Abstract
A noble metal-free lanthanum transition metal perovskite catalyst material. The noble metal-free lanthanum transition metal perovskite catalyst material may include a two phase mixture of a lanthanum transition metal perovskite with an alkali or alkaline earth metal carbonate, a lanthanum transition metal perovskite doped with an alkali or alkaline earth metal, or a combination thereof. The lanthanum transition metal perovskite catalyst material provides direct decomposition of NOx into N.sub.2 and O.sub.2 without the presence of a noble metal and in the presence of excess O.sub.2.
Claims
1. A noble metal-free (NMF) catalyst for the direct decomposition of NOx to N.sub.2 and O.sub.2 in a lean exhaust gas comprising: a NMF catalyst material selected from at least one of: a two phase mixture of a La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5) and an alkali or alkaline earth metal carbonate with a chemical formula of A.sub.nCO.sub.3 (n=integer); wherein: L′ is any combination of Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y, and M and M′ are any combination of Fe, Mn, Co, Cr, Ni, Sc, V, Nb, Ta, Sb, In or Ga, when a Goldschmidt tolerance factor for La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 is between 0.7 and 1.0, inclusive; and A.sub.nCO.sub.3 is a carbonate of Na, K, Mg, Ca, Sr and Ba; and a La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5) doped with an alkali or alkaline earth metal of A′; wherein: L′ is any combination of Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y, and M and M′ are any combination of Fe, Co, and Ni when a Goldschmidt tolerance factor for La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 is between 0.7 and 1.0, inclusive; and A′ is at least one of Na, K, Mg and Ba.
2. The NMF catalyst of claim 1, wherein the NMF catalyst material is the two phase mixture of La transition metal perovskite and the alkali or alkaline earth metal carbonate.
3. The NMF catalyst of claim 2, wherein M is at least one of Fe and Co.
4. The NMF catalyst of claim 3, wherein A.sub.nCO.sub.3 is at least one of CaCO.sub.3, SrCO.sub.3, K.sub.2CO.sub.3 and BaCO.sub.3.
5. The NMF catalyst of claim 4, wherein A.sub.nCO.sub.3 is BaCO.sub.3 and a concentration of Ba in the NMF catalyst material is between 0.1 to 10 wt %, inclusive.
6. The NMF catalyst of claim 5, wherein M is Fe, y equals 0 and x equals 0.
7. The NMF catalyst of claim 1, wherein the NMF catalyst material is the La transition metal perovskite doped with the alkali or alkaline earth metal.
8. The NMF catalyst of claim 7, wherein M is at least one of Fe and Ni.
9. The NMF catalyst of claim 8, wherein M is Fe.
10. The NMF catalyst of claim 9, wherein A′ is Ba.
11. The NMF catalyst of claim 10, wherein a concentration of Ba in the NMF catalyst material is between 0.1 to 10 wt %, inclusive.
12. A noble metal-free (NMF) catalyst for the direct decomposition of NOx to N.sub.2 and O.sub.2 in a lean exhaust gas comprising: a two phase mixture of a La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5) and an alkali or alkaline earth metal carbonate with a chemical formula of A.sub.nCO.sub.3 (n=integer); wherein: L′ is any combination of Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y, and M and M′ are any combination of Fe, Mn, Co, Cr, Ni, Sc, V, Nb, Ta, Sb, In or Ga when a Goldschmidt tolerance factor for La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 is between 0.7 and 1.0, inclusive; and A.sub.nCO.sub.3 is a carbonate of Na, K, Mg, Ca, Sr and Ba.
13. The NMF catalyst of claim 12, wherein M is at least one of Fe and Co, and A.sub.nCO.sub.3 is at least one of CaCO.sub.3, SrCO.sub.3, K.sub.2CO.sub.3 and BaCO.sub.3.
14. The NMF catalyst of claim 13, wherein A.sub.nCO.sub.3 is BaCO.sub.3.
15. The NMF catalyst of claim 14, wherein a concentration of Ba in the two phase mixture of the La transition metal perovskite and the alkali or alkali metal carbonate is between 0.1 to 10 wt %, inclusive.
