially free of D/Meso-lactide.
[0140] In some embodiments, the first lactide feed comprises at most 5% by weight L/Meso-lactide, compared to the total weight of the first lactide feed, preferably at most 4% L/Meso-lactide, preferably at most 3% L/Meso-lactide, preferably at most 2% L/Meso-lactide, preferably at most 1% L/Meso-lactide. In some embodiments, the first lactide feed is essentially free of L/Meso-lactide.
[0141] In some embodiments, the first lactide feed comprises little to no D-lactide and/or little to no Meso-lactide. In such embodiments, the second lactide feed comprises mainly D-lactide and/or Meso-lactide. In some embodiments, the first lactide feed comprises little to no L-lactide and/or little to no Meso-lactide. In such embodiments, the second lactide feed comprises mainly L-lactide and/or Meso-lactide.
[0142] When the second lactide feed comprises mainly D-lactide, the second lactide feed preferably comprises almost exclusively of D-lactide. In some preferred embodiments, the second lactide feed comprises at least 90% by weight D-lactide, compared to the total weight of the second lactide feed, preferably at least 95% D-lactide, preferably at least 97% D-lactide, preferably at least 98% D-lactide, preferably at least 99% D-lactide.
[0143] When the second lactide feed comprises mainly L-lactide, the second lactide feed preferably comprises almost exclusively of L-lactide. In some embodiments, the second lactide feed comprises at least 90% by weight L-lactide, compared to the total weight of the second lactide feed, preferably at least 95% L-lactide, preferably at least 97% L-lactide, preferably at least 98% L-lactide, preferably at least 99% L-lactide.
[0144] When the second lactide feed comprises mainly Meso-lactide, the second lactide feed preferably comprises up to about 50% Meso-lactide In some preferred embodiments, the second lactide feed comprises at least 30% by weight Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 35% Meso-lactide, preferably at least 40% Meso-lactide, preferably at least 45% Meso-lactide, preferably at least 50% Meso-lactide. The more concentrated the second lactide feed, the smaller the flow rate needs to be. This means that the pump, injection pipe, and nozzle will be smaller. In addition, the lactide injected at the second injection point still requires sufficient residence time in the second part of the reaction section to polymerise. If the flow of second lactide feed is important, the second part of the reaction section will be to be big enough to allow for sufficient residence time for polymerization. By keeping the second lactide feed flow small, this ensures that the second part of the reaction section does not need to be enlarged.
[0145] In some preferred embodiments, the second lactide feed comprises at least 40% by weight D/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 50% D/Meso-lactide, preferably at least 60% D/Meso-lactide, preferably at least 70% D/Meso-lactide, preferably at least 80% D/Meso-lactide. In some preferred embodiments, the second lactide feed comprises at least 90% by weight D/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 95% D/Meso-lactide, preferably at least 97% D/Meso-lactide, preferably at least 98% D/Meso-lactide, preferably at least 99% D/Meso-lactide.
[0146] In some embodiments, the second lactide feed comprises at least 40% by weight L/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 50% L/Meso-lactide, preferably at least 60% L/Meso-lactide, preferably at least 70% L/Meso-lactide, preferably at least 80% L/Meso-lactide. In some embodiments, the second lactide feed comprises at least 90% by weight L/Meso-lactide, compared to the total weight of the second lactide feed, preferably at least 95% L/Meso-lactide, preferably at least 97% L/Meso-lactide, preferably at least 98% L/Meso-lactide, preferably at least 99% L/Meso-lactide.
[0147] In some embodiments, the second lactide feed comprises at least 0.5% D-lactide and at most 99.5% Meso-lactide, based on the total weight of D/Meso-lactide; preferably at least 1.0% D-lactide and at most 99.0% Meso-lactide; for example at least 1.5% D-lactide and at most 98.5% Meso-lactide; for example at least 2.0% D-lactide and at most 98.0% Meso-lactide. In some embodiments, the second lactide feed comprises at most 5.0% D-lactide and at least 95.0% Meso-lactide, based on the total weight of D/Meso-lactide; preferably at most 4.0% D-lactide and at least 96.0% Meso-lactide; for example at most 3.0% D-lactide and at least 97.0% Meso-lactide; for example at most 2.0% D-lactide and at least 98.0% Meso-lactide.
