Method for manufacturing press formed product

Abstract

A method for manufacturing a press formed product is disclosed. The manufacturing method includes a first step of manufacturing an intermediate component by forming the curved part such that a line length along the longitudinal direction of a curved convex side WA is shorter than a line length in the product shape and a line length along the longitudinal direction of a curved concave side WB is longer than a line length in the product shape; and a second step of forming the intermediate component such that a line length of the curved convex side WA is longer than the line length in the first step and a line length of the curved concave side WB is shorter than the line length in the first step.

Claims

1. A method for manufacturing a press formed product comprising: when a metal sheet is press formed to manufacture a product having a product shape of a cross-sectional shape in which both sides of a top plate part in a width direction are continuous with side wall parts and having a curved part curved in the width direction along a longitudinal direction, a first step of manufacturing an intermediate component by forming the curved part such that a line length along the longitudinal direction of a curved convex side that is a convex side of a curve is shorter than a line length in the product shape and a line length along the longitudinal direction of a curved concave side that is a concave side of the curve is longer than a line length in the product shape; and a second step of forming the intermediate component such that a line length of the curved convex side at the bent line position between the top plate part and the side wall part or at the end position in the width direction of the side wall part is longer than the line length in the first step and a line length of the curved concave side at the bent line position between the top plate part and the side wall part or at the end position in the width direction of the side wall part is shorter than the line length in the first step, wherein a line length L1 of the longitudinal direction and the average amount of strain ε1 of the longitudinal direction in a compressive stress region of the longitudinal direction generated on the curved convex side are determined by performing, with a computer, simulation analysis in which the metal sheet is formed into the product shape by one press forming, and, when a line length of the curved convex side after the first step is defined as L2, a line length of the curved convex side in the first step is set such that the following equation (1) is satisfied:
0<L1−L2≤2×|L1×ε1|  (1).

2. A method for manufacturing a press formed product comprising: when a metal sheet is press formed to manufacture a product having a product shape of a cross-sectional shape in which both sides of a top plate part in a width direction are continuous with side wall parts and having a curved part curved in the width direction along a longitudinal direction, a first step of manufacturing an intermediate component by forming the curved part such that a line length along the longitudinal direction of a curved convex side that is a convex side of a curve is shorter than a line length in the product shape and a line length along the longitudinal direction of a curved concave side that is a concave side of the curve is longer than a line length in the product shape; and a second step of forming the intermediate component such that a line length of the curved convex side at the bent line position between the top plate part and the side wall part or at the end position in the width direction of the side wall part is longer than the line length in the first step and a line length of the curved concave side at the bent line position between the top plate part and the side wall part or at the end position in the width direction of the side wall part is shorter than the line length in the first step, wherein a line length L1′ of the longitudinal direction and the average amount of strain ε1′ of the longitudinal direction in a tensile stress region of the longitudinal direction generated on the curved concave side are determined by performing, with a computer, simulation analysis in which the metal sheet is formed into the product shape by one press forming, and, when a line length of the curved concave side after the first step is defined as L2′, a line length of the curved concave side in the first step is set such that the following equation (2) is satisfied:
0<L2′−L1′≤2×|L1′×ε1′|  (2).

3. The method for manufacturing a press formed product according to 1, wherein drawing or stamping is applied to the forming in the first step, and restrike processing is applied to the forming in the second step.

4. The method for manufacturing a press formed product according to 1, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

5. The method for manufacturing a press formed product according to claim 1, wherein a line length L1′ of the longitudinal direction and the average amount of strain ε1′ of the longitudinal direction in a tensile stress region of the longitudinal direction generated on the curved concave side are determined by performing, with a computer, simulation analysis in which the metal sheet is formed into the product shape by one press forming, and, when a line length of the curved concave side after the first step is defined as L2′, a line length of the curved concave side in the first step is set such that the following equation (2) is satisfied:
0<L2′−L1′≤2×|L1′×ε1′|  (2).