16. The NMF catalyst of claim 14, wherein M is Fe, y equals 0 and x equals 0.
17. A method for the direct decomposition of NOx to N.sub.2 and O.sub.2 in a lean exhaust gas comprising: flowing an exhaust gas generated by an internal combustion engine through a noble metal-free (NMF) catalyst, the exhaust gas containing NOx and excess O.sub.2, the NMF catalyst containing at least one of: a two phase mixture of La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5) and an alkali or alkaline earth metal carbonate with a chemical formula of A.sub.nCO.sub.3 (n=integer); wherein: L′ is any combination of Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y, and M and M′ are any combination of Fe, Mn, Co, Cr, Ni, Sc, V, Nb, Ta, Sb, In or Ga, when a Goldschmidt tolerance factor for the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 is between 0.7 and 1.0, inclusive; and A.sub.nCO.sub.3 is a carbonate of Na, K, Mg, Ca, Sr and Ba; a La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5) doped with an alkali or alkaline earth metal of A′; wherein: M and M′ is at least one of Mn, Fe, Co and Ni; and A′ is at least one of Na, K, Mg and Ba; and directly decomposing the NOx into N.sub.2 and O.sub.2 using the NMF catalyst.
18. The method of claim 17, wherein the NMF catalyst is the two phase mixture of La transition metal perovskite and alkali or alkaline earth metal carbonate, wherein M is at least one of Fe and Co, and A.sub.nCO.sub.3 is at least one of CaCO.sub.3, SrCO.sub.3, K.sub.2CO.sub.3 and BaCO.sub.3.
19. The method of claim 18, wherein A.sub.nCO.sub.3 is BaCO.sub.3.
20. The method of claim 19, wherein a concentration of Ba in the two phase mixture of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 and BaCO.sub.3 is between 0.1 to 10 wt %, inclusive.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0007] The embodiments set forth in the drawings are illustrative and exemplary in nature and not intended to limit the subject matter defined by the claims. The following detailed description of the illustrative embodiments can be understood when read in conjunction with the following drawings, where like structure is indicated with like reference numerals and in which:
[0008] FIG. 1 depicts a noble metal-free La transition metal perovskite catalyst material according to one or more embodiments shown and described herein;
[0009] FIG. 2 depicts a process for making an La transition metal perovskite catalyst material according to one or more embodiments shown and described herein;
[0010] FIG. 3 depicts an x-ray diffraction (XRD) scan of a La transition metal perovskite catalyst material according to one or more embodiments shown and described herein;
[0011] FIG. 4 graphically depicts NO conversion as a function of temperature for La transition metal perovskite catalyst materials according to one or more embodiments shown and described herein;
[0012] FIG. 5 graphically depicts NO conversion at 800° C. as a function of time for La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0013] FIG. 6 graphically depicts N.sub.2 signal as a function of temperature (N.sub.2 release temperature) for La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0014] FIG. 7 graphically depicts O.sub.2 signal as a function of temperature (O.sub.2 release temperature) for La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0015] FIG. 8 graphically depicts N.sub.2O signal as a function of temperature (N.sub.2O release temperature) for La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0016] FIG. 9 graphically depicts NO.sub.2 signal as a function of temperature (NO.sub.2 release temperature) for La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0017] FIG. 10 graphically depicts percentage of NO conversion at 800° C. for exhaust gases with different O.sub.2 contents for La transition metal perovskite catalyst materials according to one or more embodiments disclosed herein;
[0018] FIG. 11 graphically depicts normalized NO decomposition activity at 800° C. for exhaust gases with different O.sub.2 contents for a Ba—LaFeO.sub.3 catalyst material according to one or more embodiments disclosed herein;
[0019] FIG. 12 graphically depicts NO conversion as a function of temperature for La transition metal perovskite catalyst materials according to one or more embodiments shown and described herein;
[0020] FIG. 13A depicts La transition metal perovskite catalyst materials in a honeycomb shaped catalyst according to one or more embodiments described herein;
[0021] FIG. 13B depicts a microstructure for a La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0022] FIG. 13C depicts a microstructure for a La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0023] FIG. 14 depicts a crystal structure of La transition metal perovskite catalyst materials according to one or more embodiments described herein;
[0024] FIG. 15 depicts an internal combustion engine with an exhaust system that has a La transition metal perovskite catalyst material according to one or more embodiments described herein; and
[0025] FIG. 16 depicts a process for the direct decomposition of NOx in an exhaust gas with excess O.sub.2 using a La transition metal perovskite catalyst material according to one or more embodiments described herein.