[0148] In some embodiments, the second lactide feed comprises at least 0.5% L-lactide and at most 99.5% Meso-lactide, based on the total weight of L/Meso-lactide; preferably at least 1.0% L-lactide and at most 99.0% Meso-lactide; for example at least 1.5% L-lactide and at most 98.5% Meso-lactide; for example at least 2.0% L-lactide and at most 98.0% Meso-lactide. In some embodiments, the second lactide feed comprises at most 5.0% L-lactide and at least 95.0% Meso-lactide, based on the total weight of L/Meso-lactide; preferably at most 4.0% L-lactide and at least 96.0% Meso-lactide; for example at most 3.0% L-lactide and at least 97.0% Meso-lactide; for example at most 2.0% L-lactide and at least 98.0% Meso-lactide.
[0149] As used herein, the terms “polylactic acid” or “poly-lactide” or “PLA” are used interchangeably and refer to poly(lactic acid) polymers comprising repeat units derived from lactic acid.
[0150] Preferably, the polylactic acid has a number average molecular weight (M.sub.n) ranging between 30 kDa and 350 kDa, more preferably between 50 kDa and 175 kDa, even more preferably between 70 kDa and 150 kDa. The number average molecular weight is measured by chromatography by gel permeation compared to a standard polystyrene in chloroform at 25° C.
[0151] In some embodiments, the polylactic acid has a weight average molecular weight (M.sub.w) of at least 50 kDa to at most 500 kDa, preferably at least 75 kDa to at most 400 kDa, for example at least 100 kDa to at most 300 kDa, for example about 200 kDa. Measurement of the molecular masses may be performed at 25° C. using a liquid chromatograph PolymerChar system.
[0152] In some embodiments, the ratio of the weight average molecular weight (M.sub.w) to the number average molecular weight (M.sub.n) is generally from 1.0 to 4.0, preferably from 1.2 to 3.6, preferably from 3.2 to 2.8, preferably from 1.6 to 2.4, preferably from 1.8 to 2.0.
[0153] In some embodiments, the polylactic acid has a density of at least 1.16 g/cm.sup.3 to at most 1.40 g/cm.sup.3, for example at least 1.18 g/cm.sup.3 to at most 1.35 g/cm.sup.3, preferably at least 1.20 g/cm.sup.3 to at most 1.30 g/cm.sup.3, preferably at least 1.22 g/cm.sup.3 to at most 1.28 g/cm.sup.3, preferably at least 1.23 g/cm.sup.3 to at most 1.26 g/cm.sup.3, for example about 1.24 g/cm.sup.3, as determined in accordance with ASTM D1505 at 23° C.
[0154] In some embodiments, the polylactic acid is not a stereo-block polymer.
[0155] The polylactic acid may optionally include additives known in the art to improve processing and application of polymer films, e.g., anti-block additives, slip additives and viscosity enhancers.
[0156] When used to enhance the production of polymer films, it should be noted that these additives are not essential for blowing the PLA films per se, but may be preferentially employed to enhance the processing, performance and look of the final product. In an embodiment, the polylactic acid comprises a slip agent, preferably erucamide. In an embodiment, the polylactic acid comprises an anti-block additive, preferably talc or other silica-based products.
