ESTER PLASTICIZERS BASED ON ETHYLHEXANOL AND PROPYLHEPTANOL

Abstract

The present invention relates to an ester obtainable by reacting (a) an alcohol mixture comprising 20-50 wt % ethylhexanol, 40-64 wt % propylheptanol and 0-20 wt % of other alcohols with (b) a polycarboxylic acid. Further aspects of the invention relate to a thermoplastic polymer comprising the ester according to the invention and uses of said ester.

Claims

1. An ester obtainable by reacting (a) an alcohol mixture comprising (i) from 20-50 wt % ethylhexanol, based on the total weight of the alcohol mixture (ii) from 40-64 wt % propylheptanol, based on the total weight of the alcohol mixture (iii) from 0-20 wt % other alcohols, based on the total weight of the alcohol mixture with (b) a polycarboxylic acid or anhydride thereof

2. The ester according to claim 1, wherein the polycarboxylic acid is an aromatic polycarboxylic acid.

3. The ester according to claim 2, wherein the aromatic polycarboxylic acid is an aromatic tricarboxylic acid.

4. The ester according to claim 1, wherein the ester is a triester.

5. The ester according to claim 1, wherein the polycarboxylic acid is selected from the group consisting of mellitic acid, trimellitic acid, pyromelitic acid, hemimellitic acid, trimesic acid, naphthalenetricarboxylic acid, anthracenetricarboxylic acid, biphenyltricarboxylic acid, benzophenonetricarboxylic acid and mixtures and position isomers of the aforementioned acids.

6. The ester according to claim 1, wherein the alcohol mixture consists of (i) from 20-50 wt % ethylhexanol, based on the total weight of the alcohol mixture; and (ii) from 40-64 wt % propylheptanol, based on the total weight of the alcohol mixture; and (iii) from 0-20 wt % other alcohols, based on the total weight of the alcohol mixture.

7. The ester according to claim 1, wherein the alcohol mixture comprises 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 20 wt % of the total weight of the alcohol mixture.

8. The ester according to claim 1, wherein the alcohol mixture comprises 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

9. The ester according to claim 1, wherein the alcohol mixture comprises 38-50 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

10. The ester according to claim 1, wherein the alcohol mixture comprises 20-37 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 16 wt % of the total weight of the alcohol mixture.

11. The ester according to claim 1, wherein ethylhexanol is 2-ethylhexanol and propylheptanol is 2-propylheptanol.

12. A thermoplastic polymer comprising the ester according to claim 1.

13. The thermoplastic polymer according to claim 12, wherein the thermoplastic polymer is selected from the group consisting of polyethylene, PET, PC, ABS, polyamide, TPU, TPE, nitrile butadiene rubber (NBR), hydrogenated nitrile butadiene rubber (HNBR), chloroprene rubber (CR), polystyrene and a polyolefin, preferably a halogenated polyolefin such as polyvinyl chloride.

14. A thermoplastic polymer comprising the ester according to claim 2.

15. The thermoplastic polymer according to claim 14, wherein the thermoplastic polymer is selected from the group consisting of polyethylene, PET, PC, ABS, polyamide, TPU, TPE, nitrile butadiene rubber (NBR), hydrogenated nitrile butadiene rubber (HNBR), chloroprene rubber (CR), polystyrene and a polyolefin, preferably a halogenated polyolefin such as polyvinyl chloride.

16. The ester according to claim 2, wherein the alcohol mixture comprises 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 20 wt % of the total weight of the alcohol mixture.

17. The ester according to claim 2, wherein the alcohol mixture comprises 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

18. The ester according to claim 2, wherein the alcohol mixture comprises 38-50 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

19. The ester according to claim 2, wherein the alcohol mixture comprises 20-37 wt % ethylhexanol, based on the total weight of the alcohol mixture; and the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols, wherein said other alcohols are not more than maximally 16 wt % of the total weight of the alcohol mixture.

20. The ester according to claim 2, wherein ethylhexanol is 2-ethylhexanol and propylheptanol is 2-propylheptanol.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0017] Before the present invention is described in detail below, it is to be understood that this invention is not limited to the particular methodology, protocols and reagents described herein as these may vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to limit the scope of the present invention which will be limited only by the appended claims. Unless defined otherwise, all technical and scientific terms used herein have the same meanings as commonly understood by one of ordinary skill in the art.

[0018] In the following passages different aspects of the invention are defined in more detail. Each aspect so defined may be combined with any other aspect or aspects unless clearly indicated to the contrary. In particular, any feature indicated as being preferred or advantageous may be combined with any other feature or features indicated as being preferred or advantageous.

[0019] Some documents are cited throughout the text of this specification. Each of the documents cited herein (including all patents, patent applications, scientific publications, manufacturer's specifications, instructions, DIN norms etc.), whether supra or infra, are hereby incorporated by reference in their entirety. Nothing herein is to be construed as an admission that the invention is not entitled to antedate such disclosure by virtue of prior invention.