DETAILED DESCRIPTION
[0026] FIG. 1 generally depicts one embodiment of a NMF La transition metal perovskite catalyst material for the direct decomposition of NOx in an exhaust gas. The NMF La transition metal perovskite catalyst material can be a two phase mixture of a La transition metal perovskite and an alkali or alkaline earth metal carbonate, a La transition metal perovskite doped with an alkali or alkaline earth metal, or a combination thereof. The La transition metal perovskite catalyst materials have a high activity for the direct decomposition of NOx into N.sub.2 and O.sub.2, even in the presence of excess oxygen.
[0027] The La transition metal perovskite catalyst materials disclosed herein may be part of vehicle exhaust systems that provide direct decomposition of NOx under lean-burn conditions. It will be understood that the term “noble metal-free” as used herein refers to a catalyst material that has no intentional additions of a noble metal such as platinum, palladium, rhodium, etc.; the term “lean exhaust gas” as used herein refers to an exhaust gas generated by an internal combustion engine with excess oxygen; the term “lanthanide” or “lanthanide element” as used herein refers to the lanthanide series elements lanthanum (La), samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium (Dy), lutetium (Lu), erbium (Er), ytterbium (Yb), praseodymium (Pr), neodymium (Nd), holmium (HO), post-transition metal bismuth (Bi) and transition metal yttrium (Y); and the term “transition metal” as used herein refers to the transition metal series elements iron (Fe), manganese (Mn), cobalt (Co), chromium (Cr), nickel (Ni), scandium (Sc), vanadium (V), niobium (Nb), tantalum (Ta), metalloid antimony (Sb), and post-transition metals indium (In) and gallium (Ga).
[0028] Still referring to FIG. 1, a NMF catalyst material is shown generally at reference numeral 10. The NMF catalyst material 10 may contain a La transition metal perovskite with a chemical formula of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3, with 0.0≦y≦0.5 and 0.0≦x≦0.5, (referred to simply as LaL′MM′O.sub.3 in the figures) and an alkali or alkaline earth metal (A) as illustrated at reference numeral 100 and referred to hereafter as La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A. In embodiments, the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 100 may be a two phase mixture of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 and an alkali or alkaline earth metal carbonate A.sub.nCO.sub.3 as illustrated at reference numeral 110 and referred to hereafter as La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3, i.e. the ‘A’ in the expression La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A refers to an alkali or alkaline earth metal carbonate A.sub.nCO.sub.3. In other embodiments, the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 100 may be La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 doped with an alkali or alkaline earth metal dopant (A′) as illustrated at reference numeral 120 and referred to hereafter as La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′, i.e. the ‘A’ in the expression La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A refers to an alkali or alkaline earth metal dopant A′. In embodiments, the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 100 may contain La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3 and La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′ and the alkali or alkaline earth metal in the A.sub.nCO.sub.3 carbonate may or may not be the same as the alkali or alkaline earth metal dopant A′. The concentration of the alkali or alkaline earth metal in the A.sub.nCO3 carbonate and/or the concentration of the alkali or alkaline earth metal dopant A′ in the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 100 can be between 0.1 and 10.0 wt %, inclusive. In embodiments, the concentration of the alkali or alkaline earth metal in the A.sub.nCO3 carbonate and/or the concentration of the alkali or alkaline earth metal dopant A′ in the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 100 can be between 0.5 and 5.0 wt %, inclusive. For the purposes of the present disclosure, the term “inclusive” means the inclusion of the first and last number listed, and all numbers in between. The La in the La transition metal perovskite can be partially substituted with one or more elements (L′) selected from Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y. A particular transition metal (M) in the La transition metal perovskite can be partially substituted with one or more elements (M′) selected from Fe, Mn, Co, Cr, Ni, Sc, V, Nb, Ta, Sb, In or Ga. Any combination of La with a different lanthanide element(s) L′ and a transition metal M with a different transition element(s) M′ result in the Goldschmidt Tolerance Factor (t) for the La transition metal perovskite to be within the predefined range of 0.7≦t≦1.0. It is appreciated that the Goldschmidt Tolerance Factor as used herein is an indicator for the stability and distortion of the La transition metal crystal structure and is defined as:
[00001]
where r.sub.L′ is the radius of the L′-cation, r.sub.M′ is the radius of the M′-cation and r.sub.O is the radius of the anion (oxygen). It is also appreciated that for t<0.7 and t>1.0 the La transition metal perovskite crystal structure will not be cubic or orthorhombic/rhombohedral as desired. In embodiments, the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3 catalyst material can include a carbonate of at least one of Na, K, Mg, Ca, Sr, and Ba and the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′ catalyst material can be doped with at least one of Na, K, Mg, and Ba when M is at least one of Fe, Co, Mn, and Ni.