6. The method for manufacturing a press formed product according to claim 5, wherein drawing or stamping is applied to the forming in the first step, and restrike processing is applied to the forming in the second step.

7. The method for manufacturing a press formed product according to claim 3, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

8. The method for manufacturing a press formed product according to claim 5, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

9. The method for manufacturing a press formed product according to claim 6, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

10. The method for manufacturing a press formed product according to claim 2, wherein drawing or stamping is applied to the forming in the first step, and restrike processing is applied to the forming in the second step.

11. The method for manufacturing a press formed product according to claim 2, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

12. The method for manufacturing a press formed product according to claim 10, wherein the metal sheet is a steel sheet having a material strength of 590 MPa or more.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is an oblique view illustrating an example of a product shape;

(2) FIG. 2 is a schematic view viewed from above, which illustrates an example of a component having a hat-shaped cross-section and curved in a width direction along a longitudinal direction, and spring-back in this case;

(3) FIG. 3 is a schematic view of a top plate part viewed from above, which illustrates a state of the spring-back;

(4) FIG. 4A is an oblique view and FIG. 4B is a cross-sectional view illustrating the product shape according to embodiments based on the present invention;

(5) FIG. 5 is a view explaining steps of press forming according to the embodiments based on the present invention;

(6) FIG. 6A is a top view and FIG. 6B is a cross-sectional view of A-A in FIG. 6A, which illustrate another example of the product shape; and

(7) FIG. 7A is a top view and FIG. 7B is a cross-sectional view of A-A in FIG. 7A, which illustrate another example of the product shape.

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

(8) Embodiments according to the present invention will be described below with reference to the drawings.

(9) The embodiments described below illustrate configurations to embody the technical idea according to aspects of the present invention, and the technical idea according to aspects of the present invention does not limit the material, shape, structure, and the like of a component to those described below. Various changes can be added to the technical idea according to aspects of the present invention within the technical scope defined by claims.

(10) An intended product shape 1 of the present embodiment formed by press forming is, for example, as illustrated in FIG. 1, the product shape 1 having a cross-sectional shape in which both sides of a top plate part 1A in a width direction are continuous with side wall parts 1B and having a curved part curved in the width direction along a longitudinal direction. Representative examples of the cross-sectional shape in which the both sides of the top plate part 1A in the width direction are continuous with the side wall parts 1B include a hat-shaped cross-section and a U-shaped cross-section. In the case of the U-shaped cross-section, the side wall parts 1B are flanges.

(11) In the case of the product shape 1 which has a hat-shaped cross-sectional shape, in which the top plate part 1A and flange parts 1C are continuous in the width direction through the side wall parts 1B, and curves in the width direction along the longitudinal direction (refer to FIG. 1), the top plate part 1A and the flange parts 1C curve along the longitudinal direction in a top view.

(12) When a metal sheet made of a tabular blank material is press formed into the product shape 1, as illustrated in FIG. 2, a compressive stress is generated on a curved convex side WA and a tensile stress is generated on a curved concave side WB, and spring-back in the product width direction is generated due to a stress difference thereof.

(13) Then, when the stresses are released by removing the component from a pressing die, spring-back in the product width direction as indicated by the arrow S in FIG. 2 is generated, and both end sides in the longitudinal direction are displaced in the product width direction as illustrated in FIG. 3. For the sake of clarity, only the top plate part 1A is illustrated in FIG. 3, and the solid line indicates an example before the spring-back and the dashed-dotted line indicates an example after the spring-back.

(14) In this case, when the residual stress increases with increasing the material strength of the metal sheet, the amount of spring-back in the width direction tends to increase. More specifically, the adoption of a high tensile strength steel sheet of 590 MPa or more causes large spring-back.