[0020] Novel plasticizers were identified that have a reduced volatility at higher temperatures and are also characterized by a low pour point. Accordingly, the invention provides in a first aspect an ester obtainable by reacting

[0021] (a) an alcohol mixture comprising [0022] (i) 20-50 wt % ethylhexanol, based on the total weight of the alcohol mixture [0023] (ii) 40-64 wt % propylheptanol, based on the total weight of the alcohol mixture [0024] (iii) 0-20 wt % other alcohols, based on the total weight of the alcohol mixture

[0025] with

[0026] (b) a polycarboxylic acid or anhydride thereof.

[0027] Preferably said polycarboxylic acid used to make the ester is an aromatic polycarboxylic acid and more preferably said polycarboxylic acid is an aromatic tricarboxylic acid.

[0028] In a further preferred embodiment the ester according to the invention is a triester. For example, the ester of the invention may be a triester obtainable by reacting

[0029] (a) an alcohol mixture comprising [0030] (i) 20-50 wt % ethylhexanol, based on the total weight of the alcohol mixture [0031] (ii) 40-64 wt % propylheptanol, based on the total weight of the alcohol mixture [0032] (iii) 0-20 wt % other alcohols, based on the total weight of the alcohol mixture

[0033] with

[0034] (b) an aromatic tricarboxylic acid or anhydride thereof.

[0035] Preferably, components (i), (ii) and (iii) together are in total 100 wt % of the alcohol mixture, i.e. the alcohol mixture (a) of the invention preferably consists of components (i), (ii) and (iii). In a preferred embodiment of the ester, said polycarboxylic acid is selected from the group consisting of mellitic acid, trimellitic acid, pyromelitic acid, hemimellitic acid, trimesic acid, naphthalenetricarboxylic acid, anthracenetricarboxylic acid, biphenyltricarboxylic acid, benzophenonetricarboxylic acid and mixtures and position isomers of the aforementioned acids.

[0036] In a further preferred embodiment, the alcohol mixture consists of

[0037] (i) 20-50 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0038] (ii) 40-64 wt % propylheptanol, based on the total weight of the alcohol mixture; and

[0039] (iii) 0-20 wt % other alcohols, based on the total weight of the alcohol mixture.

[0040] “Other alcohols” as used herein are preferably alcohols other than those used as components (i) and (ii). In a more preferred embodiment, “other alcohols” are branched primary alcohols and even more preferably a decanol other than 2-propylheptanol or an alcohol mixture comprising such decanols.

[0041] Most preferably, “other alcohols” refers to a branched primary decanol different from 2-propylheptanol or refers to an alcohol mixture consisting of two or more of such branched primary decanols.

[0042] In a further preferred embodiment of the ester according to the invention the alcohol mixture comprises

[0043] 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0044] the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols,

[0045] wherein said other alcohols are not more than maximally 20 wt % of the total weight of the alcohol mixture.

[0046] It is further preferred that the alcohol mixture comprises

[0047] 30-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0048] the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols,

[0049] wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

[0050] In a more preferred embodiment the alcohol mixture comprises

[0051] 30-35 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0052] the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols,

[0053] wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

[0054] In a further preferred embodiment, the alcohol mixture comprises

[0055] 38-50 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0056] the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols,

[0057] wherein said other alcohols are not more than maximally 15 wt % of the total weight of the alcohol mixture.

[0058] In a more preferred embodiment the alcohol mixture comprises

[0059] 40-45 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0060] the remaining alcohols in the alcohol mixture consist of propylheptanol and other alcohols,

[0061] wherein said other alcohols are not more than maximally 12 wt % of the total weight of the alcohol mixture.

[0062] Alternatively, the ester of the invention may also be based on an alcohol mixture that comprises

[0063] 20-37 wt % ethylhexanol, based on the total weight of the alcohol mixture; and

[0064] the remaining alcohols in the alcohol mixture consist of propylheptanol and 5 other alcohols,

[0065] wherein said other alcohols are not more than maximally 16 wt % of the total weight of the alcohol mixture.

[0066] In a particularly preferred embodiment of the ester according to the invention said ethylhexanol is 2-ethylhexanol and said propylheptanol is 2-propylheptanol.

[0067] A further aspect of the invention relates to a thermoplastic polymer comprising the ester according to the invention.

[0068] Thereby it is preferred that the thermoplastic polymer is selected from the group consisting of polyethylene, PET, PC, ABS, polyamide, TPU, TPE, nitrile butadiene rubber (NBR), hydrogenated nitrile butadiene rubber (HNBR), chloroprene rubber (CR), polystyrene and a polyolefin, preferably a halogenated polyolefin such as polyvinyl chloride.

[0069] Preferably, the thermoplastic polymer is a halogenated polymer. More preferably, the halogenated polymer is a PVC polymer selected from the group consisting of PVC homopolymers, PVC copolymers, polyvinyl dichlorides (PVDC), and polymers of vinylchloride with vinyl, acrylic and other co-monomers.