[0029] Referring to FIG. 2, a method for making a NMF La transition metal perovskite catalyst material is shown generally at reference numeral 20. The method includes synthesis of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 powder using the citric acid method and calcination up to 800° C. at step 200. An alkali or alkali metal solution is prepared at step 202 by dissolving an alkali or alkali metal in deionized. The amount of alkali or alkali metal added to the deionized water corresponds to a target of 5 weight percent (wt %) alkali or alkali metal in the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material. The La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 powder produced in step 200 is added to the to the alkali or alkali metal solution at step 204 which is then dried at 120° C. for 24 hours and calcined at 500° C. for 30 minute at step 206. The citric acid method for the synthesis of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 includes wet impregnation of alkali or alkaline earth metal acetate followed by the drying and calcination. Examples of preparing a La transition metal perovskite with alkali metal carbonates are provided below.
[0030] Multiple batches of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 with y=1.0, x=1.0 and M=Fe, i.e. LaFeO.sub.3, were synthesized with a target yield of 4 grams per batch. Between 7.016 and 7.136 grams of La(NO.sub.3).sub.3.6H.sub.2O, between 6.571 and 6.710 grams of Fe(NO.sub.3)3.6H.sub.2O, and approximately 55 grams of deionized water were added to a glass beaker. The La(NO.sub.3).sub.3.6H.sub.2O and Fe(NO.sub.3).sub.3.6H.sub.2O were dissolved in the 55 grams of deionized water with magnetic stirring on a stir plate at ambient temperature for 30 minutes. Then, 6.100 to 6.401 grams of anhydrous citric acid was added to the glass beaker and the temperature was increased to 80° C. while maintaining stirring. After 2 hours, 1.225 milliliters of ethylene glycol was added to the glass beaker using a micropipette and the solution was stirred at 80° C. overnight and until it became a gel. Next, beakers containing the gels were placed in a drying oven and heated to 120° C. at 1° C./min and held at this temperature for 24 hours. The temperature was then increased to 130° C. and remained at this temperature for 4 hours to promote polyesterification. The temperature was then increased to 300° C. and held for 2 hours and a precursor powder of LaFeO.sub.3 was produced. The resulting powder was ground thoroughly in an agate mortar and pestle, placed in a porcelain crucible, and then into a calcination furnace. The temperature of the calcination furnace was increased to room temperature to 800° C. at a rate of 10° C./min and remained at this temperature for 4 hours before cooling to ambient without temperature control.