(15) As the product shape 1 of the present embodiment manufactured by press forming, the shape illustrated in FIG. 4 is assumed. The product shape 1 is an example of the case of a hat-shaped cross-section component. In this example, the top plate part 1A and the flange part 1C are continuous in the width direction through the side wall part 1B, and the top plate part 1A and the flange part 1C curve in the width direction along the longitudinal direction in a top view. The curvatures of curves along the longitudinal direction may be the same but are different in the present embodiment.

(16) In the example of the product shape illustrated in FIG. 4, a flange part continuous with the side wall part 1B is not provided on the curved convex side WA, and a stepped part extending in the longitudinal direction is provided on the side wall part 1B on the curved concave side WB, and the rigidity of the curved concave side WB becomes high.

(17) A method for manufacturing a press formed product of the present embodiment includes a first step of manufacturing an intermediate component by press forming and a second step of forming the intermediate component into the product shape 1 by press forming.

(18) The method for manufacturing a press formed product includes trim processing (not illustrated) for trimming the outer periphery of the flange. The trim processing may be performed before the first step, may be performed between the first step and the second step, or may be performed after the second step. In the present embodiment, the case where the trim processing is performed before press processing in the first step will be described. In this case, the intermediate component is a component in a state where the trim processing of the outer periphery of the flange has been performed.

(19) The first step is a step of manufacturing the intermediate component by forming the curved part curved in the width direction along the longitudinal direction such that a line length along the longitudinal direction of the curved convex side WA that is a convex side of the curve is shorter than a line length in the product shape 1 and a line length along the longitudinal direction of the curved concave side WB that is a concave side of the curve is longer than a line length in the product shape 1. The intermediate component to be formed in the first step is formed into a shape according to the product shape 1 except for the above line lengths. As the metal sheet to be processed in the first step, even a steel sheet having a material strength of 590 MPa or more can be applied.

(20) The second step is a step of forming the intermediate component such that a line length of the curved convex side WA is longer than the line length in the first step and a line length of the curved concave side WB is shorter than the line length in the first step.

(21) As a representative of the above line lengths, the adjustment may be performed by, for example, line lengths at bent line positions 1a between the top plate part 1A and the side wall parts 1B and bent line positions 1b between the side wall parts 1B and the flange parts 1C (refer to FIG. 1).

(22) As illustrated in FIG. 5, the manufacturing method of the present embodiment includes a designing step 10A of designing a press shape after a first step 10B by performing, with a computer, simulation analysis of forming into the product shape 1, the first step 10B of forming a metal sheet with a die corresponding to the designed press shape, and a second step 10C performed after the first step 10B, as processing for forming a tabular metal sheet into the above product shape 1.

(23) The designing step 10A is a designing step of calculating a shape, for the curved part curved in the width direction along the longitudinal direction, in which the line length along the longitudinal direction of the curved convex side WA that is a convex side of the curve is shorter than the line length in the product shape 1 and the line length along the longitudinal direction of the curved concave side WB that is a concave side of the curve is longer than the line length in the product shape 1, by simulation analysis with a computer, as described above. A die shape for the first step 10B for press forming into the designed shape is determined.

(24) In the designing step 10A, as described below, the press shape is preferably designed on the basis of a line length of the longitudinal direction and the average amount of strain of the longitudinal direction in a stress region generated in the curved part.

(25) For example, in the designing step 10A, a line length L1of the longitudinal direction and the average amount of strain ε1 of the longitudinal direction in a compressive stress region of the longitudinal direction generated on the curved convex side WA in the curved part are determined by performing, with a computer, simulation analysis in which the metal sheet is formed into the product shape 1 by one press forming. In the designing step 10A, when a line length of the curved convex side WA after the first step 10B is defined as L2, a line length of the first step 10B is set such that the following equation (1) is satisfied:
0<L1−L2≤2×|L1×ε1|  (1).