[0157] In some embodiments, the polylactic acid is obtained by polymerizing lactide, in the presence of a suitable catalyst and preferably in the presence of a compound of formula (VI), acting as a co-initiator and transfer agent of the polymerization,
R.sup.3—OH (VI)
[0158] wherein R.sup.3 is selected from the group consisting of C.sub.1-20alkyl, C.sub.6-30aryl, and C.sub.6-30arylC.sub.1-20alkyl, each group being optionally substituted by one or more substituents selected from the group consisting of halogen, hydroxyl, and C.sub.1-6alkyl. Preferably, R.sup.3 is a group selected from C.sub.3-12alkyl, C.sub.6-10aryl, and C.sub.6-10arylC.sub.3-12alkyl, each group being optionally substituted by one or more substituents each independently selected from the group consisting of halogen, hydroxyl, and C.sub.1-6 alkyl; preferably, R.sup.3 is a group selected from C.sub.3-12alkyl, C.sub.6-10aryl, and C.sub.6-10arylC.sub.3-12alkyl, each group being optionally substituted by one or more substituents each independently selected from the group consisting of halogen, hydroxyl and C.sub.1-4alkyl. The alcohol can be a polyol such as diol, triol or higher functionality polyhydric alcohol. The alcohol may be derived from biomass such as for instance glycerol or propanediol or any other sugar-based alcohol such as for example erythritol. The alcohol can be used alone or in combination with another alcohol.
[0159] In some embodiments, non-limiting examples of initiators include 1-octanol, isopropanol, propanediol, trimethylolpropane, 2-butanol, 3-buten-2-ol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol, 1,7-heptanediol, benzyl alcohol, 4-bromophenol,1,4-benzenedimethanol, and (4-trifluoromethyl)benzyl alcohol; preferably, the compound of formula (VI) is selected from 1-octanol, isopropanol, and 1,4-butanediol.
[0160] The catalyst employed for this process may have general formula M(Y.sup.1, Y.sup.2, . . . Y.sup.p).sub.q, in which M is a metal selected from the group comprising the elements of columns 3 to 12 of the periodic table of the elements, as well as the elements Al, Ga, In, TI, Ge, Sn, Pb, Sb, Ca, Mg and Bi; whereas Y.sup.1, Y.sup.2, . . . Y.sup.p are each substituents selected from the group comprising alkyl with 1 to 20 carbon atoms, aryl having from 6 to 30 carbon atoms, alkoxy having from 1 to 20 carbon atoms, aryloxy having from 6 to 30 carbon atoms, and other oxide, carboxylate, and halide groups as well as elements of group 15 and/or 16 of the periodic table; p and q are integers of from 1 to 6. As examples of suitable catalysts, we may notably mention the catalysts of Sn, Ti, Zr, Zn, and Bi; preferably an alkoxide or a carboxylate and more preferably Sn(Oct).sub.2, Ti(OiPr).sub.4, Ti(2-ethylhexanoate).sub.4, Ti(2-ethylhexyloxide).sub.4, Zr(OiPr).sub.4, Bi(neodecanoate).sub.3, (2,4-di-tert-butyl-6-(((2-(dimethylamino)ethyl)(methyl)amino)methyl)phenoxy)(ethoxy)zinc, or Zn(lactate).sub.2. Preferably, the catalyst comprises Sn(Oct).sub.2.
[0161] The current processes to obtain polylactic acid consist basically in preparing first a mix of different lactides, to which is incorporated an initiator and a catalyst, before being fed to a polymerization section. Reaction usually takes place with a bulk solution where polylactic acid is dissolved in liquid lactide.
[0162] The reaction (polymerization) section is typically composed of a mix of CSTRs (Continuously Stirred Tank Reactor), PFRs (Plug Flow Reactor), or loop reactors which may be considered equivalent to a CSTR (for example a loop reactor using Static Mixer Reactors).
[0163] CSTRs and PFRs are differentiated by the amount of required liquid renewal before a composition can be changed and are often expressed in number of average residence time. A reactor or reactor system is usually considered a CSTR when one needs to wait 3 residence time and it is considered to be a PFR when one has only to wait for less than 1.5 residence time (see literature). From an engineering point of view, CSTRs are the cheapest type of reactor and allow significant CAPEX reduction.