[0031] The multiple batches of the LaFeO.sub.3 powder were combined and again ground in a mortar and pestle. Three 100 milliliter glass beakers each had 2.250 grams of LaFeO.sub.3 added thereto followed by 50 grams of distilled water mixed by stirring on a magnetic stir plate. Then, 0.7102 grams of Na acetate trihydrate was added to one of the beakers, 1.0582 grams of Mg acetate tetrahydrate was added to another of the beakers, and 0.2231 grams of Ba acetate was added to the third glass beaker. Each beaker was stirred at room temperature for 1 hour. The temperature was increased to 80° C. and stirring was maintained overnight. The resulting solutions were placed in an oven, the temperature increased to 120° C. at 1° C./min and held at this temperature for 24 hours to produce dried powders. The dried powders were removed from the beakers, ground in a mortar and pestle, and placed into crucibles which were placed in a calcination furnace. The temperature of the furnace was increased to 500° C. at 2° C./min and held for 30 minutes before returning to ambient temperature without temperature control. For the production of Sr and Ca containing LaFeO.sub.3 catalyst materials, 1.600 grams of LaFeO.sub.3 was added two 100 milliliter glass beakers. Then, 40 grams of water was added to each of the beakers and the solution was stirred on a magnetic stir plate. Next, 0.1996 grams of strontium acetate was added to one of the beakers and 0.3741 grams of calcium acetate monohydrate was added to the other beaker. Both beakers were stirred at room temperature for 1 hour. The temperature was increased to 80° C. and stirring was maintained overnight. The resulting solutions were placed in an oven and the temperature increased to 120° C. at 1° C./min and held at this temperature for 24 hours to produce dried powders. The dried powders were removed from the beakers, ground in a mortar and pestle, placed into crucibles, and the crucibles placed into a calcination furnace. The temperature of the calcination furnace was increased to 500° C. at 2°/min and held for 30 minutes before returning to ambient temperature without temperature control. Calcined powders with K, Ca and Sr acetate additions were also prepared in a similar manner.
[0032] Calcined powders produced according to the method shown in FIG. 2 were subjected to x-ray diffraction (XRD) to determine which phases were present. The powders were scanned from 10-70 2θ at 0.02°/step and 1°/minute. All of the sample powders showed the presence of LaFeO.sub.3 with resulting peaks and unit cell values closely matching Powder Diffraction File (PDF) card #01-088-0641. Also, carbonates of Na, Ba, Sr, Mg, and Ca were detected and indexed to PDF cards. For example, FIG. 3 graphically depicts the XRD scan for the precursor LaFeO.sub.3 powders and powders produced from the precursor LaFeO.sub.3 plus barium acetate mixture. A peak for BaCO.sub.3 was observed for the powders produced from the precursor LaFeO.sub.3 plus barium acetate mixture, i.e. a two phase mixture of LaFeO.sub.3 and BaCO.sub.3 was detected. The alkali and alkaline earth metals did not incorporate (dope) into the perovskite structure of the LaFeO.sub.3. For example, the LaFeO.sub.3 unit cell did not match the unit cell value of La.sup.0.9Ba.sup.0.1FeO.sub.3 which would be expected based on the quantity of Ba added to the material.
[0033] The activity of the LaFeO.sub.3-alkali and alkaline earth metal carbonate mixtures was evaluated using a micro reactor system (Micromeritics Particulate Systems PID Microactivity Reactor) equipped with a quartz plug flow reactor and coupled with a mass spectrometer (MKS Cirrus-2). The NO concentration was tracked by the detector signal for M/Z 30. The evaluation included placing approximately 1 gram of each LaFeO.sub.3-A.sub.nCO.sub.3 sample between a bed of quartz wool. The samples were preheated to 800° C. in ultrahigh purity helium (UHP He) and then cooled to 100° C. The UHP He was passed through the reactor with the powders for 15 minutes to determine 100% conversion of NO, i.e. 0.0% NO detected by the mass spectrometer. Then a reaction mixture containing 13.3 ml/min of UHP He and 14.5 ml/min of 1.911% NO/He was passed through a bypass around each LaFeO.sub.3-A.sub.nCO.sub.3 sample for 30 minutes to determine 0% conversion of NO. The flow was stabilized over the catalyst for 30 minutes and the temperature was increased from 0 to 800° C. with a furnace ramp rate of 10°/min. The temperature was held at 800° C. for approximately 30 minutes to obtain data at steady state. Next, and to determine performance in excess oxygen, five oxygen concentrations of approximately 0.78%, 1.01%, 1.26%, 1.51%, and 1.78% were added to the reaction mixture for 30, 15, 15, 15, and 15 minutes, respectively.