(26) Furthermore, for example, in the designing step 10A, a line length L1′ of the longitudinal direction and the average amount of strain ε1′ of the longitudinal direction in a tensile stress region of the longitudinal direction generated on the curved concave side WB in the curved part are determined by performing, with a computer, simulation analysis in which the metal sheet is formed into the product shape 1 by one press forming. In the designing step 10A, when a line length of the curved concave side after the first step 10B is defined as L2′, a line length of the first step 10B is set such that the following equation (2) is satisfied:
0<L2′−L1′≤2×|L1′×ε1′|  (2).

(27) When (L1−L2) becomes larger than 2×|L1×ε1|, an excessive tensile stress is generated on the curved convex side at a forming bottom dead center in the second forming step, and spring-back in the opposite direction might be generated. Furthermore, when (L2′−L1′) becomes larger than 2×|L1′×ε1′|, an excessive compressive stress is generated on the curved concave side at the forming bottom dead center in the second forming step, and spring-back in the opposite direction might be generated.

(28) In the first step 10B, the metal sheet is press formed to manufacture the intermediate component using the die shape determined in the designing step 10A.

(29) Drawing or stamping may be applied to the forming in the first step 10B.

(30) As described above, the second step 10C is a step of forming the intermediate component such that, in the curved part, the line length of the curved convex side WA is longer than the line length in the first step 10B and the line length of the curved concave side WB is shorter than the line length in the first step 10B.

(31) When the line length of the curved convex side in the first step 10B is defined as L2, a line length of the curved convex side WA in the second step 10C is preferably set such that a line length L3 of the curved convex side WA of a die in the second step 10C becomes a value that satisfies the following equation (3):
L2<L3≤1.01×L2   (3).

(32) Furthermore, when the line length of the curved concave side WB in the first step 10B is defined as L2′, a line length of the curved concave side WB in the second step 10C is preferably set such that a line length L3′ of the curved concave side WB of the die in the second step 10C becomes a value that satisfies the following equation (4):
L2′>L3′≥0.99×L2′  (4).

(33) When L3 is L2 or less, the stress is not reversed on the curved convex side WA at the forming bottom dead center in the second forming step, and the spring-back is not sufficiently suppressed. Furthermore, when L3 is more than 1.01×L2, an excessive tensile stress is generated on the curved convex side WA at the forming bottom dead center in the second forming step, and spring-back in the opposite direction might be generated.

(34) Furthermore, when L3′ is L2′ or more, the stress is not reversed on the curved concave side WB at the forming bottom dead center in the second forming step, and the spring-back is not sufficiently suppressed. Furthermore, when L3′ is less than 0.99×L2′, an excessive tensile stress is generated on the curved concave side WB at the forming bottom dead center in the second forming step, and spring-back in the opposite direction might be generated.

(35) The shape of the die used in the second step 10C may also be designed in the designing step 10A by performing, with a computer, simulation analysis in which the metal sheet is press formed into the product shape 1.

Operations and Others

(36) In the method for manufacturing a press formed product of the present embodiment, in order to reduce spring-back, the intermediate component is manufactured by forming the curved part such that, in the first step 10B, the line length of the curved part along the longitudinal direction is shorter than the line length in the product shape 1 on the curved convex side WA and the line length of the curved part along the longitudinal direction is longer than the line length in the product shape 1 on the curved concave side WB, and, in the second step 10C, the curved part of the intermediate component is formed such that the line length of the curved convex side WA is longer than the line length in the first step 10B and the line length of the curved concave side WB is shorter than the line length in the first step 10B, so that an intended manufacturing component is obtained.

(37) A high tensile strength steel sheet is targeted as the metal sheet to be press processed, but a steel sheet or an aluminum sheet may be used.

(38) In the present embodiment, in the forming in the first step 10B, the curved part is formed such that the line length of the curved part along the longitudinal direction is shorter than the line length in the product shape 1 on the curved convex side WA and the line length of the curved part along the longitudinal direction is longer than the line length in the product shape 1 on the curved concave side WB. Furthermore, in the forming in the second step 10C, the manufactured intermediate component is formed such that the line length of the curved convex side WA is longer than the line length in the first step 10B and the line length of the curved concave side WB is shorter than the line length in the first step 10B, so that a small tensile stress is generated on the curved convex side and a small compressive stress is generated on the curved concave side at the press forming bottom dead center in the second step 10C.