[0070] In a further aspect the invention provides the use of the ester of the invention as defined herein as plasticizer in a thermoplastic polymer.

[0071] A preferred embodiment of the use according to the invention relates to a use, wherein the thermoplastic polymer is selected from the group consisting of polyethylene, PET, PC, ABS, polyamide, TPU, TPE, nitrile butadiene rubber (NBR), hydrogenated nitrile butadiene rubber (HNBR), chloroprene rubber (CR), polystyrene and a polyolefin, preferably a halogenated polyolefin such as polyvinyl chloride.

[0072] Various modifications and variations of the invention will be apparent to those skilled in the art without departing from the scope of the invention. Although the invention has been described in connection with specific preferred embodiments, it should be understood that the invention as claimed should not be unduly limited to such specific embodiments.

[0073] The following examples are merely illustrative of the present invention and should not be construed to limit the scope of the invention as indicated by the appended claims in any way.

EXAMPLES

Example 1: Ester Production

[0074] The amount of 2-ethylhexanol (“2 EH”) and 2-propylheptanol (“2 PH”) indicated in table 1 below was heated under nitrogen with trimellitic acid anhydride (“TMA”; respective amounts see table) and 500 ppm of tin-(II)-oxalate (Evonic), based on the total amount of the composition. The 2-propylheptanol that was used was of technical grade purity and therefore consisted of 80% 2-propylheptanol and 20% decanol isomers other than 2-propylheptanol. The esterification reaction begins at about 150° C. with the formation of water and the temperature is slowly increased to 220° C. After 4 hours the reaction water was further removed and the vacuum was reduced over 10 hours to about 5 mbar. The reaction was stopped when the acid number dropped below 1. Remaining unreacted alcohol was removed by distillation. Thereafter, the product was filtered.

TABLE-US-00001 TABLE 1 Amounts of compounds used Example 2 EH in g 2 PH in g TMA in g Yield in g 1 996 0 352 998 2 682 415 403 1163 3 990 1370 837 2430 4 343 755 406 1228 5 0 1134 367 1153

Example 2: Determination of Physical Properties of the Ester

[0075] The degree of discoloration of the ester was measured in Hazen units according to the method described in DIN EN ISO 6271-2005.

[0076] The acid number was determined according to DIN 53402.

[0077] The viscosity was measured using DIN 53019.

[0078] Furthermore, the pourpoint, which indicates the lowest temperature at which a liquid becomes semi solid and loses its flow characteristics, was determined according to DIN ISO 3016(10/82).

[0079] The cloud point was determined according 5 to DIN EU 23015.

[0080] Volatility of the ester was tested using a Netzsch instrument for thermogravimetry by heating a sample under N2 from 20° C. to a final temperature of 300° C. at a rate of at a 10 K/min. After the sample reached a temperature of 300° C. the sample was kept at this temperature for 30 minutes.

[0081] The results are shown in table 2 and 3 below:

TABLE-US-00002 TABLE 2 Acid number Calculation Viscosity 20° C. Example Color Hazen (mg KOH/g) index 20° C. (mPa .Math. s) 1 95 0.2 1.4853 300 2 96 0.09 1.4844 333 3 88 0.12 1.4837 364 4 108 0.11 1.4835 368 5 159 0.74 1.4826 401

TABLE-US-00003 TABLE 3 % weight loss of ester after heat treatment as Example pour-point described cloud point 1 −42 93% −25 2 −36 n.d. n.d. 3 −40 70% −35 4 −45 n.d. n.d. 5 −35 56% −17

[0082] Examples 3 and 4 are according to the invention

Example 3: Thermoplastic Composition Comprising Ester

[0083] The following compositions were prepared:

TABLE-US-00004 TABLE 4 Preparation of test specimens Example: B6 B7 B8 B9 B10 Polyvinyl chloride 100  100  100  100  100  Edenol D 81 3 3 3 3 3 (epoxidized soybean oil) Stabiol CZ 2222 2 2 2 2 2 (Ca/Zn-based stabilizer) Ester of example 1 40  — — — — Ester of example 2 — 40  — — — Ester of example 3 — — 40  — — Ester of example 4 — — — 40  — Ester of example 5 — — — — 40 

[0084] The components as shown above were mixed together and milled on a laboratory rolling mill for 5 minutes at 185° C. Using rolled sheets 3 mm press plates were produced in a laboratory press at 180° C. and on these test specimens were examined according to DIN ISO 868 for their Shore A hardness (three measurements per sample). The results are outlined in table 5 below:

TABLE-US-00005 Example: B6 B7 B8 B9 B10 Shore A 94.8 96.9 96.9 97.6 97.8 96.3 96.6 96.9 98.11 97.7 95.1 96.6 96.9 98.0 97.7

[0085] Examples B8 and B9 are according to the invention.

[0086] As can be seen from the examples above, the optimized ester of the invention can be used as plasticizer in the processing of thermoplastic resins. The ester shows good compatibility with the polymer, low volatilities and also provides excellent low temperature properties.