[0034] Referring to FIG. 4, results are shown for NO conversion as a function of temperature for NMF LaFeO.sub.3—BaCO.sub.3, LaFeO.sub.3—K.sub.2CO.sub.3, LaFeO.sub.3—SrCO.sub.3, LaFeO.sub.3—CaCO.sub.3, LaFeO.sub.3—Na.sub.2CO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials produced according to one or more embodiments disclosed herein. In addition, results for a baseline NMF LaFeO.sub.3 material are shown. As shown in FIG. 4, the LaFeO.sub.3—Na.sub.2CO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials perform similarly to LaFeO.sub.3 at temperatures from about 600-800° C. Specifically, LaFeO.sub.3—Na.sub.2CO.sub.3, LaFeO.sub.3—MgCO.sub.3 and LaFeO.sub.3 have an approximate 0-5% NO conversion at temperatures between 600-800° C. In contrast, the NMF LaFeO.sub.3—CaCO.sub.3 and LaFeO.sub.3—SrCO.sub.3 catalyst materials provide an approximate 8-10% NO conversion at 800° C., and the LaFeO.sub.3—K.sub.2CO.sub.3 and LaFeO.sub.3—BaCO.sub.3 catalyst materials show a significant improvement over the baseline LaFeO.sub.3. The LaFeO.sub.3—K.sub.2CO.sub.3 catalyst material provides an approximate 10% NO conversion at 600° C. and an approximate 25% NO conversion at 700° C. The LaFeO.sub.3—BaCO.sub.3 catalyst material provides an approximate 37-40% NO conversion at 800° C.
[0035] Referring to FIG. 5, results are shown for steady state NO conversion at 800° C. for the materials is shown in FIG. 4. Specifically, the baseline LaFeO.sub.3 provided an approximate 2% NO conversion, LaFeO.sub.3—MgCO.sub.3 provided an approximate 1% NO conversion, LaFeO.sub.3—CaCO.sub.3 provided an approximate 11.5% NO conversion, LaFeO.sub.3—SrCO.sub.3 provided an approximate 12.5% NO conversion and LaFeO.sub.3—BaCO.sub.3 provided an approximate 40% NO conversion. The NMF LaFeO.sub.3—BaCO.sub.3 catalyst material exhibited an approximate 20-fold increase in NO conversion at 800° C. compared to the baseline LaFeO.sub.3.
[0036] Referring to FIGS. 6, 7, 8, and 9, the release temperatures for the NMF LaFeO.sub.3, LaFeO.sub.3—BaCO.sub.3, LaFeO.sub.3—SrCO.sub.3, LaFeO.sub.3—CaCO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials for N.sub.2, O.sub.2, N.sub.2O, and NO.sub.2 are shown. It should be appreciated that the release temperature is estimated for a given catalyst material at the inflection of a given signal-temperature curve, i.e. where the signal versus temperature curve shows a significant increase. Specifically, an N.sub.2 release temperature (FIG. 6) for the LaFeO.sub.3—BaCO.sub.3 catalyst material is about 600-625° C., which is approximately 200° C. lower than the baseline LaFeO.sub.3 catalyst material and approximately 150° C. lower than the LaFeO.sub.3—CaCO.sub.3 and LaFeO.sub.3—SrCO.sub.3 catalyst materials. The O.sub.2 release temperature (FIG. 7) for the LaFeO.sub.3—BaCO.sub.3 catalyst material is about 550° C., which is approximately 150° C. lower than the LaFeO.sub.3—CaCO.sub.3 and the LaFeO.sub.3—SrCO.sub.3 catalyst materials, but about 150° C. higher than the baseline LaFeO.sub.3 and the LaFeO.sub.3—MgCO.sub.3 catalyst material. The N.sub.2O release temperature (FIG. 8) for the LaFeO.sub.3—CaCO.sub.3 catalyst is approximately 450° C., which is approximately 200° C. less than the release temperature provided by the LaFeO.sub.3—SrCO.sub.3, and approximately 300° C. lower than the release temperature provided by the LaFeO.sub.3—BaCO.sub.3. The NO.sub.2 release temperature (FIG. 9) for the baseline LaFeO.sub.3 and the LaFeO.sub.3—MgCO.sub.3 is approximately 325° C., which is approximately 200° C. less than the release temperature provided LaFeO.sub.3—BaCO.sub.3 and approximately 250° C. less than the release temperature provided by LaFeO.sub.3—CaCO.sub.3.