(39) Accordingly, the stress difference is reduced, thereby resulting in reduction in the amount of spring-back in the product width direction, and the material strength sensitivity can be reduced even when the material strength varies.

(40) As described above, according to the method for manufacturing a press formed product of the present embodiment, even when a high tensile strength steel sheet is used, spring-back in the product width direction can be greatly reduced without complicating a die. Accordingly, a component having a high-accuracy hat-shaped cross-section curved shape close to the intended product shape 1 can be obtained. As just described, the method for manufacturing a press formed product of the present embodiment has excellent shape fixability and material strength sensitivity.

(41) As a result, according to the present embodiment, even when the material strength varies, a component having high dimensional accuracy can be obtained, thereby leading to improvement in yield. Furthermore, when a vehicle structural component is made using a component having a hat-shaped cross-sectional shape, assembly of the component can be easily performed.

(42) Although the product shape 1 wholly curved in the width direction along the longitudinal direction has been illustrated, the manufacturing method of the present embodiment can be applied to a product shape having one or two or more curved parts curved in the width direction along a part of the longitudinal direction. Furthermore, the cross-sectional shape of the product shape 1 is not limited to the hat-shaped cross-section, and the present embodiment can be applied to a cross-sectional shape such as a U-shaped cross-section.

(43) FIG. 6 illustrates a case where the product shape 1 is composed of one straight part K and one curved part Q along the longitudinal direction.

(44) FIG. 7 illustrates a case where the product shape 1 is composed of two curved parts Q1, Q2 along the longitudinal direction. In this case, for each of the curved parts Q1, Q2, the above line lengths may be separately determined.

EXAMPLES

(45) In order to confirm a spring-back reduction effect by the method for manufacturing a press formed product according to aspects of the present invention, press forming analysis and spring-back analysis by a finite element method (FEM) were performed. The results are described below.

(46) In the present example, the case where the substantially hat-shaped cross-section component curved in the width direction along the longitudinal direction in a top view illustrated in FIG. 4 is press formed was targeted. The dimensions of the press formed product (unit: mm) are as illustrated in FIG. 4.

(47) Forming conditions and the amounts of generated spring-back in Comparative Examples (No. 1 to No. 3) and Invention Examples (No. 4 to No. 6) are shown in Table 1.

(48) TABLE-US-00001 TABLE 1 Line Length Line Length Difference of Difference of Line Length of Line Length of Curved Curved Curved Curved Convex Side Concave Side Convex Side Concave Side Material Amount of in First Step in First Step in Second Step in Second Step Strength Spring-back No. (L1-L2) (L2′-L1′) L3 L3′ [MPa] [mm] 1 — — — —  590  −9.2 2  980 −12.7 3 1180 −16.1 4 0.7 × |L1 × ε1| 0.3 × |L1′ × ε1′| 1.004 × L2 0.998 × L2′  590  −3.1 5  980  −4.8 6 1180  −6.5

Comparative Examples

(49) In Comparative Examples (No. 1 to No. 3) , as conditions of forming into the product shape 1 by one press forming, press forming analysis and spring-back analysis in a die of the product shape 1 were performed, and the amount of spring-back in the width direction in a top view (displacement in Y direction) was determined.

(50) A metal sheet used in press forming was a steel sheet having a sheet thickness of t=1.6 mm. A steel sheet having a material strength (tensile strength) of 590 MPa was used in No. 1, a steel sheet having a material strength of 980 MPa was used in No. 2, and a steel sheet having a material strength of 1180 MPa was used in No. 3.