[0164] The behaviour of a CSTR is often approximated or modelled by that of a Continuous Ideally Stirred-Tank Reactor (CISTR). All calculations performed with CISTRs assume perfect mixing. In a perfectly mixed reactor, the output composition is identical to composition of the material inside the reactor, which is a function of residence time and rate of reaction. If the residence time is 5-10 times the mixing time, this approximation is valid for engineering purposes
[0165] As used herein, the term “CSTR type reactor” refers to CSTR reactors as well as to CSTR equivalents in the case of a loop reactor made of tubular reactors.
[0166] An ideal plug flow reactor has a fixed residence time which is the flowrate divided by the useful volume of the reactor. A real plug flow reactor has a narrow residence time distribution that is centred around the mean residence time also called the average residence time. Usually the behaviour is considered to be a good PFR when 2 sigma of the residence times are covered within +/−0.25 average residence time
[0167] As used herein, the term “PFR type reactor” refers to PFR reactors as well as to PFR equivalents in the case of tubular reactors.
[0168] As illustrated herein, the PFR type reactors are represented vertically. However, the present invention equally comprises the use of horizontal PFR type reactors.
[0169] CSTR type reactors are typically cheaper than other types of reactors. However, the transition time is longer. Therefore, the benefits of the present application are more outspoken when CSTR type reactors are used, particularly in the first section. This combines a reduction in cost while still keeping the transition time short.
[0170] In some preferred embodiments, the first polymerisation reactor section comprises one or more CSTR type reactors. In some preferred embodiments, the first polymerisation reactor section comprises only CSTR type reactors. In some preferred embodiments, the first polymerisation reactor section comprises one or more CSTR type reactors and one or more PFR type reactors.
[0171] PFR type reactors are typically better for PLA in terms of precision of temperature adjustment. PFR type reactors also have the advantage of being able to handle higher viscosities. In some preferred embodiments, the second polymerisation reactor section comprises one or more PFR type reactors. In some preferred embodiments, the second polymerisation reactor section comprises only PFR type reactors.
[0172] In some embodiments, the PLA reaction section is composed of two parts, a first part which handles relatively low viscosity solutions allowing to get a conversion rate of 50-70% and which is composed of one or two Continuously Stirred Tank Reactors (CSTRs) or a loop reactor which is also assimilated to CSTRs, and a second part which is able to handle higher viscosities solution (usually at least 90% conversion and preferable 95% of conversion) which is composed of one or more PFRs.
[0173] More generally, a typical PLA unit reaction section comprises a series of multiple reactors which may be different types. As there is reaction equilibrium around 95-96% conversion, the end part of the reaction section is typically always viscous. As CSTRs are usually not suitable therefor, the reaction section end part preferably comprises a PFR portion. However, since CSTRs are cheaper, an optimized configuration in terms of CAPEX could then be one or two CSTR type reactors to handle the first part (which is of relatively low viscosity) and one or two PFR type reactors to handle the relatively high viscosity of the second part.
[0174] In some preferred embodiments, the first polymerisation reactor section comprises one or more CSTR type reactors, and the second polymerisation reactor section comprises one or more PFR type reactors. In some preferred embodiments, the first polymerisation reactor section comprises one or more CSTR type reactors and one or more PFR type reactors, and the second polymerisation reactor section comprises one or more PFR type reactors.
EXAMPLES
Example 1: Exemplary Reaction Sections
[0175]
[0176]
[0177]
Example 2: Reduction of Transition Material (Losses) Thanks to Shorter Grade Change
[0178] When there are grade changes with modification of D content in the final product, some transition products are usually generated. However, since such product is typically out of commercial specifications (off-spec), it has to be recycled or sold at a reduced price compared to prime quality material.
[0179] In this example, a 100 kty plant comprises 1 CSTR and 2 PFR in series. On average, there is one grade change with D content adjustment every week. The yearly operating hours are 8400. The conversion rate is 95%, and the feed rate is 12.5 T/H. With an average specific gravity of 1.1 kg/I, the volumetric rate would be 11.2 m.sup.3/h.