[0037] The performance of the NMF LaFeO.sub.3, LaFeO.sub.3—BaCO.sub.3, LaFeO.sub.3—SrCO.sub.3, LaFeO.sub.3—CaCO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials in the presence of excess oxygen is shown in FIG. 10. Specifically, the NO conversion of the NMF LaFeO.sub.3, LaFeO.sub.3—BaCO.sub.3, LaFeO.sub.3—SrCO.sub.3, LaFeO.sub.3—CaCO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials tested at 800° C. in the 13.3 ml/min of UHP He+14.5 ml/min of 1.911% NO/UHP He gas mixture with the additions of 0.78%, 1.01%, 1.26%, 1.51%, and 1.78% O.sub.2 are shown in FIG. 10. Regarding the LaFeO.sub.3 and LaFeO.sub.3—MgCO.sub.3 catalyst materials, the NO conversion remained generally constant near 0.0% for all of the O.sub.2 concentrations. For LaFeO.sub.3—CaCO.sub.3, the NMF catalyst material's NO conversion was reduced from approximately 11.5% for 0.0% O.sub.2 to approximately 4.5% with 0.78% O.sub.2 present I the gas mixture and down to approximately 4.0% with 1.01, 1.26, 1.51 and 1.78% O.sub.2 present. Regarding LaFeO.sub.3—SrCO.sub.3, the NMF catalyst material's NO conversion was reduced from approximately 12.5% for 0.0% O.sub.2 to approximately 7.0% with 0.78, 1.01, 1.26, 1.51 and 1.78% O.sub.2 present in the gas mixture. Regarding LaFeO.sub.3—BaCO.sub.3, the NMF catalyst material's NO conversion was reduced from approximately 40.0% for 0.0% O.sub.2 to approximately 28.0% with 0.78% O.sub.2 present in the gas mixture, 26.5% with 1.01% O.sub.2 present, 25.0% with 1.26% O.sub.2 present, 24.0% with 1.51% O.sub.2 present and 23.0% with 1.78% O.sub.2 present. FIG. 11 shows the normalized NO decomposition activity for the LaFeO.sub.3—BaCO.sub.3 catalyst material as a function of O.sub.2 in the reaction mixture. It should be appreciated that the LaFeO.sub.3—BaCO.sub.3 catalyst material exhibits a normalized NO decomposition activity of approximately 0.6 even with 1.8% excess O.sub.2 in the reaction mixture.
[0038] Referring to FIG. 12, NO conversion as a function of temperature for a baseline La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 with y=1.0, x=1.0 and M=Co, i.e. LaCoO.sub.3, and a NMF LaCoO.sub.3—BaCO.sub.3 catalyst material is shown. The LaCoO.sub.3 and LaCoO.sub.3—BaCO.sub.3 materials were produced according to the citric acid method described above. As shown in FIG. 12, adding BaCO.sub.3 to the LaCoO.sub.3 material provides an increase of NO conversion activity compared to the baseline LaCoO.sub.3 material of approximately 1.5-2.0% at 550° C. At 650° C., adding BaCO.sub.3 to the LaCoO.sub.3 material provides an increase of NO conversion activity compared to the baseline LaCoO.sub.3 material of approximately 5.0%, and at 750° C. the addition of BaCO.sub.3 to the LaCoO.sub.3 material provides an increase of NO conversion activity compared to the baseline LaCoO.sub.3 material of approximately 12.5%. Accordingly, it should be appreciated that a wide range of NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst materials are disclosed herein for the direct decomposition of NOx.
[0039] Referring to FIG. 13A, a honeycomb catalyst 30 made from a NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material according to one or more embodiments disclosed herein is shown. In embodiments, the NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material has a microstructure of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 grains 302 with precipitates or particles A.sub.nCO.sub.3 304 as shown at reference numeral 300 in FIG. 13B. The mixture of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3 shown at reference numeral 300 can include precipitates, particles, etc. of A.sub.nCO.sub.3 within La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 grains, at La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 grain boundaries, at triple junctions between La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 grains, etc. In other embodiments, the NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material has a microstructure of La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3 grains 312 doped with an alkali or alkaline earth metal at shown at reference numeral 310 in FIG. 13C. The La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′ catalyst material shown at reference numeral 310 can have atoms of alkali and alkaline earth metals at La, M and/or O sites within a perovskite crystal structure (see FIG. 14).