(51) As can be seen from Table 1, the amount of spring-back was −9.2 mm in the sample of No. 1, the amount of spring-back was −12.7 mm in the sample of No. 2, the amount of spring-back was −16.1 mm in the sample of No. 3, and the amount of spring-back became larger as the material strength increased.

Invention Examples

(52) On the basis of the results of Comparative Examples described above, in Examples based on the present invention (No. 4 to No. 6), press forming analysis, in which forming is performed such that, in the first step 10B, the line length of the curved convex side WA is shorter than that of the product and the line length of the curved concave side WB is longer than that of the product and such that, in the second step 10C, the line length of the curved convex side WA is longer than the line length in the first step 10B and the line length of the curved concave side WB is shorter than the line length in the first step 10B, was performed.

(53) Specifically, by performing, with a computer, simulation analysis in which each metal sheet is formed into the product shape 1 by one press forming, actually, from the analysis results of Comparative Examples described above, the line length L1 of the longitudinal direction and the average amount of strain ε1 of the longitudinal direction in the compressive stress region of the longitudinal direction generated on the curved convex side WA, and the line length L1′ of the longitudinal direction and the average amount of strain ε1′ of the longitudinal direction in the tensile stress region of the longitudinal direction generated on the curved concave side WB were determined.

(54) The line lengths of the curved convex side WA and the curved concave side WB in the first step 10B were set such that:
L1−L2=0.7×|L1×ε1|
L2′−L1′=0.3×|L1′×ε1′|
where L2 is the line length of the curved convex side WA after the first step 10B, and L2′ is the line length of the curved concave side WB after the first step 10B.

(55) Furthermore, the line length L3 of the curved convex side WA in the second step 10C was set to be 1.00×L2, and the line length L3′ of the curved concave side WB was set to be 0.998×L2′.

(56) In the same manner as Comparative Examples, a metal sheet used in press forming was a steel sheet having a sheet thickness of t=1.6 mm. More specifically, a steel sheet having a material strength (tensile strength) of 590 MPa was used in No. 4, a steel sheet having a material strength of 980 MPa was used in No. 5, and a steel sheet having a material strength of 1180 MPa was used in No. 6.

(57) Under the above conditions, press forming analysis was performed using a model of the die in the first step 10B, and spring-back analysis after the press formed product formed to the forming bottom dead center is removed from the die was performed. Then, forming analysis in which the formed product after the spring-back is restrike formed in the second step 10C was performed, and spring-back analysis after the press formed product formed to the forming bottom dead center is removed from the die was performed.

(58) When the manufacturing method according to aspects of the present invention is applied, as can be seen from Table 1, the amount of spring-back was −3.1 mm in the sample of No. 4, the amount of spring-back was −4.8 mm in the sample of No. 5, and the amount of spring-back was −6.5 mm in the sample of No. 6.

(59) More specifically, in Invention Examples, the amount of spring-back was reduced compared to Comparative Examples. Furthermore, in a comparison of a dimensional accuracy difference between the 590 MPa material and the 1180 MPa material, the dimensional accuracy difference was 6.9 mm in Comparative Examples, whereas the dimensional accuracy difference was 3.4 mm and a variation in dimensional accuracy was reduced in Invention Examples.

(60) It is found that, even when the material strength varies, a component having high dimensional accuracy can be obtained by applying aspects of the present invention as described above.

(61) The entire contents of Japanese Patent Application No. 2017-152412 (filed on Aug. 7, 2017) to which the present application claims priority are a part of the present disclosure by reference.

(62) Although the present invention has been described with reference to the limited number of embodiments, the scope of the present invention is not limited thereto, and modifications of the respective embodiments based on the above disclosure are obvious to those skilled in the art.

REFERENCE SIGNS LIST

(63) 1 product shape 1A top plate part 1B side wall part 1C flange part 1a, 1b bent line position 10A designing step 10B first step 10C second step K straight part Q, Q1, Q2 curved part WA curved convex side WB curved concave side