[0180] The reaction section configuration is illustrated in
[0181] Table 1 illustrates a reference case, whereby the D/Meso-lactide is fed in the first feeding line.
[0182] Table 2 illustrates an example according to the invention, whereby the D/Meso-lactide is fed in the second feeding line, between the 2 PFR type reactors.
TABLE-US-00001 TABLE 1 D/Meso incorporation from beginning 1 CSTR minutes 30 useful volume m.sup.3 5.6 2 PFRs minutes 90 useful volume m.sup.3 16.8 Transition time CSTR number of renewals 3 transition time minutes 90 Transition time PFR number of renewals 1.5 transition time minutes 135 TOTAL transition time minutes 225
TABLE-US-00002 TABLE 2 D/Meso incorporation between the 2 PFR type reactors 1 CSTR minutes 30 useful volume m3 5.6 2 PFRs minutes 90 useful volume m3 16.8 Transition time CSTR number of renewals 0 transition time minutes 0 Transition time PFR number of renewals 1.5 transition time minutes 67.5 TOTAL transition time minutes 67.5 GAIN PER GRADE CHANGE minutes 158 TONS 32.89 Number of grade changes/year 50 TOTAL LOSS REDUCTION TONS 1645
[0183] If, for example, a 100 to 200 $/T discount is given for transition material sale, this would represent a loss reduction of about 150 to 300 k$ per year.
Example 3: Increase in PLA Production Capacity
[0184] As can be seen in example 2, up to 1645 tons loss can be ‘gained’ if the line is saturated. This translates into an increase of capacity, which represents 1.6% of line capacity without any additional CAPEX or OPEX. If, for example, a 200 to 400 $/T margin is given for additional PLA sale, this would represent a loss reduction of about 300 to 600 k$ per year.
Example 4: Reduction of Lactide Loss
[0185] Taking the same reaction configuration as in example 2, this PLA unit capacity is 100 kty, with PLLA grade (0% D) requirements of 10 kty, and PLA requirements for Max D % crystallised grades of 90 kty. The PLA unit conversion rate is 95% and the Meso-lactide generation in the lactide production unit is 7%.
[0186] Table 3 illustrates a reference case, whereby the D/Meso-lactide is fed in the first feeding line.
[0187] Table 4 illustrates an example according to the invention, whereby the D/Meso-lactide is fed in the second feeding line, between the 2 PFR type reactors.
TABLE-US-00003 TABLE 3 D/Meso incorporation from beginning 1 CSTR minutes 30 2 PFRs minutes 90 Time before D adjustment minutes 120 is coming out from pelletizer Max D content % 3.5 Required Meso-lactide tons 6632 Required L-lactide tons 98632 TOTAL lactide required to meet PLA mix tons 105263 Required Lactide tons 106055 production for L lactide PLA needs Corresponding generation of meso lactide tons 7424 Excess meso lactide tons 792
TABLE-US-00004 TABLE 4 D/Meso incorporation in the middle of last PFR 1 CSTR Minutes 30 2 PFRs Minutes 90 Time before D adjustment Minutes 22.5 is coming out from pelletizer Max D content % 3.75 Required Meso-lactide Tons 7105 Required L-lactide Tons 98158 TOTAL lactide required to meet PLA mix Tons 105263 Required Lactide Tons 105546 production for L-lactide PLA needs Corresponding generation of meso lactide Tons 7388 Excess meso lactide Tons 283 Reduction 509
[0188] In this example shown in above table, one can avoid recycling about 500 tons every year. Taking a cost of recycling Lactide of 200 $/T, that represents about 100 k$ per year.
Example 5: Lower Temperature Melting Point PLA
[0189] As shown in Example 5, going from 3.5% to 3.75% D content would reduce the melting point of PLA product by about 1.5° C. Although it is a small gain, it is still a significant advantage for the manufacturers of goods made of PLA, as this leads to a higher production rate and lower energy requirement for manufacturers of PLA goods. Such a change in melting point could represent an energy reduction of about 1% and a production rate increase by about the same amount.