[0040] Referring now to FIG. 15, an internal combustion engine with a NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material according to one or more embodiments is shown generally at reference numeral 40. The internal combustion engine 40 has an engine block 400 with a plurality of cylinders and an exhaust manifold 402 that receives exhaust gas from the plurality of cylinders during operation of the internal combustion engine 40. The internal combustion engine 40 can be a spark-ignition internal combustion engine (petrol engine), a compression-ignition internal combustion engine (diesel engine) or a combination spark-ignition/compression-ignition internal combustion engine. The exhaust manifold 402 is in fluid communication with an exhaust duct 404 and exhaust gas originating from the one or more cylinders in the engine block 400 flows through the exhaust manifold 402, the exhaust duct 404 out an exhaust exit 408. Within the exhaust duct 404 is a La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 406. The La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 406 can be at least one of the two phase mixture La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3 illustrated at reference numeral 300 in FIG. 13B and the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′ illustrated at reference numeral 310 in FIG. 13C. The La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material 406 can be in the form of a honeycomb such as the honeycomb catalyst 30 illustrated in FIG. 13A, but it should be appreciated that other shapes and structures that are at least partially made from the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material can be used.
[0041] Referring now to FIG. 16, a method for the direct decomposition of NOx is shown generally at reference numeral 50. The method 50 includes providing an internal combustion engine with an exhaust system at step 500. The exhaust system has an exhaust duct and a NMF La transition metal perovskite catalyst material according to one or more embodiments disclosed herein. In embodiments, the LMF transition metal perovskite catalyst material is a La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material, for example La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A.sub.nCO.sub.3 (0.0≦y≦0.5; 0.0≦x≦0.5), La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3-A′ (0.0≦y≦0.5; 0.0≦x≦0.5), or a combination thereof. The La in the La transition metal perovskite can be partially substituted with one or more elements (L′) selected from Sm, Eu, Gd, Tb, Dy, Lu, Er, Yb, Pr, Nd, Ho, Bi or Y. A particular transition metal (M) in the La transition metal perovskite can be partially substituted with one or more elements (M′) selected from Fe, Mn, Co, Cr, Ni, Sc, V, Nb, Ta, Sb, In or Ga. Any combination of La with a different lanthanide element(s) L′ and a transition metal M with a different transition element(s) M′ result in the Goldschmidt Tolerance Factor (t) for the La transition metal perovskite to be within the predefined range of 0.7<t<1.0. Exhaust gas with NOx and excess O.sub.2 is generated by the internal combustion engine, e.g. during lean-burn conditions, at step 520. The exhaust gas with NOx and excess O.sub.2 flows through the exhaust system and into contact with the NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material. Upon contact with the La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst material, NOx in the exhaust gas decomposes into N.sub.2 and O.sub.2, e.g. 2NO.fwdarw.N.sub.2+O.sub.2, even with excess oxygen in the exhaust gas.
[0042] The NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst materials and methods for the direct decomposition of NOx disclosed herein can be used with other exhaust gas catalysts, sensors, etc. When used as part of an exhaust system, the NMF La.sub.(1-y)L′.sub.(y)M.sub.(1-x)M′.sub.(x)O.sub.3+A catalyst materials have sufficient activity for the direct decomposition of NOx such that noble metals are not needed. The terms “approximately” and “about” may be utilized herein to represent the inherent degree of uncertainty that may be attributed to any quantitative comparison, value, measurement, or other representation. These terms are also utilized herein to represent the degree by which a quantitative representation may vary from a stated reference without resulting in a change in the basic function of the subject matter at issue.
[0043] While particular embodiments have been illustrated and described herein, it should be understood that various other changes and modifications may be made without departing from the spirit and scope of the claimed subject matter. Moreover, although various aspects of the claimed subject matter have been described herein, such aspects need not be utilized in combination. It is therefore intended that the appended claims cover all such changes and modifications that are within the scope of the claimed subject matter.